TY - CONF A1 - Omar, Hassan T1 - Invesitgation of Thin Film Interactions with Inorganic Surfaces N2 - Thin polymer films are of vital importance due to their low production costs and wide range of applications in sensors, electronics, and coatings. Their geometry is ideal for the study of confinement effects, specifically one-dimensional confinement, on the thermodynamic properties and segmental dynamics of polymers. For this investigation, films of PC are prepared on both glass and silica substrates to measure the dielectric and calorimetric behavior as a function of film thickness. The methodology consists of broadband dielectric spectroscopy (BDS), ellipsometry, and atomic force microscopy (AFM). Using ellipsometry, the glass transition shows an increase with decreasing film thickness. Compared to a previous investigation of PC where dilatometry was used, an increase in PC was seen, but now only at thicknesses below 20 nm. Therefore, the critical thickness of PC, where the bulk-like layer no longer percolates through the film, is dependent on the method probing the glass transition. The dielectric behavior shows a deviation from bulk behavior with decreasing film thickness, although still showing a Vogel-Fulcher-Tammann (VFT) temperature dependence for all films. The influence of the adsorbed layer on the molecular mobility was also addressed. T2 - Deutschen Physikalische Gesellschaft (DPG) Tagung CY - Regensburg, Germany DA - 04.09.2022 KW - Thin films KW - Adsorbed Layer KW - Broadband dielectric spectroscopy PY - 2022 AN - OPUS4-55706 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Szymoniak, Paulina A1 - Omar, Hassan A1 - Gawek, Marcel A1 - Hertwik, Andreas A1 - Madkour, Sherif A1 - Schönhals, Andreas T1 - Investigation of the behavior of thin polymeric films including the adsorbed layer on the substrate by nano-sized relaxation spectroscopy and complementary methods N2 - Thin polymeric films are of great importance of high number of high-tech applications for instance in sensors and nanoelectronics. Form the scientific point of view thin films with thickness below 100 nm are ideal model systems to study confinement effects on its properties for instance on the molecular relaxation processes. In this contribution an overview is presented about the behavior of different systems as investigated by nanosized relaxation spectroscopy like broadband dielectric spectroscopy employing nano structured capacitors and AC chip calorimetry complimented by ellipsometry. The systems considered are PVME1, PVME/PS blends2,3 P2VP4, PBAC5 and polysulfone6. Besides the film also the adsorbed layer on the substrate prepared by a leaching approach and investigated by AFM is considered.1,4-7. For these investigationsss it is found that the adsorbed layer itself exhibits a relaxation dynamics which might be assigned either to molecular motions or to adsorptions desorption kinetics. T2 - 9. International Discussion Meeting Relaxation Complex Systems CY - Chiba, Japan DA - 12.08.2023 KW - Thin polymer films PY - 2023 AN - OPUS4-58103 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fahmy, Alaa A1 - Omar, Hassan A1 - Szymoniak, Paulina A1 - Schönhals, Andreas A1 - Friedrich, J. T1 - Structure of plasma deposited acrylic acid‐allyl alcohol copolymers N2 - Copolymer thin films with two types of functional groups have excellent performance as sensors, for example. The formation and deposition of allyl alcohol‐acrylic acid copolymer films by pulsed high frequency plasma is a complex process. As usual, the chemical composition of the top surface of the films was investigated by XPS and FTIR measurements. Furthermore, contact angle measurements with water were used to characterise the hydrophilicity and wettability of the polymer films. After plasma deposition, a significant decrease in functional groups (OH and COOH) was observed compared to the classically copolymerised equivalent. The remaining functional groups, i.e. the majority of these groups, were sufficient for application as sensor layers. Segmental mobility and conductivity, important for sensor applications, were analysed by broadband dielectric spectroscopy. KW - Plasma Polymerization PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-578349 DO - https://doi.org/10.1002/ppap.202300071 SN - 1612-8850 SP - 1 EP - 14 PB - Wiley online library AN - OPUS4-57834 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Omar, Hassan A1 - Hertwig, Andreas A1 - Szymoniak, Paulina A1 - Schönhals, Andreas T1 - Signature of the Adsorbed Layer on the glass transition of thin polymer Films: Broadband Dielectric spectroscopy and related techniques N2 - In well annealed thin polymer films with non-repulsive polymer/substrate interaction with a substrate an irreversibly adsorbed layer is expected to form. These adsorbed layers have shown a great potential for technological applications [1]. However, the growth kinetics and the molecular mobility of the adsorbed layer is still not fully understood. This concerns also the influence of the adsorbed layer on the thickness dependence of the glass transition temperature of thin films. This is partly due to the difficult accessibility of these layers in thin films. Here, the irreversibly adsorbed layers of semi-rigid mail chain polymers like polycarbonate or polysulfone are revealed by solvent-leaching experiments. First, the growth kinetics of these layers is investigated as a function of annealing time. The film thickness, topography and the quality of the adsorbed layer is controlled by Atomic Force Microscopy (AFM). Secondly, the molecular mobility of the adsorbed layer is investigated by Broadband Dielectric Spectroscopy (BDS). A developed nanostructured capacitor arrangement is employed to measure the layer with a free surface. In addition to the dielectric experiments, spectroscopic Ellipsometry measurements are carried out to estimate the glass transition of the thin films. The thickness dependence of the glass transition of the thin films is correlated with the adsorbed layer [2,3]. Acknowledgments D. Hülagü and G. Hidde thanked for the help with the ellipsometry measurements. T2 - 12. Conference on Broabband Dielectric Spectroscopy and its Application CY - Lisbon, Portugal DA - 01.09.2024 KW - Thin films PY - 2024 AN - OPUS4-60959 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Omar, Hassan A1 - Ahmadi, Shayan A1 - Szymoniak, Paulina A1 - Schönhals, Andreas T1 - Molecular Mobility of Thin Films of Poly (bisphenol-A carbonate) Capped and with one Free Surface: From Bulk-like Samples down to the Adsorbed Layer N2 - The molecular mobility of thin films of poly(bisphenol A carbonate) (PBAC) was systematically investigated using broadband dielectric spectroscopy, employing two distinct electrode configurations. First, films were prepared in a capped geometry between aluminum electrodes employing a crossed electrode capacitor (CEC) configuration, down to film thicknesses of 40 nm. The Vogel temperature, derived from the temperature dependence of relaxation rate of the α-relaxation, increases with decreasing film thickness characterized by an onset thickness. The onset thickness depends on the annealing conditions, with less intense annealing yielding a lower onset thickness. Additionally, a broadening of the β-relaxation peak was observed with decreasing thickness, attributed to the interaction of phenyl groups with thermally evaporated aluminum, resulting in a shift of certain relaxation modes to higher temperatures relative to the bulk material. A novel phenomenon, termed the slow Arrhenius process (SAP), was also identified in proximity to the α-relaxation temperature. For films with thicknesses below 40 nm, nanostructured electrodes (NSE) were utilized, incorporating nanostructured silica spacers to establish a free surface with air. This free surface causes an enhancement in the molecular mobility for the 40 nm sample, preserving the β-relaxation as a distinct peak. The α-relaxation was detectable in the dielectric loss down to 18 nm, shifting to higher temperatures as film thickness is decreased. Notably, the onset thickness for the increase in Vogel temperature was lower in the NSE configuration compared to the CEC setup, attributed to the presence of the polymer-air interface. KW - Thin polymer films PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-623422 DO - https://doi.org/10.1039/d4sm01238k SN - 1744-6848 VL - 21 IS - 2 SP - 241 EP - 254 PB - RSC AN - OPUS4-62342 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Omar, Hassan A1 - Hiid, Gundula A1 - Szymoniak, Paulina A1 - Hertwig, Andreas A1 - Schönhals, Andreas T1 - Growth kinetics of the adsorbed layer of poly(bisphenol A carbonate) and its effect on the glass transition behavior in thin films N2 - The glass transition behavior of thin films of poly(bisphenol A carbonate) (PBAC) was studied employing ellipsometry. The glass transition temperature increases with the reduction of the film thickness. This result is attributed to the formation of an adsorbed layer with a reduced mobility compared to bulk PBAC. Therefore, for the first time, the growth kinetics of the adsorbed layer of PBAC was investigated, prepared by leaching samples from a 200 nm thin film which were annealed for several times at three different temperatures. The thickness of each prepared adsorbed layer was measured by multiple scans using atomic force microscopy (AFM). Additionally, an unannealed sample was measured. Comparison of the measurements of the unannealed and the annealed samples provides proof of a pre-growth regime for all annealing temperatures which was not observed for other polymers. For the lowest annealing temperature after the pre-growth stage only a growth regime with a linear time dependence is observed. For higher annealing temperatures the growth kinetics changes from a linear to a logarithmic growth regime at a critical time. At the longest annealing times the films showed signs of dewetting where segments of the adsorbed film were removed from the substrate (dewetting by desorption). The dependence of the surface roughness of the PBAC surface on annealing time also confirmed that the films annealed at highest temperatures for the longest times desorbed from the substrate. KW - Ultra thin polymer films PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-574531 DO - https://doi.org/10.1039/D3RA02020G SN - 2046-2069 VL - 13 IS - 21 SP - 14473 EP - 14483 PB - RSC Publishing CY - London AN - OPUS4-57453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Omar, Hassan T1 - Growth Kinetics and Molecular Mobility of the Adsorbed Layer of Poly(bisphenol-A Carbonate) (PBAC), Polysulfone (PSU), and Poly (2-Vinyl Pyridine) (P2VP) N2 - Interactions between a polymer and a substrate interface play a vital role in understanding the improvement in thin film material properties as well as serving as a model for nanocomposites. For any non-repulsive polymer-substrate interactions, polymer segments form an irreversibly adsorbed layer and show a slowdown in the glassy dynamics and thus an increase in the thermal glass transition temperature compared to the bulk-like values. The growth kinetics of the adsorbed layer obey a two-step mechanism: formation of immobilized layer with flat segmental conformations and a loosely bound layer with stretched chains pinned to the surface. Here the adsorbed layer was studied for: poly (bisphenol-A carbonate) (PBAC) and polysulfone (PSU), two bulky polymers containing a functional group (phenyl ring) in the backbone and compared to poly (2-vinyl pyridine) (P2VP), where the backbone is a vinyl-derivative and the functional group (pyridine) is in the side chain. The growth kinetics for PBAC and PSU were found to deviate from the well-known mechanism, observed for polymers such as P2VP. Atomic force microscopy and ellipsometry were used for this investigation and was additionally supported by broadband dielectric spectroscopy. T2 - 11th International Conference on Times of Polymers (TOP) and Composites CY - Ischia, Italy DA - 11.06.2023 KW - Adsorbed Layer KW - Dielectric Spectroscopy KW - Atomic Force Microscopy KW - Ellipsometry KW - Growth Kinetics KW - Molecular Mobility PY - 2023 AN - OPUS4-57709 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Omar, Hassan T1 - Growth Kinetics and Molecular Mobility of the Adsorbed Layer of Poly(bisphenol-A Carbonate) (PBAC), Polysulfone (PSU), and Poly (2-Vinyl Pyridine) (P2VP) N2 - Interactions between a polymer and a substrate interface play a vital role in understanding the improvement in thin film material properties as well as serving as a model for nanocomposites. For any non-repulsive polymer-substrate interactions, polymer segments form an irreversibly adsorbed layer and show a slowdown in the glassy dynamics and thus an increase in the thermal glass transition temperature compared to the bulk-like values. The growth kinetics of the adsorbed layer showed a deviation for both poly (bisphenol-A carbonate) (PBAC) and polysulfone (PSU), two bulky polymers containing a functional group (phenyl ring) in the backbone, compared to conventional polymers previously studied like poly-2-vinyl pyridine (P2VP). This deviation was attributed to the bulkiness of the phenyl rings. . Further investigations into the influence of the adsorbed layer on glassy dynamics were conducted. The molecular mobility and glass transition for thin films of PBAC and PSU were compared to bulk samples of each polymer. Broadband dielectric spectroscopy, atomic force microscopy, and ellipsometry were primarily used and additionally supported by sum frequency generation spectroscopy. T2 - Deutsche Physikalische Gesellschaft (DPG) Tagung CY - Berlin, Germany DA - 17.03.2024 KW - Thin films KW - Adsorbed Layer KW - Atomic Force Microscopy KW - Ellipsometry KW - Dielectric Spectroscopy PY - 2024 AN - OPUS4-59821 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Omar, Hassan T1 - Growth Kinetics and Molecular Mobility of the adsorbed Layer of Poly(bisphenol-A Carbonate) (PBAC), Polysulfone (PSU), and Poly (2-Vinyl Pyridine) (P2VP) N2 - Interactions between a polymer and a substrate interface play a vital role in understanding the improvement in thin film material properties as well as serving as a model for nanocomposites. For any non-repulsive polymer-substrate interactions, polymer segments form an irreversibly adsorbed layer and show a slowdown in the glassy dynamics and thus an increase in the thermal glass transition temperature compared to the bulk-like values. The growth kinetics of the adsorbed layer obey a two-step mechanism: formation of immobilized layer with flat segmental conformations and a loosely bound layer with stretched chains pinned to the surface. Here the adsorbed layer was studied for: poly (bisphenol-A carbonate) (PBAC) and polysulfone (PSU), two bulky polymers containing a functional group (phenyl ring) in the backbone and compared to poly (2-vinyl pyridine) (P2VP), where the backbone is a vinyl-derivative and the functional group (pyridine) is in the side chain. The growth kinetics for PBAC and PSU were found to deviate from the well-known mechanism, observed for polymers such as P2VP. Atomic force microscopy and ellipsometry were used for this investigation and was additionally supported by broadband dielectric spectroscopy. T2 - Deutschen Physikalische Gesellschaft (DPG) Tagung CY - Dresden, Germany DA - 26.03.2023 KW - Thin films KW - Adsorbed Layer KW - Broadband dielectric spectroscopy KW - Atomic force microscopy KW - Growth Kinetics PY - 2023 AN - OPUS4-57282 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Omar, Hassan A1 - Ahamadi, Shayan A1 - Hülagü, Deniz A1 - Hidde, Gundula A1 - Hertwig, Andreas A1 - Szymoniak, Paulina A1 - Schönhals, Andreas T1 - Investigations of the adsorbed layer of polysulfone: Influence of the thickness of the adsorbed layer on the glass transition of thin films N2 - This work studies the influence of the adsorbed layer on the glass transition of thin films of polysulfone. Therefore, the growth kinetics of the irreversibly adsorbed layer of polysulfone on silicon substrates was first investigated using the solvent leaching approach, and the thickness of the remaining layer was measured with atomic force microscopy. Annealing conditions before leaching were varied in temperature and time (0–336 h). The growth kinetics showed three distinct regions: a pre-growth step where it was assumed that phenyl rings align parallel to the substrate at the shortest annealing times, a linear growth region, and a crossover from linear to logarithmic growth observed at higher temperatures for the longest annealing times. No signs of desorption were observed, pointing to the formation of a strongly adsorbed layer. Second, the glass transition of thin polysulfone films was studied in dependence on the film thickness using spectroscopic ellipsometry. Three annealing conditions were compared: two with only a tightly bound layer formed in the linear growth regime and one with both tightly bound and loosely adsorbed layers formed in the logarithmic growth regime. The onset thickness and increase in the glass transition temperature increases with annealing time and temperature. These differences were attributed to the distinct conformations of the formed adsorbed layers. KW - Glass transition KW - Adsorbed Layer PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-607701 DO - https://doi.org/10.1063/5.0223415 SN - 0021-9606 VL - 161 IS - 5 SP - 1 EP - 12 PB - AIP Publishing AN - OPUS4-60770 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -