TY - JOUR A1 - Sut, Aleksandra A1 - Greiser, Sebastian A1 - Jäger, Christian A1 - Schartel, Bernhard T1 - Synergy in flame-retarded epoxy resin - Identification of chemical interactions by solid-state NMR JF - Journal of Thermal Analysis and Calorimetry N2 - The potential synergists aluminium diethylphosphinate (AlPi), boehmite (AlO(OH)) and melamine polyphosphate (MPP) were compared in flame-retardant epoxy resin (EP)/melamine poly(magnesium phosphate) (S600). The pyrolysis, the fire behaviour as well as the chemical interactions in the gas and condensed phases were investigated by various methods. Flammability was investigated by cone calorimeter and oxygen index (OI). The thermal and thermo-oxidative decomposition were studied by thermogravimetric analysis coupled with FTIR spectrometer. The special focus was on the Investigation of structural changes in the condensed phase via solid-state NMR of 27Al and 31P nuclei. By the comparison of epoxy resin with only one additive or with S600 in combination with AlPi, AlO(OH) or MPP, it was possible to calculate the synergy index. The best performance in terms of fire behaviour was observed for EP/S600/MPP with a PHRR (Peak heat release rate) of 208 kW m-2 due to slight synergy. In the case of THE (total heat evolved), clear synergy occurred for EP/S600/AlPi and EP/S600/AlO(OH). By solid-state NMR, different phosphates and aluminates were identified, indicating the chemical interactions between S600 and AlPi, AlO(OH) or MPP. The systematic multi-methodical approach yielded insight into the synergistic effects in the flame-retarded epoxy resin. KW - Synergy KW - Epoxy resin KW - Flame retardancy KW - Melamine poly(magnesium phosphate) KW - Solid-state NMR PY - 2017 DO - https://doi.org/10.1007/s10973-016-5934-4 SN - 1388-6150 SN - 1588-2926 VL - 128 IS - 1 SP - 141 EP - 153 PB - Springer AN - OPUS4-39298 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Langfeld, Kirsten A1 - Wilke, Antje A1 - Sut, Aleksandra A1 - Greiser, Sebastian A1 - Ulmer, B. A1 - Andrievici, V. A1 - Limbach, P. A1 - Bastian, Martin A1 - Schartel, Bernhard T1 - Halogen-free fire retardant styrene-ethylene-butylene-styrene-based thermoplastic elastomers using synergistic aluminium diethylphosphinate-based combinations JF - Journal of fire sciences N2 - Multicomponent flame retardant systems containing aluminum diethylphosphinate in thermoplastic styrene–ethylene–butylene–styrene elastomers are investigated (oxygen index, UL 94, cone calorimeter, and mechanical testing). Solid-state nuclear magnetic resonance, scanning electron microscopy, and elemental analysis illuminate the interactions in the condensed phase. Thermoplastic styrene–ethylene–butylene–styrene elastomers are a challenge for flame retardancy (peak heat release rate at 50 kW m-2 > 2000 kW m-2, oxygen index = 17.2 vol%, no UL-94 horizontal burn rating) since it burns without residue and with a very high effective heat of combustion. Adding aluminum diethylphosphinate results in efficient flame inhibition and improves the reaction to small flame, but it is less effective in the cone calorimeter. Its efficacy levels off for amounts >~25 wt%. As the most promising synergistic system, aluminum diethylphosphinate/melamine polyphosphate was identified, combining the main gas action of aluminum diethylphosphinate with condensed phase mechanisms. The protection layer was further improved with several adjuvants. Keeping the overall flame retardant content at 30 wt%, aluminum diethylphosphinate/melamine polyphosphate/titanium dioxide and aluminum diethylphosphinate/melamine polyphosphate/boehmite were the best approaches. An oxygen index of up to 27 vol% was achieved and a horizontal burn rating in UL 94 with immediate self-extinction; peak heat release rate decreased by up to 85% compared to thermoplastic styrene–ethylene–butylene–styrene elastomers, to <300 kW m-2. KW - Flame retardancy KW - Aluminium phosphinate KW - Thermoplastic elastomers KW - Cone calorimetry KW - Flammability PY - 2015 DO - https://doi.org/10.1177/0734904114565581 SN - 0734-9041 SN - 1530-8049 VL - 33 IS - 2 SP - 157 EP - 177 PB - Sage CY - London AN - OPUS4-32692 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sut, Aleksandra A1 - Greiser, Sebastian A1 - Jäger, Christian A1 - Schartel, Bernhard T1 - Interactions in multicomponent flame-retardant polymers: Solid-state NMR identifying the chemistry behind it JF - Polymer degradation and stability N2 - Distinct approaches are used to reduce the fire risks of polymers, a key issue for many industrial applications. Among the variety of approaches, the use of synergy in halogen-free multicomponent systems is one of the most auspicious. To optimize the composition of such flame-retardant systems it is essential to understand the mechanisms and the corresponding chemistry in the condensed phase. In this work different methods are used, including cone calorimeter, thermogravimetry (TG), and TG-FTIR, with the main focus on the solid-state NMR analysis of the solid residues. The structural changes in the condensed phase of two thermoplastic elastomer systems based on copolymer styrene-ethylene-butadiene-styrene (TPE-S) were investigated: TPE-S/aluminium diethylphosphinate (AlPi)/magnesium hydroxide (MH) and TPE-S/AlPi/zinc borate (ZB)/poly(phenylene oxide) (PPO). Strong flame inhibition is synergistically combined with protective layer formation. 13C-, 27Al-, 11B- and 31P MAS NMR (magic angle spinning nuclear magnetic resonance) experiments using direct excitation with a single pulse and 1H–31P cross-polarization (CP) were carried out as well as double resonance techniques. Magnesium phosphates were formed during the pyrolysis of TPE-S/AlPi/MH, while for the system TPE-S/AlPi/ZB/PPO zinc phosphates and borophosphates were observed. Thus, the chemistry behind the chemical interaction was characterized unambiguously for the investigated systems. KW - Synergy KW - Solid-state NMR KW - Flame retardancy KW - SEBS KW - Aluminium diethylphosphinate KW - Magnesium hydroxide KW - Zinc borate KW - Poly(phenylene) oxide PY - 2015 DO - https://doi.org/10.1016/j.polymdegradstab.2015.08.018 SN - 0141-3910 SN - 1873-2321 VL - 121 SP - 116 EP - 125 PB - Applied Science Publ. CY - London AN - OPUS4-34306 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sut, Aleksandra A1 - Greiser, Sebastian A1 - Jäger, Christian A1 - Schartel, Bernhard T1 - Aluminium diethylphosphinate versus ammonium polyphosphate: A comprehensive comparison of the chemical interactions during pyrolysis in flame-retarded polyolefine/poly(phenylene oxide) JF - Thermochimica Acta N2 - A systematic comparison of chemical interactions and fire behaviour is presented for the thermoplas-tic elastomer (block copolymer styrene-ethylene-butadiene-styrene) (TPE-S)/diethyl- and methylvinylsiloxane (Si)/poly(phenylene oxide) (PPO), flame-retarded with aluminium diethylphosphinate (AlPi)and with ammonium polyphosphate (APP), respectively. TPE-S/APP/Si/PPO performed better in the conecalorimeter test (reduction in peak heat release rate from 2042 to 475 kW m−2), but TPE-S/AlPi/Si/PPO inthe flammability tests (oxygen index (OI) and UL 94). This difference was caused by the different modes ofaction of APP (more in the condensed phase) and AlPi (mainly in the gas phase). Thermogravimetry cou-pled with Fourier transform infrared spectroscopy (TG-FTIR) was used to analyse the mass loss and theevolved gas products, while a Linkam hot-stage cell to investigate the decomposition in the condensedphase. Moreover, a detailed analysis of the fire residues was done using solid-state NMR.13C MAS NMRshowed that both flame-retarded compositions form graphite-like amorphous carbonaceous char, orig-inating from PPO.31P MAS NMR and29Si MAS NMR delivered important information about interactionbetween phosphorus and the siloxane. For TPE-S/AlPi/Si/PPO aluminium phosphate and silicon dioxideoccurred, while also silicophosphate was produced in TPE-S/APP/Si/PPO. The direct comparison of two ofthe most prominent halogen-free flame retardants containing phosphorus delivered meaningful insightsinto the modes of action and molecular mechanisms controlling flame retardancy. KW - Aluminium diethylphosphinate KW - Ammonium polyphosphate KW - Flame retardancy KW - Solid-state NMR KW - SEBS PY - 2016 SN - 0040-6031 SN - 1872-762X VL - 640 SP - 74 EP - 84 PB - Elsevier AN - OPUS4-37802 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -