TY - JOUR A1 - Schlick-Hasper, Eva A1 - Eiben, Mario A1 - Drousch, Björn A1 - Heinrich, Annika A1 - Goedecke, Thomas A1 - Kraume, M. T1 - Influence of the length of the internal sleeve valve on the release of powdery substances from the closures of valved bags for dangerous goods N2 - In practice, checks on dangerous goods transports often detect leaks of powdered dangerous goods from valved bags. In this work, the influence factors of a sudden release of powdery substances from the valves of valved bags were investigated. Drop tests were performed on paper bags of UN design type 5M2 with internal sleeve valve using 2 different powdery substances (Esplas H130 and zinc oxide “Rotsiegel”). The internal sleeve valves of all test samples were not sift‐proof with respect to both filling substances. For almost all test samples, the Esplas H130 powder already leaked out of pasted joints during manual filling. This is a contradiction to the requirement in UN 6.1.4.18.1, according to which closures and joints of paper bags 5M2 should be sift‐proof. In the drop tests, longer valve lengths had a greater sealing effect for both filling substances (for filling degrees of at least 95% and for test samples which had already been mechanically loaded). As an extreme example, at the drop height of 1.20 m and a filling degree of 100%, the released amount of zinc oxide powder from a 10‐cm‐long valve was about 16 times higher than from a valve length of 12.5 cm. The valve length is therefore a safety‐relevant parameter and should be specified by the manufacturer. To ensure that only filling goods with similar physical properties in comparison with the test substance are used for valved bags, the user must be informed of the particle size of the test substance. KW - Sacks KW - Bags KW - Dangerous goods packagings KW - Drop test KW - Sift-proofness PY - 2018 DO - https://doi.org/10.1002/pts.2377 SN - 0894-3214 SN - 1099-1522 VL - 31 IS - 8 SP - 532 EP - 544 PB - John Wiley & Sons, Ltd. AN - OPUS4-45835 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ried, Peter A1 - Gaber, Martin A1 - Beyer, Katrin A1 - Müller, Ralf A1 - Kipphardt, Heinrich A1 - Kannengießer, Thomas T1 - Thermo Analytic Investigation of Hydrogen Effusion Behavior - Sensor Evaluation and Calibration N2 - The well established carrier gas analysis (CGA) method was used to test different hydrogen detectors comprising a thermal conductivity detector (TCD) and a metal oxide semiconducting (MOx) sensor. The MOx sensor provides high hydrogen sensitivity and selectivity, whereas the TCD exhibits a much shorter response time and a linear hydrogen concentration dependency. Therefore, the TCD was used for quantitative hydrogen concentration measurements above 50?µmol/mol. The respective calibration was made using N2/H2 gas mixtures. Furthermore, the hydrogen content and degassing behaviour of titanium hydride (TiH2-x) was studied. This material turned out to be a potential candidate for a solid sample calibration. Vacuum hot extraction (VHE) coupled with a mass spectrometer (MS) was then calibrated with TiH2-x as transfer standard. The calibration was applied for the evaluation of the hydrogen content of austenitic steel samples (1.4301) and the comparison of CGA-TCD and VHE-MS. KW - Hydrogen KW - Steel KW - Vacuum hot extraction KW - Carrier gas analysis KW - Titanium hydride KW - Gas calibration PY - 2011 DO - https://doi.org/10.1002/srin.201000237 SN - 1611-3683 SN - 0177-4832 VL - 82 IS - 1 SP - 14 EP - 19 PB - Verl. Stahleisen CY - Düsseldorf AN - OPUS4-23202 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Abad Andrade, Carlos Enrique A1 - Florek, S. A1 - Becker-Ross, H. A1 - Huang, M.-D. A1 - de Oliveira Guilherme Buzanich, Ana A1 - Radtke, Martin A1 - Lippitz, Andreas A1 - Hodoroaba, Vasile-Dan A1 - Schmid, Thomas A1 - Heinrich, Hans-Joachim A1 - Recknagel, Sebastian A1 - Jakubowski, Norbert A1 - Panne, Ulrich T1 - Zirconium permanent modifiers for graphite furnaces used in absorption spectrometry: understanding their structure and mechanism of action N2 - The mechanism of action of zirconium permanent modifiers on graphite surfaces was investigated in order to understand its influence on the analytical signal in atomic and molecular absorption spectrometry (AAS/MAS). For this, the molecule formation of CaF was studied, which is used for the indirect analytical determination of fluorine in high-resolution continuum source graphite furnace molecular absorption spectrometry (HR-CS-GFMAS). The kinetics of this reaction was established by monitoring its molecular spectrum at different atomisation temperatures. An Arrhenius plot showed a pseudo-first order reaction with respect to fluorine (n = 1). An intermediate state was isolated, and its structure was elucidated by spectroscopic methods: scanning electron microscopy with energy dispersive X-ray spectroscopy (SEMEDX), X-ray photoelectron spectroscopy (XPS), X-ray absorption spectroscopy (XANES and EXAFS), and Raman microspectroscopy. We propose here a mechanism, where ZrO2 acts as a heterogeneous catalyst: after a pyrolytic step, an intermediate state of ZrO(OCaF) is activated, and at higher temperatures, CaF(g) is released from the zirconium-coated graphite surface. No evidence of the formation of zirconium carbide was found. Consequently, as the CaF formation is catalysed by a heterogeneous catalyst, surface modifications with ZrO2 nanoparticles and ZrO xerogels were investigated in order to increase the surface area. Their influence was evaluated in the molecule formation of CaF, CaCl, CaBr, and CaI. Graphite furnace modification with zirconium oxide nanoparticles proves to be the best choice for fluorine analysis with a signal enhancement of more than eleven times with respect a non-coated graphite furnace. However, the influence of zirconium modifications in the analytical signals of Cl, and I is lower than the F signals or even negative in case of the Br. Understanding zirconium modifiers as heterogeneous catalysts offers a new perspective to AAS and MAS, and reveals the potential of surface analytical methods for development of improved permanent modifiers and graphite furnace coatings. KW - Zirconium KW - HR-CS-MAS KW - Graphite furnace KW - Nanoparticles KW - Xerogel KW - Calcium monofluoride KW - Absorption spectrometry PY - 2018 UR - https://pubs.rsc.org/en/content/articlelanding/2018/ja/c8ja00190a DO - https://doi.org/10.1039/C8JA00190A SN - 0267-9477 VL - 33 IS - 12 SP - 2034 EP - 2042 PB - Royal Society of Chemistry AN - OPUS4-46775 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Anja A1 - Heinrich, Thomas A1 - Tougaard, S. A1 - Werner, W. S. M. A1 - Hronek, M. A1 - Kunz, Valentin A1 - Radnik, Jörg A1 - Stockmann, Jörg M. A1 - Hodoroaba, Vasile-Dan A1 - Benemann, Sigrid A1 - Nirmalananthan-Budau, Nithiya A1 - Geißler, Daniel A1 - Sparnacci, K. A1 - Unger, Wolfgang T1 - Determining the thickness and completeness of the shell of polymer core-shell nanoparticles by X-ray photoelectron spectroscopy, secondary ion mass spectrometry, and transmission scanning electron microscopy N2 - Core–shell nanoparticles (CSNPs) have become indispensable in various industrial applications. However, their real internal structure usually deviates from an ideal core–shell structure. To control how the particles perform with regard to their specific applications, characterization techniques are required that can distinguish an ideal from a nonideal morphology. In this work, we investigated poly(tetrafluoroethylene)–poly(methyl methacrylate) (PTFE–PMMA) and poly(tetrafluoroethylene)–polystyrene (PTFE–PS) polymer CSNPs with a constant core diameter (45 nm) but varying shell thicknesses (4–50 nm). As confirmed by transmission scanning electron microscopy (T-SEM), the shell completely covers the core for the PTFE–PMMA nanoparticles, while the encapsulation of the core by the shell material is incomplete for the PTFE–PS nanoparticles. X-ray photoelectron spectroscopy (XPS) was applied to determine the shell thickness of the nanoparticles. The software SESSA v2.0 was used to analyze the intensities of the elastic peaks, and the QUASES software package was employed to evaluate the shape of the inelastic background in the XPS survey spectra. For the first time, nanoparticle shell thicknesses are presented, which are exclusively based on the analysis of the XPS inelastic background. Furthermore, principal component analysis (PCA)-assisted time-of-flight secondary-ion mass spectrometry (ToF-SIMS) of the PTFE–PS nanoparticle sample set revealed a systematic variation among the samples and, thus, confirmed the incomplete encapsulation of the core by the shell material. As opposed to that, no variation is observed in the PCA score plots of the PTFE–PMMA nanoparticle sample set. Consequently, the complete coverage of the core by the shell material is proved by ToF-SIMS with a certainty that cannot be achieved by XPS and T-SEM. KW - XPS KW - T-SEM KW - ToF-SIMS KW - Core-shell nanoparticles PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-499165 DO - https://doi.org/10.1021/acs.jpcc.9b09258 VL - 123 IS - 49 SP - 29765 EP - 29775 PB - American Chemical Society CY - Washington, DC AN - OPUS4-49916 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schaepe, Kaija A1 - Jungnickel, H. A1 - Heinrich, Thomas A1 - Tentschert, J. A1 - Luch, A. A1 - Unger, Wolfgang ED - Hodoroaba, Vasile-Dan ED - Unger, Wolfgang ED - Shard, A. G. T1 - Secondary ion mass spectrometry N2 - This chapter provides an introduction in secondary ion mass spectrometry as one of the leading surface chemical analysis and imaging techniques with molecular specificity in the field of material sciences. The physical basics of the technique are explained along with a description of the typical instrumental setups and their modes of operation. The application paragraph specifically focuses on nanoparticle analysis by SIMS in terms of surface spectrometry, imaging, analysis in organic and complex media, and depth profiling. A review of the existing literature is provided, and selected studies are showcased. Limitations and pitfalls as well as current technical developments of SIMS application in nanoparticle surface chemical analysis are equally discussed. KW - Time-of-flight secondary ion mass spectrometry KW - Surface chemical analysis KW - Imaging KW - Nanomaterials KW - Nanoparticles KW - Core-shell PY - 2020 SN - 978-0-12-814182-3 DO - https://doi.org/10.1016/B978-0-12-814182-3.00025-0 SP - 481 EP - 509 PB - Elsevier CY - Amsterdam AN - OPUS4-50187 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heinrich, Thomas A1 - Darlatt, Erik A1 - Lippitz, Andreas A1 - Müller, S. A1 - Schalley, C. A1 - Unger, Wolfgang T1 - Systematic XP and NEXAFS spectroscopy studies of (ter-)pyridineterminated self-assembled monolayers and their addressability for functional molecules N2 - The chemical composition of surfaces functionalized with self-assembled monolayers (SAMs) is an important parameter that determines their performance in a broad range of applications, from immobilizing molecular machines to initiation and growth control of MOFs (Metal-Organic Frameworks). In this article, a critical Survey of XPS (X-ray photoelectron spectroscopy) and NEXAFS (near edge X-ray absorption fine structure) spectroscopy data for pyridine-functionalized monolayers on gold surfaces is presented to compile correlations that have been indiscernible before. Monolayers with aromatic backbones are compared to monolayers with aliphatic backbones. Monolayers with pyridine end-groups are compared to mixed monolayers formed terpyridine-functionalized by molecules end-groups and non-functionalized molecules. Thiol-oxidation during ageing of the SAMs in air is addressed. And finally, the addressability of the SAMs for the deposition of metal-ions and organic molecules is investigated and compared. This work consequently delivers a comprehensive set of spectroscopic data of (ter-)pyridine-terminated SAMs and their performance as template for the preparation of functional multilayers of macrocycles exhibiting a preferential orientation. KW - (ter-)pyridineterminated self-assembled monolayer KW - X-ray Photoelectron Spectroscopy (XPS) KW - NEXAFS PY - 2019 DO - https://doi.org/10.1016/j.elspec.2019.03.011 VL - 233 SP - 28 EP - 37 PB - Elsevier B.V. AN - OPUS4-48018 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heinrich, Thomas A1 - Traulsen, Christoph Hans-Henning A1 - Darlatt, Erik A1 - Richter, S. A1 - Poppenberg, J. A1 - Traulsen, N.L. A1 - Linder, I. A1 - Lippitz, Andreas A1 - Dietrich, Paul A1 - Dib, B. A1 - Unger, Wolfgang A1 - Schalley, C.A. T1 - The versatility of 'Click' reactions at surfaces: Molecular recognition at interfaces N2 - In order to investigate molecular recognition on surfaces, an azide-functionalized monolayer was deposited on gold. The monolayer was characterized by X-ray photoelectron spectroscopy (XPS) and angle-resolved near-edge X-ray absorption fine structure (NEXAFS) experiments and the decomposition of the azide upon irradiation with X-ray beams was investigated. Subsequently, various alkyne-functionalized host and guest molecules were attached to the azide by 1,3-dipolar cycloaddition. These modified surfaces and their host–guest chemistry were analysed by XPS and angle-resolved NEXAFS. The reversibility of guest binding was shown for one example as a proof of principle. KW - 'Click' reaction KW - Azide-terminated surfaces KW - SAMs KW - Host guest molecules KW - Molecular recognition at interfaces PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-306463 DO - https://doi.org/10.1039/C4RA01730G SN - 2046-2069 VL - 4 IS - 34 SP - 17694 EP - 17702 PB - RSC Publishing CY - London AN - OPUS4-30646 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schwarz, F. A1 - Heinrich, Thomas A1 - Lippitz, Andreas A1 - Unger, Wolfgang A1 - Schalley, C. T1 - A photoswitchable rotaxane operating in monolayers on solid support N2 - A novel photoswitchable rotaxane was synthesised and its switching behaviour in solution was analysed with NMR and UV-Vis. A monolayer of rotaxanes was deposited on glass surfaces and the on-surface photoswitching was investigated. Angle-resolved NEXAFS spectra revealed a preferential orientation that reversibly changes upon switching. KW - XPS KW - NEXAFS KW - Photoswitchable rotaxane KW - Self assembly PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-386814 DO - https://doi.org/10.1039/c6cc08586e SN - 0022-4936 SN - 1364-548X SN - 0009-241x SN - 1359-7345 VL - 52 IS - 100 SP - 14458 EP - 14461 PB - Royal Society of Chemistry (RSC) AN - OPUS4-38681 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Müller, Anja A1 - Heinrich, Thomas A1 - Tougaard, S. A1 - Werner, W. S. M. A1 - Hronek, M. A1 - Kunz, Valentin A1 - Radnik, Jörg A1 - Stockmann, Jörg M. A1 - Hodoroaba, Vasile-Dan A1 - Benemann, Sigrid A1 - Nirmalananthan-Budau, Nithiya A1 - Geißler, Daniel A1 - Sparnacci, K. A1 - Unger, Wolfgang T1 - Correction to "Determining the thickness and completeness of the shell of polymer core-shell nanoparticles by X-ray photoelectron spectroscopy, secondary ion mass spectrometry, and transmission scanning electron microscopy" N2 - This is a corrigendum to the original article "Determining the thickness and completeness of the shell of polymer core-shell nanoparticles by X-ray photoelectron spectroscopy, secondary ion mass spectrometry, and transmission scanning electron microscopy" that was published in "The journal of physical chemistry C", vol. 123 (2019), no. 49 pp. 29765-29775. PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-505451 DO - https://doi.org/10.1021/acs.jpcc.0c00027 SN - 1932-7447 SN - 1932-7455 VL - 124 IS - 6 SP - 3923 PB - American Chemical Society CY - Washington, DC AN - OPUS4-50545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -