TY - JOUR A1 - Lu, J. A1 - Zhang, S. A1 - Yao, J. A1 - Guo, Z. A1 - Osenberg, M. A1 - Hilger, A. A1 - Markötter, Henning A1 - Wilde, F. A1 - Manke, I. A1 - Zhang, X. A1 - Sun, F. A1 - Cui, G. T1 - Synergistic Effect of CO2 in Accelerating the Galvanic Corrosion of Lithium/Sodium Anodes in Alkali Metal−Carbon Dioxide Batteries N2 - Rechargeable alkali metal−CO2 batteries, which combine high theoretical energy density and environmentally friendly CO2 fixation ability, have attracted worldwide attention. Unfortunately, their electrochemical performances are usually inferior for practical applications. Aiming to reveal the underlying causes, a combinatorial usage of advanced nondestructive and postmortem characterization tools is used to intensively study the failure mechanisms of Li/Na−CO2 batteries. It is found that a porous interphase layer is formed between the separator and the Li/Na anode during the overvoltage rising and battery performance decaying process. A series of control experiments are designed to identify the underlying mechanisms dictating the observed morphological evolution of Li/Na anodes, and it is found that the CO2 synergist facilitates Li/Na chemical corrosion, the process of which is further promoted by the unwanted galvanic corrosion and the electrochemical cycling conditions. A detailed compositional analysis reveals that the as-formed interphase layers under different conditions are similar in species, with the main differences being their inconsistent quantity. Theoretical calculation results not only suggest an inherent intermolecular affinity between the CO2 and the electrolyte solvent but also provide the most thermodynamically favored CO2 reaction pathways. Based on these results, important implications for the further development of rechargeable alkali metal−CO2 batteries are discussed. The current discoveries not only fundamentally enrich our knowledge of the failure mechanisms of rechargeable alkali metal−CO2 batteries but also provide mechanistic directions for protecting metal anodes to build high-reversible alkali metal−CO2 batteries. KW - Alkali metal batteries KW - Synchrotron X-ray computed tomography KW - Lithium/sodium−carbon dioxide batteries KW - Battery failure mechanisms KW - Alkali metal anodes PY - 2024 DO - https://doi.org/10.1021/acsnano.4c02329 SP - 1 EP - 16 AN - OPUS4-59922 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pohl, P. A1 - Serrano-Munoz, Itziar A1 - Markötter, Henning A1 - Göken, Mathias A1 - Höppel, H. W. T1 - Toughening mechanisms and enhanced damage tolerant fatigue behaviour in laminated metal composites N2 - In the present study, fatigue crack growth (FCG) in a laminated metal composite (LMC) consisting of Al-based constituents with dissimilar strength was studied. Additionally, the FCG in both monolithic constituent materials was determined and a linear elastic rule of mixture (ROM) concept was calculated as a reference for the FCG of the laminated composite. Crack networks in the laminates were analyzed post-mortem by means of light microscopy and synchrotron X-Ray tomography (SXCT). Significantly reduced FCG rates for the LMC were found at elevated stress intensity ranges compared to both the monolithic constituents as well as the ROM concept. This is the result of the formation of a complex 3D crack network in the laminated architecture caused by the appearance of the two different toughening mechanisms a) crack deflection and b) crack bifurcation at the vicinity of the interfaces. T2 - Ninth International Conference on Low Cycle Fatigue CY - Berlin, Germany DA - 21.06.2022 KW - Laminated metal composite KW - Damage tolerance KW - Fatigue crack growth KW - Toughening mechanism KW - Synchrotron X-ray computed tomography PY - 2022 DO - https://doi.org/10.48447/LCF9-2022-035 SP - 153 EP - 158 PB - DVM AN - OPUS4-55231 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishurova, Tatiana A1 - Evsevleev, Sergei A1 - Mehta, B. A1 - Nyborg, L. A1 - Virtanen, E. A1 - Markötter, Henning A1 - Hryha, E. A1 - Bruno, Giovanni T1 - Failure Mechanisms Investigation by Means of in-situ Synchrotron Computed Tomography in Aluminum MMC-based Alloy Tailored for Additive Manufacturing (AM) N2 - The availability of high-performance Al alloys in AM is limited due to difficulties in printability, requiring both the development of synergetic material and AM process to mitigate problems such as solidification cracking during laser powder bed fusion (LPBF). The goal of this work was to investigate the failure mechanism in a LPBF 7017 Aluminium alloy + 3 wt% Zr + 0.5 wt% TiC. The processing leads to different categories of Zr-rich inclusions, precipitates and defects. T2 - Alloys for Additive Manufacturing Symposium 2022 (AAMS22) CY - Munich, Germany DA - 11.09.2022 KW - Additive manufacturing KW - Laser powder bed fusion KW - Synchrotron X-ray computed tomography KW - MMC PY - 2022 AN - OPUS4-56110 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhang, X. A1 - Zhang, S. A1 - Lu, J. A1 - Tang, F. A1 - Dong, K. A1 - Yu, Z. A1 - Hilger, A. A1 - Osenberg, M. A1 - Markötter, Henning A1 - Wilde, F. A1 - Zhang, S. A1 - Zhao, J. A1 - Xu, G. A1 - Manke, I. A1 - Sun, F. A1 - Cui, G. T1 - Unveiling the Electro-Chemo-Mechanical Failure Mechanism of Sodium Metal Anodes in Sodium–Oxygen Batteries by Synchrotron X-Ray Computed Tomography N2 - Rechargeable sodium–oxygen batteries (NaOBs) are receiving extensive research interests because of their advantages such as ultrahigh energy density and cost efficiency. However, the severe failure of Na metal anodes has impeded the commercial development of NaOBs. Herein, combining in situ synchrotron X-ray computed tomography (SXCT) and other complementary characterizations, a novel electro-chemo-mechanical failure mechanism of sodium metal anode in NaOBs is elucidated. It is visually showcased that the Na metal anodes involve a three-stage decay evolution of a porous Na reactive interphase layer (NRIL): from the initially dot-shaped voids evolved into the spindle-shaped voids and the eventually-developed ruptured cracks. The initiation of this three-stage evolution begins with chemical-resting and is exacerbated by further electrochemical cycling. From corrosion science and fracture mechanics, theoretical simulations suggest that the evolution of porous NRIL is driven by the concentrated stress at crack tips. The findings illustrate the importance of preventing electro-chemo-mechanical degradation of Na anodes in practically rechargeable NaOBs. KW - Synchrotron radiation KW - X-ray imaging KW - NaO-battery PY - 2024 DO - https://doi.org/10.1002/adfm.202402253 SN - 1616-301X SP - 1 EP - 12 PB - Wiley VHC-Verlag AN - OPUS4-59820 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, R. A1 - Boenke, T. A1 - Dörfler, S. A1 - Abendroth, T. A1 - Härtel, P. A1 - Althues, H. A1 - Kaskel, S. A1 - Kardjilov, N. A1 - Markötter, Henning A1 - Sintschuk, Michael A1 - Hilger, A. A1 - Manke, I. A1 - Risse, S. T1 - Multimodal Operando Analysis of Lithium Sulfur Multilayer Pouch Cells: An In-Depth Investigation on Cell Component Design and Performance N2 - This study presents an innovative operando analysis of lithium-sulfur (Li/S) multilayer pouch cells, employing a combination of lab-source and synchrotron x-ray imaging to investigate sulfur crystallite dissolution and lithium dendrite formation. By integrating advanced X-ray imaging, impedance spectroscopy, and simultaneous monitoring of temperature and pressure, the research uncovers critical insights into the behavior of active and inactive cell components. The analysis reveals significant degradation increments, primarily driven by side product accumulation and the deterioration of lithium microstructures, which contribute to performance loss over cycling. Additionally, temperature distribution analysis shows a strong correlation between joule heating, polarization resistance, and the observed endothermic processes during crystallization. These findings provide a comprehensive understanding of the mechanistic processes within industrially relevant pouch cells, highlighting opportunities for optimizing Li/S cell designs and advancing high-energy-density battery systems for commercial applications. KW - Current collector perforation KW - Impedance spectroscopy KW - Lthium sulfur batteries KW - Multilayer pouch cells KW - X-ray imaging PY - 2025 DO - https://doi.org/10.1002/aenm.202404256 SP - 1 EP - 12 PB - Wiley VHC-Verlag AN - OPUS4-62436 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Markötter, Henning T1 - Synchrotron X-Ray Tomography Techniques at BAMline N2 - Synchrotron X-Ray computed tomography at the BAMline is constantly evolving. During monochromatic tomographic scans a preview reconstruction is offered. Newly introduced scanning schemes suppress certain types of reconstruction artifacts. Additionally, the application of a pink beam enables for faster tomographic scans even within seconds. T2 - HZB User Meeting CY - Online meeting DA - 09.12.2021 KW - BAMline KW - X-ray imaging KW - Tomography PY - 2021 AN - OPUS4-54075 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Al-Falahat, A.M. A1 - Kupsch, Andreas A1 - Hentschel, M.P. A1 - Lange, A. A1 - Kardjilov, N. A1 - Markötter, Henning A1 - Manke, I. T1 - Correction approach of detector backlighting in radiography N2 - In various kinds of radiography, deficient transmission imaging may occur due to backlighting inside the detector itself arising from light or radiation scattering. The related intensity mismatches barely disturb the high resolution contrast, but its long range nature results in reduced attenuation levels which are often disregarded. Based on X-ray observations and an empirical formalism, a procedure is developed for a first order correction of detector backlighting. A backlighting factor is modeled as a function of the relative detector coverage by the sample projection. Different cases of sample transmission are regarded at different backlight factors and detector coverage. The additional intensity of backlighting may strongly affect the values of materials’ attenuation up to a few 10%. The presented scenario provides a comfortable procedure for corrections of X-ray or neutron transmission imaging data. KW - X-ray imaging KW - Neutron imaging KW - Radiology KW - Backlighting KW - Digital detector array PY - 2019 DO - https://doi.org/10.1063/1.5097170 SN - 0034-6748 VL - 90 IS - 12 SP - 125108 PB - American Institute of Physics CY - Melville, NY, USA AN - OPUS4-50217 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Eddah, Mustapha A1 - Markötter, Henning A1 - Mieller, Björn A1 - Widjaja, Martinus Putra A1 - Beckmann, Jörg A1 - Bruno, Giovanni T1 - Multi-energy high dynamic range synchrotron X-ray computed tomography N2 - Synchrotron X-ray computed tomography (SXCT) is regularly used in materials science to correlate structural properties with macroscopic properties and to optimize manufacturing processes. The X-ray beam energy must be adapted to the sample properties, such as size and density. If both strongly and weakly absorbing materials are present, the contrast to the weakly absorbing materials is lost, resulting in image artifacts and a poor signal-tonoise ratio (SNR). One particular example is a low-temperature co-fired ceramics (LTCC), in which metal connections are embedded in a ceramic matrix and form 3-dimensional conducting structures. This article describes a method of combining SXCT scans acquired at different beam energies, significantly reducing metal artifacts, and improving image quality. We show how to solve the difficult task of merging the scans at low and high beam energy. Our proposed merging approach achieves up to 35 % improvement in SNR within ceramic regions adjacent to metallic conductors. In this way, previously inaccessible regions within the ceramic structure close to the metallic conductors are made accessible. The paper further discusses methodological requirements, limitations, and potential extensions of the presented multi-energy SXCT merging technique. KW - Synchrotron computed tomography KW - Reconstruction algorithm KW - High dynamic range KW - Data merging KW - Low-temperature cofired ceramics PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-652339 DO - https://doi.org/10.1016/j.tmater.2025.100079 SN - 2949-673X VL - 9 SP - 1 EP - 10 PB - Elsevier CY - Amsterdam AN - OPUS4-65233 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Markötter, Henning A1 - Alink, R. A1 - Haußmann, J. A1 - Dittmann, K. A1 - Arlt, Tobias A1 - Wieder, F. A1 - Tötzke, C. A1 - Klages, M. A1 - Reiter, C. A1 - Riesemeier, Heinrich A1 - Scholta, J. A1 - Gerteisen, D. A1 - Banhart, J. A1 - Manke, I. T1 - Visualization of the water distribution in perforated gas diffusion layers by means of synchrotron X-ray radiography N2 - Perforated gas diffusion layers (GDLs) of polymer electrolyte membrane fuel cells (PEMFCs) were investigated by means of in-situ synchrotron X-ray radiography during operation. We found a strong influence of perforations on the water distribution and transport in the investigated Toray TGP-H-090 GDL. The water occurs mainly around the perforations, while the holes themselves show varying water distributions. Some remain dry, while most of them fill up with liquid water after a certain period or might serve as drainage volume for effective water transport. KW - Polymer electrolyte membrane fuel cell (PEMFC) KW - Radiography KW - Synchrotron KW - X-ray imaging KW - Perforated gas diffusion layer (GDL) KW - Water transport PY - 2012 DO - https://doi.org/10.1016/j.ijhydene.2012.01.141 SN - 0360-3199 VL - 37 IS - 9 SP - 7757 EP - 7761 PB - Elsevier CY - Oxford AN - OPUS4-26434 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dayani, Shahabeddin A1 - Markötter, Henning A1 - Krug von Nidda, Jonas A1 - Schmidt, Anita A1 - Bruno, Giovanni T1 - Quantification of the Deep Discharge Induced Asymmetric Copper Deposition in Lithium‐Ion Cells by Operando Synchrotron X‐Ray Tomography N2 - AbstractLithium‐ion cells connected in series are prone to an electrical safety risk called overdischarge. This paper presents a comprehensive investigation of the overdischarge phenomenon in lithium‐ion cells using operando nondestructive imaging. The study focuses on understanding the behavior of copper dissolution and deposition during overdischarge, which can lead to irreversible capacity loss and internal short‐circuits. By utilizing synchrotron X‐ray computed tomography (SXCT), the concentration of dissolved and deposited copper per surface area is quantified as a function of depth of discharge, confirming previous findings. The results also highlight for the first time a nonuniform distribution pattern for copper deposition on the cathode. This research provides insights for safer battery cell design. KW - Lithium Ion Batteries KW - Deep Discharge KW - Computer Tomography KW - Copper Deposition KW - Litium Ion Cells PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-592717 DO - https://doi.org/10.1002/admt.202301246 SP - 1 EP - 7 PB - Wiley AN - OPUS4-59271 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Böttcher, Nils A1 - Dayani, Shahabeddin A1 - Markötter, Henning A1 - Bau, Alexander A1 - Setzchen, Max A1 - Schmidt, Anita A1 - Kowal, Julia A1 - Krug von Nidda, Jonas T1 - High Precision Nail‐Penetration Setup for the Controlled Thermal Runaway Initiation of Lithium‐Ion Cells at Very Low Temperatures N2 - A high precision nail‐penetration (NP) tool for characterizing the mechanically induced thermal‐runaway (TR) of lithium‐ion battery (LIB) cells in a defined range of temperatures down to −140 °C was developed. To understand the cell specific behavior at low temperatures aiming at the determination of safe handling conditions, different scenarios are analyzed. First, accuracy tests of the NP‐tool regarding motion and penetration depth are conducted with cylindrical cells at different temperatures. Thus, postmortem computer tomographic (CT) images are compared to the data measured with the newly integrated 3‐axis force sensor which is further combined with a high‐resolution position sensor. The herein developed setup allows evaluation of the NP‐metrics at an accuracy of ±1 pierced electrode layer without CT‐scans. Further NP examinations at 20 °C of fully charged cylindrical lithium nickel manganese cobalt oxide cells reveal a reproducible minimum damage as a reliable TR‐trigger. Moreover, NP‐tests at low temperature disclose a relation of the short circuit conductivity and TR‐reactions during subsequent rethermalization to room temperature. Finally, the implementation of a novel fixture for a controlled very fast cooling of LIB‐cells during critical damage opens the way to investigate the individual steps during a TR and, thus, to gain important information of the specific TR‐mechanism of different LIB‐cells. KW - Battery Safety KW - High-precision nail penetration KW - Lithium-ion batteries KW - Abuse testing KW - Thermal runaway PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-598127 DO - https://doi.org/10.1002/ente.202301379 SN - 2194-4288 SP - 1 EP - 13 PB - Wiley VHC-Verlag AN - OPUS4-59812 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Leonhardt, Robert A1 - Böttcher, Nils A1 - Dayani, Shahabeddin A1 - Rieck, Arielle A1 - Markötter, Henning A1 - Schmidt, Anita A1 - Kowal, Julia A1 - Tichter, Tim A1 - Krug von Nidda, Jonas T1 - Exploring the electrochemical and physical stability of lithium-ion cells exposed to liquid nitrogen N2 - The transport and storage of lithium-ion (Li-ion) batteries — damaged or in an undefined state — is a major safety concern for regulatory institutions, transportation companies, and manufacturers. Since (electro)chemical reactivity is exponentially temperature-dependent, cooling such batteries is an obvious measure for increasing their safety. The present study explores the effect of cryogenic freezing on the electrochemical and physical stability of Li-ion cells. For this purpose, three different types of cells were repeatedly exposed to liquid nitrogen (LN2). Before and after each cooling cycle, electrical and electrochemical measurements were conducted to assess the impact of the individual freezing steps. While the electrochemical behavior of the cells did not change significantly upon exposure to LN2 , it became apparent that a non-negligible number of cells suffered from physical changes (swelling) and functional failures. The latter defect was found to be caused by the current interrupt device of the cylindrical cells. This safety mechanism is triggered by the overpressure of expanding nitrogen which enters the cells at cryogenic temperatures. This study underlines that the widely accepted reversibility of LN2 -cooling on a material scale does not allow for a direct extrapolation toward the physical integrity of full cells. Since nitrogen enters the cell at cryogenic temperatures and expands upon rethermalization, it can cause an internal overpressure. This can, in turn, lead to mechanical damage to the cell. Consequently, a more appropriate temperature condition — less extreme than direct LN2 exposure — needs to be found KW - Lithium-ion battery KW - LN2 cooling KW - Battery characterization PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599248 DO - https://doi.org/10.1016/j.est.2024.111650 VL - 89 SP - 1 EP - 7 PB - Elsevier B.V. AN - OPUS4-59924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Böttcher, Nils A1 - Dayani, Shahabeddin A1 - Markötter, Henning A1 - Schmidt, Anita A1 - Kowal, J. A1 - Lu, Y. A1 - Krug von Nidda, Jonas A1 - Bruno, Giovanni T1 - Visualization of stepwise electrode decomposition in a nail penetrated commercial lithium-ion cell using low-temperature synchrotron X-ray computed tomography N2 - The transition towards zero carbon emissions in power generation hinges on the integration of efficient electrical energy storage systems, with lithium-ion batteries (LIBs) positioned as a pivotal technology. While generally safe, deviations in their operational guidelines due to manufacturing defects or misuse can lead to critical safety concerns, notably thermal runaway (TR) events. Internal short circuits (ISCs) are primary initiators of TR within LIBs. For abuse testing, ISCs are often triggered by nail penetration. This study explores the morphological changes and mechanisms underlying ISC-induced TR in LIBs using operando synchrotron X-ray computed tomography (SXCT) at subzero temperatures. A novel cryogenic setup was developed to control a stepwise temperature increase in the damaged sample while monitoring electrochemical characteristics and simultaneously enabling acquisition of high-resolution SXCT images. The findings reveal that conducting nail penetration at minus 80°C prevents immediate TR, enabling detailed analysis of subsequent structural and electrochemical behavior during controlled thawing. Thus, the initiation of TR processes at localized ISC sites has been observed, evidenced by voltage fluctuations and morphological changes, such as cathode material cracking and decomposition. These results underscore the importance of temperature control in mitigating TR risks and provide critical insights into the internal dynamics of LIBs under abusive conditions. The developed cryogenic SXCT methodology offers a powerful tool for non-destructive, high-resolution investigation of battery failure mechanisms, contributing to the enhancement of LIB safety. KW - Tomography KW - X-ray imaging KW - Lithium-ion battery PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611327 DO - https://doi.org/10.1016/j.jpowsour.2024.235472 VL - 623 SP - 1 EP - 10 PB - Elsevier CY - New York, NY AN - OPUS4-61132 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Markötter, Henning A1 - Manke, I. A1 - Haußmann, J. A1 - Arlt, Tobias A1 - Klages, M. A1 - Krüger, P. A1 - Hartnig, C. A1 - Scholta, J. A1 - Müller, Bernd R. A1 - Riesemeier, Heinrich A1 - Banhart, J. T1 - Combined synchrotron X-ray radiography and tomography study of water transport in gas diffusion layers N2 - Synchrotron X-ray radiography and tomography investigations of a custom-made polymer electrolyte membrane fuel cell optimised for visualisation purposes are presented. The 3D water distribution and transport pathways in the porous carbon fibre gas diffusion layers (GDLs) were investigated. The authors found that water is not only moving from the GDL into the channel, but can also take the opposite way, that is, from the channel into free pore space of the GDL. Such movement of water into the opposite direction has been subject of speculations but has so far not yet been reported and might bring new insights into the general water transport behaviour, which might give new aspects to the general description of water transport processes and influence modelling assumptions to describe the process taking place in the GDL. KW - Synchrotron radiography KW - Synchrotron tomography KW - Gas diffusion layers KW - Water transport PY - 2012 DO - https://doi.org/10.1049/mnl.2012.0410 SN - 1750-0443 VL - 7 IS - 7 SP - 689 EP - 692 PB - IET CY - London AN - OPUS4-26282 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eddah, Mustapha A1 - Markötter, Henning A1 - Mieller, Björn A1 - Widjaja, Martinus Putra A1 - Beckmann, Jörg A1 - Bruno, Giovanni T1 - Multi-Energy High Dynamic Range (HDR) Synchrotron X-ray Computed Tomography applied to LTCC samples N2 - Synchrotron X-ray computed tomography (SXCT) is regularly used in materials science to correlate structural properties with macroscopic properties and to optimize manufacturing processes. The X-ray beam energy must be adapted to the sample properties, such as size and density. If both strongly and weakly absorbing materials are present, the contrast to the weakly absorbing materials is lost, resulting in image artifacts and a poor signal-to-noise ratio (SNR). One example is a low-temperature co-fired ceramics (LTCC), in which metal connections are embedded in a ceramic matrix and form 3-dimensional conducting structures. This article describes a method of combining SXCT scans acquired at different beam energies, significantly reducing metal artifacts, and improving image quality. We show how to solve the difficult task of merging the scans at low and high beam energy. Our proposed merging approach achieves up to 35% improvement in SNR within ceramic regions adjacent to metallic conductors. In this way, previously inaccessible regions within the ceramic structure close to the metallic conductors are made accessible. The paper further discusses methodological requirements, limitations, and potential extensions of the presented multienergy SXCT merging technique. T2 - iCT 2026 CY - Linz, Austria DA - 10.02.2026 KW - Synchrotron x-ray CT KW - Multi-energy CT KW - Low-Temperature cofired ceramics PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-655848 SP - 1 EP - 7 CY - e-Journal of Nondestructive Testing AN - OPUS4-65584 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Markötter, Henning T1 - In situ tomographic imaging with hard x rays at Bamline (BESSY II) N2 - The BAMline at the synchrotron X-ray source BESSY II (Berlin, Germany) is supporting researchers especially in materials science [1]. As a non-destructive characterization method, synchrotron X-ray imaging, especially tomography (SXCT) with hard X-Rays, plays an important role in structural 3D characterization. The imaging capabilities allow for in-situ and operando experiments. In this presentation the equipment, data handling pipeline as well as various examples from material science are presented. In series-connected lithium-ion cells are susceptible to an electrical safety hazard called over-discharge. Here the behavior of copper dissolution and deposition during over-discharge is presented, which leads to irreversible loss of capacity and internal short circuits. The concentration of dissolved and deposited copper is quantified. Also, a non-uniform distribution pattern of copper deposition on the cathode is shown. The second example deals with an Al alloy 7017 customized for a 3d-printing process by means of laser-based powder bed fusion (PBF-LB) technique. These advanced alloys have a significantly higher modulus of elasticity than conventional Al alloys, making them attractive for applications requiring high stiffness. SXCT during In-situ tensile tests confirmed that fracture initiation strongly depends on defects created during printing. However, the cracks are deflected from decohesion around inclusions/precipitates embedded in the Al matrix, increasing ductility. Low temperature cofired ceramic (LTCC) multilayer housings offer 3D-circuits for a wide range of applications in telecommunications, microsystems and sensor technology. Such housings are produced by combining structured and metallized ceramic layers using tape-casting and multilayer technology. The characterization of the integrity, deformation, defects, and positioning of the internal metal features was carried out using in-situ SXCT at up to 950°C. A high-precision nail penetration tool was developed to characterize the mechanically induced thermal runaway (TR) of lithium-ion battery (LIB) cells in a dynamic temperature range down to -190 °C. To investigate safety-specific low-temperature transport conditions, the damaged cells were tomographically imaged during thawing. T2 - ICTMS - International Conference on Materials and Structures 2024 CY - Cape Town, South Africa DA - 01.07.2024 KW - Synchrotron radiation KW - X-ray tomography KW - Li-ion battery PY - 2024 AN - OPUS4-60658 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sun, F. A1 - Wang, C. A1 - Osenberg, M. A1 - Dong, K. A1 - Zhang, S. A1 - Yang, C. A1 - Wang, Y. A1 - Hilger, A. A1 - Zhang, J. A1 - Dong, S. A1 - Markötter, Henning A1 - Manke, I. A1 - Cui, G. T1 - Clarifying the Electro-Chemo-Mechanical Coupling in Li10SnP2S12 based All-Solid-State Batteries N2 - A fundamental clarification of the electro-chemo-mechanical coupling at the solid–solid electrode|electrolyte interface in all-solid-state batteries (ASSBs) is of crucial significance but has proven challenging. Herein, (synchrotron) X-ray tomography, electrochemical impedance spectroscopy (EIS), time-of-flight secondary-ion mass spectrometry (TOF-SIMS), and finite element analysis (FEA) modeling are jointly used to decouple the electro-chemo-mechanical coupling in Li10SnP2S12-based ASSBs. Non-destructive (synchrotron) X-ray tomography results visually disclose unexpected mechanical deformation of the solid electrolyte and electrode as well as an unanticipated evolving behavior of the (electro)chemically generated interphase. The EIS and TOFSIMS probing results provide additional information that links the interphase/electrode properties to the overall battery performance. The modeling results complete the picture by providing the detailed distribution of the mechanical stress/strain and the potential/ionic flux within the electrolyte. Collectively, these results suggest that 1) the interfacial volume changes induced by the (electro)chemical reactions can trigger the mechanical deformation of the solid electrode and electrolyte; 2) the overall electrochemical process can accelerate the interfacial chemical reactions; 3) the reconfigured interfaces in turn influence the electric potential distribution as well as charge transportation within the SE. These fundamental discoveries that remain unreported until now significantly improve the understanding of the complicated electro-chemo-mechanical couplings in ASSBs. KW - All-solid-state batteries KW - Lithium metal batteries KW - Solid electrolytes KW - Sulfide solid electrolytes KW - Synchrotron X-ray tomography PY - 2022 DO - https://doi.org/10.1002/aenm.202103714 SN - 1614-6832 SP - 2103714 PB - Wiley VHC-Verlag AN - OPUS4-54431 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Göbel, M. A1 - Kirsch, S. A1 - Schwarze, L: A1 - Schmidt, L. A1 - Scholz, H. A1 - Haußmann, J. A1 - Klages, M. A1 - Scholta, J. A1 - Markötter, Henning A1 - Alrwashdeh, S. A1 - Manke, I. A1 - Müller, Bernd R. T1 - Transient limiting current measurements for characterization of gas diffusion layers N2 - The water management in proton exchange membrane fuel cells (PEMFC) is strongly influenced by the design of the gas diffusion layers (GDL). Limiting current measurements in small-scale cells operating at high stoichiometries are useful to determine the oxygen transport resistance. The oxygen transport resistance increases, once water condenses inside the GDL. In this study a new electrochemical method for voltage loss estimation of GDL induced oxygen transport losses are presented. This new method, referred to as “transient limiting current” (TLC), is compared with the literature method. TLC allows a direct estimation of oxygen transport resistance at an arbitrarily conditioned state. This study also presents a case study of liquid water visualization of a PEM fuel cell with varying GDLs types. With the help of quasi in-situ synchrotron X-ray computed tomography and time resolved radiography measurements we investigate appearance and distribution of liquid water inside the GDLs under limiting current conditions. KW - In-situ characterization of GDLs KW - In-situ synchrotron X-ray computed tomography KW - In-situ synchrotron X-ray radiography KW - BAMline PY - 2018 DO - https://doi.org/10.1016/j.jpowsour.2018.09.003 SN - 0378-7753 SN - 1873-2755 VL - 402 SP - 237 EP - 245 PB - Elsevier B.V. AN - OPUS4-46552 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mehta, B. A1 - Mishurova, Tatiana A1 - Evsevleev, Sergei A1 - Markötter, Henning A1 - Bruno, Giovanni A1 - Hryha, E. A1 - Nyborg, L. A1 - Virtanen, E. T1 - Microstructure, mechanical properties and fracture mechanisms in a 7017 aluminium alloy tailored for powder bed fusion – laser beam N2 - This study addressed a 7017 Al-alloy tailored for powder bed fusion – laser beam (PBF-LB) process. The alloy was prepared by mixing 3 wt% Zr and 0.5 wt% TiC powder to standard pre-alloyed 7017 grade aluminium powder. This made printing of the alloys possible avoiding solidification cracking in the bulk and achieving high relative density (99.8 %). Such advanced alloys have significantly higher Young’s modulus (>80 GPa) than conventional Al-alloys (70–75 GPa), thus making them attractive for applications requiring high stiffness. The resulting microstructure in as-printed condition was rich in particles originating from admixed powders and primary precipitates/inclusions originating from the PBF-LB process. After performing a T6-like heat treatment designed for the PBF-LB process, the microstructure changed: Zr-nanoparticles and Fe- or Mg/Zn- containing precipitates formed thus providing 75 % increase in yield strength (from 254 MPa to 444 MPa) at the cost of decreasing ductility (∼20 % to ∼9 %). In-situ tensile testing combined with SXCT, and ex-situ tensile testing combined with fracture analysis confirmed that the fracture initiation in both conditions is highly dependent on defects originated during printing. However, cracks are deflected from decohesion around Zr-containing inclusions/precipitates embedded in the Al-matrix. This deflection is seen to improve the ductility of the material. KW - Additive manufacturing KW - Powder bed fusion Laser beam KW - X-ray computed tomography KW - Strengthening mechanisms KW - Crack propagation KW - Zirconium PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-568243 DO - https://doi.org/10.1016/j.matdes.2023.111602 SN - 0264-1275 VL - 226 SP - 1 EP - 14 PB - Elsevier Science CY - Amsterdam [u.a.] AN - OPUS4-56824 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ziesche, R.F. A1 - Hack, J. A1 - Rasha, L. A1 - Maier, M. A1 - Tan, C. A1 - Heenan, T.M.M. A1 - Markötter, Henning A1 - Kardjilov, N. A1 - Manke, I. A1 - Kockelmann, W. A1 - Brett, D.J.L. A1 - Shearing, P.R. T1 - High-speed 4D neutron computed tomography for quantifying water dynamics in polymer electrolyte fuel cells N2 - In recent years, low-temperature polymer electrolyte fuel cells have become an increasingly important pillar in a zero-carbon strategy for curbing climate change, with their potential to power multiscale stationary and mobile applications. The performance improvement is a particular focus of research and engineering roadmaps, with water management being one of the major areas of interest for development. Appropriate characterisation tools for mapping the evolution, motion and removal of water are of high importance to tackle shortcomings. This article demonstrates the development of a 4D high-speed neutron imaging technique, which enables a quantitative analysis of the local water evolution. 4D visualisation allows the time-resolved studies of droplet formation in the flow fields and water quantification in various cell parts. Performance parameters for water management are identified that offer a method of cell classification, which will, in turn, support computer modelling and the engineering of next-generation flow field designs. KW - Neutron imaging KW - Tomography KW - Polymer electrolyte membrane fuel cell PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-545978 DO - https://doi.org/10.1038/s41467-022-29313-5 VL - 13 IS - 1 SP - 1616 PB - Nature Publishing Group UK CY - London AN - OPUS4-54597 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -