TY - JOUR A1 - Valentini, Martino A1 - De Almeida, Olivier A1 - Kakkonen, Markus A1 - Kalinka, Gerhard A1 - Dorigato, Andrea A1 - Kallio, Pasi A1 - Fredi, Giulia T1 - Effect of fiber surface state on the thermomechanical and interfacial properties of in situ polymerized polyamide 6/basalt fiber composites N2 - This study investigates the thermomechanical properties and interfacial adhesion of novel in-situ polymerized anionic polyamide 6 (aPA6) composites reinforced with basalt fibers (BF). The impact of different BF surface states - as-received (BFa), ethanol-washed (BFw), and thermally desized (BFu) on composite performance is examined through a comprehensive approach. For the first time, anionic PA6/BF composites with very low residual monomer content were successfully produced via thermoplastic resin transfer molding (tRTM). The PA6/BFw composites exhibited the highest interlaminar/interfacial shear strength in short beam shear test (52 ±8 MPa) and fiber push out test (34 ± 11 MPa) tests. Fiber microdebonding test, performed only on PA6/BFw, yielded a low interfacial shear strength (12 ± 4 MPa), which was attributed to droplet porosity resulting from concurrent polymerization and crystallization. Thermal desizing significantly deteriorated interfacial strength (19.6 ± 1.2 MPa in short beam shear test). This multi-technique characterization provides insights into optimizing the fiber–matrix adhesion in these advanced thermoplastic composites. KW - Anionic Polyamide 6 KW - Reactive thermoplastics KW - Basalt fibers KW - Microdebonding KW - Fiber push out KW - Short beam shear test PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-623596 DO - https://doi.org/10.1016/j.compositesa.2024.108681 SN - 1878-5840 VL - 190 SP - 1 EP - 15 PB - Elsevier Ltd. CY - Niederlande AN - OPUS4-62359 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -