TY - JOUR A1 - Schwarz, W. A1 - Wilsch, Gerd A1 - Katsumi, N. A1 - Ebell, Gino A1 - Völker, Tobias T1 - Ion distribution in concrete overlay, mapped by laser induced breakdown spectroscopy (LIBS), modified by an embedded zinc anode JF - MATEC web of conferences N2 - Galvanic corrosion protection by embedded zinc anodes is an accepted technique for the corrosion protection of reinforcing steel in concrete. Galvanic currents flow between the zinc anode and the steel reinforcement due to the potential difference that is in the range of a few hundred mV. The ion distribution was studied on two steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied EZ-anode. On both specimens, a zinc anode was embedded and glued to the concrete surface by a geo-polymer-based chloride-free binder. At one specimen, the EZ-anode was operated for 2,5 years, the EZ-anode at the other specimen was not electrically connected to the reinforcement, this specimen serves as a reference. Both specimens have been stored under identical conditions. The ion distribution between the anode (EZ-ANODE) and cathode (steel reinforcement) was studied by laser-induced breakdown spectroscopy (LIBS) after 7 months, 12 months, and 2,5 years. Results of the LIBS studies on the specimen with activated EZ-anode after 7 months, 12 months, and 2,5 years and of the reference specimen after 2,5 years are reported. Results show that diffusion of ions contributes to the changes in the ion distribution but migration, especially of chlorides towards the EZ-anode is significant despite the weak electric field – several hundred millivolts - generated by the galvanic current. Results show that chloride ions accumulate near the zinc-anode as in water-insoluble zinc-hydroxy chlorides - Simonkollite. T2 - ICCRRR 2022 CY - Capetown, South Africa KW - Corrosion KW - LIBS KW - Zinc KW - Anode PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-560576 DO - https://doi.org/10.1051/matecconf/202236404023 SN - 2261-236X VL - 364 SP - 1 EP - 7 PB - EDP Sciences CY - Les Ulis AN - OPUS4-56057 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwarz, W. A1 - Wilsch, Gerd A1 - Katsumi, N. A1 - Ebell, Gino A1 - Völker, Tobias T1 - Ion distribution in concrete overlay, mapped by laser induced breakdown spectroscopy (LIBS), modified by an embedded zinc anode N2 - Galvanic corrosion protection by embedded zinc anodes is an accepted technique for the corrosion protection of reinforcing steel in concrete. Galvanic currents flow between the zinc anode and the steel reinforcement due to the potential difference that is in the range of a few hundred mV. The ion distribution was studied on two steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied EZ-anode. On both specimens, a zinc anode was embedded and glued to the concrete surface by a geo-polymer-based chloride-free binder. At one specimen, the EZ-anode was operated for 2,5 years, the EZ-anode at the other specimen was not electrically connected to the reinforcement, this specimen serves as a reference. Both specimens have been stored under identical conditions. The ion distribution between the anode (EZ-anode) and cathode (steel reinforcement) was studied by laser-induced breakdown spectroscopy (LIBS) after 7 months, 12 months, and 2,5 years. Results of the LIBS studies on the specimen with activated EZ-anode after 7 months, 12 months, and 2,5 years and of the reference specimen after 2,5 years are reported. Results show that diffusion of ions contributes to the changes in the ion distribution but migration, especially of chlorides towards the EZ-anode is significant despite the weak electric field – several hundred millivolts - generated by the galvanic current. Results show that chloride ions accumulate near the zinc-anode as in water-insoluble zinc-hydroxy chlorides - Simonkolleit. T2 - ICCRRR 2022 CY - Capetown, South Africa DA - 03.10.2022 KW - Korrosion KW - Corrosion KW - LIBS KW - Zinc PY - 2022 AN - OPUS4-55948 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwarz, W. A1 - Wilsch, Gerd A1 - Pichelhöfer, A. A1 - Ebell, Gino A1 - Völker, Tobias T1 - Galvanic chloride extraction by an embedded zinc anode: Ion distribution mapped by laser induced breakdown spectroscopy (LIBS) T2 - Concrete Solutions 2019 N2 - An important aspect with regard to the service life of zinc based galvanic anodes and the durability of the corrosion protection of steel in concrete is the “galvanic chloride extraction”. Chloride ions move in the electric field generated by the current, flowing between the galvanic anode and the cathodic steel. Migration leads to an accumulation of anions, e.g. chloride ions, at the anode and depletion of chlorides near the steel rebar surface. The ion migration was studied on steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied embedded zinc anode (EZA). The zinc anode was embedded and glued to the concrete surface by a geo-polymer based chloride free binder. The EZA was operated over a period of 1 year and the ion distribution between anode (EZA) and cathode (steel reinforcement) was studied by laser induced breakdown spectroscopy (LIBS) after 5 months, 7 months and 12 months. The results show that chloride ions efficiently migrate in the direction of the zinc-anode and accumulate there. Chloride distribution in the EZA correlates with the distribution of zinc ions generated by the anodic dissolution of the zinc anode in the binder matrix. The microstructure of the binder matrix and its interface to the zinc-anode are studied by REM/EDX – preliminary results will be reported. T2 - Concrete Solutions 2019 CY - Cluj Napoca, Romania DA - 30.09.2019 KW - Galvanic corrosion KW - Corrosion KW - Chloride extraction PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-488189 DO - https://doi.org/10.1051/matecconf/201928903010 VL - 289 SP - 03010, 1 EP - 5 PB - MATEC Web of Conferences AN - OPUS4-48818 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Günther, Tobias A1 - Wilsch, Gerd T1 - Untersuchungen zum korrosionsauslösenden Chloridgehalt an nicht rostendem ferritischem Betonstahl in Mörtel JF - Bautechnik N2 - Der maßgebliche Korrosionsschutz von nicht rostendem Stahl in Beton basiert, anders als bei unlegiertem Betonstahl, auf der Ausbildung einer Chromoxidschicht. Die Chromoxidschicht ist in alkalischem und in carbonatisiertem Beton beständig, sodass nicht rostende Stähle in einem passiven Zustand vorliegen. Die Initiierung von Lochkorrosionserscheinungen ist dagegen auch an nicht rostenden Stählen in Beton möglich. Der korrosionsauslösende Chloridgehalt ist neben dem Gehalt an Legierungselementen (insbesondere dem Chromgehalt) und der Oberflächenbeschaffenheit auch vom Konzentrationsverhältnis von OH“ zu CI“ im Elektrolyten abhängig. Daher ist prinzipiell zu erwarten, dass in karbonatisierten Betonen geringere Chloridgehalte Korrosion initiieren können als in Betonen mit höheren pH-Werten. Dies gilt in besonderem Maße für nicht rostende Betonstähle mit geringen Chromgehalten, wie z. B. Produkte aus dem Werkstoff 1.4003 (X2CrNi12) mit seiner im Vergleich zu den Standardausteniten geringen Beständigkeit. Um den kritischen korrosionsauslösenden Chloridgehalt am Beispiel eines am Markt verfügbaren ferritischen Chromstahls zu bestimmen, wurden an der Bundesanstalt für Materialforschung und -prüfung (BAM) umfangreiche Untersuchungen zu beschleunigten Korrosionsversuchen in alkalischen und karbonatisierten Mörteln durchgeführt. Mittels Laser-induced Breakdown Spectroscopy (LIBS) konnten die korrosionsauslösenden Chloridgehalte im Phasengrenzbereich Betonstahl-Mörtel ermittelt werden. KW - Korrosion KW - Betonstahl KW - Nicht rostender KW - LIBS KW - Chloridgehalt KW - Kritischer PY - 2020 DO - https://doi.org/10.1002/bate.201900077 SN - 0932-8351 VL - 97 IS - 1 SP - 21 EP - 31 PB - Ernst & Sohn CY - Berlin AN - OPUS4-50247 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -