TY - JOUR A1 - Omar, Hassan A1 - Ahamadi, Shayan A1 - Hülagü, Deniz A1 - Hidde, Gundula A1 - Hertwig, Andreas A1 - Szymoniak, Paulina A1 - Schönhals, Andreas T1 - Investigations of the adsorbed layer of polysulfone: Influence of the thickness of the adsorbed layer on the glass transition of thin films N2 - This work studies the influence of the adsorbed layer on the glass transition of thin films of polysulfone. Therefore, the growth kinetics of the irreversibly adsorbed layer of polysulfone on silicon substrates was first investigated using the solvent leaching approach, and the thickness of the remaining layer was measured with atomic force microscopy. Annealing conditions before leaching were varied in temperature and time (0–336 h). The growth kinetics showed three distinct regions: a pre-growth step where it was assumed that phenyl rings align parallel to the substrate at the shortest annealing times, a linear growth region, and a crossover from linear to logarithmic growth observed at higher temperatures for the longest annealing times. No signs of desorption were observed, pointing to the formation of a strongly adsorbed layer. Second, the glass transition of thin polysulfone films was studied in dependence on the film thickness using spectroscopic ellipsometry. Three annealing conditions were compared: two with only a tightly bound layer formed in the linear growth regime and one with both tightly bound and loosely adsorbed layers formed in the logarithmic growth regime. The onset thickness and increase in the glass transition temperature increases with annealing time and temperature. These differences were attributed to the distinct conformations of the formed adsorbed layers. KW - Glass transition KW - Adsorbed Layer PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-607701 DO - https://doi.org/10.1063/5.0223415 SN - 0021-9606 VL - 161 IS - 5 SP - 1 EP - 12 PB - AIP Publishing AN - OPUS4-60770 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - An, Q. A1 - Bäßler, Ralph A1 - Hertwig, Andreas A1 - Rehfeldt, Rainer A1 - Hidde, Gundula A1 - Otremba, Frank T1 - Investigation of Mechanical Stress and B10 Exposure on FKM Polymer N2 - Mechanical stress often accelerates the failure of polymer materials. The aim of this research is to study the interaction between the sealing material FKM and biofuels B10 (heating oil with 10% biodiesel). The mechanical stress test was carried out in a special apparatus. Both mechanical and non-mechanical stress tests were conducted on specimens at 20, 40, and 70 °C for 28 days to document changes in mass, volume, and tensile properties. Both increasing temperature and mechanical stress have a significant effect on the tensile strength of the FKM polymer when exposed to B10. The combination of increasing temperature and mechanical stress induced rupture within 2 h. It was also established that FKM polymer with pre-exposure in B10 survived longer during mechanical stress compared to specimens exposed only to air. With the support of infrared (IR) spectroscopy, we were able to confirm the penetration of B10 into the FKM polymer. T2 - TMS 2024 Annual Meeting & Exhibition Teilnahme mit Präsentation CY - Orlando-Florida / USA DA - 03.03.2024 KW - Biofuels KW - Sealing materials KW - Mechanical stress KW - Change in tensile properties PY - 2024 SN - 978-3-031-50349-8 DO - https://doi.org/10.1007/978-3-031-50349-8_108 SP - 1253 EP - 1261 PB - Springer CY - Orlando-Florida / USA AN - OPUS4-59638 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Otremba, Frank A1 - An, Q. A1 - Bäßler, Ralph A1 - Hertwig, Andreas A1 - Rehfeldt, Rainer A1 - Hidde, Gundula T1 - Investigation of mechanical stress and B10 exposure on FKM polymer N2 - Biofuels, particularly biodiesel, have gained significant attention as an alternative to traditional fossil fuels in recent years. Unlike diesel, which contains hundreds of compounds, biodiesel only contains a few compounds in the C16-C18 carbon chain. However, the use of biodiesel in automobile and transportation applications can result in problems of degradation or even damage in materials. Among the commonly used polymer materials, fluorocarbon (FKM) shows excellent performance and high stability and compatibility towards oil, diesel, ethanol, and other chemicals. FKM is a family of fluorocarbon-based fluoroelastomer materials, which provide excellent high-temperature and chemical stability compared to other elastomers. As a result, FKM is widely used in chemical processes such as petroleum refining, where it is used for sealings, pumps, and other components. T2 - TMS 2024 153rd Annual Meeting & Exhibition Supplemental Proceedings CY - Orlando, Florida, USA DA - 03.03.2024 KW - B10 exposure KW - FKM polymer PY - 2024 AN - OPUS4-59636 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -