TY - CONF A1 - Behrens, H. A1 - Bauer, Ute A1 - Reinsch, Stefan A1 - Müller, Ralf A1 - Morin, E. I. A1 - Stebbins, J. F. A1 - Kiefer, P. A1 - Deubener, J. T1 - Effect of water on structure and dynamics of sodium borosilicate glasses N2 - Borosilicate glass has a wide range of technical applications due to its high chemical durability and thermal-shock resistivity. Here the effect of H2O on 16 Na2O, 10 B2O3,74 SiO2 glass is studied over a wide range of water contents from 0 to 8 wt.%. MIR spectra give evidence for the coexistence of strongly and weakly H-bonded hydrous species. Evaluation of NIR bands at 5200 cm-1 (molecular H2O), 4700 cm-1 (B-OH), and 4500 cm-1 (Si-OH) reveal that OH groups dominate up to ~6 wt.% H2O, with B-OH/Si-OH of ≈ 0.8. The incorporation of low amounts of H2O has strong impact on structure. NMR spectra of nominally dry glasses indicate a significant fraction (12 %) of 3-coordinated boron, but almost all boron is 4-coordinated after addition of 3 wt.% H2O. Raman spectra show that hydration results preferentially in transformation of Q4 to Q2 while Q3 remain unchanged, probably stabilized by bonding to BO4 tetrahedra. Viscosity measurements and differential thermal analysis give consistent results, confirming strong decrease of the glass transition temperature with addition of water from 849 K (dry) to 540 K (5 wt% H2O). An additional relaxation mechanism in hydrous glasses is inferred from dynamic mechanical analysis and is assigned to cooperative processes involving hydrous species. It is postulated that this relaxation mechanism plays an important role in crack growth kinetics. T2 - 9th International Conference on Borate Glasses, Crystals and Melts CY - Oxford, UK DA - 24.07.2017 KW - Borosilicate glass KW - Water speciation KW - Sub-Tg relaxation KW - High water bearing glass PY - 2017 AN - OPUS4-44355 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Behrens, H. A1 - Bauer, Ute A1 - Reinsch, Stefan A1 - Müller, Ralf A1 - Morin, E. I. A1 - Stebbins, J. F. A1 - Kiefer, P. A1 - Deubener, J. T1 - Effect of water on structure and dynamics of sodium borosilicate glasses N2 - Borosilicate glass has a wide range of technical applications due to its high chemical durability and thermal-shock resistivity. Here the effect of H2O on 16 Na2O, 10 B2O3,74 SiO2 glass is studied over a wide range of water contents from 0 to 8 wt.%. MIR spectra give evidence for the coexistence of strongly and weakly H-bonded hydrous species. Evaluation of NIR bands at 5200 cm-1 (molecular H2O), 4700 cm-1 (B-OH), and 4500 cm-1 (Si-OH) reveal that OH groups dominate up to ~6 wt.% H2O, with B-OH/Si-OH of ≈ 0.8. The incorporation of low amounts of H2O has strong impact on structure. NMR spectra of nominally dry glasses indicate a significant fraction (12 %) of 3-coordinated boron, but almost all boron is 4-coordinated after addition of 3 wt.% H2O. Raman spectra show that hydration results preferentially in transformation of Q4 to Q2 while Q3 remain unchanged, probably stabilized by bonding to BO4 tetrahedra. Viscosity measurements and differential thermal analysis give consistent results, confirming strong decrease of the glass transition temperature with addition of water from 849 K (dry) to 540 K (5 wt% H2O). An additional relaxation mechanism in hydrous glasses is inferred from dynamic mechanical analysis and is assigned to cooperative processes involving hydrous species. It is postulated that this relaxation mechanism plays an important role in crack growth kinetics. T2 - 12th Pacific Rim Conference on Ceramic and Glass Technology including Glass & Optical Materials Division Meeting CY - Waikoloa, USA DA - 21.05.2017 KW - Borosilicate glass KW - Water speciation KW - Sub-Tg relaxation KW - High water bearing glass PY - 2017 AN - OPUS4-44383 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Behrens, H. A1 - Bauer, U. A1 - Reinsch, Stefan A1 - Kiefer, P. A1 - Müller, Ralf A1 - Deubener, J. T1 - Structural relaxation mechanisms in hydrous sodium borosilicate glasses JF - Journal of Non-Crystalline Solids N2 - Borosilicate glasses (16Na2O–10B2O3–74SiO2, NBS) with water contents up to 22 mol% H2O were prepared to study the effect of water on structural relaxation using DTA, viscometry and internal friction measurements. The results show that the glass transition temperature Tg of DTA and the isokom temperature T12, of viscometry are in excellent agreement, confirming the equivalence of enthalpy and viscous relaxation for NBS glass. Combining Tg data with water speciation data demonstrates that OH groups are mainly responsible for the decrease of Tg with increasing hydration, while molecular water plays only a minor role. Internal friction spectra at 7.125 Hz confirm the decisive influence of water on mechanical relaxation. The temperature range of α-relaxation (glass transition) strongly decreases while two β-relaxation peaks (sub-Tg) progressively appear with increasing water content. A high temperature β-relaxation peak, attributed to the presence of OH groups, shifts from 670 to 450 K as total water content increases from 0.01 to 5 wt%. A low temperature β-relaxation peak, attributed to molecular water, appears at 380 K and 330 K in glasses containing 3 and 5 wt% H2O, respectively. These findings suggest that relaxation mechanism of different hydrous species at low temperature may contribute to fatigue of stressed glasses. KW - Borosilicate glass KW - Water KW - Relaxation KW - Internal friction KW - Glass transition PY - 2018 DO - https://doi.org/10.1016/j.jnoncrysol.2018.05.025 VL - 497 SP - 30 EP - 39 PB - Elsevier B.V. AN - OPUS4-45608 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -