TY - CONF A1 - Dmitriev, A.I. A1 - Kloß, Heinz A1 - Österle, Werner T1 - Final outcome of a fundamental research project on tribofilms formed during automotive braking, Part 2: Numerical simulation T2 - EuroBrake 2014 (Proceedings) N2 - In part 1 it was shown that tribofilms usually are 100 nm thick and exhibit a multiphase nanocrystalline structure. The objective of our modelling efforts was to obtain a better understanding of the sliding behaviour and associated friction properties and to study the impact of internal and external parameters on these properties. The method of movable cellular automata (MCA) was used. The third bodies were considered as aggregates of linked nanoparticles which may decompose and form a layer of granulär material, the so-called mechanically mixed layer (MML), if certain fracture criteria are fulfilled. The basic model structure which consists of Fe3Ü4 nanoparticles with 13 % graphite inclusions was used. In order to assess the robustness of the model the following parameter studies were performed. The pressure ränge at an asperity contact was varied between 15 and 50 MPa. The mechanical properties of the oxide were varied between brittle and ductile behaviour corresponding to room temperature and high temperature behaviour. The mechanical properties of the soft ingredient were varied + 50 % of the properties of graphite. The influence T2 - EuroBrake 2014 CY - Lille, France DA - 13.05.2014 KW - Tribofilm KW - Third body KW - Dry friction KW - Modelling KW - Movable cellular automata PY - 2014 SN - 978-0-9572076-4-6 SP - 1 EP - 9 PB - FISITA CY - London AN - OPUS4-35040 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kloß, Heinz A1 - Österle, Werner A1 - Dmitriev, A.I. ED - Bartz, Wilfried J. T1 - Modelling mechanical friction and wear behaviour using numerical results of the movable cellular automata (MCA) method T2 - 19th International colloquium tribology - Industrial and automotive lubrication N2 - In the mechanical friction and wear process, normal and tangential (shear) forces cause elastic and plastic deformations, generate cracks and form loose wear particles through fracture processes. Depending on the working conditions, the material properties and the real contact Situation (topography), a third body is formed as a mechanical ly mixed layer, which determines different running-in and steady-state behaviours. Two dimensional (2D) MCA Simulation results will be described via empirical equations, which are related to the incubation time (period without wear) and the following running-in wear rate (kinetic concept of strength, fatigue wear model). In order to understand the running-in and steady-state wear, kinetic model equations for mass balance of the third body are useful and are therefore to be included in the investigation. For a more complex material behaviour, numerical Simulation results are also presented for friction at the pad-disk interface of automotive brakes. T2 - 19th International colloquium Tribology - Industrial and automotive lubrication CY - Stuttgart/Ostfildern, Germany DA - 21.01.2014 PY - 2014 SN - 978-3-943563-10-8 SP - Paper 8.10, 1 EP - 7 CY - Stuttgart/Ostfildern AN - OPUS4-30437 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Österle, Werner A1 - Dmitriev, A.I. A1 - Kloß, Heinz T1 - Does ultra-mild wear play any role for dry friction applications, such as automotive braking? JF - Faraday discussions N2 - Nanostructured third body films and/or storage of wear debris at the surfaces of the first bodies are deemed as prerequisites of sliding under ultra-mild wear conditions. Since such features have been observed experimentally on brake pads and discs, attempts were undertaken to study their sliding behaviour by modelling on the nanoscopic scale with an approach based on Movable Cellular Automata (MCA). The model rendered the possibility to study the influence of different nanostructures systematically and to assess the impact of different brake pad ingredients on the sliding behaviour, velocity accommodation and friction force stabilization at a sliding contact. Besides providing a review on previously published modelling results, some additional new graphs enabling better visualization of dynamic processes are presented. Although ultra-mild wear conditions were considered to be essential for achieving the desired tribological properties, transitions to mesoscopic and macroscopic wear mechanisms were studied as well. The final conclusion is that ultra-mild wear and corresponding smooth sliding behaviour play an important role during automotive braking, even though temporarily and locally events of severe wear may cause friction instabilities, surface damage and release of coarse wear particles. KW - Dry friction KW - Ultra-mild wear KW - Third body KW - MCA-model KW - Simulation PY - 2012 DO - https://doi.org/10.1039/c2fd00117a SN - 1359-6640 SN - 1364-5498 VL - 156 IS - 0 SP - 159 EP - 171 PB - Soc. CY - Cambridge [u.a.] AN - OPUS4-26822 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Österle, Werner A1 - Dmitriev, A.I. A1 - Kloß, Heinz T1 - Possible impacts of third body nanostructure on friction performance during dry sliding determined by computer simulation based on the method of movable cellular automata JF - Tribology International N2 - The tribological properties of nanostructured surface films formed during dry sliding, for example during automotive braking, were determined by modelling using the method of movable cellular automata. Starting from a basic model structure, consisting of magnetite with 13% graphite inclusions, the impact of additional soft and hard particles of different size and volume fraction was studied systematically. It was revealed that agglomerates of soft particles decomposed and finally mixed with the oxide in the same way as single nanoparticles. On the other hand, agglomerates of hard particles mixed with the other components without decomposing. Whereas increasing the amount of soft components in the third body lowered the coefficient of friction, the opposite occurred with the hard particles. The boundary conditions for obtaining smooth sliding conditions with minor fluctuations between friction forces at successive time steps could be defined. In addition to features of the nanostructure, the applied normal pressure impacted modelling results. Within the parameter range of smooth sliding behaviour, increasing pressure induced thicker granular interface layers, which lead to a slight decrease of the coefficient of friction. Changing the amount of soft or hard particles did not change this pressure dependency but only the friction level. KW - MCA-modelling KW - Third body KW - Nanoparticles KW - Dry friction PY - 2012 DO - https://doi.org/10.1016/j.triboint.2011.11.018 SN - 0301-679X VL - 48 SP - 128 EP - 136 PB - Butterworth-Heinemann CY - Oxford AN - OPUS4-25469 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dmitriev, A.I. A1 - Österle, Werner A1 - Kloß, Heinz T1 - Nano-scale modeling of pad-disc interface. The influence of copper as a pad ingredient. T2 - JEF 2010 - 6th European conference on braking (Proceedings) T2 - JEF 2010 - 6th European conference on braking CY - Lille, France DA - 2010-11-24 KW - Friction layer KW - Copper particles KW - MCA-modelling PY - 2010 SP - 1 EP - 6(?) AN - OPUS4-22656 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Österle, Werner A1 - Kloß, Heinz A1 - Dmitriev, A.I. ED - Bartz, Wilfried J. ED - Friedrich Franek, T1 - Friction control during automotive braking - experimental observations and simulation at the nanometer scale T2 - 3rd Vienna International Conference - Nano-Technology T2 - 3rd Vienna International Conference - Nano-Technology CY - Vienna, Austria DA - 2009-03-18 KW - Bremse KW - Dritter Körper KW - Verschleiß KW - Reibung KW - Nanocharakterisierung KW - Modellierung PY - 2009 SN - 978-3-901657-32-0 SP - 335 EP - 341 AN - OPUS4-19222 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Österle, Werner A1 - Kloß, Heinz A1 - Dmitriev, A.I. T1 - Friction control during automotive braking: experimental observations and simulation at nanometer scale JF - Tribology : materials, surfaces & interfaces KW - Friction control KW - Friction film KW - Automotive braking KW - MCA model KW - Nanostructure PY - 2009 DO - https://doi.org/10.1179/175158309X12586382418454 SN - 1751-5831 VL - 3 IS - 4 SP - 196 EP - 202 PB - Maney CY - London AN - OPUS4-20829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dmitriev, A.I. A1 - Österle, Werner A1 - Kloß, Heinz T1 - Numerical simulation of typical contact situations of brake friction materials JF - Tribology International N2 - In the paper, a model typical for contact situations of automotive brakes is established based on the method of movable cellular automata. The processes taking place at local contacts in an automotive brake system are analysed. Based on microscopic and micro-analytical observations, the following contact situations were simulated: (i) a couple of ferritic steel against pearlitic steel, both covered by an oxide layer mixed with graphite nanoparticles and (ii) the same situation but without oxide layers. The results of calculated mean coefficients of friction of the oxide-on-oxide contact correspond well to expected values for a real braking system, whereas steel-on-steel contact are twice as high. This allows one to make some conclusions; for example, oxide formation will take place more quickly than friction layer elimination, and finally this is responsible for the stabilisation of the coefficient of friction. KW - Friction KW - Primary contact KW - Automotive brake system KW - Numerical simulation KW - Method of movable cellular automata PY - 2008 DO - https://doi.org/10.1016/j.triboint.2007.04.001 SN - 0301-679X VL - 41 IS - 1 SP - 1 EP - 8 PB - Butterworth-Heinemann CY - Oxford AN - OPUS4-15841 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Österle, Werner A1 - Kloß, Heinz A1 - Dmitriev, A.I. T1 - Modeling of Friction Evolution and Assessment of Impacts on Vibration Excitation at the Pad-Disc Interface T2 - 26th Annual Brake Colloquium & Exhibition, October 12-15, 2008, San Antonio, Texas, USA T2 - 26th Annual Brake Colloquium & Exhibition CY - San Antonio, Texas, USA DA - 2008-10-12 KW - Friction materials KW - MCA-modeling KW - Friction films KW - Noise propensity KW - Friction-induced vibrations PY - 2008 SN - 978-0-7680-2097-7 IS - 2008-01-2582 SP - 303 EP - 311 AN - OPUS4-18695 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dmitriev, A.I. A1 - Österle, Werner A1 - Kloß, Heinz T1 - Numerical Simulation of Mechanically Mixed Layer Formation at Local Contacts of an Automotive Brake System JF - Tribology transactions KW - Nanotribology KW - Automotive Brakes KW - Dynamic Modelling KW - Friction Mechanisms KW - Mechanically Mixed Layer KW - Movable Cellular Automata PY - 2008 DO - https://doi.org/10.1080/10.40.2000802380314 SN - 1040-2004 SN - 1547-397X VL - 51 SP - 1 EP - 7 PB - Taylor & Francis CY - Philadelphia, Pa. AN - OPUS4-18696 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -