TY - JOUR A1 - Dixneit, J. A1 - Gibmeier, J. A1 - Kromm, Arne A1 - Schubnell, J. A1 - Lang, F. A1 - Loebich, F. A1 - Carl, E.-R. A1 - Ya, W. T1 - Residual stress distribution of a large component manufactured by AM-DED-Arc from high-strength weld filler material X90 N2 - Currently, DED-Arc manufactured components are not covered by design guidelines, and design factors such as residual stress factors are not defined for such components. This hinders industrial use, especially for components with a remaining surface waviness required by industry. For the first time the stress state of a high-strength, low-alloy, large-scale DED-Arc component was characterised in the as-built state and after cutting off the component from the substrate plate. Complementary methods of residual stress analyses were applied to gain a holistic insight into the residual stress distributions of a thick-walled part. In the as-built state, direction-dependent and position-dependent tensile residual stresses were found for the component at the level of the yield strength of the part. The additive manufacturing strategy continuous spiral deposition has no significant influence on the residual stresses in bead threshold area compared to the residual stresses of the remaining component. For this case, bead threshold is no structural imperfection. By removing the part from the substrate plate, the residual stresses are significantly redistributed. Tensile residual stresses are then present at a moderate level. Compressive residual stresses were determined in the volume of the deposited material. The general consideration of ‘‘high’’ tensile residual stresses in such thick-walled components is rather conservative. Therefore, design guidelines should take the manufacturing condition into account. KW - AM-DED-Arc KW - Residual stress KW - High strength steel PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-655239 DO - https://doi.org/10.1177/03093247251406876 SN - 2041-3130 SP - 1 EP - 18 PB - SAGE AN - OPUS4-65523 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vollert, F. A1 - Gibmeier, J. A1 - Rebelo-Kornmeier, J. A1 - Dixneit, Jonny A1 - Pirling, T. ED - Neu, R. W. ED - Totten, G. E. T1 - Two-dimensional residual stress mapping of multilayer LTT weld joints using the contour method N2 - Low transformation temperature (LTT) weld filler materials offer an attractive alternative to cost intensive postweld treatments as they can mitigate detrimental welding residual stresses during the welding process. Compared to conventional weld filler materials, LTT alloys are characterized by a delayed martensite transformation at low temperatures, which can result in compressive residual stresses in the weld. The high strength of these filler materials makes them potentially applicable to high-strength steels as well as for a large amount of requested repair works in steel structures. The focus of the study is on the confirmation of the LTT idea with regard to the residual stress state for multipass weld lines processed by metal active gas welding. It is demonstrated that the contour method is a well-suited technique for measuring the residual stress in the weld joint as it gives an entire two-dimensional map of the residual stress state in the weld line, heat affected zone (HAZ), and base material. The technique was applied at different LTT alloys with varying chemical compositions. Additionally, the results are compared to residual stress maps that were determined by Neutron diffraction using the Strain Analyzer for Large Scale Engineering Applications, an instrument referred to as SALSA, at the Institut Laue-Langevin in Grenoble. For all investigated specimens, compressive residual stress distributions were determined in the area of the weld joint and the HAZ. They are balanced by tensile residual stresses in the surrounding base material. However, it is shown that the size of theregion exhibiting compressive residual stresses and the absolute values of the compressive residual stresses depend on the chemical composition of the weld filler material. KW - LTT Weld Filler Materials KW - contour method KW - neutron diffraction KW - Welding KW - residual stress analysis PY - 2018 DO - https://doi.org/10.1520/MPC20170110 SN - 2379-1365 VL - 7 IS - 4 SP - 545 EP - 558 PB - ASTM International CY - West Conshohocken, PA, USA AN - OPUS4-46694 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gibmeier, J. A1 - Obelode, E. A1 - Altenkirch, J. A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Residual stress in steel fusion welds joined using low transformation temperature (LTT) filler material N2 - Welding residual stress is of major concern for structural integrity assessment in industrial components. Shear and volume strains resulting from the austenite-martensite-transformation affect the development of residual stress during welding. Controlling the phase transformation allows adjustment of the welding residual stress. Low transformation temperature (LTT) weld filler materials exhibiting reduced MS-temperatures allow postponing the phase transformation. The associated strain arising from the delayed transformation compensates for the thermal contraction strains and as such may reduce tensile or even introduce compressive residual stress. In this article we discuss the tri-axial residual stress distribution in 15 mm S690Q steel plates joined with LTT filler materials with 10 wt% Cr and a Ni-content that varies from 8 to 12 wt%. Using complementary synchrotron X-ray and neutron diffraction stress analysis the macroscopic residual stress was derived from the phase specific lattice strain and phase fraction of martensite and retained austenite, respectively. The local phase specific unstrained lattice parameters were determined using stress relieved combs. The investigation revealed increasing phase fraction of retained austenite with increasing Ni-content. Further, independent of the Ni-content in each weld in the fusion zone, significant compressive residual stresses were found in the longitudinal direction, which are balanced by tensile residual stresses in the heat affected zone (HAZ). In the weld transverse and normal direction the stress distribution is qualitatively similar but less in magnitude. The increased amount of retained austenite reduces the compressive stress arising from shear and volume strains during the delayed phase transformation and therefore no significant increase in compression was observed for decreasing MS-temperatures. KW - Welding residual stresses KW - Neutron diffraction KW - LTT filler materials PY - 2014 DO - https://doi.org/10.4028/www.scientific.net/MSF.768-769.620 SN - 0255-5476 VL - 768-769 SP - 620 EP - 627 PB - Trans Tech Publications CY - Aedermannsdorf, Switzerland AN - OPUS4-29706 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gibmeier, J. A1 - Held, A. A1 - Altenkirch, J. A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Buslaps, T. T1 - Real time monitoring of phase transformation and strain evolution in LTT weld filler material using EDXRD N2 - For a newly developed 10% Cr and 10% Ni low transformation temperature (LTT) weld filler material, the local phase transformation kinetics and the strain evolution during gas tungsten arc welding (GTAW) under real welding conditions was studied. An experimental set-up and a measuring and evaluation strategy are presented to gain a real time insight into the welding process. The experiments were carried out at the beam line ID15@ESRF using a two detector EDXRD (energy dispersive X-ray diffraction) set-up and high energy synchrotron X-rays. The time-resolved diffraction analysis during welding was carried out locally throughout the weld in longitudinal as well as in transverse direction to the weld line to examine the interdependence of the strain state and the transformation kinetics. This comprehension is crucial for the optimization of the weld process, and thus for the tailoring of the resulting residual stress states, which is one of the main issues for the application of LTT alloys. Using the herein proposed approach EDXRD diffraction pattern can be monitored during real welding with a counting rate of 5 Hz. By means of the time resolved diffraction data the local transformation temperatures and times were determined and the local phasespecific strain evolutions are discussed with respect to the transformation rates and the time-delayed phase transformations. KW - In situ synchrotron X-ray diffraction KW - Low transformation temperature KW - Welding PY - 2014 DO - https://doi.org/10.1016/j.jmatprotec.2014.06.008 SN - 0924-0136 SN - 1873-4774 VL - 214 IS - 11 SP - 2739 EP - 2747 PB - Elsevier CY - Amsterdam AN - OPUS4-30955 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Altenkirch, J. A1 - Gibmeier, J. T1 - Residual stresses in multilayer welds with different martensitic transformation temperatures analyzed by high-energy synchrotron diffraction N2 - Low Transformation Temperature (LTT) alloys were developed in order to control the residual stress development by the martensitic phase transformation already during cooling of the weld metal. The positive effect of such LTT alloys on the mitigation of detrimental tensile residual stresses during welding has already been confirmed on the basis of individual laboratory tests. Within the current project it was experimentally investigated whether the phase transformation mechanisms are effective under increased restraint due to multi-pass welding of thicker specimens. The local residual stress depth distribution was analyzed non-destructively for V-type welds processed by arc welding using energy dispersive synchrotron X-ray diffraction (EDXRD). The use of high energy (20 keV to 150 keV) EDXRD allowed for the evaluation of diffraction spectra containing information of all contributing phases. As the investigated LTT alloy contains retained austenite after welding, this phase was also considered for stress analysis. The results show in particular how the constraining effect of increased thickness of the welded plates and additional deposited weld metal influences the level of the residual stresses in near weld surface areas. While the longitudinal residual stresses were reduced in general, in the transition zone from the weld to the heat-affected zone (HAZ) compressive residual stresses were found. KW - Low Transformation Temperature KW - Phase Transformation KW - Residual Stress KW - Synchrotron Diffraction PY - 2011 DO - https://doi.org/10.4028/www.scientific.net/MSF.681.37 SN - 0255-5476 VL - 681 SP - 37 EP - 42 PB - Trans Tech Publications CY - Aedermannsdorf, Switzerland AN - OPUS4-23470 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Altenkirch, J. A1 - Gibmeier, J. A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Nitschke-Pagel, T. A1 - Hofmann, M. T1 - In situ study of structural integrity of low transformation temperature (LTT)-welds N2 - We discuss the stability of weld residual strain under static and quasi cyclic transverse tensile loading in the elastic and elastic–plastic region. The test welds were joined with low transformation temperature weld filler materials with 10 wt% Cr and varying Ni-content from 8 to 12 wt%. Using neutron diffraction the residual lattice strain in the martensitic α'- and austenitic γ-phase in the fusion zone as well as the ferritic α-phase in the heat affected zone and base metal as induced by welding, superimposed by stepwise tensile loading and after unloading was measured. The amount of retained austenite in the fusion zone increases with increasing Ni-content, but it decreases with increasing load level due to stress induced martensite formation. In the as-welded condition the transverse macroscopic residual lattice strain was found to be in low compression in the fusion zone in each weld, while the heat affected zone was in tension. Local plastic deformation of the γ-phase as a result of yielding during tensile loading in combination with the change in phase fraction resulted in increased macroscopic compression in the fusion zone. The reduced yield strength in the heat affected zone resulted in plastic deformation and a considerable shift into compression. Comparison with the cross weld distribution of the hardness and FWHM of the neutron diffraction interference lines supported the assumption of plastic deformation of the γ- and α-phase in the fusion and heat affected zone, respectively, while the α'-phase in the fusion zone was stressed within the elastic regime only. Microstructural observations as well as measurement of the local γ-phase fraction by means of laboratory X-ray diffraction in the fusion zone strengthen these observations. KW - Low transformation temperature KW - Residual stress KW - Neutron diffraction PY - 2011 DO - https://doi.org/10.1016/j.msea.2011.03.091 SN - 0921-5093 SN - 1873-4936 VL - 528 IS - 16-17 SP - 5566 EP - 5575 PB - Elsevier CY - Amsterdam AN - OPUS4-24359 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Altenkirch, J. A1 - Gibmeier, J. A1 - Kostov, V. A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Doyle, S. A1 - Wanner, A. T1 - Time- and temperature-resolved synchrotron X-ray diffraction: observation of phase transformation and strain evolution in novel low temperature transformation weld filler materials N2 - Solid-state phase transformations and the evolution of thermal and elastic strains in novel low temperature transformation (LTT) weld filler materials in the near surface region are monitored in real time by means of an innovative experimental set-up at the PDIFF (powder diffraction) beamline at the synchrotron light source ANKA (Angströmquelle Karlsruhe) at the KIT (Karlsruhe Institute for Technology). The key components of the diffraction set-up are two fast microstrip line detectors, which enables the strain evolution to be followed as a function of time and temperature for a 0.5?s counting time. During controlled heating and cooling cycles, as well as during near welding cycles, the martensite–austenite–martensite phase transitions are analysed. The transformation kinetics are monitored during resistance heating of small chips of the pure LTT alloys and during gas tungsten arc welding of simplified LTT welds using a specially designed welding rig for in-situ studies on the diffraction instruments. Under the mechanically unconstrained condition allowing free thermal expansion and shrinkage, the LTT alloys are found to exhibit decreasing transformation temperatures Ac and MS and increasing phase fraction of retained austenite for increasing Ni content. The strain evolution during welding reveals increased compressive stresses upon welding, which is attributed to the martensite formation upon cooling, which counteracts the thermal contraction strains. Comparison of the transformation temperatures reveals higher values than in the pure LTT alloys, but no variation between the different alloys. On the one hand, this is attributed to preferred grain orientation affecting the diffraction measurements and the determination of the transformation temperatures. On the other hand, it is possible that with the different chemical compositions of the LTT alloys and the mechanical constraints during welding, the evolution of the residual strain and stress may vary and result in counteracting affects with respect to lowered martensite start temperatures. KW - In-situ synchrotron X-ray diffraction KW - Low temperature transformation KW - Welding PY - 2011 DO - https://doi.org/10.1177/0309324711413190 SN - 0309-3247 SN - 2041-3130 VL - 46 IS - 7 SP - 563 EP - 579 PB - Sage CY - London AN - OPUS4-24683 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vollert, F. A1 - Thomas, Maximilian A1 - Kromm, Arne A1 - Gibmeier, J. T1 - Solidification Cracking Assessment of LTT Filler Materials by Means of Varestraint Testing and μCT N2 - Investigations of the weldability of metals often deal with hot cracking, as one of the most dreaded imperfections during weld fabrication. The hot cracking investigations presented in this paper were carried out as part of a study on the development of low transformation temperature (LTT) weld filler materials. These alloys allow to mitigate tensile residual stresses that usually arise during welding using conventional weld filler materials. By this means, higher fatigue strength and higher lifetimes of the weld can be achieved. However, LTT weld filler materials are for example, high-alloyed Cr/Ni steels that are susceptible to the formation of hot cracks. To assess hot cracking, we applied the standardized modified varestraint transvarestraint hot cracking test (MVT), which is well appropriate to evaluate different base or filler materials with regard to their hot cracking susceptibility. In order to consider the complete material volume for the assessment of hot cracking, we additionally applied microfocus X-ray computer tomography (μCT). It is shown that by a suitable selection of welding and MVT parameter the analysis of the complete 3D hot crack network can provide additional information with regard to the hot cracking model following Prokhorov. It is now possible to determine easy accessible substitute values (e.g., maximum crack depth) for the extent of the Brittleness Temperature Range (BTR) and the minimum critical strain Pmin. KW - LTT weld filler materials KW - μCT-analysis KW - Hot cracking KW - Varestraint test PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-509126 DO - https://doi.org/10.3390/ma13122726 VL - 13 IS - 12 SP - 2726 PB - MDPI AN - OPUS4-50912 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vollert, F. A1 - Thomas, Maximilian A1 - Kromm, Arne A1 - Gibmeier, J. T1 - Hot crack assessment of LTT welds using μCT N2 - Investigations on weldability often deal with hot cracking, as one of the most popular failure during weld fabrication. The modified varestraint transvarestraint hot cracking test (MVT) is well known for the assessment of the hot cracking susceptibility of materials. The shortcoming of this approach is that the information is only from the very near surface region, which inhibits access to the characteristic of the hot crack network in the bulk. Here, we report about a new approach, illustrated in the example of low transformation temperature (LTT) weld filler materials, to monitor the entire 3D hot crack network after welding by means of microfocus X-ray computer tomography (μCT). T2 - 10th Conference on Industrial Computed Tomography (iCT 2020) CY - Wels, Austria DA - 04.02.2020 KW - Varestraint testing KW - LTT weld filler materials KW - Hot cracking KW - Welding KW - μCT-analysis PY - 2020 DO - https://doi.org/https://doi.org/10.58286/25121 SN - 1435-4934 VL - 25 IS - 2 SP - 1 EP - 7 PB - NDT.net CY - Kirchwald AN - OPUS4-50341 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Abou-Ras, D. A1 - Gibmeier, J. A1 - Nolze, Gert A1 - Gholinia, A. A1 - Konijnenberg, P. T1 - On the capability of revealing the pseudosymmetry of the chalcopyrite-type crystal structure N2 - The tetragonal crystal- structure type of chalcopyrites (chemical formula AIBIIICVI2) is a superstructure of sphalerite type. The c/a ratio differs generally from the ideal value 2, i.e., the crystal structure is pseudocubically distorted. For CuInSe2 and CuGaSe2 thin films, simulations demonstrate that it is theoretically possible to reveal the tetragonality in electron backscatter-diffraction (EBSD) patterns for CuGaSe2, whereas it may not be possible for CuInSe2. EBSD experiments on CuGaSe2 thin films using the ”Advanced Fit” band-detection method show that it is possible to extract accurate misorientation-angle distributions from the CuGaSe2 thin film. Pole figures revealing the texture of the CuGaSe2 thin film are shown, which agree well with X-ray texture measurements from the same layer. KW - Pseudosymmetry KW - Chalcopyrite KW - Electron backscatter diffraction KW - Pattern simulation KW - Pattern matching KW - Sphalerite PY - 2008 DO - https://doi.org/10.1002/crat.200711082 VL - 43 IS - 3 SP - 234 EP - 239 PB - WILEY-VCH AN - OPUS4-38003 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dixneit, Jonny A1 - Vollert, F. A1 - Kromm, Arne A1 - Gibmeier, J. A1 - Hannemann, Andreas A1 - Fischer, Tobias A1 - Kannengießer, Thomas T1 - In situ analysis of the strain evolution during welding using low transformation temperature filler materials N2 - Compared to conventional welding consumables using low transformation temperature (LTT) filler materials is an innovative method to mitigate tensile residual stresses due to delayed martensite transformation of the weld. For the effective usage of LTT filler materials, a deeper understanding of the complex processes that lead to the final residual stress state during multipass welding is necessary. Transformation kinetics and the strain evolution of multi-pass welds during welding were investigated in situ at the beamline HEMS@PETRAIII, Germany. Compared to conventional welds, the total strain was reduced and compression strain was achieved when using LTT filler materials. For an optimal use of the LTT effect in the root of multi-pass welds, the alloying concept must be adapted taking care of dilution. KW - Low transformation temperature filler materials KW - Synchrotron diffraction KW - Phase transformation KW - Multi-pass welding KW - ADXRD PY - 2018 DO - https://doi.org/10.1080/13621718.2018.1525150 SN - 1362-1718 SN - 1743-2936 VL - 24 IS - 3 SP - 243 EP - 255 PB - Taylor & Francis AN - OPUS4-46039 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -