TY - CONF A1 - Gibmeier, J. A1 - Weidemann, Jens A1 - Dixneit, Jonny A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - Influence of structural stiffness on the residual stresses during welding of low transformation temperature alloys N2 - Low Transformation Temperature (LTT) alloys are high alloyed filler materials, which exhibit a martensitic phase transformation at comparatively low temperatures in order to prevent high tensile residual stresses. A number of publications have already shown that even compressive residual stresses can be observed when using LTT filler materials. Up to know it is not clear in which way this it applicable to multi-run welding exhibiting high shrinkage restraint and complex heat input. In this study the potential for stress reduction during welding of LTT alloys was studied by numerical simulation. This allows for evaluation of the stress development in every single weid run. Additionally, the impact of the structural stiffness was incorporated by modelling a special sample geometry exhibiting a high intensity of restraint. The results show that the stress formation in weid longitudinal direction is determined by the phase transformation as high compressive residual stresses were found here independent from the weid run. On the other hand the transformation induced stresses in weid transverse direction are superimposed by tensile stresses originated from shrinkage restraint. With increasing number of runs the tensile residual stress level is raised. The results were confirmed by residual stress measurements using diffraction methods. T2 - 11th International Seminar - Numerical Analysis of Weldability CY - Graz, Austria DA - 27.09.2015 KW - Influence KW - Structural stiffness KW - Residual stresses KW - Low transformation KW - Temperature alloys KW - Welding PY - 2016 SN - 978-3-85125-490-7 SN - 2410-0544 SP - 259 EP - 276 PB - Verlag der Technischen Universität Graz CY - Graz AN - OPUS4-38998 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Held, E. A1 - Ohl, H. A1 - Gibmeier, J. A1 - Dixneit, Jonny A1 - Kromm, Arne A1 - Kannengießer, Thomas ED - Petzow, G. T1 - Mikrostruktur- und Härteentwicklung in Schweißnähten mit neuartigen LTT-Schweißzusatzwerkstoffen N2 - Das Schweißen von hochfesten Stahlstrukturen ist Gegenstand aktueller Forschungsbestrebungen wobei unter anderem der Eigenspannungsausbildung eine entscheidende Rolle zugeordnet wird. Neuartige LTT (Low Transformation Temperature) Schweißzusatzwerkstoffe mit deutlich abgesenkten Martensitstarttemperaturen wurden entwickelt, um die Eigenspannungsentwicklung in der Schweißnaht durch die späte Martensitumformung während des Abkühlens des Schweißguts kontrollieren zu können. Auf diese Weise können in den Schweißnähten nicht nur Zugeigenspannungen reduziert sondern sogar gezielt Druckeigenspannungen eingebracht werden. Dies konnte bereits in verschiedenen Arbeiten zu diesem Themenkomplex gezeigt werden. Durch das gezielte Einbringen von Druckeigenspannungen in die Schweißnaht kann die Lebensdauer und die mechanische Integrität von hochfesten Schweißverbindungen ohne aufwändige mechanische oder thermische Nachbehandlungsverfahren deutlich erhöht w erden. Einen großen Einfluss auf die Eigenspannungsausbildung in Schweißnähten haben die Umwandlungstemperatur und die Schrumpfungsbehinderung bei der Abkühlung. In der vorliegenden Arbeit wird nun untersucht, wie der Grad der Einspannung sich auf die Mikrostruktur- und Härteentwicklung in Schweißnähten mit LTT -Zusatzwerkstoffen auswirkt. Der in dieser Arbeit untersuchte neuartige LTT-Schweißzusatzstoff wurde nach dem 10%Ni - 10%Cr-Konzept nach 111 ausgewählt. Die Schweißeignung des untersuchten Werkstoffes sowie die Beeinflussung der Mikrostrukturausbildung durch eine Variation des Nickelgehalt wurden bereits in vorangehenden Arbeiten eingehend untersucht. Hierbei zeigte sich, dass der Nickelgehalt einen signifikanten Einfluss auf die Martensitstarttemperatur und damit auf die lokale Mikrostrukturausbildung hat. Eine Erhöhung des Nickelgehaltes von S auf 12 Ma-% führt zu einer Verminderung der Martensitstarttemperatur von 16()°C auf etwa 60°C (bestimmt mittels in-situ Röntgenbeugungsanalysen im reinen Schweißgut). T2 - 47. Metallographie-Tagung CY - Friedrichshafen, Germany DA - 18.09.2013 PY - 2013 SN - 978-3-88355-398-6 VL - 45 SP - 297 EP - 302 AN - OPUS4-29710 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Gibmeier, J. A1 - Rethmeier, Michael T1 - In-situ-Analyse der Phasenumwandlungskinetik während des Schweißens N2 - Zugeigenspannungen, wie sie beim Schweißprozess durch inhomogene Temperaturverteilungen und Schrumpfungen hervorgerufen werden, können die Lebensdauer geschweißter Verbindungen signifikant herabsetzen. Eine neue und außerordentlich attraktive Methode, um Druckeigenspannungen bereits während des Schweißens gezielt einzustellen, gelingt mit sogenannten LTT (Low Transformation Temperature)-Legierungen. LTT-Legierungen weisen eine martensitische Phasenumwandlung bei relativ niedrigen Temperaturen auf, wobei die damit verbundene Volumenexpansion zu einer Reduktion der Schrumpfeigenspannungen bzw. Erzeugung von Druckeigenspannungen führt. Zum direkten Nachweis der Phasenumwandlungen und der damit verbundenen resultierenden Schweißeigenspannungen wurden erstmals In-situ-Schweißexperimente unter Nutzung hoch energetischer, polychromatischer Synchrotronstrahlung (Weißstrahl) realisiert, um die Umwandlungskinetik während eines realen Schweißprozesses und die daraus resultierenden Schweißeigenspannungen zu analysieren. Es wird gezeigt, dass mit LTT-Legierungen signifikante Druckeigenspannungen in der Schweißnaht erreicht werden. PY - 2010 SN - 0025-5300 VL - 52 IS - 4 SP - 204 EP - 210 PB - Hanser CY - München AN - OPUS4-21219 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Rethmeier, Michael A1 - Gibmeier, J. A1 - Genzel, C. T1 - Residual stresses and in-situ measurement of phase transformation in low transformation temperature (LTT) welding materials PY - 2009 SN - 1097-0002 SN - 0069-8490 SN - 0376-0308 VL - 52 SP - 755 EP - 762 CY - Newtown Square, Pa., USA AN - OPUS4-19817 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Gibmeier, J. A1 - Genzel, C. A1 - Mee, V. van der T1 - Determination of Residual Stresses in Low Transformation Temperature (LTT-) Weld Metals using X-ray and High Energy Synchrotron Radiation KW - Filler material KW - Low transformation temperature KW - Synchrotron radiation KW - Phase specific residual stresses KW - Energy dispersive diffraction PY - 2007 IS - II-1658r1-07 SP - 1 EP - 17 PB - International Institute of Welding CY - Paris AN - OPUS4-15716 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Thomas, Maximilian A1 - Kannengießer, Thomas A1 - Gibmeier, J. A1 - Vollert, F. T1 - Assessment of the Solidification Cracking Susceptibility of Welding Consumables in the Varestraint Test by Means of an Extended Evaluation Methodology N2 - Various test methods are available for assessing the susceptibility of materials to solidification cracking during welding. In the widely used Varestraint test, the crack length is selected as a criterion as a function of the applied bending strain. Unfortunately, the crack length does not characterize the material behavior alone but depends to varying degrees on the individual test parameters used, which makes the interpretation of the results difficult. In addition, the crack length is not comparable under different test conditions. To overcome these disadvantages, we have developed a novel evaluation methodology that decouples the machine influence from the material behavior. The measured crack length is related to the maximum possible value specified by welding speed and deformation time. This relative crack length is calculated numerically, considering the orientation of the cracks. Experiments on two high-alloy martensitic welding consumables show that, in contrast to the conventional evaluation, a comparison of different welding parameters becomes possible. Furthermore, the strain rate proved to be a suitable crack criterion in agreement with Prokhorov's hot cracking model. KW - Welding KW - Solidification cracking KW - Varestraint test PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-545780 DO - https://doi.org/10.1002/adem.202101650 SN - 1438-1656 SP - 2101650 PB - Wiley online library AN - OPUS4-54578 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dixneit, Jonny A1 - Kromm, Arne A1 - Boin, M. A1 - Kannengießer, Thomas A1 - Gibmeier, J. ED - Olden, T.-M. ED - Muransky, O. Muransky ED - Edwards, L. T1 - Influence of heat control on residual stresses in low transformation temperature (LTT) large scale welds N2 - The current paper presents residual stress analyses of large scale LTT (Low Transformation Temperature) welds. LTT filler materials are specially designed for residual stress engineering by means of an adjusted martensite phase transformation. Controlling the level of mostly detrimental residual stresses already during the welding process would be highly attractive as time and cost consuming post processing may be prevented. In large scale welds the residual stress state is influenced by the heat control (e.g. interpass temperature) during welding. Therefore, welding residual stresses are studied here putting the focus on the influence of welding process parameters while joining heavy steel sections with a thickness of 25 mm. The residual stress state was determined at the top surface using X-ray diffraction as well as in the bulk by neutron diffraction. The results show that control of the interpass temperature is vital for the residual stresses present in the joints. This accounts for the top surface but is most pronounced for the bulk of the welds. While high interpass temperatures are appropriate to induce compressive residual stresses in the weld metal, low interpass temperatures favor unwanted tensile residual stresses instead. T2 - ICRS 2016 - 10th International Conference on Residual Stresses CY - Sydney, Australia DA - 03.07.2016 KW - LTT KW - Welding residual stress KW - Phase transformation KW - Interpass temperature PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-389628 SN - 978-1-94529117-3 SN - 978-1-94529116-6 DO - https://doi.org/10.21741/9781945291173-38 SN - 2474-395X VL - 2 SP - 223 EP - 228 PB - Materials Research Forum LLC CY - Millersville (PA), USA AN - OPUS4-38962 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Thomas, Maximilian A1 - Vollert, F. A1 - Weidemann, Jens A1 - Gibmeier, J. A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Surface- and volume-based investigation on influences of different Varestraint testing parameters and chemical compositions on solidification cracking in LTT filler metals N2 - The subject of this study is how, and to what extent, Varestraint/Transvarestraint test results are influenced by both testing parameters and characteristics of evaluation methods. Several different high-alloyed martensitic LTT (low Transformation temperature) filler materials, CrNi and CrMn type, were selected for examination due to their rather distinctive solidification cracking behaviour, which aroused interest after previous studies. First, the effects of different process parameter sets on the solidification cracking response were measured using standard approaches. Subsequently, microfocus X-ray computer tomography (μCT) scans were performed on the specimens. The results consistently show sub-surface cracking to significant yet varying extents. Different primary solidification types were found using wavelength dispersive X-ray (WDX) analysis conducted on filler metals with varying Cr/Ni equivalent ratios. This aspect is regarded as the main difference between the CrNiand CrMn-type materials in matters of cracking characteristics. Results show that when it comes to testing of modern highperformance alloys, one set of standard Varestraint testing parameters might not be equally suitable for all materials. Also, to properly accommodate different solidification types, sub-surface cracking has to be taken into account. KW - Solidification cracking KW - Varestraint testing KW - MVT KW - LTT filler metal KW - Microfocus X-ray computer tomography (μCT) PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-506039 DO - https://doi.org/10.1007/s40194-020-00895-2 VL - 64 SP - 913 EP - 923 PB - Springer Nature CY - Heidelberg, New York AN - OPUS4-50603 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dixneit, Jonny A1 - Kromm, Arne A1 - Boin, M. A1 - Wimpory, Robert A1 - Kannengießer, Thomas A1 - Gibmeier, J. A1 - Schröpfer, Dirk T1 - Residual stresses of LTT welds in large-scale components N2 - Residual stresses of welds become more and more important influencing cold cracking as well as the fatigue life of welded components. Low transformation temperature (LTT) filler materials offer the opportunity to alter the residual stresses already during the welding process by means of ad- justed martensite phase transformation temperature (MS). In the current paper, welding residual stresses are studied putting the focus on MS while joining heavy steel sections with a thickness of 20 and 25 mm, respectively. The residual stress state was determined at the top surface using X-ray diffraction as well as in the bulk by neutron diffraction. The results com- pare the residual stresses present in a conventional weld and LTT welds when multi-pass welding of large-scale compo- nents was applied. Repeated phase transformation in the case of the LTT weld is more vital for the residual stresses present in the real-life-like joints. This accounts for the top surface in longitudinal direction but is most pronounced for the bulk of the welds. Detrimental tensile residual stresses are mainly re- duced in the bulk in comparison to a conventional filler wire even in multi-pass welds of thick steel sections. T2 - IIW AA 2016 CY - Melbourne, Australia DA - 10.07.2016 KW - LTT KW - Welding residual stress KW - Phase transformation KW - Interpass temperature PY - 2017 DO - https://doi.org/10.1007/s40194-017-0502-5 SN - 0043-2288 SN - 1878-6669 VL - 61 IS - 6 SP - 1089 EP - 1097 PB - Springer CY - Heidelberg AN - OPUS4-41169 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Gibmeier, J. A1 - Genzel, C. A1 - Van der Mee, V. T1 - Determination of residual stresses in low transformation temperature (LTT -) welds metals using X-rayand high energy synchrotron radiation N2 - Crack and fatigue resistance are relevant evaluation criteria for welded joints and are decreased by tensile residual stresses resulting from the welding and cooling process, while compressive residual stresses can have a positive influence on the characteristics mentioned. In order to generate compressive residual stresses, a set of post weld treatment procedures is available, like shot peening, hammering, etc. These procedures have the disadvantage that they are time and cost extensive and have to be applied after welding. As another point, such technologies can only produce compressive stresses at the top surface, i.e. can only contribute to the reduction of the risk of cracks initiated at the surface, like fatigue cracks. A chance to generate compressive stresses over the complete weld joint during the welding procedure is offered by the so-called Low Transformation Temperature (LTT -) filler wires. Compared to conventional wires, these materials show lower phase transformation temperatures, which can work against coolingrelated tensile stresses, resulting from respective shrinkage restraint. In consequence, distinct compressive residual stresses can be observed within the weld and adjacent areas. The strength of these fillers makes them potentially applicable to high-strength steel welding. Welds produced with different LTT – filler wires have shown different levels and distributions of the resulting residual stresses depending on the specific transformation temperature. The transformation temperatures are determined by temperature measurement. Classical X-ray diffraction as well as diffraction methods using high energy synchrotron radiation have been used for residual stress analysis. By means of high energy synchrotron diffraction in reflection mode residual stress depth gradients can be determined nondestructively. The phase selective nature of the diffraction measurements enables the simultaneous determination of the phase specific residual stresses of all contributing crystalline phases within one experiment. The application of white beam diffraction implies recording of a multitude of diffraction lines within the energy range of the provided energy spectrum of the white beam. By this means phase specific residual stress depth distributions up to distances of 150 ìm below the surface can be analysed for steel using the energy dispersive set-up of the HMI-beamline EDDI at the Bessy site, Berlin, providing an energy range between 20-150 keV. As a side effect quantitative phase analysis can be carried out using white energy dispersive diffraction e.g. the determination of the content of retained austenite in the weld. KW - Filler materials KW - Low temperature KW - Reference lists KW - Residual stresses KW - Temperature KW - Transformation KW - Synchrotron radiation KW - Phase specific residual stresses KW - Energy dispersive diffraction PY - 2009 SN - 0043-2288 SN - 1878-6669 VL - 53 IS - 1/2 SP - 3 EP - 16 PB - Springer CY - Oxford AN - OPUS4-19214 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Gibmeier, J. T1 - In-situ observation of phase transformations during welding of low transformation temperature filler material KW - LTT filler material KW - In-situ observation KW - Energy dispersive diffraction KW - Transformation temperature KW - Residual stress PY - 2010 DO - https://doi.org/10.4028/www.scientific.net/MSF.638-642.3769 SN - 0255-5476 VL - 638-642 SP - 3769 EP - 3774 PB - Trans Tech Publications CY - Aedermannsdorf, Switzerland AN - OPUS4-20725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -