TY - CONF A1 - Bonse, Jörn T1 - Tribological performance of titanium samples oxidized by fs-laser radiation, thermal heating, or electrochemical anodization N2 - Commercial grade-1 titanium samples (Ti, 99.5% purity) were treated using three alternative methods, i.e., fs-laser processing in air, thermal heat treatment in an oven, or anodization in an electrochemical bath, all resulting in the formation of differently conditioned superficial oxide layers. The laser processing was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning geometry for the processing of several square-millimetres large surface areas covered homogeneously by these nanostructures. The thermal processing in the oven was done at two different temperatures, while the electrochemical anodization was performed at room temperature, aiming to generate different polymorphs of titanium oxide at similar oxide layer thickness. The irradiated surface regions were characterized by optical and scanning electron microscopy, and micro Raman spectroscopy. The tribological performance of the differently treated titanium surfaces was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in un-additivated paraffin oil and fully formulated engine oil as lubricants. The specific tribological performance of the differently treated surfaces is discussed on the basis of possible physical and chemical mechanisms. T2 - International Conference on Laser Ablation, COLA 2017 CY - Marseille, France DA - 03.09.2017 KW - Femtosecond laser KW - Oxidation KW - Laser-induced periodic surface strcutures, LIPSS KW - Friction KW - Wear PY - 2017 AN - OPUS4-42032 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kirner, Sabrina A1 - Wirth, Thomas A1 - Sturm, Heinz A1 - Krüger, Jörg A1 - Bonse, Jörn T1 - Nanometer-resolved chemical analyses of femtosecond laser-induced periodic surface structures on titanium N2 - The chemical characteristics of two different types of laser-induced periodic surface structures (LIPSS), so-called high and low spatial frequency LIPSS (HSFL and LSFL), formed upon irradiation of titanium surfaces by multiple femtosecond laser pulses in air (30 fs, 790 nm, 1 kHz), are analyzed by various optical and electron beam based surface analytical techniques, including micro-Raman spectroscopy, energy dispersive X-ray analysis, X-ray photoelectron spectroscopy, and Auger electron spectroscopy. The latter method was employed in a high-resolution mode being capable of spatially resolving even the smallest HSFL structures featuring spatial periods below 100 nm. In combination with an ion sputtering technique, depths-resolved chemical information of superficial oxidation processes was obtained, revealing characteristic differences between the two different types of LIPSS. Our results indicate that a few tens of nanometer shallow HSFL are formed on top of a ∼150 nm thick graded superficial oxide layer without sharp interfaces, consisting of amorphous TiO2 and partially crystallized Ti2O3. The larger LSFL structures with periods close to the irradiation wavelength originate from the laser-interaction with metallic titanium. They are covered by a ∼200 nm thick amorphous oxide layer, which consists mainly of TiO2 (at the surface) and other titanium oxide species of lower oxidation states underneath. KW - Laser-induced periodic surface structures (LIPSS) KW - Femtosecond laser KW - Oxidation KW - Titanium KW - Auger electron spectroscopy PY - 2017 DO - https://doi.org/10.1063/1.4993128 SN - 0021-8979 VL - 122 IS - 10 SP - 104901, 1 EP - 9 PB - AIP Publishing CY - Melville, NY, USA AN - OPUS4-41905 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rahner, E. A1 - Thiele, T. A1 - Voss, Heike A1 - Müller, F.A. A1 - Bonse, Jörn A1 - Gräf, S. T1 - Objective, high-throughput regularity quantification of laser-induced periodic surface structures (LIPSS) N2 - The growing demand for precise surface functionalization through laser-generated periodic surface structures highlights the necessity for efficient, reproducible, and objective evaluation methods to evaluate their structural regularity. We introduce ReguΛarity (v.1.2.7), a freely available, Python-based software with a graphical user interface for the automated, quantitative assessment of the regularity of laser-induced periodic surfaces structures (LIPSS), obtained from optical microscopy, SEM, or AFM. The software integrates image segmentation, one- and two-dimensional Fourier analyses, and gradient-based orientation determination to facilitate a comprehensive regularity analysis of grating-like (quasi-)periodic surface patterns with spatial periods Λ. This is achieved through the proposed regularity tuple R, composed of five key parameters: the normalized spread of the spatial period RΛ,2D (from 2D-FT), the normalized variation of the most frequent spatial period RΛ (from 1D-FT), the Gini coefficient G, the Dispersion of the LIPSS Orientation Angle δθ (DLOA), and the mean phase deviation . To demonstrate its applicability, we compare ideal sinusoidal patterns with SEM images obtained from LIPSS on stainless steel (AISI 316L) and aluminum alloy (AlMg5) surfaces, confirming the software’s ability to objectively distinguish between varying levels of structural regularity. ReguΛarity facilitates high-throughput analysis and data-driven process optimization in surface engineering and laser materials processing. KW - Laser-induced periodic surface structures (LIPSS) KW - Image processing KW - Regularity quantification KW - Fourier analysis KW - Structural homogeneity PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-654070 DO - https://doi.org/10.1016/j.apsusc.2026.165919 SN - 0169-4332 VL - 726 SP - 1 EP - 12 PB - Elsevier B.V. AN - OPUS4-65407 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bonse, Jörn T1 - Femtosecond Laser Ablation of Semiconductors: Dynamical, Structural and Morphological T2 - European Materials Research Society (EMRS), Spring Meeting, Symposium Q "Laser and Plasma Processing for Advanced Materials" CY - Strasbourg, France DA - 2009-06-08 PY - 2009 AN - OPUS4-19465 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bonse, Jörn A1 - Baudach, Steffen A1 - Kautek, Wolfgang A1 - Geuss, Markus A1 - Sturm, Heinz T1 - The precision of the femtosecond-pulse laser ablation of TiN films on silicon N2 - Ti:sapphire laser pulses of 130 fs and 800 nm were focused on 3.2-7m-thick TiN films by a 60-mm focal length lens in air. The morphology of the ablated areas generated by laser pulses at a fluence slightly above the ablation threshold was characterized in dependence on the pulse number by scanning electron microscopy (SEM) and atomic force microscopy (AFM). The cavity profiles, depths, diameters, and volumes were quantitatively evaluated by AFM. The polarization state of the laser light is discussed as a further parameter, in addition to fluence and pulse number, that influences and controls the ablation precision of these materials. It was observed that circularly polarized radiation enhances the average ablation rates and reduces the roughness in the cavities by a factor of 2-3 as compared to linearly polarized radiation of the same incident laser fluence. Special attention was paid to the interfacial region between the coating and substrate. Ultrashort-pulse laser drilling into the Si substrate revealed the generation of columnar features which even may surmount the original coating under laser conditions. T2 - 5th International Conference on Laser Ablation ; COLA '99 CY - Göttingen, Germany DA - 1999-07-19 KW - Laser ablation KW - Picosecond PY - 1999 DO - https://doi.org/10.1007/s003390051425 SN - 0947-8396 VL - 69 IS - 7 SP - S399 EP - S402 PB - Springer CY - Berlin AN - OPUS4-778 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bonse, Jörn T1 - Scanning force microscopic investigations of the femtosecond pulse laser ablation of indium phosphide in air T2 - SPIE conference Nanotechnology Gran Canaria CY - Maspalomas, Spain DA - 2003-05-20 PY - 2003 AN - OPUS4-4081 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bonse, Jörn A1 - Bachelier, G. A1 - Siegel, J. A1 - Solis, J. A1 - Sturm, Heinz T1 - Time- and space-resolved dynamics of ablation and optical breakdown induced by femtosecond laser pulses in indium phosphide N2 - Femtosecond time-resolved microscopy has been used to analyze the structural transformation dynamics (melting, ablation, and solidification phenomena) induced by single intense 130 fs laser pulses in single-crystalline (100)-indium phosphide wafers in air on a time scale from ~100 fs up to 8 ns. In the ablative regime close to the ablation threshold, transient surface reflectivity patterns are observed by fs microscopy on a ps to ns time scale as a consequence of the complex spatial density structure of the ablating material (dynamic Newton fringes). At higher fluences, exceeding six times the ablation threshold, optical breakdown causes another, more violent ablation regime, which reduces the energy deposition depth along with the time of significant material removal. As a consequence, ablation lasts longer in a ring-shaped region around the region of optical breakdown. This leads to the formation of a crater profile with a central protrusion. In the melting regime below the ablation threshold, the melting dynamics of indium phosphide has been quantified and subsequent superficial amorphization has been observed upon solidification on the ns time scale leading to amorphous layer thicknesses of the order of a few tens of nanometers. KW - Femtosecond laser pulse KW - Indium Phosphide KW - Ablation KW - Surface reflectivity KW - Fs-time resolved microscopy KW - Scanning Force Microscopy PY - 2008 DO - https://doi.org/10.1063/1.2885105 SN - 0021-8979 SN - 1089-7550 VL - 103 IS - 5 SP - 054910-1 EP - 054910-6 PB - American Institute of Physics CY - Melville, NY AN - OPUS4-17090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bonse, Jörn A1 - Munz, Martin A1 - Sturm, Heinz ED - Vajtai, R. T1 - Scanning force microscopic investigations of the femtosecond pulse laser ablation of indium phosphide in air N2 - Laser ablation of single-crystalline indium phosphide (InP) was performed in air by means of linearly polarized Ti:sapphire femtosecond-pulses (800 nm, 130 fs, 10 Hz). As a result of the first laser pulses, several morphological changes (crater formation, rim formation, ripple structures and cones) were observed. These effects were explored using force modulation microscopy (FMM), a technique based on scanning force microscopy (SFM), allowing the simultaneous imaging of both topography and local stiffness at a high lateral resolution. The first laser pulse induces the formation of a protruding rim (height <20 nm, width ~300 nm) bordering the ablated crater. A Fourier-analysis of the multi-pulse generated topographies reveals the formation of wavelength-sized periodic ripples (modulation depth <100 nm) with an orientation perpendicular to that of the electric field vector of the laser radiation. Besides these morphological alterations, also material modifications were observed in the irradiated regions by means of the FFM technique. Within the ablated craters, local stiffness variations were found revealing an inhomogeneous material composition/structure as a consequence of the femtosecond pulse laser treatment. T2 - Nanotechnology Conference 2003 CY - Maspalomas, Gran Canaria, Spain DA - 2003-05-19 KW - Femtosecond laser irradiation KW - Microstructure KW - Indium phosphide KW - Scanning/atomic force microscopy (SFM/AFM) KW - Stiffness KW - Laser induced periodic surface structures (LIPSS) PY - 2003 UR - http://cat.inist.fr/?aModele=afficheN&cpsidt=15329222 SN - 0-8194-4978-4 N1 - Serientitel: SPIE proceedings series – Series title: SPIE proceedings series IS - 5118 SP - 221 EP - 234 PB - SPIE, the International Society for Optical Engineering CY - Bellingham, Wash. AN - OPUS4-2865 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kirner, Sabrina V. A1 - Slachciak, Nadine A1 - Elert, Anna Maria A1 - Griepentrog, Michael A1 - Fischer, Daniel A1 - Hertwig, Andreas A1 - Sahre, Mario A1 - Dörfel, Ilona A1 - Sturm, Heinz A1 - Pentzien, Simone A1 - Koter, Robert A1 - Spaltmann, Dirk A1 - Krüger, Jörg A1 - Bonse, Jörn T1 - Tribological performance of titanium samples oxidized by fs-laser radiation, thermal heating, or electrochemical anodization N2 - Commercial grade-1 titanium samples (Ti, 99.6%) were treated using three alternative methods, (i) femtosecond laser processing, (ii) thermal heat treatment, and (iii) electrochemical anodization, respectively, resulting in the formation of differently conditioned superficial titanium oxide layers. The laser processing (i) was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning setup for the processing of several square-millimeters large surface areas covered homogeneously by these nanostructures. The differently oxidized titanium surfaces were characterized by optical microscopy, micro Raman spectroscopy, variable angle spectroscopic ellipsometry, and instrumented indentation testing. The tribological performance was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in fully formulated engine oil as lubricant. The specific tribological performance of the differently treated surfaces is discussed with respect to possible physical and chemical mechanisms. KW - Femtosecond laser KW - Titanium KW - Oxidation KW - Friction PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-445609 DO - https://doi.org/10.1007/s00339-018-1745-8 SN - 0947-8396 SN - 1432-0630 VL - 124 IS - 4 SP - 326, 1 EP - 10 PB - Springer-Verlag AN - OPUS4-44560 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bonse, Jörn A1 - Munz, Martin A1 - Sturm, Heinz T1 - Structure formation on the surface of indium phosphide irradiated by femtosecond laser pulses N2 - Laser-induced periodic surface structures (LIPSS; ripples) with different spatial characteristics have been observed after irradiation of single-crystalline indium phosphide (c-InP) with multiple linearly polarized femtosecond pulses (130 fs, 800 nm) in air. With an increasing number of pulses per spot, N, up to 100, a characteristic evolution of two different types of ripples has been observed, i.e., (i) the growth of a grating perpendicular to the polarization vector consisting of nearly wavelength-sized periodic lines and (ii), in a specific pulse number regime (N = 5-30), the additional formation of equally oriented ripples with a spatial period close to half of the laser wavelength. For pulse numbers higher than 50, the formation of micrometer-spaced grooves has been found, which are oriented perpendicular to the ripples. These topographical surface alterations are discussed in the frame of existing LIPSS theories. KW - Femtosecond laser irradiation KW - Indium phosphide KW - Microstructure KW - Laser induced periodic surface structures KW - LIPSS KW - SEM PY - 2005 DO - https://doi.org/10.1063/1.1827919 SN - 0021-8979 SN - 1089-7550 VL - 97 SP - 1 EP - 9 PB - American Institute of Physics CY - Melville, NY AN - OPUS4-5992 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bonse, Jörn A1 - Munz, Martin A1 - Sturm, Heinz T1 - Scanning force microscopic investigations of the femtosecond laser pulse irradiation of indium phosphide in air N2 - Laser ablation of single-crystalline indium phosphide (InP) was performed in air by means of linearly polarized Ti : sapphire femtosecond pulses (800 nm, 130 fs, 10 Hz). As a result of the irradiation with a variable number of laser pulses per spot (N /spl les/ 5), several morphological changes (crater formation, rim formation, ripple structures, and cones) were observed. These effects were explored using force modulation microscopy (FMM), a technique based on scanning force microscopy, allowing the simultaneous imaging of both topography and local stiffness at a high lateral resolution. The first laser pulse induces the formation of a protruding rim (height < 20 nm, width /spl ap/ 300 nm) bordering the ablated crater. A Fourier analysis of the multipulse generated topographies reveals the formation of wavelength-sized periodic ripples (modulation depth < 100 nm) with an orientation perpendicular to that of the electric field vector of the laser radiation. Besides these morphological alterations, material modifications were also observed in the irradiated regions by means of the FMM technique. Within the ablated craters, local stiffness variations were found revealing an inhomogeneous material composition/structure as a consequence of the femtosecond pulse laser treatment. KW - Laser materials-processing applications KW - Laser radiation effects KW - Microscopy KW - Semiconductor materials KW - Ultrafast optics PY - 2004 DO - https://doi.org/10.1109/TNANO.2004.828574 SN - 1536-125X SN - 1941-0085 VL - 3 IS - 3 SP - 358 EP - 367 PB - Institute of Electrical and Electronics Engineers CY - New York, NY AN - OPUS4-4067 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -