TY - JOUR A1 - Lorenz, S. A1 - Kannengießer, Thomas A1 - Posch, G. T1 - Suitability of high-alloyed flux-cored wire electrodes for laser-GMA hybrid welding JF - Welding and cutting N2 - The object of this research project related to investigations into the qualification of flux-cored wire electrodes for the laser-GMA hybrid welding of high-alloyed steels. Because of its annular metal shell and the powdery filling, this type of wire electrode permits stable, low-spatter metal transfer comparable with that in the spray arc, particularly in the upper range of the attainable deposition rates. In contrast with this, controlled metal transfer during the deposition of solid wire electrodes is achieved using pulsed arc technology. When these filler materials are welded, the properties specific to the material and to the process have a significant influence on the weld metallurgy as well as on the process stability. Tests were carried out on the AISI 403L (X2CrNi1911) high-alloyed base material in order to investigate the transferability of the attainable material properties from GMA welding to laser-GMA hybrid welding. Four wire electrodes were used according to DIN EN 12072 and DIN EN ISO 17633: a T 19 9 L P M 1 rutile fluxcored wire designed specifically for welding in position, a T 19 9 L R M (C) 3 rutile flux-cored wire suitable for welding in the flat position, a T 19 9 L M M 1 metal-powder flux-cored wire as well as a G 19 9 L Si solid wire. KW - Welding KW - Laser GMA hybrid welding PY - 2012 SN - 1612-3433 VL - 11 IS - 3 SP - 181 EP - 187 PB - DVS - German Welding Society CY - Düsseldorf AN - OPUS4-26298 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lorenz, Stephan A1 - Kannengießer, Thomas A1 - Posch, G. ED - Karoly Jarmai, ED - Jozsef Farkas, T1 - Solid wire vs. flux cored wire - comparing investigations for GMA-laser-hybrid welding T2 - Design, Fabrication and Economy of Welded Structures - International Conference Proceedings, April 24-26, 2008, Miskolc, Hungary T2 - Design, Fabrication and Economy of Welded Structures - International Conference CY - Miskolc, Hungary DA - 2008-04-24 KW - Tubular cored electrode KW - Solid wire electrode KW - GMA-laser-hybrid welding KW - Structural optimization KW - Fatigue design KW - Frames KW - Hollow sections KW - Plated structures PY - 2008 SN - 978-1-904275-28-2 SP - 477 EP - 484 PB - Horwood Publishing Ltd. AN - OPUS4-17509 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lorenz, Stephan A1 - Kannengießer, Thomas A1 - Herold, H. A1 - Posch, G. ED - P. Mayr, ED - G. Posch, ED - H. Cerjak, T1 - Aspects of positional laser-GMA-hybrid welding using high alloyed tubular cored wire electrodes T2 - 61st Annual Assembly and International Conference of the International Institute of Welding (IIW) "Safety and Reliability of Welded Components in Energy and Processing Industry" (Proceedings) T2 - 61st Annual Assembly and International Conference of the International Institute of Welding (IIW) "Safety and Reliability of Welded Components in Energy and Processing Industry" CY - Graz, Austria DA - 2008-07-06 KW - Laser-GMA-hybrid welding KW - Positional welding KW - Vertical position KW - Metal cored wire electrode KW - Rutile tubular cored wire KW - Solid wire PY - 2008 SN - 978-3-85125-019-0 SP - 479 EP - 484 PB - Verlag der Technischen Universität Graz CY - Graz, Austria AN - OPUS4-17800 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lorenz, Stephan A1 - Kannengießer, Thomas A1 - Herold, H. A1 - Posch, G. T1 - Laser-GMA-hybrid welding with high alloyed cored wire electrodes T2 - Stainless Steel World 2007 Conference papers T2 - Stainless Steel World 2007 Conference CY - Maastricht, The Netherlands DA - 2007-11-06 KW - Laser-GMA-hybrid welding KW - Solid-state laser KW - Tubular cored wire electrodes KW - Solid wire electrodes KW - High alloyed steel AISI 304L KW - Welding metallurgy PY - 2007 SN - 9789073168282 IS - CD-ROM SP - 1 EP - 16 AN - OPUS4-16184 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lorenz, Stephan A1 - Kannengießer, Thomas A1 - Herold, H. A1 - Posch, G. T1 - Suitability of high alloyed wire electrodes for the positional laser-GMA-hybrid welding JF - international journal of microstructure and materials properties N2 - Laser-gas metal arc (GMA)-hybrid welding enables a high deposition rate and a stable welding process. Process stability was found to be profoundly dependent on the type of the applied filler wire (solid or tubular cored). Whereas solid wires are deposited in pulsed arc mode, tubular cored wire electrodes are weldable by a stable spray-arc process within a wide operating range. This fact applies above all to a high alloyed metal cored wire electrode, of which the achievable deposition rates exceed the upper limits recommended by the manufacturer. A further interesting aspect is the application of a rutile tubular cored wire for positional laser-GMA-hybrid welding. A modern 20 kW-fibre laser source was available for the experiments. This study is concerned with the weldability of high alloyed tubular cored electrodes for high power laser-GMA-hybrid welding. Results obtained from comparative investigations between tubular cored and solid wire electrodes relating to process stability are summarised. KW - Austenitic stainless steel KW - Flux cored wire electrodes KW - Solid wire electrodes KW - Laser hybrid welding KW - Stainless steel KW - Laser welding KW - Welding speed KW - Welding position KW - Fibre laser KW - Process stability KW - Vertical position down KW - Charpy V-notch impact test KW - GMA welding KW - Gas metal arc welding KW - Weldability PY - 2010 DO - https://doi.org/10.1504/IJMMP.2010.035943 SN - 1741-8410 SN - 1741-8429 VL - 5 IS - 2/3 SP - 245 EP - 260 PB - Inderscience Enterprises Ltd CY - Genève, Switzerland AN - OPUS4-22270 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lorenz, Stephan A1 - Kannengießer, Thomas A1 - Posch, G. T1 - Eignung hochlegierter Fülldrahtelektroden zum Laserstrahl-MSG-Hybridschweißen JF - Schweißen und Schneiden : Fachzeitschrift für Schweißen und verwandte Verfahren N2 - Gegenstand dieses Forschungsprojekts waren Untersuchungen zur Qualifikation von Fülldrahtelektroden für das Laserstrahl-MSG-Hybridschweißen hochlegierter Stähle. Dieser Typ Drahtelektrode ermöglicht aufgrund seines ringförmigen Metallmantels und der pulverartigen Füllung insbesondere im oberen Bereich der erzielbaren Abschmelzleistungen einen stabilen, spritzerarmen Werkstoffübergang vergleichbar dem im Sprühlichtbogen. Im Gegensatz dazu wird beim Abschmelzen von Massivdrahtelektroden ein kontrollierter Werkstoffübergang durch die Impulslichtbogentechnik erreicht. Die Werkstoff- und prozessspezifischen Eigenschaften beim Schweißen dieser Zusatzwerkstoffe haben einen signifikanten Einfluss auf die Schweißnahtmetallurgie sowie die Prozessstabilität. Zur Untersuchung der Übertragbarkeit der erzielbaren Werkstoffeigenschaften vom MSG-Schweißen auf das Laserstrahl-MSG-Hybridschweißen wurden Versuche am hochlegierten Grundwerkstoff AISI403L (X2CrNil911) durchgeführt. Als Zusatzwerkstoffe gemäß DIN EN 12 072 und DIN EN ISO 17 633 kamen vier Drahtelektroden, ein eigens für das Positionsschweißen konzipierter Rutilfülldraht 19 9 L P M1, ein zum Schweißen in Wannenposition geeigneter Rutilfülldraht T 19 9 L R M (C) 3, ein Metallpulverfülldraht T199LMM1 sowie ein Massivdraht G19 9 L Si zum Einsatz. KW - Fülldrahtelektroden KW - Laserstrahlschweißen KW - Metall-Schutzgasschweißen KW - Hybridschweißen KW - Werkstofffragen KW - Zusatzwerkstoffe PY - 2011 SN - 0036-7184 VL - 63 IS - 5 SP - 222 EP - 228 PB - Verl. für Schweißen u. Verwandte Verfahren, DVS-Verl. CY - Düsseldorf AN - OPUS4-23850 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lorenz, Stephan A1 - Kannengießer, Thomas A1 - Michael, Thomas A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Posch, G. T1 - Laserstrahl-MSG-Hybridschweißen mit hochlegierten Massiv- und Fülldrahtelektroden T2 - Die Verbindungs Spezialisten 2009 - Große Schweißtechnische Tagung (DVS-Berichte) T2 - Die Verbindungs Spezialisten 2009 - Große Schweißtechnische Tagung CY - Essen, Deutschland DA - 2009-09-14 KW - Laserstrahl-MSG-Hybridschweißen KW - Hochlegiert KW - 1.4306 KW - AISI 304L KW - Positionsschweißen KW - Metastabiler austenitischer Chrom-Nickel-Stahl KW - Metallurgie PY - 2009 SN - 978-3-87155-584-8 VL - 258 SP - 75 EP - 80 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-20107 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -