TY - JOUR A1 - Priebe, Nsesheye Susan A1 - Schmidt, Wolfram A1 - Rogge, Andreas A1 - Kühne, Hans-Carsten T1 - Performance of rice husk ash as an alternative binder in a modified cementitious system with added superplasticizers N2 - Rice husk as (RHA) is an eco-friendly material, which can be used as a supplementary cementitious material (SCM) in cement and concrete. Due to the high water demand for the material, superplasticizers (SPs) are essential to improve the performance. However, the interaction between the SPs and RHA systems is limited. This paper investigates the interaction of the binders with three SPs, i.e. two polycarboxylate ethers (PCEs) and one lignosulphonate (LS). The investigations are performed on blended systems of mortar containing various percentages of RHA and limestone powder (LSP). LSP is used in this research to improve the workability of the mortar. The results from the zeta potential (ZP) shows that the SPs are extremely dependent on the pH of the suspension. At higher pH values such as in a cementitious system, the ZP becomes less negative indicating that the ions in the suspension interact with the carboxyl groups in the backbone of the polymers thus reducing the surface charges of the SP. The mini-slump flow shows that the workability of the blended mortar systems is significantly improved with the addition of SPs. LS systems with increasing RHA is observed to have similar workability as the control mix over time. The compressive strength test results show increased strength for all mortar specimens with added RHA and LSP at later ages. KW - Compressive strength KW - Rice husk ash KW - Superplasticizers KW - Zeta potential KW - Workability PY - 2017 DO - https://doi.org/10.1016/j.cemconcomp.2017.07.014 N1 - Geburtsname von Priebe, Nsesheye Susan: Msinjili, N. S. - Birth name of Priebe, Nsesheye Susan: Msinjili, N. S. VL - 83 SP - 202 EP - 208 PB - Elsevier Ltd. AN - OPUS4-42602 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sturm, Patrick A1 - Gluth, Gregor A1 - Schmidt, Wolfram A1 - Astorg, Adéle A1 - Kühne, Hans-Carsten A1 - Brouwers, H.J.H. T1 - Rheological properties of microsilica and sodium aluminate based one-part geopolymers compared to ordinary Portland cement N2 - One-part (“just-add-water”) geopolymers are a new dass of mineral binders that are produced without the use of alkaline activating Solutions. Compared to conventional geopolymers, i. e. those activated by highly alkaline Solutions, much less is known about the one-part geopolymers ’ microstructure and with regard to their rheology. In this work, the rheology of one-part geopolymers, produced from microsilica and sodium aluminate, with several SiO-flACOiratios and two different water/binder-ratios (w/b) were investigated qualitatively with a viscometer (mortar measuring cellj. Absolute values of plastic viscosity and yield stress were determined with a double gap measuring cell. In addition spread flow tests were conducted. The aim was to classify the early behavior of geopolymer pastes and to compare it to ordinary Portland cement (CEM 142.5 R) pastes. At moderate to high shear rates, the measured flow curves cotdd be fltted well by the Bingham model. With increasing silica content the yield stress increased. Up to a certain SiOi/Al2O3-ratio viscosity also increased with increasing silica content; however, at higher silica/alumina-ratios the viscosity decreased again. Higher w/b-ratios caused lower yield stresses and viscosities. Compared to Portland cement pastes, most of the considered geopolymers were signiflcantly stiffer. The results were further Interpreted in terms of pore solution viscosity and volume-based water to binder ratios (w/b) of the geopolymer pastes. T2 - 5th International Conference Non-Traditional Cement & Concrete CY - Brno, Czech Republic DA - 16.06.2014 KW - Alkali-activated binders KW - One-part geopolymers KW - Rheology PY - 2014 SN - 978-80-214-4867-4 SP - 71 EP - 74 AN - OPUS4-31159 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - de Carvello, J. M. F. A1 - Schmidt, Wolfram A1 - Kühne, Hans-Carsten A1 - Fiorotti Peixoto, R. A. T1 - Influence of high-charge and low-charge PCE-based superplasticizers on Portland cement pastes containing particle-size designed recycled mineral admixtures N2 - Design : and use of engineered recycled mineral admixtures obtained from industrial and mineral waste are promising strategies to increase the range of materials suitable for use in cement-based composites. In this work, Portland cement-blended pastes containing mineral admixtures designed for improving particle packing were evaluated in the presence of low- and high-charge polycarboxylate-based superplasticizers. The powders were obtained from basic oxygen furnace slag, iron ore tailings, quartz mining tailings, and quartzite mining tailings. The zeta-potentials of the particles were obtained via electrophoretic mobility. The flow properties were evaluated by rheological tests performed in a Couette type rheometer. The hydration kinetics was evaluated by isothermal calorimetry and an adapted method based on the Vicat needle test. The high-charge PCE and the finer mineral admixtures produced more stable blends. Coarser mineral admixtures led to increased flowability and delayed hydration compared to finer ones. Steel slag powders presented the most significant plasticizer effects, but also the largest setting delays and segregation tendency. Quartz-rich superfines reduced the setting delays caused by the superplasticizers. In summary, both superplasticizers were effective in improving flow properties, but the high-charge PCE was effective in preventing segregation in pastes containing mineral admixtures coarser and heavier than cement. KW - Engineered recycled mineral admixtures KW - Rheology KW - PCE-Based superplasticizer KW - Steel slag KW - Mining tailing PY - 2020 DO - https://doi.org/10.1016/j.jobe.2020.101515 VL - 32 SP - 1 EP - 16 PB - Elsevier AN - OPUS4-58395 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Barthel, Maria A1 - Kühne, Hans-Carsten A1 - Schmidt, Wolfram ED - Bager, D. H. ED - Silfwerbrand, J. T1 - Multilayer concrete pavers - solutions for the mitigation of the urban heat island effect N2 - The large scale application of self-cooling concrete pavers is a future-oriented approach to reduce the urban heat island effect in inner-city areas. Making use of evaporation enthalpy, these new pavements counterbalance the absorption of solar radiation and the subsequent transfer of heat to the surrounding environment. The concrete pavers consist of a permeable top-layer and a storage layer. As the different requirements of these layers demand different concrete mixtures they are developed and optimised for their respective functions. This paper presents some results of the concrete mixture design and Solutions that combine a sufficient compressive strength as well as good water transportation properties for the face concrete layer. T2 - fib Symposium Stockholm 2012 'Concrete structures for a sustainable community' CY - Stockholm, Sweden DA - 11.06.2012 KW - Urban heat island effect KW - Concrete multilayer pavers KW - Permeability KW - Fibre concrete PY - 2012 SN - 978-91-980098-1-1 SP - 513 EP - 516 PB - Royal Institute of Technology CY - Stockholm AN - OPUS4-27271 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Brouwers, H.J.H. A1 - Kühne, Hans-Carsten A1 - Meng, Birgit T1 - Zum Einfluss der Menge und Modifikation des Fließmittels auf das Erstarren, die Wärmeentwicklung und die frühen Verformungen von Bindemittelleimen N2 - Es wurden Bindemittelleime aus Zement, Kalksteinmehl, Stabilisierer und Wasser mit Polycarboxylatether-Fließmitteln (PCE) unterschiedlicher Ladungsdichte modifiziert. Die Mischungen wurden in einem automatischen Vicat-Gerät, einem isothermen Wärmeflusskalorimeter sowie mit zwei Schwindkegeln bei Temperaturen von 5, 20 und 30 °C analysiert. Begleitend wurden XRD Messungen durchgeführt. Die Ergebnisse zeigen, dass bei Verwendung von PCE das Erstarrungsende unabhängig von der Temperatur oder der PCE-Modifikation sehr gut mit dem Wendepunkt der Wärmeflusskurve korreliert. Eine derartige Korrelation kann nicht für den Erstarrungsbeginn beobachtet werden. Im Wesentlichen bestimmt die Menge an Polymeren im Gesamtsystem unabhängig von der Struktur eines PCEs den zeitlichen Verlauf des Erstarrens. Der zeitliche Verlauf der frühen Verformungen wird weder von der Menge noch von der Art des Fließmittels signifikant beeinflusst. Aufgrund des starken Einflusses der PCE-Menge auf das Erstarren, kann folglich durch geeignete Fließmittelauswahl das Erstarren gezielt an die Verformungen angepasst werden, so dass signifikante Verformungen überwiegend in einem noch plastischen Zustand stattfinden können. T2 - 18. Ibausil - Internationale Baustofftagung CY - Weimar, Germany DA - 12.09.2012 KW - Polycarboxylatether KW - Fließmittel KW - Erstarren KW - Hydratationswärme KW - Schwinden PY - 2012 SN - 978-3-00-034075-8 VL - 2 IS - 3.07 SP - 2-0392 EP - 2-0399 AN - OPUS4-26543 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmidt, Wolfram A1 - Tchetgnia Ngassam, Ines Leana A1 - Olonade, K. A. A1 - Mbugua, R. A1 - Kühne, Hans-Carsten T1 - Plant based chemical admixtures – potentials and effects on the performance of cementitious materials N2 - While today, engineers can choose from a wide range of rheology modifying admixtures, in some parts of the world, these are difficult to access, due to their complex processing. However, alternatives can be bio‐based polymers such as polysaccharides from various sources. These are easily accessible all over the world, do not demand for complicated processing, and typically they are more sustainable than many established materials, which are crude oil‐based. The paper presents the effects of acacia gum, cassava starch and the gum of triumfetta pendrata A. Rich on the rheological performance of cementitious systems. It is shown that acacia gum can be as efficient as polycarboxylate based superplasticisers, cassava starch can reduce the yield stress slightly with little effect on the plastic viscosity, and the gum of triumfet ta pendrata A. Rich increases the thixotropy of cement pastes with plasticizing polymers significantly. KW - Polysaccharides KW - Rheology KW - Cement KW - Chemical admixtures KW - Bio-based concrete PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-476748 DO - https://doi.org/10.21809/rilemtechlett.2018.83 VL - 3 SP - 124 EP - 128 PB - RILEM S.A.R.L. CY - Paris AN - OPUS4-47674 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Kühne, Hans-Carsten A1 - Leinitz, Sarah ED - Diouri, A. ED - Boukhari, A. ED - Ait Brahim, L. ED - Bahi, L. ED - N., Khachani ED - Saadi, M ED - Aride, J. ED - Nounah, A. T1 - Concrete casting robustness improvement due to active rheology N2 - With ongoing innovation in process technology, the challenges of concrete technology are more and more focused on the rheological optimisation for these processes, since improper mixture stability or poor compaction ability negatively affect the concrete homogeneity and quality. However, along with the increasing complexity of today’s concrete mixture compositions, concrete becomes more prone to failure regarding the casting process. Variable properties of the raw materials typically cause changing workability. The reasons can be found among others in scattering water contents, physical or chemical properties of the cement or varying environmental temperatures. Robustness in the delicately adjusted rheology, however, is of utmost importance for modern and future process technology, from sprayed concrete over pumpable concrete towards 3D-printing, with regard to the long-term strength, the function and the durability. Typically, material induced changes cannot be identified easily due to the complex interactions of concrete constituents. Therefore, a precise and prompt counteraction is impossible. However, it is known that the yield stress can be controlled by addition of supplementary superplasticizer or stabilising agent. In combination with computerized process observation tools that can rapidly interpret and react on changes in the rheology, it is therefore thinkable, that only these two admixture types can adjust the rheology steadily and permanently, regardless of the actual root cause for observed macroscopic rheology change. The presentation will firstly give a comprehensive overview of effects at the interface between pore solution, particles and hydrates, which affect the rheology of fresh concrete. Secondly, ways are recommended how the rheology can be actively manipulated before eventually computerized methods are demonstrated that help to actively and rapidly assess and counteract performance scatter during steady casting processes. T2 - 2nd International Congress on Materials & Structural Stability (CMSS-2017) CY - Rabat, Morocco DA - 22.11.2017 KW - Cusum KW - Rheology KW - Control Chart KW - Concrete KW - Robustness PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-444317 DO - https://doi.org/10.1051/matecconf/201814901001 SN - 2261-236X VL - 149 SP - 01001-1 EP - 01001-7 PB - EDP Sciences CY - Les Ulis AN - OPUS4-44431 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shamsuddoha, Md A1 - Hüsken, Götz A1 - Schmidt, Wolfram A1 - Kühne, Hans-Carsten A1 - Baeßler, Matthias T1 - Superplasticizer and Shrinkage Reducing Admixture Dosages for Microfine Cement in Grout Systems N2 - Grouts have numerous applications including crack repair as maintenance in construction industries. Microfine cements are intensively used for high strength mortar and grout products. They are ideal for injection grouting in structural repair. Such grouts should have suitable rheological properties to be injectable, especially those used in repair and rehabilitation. The use of superplasticizers (SP) in these products is thus becoming increasingly crucial to achieve favorable workability and viscosity properties. A difficulty in such grouts is the plastic shrinkage due to finer particles used. It is thus necessary to determine optimum SP and shrinkage reducing admixture (SRA) dosages for a microfine cement based grout. In this study, a saturation dosage was decided from two Polycarboxylate ether (PCE) based SPs in relation to neat cement using slump flow and rheological parameters. A range of grout mixtures was formulated containing micro silica (MS) and fly ash (FA), and tested for suitable rheological and mechanical parameters. Based on the results, a grout mixture with MS and FA was selected to determine optimum SRA content. According to the results, a SP dosage of 3% by weight of neat cement is sufficient to achieve saturation. The grout material including MS and FA can produce comparable properties to neat cement grout. MS is found to improve compressive strength within the range considered, whereas a higher FA content provides favourable rheological properties. Finally, a SRA dosage of 4%, which could reduce the shrinkage by about 43% after 28d days, is determined for the grout system. T2 - 2nd International Conference on Building Materials and Materials Engineering (ICBMM 2018) CY - University of Lisbon, Portugal DA - 26.09.2018 KW - Grout KW - Microfine Cement KW - Superplasticizer KW - Supplementary Cementitious Materials KW - Shrinkage Reducing Admixture PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-478319 DO - https://doi.org/10.1051/matecconf/201927801001 VL - 278 SP - Article Number 01001 PB - EDP Sciences AN - OPUS4-47831 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shamsuddoha, Md A1 - Hüsken, Götz A1 - Schmidt, Wolfram A1 - Kühne, Hans-Carsten A1 - Baeßler, Matthias ED - Alexander, M.G. ED - Beushausen, H. ED - Dehn, F. ED - Moyo, P. T1 - Workability and mechanical properties of ultrafine cement based grout for structural rehabilitation: A parametric study on the partial replacement with SCMs N2 - Grouting is a universal repair and strengthening technique, which is constantly used for structural remediation of concrete components, trenches, mine subsidence, dam joints, restoration of masonry structures, and geological stabilizations. Having an extremely small particle size of only few microns, ultrafine cements are ideal for grouting applications due to their superior permeability and compressive strength properties of the hardened cement paste compared to that of the less-expensive, but coarser ordinary Portland cements. Supplementary cementitious materials (SCMs) are often used to replace ultrafine cement in order to modify certain properties and to reduce costs. The aim of this experimental study is to investigate the effect of three supplementary materials: microsilica (MS), fly ash (FA), and metakaolin (MK) on the workability, and mechanical properties of an ultrafine cement based grout with a constant water-binder ratio and constant superplasticizer content. Maximum percentages of replacement with ultrafine cement were 6% by volume of cement for MS and 16% for FA, and MK. In general, results suggest that the workability is improved by addition of FA, whereas is reduced, when modified with MS and MK. The compressive strength of grout after cement replacement remains comparable to that of pure cement grout. However, there is a tendency of the MS to positively affect the compressive strength opposite to FA, whereas flexural strength is positively affected by FA. Based on the results, it is evident that grouts with Hägerman cone flow more than 500 mm and compressive strength of more than 90 MPa after 28 days can be produced. T2 - International Conference on Concrete Repair, Rehabilitation and Retrofitting (ICCRRR 2018) CY - Cape Town, South Africa DA - 19.11.2018 KW - Grouting KW - Repair KW - Box-Behnken KW - Supplementary cementitious materials KW - Analysis of variance PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-464769 DO - https://doi.org/10.1051/matecconf/201819907006 SN - 2261-236X VL - 199 SP - 07006-1 EP - 07006-7 PB - MATEC Web of Conferences AN - OPUS4-46476 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Franco de Carvalho, J. M. A1 - Defàveri, K- A1 - Castro Mendes, J. A1 - Schmidt, Wolfram A1 - Kühne, Hans-Carsten A1 - Fiorotti Peixoto, R. A. T1 - Influence of particle size-designed recycled mineral admixtures on the properties of cement-based composites N2 - In this work, engineered recycled mineral admixtures were obtained from four different industrial residues: basic oxygen furnace slag, iron ore tailings, quartz mining tailings and quartzite mining tailings. The grinding performance was evaluated in two different programs and the characterization included chemical and mineralogical composition, particle morphology, and physical properties. Performance evaluations were carried out in blended pastes and mortars, including flow properties, hydration kinetics, soundness, pozzolanic activity, and compressive strength. Coarser-than-cement admixtures allowed better flow performance, greater dimensional stability and more economical production, while finer-thancementn admixtures improved mechanical performance by both filler effect and cementing activity. KW - Engineered recycled mineral admixtures KW - Rheology KW - Hydration kinetics KW - Basic oxygen furnace slag KW - Iron ore tailings KW - Mining tailings PY - 2021 DO - https://doi.org/10.1016/j.conbuildmat.2020.121640 SN - 0950-0618 VL - 272 SP - 1 EP - 13 PB - Elsevier Ltd. AN - OPUS4-58255 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kühne, Hans-Carsten A1 - Priebe, Nsesheye Susan A1 - Schmidt, Wolfram A1 - Uzoegbo, H. C. T1 - Baupraxis und Infrastrukturentwicklung im Hinblick auf die Betonindustrie in Ost- und Südafrika N2 - Der Bausektor stellt in Afrika traditionell eine der stabileren Quellen für den Arbeitsmarkt dar. Durch ständige Wechsel in der Politik wurden jedoch in zahlreichen Ländern Einschnitte bei den öffentlichen Investitionen sowie ein Rückgang der Beschäftigtenzahlen im Privatsektor beobachtet. Darüber hinaus konnte eine Verlagerung von offiziell tätigen und registrierten hin zu nicht registrierten Bauunternehmen festgestellt werden. Zahlreiche Bauunternehmen bieten Dienstleistungen an, die sie nicht ständig ausführen oder für die sie sich das erforderliche Gerät leihen müssen. Einer im Jahre 2000 hinsichtlich der Situation in Tansania veröffentlichten Studie zufolge verfügen nur etwa 15 % der Unternehmen, die Betonbauarbeiten anbieten, über einen eigenen Betonmischer. Die auf dem afrikanischen Kontinent angewandten Baupraktiken im Betonbau weichen erheblich voneinander ab. Während Südafrika über eine fortgeschrittene Technologie und eine hoch entwickelte Infrastruktur im Hinblick auf die Zement- und Betonindustrie verfügt, sind Zement und Beton in den ostafrikanischen Ländern, insbesondere in jenen, die in den 90er Jahren des vergangenen Jahrhunderts von schweren Bürgerkriegen erschüttert wurden, kaum verfügbar und zählen keinesfalls zu den in der täglichen Baupraxis verwendeten Baustoffen. Hier wird auf einheimische Baumethoden, bei denen vorwiegend Holz verwendet wird, zurückgegriffen. Dieses wird durch Abholzung gewonnen, was schließlich zur Rodung ganzer Waldgebiete führt. Die ohne entsprechende Planung, Genehmigung und Erschließung errichteten Siedlungen in Südafrika und Kenia veranschaulichen erschreckend, wie einstmals von grüner Vegetation bedeckte Landstriche in künstliche, wüstenartige Landschaften verwandelt wurden. PY - 2011 SN - 1439-7706 N1 - Geburtsname von Priebe, Nsesheye Susan: Msinjili, N. S. - Birth name of Priebe, Nsesheye Susan: Msinjili, N. S. VL - 3 SP - 32 EP - 37 PB - ad-media-Verl. CY - Köln AN - OPUS4-25361 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Kühne, Hans-Carsten A1 - Meng, Birgit ED - Toutlemonde, F. ED - et al., T1 - Performance and interactions of admixtures for SCC exposed to different climatic conditions T2 - Fifth International Conference on Concrete under Severe Conditions: Environment and Loading (CONSEC `07) CY - Tours, France DA - 2007-06-04 PY - 2007 SN - 1628-4704 VL - 2 SP - 979 EP - 986 CY - Tours, France AN - OPUS4-15050 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -