TY - JOUR A1 - Farag, Zeinab Ramadan A1 - Friedrich, Jörg Florian A1 - Krüger, Simone A1 - Hidde, Gundula A1 - Moustapha, M. E. T1 - Adhesion promotion of thick polyphosphate-poly(allylamine) films onto polyolefin substrates by plasma polymers N2 - The adhesion of thick poly(allylamine)-polyphosphate layers (1 µm) deposited by the wet-chemical layer-by-layer technique (LbL) onto polyethylene or polystyrene (each 100 µm) was very low. To promote the adhesion of these LbL layers the polyolefin substrates were oxidized at the surface by short exposure to the oxygen plasma (2 or 5 s) and subsequently coated with an interlayer of plasma-deposited poly(allylamine) or poly(allyl alcohol) (100 nm). The plasma polymer interlayers have improved strongly the adhesion between polyolefin substrates and polyphosphate coatings. Such phosphate coatings are interesting for life sciences (nucleotide formation) but also for fire retardancy in combination with N-rich compounds such as melamine. The intention was to prefer chemical and hydrogen bonds for adhesion promoting because of their high binding energy. Therefore, the introduced oxygen-containing groups at the polyolefin surface could interact with the OH or NH2 groups of the adhesion-promoting plasma polymer interlayer. These groups were also able to interact strongly with the poly(allylamine)-polyphosphate topcoating. The coated polyolefins were investigated using Fourier Transform Infrared Spectroscopy in Attenuated Total Reflectance mode (FTIR-ATR), X-ray Photoelectron Spectroscopy (XPS), Thermo-Gravimetric Analyses (TGA) and Atomic Force Spectroscopy (AFM) and 90° peel test. KW - Plasma-polymerized poly(allylamine) KW - Adhesion KW - Layer-by-layer deposition KW - Plasma polymerization PY - 2016 UR - http://www.tandfonline.com/doi/abs/10.1080/01694243.2015.1095626 DO - https://doi.org/10.1080/01694243.2015.1095626 SN - 1648-4142 VL - 30 IS - 3 SP - 231 EP - 246 PB - Taylor & Francis AN - OPUS4-35885 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dimitriev, O.P. A1 - Grytsenko, K.P. A1 - Lytvyn, P.M. A1 - Doroshenko, T.P. A1 - Briks, J.L. A1 - Tolmachev, A.I. A1 - Slominskii, Y.L. A1 - Kudinova, M.A. A1 - Schrader, S. A1 - Schulze, Rolf-Dieter A1 - Friedrich, Jörg Florian T1 - Substrate-induced self-assembly of donor-acceptor type compounds with terminal thiocarbonyl groups N2 - Two types of conjugated thiocarbonyl-terminated compounds have been synthesized and their ability to be adsorbed on surfaces of the different nature, namely, glass, polytetrafluoroethylene (PTFE), and gold has been studied. Different morphology of the films prepared by thermal vacuum evaporation and drop-casting from solutions has been observed depending on the surface used. It has been found that gold surface has a unique property to influence self-assembly of both monolayer and larger aggregates or crystals of the compounds, in contrast to glass and PTFE substrates. It was found that thiocarbonyl group is able to be chemisorbed to the gold surface. However, it was concluded that in spite of the fact that the thiocarbonyl groups are important for the chemical interaction with the gold surface, physical adsorption on the substrate surface, compound–compound and compound–solvent (when using solution) interactions are of great significance to drive self-assembly of the final film. KW - Thiocarbonyl group KW - Donor–acceptor compound KW - Gold surface KW - Aggregation KW - Film morphology PY - 2013 DO - https://doi.org/10.1016/j.tsf.2013.05.084 SN - 0040-6090 VL - 539 SP - 127 EP - 133 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-30571 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ramanujam, Maalolan A1 - Mix, Renate A1 - Wagner, M. A1 - Friedrich, Jörg Florian T1 - Effect of Br gassing after Ar plasma treatment of polyolefins N2 - For simulation and acceleration of artificial polymer ageing, polyolefin foils were exposed to low-pressure Ar plasma. Plasma particle bombardment and irradiation induce C–C and C–H bond scissions by σ→σ* excitations on the surface and in near-surface layers. Consequently, radicals are generated. They react by recombination, cross-linking, metastable trapping of the radical site or formation of olefinic double bonds. The long-living and metastable trapped C-radicals as well as double bonds in polyolefins were immediately exposed to bromine vapour without breaking the vacuum after switching-off the plasma. These reactive sites rapidly react with the molecular bromine under formation of C–Br bonds. For 5 min of argon plasma exposure, the elemental concentration of bromine was 13% for polyethylene and 22% Br/C for polypropylene as analysed by X-ray photoelectron spectroscopy. Nevertheless, not all C radical sites have reacted with bromine. Later on, when the polyolefins brought in contact with ambient air, an additional post-plasma reaction of the remaining trapped radicals with oxygen was observed. The oxygen concentrations were lower after bromine gassing, thus repressing partially the post-plasma oxidation in the analysed layer (ca. 6 nm) by radical quenching. Such bromination took place either at the surface or in near-surface layers because the Attenuated Total Reflectance (ATR)-FTIR spectra (sampling depth ca. 2500 nm) did not show significant changes for argon plasma-treated PE foils with and without bromine vapour exposure. Further addition of bromine may also occur on C=C double bonds. KW - Ageing of polyolefins KW - Argon plasma KW - Radical formation KW - Formation of double bonds PY - 2013 DO - https://doi.org/10.1080/01694243.2012.762326 SN - 0169-4243 SN - 1568-5616 VL - 27 IS - 6 SP - 1828 EP - 1839 PB - VNU Science Press CY - Utrecht AN - OPUS4-30572 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Jörg Florian A1 - Hidde, Gundula A1 - Lippitz, Andreas A1 - Unger, Wolfgang T1 - Plasma bromination of graphene for covalent bonding of organic molecules N2 - Plasma-chemical bromination applied to graphitic materials, in particular to highly ordered pyrolytic graphite is reviewed. The resulting bromination efficiency of the plasma-chemical treatment was subject of systematic process optimization. The plasma of elemental bromine vapour produced bromine concentrations on graphene surfaces of more than 30 % Br/C using either inductively or capacitively coupled low-pressure radio-frequency plasmas. Plasma brominated graphite surfaces have been studied by Near Edge X-ray Absorption Fine Structure, X-ray Photoelectron Spectroscopy, Atomic Force Microscopy and Scanning Electron Microscopy. The introduction of bromine into graphene-like graphite layers and its binding situation were investigated. To study the physical effect of the plasma bromination process, Kr plasma was also used because of its chemical inertness but similar atomic mass. Covering the samples with a Faraday cage or with a LiF window should help to differentiate between physical, chemical and radiation effects of the plasma. Bromination was assigned to radical or electrophilic addition of bromine onto fully substituted aromatic double bonds (sp² C) with exothermal reaction enthalpy. Low bromination shows a strong decay of aromatic double bonds, higher bromination percentage let disappear all aromatic rings. The formed C–Br bonds were well suited for efficient grafting of organic molecules by post-plasma wet-chemical nucleophilic substitution. This grafting onto the graphene surface was demonstrated using aminosilane and different diamines. The bromination of double bonds changes the hybridization of carbon atoms from plane sp² to tetrahedral sp³ hybridization. Thus, the plane topography of graphene is destroyed and the conductivity is lost. KW - Graphene KW - Bromination KW - Grafting of diamines KW - Plasma KW - Organic graphting PY - 2014 DO - https://doi.org/10.1007/s11090-013-9509-x SN - 0272-4324 VL - 34 SP - 621 EP - 645 PB - Plenum Publ. Corp. CY - New York, NY, USA AN - OPUS4-30575 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Friedrich, Jörg Florian ED - Gutowski, W. ED - Dodiuk, H. T1 - Study of metal-polymer interfaces: Relevance to adhesion KW - Polymer surface modification KW - Adhesion KW - Spacer PY - 2013 SN - 978-90-04-20173-6 SN - 978-90-04-20174-3 SP - 3 EP - 33 PB - CRC Press AN - OPUS4-30576 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heise, C. A1 - Schedler, U. A1 - Wettmarshausen, Sascha A1 - Friedrich, Jörg Florian T1 - Plasma-brominated cyclo-olefin polymer slides: Suiitable macroinitiators for activator regenerated by electron transfer/atom radical transfer polymerization N2 - Activators regenerated by electron transfer–atom radical transfer polymerization (ATRP) as a controlled living polymerization are distinguished by their acceptance of small amounts of transition-metal complexes and oxygen and by their tolerance of reducing agents at a high concentration. The precondition of all ATRP applications is the use of homolytic or heterolytic cleavable halides as a dormant species; this allows the propagation of monomer chains. Hence, alkyl bromides are slightly cleavable and are the preferred initiators for ATRP. The bromination of polymer slides used as macroinitiators was carried out under gentle bromoform plasma conditions. This led to an oxidation-resistant stable bromine layer. More than 20 bromines per 100 carbons on the polymer scaffold were permanently bound to the substrate after plasma treatment. The resulting amounts of secondary and tertiary bromines on the polymer scaffold exhibited a suitable macroinitiator concentration for the surface-initiated polymerization of methyl methacrylate and glycidyl methacrylate. KW - Copolymers KW - Functionalization of polymers KW - Grafting KW - Monolayers and polymer brushes KW - Radical polymerization PY - 2014 UR - http://onlinelibrary.wiley.com/doi/10.1002/app.40662/full DO - https://doi.org/10.1002/APP.40662 SN - 0021-8995 SN - 1097-4628 VL - 131 IS - 16 SP - 40662-1 EP - 40662-10 PB - Wiley InterScience CY - Hoboken, NJ AN - OPUS4-30577 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Natte, Kishore A1 - Friedrich, Jörg Florian A1 - Wohlrab, Sebastian A1 - Lutzki, J. A1 - von Klitzing, R. A1 - Österle, Werner A1 - Orts-Gil, Guillermo T1 - Impact of polymer shell on the formation and time evolution of nanoparticle-protein corona N2 - The study of protein corona formation on nanoparticles (NPs) represents an actual main issue in colloidal, biomedical and toxicological sciences. However, little is known about the influence of polymer shells on the formation and time evolution of protein corona onto functionalized NPs. Therefore, silicapoly(ethylene glycol) core–shell nanohybrids (SNPs@PEG) with different polymer molecular weights (MW) were synthesized and exhaustively characterized. Bovine serum albumin (BSA) at different concentrations (0.1–6 wt%) was used as model protein to study protein corona formation and time evolution. For pristine SNPs and SNPs@PEG (MW = 350 g/mol), zeta potential at different incubation times show a dynamical evolution of the nanoparticle–protein corona. Oppositely, for SNPs@PEG with MW ≥2000 g/mol a significant suppression of corona formation and time evolution was observed. Furthermore, AFM investigations suggest a different orientation (side-chain or perpendicular) and Penetration depth of BSA toward PEGylated surfaces depending on the polymer length which may explain differences in protein corona evolution. KW - Nanoparticles KW - Silica KW - PEGylation KW - Protein corona KW - BSA KW - Biointerface PY - 2013 DO - https://doi.org/10.1016/j.colsurfb.2012.11.019 SN - 0927-7765 VL - 104 SP - 213 EP - 220 PB - Elsevier AN - OPUS4-38547 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Natte, Kishore A1 - Österle, Werner A1 - Friedrich, Jörg Florian A1 - von Klitzing, R. A1 - Orts-Gil, Guillermo T1 - Tuning interfacial properties and colloidal behavior of hybrid nanoparticles by controlling the polymer precursor N2 - A facile and versatile synthetic route for controlling the size and surface potential of organic–inorganic hybrid silica nanoparticles (NPs) is introduced in this paper. For polymer-grafted NPs, the density of polymer chains on the surface is strongly affected by the concentration of precursor. Nevertheless, for condensed NPs, the precursor concentration determines the particle size but not the density of polymer chains on the surface or the adsorption of bovine serum albumin (BSA). Results presented here may have Major implications in biomedical and colloidal chemistry since interfacial and colloidal properties are known to drive several processes associated with nanoparticles in biological media. KW - BSA KW - Bio-interface KW - Nanosilica hybrids KW - PEG KW - Protein corona PY - 2012 DO - https://doi.org/10.1002/macp.201200148 SN - 0025-116X SN - 1022-1352 SN - 1521-3935 VL - 213 IS - 22 SP - 2412 EP - 2419 PB - Whiley-VCH CY - Weinheim AN - OPUS4-38549 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Farag, Zeinab A1 - Moustapha, M. A1 - Hidde, Gundula A1 - Friedrich, Jörg A1 - Azzam, M. A1 - Krüger, Simone ED - Mital, K.L. T1 - Promotion of Adhesion of Green Flame Retardant Coatings onto Polyolefins by Depositing Ultra-Thin Plasma Polymer Films N2 - Various methods have been used for introducing fire retardant additives into polymers. Deposition of thick fire retardant coatings directly onto polymer substrates is an alternative technique. An important advantage of the coating technique is the preservation of the physical and chemical integrity of the polymer material. Moreover, the fire retardancy of the polymer materials can be achieved following their production. Suitable coating materials are inorganics, intumescent, char-forming, oxygendiluting, and cooling or radical quenching layers. The most important problem is to achieve sufficient coating thickness to withstand the direct attack of flame and to protect the polymer bulk from pyrolysis, otherwise blistering of coating, caused by emitted pyrolysis gases, is often observed. To avoid blistering of coating, the adhesion between polyolefin substrate and fire retardant coating has to be extraordinarily high. In order to achieve such a high level of adhesion, the polymer surface has to be modified with adhesion-promoting functional groups. The deposition of thin plasma polymers as adhesion-promoting layers with NH2, OH or COOH groups has been the most suited method. These functional groups are able to form covalent bonds and other interactions between the fire-resistant coating and the plasma-modified polyolefin substrate. Additionally, the plasma polymer counteracts the strong mechanical stresses in the laminate on exposure to high temperatures by its flexibility. KW - Plasma KW - Adhesion PY - 2017 SN - 978-1-119-40748-5 SN - 978-1-119-40638-9 DO - https://doi.org/10.1002/9781119407485 VL - 2 SP - 399 EP - 427 PB - Scrivener Publishing CY - Beverly, USA AN - OPUS4-47227 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krüger, Simone A1 - Friedrich, Jörg A1 - Hidde, Gundula A1 - Farag, Zeinab R. A1 - Moustapha, Moustapha E. A1 - Azzam, Maged M. T1 - Promotion of adhesion of green flame retardant coatings onto polyolefins by depositing ultra-thin plasma polymer films: A critical review N2 - Various methods have been used for introducing fire retardant additives into polymers. Deposition of thick fire retardant coatings directly onto polymer substrates is an alternative technique. An important Advantage of the coating technique is the preservation of the physical and chemical integrity of the polymer material. Moreover, the fire retardancy of the polymer materials can be achieved following their production. Suitable coating materials are inorganics, intumescent, char-forming, oxygendiluting, and cooling or radical quenching layers. The most important problem is to achieve sufficient coating thickness to withstand the direct attack of flame and to protect the polymer bulk from pyrolysis, otherwise blistering of coating, caused by emitted pyrolysis gases, is often observed. To avoid blistering of coating, the adhesion between polyolefin Substrate and fire retardant coating has to be extraordinarily high. In order to achieve such a high level of adhesion, the polymer surface has to be modified with adhesion-promoting functional groups. The deposition of thin plasma polymers as adhesion-promoting layers with NH2, OH or COOH groups has been the most suited method. These functional groups are able to form covalent bonds and other interactions between the fire-resistant coating and the plasma-modified polyolefin substrate. Additionally, the plasma polymer counteracts the strong mechanical stresses in the laminate on exposure to high temperatures by its flexibility. The thick fire retardant coatings were chosen based on “green” ecological aspects to avoid flame-initiated emission of toxic or corrosive gases and remains of toxic char. KW - Flame retardant KW - Adhesion KW - Coating PY - 2016 DO - https://doi.org/10.7569/RAA.2016.097314 SN - 2168-0965 SN - 2168-0973 VL - 4 IS - 4 SP - 417 EP - 447 PB - Scrivener Publishing LLC AN - OPUS4-48164 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -