TY - CONF A1 - Weber, Gert A1 - Göklü, S. T1 - Schweißeignung und Prozesssicherheit beim Widerstandspunktschweißen hoch fester Mehrphasenstähle im Rohkarosserie-Leichtbau T2 - EUROJOIN 5 ; 5th European Conference on Welding, Joining and Cutting CY - Wien, Österreich DA - 2004-05-13 KW - Hoch feste Mehrphasenstähle KW - Widerstandspunktschweißen PY - 2004 VL - 5 SP - V9-1-V9-30 CY - Wien AN - OPUS4-4721 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert A1 - Göklü, S. T1 - Resistance Spot Welding of High-Strength Multi-Phase Steels T2 - 3rd International Seminar on Advances in Resistance Welding CY - Berlin, Germany DA - 2004-11-17 KW - Resistance spot welding KW - Multi-phase steels KW - Advanced high-strength steels KW - AHSS PY - 2004 SP - 18 EP - 35 PB - SWANTEC Software and Engineering CY - Hoersholm, Denmark AN - OPUS4-4722 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert T1 - Resistance Spot Welding of High Strength Multi Phase Steels N2 - In the lightweight body shell mass production of automobiles the resistance welding process for joining high strengths multi phase steels is the most important joint procedure. For uncoated and hot dip zinc coated high strength TRIP steels, complex phase steels and martensite phase steels statements on process reliability in resistance spot welding based on two- and three-dimensional weldability lobes will be given. A comparison of weldability lobes of uncoated and hot dip zinc coated high strength steel sheets with reference sheets of mild steels will be carried out. This is realized with different electrode forces for short-, medium- and longtime welds. Especially the influence of the electrode force and welding time are studied separately in two-dimensional and commonly in threedimensional weldability lobes. A procedure for welding parameter optimisation in regard to maximal process reliability for the high strength multi phase steels is applied. Based on the electrode wear and the process reliability, statements on the weldability of high strength multi phase steels are formulated. Furthermore, results on the influence of the welding parameters on the hardness and the fatigue behaviour of the spot welded joints will be given. T2 - The 3rd International Seminar on Advances in Resistance Welding CY - Berlin, Germany DA - 2004-11-16 PY - 2004 AN - OPUS4-4727 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert T1 - Widerstandspunktschweißen hochfester Mehrphasenstähle für den Karosserie-Leichtbau: Schweißbereiche - Pro-zesssicherheit - Aufhärtung - Festigkeit N2 - Das Widerstandspunktschweißen ist das dominierende Fügeverfahren in der Massenfertigung von Automobil-Rohkarosserien aus Stahlfeinblechen. Dies gilt insbesondere für moderne hoch feste Mehrphasenstähle, die bei sehr hoher Festigkeit gleichzeitig ein gutes Umformvermögen aufweisen. Diese hoch festen Stahlwerkstoffe werden zur Gewichtsreduzierung und zur Verbrauchsminimierung bei gleichbleibender oder verbesserter Fahrgastzellensicherheit zunehmend im Rohkarosserie-Leichtbau eingesetzt. Mit dem Widerstandspunktschweißen liegt ein Verfahren vor, mit dem sich diese innovativen Werkstoffe prozesssicher und wirtschaftlich fügen lassen. Die neuentwickelten hoch festen Mehrphasenstähle sind - nach steigender Festigkeit geordnet - Dualphasenstähle (DP), Restaustenitstähle (RA) Komplexphasenstähle (CP) und Martensitphasenstähle (MS). Im vorliegenden Beitrag werden für unverzinkte und feuerverzinkte Varianten dieser Stähle Schweißbereiche für verschiedene Schweißparameter ermittelt und in Schweißbereichsdiagrammen dargestellt. Aus den dreidimensionalen Schweißbereichsdiagrammen werden für jeden der Stähle die optimalen Schweißparameter hinsichtlich einer hinreichend großen Prozesssicherheit abgeleitet. Für ausgewählte feuerverzinkte Stähle wird der Einfluss der Schweißparameter Elektrodenkraft und Schweißzeit auf die Qualitätsmerkmale Punktdurchmesser und Scherzugkraft untersucht. Darüber hinaus werden für alle Mehrphasenstähle exemplarische Härteverläufe über der Fügestelle dargestellt. T2 - 19. DVS-Sondertagung Widerstandsschweißen CY - Duisburg, Germany DA - 2004-05-26 PY - 2004 AN - OPUS4-4728 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert T1 - Resistance Spot Welding of High-Strength Multi-Phase Steels T2 - Seminar on Advances in Resistance Welding CY - Berlin, Germany DA - 2004-11-17 PY - 2004 AN - OPUS4-7597 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert A1 - Göklü, S. T1 - Resistance Spot Welding of Advanced High Strength Steels - Influence of Welding Parameters and Electrode Cap Type T2 - International Conference of IIW CY - Prague, Czech Republic DA - 2005-07-14 KW - Resistance spot welding KW - Advanced high-strength steels (AHSS) PY - 2005 SP - 22 pages PB - IIW CY - Prag AN - OPUS4-10302 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert T1 - Weldability and Process Reliability in Resistance Spot Welding of High Strength Multi Phase Steels in Lightweight Body Shell Mass Production T2 - Eurojoin 5 Internationaler Kongress der EWF CY - Vienna, Austria DA - 2004-05-13 PY - 2004 AN - OPUS4-4941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weber, Gert A1 - Göklü, S. T1 - Resistance Spot Welding of Uncoated and Zinc Coated Advanced High-Strength Steels (AHSS) Weldability and Process Reliability-Influence of Welding Parameters KW - Resistance Spot Welding KW - Advanced High-Strength Steels (AHSS) PY - 2006 SN - 0043-2288 SN - 1878-6669 VL - 50 IS - 3/4 (IIW-1722-05 (ex-doc. III-1347-05)) PB - Springer CY - Oxford AN - OPUS4-11079 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert T1 - Schweißeignung beim Widerstandspunktschweißen hoch fester Mehrphasenstähle (AHSS) für den Rohkarosserie-Leichtbau T2 - SWAC Innovationsdays 2005, Fa. S.W.A.C. GmbH, Safeweld Center CY - Taufkirchen, Germany DA - 2005-09-29 PY - 2005 AN - OPUS4-11160 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert A1 - Mellmann, Günter T1 - Zkušenosti o úcincích vnejších vlivù na prevnost v tlaku u predpjatých betonových mostù T2 - Die Lebensdauer von Tragkonstruktionen von Betonbauten und Großplattenhäusern CY - Brno, Czech Republic DA - 1975-10-13 PY - 1975 SP - 249 EP - 252 CY - Brno AN - OPUS4-16141 LA - ces AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gaul, Holger A1 - Weber, Gert A1 - Rethmeier, Michael T1 - Influence of HAZ cracks on fatigue resistance of resistance spot welded joints made of advanced high strength steels N2 - A method is reported with which heat affected zone (HAZ) cracks in a specific region of spot welded joints, made of advanced high strength steels, could be realised. The influence of HAZ cracks on the fatigue behaviour, which is the focus of the contribution, was studied by evaluating the stiffness characteristics as a function of the number of cycles N in comparison with crack-free specimens, i.e. by analysing HAZ and fatigue cracks on the specimen surface and the surface of fatigue fractures containing beach marks. It was found that the fatigue cracks are not initiated at the HAZ cracks. The number of cycles to failure Nf is not significantly reduced for specimens with HAZ cracks. Overall, the examinations did not reveal any influence of HAZ cracks on the fatigue strength of resistance spot welded joints. KW - Discontinuities KW - AHSS KW - HAZ crack KW - Spot welding KW - Advanced high strength steels KW - Fatigue PY - 2011 DO - https://doi.org/10.1179/1362171810Y.0000000031 SN - 1362-1718 SN - 1743-2936 VL - 16 IS - 5 SP - 440 EP - 445 PB - Maney CY - London AN - OPUS4-24214 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Rethmeier, Michael A1 - Weber, Gert A1 - Gaul, H. A1 - Brauser, Stephan T1 - Untersuchungen zur Ermüdungsfestigkeit von Widerstandspunktschweißverbindungen aus hochfesten Mehrphasenstählen unter Berücksichtigung fertigungsspezifischer Einflüsse N2 - Unter den rauen Bedingungen in der Automobilrohkarosseriefertigung lassen sich schweißbedingte Imperfektionen wie Risse beim Widerstandspunktschweißen von hochfesten Stählen nicht immer vermeiden. Für die sichere Auslegung ist die Kenntnis über den Einfluss solcher Risse von erheblicher Bedeutung. PY - 2011 SN - 978-3-942541-04-6 VL - P 802 SP - 1 EP - 86 PB - Verlag und Vertriebsgesellschaft mbH CY - Düsseldorf AN - OPUS4-25450 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Xu, Ping A1 - Krause, Hans-Joachim A1 - Weber, Gert T1 - Vereinheitlichung von gefügten Dünnblechproben für Schwingversuche im Zeitfestigkeitsbereich PY - 2001 SN - 3-87155-671-8 N1 - Serientitel: DVS-Berichte – Series title: DVS-Berichte IS - 213 SP - 59 EP - 68 PB - DVS-Verl. CY - Düsseldorf AN - OPUS4-1119 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weber, Gert A1 - Xu, Ping T1 - Unification of Specimens and Test Procedures for Fatigue Testing of Joined Thin Sheet Metal Structures T2 - 55th International Conference Advanced Processes and Technologies in Welding and Allied Processes CY - Copenhagen, Denmark DA - 2002-06-24 PY - 2002 SN - 0043-2288 SN - 1878-6669 VL - 46 IS - III-1206-02 PB - Springer CY - Oxford AN - OPUS4-1445 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weber, Gert T1 - Weldability Lobes in Resistance Spot Welding T2 - 55th International Conference Advanced Processes and Technologies in Welding and Allied Processes CY - Copenhagen, Denmark DA - 2002-06-24 PY - 2002 SN - 0043-2288 SN - 1878-6669 VL - 46 IS - III-1207-02 PB - Springer CY - Oxford AN - OPUS4-1446 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Weber, Gert T1 - Fuzzy-Klassifikation beim Punktschweißen T2 - MessComp '95 CY - Wiesbaden, Deutschland DA - 1995-09-05 KW - Punktschweissen KW - Qualitätssicherung KW - Fuzzy-Klassifikation PY - 1995 SN - 3-924651-48-5 SP - 48 EP - 50 PB - Network CY - Hagenburg AN - OPUS4-588 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert A1 - Burmeister, J. T1 - Online Process Monitoring by Fuzzy Classification during AC Resistance Welding T2 - International Conference at the 53rd Annual Assembly of the International Institute of Welding CY - Florence, Italy DA - 2000-07-13 KW - Online Process Monitoring PY - 2000 SP - 1 EP - 12 AN - OPUS4-763 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Weber, Gert A1 - Bschorr, T. A1 - Cramer, H. A1 - Hahn, Oliver A1 - Rethmeier, Michael A1 - Thommes, H. ED - da Silva, L.F.M. ED - Altenbach, H. T1 - Hybrid bonding of advanced high strength steels in the lightweight body shell design for the automobile manufacturing N2 - In the lightweight body shell mass production of automobiles, the application of hybrid bonding techniques becomes more and more important. Especially the combination of adhesive bonding and resistance spot welding called weldbonding is of great importance. The target of this contribution is to show the influence of medium-viscosity and low-viscosity structural adhesives on the process reliability of the weldbonding process and the mechanical properties of the hybrid bonded joints. The given results are based on the application of an epoxy PUR-based, an epoxy resin-based and a rubber-based adhesive system for joining a mild and some different advanced high strength steels (AHSS). It will be shown that both the process reliability of the weldbonding process and the mechanical behaviour of the weldbonded joints are influenced by the combinations of the base metals, the applied adhesive systems and the choice of the joining parameters. The behaviour of the weldbonded joints will be studied under quasi-static and impact loads. The discussion of the metallurgical structure of the weldbonded joints depending on the joining parameters will be given, too. Furthermore, the fatigue behaviour of the weldbonded joints will be studied. KW - Advanced high strength steels KW - Hybrid bonding KW - Lightweight body shell design KW - Weldbonding process reliability KW - Weldbonded joint behaviour PY - 2010 SN - 978-3-642-12666-6 DO - https://doi.org/10.1007/978-3-642-12667-3_22 N1 - Serientitel: Advanced Structured Materials – Series title: Advanced Structured Materials VL - 3 SP - 343 EP - 372 PB - Springer AN - OPUS4-23150 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gaul, Holger A1 - Weber, Gert A1 - Rethmeier, Michael T1 - Evaluation of fatigue crack propagation in spot welded joints by stiffness measurements N2 - Resistance spot welded joints made of two advanced high strength steels (AHSS) and one high strength steel (HSS) were examined. In the high cycle fatigue regime tests were realised for one loading condition, and the load and the displacement were measured. From the load and displacement range, the stiffness was calculated and in situ normalised to its value after 1000 cycles. It was thus possible to use the normalised stiffness evaluated during the experiment as failure criterion for the fatigue test of resistance spot welded joints. In order to evaluate this failure criterion, fatigue cracks were produced in the three different steel grades mentioned above according to user-specified levels of the normalised stiffness. It was found that the fatigue crack area increases linearly and the through-sheet-thickness crack length exponentially with decreasing stiffness. The comparison of the fatigue crack propagation during the fatigue test of the three different tested base metals showed very similar values. The comparability of fatigue tests performed on spot welded joints might thus be improved by the in situ evaluated stiffness as a failure criterion. This can be also used in further work to verify results of computer simulations of the stress intensity factor at spot welds with the help of experimental results. KW - Resistance spot welding KW - Fatigue KW - Frequency KW - Stiffness KW - Advanced high strength steels KW - Crack growth PY - 2011 DO - https://doi.org/10.1016/j.ijfatigue.2010.12.005 SN - 0142-1123 VL - 33 IS - 5 SP - 740 EP - 745 PB - Elsevier CY - Oxford AN - OPUS4-22207 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brauser, Stephan A1 - Pepke, Lutz-Alexander A1 - Weber, Gert A1 - Rethmeier, Michael A1 - Göklü, S. T1 - Einfluss der Schweißstromform auf die Schweißbereiche und die Festigkeit beim Widerstandpunktschweißen moderner Automobilwerkstoffe T2 - 21. DVS-Sondertagung "Widerstandsschweissen 2010" CY - Duisburg, Deutschland DA - 2010-05-05 KW - Widerstandschweißen KW - Schweißbereiche KW - Anlagenkonfiguration KW - Schwingfestigkeit PY - 2010 SP - 1 EP - 7(?) CY - Duisburg AN - OPUS4-21561 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert A1 - Rethmeier, Michael A1 - Brauser, Stephan T1 - Extended weldability lobes in resistance spot welding of advanced high strength steels (AHSS) T2 - EUROJOIN 7 - 7th European congress on joining technology CY - Venice, Italy DA - 2009-05-21 KW - Resistance welding KW - High strength steels PY - 2009 IS - Technical Session 2 SP - 1 EP - 15 AN - OPUS4-20524 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert T1 - Extended Weldability Lobes in Resistance Spot Welding of Advanced High Strength Steels (AHSS) T2 - EUROJOIN 7 - Seventh European Congress on Joining Technology CY - Venice, Italy DA - 2009-05-21 PY - 2009 AN - OPUS4-20369 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brauser, Stephan A1 - Weber, Gert A1 - Rethmeier, Michael T1 - Potenzial optischer Dehnungsfeldmessung zur Charakterisierung der Eigenschaften von Widerstandspunktschweißverbindungen N2 - Die Ermittlung lokaler Werkstoffkennwerte im Schweißbereich ist für die Auslegung sicherheitsrelevanter Bauteile insbesondere durch Finite-Elemente-Berechnungen von großer Bedeutung. Konventionelle Prüfmethoden können lediglich globale Kennwerte bereitstellen, die jedoch gerade für die Berechnung widerstandspunktgeschweißter Bauteile häufig nicht ausreichen, da diese durch das Vorliegen örtlich eng begrenzter Fügezonen gekennzeichnet sind. Moderne Prüfmethoden wie die optische Dehnungsfeldmessung ermöglichen hingegen eine orts- und zeitkonkrete Bestimmung der Werkstoffkenndaten. Um das Potenzial optischer Dehnungsfeldmessungen für das Charakterisieren des lokalen Werkstoffverhaltens von Punktschweißverbindungen zu ermitteln, wurden Scherzugversuche sowie Zugversuche an widerstandspunktgeschweißten hochfesten Stählen durchgeführt. Die Ergebnisse zeigen das hohe Potenzial dieses Verfahrens sowohl für die Quantifizierung des lokalen Dehnungsverhaltens im Fügebereich als auch für die Ermittlung lokaler Werkstoffkenndaten. PY - 2010 SN - 0036-7184 VL - 62 IS - 9 SP - 496 EP - 500 PB - Verl. für Schweißen u. Verwandte Verfahren, DVS-Verl. CY - Düsseldorf AN - OPUS4-22163 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert T1 - Mechanical Properties of Weldbonded Joints of Advanced High Strength Steels T2 - 4th International Conference on Advanced Computational Engineering and Experimenting, ACE-X CY - Paris, France DA - 2010-07-08 PY - 2010 AN - OPUS4-22151 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -