TY - JOUR A1 - Goryacheva, O. A. A1 - Wegner, Karl David A1 - Sobolev, A. M. A1 - Häusler, I. A1 - Gaponik, N. A1 - Gorycheva, I. Y. A1 - Resch-Genger, Ute T1 - Influence of particle architecture on the photoluminescence properties of silica‑coated CdSe core/shell quantum dots N2 - Light-emitting nanoparticles like semiconductor nanocrystals (termed quantum dots, QDs) are promising candidates for biosensing and bioimaging applications based on their bright and stable photoluminescent properties. As high-quality QDs are often synthesized in organic solvents, strategies needed to be developed to render them water-dispersible without affecting their optical properties and prevent changes in postmodification steps like the biofunctionalization with antibodies or DNA. Despite a large number of studies on suitable surface modification procedures, the preparation of water-soluble QDs for nanobiotechnology applications still presents a challenge. To highlight the advantages of surface silanization, we systematically explored the influence of the core/multishell architecture of CdSe/CdS/ZnS QDs and the silanization conditions on the optical properties of the resulting silanized QDs. Our results show that the optical properties of silica-coated CdSe/CdS/ZnS QDs are best preserved in the presence of a thick CdS (6 monolayers (ML)) intermediate shell, providing a high photoluminescence quantum yield (PL QY), and a relatively thick ZnS (4.5 ML) external shell, effectively shielding the QDs from the chemical changes during silica coating. In addition to the QD core/shell architecture, other critical parameters of the silica-coating process, that can have an influence on the optical properties of the QD, include the choice of the surfactant and its concentration used for silica coating. The highest PL QY of about 46% was obtained by a microemulsion silica-coating procedure with the surfactant Brij L4, making these water-dispersible QDs to wellsuited optical reporters in future applications like fluorescence immunoassays, biomedicine, and bioimaging. KW - Nano KW - Nanomaterial KW - Particle KW - Semiconductor KW - Quantum do KW - Photoluminescence KW - Photophysics KW - Lifetime KW - Sensor KW - Mechanism KW - Surface KW - Shell KW - Silica KW - Silanization KW - Synthesis PY - 2022 DO - https://doi.org/10.1007/s00216-022-04005-7 SP - 1 EP - 13 PB - Springer AN - OPUS4-54546 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Myshkin, N. A1 - Kovalev, Alexander A1 - Makhovskaya, Y. A1 - Torskaya, E. A1 - Goryacheva, I. T1 - Influence of adhesion induced contact areas on sliding friction N2 - Recent developments in micromechanics and nanotribology have made adhesion effects very important in the study of actual contact formation and sliding friction. The present work considers the experimental and simulation data on the formation of the adhesion contact and sliding friction for rough surfaces. The simulation of discrete contact was carried out using the AFM images of topography as a source of real surface geometry at micro/nanoscale. The proposed approach of contact modelling is not using the statistical parameters of roughness, but it provides the estimation of the additional adhesion induced contact areas and their influence on sliding friction. The friction law of Bowden and Tabor was used for validation of simulation and experimental data. Furthermore, the workhardening effect was taken into account in simulation of sliding friction, and this enabled to reach a more successful fit of experimental data. The obtained results of the computer simulations will provide a way of studying the movable contact or at least transition from static to dynamic friction at the micro/nanoscale level. KW - Rough surface KW - Real contact area KW - Adhesion KW - Elastic contact KW - Plastic contact PY - 2010 DO - https://doi.org/10.1179/175158310X12678019274363 SN - 1751-5831 VL - 4 IS - 3 SP - 130 EP - 135 PB - Maney CY - London AN - OPUS4-22231 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Potapkin, D. V. A1 - Geißler, Daniel A1 - Resch-Genger, Ute A1 - Goryacheva, I. Y. T1 - Fluorescent quantum dot hydrophilization with PAMAM dendrimer N2 - Polyamidoamine (PAMAM) dendrimers were used to produce CdSe core/multi-shell fluorescent quantum dots (QDs) which are colloidally stable in aqueous solutions. The size, charge, and optical properties of QDs functionalized with the 4th (G4) and 5th (G5) generation of PAMAM were compared with amphiphilic polymer-covered QDs and used as criteria for the evaluation of the suitability of both water solubilization methods. As revealed by dynamic and electrophoretic light scattering (DLS and ELS), the hydrodynamic sizes of the QDs varied from 30 to 65 nm depending on QD type and dendrimer generation, with all QDs displaying highly positive surface charges, i.e., zeta potentials of around +50 mV in water. PAMAM functionalization yielded stable core/multi-shell QDs with photoluminescence quantum yields (Φ) of up to 45%. These dendrimer-covered QDs showed a smaller decrease in their Φ upon phase transfer compared with QDs made water soluble via encapsulation with amphiphilic brush polymer bearing polyoxyethylene/ polyoxypropylene chains. KW - Photoluminescence quantum yield KW - Quantum dots KW - PAMAM dendrimers KW - Phase transfer KW - Fluorescence PY - 2016 DO - https://doi.org/10.1007/s11051-016-3411-4 VL - 18 IS - 108 SP - 1 EP - 9 PB - Springer Science + Business Media B.V. CY - Dordrecht, Netherlands AN - OPUS4-35857 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -