TY - JOUR A1 - Wäsche, Rolf A1 - Brandt, Guido A1 - Ehrke, Roman A1 - Nolze, Gert A1 - Schmid, Thomas A1 - Sasaki, S. A1 - Woydt, Mathias T1 - Wear behaviour of alpha-alumina in hot steam at high contact pressure N2 - The work examines the wear behaviour of α-aluminium oxide by combining thermodynamic modelling with advanced wear testing as well as analytical methods to get a better understanding of this structural ceramic material wear behavior and its possible use in high temperature steam environment. KW - Aluminium oxide KW - Temperature KW - Hot steam KW - Diaspore KW - Ceramic KW - Wear PY - 2018 U6 - https://doi.org/10.1016/j.wear.2018.02.012 SN - 0043-1648 SN - 1873-2577 VL - 404-405 SP - 22 EP - 30 PB - Elsevier B.V. AN - OPUS4-44449 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Genga, R. M. A1 - Rokebrand, P. A1 - Cornish, L. A. A1 - Nelwalani, N. A1 - Brandt, Guido A1 - Kelling, Norbert A1 - Woydt, Mathias A1 - Janse van Vuuren, A. A1 - Polese, C. T1 - High-temperature sliding wear, elastic modulus and transverse rupture strength of Ni bonded NbC and WC cermets N2 - The effects of rapid pulse electric current sintering (PECS), substitution of WC by NbC and Co by Ni, and carbide additives (TiC and Mo2C) on the microstructure, elastic modulus, B3B transverse rupture strength (TRS) and high temperature sliding wear on WC-Co, WC-Ni, NbC-Co and NbC-Ni cermets were studied. High temperature sliding wear tests were carried out using a ball-on-disk tribometer, with a 10 N force, at a sliding speed of 1.34 m/s for 0.8 km (10 min) and 2.4 km (30 min), using 100Cr6 (AISI 52100) steel balls at 400 °C and 0% humidity. Additions of TiC and Mo2C to NbC-12Ni improved the sliding wear resistance, with TiC having the greater effect, reducing the sample wear rate by over 30% from 15.1×10−6mm3/N·m to 9.4×10−6mm3/N·m after sliding distance of 2.4 km. Generally, the LPS samples had lower wear volumes than the corresponding SPS samples, due to higher K1c and TRS. KW - Pulse electric current sintering KW - Niobium carbide KW - Nickel KW - Molybdenum carbide KW - Titanium carbide PY - 2020 U6 - https://doi.org/10.1016/j.ijrmhm.2019.105143 SN - 0263-4368 VL - 87 SP - 105143 PB - Elsevier Ltd. AN - OPUS4-51473 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wäsche, Rolf A1 - Jayachandran, Ashok Raj A1 - Brandt, Guido A1 - Schmid, Thomas A1 - Tamura, T. A1 - Nakase, T. T1 - Tribofilm formation of a-C:H coatings under influence of temperature in boundary lubricated oscillating sliding against alumina and silicon nitride N2 - Gegenstand dieses Beitrags ist der Einfluss von Temperatur und Gegenkörperwerkstoff auf die Bildung von Tribofilmen auf a-C:H Beschichtungen. Dies wurde mit einer Kugel-Ebene Anordnung im geschmierten Kontakt untersucht. KW - a-C:H KW - Temperature KW - Tribofilm KW - Lubricated sliding KW - Alumina KW - Silicon nitride PY - 2018 SN - 0724-3472 VL - 65 IS - 5 SP - 28 EP - 37 PB - expert Verlag CY - Tübingen AN - OPUS4-46034 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wäsche, Rolf A1 - Sato, K. A1 - Brandt, Guido A1 - Schmid, Thomas A1 - Sasaki, S. A1 - Woydt, Mathias T1 - Wear behaviour of MgO stabilized zirconia in hot steam environment up to 400°C N2 - Self-mated magnesia stabilized zirconia (Mg-PSZ) ceramic sliding couples have been investigated at 100 N load (P0max= 1324 MPa) in oscillating sliding conditions in different humidity conditions in air and in hot steam. Temperatures have been varied up to 400 °C and pressures up to 6 bars. The results show that the wear behavior of MgO-ZrO2 under high Hertzian contact pressures is strongly dependent on temperature and is similar for both dry oscillating and oscillating in hot steam. However, although the evolution in wear rates on temperature is similar and the wear rates of MgO-ZrO2 plunged above 300 °C in hot steam and air by nearly three orders of magnitude, SEM micrographs revealed in hot steam at 400 °C smooth wear tracks. In contrast, hot steam enhanced the tribochemistry of self-mated alumina couples and reduced wear rates. Hot steam decreased the coefficients of friction of MgO-ZrO2 with increasing temperature, but not the wear rates. KW - Hot steam KW - Zirconia KW - Friction KW - Wear KW - Tribofilm KW - Raman spectroscopy PY - 2019 U6 - https://doi.org/10.1016/j.wear.2019.01.047 VL - 426-427 SP - 428 EP - 432 PB - Elsevier B.V. AN - OPUS4-47873 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -