TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. ED - Singh, D. ED - Salem, J. ED - Wang, J. ED - Kirihara, S. T1 - Hardmetals based on niobium carbide (NbC) versus casted NbC bearing MMCs N2 - Thc tribological behavior under dry sliding of a Fe3Al-NbC composite prepared by pyrometallurgical synthesis is compared to NbC-based hard metals bonded by cobalt or Fe3Al. The dry sliding wear resistance (0,1-7/10 m/s) of the present Fe3Al-NbC with 60% NbC was close to those known of NbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks, as a metallurgical interphase was formed between matrix and NbC grains. T2 - 39th International conference on advanced ceramics and composites CY - Daytona Beach, FL, USA DA - 25.01.2015 PY - 2015 SN - 978-1-119-21128-0 SP - 87 EP - 92 PB - Wiley AN - OPUS4-34888 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - The background for the use of hardmetals and MMCs based on niobium carbide (NbC) as cutting tools and for wear resistant tribosystems N2 - In this present study, the mechanical properties (strength, hardness, moduli) and the dry sliding properties of stoichiometric and sub-stoichiometric NbC were compared. Microhardness and elastic properties of NbC depend from the C/Nb ratio, because the binary phase diagram Nb-C shows a region of homogeneity of NbCx of 0,72≤ x ≤1.0. At RT, hard metals of stoichiometric NbC have an elastic modulus E of ~440 GPa, those of substochiometric NbC0,88 an E of 405 GPa. The hot hardness of sub-stoichiometric NbC is above 600°C higher than of WC. The dry sliding wear resistance (0,1-7/10 m/s) of the present Fe3Al-NbC0,94 with ~61 vol.-% NbC as hard phase was close to those known of NbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks of the Fe3Al-NbC composite (MMC), as a metallurgical interphase was formed between matrix and NbC grains. Stoichiometric and sub-stoichiometric niobium carbides have at RT and 400°C under dry sliding a prone intrinsic wear resistance more or less independent from sliding speed, either as hardmetal or as hard phase in metal matrix composite, associated with an exceptional high load carrying capacity. T2 - 3rd International Conference on Stone and Concrete Machining (ICSCM) CY - Bochum, Germany DA - 02.11.2015 KW - NbC KW - Niobium carbide KW - Cobalt KW - Fe3Al KW - Hardmetals KW - Metal matrix composite KW - Wear resistance KW - Cutting KW - Milling PY - 2015 SN - 978-3-943063-20-2 SP - 199 EP - 207 PB - Ruhr-Universität Bochum CY - Bochum AN - OPUS4-34846 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - Influence of stoichiometry and processing on the tribological profile of hardmetals based on niobium carbide (NbC) N2 - The tribological behavior under dry sliding of a Fe3Al-NbC composite prepared by pyro-metallurgical synthesis is compared to different SPS sintered NbC-based hardmetals bonded by cobalt or Fe3AI. The dry sliding wear resistance (0. 1-7 /10 m/s) of the present Fe3Al-NbC with -60 % NbC was close to those known ofNbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks of the Fe3Al-NbC composite, as a metallurgical interphase was formed between matrix and NbC grains. The physical prope1ties of melt grown NbC match those known from powder metallurgically sintered NbC using powders converted from Nb205. T2 - International conference on powder metallurgy & particulate materials 2015 CY - San Diego, USA DA - 17.05.2015 PY - 2015 SN - 978-1-943694-01-3 SP - 08-83 EP - 08-91 CY - Princeton, NJ, USA AN - OPUS4-34884 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - The use of niobium carbide (Nbc) for wear resistant tribosystems and the tribological backgrounds as cutting tools N2 - The tribological profile of rotating disks made in binder-less niobium Carbide (hot-pressed NbC) and cobalt-bonded NbCs (NbC-8Co and NbC-12Co) mated against alumina (99.7%) were determined under unidirectional sliding tests (0.1 m/s to 8.0 m/s; 22°C and 400°C) as well as in oscillation tests (f= 20 Hz, Ax= 0.2 mm, 2/50/98% rel. humidity, n= 105/l 06 cycles) under unlubricated (dry) conditions. In addition, the microstructure and mechanical properties of HPNbCl and NbC bonded with 8 vol.-% and 12 vol.-% cobalt were determined as well. The tribological data obtained were benchmarked with different ceramics, cermets, hard metals and thermally sprayed coatings, where the NbCs bonded with 8% and 12% Co presented above 7 m/s the lowest wear rates so far in such a bench mark. HP-NbCl, NbC-8Co and NbC-12Co exhibited low wear rates under dry sliding associated with PV high load carrying capacities. The tribological profile established revealed a strong position of NbC bearing materials under tribological considerations and for closed tribo-systems against traditional references. T2 - 9th International conference on tungsten, refractory & hardmaterials CY - Orlando, FL, USA DA - 18.05.2014 KW - Friction KW - Wear KW - Ceramic KW - Oscillation KW - NbC KW - Niobium carbide KW - Cobalt KW - Hard metal KW - Strength KW - Sliding KW - Modulus KW - High temperatures PY - 2014 SN - 978-0-9853397-7-7 SP - 222 EP - 232 AN - OPUS4-31630 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - The tribological and mechanical properties of niobium carbides (NbC) bonded with cobalt of Fe3Al N2 - The tribological and mechanical properties of niobium carbide bonded with 8 vol.-% (NbC-8Co), 12 vol.-% of cobalt (NbC-12Co) or 12 vol.-% of Fe3Al (NbC-12Fe3Al) are presented. Rotating discs made of metal-bonded niobium carbide were mated against alumina (99.7%) under unlubricated (dry) unidirectional sliding tests (0.1 m/s to 12.0 m/s; 22 °C and 400 C) as well as in oscillation tests (f=20 Hz, Δx=0.2 mm, 2/50/98% rel. humidity, n=105/106 cycles). Microstructure and phase compositions were determined as well. The tribological data obtained were benchmarked with different ceramics, cermets, hard metals and thermally sprayed coatings, where NbC bonded with 8% and 12% Co presented above 7 m/s the lowest wear rates so far in such a benchmark. Binderless NbC (HP-NbC1) and the metal-bonded NbCs exhibited low wear rates under dry sliding associated with P·V high load carrying capacities. NbC-based hard metal bonded with 12 vol.-% of Fe3Al resulted in a higher hardness level than for 12 vol.-% cobalt. The tribological profile established revealed a strong position of NbC-bearing materials under tribological considerations and for closed tribosystems against established reference tribo-couples. KW - Sliding KW - Ceramic KW - Oscillation KW - Strength KW - Modulus KW - High temperatures KW - Friction KW - Wear KW - NbC KW - Niobium carbide KW - Cobalt KW - Fe3Al KW - Hard metal PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-316129 DO - https://doi.org/10.1016/j.wear.2014.09.007 SN - 0043-1648 VL - 321 SP - 1 EP - 7 PB - Elsevier CY - Amsterdam AN - OPUS4-31612 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. A1 - Vleugels, J. A1 - Huang, S. T1 - Substitution of tungsten carbide by niobium carbide as cutting materials and for wear protection N2 - Im binären System NbC-C existieren verschiedene Phasen im Homogenitätsbereich NbCₓ, mit 0,75 ≤ x ≤ 1,0, wie NbC, Nb₆C₅ und Nb₄ C₃ , die ein breites Prozessfenster beim Sintern und in der Werkstoffentwicklung ermöglichen. Die Mikrohärte, die Warmhärte, der Verschleißwiderstand, das Elastizitätsmodul und die Zähigkeit von Hartmetallen hängen vom C/Nb-Verhältnis ab, wie auch von der Zugabe von Sekundärcarbiden. N2 - Several phases, like Nb₄ C₃ , Nb₆C₅ and other short and long range ordered phases occur in the region of homogeneity of NbCₓ (0.75 ≤ x ≤ 1.0) in the binary phase diagram. Properties, like micro-hardness, hot hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, the addition of secondary carbides and the type of binder. Supporting results from different grades with varying C/Nb ratio or binder types were illuminated. Thus, the NbC system offers to producers a wider process window, than WC. The impact of these tailored properties on sliding wear and cutting performance was illuminated by tribological and machining results. Niobium is today largely available. NbC can be synthesized by carbothermal conversion of Nb₂O₅ or be metallurgically grown and leached out, provides comparably low friction in many relevant tribo-contacts and displays low wear. NbC and Nb₂O₅ have so far no REACH classification related to human toxicology and are not listed as substances of very high concern contrary to WO₃ and Co₃ O₄ . T2 - 57. Tribologie-Fachtagung CY - Göttingen, Germany DA - 26.09.2016 KW - cutting materials KW - niobium carbide KW - wear protection PY - 2016 SN - 978-3-9817451-1-5 SP - 65/1 EP - 65/14 AN - OPUS4-37833 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias A1 - Huang, S. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Cannizza, E. T1 - Potentials of niobium carbide (NbC) as cutting tools and for wear protection N2 - Research and development of WC grades is 90 years ahead of niobium carbide-based hard materials, which showed already as light-weight and unexplored material a very high potential for many technical applications, especially for wear protection and machining. NbC evoluted recently from lab scale to pilot scale, especially in areas where established WC-based materials are causing economic, environmental or technical concerns. Benchmark trials of NbC-based hard metals indicated already a favorable performance in machining of steel components. KW - Niobium carbide KW - Friction KW - Wear KW - NbC KW - Hard metals KW - Machining KW - Nickel PY - 2018 DO - https://doi.org/10.1016/j.ijrmhm.2018.01.009 SN - 0263-4368 VL - 72 SP - 380 EP - 387 PB - Elsevier Ltd. AN - OPUS4-44166 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - The tribological property profile of hard metals and metal matrix composites based on niobium carbide N2 - This work is focused on the tribological profile of NbC-based material, as well as their potential applications and environmental implications. T2 - International Symposium on Wear Resistant Alloys for the Mining and Processing Industry CY - Sao Paulo, Brazil DA - 04.05.2015 KW - Niobium carbide KW - Metal KW - Binder KW - Metal matrix composite KW - Friction KW - Wear KW - Hardness KW - Solubility KW - Toughness KW - Abrasion PY - 2018 SN - 978-0-692-05382-9 SP - 427 EP - 461 AN - OPUS4-44201 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huang, S. G. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias T1 - NbC-based cermets: influence of secondary carbide addition and metal binder N2 - Full densification of Fe, Co and Ni bonded NbC based cermet’s was achieved by pressure less liquid phase sintering in vacuum for one hour at 1420°C. The hardness and toughness of the NbC matrix cermet’s can be mainly tailored by the binder composition and secondary carbide additions. Ni binder based NbC cermet’s allow the combination of high hardness and improved toughness. The addition of lesser amounts of VC/Cr3C2 in a NbC partially substituted WC-Co cemented carbide increased significantly the hardness in combination with a moderate fracture toughness. T2 - International Symposium on Wear Resistant Alloys for the Mining and Processing Industry CY - Sao Paulo, Brazil DA - 04.05.2015 KW - Niobium carbide KW - Hardmetal KW - Cemented carbide KW - Sintering KW - Grain growth KW - Microstructure KW - Hardness KW - Fracture toughness PY - 2018 SN - 978-0-692-05382-9 SP - 521 EP - 534 AN - OPUS4-44206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Huang, S. A1 - De Beats, P. A1 - Sukumaran, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias A1 - Vleugels, J. T1 - Effect of carbon content on the microstructure and mechanical properties of NbC-Ni based cermets N2 - The aim of this work was to correlate the overall carbon contents in NbC-Ni, NbC-Ni-VC and NbC-Ni-Mo starting powders with the resulting microstructure, hardness, and fracture toughness of Ni-bonded NbC cermets. KW - Niobium carbide KW - Cermet KW - Hardmetal KW - Liquid phase sintering KW - Carbon KW - Hardness PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-444608 DO - https://doi.org/10.3390/met8030178 SN - 2075-4701 VL - 8 IS - 3 SP - Article 178, 1 EP - 13 PB - MDPI AN - OPUS4-44460 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Huang, S. G. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias T1 - Effect of Ti(C0.7N0.3) content on the microstructure and mechanical properties of Ni bonded NbC-Ti(C0.7N0.3) based cermets N2 - In the present work it was shown that the addition of VC or a combination of VC + Ti(C0.7N0.3) was efficient in reducing the NbC grain growth during liquid phase sintering, when compared to NbC-Ni equivalents. A finest NbC grain size of 1.48 µm was obtained in the NbC-15 Ti(C0.7N0.3)-10 Ni-7.5 VC cermet, exhibiting a hardness of 1486 +/- 7 kg/mm2 and a fracture toughness of 8.7 +/- 0.1 MPa m 1/2. KW - Cermet KW - Niobium carbide KW - Carbonitride KW - Sintering KW - Mechanical properties PY - 2018 DO - https://doi.org/10.4028/www.scientific.net/SSP.274.43 SN - 1662-9779 VL - 274 SP - 43 EP - 52 PB - Trans Tech Publ. CY - Uetikon AN - OPUS4-44962 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Huang, S. G. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias T1 - Microstructure and mechanical properties of NbC matrix cermets using Ni containing metal binder N2 - The current study reports on the effect of the addition of Al metal and secondary refractory carbides on the microstructure and mechanical properties of Ni bonded NbC matrix cermets. KW - NbC KW - Niobium carbide KW - Hardness KW - Hard materials PY - 2016 DO - https://doi.org/10.1016/j.mprp.2016.05.009 VL - 71 IS - 5 SP - 349 EP - 355 PB - Elsevier Ltd. AN - OPUS4-44623 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. A1 - Vleugels, J. A1 - Huang, S. T1 - Potentials of niobium carbide (NBC) as cutting tools and for wear protection N2 - Niobium is today largely available. NbC displayed lower dry sliding friction over WC grades. The softer Ni- and NiMo-bonded NbC1.0-grades have a higer abrasive wear resistance (ASTM G65), even with lower toughnesses, than the tougher WC-Co grades and harder NbC-Co grades. T2 - 41st International Conference and Exposition on Advanced Ceramics and Composites CY - Daytona Beach, FL, USA DA - 22.01.2017 KW - Niobium Carbide (NbC) KW - Cutting tool KW - Hardness KW - Friction PY - 2017 VL - 38 SP - 1 EP - 13 AN - OPUS4-43430 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Huang, S. G. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias T1 - NbC grain growth control and mechanical properties of Ni bonded NbC cermets prepared by vacuum liquid phase sintering N2 - The current study reports on the effect of the sintering temperature and secondary carbide (VC, Mo2C and TiC) and Mo additions on the NbC grain growth, microstructure evolution as well as concomitant Vickers hardness (HV30) and fracture toughness of Ni-bonded NbC cermets. KW - Cermet KW - Niobium carbide KW - Sintering KW - Microstructure KW - Mechanical properties PY - 2018 DO - https://doi.org/10.1016/j.ijrmhm.2017.12.013 SN - 0263-4368 VL - 72 SP - 63 EP - 70 PB - Elsevier Science CY - Amsterdam AN - OPUS4-43582 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huang, S. A1 - Vleugels, J. A1 - Cannizza, E. A1 - Woydt, Mathias A1 - Liu, Z. A1 - Mohrbacher, H. T1 - Niobium carbide based cermets with secondary carbide and carbonitride addition N2 - In this study, the influence of Ni binder content and carbide/carbonitride additions on the microstructure and mechanical properties of NbC-Ni matrix cermets were investigated. T2 - WORLDPM2018 CY - Beijing, China DA - 16.09.2018 KW - Cermet KW - Niobium carbide KW - Carbonitride KW - Sintering KW - Mechanical properties PY - 2018 SP - Part 5, 801 EP - 809 AN - OPUS4-46201 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Huang, S. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Cannizza, E. T1 - Tailoring the functional profile of niobium carbide (NbC) as cutting tool materials and for wear protection N2 - In the present work it was shown that the properties of NbCx, like micro-hardness, hot-hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, the addition of secondary carbides and the type of binder. T2 - WORLDPM2018 CY - Beijing, China DA - 16.09.2018 KW - Niobium carbide KW - Properties KW - Wear KW - Machining PY - 2018 SP - Part 5, 785 EP - 795 AN - OPUS4-46204 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vleugels, J. A1 - Cannizza, E. A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - Influence of sintering temperature and carbide additions on the microstructure and mechanical properties of NbC-Ni based cermets N2 - This study reports on the effect of the sintering temperature and VC, Mo2C and TiC as well as the combination of Mo+VC on the densification, NbC grain growth, microstructure evolution as well as mechanical properties of novel NbC-Ni based cermets. KW - Cermet KW - Niobium carbide KW - Nickel KW - Sintering KW - Mechanical properties PY - 2018 DO - https://doi.org/10.3969/j.issn.1003-7292.2018.02.001 SN - 1003-7292 VL - 35 IS - 2 SP - 69 EP - 78 PB - Yingzhi Hejin Bianjibu CY - Zhuzhou AN - OPUS4-46136 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Huang, S.G. A1 - Vanmeensel, K. A1 - Mohrbacher, H. A1 - Woydt, Mathias A1 - Vleugels, J. T1 - Microstructure and mechanical porperties of NbC-matrix hardmetals with secondary carbide addition and different metal binders N2 - NbC has a relatively high hardness (19.6 GPa) and melting temperature (3600 °C) and is usually applied as a grain growth inhibitor in WC–Co hardmetals. The current study reports on the influence of the sintering technology and overall chemical composition on the microstructure and mechanical properties of NbC-based hardmetals, using Co as a binder. The partial replacement of NbC by 5 wt.% WC, Mo2C, VC or TiC allows one to significantly improve the hardness and toughness of the NbC–Co materials. The influence of different binders, i.e., Co, 316L stainless steel and Fe3Al on the microstructure and mechanical properties of NbC-based hardmetals was also investigated. The powder mixtures were sintered in the solid state by PECS and liquid state by conventional vacuum sintering. Detailed microstructural analysis was conducted by EPMA elemental mapping and WDS point analysis. Mechanical properties, including Vickers hardness and indentation toughness were assessed. KW - Niobium carbide KW - Sintering KW - Grain growth KW - Microstructure KW - Mechanical properties PY - 2015 DO - https://doi.org/10.1016/j.ijrmhm.2014.10.014 SN - 0263-4368 SN - 0958-0611 VL - 48 SP - 418 EP - 426 PB - Elsevier AN - OPUS4-31974 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scholz, Christian A1 - Woydt, Mathias A1 - Mohrbacher, H. ED - Mohrbacher, H. T1 - Slip-rolling resistance and load carrying capacity of 36NiCrMoV1-5-7 steel N2 - The approaching CO2 targets have now enforced automotive OEMs to engage R&D efforts also in powertrain to reduce friction, increase lifetime properties, and load carrying capacities of running systems. Martensitic steels such as 36NiCrMoV1-5-7 have a great potential to be used in automotive powertrain applications due to its favorable mechanical properties. In order to realize lightweight strategies, it is essential that steels with improved fracture toughness values and higher annealing temperatures with regard to higher contact pressures and possible thin film coating application be considered. State-of-the-art steels, like 16MnCr5, 21NiCrMo, 30CrMoV9, and 100Cr6 are not able to sustain a further increase in torque or load during operating time as well as annealing effects under higher oil or deposition temperatures. Therefore, the recent research on the slip-rolling resistance, frictional, and wear behavior of steels such as 36NiCrMoV1-5-7, Cronidur 30 (AMS 5898), 20MnCr5 (SAE 4820 or 5120), and 100Cr6H (SAE E52100) showed that possible lean alloying concept alternatives with promising performance characteristics are already available. T2 - 2nd International symposium on fundamentals and applications of Mo and Nb alloying in high performance steels CY - Jeju Island, South Korea DA - 24.04.2013 KW - Molybdenum KW - Steel KW - Slip-rolling resistance KW - High contact pressure KW - Oil PY - 2015 SN - 978-0-692-34620-4 DO - https://doi.org/10.1520/MPC20130022 SN - 2165-3992 VL - 2 SP - 191 EP - 203 AN - OPUS4-32668 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. ED - Gyekenyesi, A. ED - Halbig, M. T1 - Tribological background for the use of niobium carbide (NBC) as cutting tools and for wear resistant tribosystems N2 - The tribological profile of rotating disks made of binder-less niobium carbide (hot-pressed NbC) and cobalt-bonded NbC (NbC-8Co) mated against alumina (99.7%) were determined under unidirectional sliding tests (0.1 m/s to 8.0 m/s; 22°C and 400°C) as well as in oscillation tests (f= 20 Hz, Δx= 0.2 mm, 2/50/98% rel. humidity, n= 105/106 cycles) under un-lubricated (dry) conditions. In addition, the microstructure and mechanical properties of NbC and NbC bonded with 8% cobalt were determined as well. The tribological data obtained were benchmarked with different ceramics, cermets, hard metals and thermally sprayed coatings, where the NbC-8Co presented above 7 m/s the lowest wear rates so far in such a bench mark. NbC and NbC-8Co exhibited low wear rates under dry sliding associated with P·V high load carrying capacity. The tribological profile established revealed a strong position of NbC bearing materials under tribological considerations and for closed tribo-systems against traditional references. T2 - 38th International conference on advanced ceramics and composites CY - Daytona Beach, FL, USA DA - 26.01.2014 KW - Sliding friction KW - Wear KW - Ceramic KW - Oscillation KW - Coating KW - NbC KW - Niobium carbide KW - Cobalt KW - Hard metal PY - 2014 SP - Paper 1 EP - Paper 21 AN - OPUS4-32561 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - The use of niobium carbide (NbC) as cutting tools and for wear resistant tribosystems N2 - The tribological profile of alumina (99.7%) mated against rotating disks made in binder-less niobium carbide (NbC) and cobalt-bonded NbC were determined under unidirectional sliding tests (0.1 m/s to 8.0 m/s; 22 °C and 400 °C) as well as in oscillation tests (f = 20 Hz, Δx = 0.2 mm, 2/50/98% rel. humidity, n = 105/106 cycles) under unlubricated (dry) conditions. In addition, the microstructure and mechanical properties of binderless NbC and NbC bonded with 8% cobalt were determined as well. The reason for testing hot-pressed NbC was to avoid side effects generated by sintering additives and/or second phases. The tribological data obtained were benchmarked with different ceramics, cermets and thermally sprayed coatings. NbC and cobalt-bonded NbC exhibited low wear rates under dry sliding associated with high load carrying capacity. The tribological profile established revealed a strong position of NbC bearing materials under tribological considerations and for closed tribo-systems against traditional references, such as WC, Cr3C2 and (Ti,Mo)(C,N). KW - Sliding friction KW - Sliding wear KW - Ceramic KW - Oscillation KW - Coating KW - NbC KW - Niobium carbide KW - Hard metal KW - Cobalt PY - 2015 DO - https://doi.org/10.1016/j.ijrmhm.2014.07.002 SN - 0263-4368 SN - 0958-0611 VL - 49 SP - 212 EP - 218 PB - Elsevier AN - OPUS4-32896 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - Niobcarbid - Ein vergessener Hartstoff für den Verschleißschutz in offenen und geschlossenen Tribosystemen N2 - Das triboiogische Profil von binderlosem NbC und mit 8% bzw. mit 12% Cobalt oder 12% FeaAl gebundenem NbC wird unter unidirektionaler Gleitreibung (v= 0,1-10 m/s, T= 22°C und 400°C) und unter oszillierender Gleitreibung vergleichend gegenüber Ingenieurkeramiken und Hartmetallen dargestellt. Zusätzlich werden die 4-Punkt-Biegebruchfestigkeit, elastische Eigenschaften (E,G) bis 1.000°C die lastabhängige Mikrohärte sowie die Phasenzusammensetzung und Gefügestrukturen vorgestellt. Die Verschleißkoeffizienten des binderlosen NbC lagen bei T unterhalb von 10'6mm31 / *N* m, während diejenigen der cobaltgebundenen NbCs mit ansteigender Gleitgeschwindigkeit von 2-4 10‘6 mm3/Nm bei 0,1 m/s auf 5-7 10"7 mm3/Nm bei 10 m/s abnahmen. Die Verschleißkoeffizienten bei 400°C lagen für die NbCs generell unterhalb von 10‘6 mm3/Nm. Das triboiogische Lasttragevermögen im Trockenlauf, ausgedrückt als PV-Wert, nimmt mit ansteigender Gleitgeschwindigkeit auf 100 W/mm2 zu. Bedingt durch die geringe Löslichkeit von NbC in Legierungen offenbarten erste Zerspanversuche mit verschiedenen Stählen eine gegenüber WC-basierten Schneidstoffen signifikant angehobene Zerspanungsvolumina. Somit offenbart NbC in offenen und geschlossenen Tribosystemen Anwendungspotentiale. T2 - 55. Tribologie-Fachtagung - Reibung, Schmierung und Verschleiß - Forschung und praktische Anwendungen CY - Göttingen, Germany DA - 22.09.2014 PY - 2014 SN - 978-3-00-046545-1 VL - II SP - 03/1 EP - 03/14 AN - OPUS4-31531 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Huang, S. G. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias T1 - Microstructure and tribological performance of NbC-Ni cermets modified by VC and Mo2C N2 - The current study reports on the influence of the Addition of 5–15 vol% VC or/and Mo2C carbide on the microstructure and mechanical properties of nickel bonded NbC cermets, which are compared to cobalt bonded NbC cermets. The NbC, Ni and secondary carbides powder mixtures were liquid phase sintered for 1 h at 1420 °C in vacuum. The fully densified cermets are composed of a cubic NbC grains matrix and an evenly distributed fcc Ni binder. NbC grain growth was significantly inhibited and a homogeneous NbC grain size distribution was obtained in the cermets with VC/Mo2C additions. The mechanical properties of the NbC-Ni matrix cermets are strongly dependent on the carbide and Ni binder content and are directly compared to their NbC-Co equivalents. The liquid phase sintered NbC-12 vol% Ni cermet had a modest Vickers hardness (HV30) of 1077 ± 22 kg/mm2 and an indentation toughness of 9.1 ± 0.5 MPa·m1/2. With the addition of 10–15 vol% VC, the hardness increased to 1359 ± 15 kg/mm2, whereas the toughness increased to 11.3 ± 0.1 MPa·m1/2. Addition of 5 and 10 vol% Mo2C into a NbC-12 vol% Ni mixtures generated the same values in HV30 and KIC when compared to VC additions. A maximum flexural strength of 1899 ± 77 MPa was obtained in the cermet with 20 vol% Ni binder and 4 vol% VC+4 vol% Mo2C addition, exhibiting a high fracture toughness of 15.0 ± 0.5 MPa·m1/2, but associated with a loss in hardness due to the high Ni content. The dry sliding wear behaviour was established at room temperature and 400 °C from 0.1 to 10 m/s. KW - Cermet KW - Liquid phase sintering KW - Grain growth KW - Wear KW - Niobium carbide PY - 2017 DO - https://doi.org/10.1016/j.ijrmhm.2017.03.012 SN - 0263-4368 VL - 66 SP - 188 EP - 197 AN - OPUS4-40505 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias A1 - Mohrbacher, H. A1 - Vleugels, J. A1 - Huang, S. T1 - Niobium carbide for wear protection - tailoring its properties by processing and stoichiometry N2 - Niobium carbide is a hardly explored carbide but its functional profile shows a high potential for wear protection and tribological applications, which are currently dominated by tungsten carbide. Surprisingly little information is available on niobium carbide (NbC). Niobium carbide can be either synthesized by carbothermal conversion of Nb2O5 or be metallurgically grown and leached out. Furthermore, NbC hardmetal grades can be bonded by all known metallic binders and processed and sintered in exactly the same way as WC-based hardmetals. Niobium is today largely available. NbC can be efficiently produced, provides comparably low friction in many relevant tribo-contacts and displays low wear. NbC and Nb2O5 have so far no REACH classification related to human toxicology and are not listed as substances of very high concern contrary to WO3 and Co3O4. This contribution demonstrates the key characteristics of NbC and discusses its sustainability and reliable value chain. KW - niobium carbide KW - wear KW - machining PY - 2016 DO - https://doi.org/10.1016/j.mprp.2015.12.010 SN - 0026-0657 VL - 71 IS - 4 SP - 265 EP - 272 PB - Elsevier Ltd. AN - OPUS4-37150 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huang, S. G. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias T1 - Influence of VC and Mo2C on the microstructure and mechanical properties of Ni bonded NbC-cermets N2 - The current study reports on the effect of VC and Mo2C carbides on the microstructure and mechanical properties of Ni bonded NbC cermets. T2 - World PM2016 CY - Hamburg, Germany DA - 09.10.2016 KW - Niobium carbide KW - NbC KW - Liquid phase sintering (LPS) KW - Hard materials PY - 2016 SN - ISBN 978-1-899072-47-7 SP - 1 EP - 7 AN - OPUS4-37891 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - Niobcarbid - Ein vergessener Hartstoff für den Verschleißschutz in offenen und geschlossenen Tribosystemen N2 - Das tribologische Profil von binderlosem NbC und mit 8% bzw. mit 12% Cobalt oder 12% Fe3Al gebundenem NbC wird unter unidirektionaler Gleitreibung (v= 0,1-10 m/s, T= 22°C und 400°C) und unter oszillierender Gleitreibung vergleichend gegenüber Ingenieurkeramiken und Hartmetallen dargestellt. Zusätzlich werden die 4-Punkt-Biegebruchfestigkeit, elastische Eigenschaften (E,G) bis 1.000�C die lastabhängige Mikrohärte sowie die Phasenzusammensetzung und Gefügestrukturen vorgestellt. Die Verschleißkoeffizienten des binderlosen NbC lagen bei T unterhalb von 10-6 mm³/N?m, während diejenigen der cobaltgebundenen NbCs mit ansteigender Gleitgeschwindigkeit von 2-4 10-6 mm³/N?m bei 0,1 m/s auf 5-7 10-7 mm³/N.m bei 10 m/s abnahmen. Die Verschleißkoeffizienten bei 400°C lagen für die NbCs generell unterhalb von 10-6 mm³/N.m. Das tribologische Lasttragevermögen im Trockenlauf, ausgedrückt als PV-Wert, nimmt mit ansteigender Gleitgeschwindigkeit auf 100 W/mm² zu. Bedingt durch die geringe Löslichkeit von NbC in Legierungen offenbarten erste Zerspanversuche mit verschiedenen Stählen eine gegenüber WC-basierten Schneidstoffen signifikant angehobene Zerspanungsvolumina. Somit offenbart NbC in offenen und geschlossenen Tribosystemen Anwendungspotentiale. KW - Gleiten KW - Reibung KW - Verschleiß KW - Oszillation KW - NbC KW - Niobcarbid KW - Cobalt KW - Fe3Al KW - Hartmetall KW - Festigkeit KW - Hohe Temperaturen KW - Sliding KW - Friction KW - Wear KW - Oscillation KW - Niobium carbide KW - Hard metal KW - Strength KW - Modulus KW - High temperatures PY - 2015 SN - 0724-3472 VL - 62 IS - 3 SP - 5 EP - 13 PB - Expert Verlag CY - Renningen AN - OPUS4-33493 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Huang, S. G. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias T1 - Densification and tribological profile of niobium oxide N2 - The origin of the intrinsic wear resistance of NbC-based materials is investigated through an assessment of the tribological performance of fully dense, crack-free spark plasma sintered Nb2O5 (here as a reduced polymorph: monoclinic Nb12O29 or NbO2.416). The most likely wear mechanism on NbC is the tribo-oxidation to Nb2O5. The unlubricated (dry) friction and wear behavior of alumina (99.7%) mated against rotating disks of crack-free niobium(V)oxide (Nb2O5) under unidirectional sliding (0.03–10m/s; 22°C and 400°C) and oscillation (f=20 Hz, dx=200 mm, 2/50/98% rel. humidity, n=105/106 cycles) will be presented. The microstructure and mechanical properties of the crack-free Nb2O5 are assessed. The tribological data obtained are benchmarked with different NbC grades, ceramics, cermets and thermally sprayed coatings. KW - Friction KW - Wear KW - Nb2O5 KW - Nb12O29 KW - Niobium oxide KW - Strength KW - Modulus KW - High temperatures PY - 2016 DO - https://doi.org/10.1016/j.wear.2016.02.003 SN - 0043-1648 VL - 352-353 SP - 65 EP - 71 PB - Elsevier B.V. AN - OPUS4-35805 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huang, S. G. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias T1 - NbC grain growth control and mechanical properties of Ni bonded NbC cermets prepared by vacuum liquid phase sintering N2 - The current study reports on the effect of the sintering temperature and secondary carbide (VC, Mo2C and TiC) additions on the microstructure and concommitant Vickers hardness (HV30) and fracture toughness of Ni-bonded NbC cermets. All cermets were prepared by pressureless sintering in vacuum. Detailed microstructural investigation was performed by electron probe microanalysis (EPMA) and X-ray diffraction (XRD) analysis. Sintering results indicated that both the sintering temperature and secondary carbide additions had a significant effect on the properties of NbC-Ni cermets. Nickel pools and residual pores were observed in the cermets sintered at temperatures ≤ 1340 °C. Increasing of the sintering temperature up to 1420 or 1480 °C resulted in fully densified NbC-Ni based cermets composed of homogeneous contrast cubic NbC grains for the single carbide (VC or Mo2C) modyfied system, whereas core-rim structured NbC grains were observed with the additon of TiC + VC or TiC+Mo2C. The secondary carbide doped cermets with 5–10 vol.% VC/Mo2C and 10 vol.% TiC showed a significantly improved hardness and fracture toughness, as compared to the plain NbC-Ni cermets. T2 - 19. Plansee Seminar CY - Reutte, Austria DA - 29.05.2017 KW - Cermet KW - Hard materials KW - Sintering KW - Microstructure KW - Core-rim KW - Mechanical properties PY - 2017 SP - HM 13/1 EP - HM 13/11 AN - OPUS4-40592 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. A1 - Vleugels, J. A1 - Huang, S. T1 - Potentials of niobium carbide (NbC) as cutting tools and for wear protection N2 - The tool lifes of uncoated NiMo and NiMo2C-bonded stoichiometric NbC1.0 grades under dry turning 42CrMo4 and C45E were between +30 % to + 100 % higher and up compared to WC-6Co (fine grain). Niobium is today largely available. NbC grades displayed lower dry sliding friction over WC grades. T2 - 19. Plansee Seminar CY - Reutte, Austria DA - 29.05.2017 KW - Niobium carbide KW - Friction KW - Wear KW - NbC KW - Hard metal KW - Machining KW - Nickel PY - 2017 SP - HM 102/1 EP - HM 102/16 AN - OPUS4-40593 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huang, S. G. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias T1 - Effect of carbon content on the microstructure and mechanical properties of NbC-Ni based cermets N2 - The aim of this work was to correlate the carbon content in NbC-Ni starting powders with the resulting microstructure, hardness and fracture toughness of Ni-bonded NbC cermets. T2 - 19. Plansee Seminar CY - Reutte, Austria DA - 29.05.2017 KW - Cermet KW - Liquid phase sintering KW - Microstructure KW - Hardness KW - Carbon PY - 2017 SP - HM 109/1 EP - HM 109/11 AN - OPUS4-40595 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. A1 - Vleugels, J. A1 - Huang, S. T1 - Status of nickel bonded niobium carbide (NbC) as a substitute for cobalt-bonded tungsten carbide (WC) as cutting tools and for wear protection N2 - Niobium is today largely available. The initial NbC grade was substoichiometric, SPS sintered and cobalt bonded (NbC0.88-12Co SPS). The NiMo-bonded stoichiometric NbC1.0 grades enable the subtituion of cobalt by nickel, SPS by conventional sintering and NbC0.88 by NbC1.0 in view of functional properties. Nickel bonded NbC grades have improved toughnesses versus cobalt bonded NbC grades, but lose hardness. NiMo and NiMo2C bonded NbC1.0 grades compensated the loss in hardness while keeping the toughness. T2 - POWDERMET 2017 CY - Las Vegas, USA DA - 13.06.2017 KW - Niobium carbide (NbC) KW - Cutting tools KW - Wear PY - 2017 SP - 721 EP - 734 PB - Metal Powder Industries Federation AN - OPUS4-40671 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - Friction and wear of binder-less niobium carbide N2 - The tribological profile of alumina (99.7%) mated against binder-less niobium carbide (NbC) rotating disks were determined unidirectional sliding tests (0.1–7.5 m/s; 22 °C and 400 °C) as well as in oscillation tests (f=20 Hz, Δx=0.2 mm, 2/50/98% rel. humidity, n=105/106 cycles) under un-lubricated (dry) conditions. In addition, the microstructure and mechanical properties of NbC were determined as well. The reason for testing hot-pressed NbC was to avoid side effects generated by sintering additives and/or second phases. The tribological data obtained were benchmarked with different ceramics, cermets and thermally sprayed coatings. NbC exhibited low wear rates under dry sliding associated with high load carrying capacity. The tribological profile established revealed a strong position of NbC under tribological considerations and for closed tribo-systems against traditional references, such as WC, Cr3C2, (Ti,Mo)(C,N), etc. KW - Sliding friction KW - Sliding wear KW - Ceramic KW - Coating KW - NbC PY - 2013 DO - https://doi.org/10.1016/j.wear.2013.07.013 SN - 0043-1648 VL - 306 IS - 1-2 SP - 126 EP - 130 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-28985 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - Tribological profile of binderless niobium carbide N2 - The tribological profile of alumina (99,7%) mated against binderless niobium Carbide (NbC) rotating disks under under unlubricated (dry) friction and the type of motions of unidirectional sliding (0.1 m/s to 7.5 m/s; 22°C and 400°C) and oscillation (f= 20 Hz, Ax= 200 mm, 2/50/98% rel. humidity, n= 105/106 cycles) was determined including the microstructure and mechanical properties. The obtained tribological data were benchmarked with different ceramics, cermets and thermally sprayed coatings. The established tribological profile revealed a strong position of NbC under tribological considerations and for closed tribosystems against traditional references, like WC, Ci‘3C2, (Ti,Mo)(C,N), etc.. T2 - 37th International Conference on Advanced Ceramics and Composites CY - Daytona Beach, FL, USA DA - 27.01.2013 PY - 2013 SN - 978-1-118-83995-9 SP - Datei 01/20 reviewed, 5 pages PB - Wiley AN - OPUS4-29461 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias A1 - Huang, S. A1 - Cannizza, E. A1 - Vleugels, J. A1 - Mohrbacher, H. T1 - Niobium carbide for machining and wear protection - Evolution of properties N2 - The sales of niobium carbide (NbC) have grown in the last years, but NbC is still a hidden carbide and mainly used as grain growth inhibitor in hard metals. In the present work it was shown that the progress in the key properties, like HV30, KIC and strength, followed by machining and tribological results of the respective NbC grades. KW - Niobium carbide KW - Hard metals KW - Tribology PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-485507 DO - https://doi.org/10.1016/j.mprp.2019.02.002 SN - 0026-0657 VL - 74 IS - 2 SP - 82 EP - 89 PB - Elsevier Ltd. AN - OPUS4-48550 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -