TY - JOUR A1 - Robens-Radermacher, Annika A1 - Schmidt, Wolfram A1 - Unger, Jörg F. A1 - Mezhov, Alexander T1 - Characterization of temperature influence on the structural build-up of 3D printed concrete N2 - 3D concrete printing technologies enhance design freedom while reducing material use and costs without the need for formwork. Thereby, structural build-up is the key property governing stability and early strength evolution of 3D printed concrete after placement. Structural build-up is influenced by various factors, i.e., environmental conditions such as temperature. In this paper, the influence of ambient temperature on structural build-up was investigated through experimental and numerical approaches. Three experimental setups (small amplitude oscillatory shear, constant shear rate, and small amplitude oscillatory extensional tests) were applied to materials of increasing complexity under varying temperature conditions. A common modeling framework based on the maturity approach was developed to capture the time and temperature evolution. A stochastic framework was employed to estimate the unknown model parameters using experimental data. Experimental results demonstrate a significant temperature influence on structural build-up, consistent across all test setups and materials. The calibrated models successfully predict the structural build-up under different temperatures, confirming the applicability of the maturity approach to rheological parameters at early age. Furthermore, the stochastic parameter estimation allows a correct quantification of the uncertainties, enhancing model reliability. The comparison of two time evolution formulations indicates that a model with an additional linear stage is required for predicting the increase of the storage moduli ( $${G}{\prime}$$ G ′ , $${E}{\prime}$$ E ′ ). In conclusion, the study demonstrates that temperature significantly affects the structural build-up, and that the proposed modeling approach allows to predict this behavior. KW - Structural build-up KW - 3D concrete printing KW - Rheology KW - Temperature influence KW - Modeling KW - Green intelligent building PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-654138 DO - https://doi.org/10.1617/s11527-025-02931-3 SN - 1359-5997 VL - 59 IS - 2 SP - 1 EP - 20 PB - Springer Science and Business Media LLC AN - OPUS4-65413 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Cunnigham, P. R. A1 - Shaba, A. F. A1 - Olonade, K. A. A1 - Ndawula, J. A1 - Tawiah, A. T. A1 - Marangu, J. M. A1 - Tlhatlha, Pheladi A1 - Obeng, E. ED - Banhia, N. T1 - Informal Sector Inclusion in Sustainable Concrete Construction in Africa N2 - Concrete used as a construction material is inevitable in Africa’s rapid urban growth, despite its significant contribution to carbon emissions. Hence, best practice concrete with reduced Portland cement clinker needs to be applied. The highly informal nature ofAfrica’s construction sector could impede the implementation of sustainable concrete construction. Although urgent need for economisation unintentionally often leads informal actors to operate according to circularity principles, the sector lacks awareness of climate challenges and incentives for adopting climate-friendly materials and technologies. In addition, the informal sector is prone to fraudulent adulterated materials and components causing challenges for safe and durable construction. The authors elaborate on the crucial role of the informal sector in driving sustainable construction forward, despite the lack of policies and disinterest from regulatory bodies. Solutions through education, communication, and quality control are proposed and discussed. T2 - 77th RILEM Annual Week and the 1st Interdisciplinary Symposium on Smart & Sustainable Infrastructures (ISSSI 2023) CY - Vancouver, Canada DA - 04.09.2023 KW - Cement testing KW - Hydration KW - Economic development KW - Informal sector KW - Cement chemistry PY - 2024 SN - 978-3-031-53391-4 DO - https://doi.org/10.1007/978-3-031-53389-1_47 VL - 48 SP - 506 EP - 520 PB - Springer Nature Switzerland AG CY - Schweiz AN - OPUS4-61586 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - de Carvello, J. M. F. A1 - Schmidt, Wolfram A1 - Kühne, Hans-Carsten A1 - Fiorotti Peixoto, R. A. T1 - Influence of high-charge and low-charge PCE-based superplasticizers on Portland cement pastes containing particle-size designed recycled mineral admixtures N2 - Design : and use of engineered recycled mineral admixtures obtained from industrial and mineral waste are promising strategies to increase the range of materials suitable for use in cement-based composites. In this work, Portland cement-blended pastes containing mineral admixtures designed for improving particle packing were evaluated in the presence of low- and high-charge polycarboxylate-based superplasticizers. The powders were obtained from basic oxygen furnace slag, iron ore tailings, quartz mining tailings, and quartzite mining tailings. The zeta-potentials of the particles were obtained via electrophoretic mobility. The flow properties were evaluated by rheological tests performed in a Couette type rheometer. The hydration kinetics was evaluated by isothermal calorimetry and an adapted method based on the Vicat needle test. The high-charge PCE and the finer mineral admixtures produced more stable blends. Coarser mineral admixtures led to increased flowability and delayed hydration compared to finer ones. Steel slag powders presented the most significant plasticizer effects, but also the largest setting delays and segregation tendency. Quartz-rich superfines reduced the setting delays caused by the superplasticizers. In summary, both superplasticizers were effective in improving flow properties, but the high-charge PCE was effective in preventing segregation in pastes containing mineral admixtures coarser and heavier than cement. KW - Engineered recycled mineral admixtures KW - Rheology KW - PCE-Based superplasticizer KW - Steel slag KW - Mining tailing PY - 2020 DO - https://doi.org/10.1016/j.jobe.2020.101515 VL - 32 SP - 1 EP - 16 PB - Elsevier AN - OPUS4-58395 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Olonade, K. A. A1 - Mbugua, R. N. A1 - Lenz, F. J. A1 - Tchetgnia Ngassam, I. T1 - Bio-Based Rheology Modifiers for High Performance Concrete – Possible Modes of Actions and Case Study for Cassava Starch in West Africa N2 - Polymers that help tailoring rheological properties during the casting process have become inevitable constituents for all kinds of high-performance concrete technologies. Due to lacking industries, these typically crude-oil based admixtures are not readily available in many parts of the world, which limits the implementation of more sustainable high-performance construction technologies in these regions. Alternative polymers, which often demand for less processing, can be derived from local plant-based resources. The paper provides experimental data of flow tests of cement pastes with polysaccharides from Triumfetta pendrata A. Rich, acacia gum and cassava without and in the presence of polycarboxylate ether superplasticizer. The flow tests are amended by observations of the zeta potentials and the hydrodynamic diameters in the presence of and without calcium ions in the dispersion medium. The results show that in the presence of and without calcium ions all polysaccharides provide negative zeta potentials, yet, they affect flowability and thixotropy in different ways. Cassava starch, acacia gum, and the gum of Triumfetta pendrata A. Rich qualified well for robustness improvement, strong stiffening, and additive manufacturing, respectively. The reason for the different effects can be found in their average sizes and size distribution. Due to the promising results, a flow chart for local value chains is derived on the example of yet unused cassava wastes, which can be converted in parallel. T2 - 3rd International Conference on the Application of Superabsorbent Polymers CY - Skukuza, South Africa KW - Admixtures KW - Polysaccharides KW - Rheology KW - Thixotropy KW - Concrete PY - 2020 SN - 978-3-030-33341-6 SN - 978-3-030-33342-3 DO - https://doi.org/10.1007/978-3-030-33342-3_17 SP - 158 EP - 166 PB - Springer AN - OPUS4-58404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Robens-Radermacher, Annika A1 - Unger, Jörg F. A1 - Mezhov, Alexander A1 - Schmidt, Wolfram ED - Biondini, F. ED - Frangopo, D. M. T1 - Temperature dependent modelling approach for early age behavior of printable mortars N2 - Structural build-up describes the stability and early-age strength development of fresh mortar used in 3D printing. lt is influenced by several factors, i.e. the composition of the print­ able material, the printing regime, and the ambient conditions. The existing modelling approaches for structural build-up usually define the model parameters for a specific material composition with­ out considering the influence of the ambient conditions. The goal of this contribution is to explicitly include the temperature dependency in the modelling approach. Temperature changes have signifi­ cant impact on the structural build-up process: an increase of the temperature leads to a faster dissol­ ution of cement phases and accelerates hydration. The proposed extended model includes temperature dependency using the Arrhenius theory. The new model parameters are successfully calibrated based on Viskomat measurement data using Bayesian inference. Furthermore, a higher impact of the temperature in the re-flocculation as in the structuration stage is observed. T2 - The Eighth International Symposium on Life-Cycle Civil Engineering (IALCCE 2023) CY - Milano, Italien DA - 02.07.2023 KW - 3D concrete printing KW - Material characterization KW - Structural build-up KW - Thixotropy KW - Model calibration PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-582175 SN - 978-1-003-32302-0 DO - https://doi.org/10.1201/9781003323020-146 SN - 978-1-003-32302-0 VL - 1st Edition SP - 1193 EP - 1200 PB - CRC Press AN - OPUS4-58217 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hmood, F. A1 - Schmidt, Franziska A1 - Görke, O. A1 - Günster, Jens T1 - Investigation of chemically modified ICIE16 bioactive glass, part II N2 - Chemically modified bioactive glasses based on ICIE16 were prepared with the melt-quenching method using water as a quenching medium. The sinterability of these bioactive glasses was investigated and is discussed in this article. The sintering experiments were conducted with different sintering temperatures, sintering times and heating rates. Those parameters are crucial for dense glass with an amorphous structure. The particle size (d50) of the starting glass powder was determined at 88 μm and kept constant. The pre-pressed glass pellets were cold-isostatically pressed at 300 MPa to a green density of around 63 %. Density development, phase identification, shrinkage behavior and the microstructure were investigated to determine the sinterability of the developed glasses. The glass powders were sintered at different temperatures inside the processing window while crystallization was monitored. The results have shown that the sinterability of the developed glasses strongly dependsonthe proposed chemical additions. The highest density reached was 96 %, which belongs to BP1 glass with sintering conditions of 20 K/min heating rate for 60 min at 750 °C. KW - Bioactive glass KW - Viscous sintering KW - Crystallization KW - Processing window KW - Grain boundary PY - 2019 DO - https://doi.org/10.4416/JCST2019-00031 VL - 11 IS - 1 SP - 1 EP - 9 PB - Göller Verlag AN - OPUS4-49913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Henning, L. M. A1 - Diaz Cubas, D. A1 - Colmenares, M. G. A1 - Schmidt, J. A1 - Bekheet, M. F. A1 - Pauw, Brian Richard A1 - Gurlo, A. A1 - Simon, U. T1 - High specific surface area ordered mesoporous silica COK-12 with tailored pore size N2 - Ordered mesoporous silica materials such as COK-12, analogous to the well-known SBA-15, are characterized by high surface areas and unique features such as defined pore sizes in the meso-size range and high pore ordering. The aim of this work was to prove the washing step and choice of calcination and aging temperature during the COK-12 synthesis as effective tools in tailoring, markedly improving the specific surface area, pore size, and pore volume. By controlling the aging temperature, the pore size was linearly adjusted between 5.7 and 8.1 nm, while preserving the hexagonal ordering of the pores. The synthesized COK-12 powders possess pore volumes and specific surface areas up to 1.23 cm3 g−1 and 860m2 g−1, respectively, which is markedly higher than what has previously been reported about COK-12. The presented results and the environmentally friendly character of the synthesis will make COK-12 more interesting for future adaption to the industrial processes, for example in catalysis, adsorption, or drug delivery. KW - Ordered mesoporous silica KW - Pore size tailoring KW - High specific surface area KW - SAXS KW - Small angle scattering PY - 2019 DO - https://doi.org/10.1016/j.micromeso.2019.01.050 SN - 1387-1811 VL - 280 SP - 133 EP - 143 PB - Elsevier AN - OPUS4-47378 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Senoner, Mathias A1 - Maaßdorf, A. A1 - Rooch, Heidemarie A1 - Österle, Werner A1 - Malcher, M. A1 - Schmidt, M. A1 - Kollmer, F. A1 - Paul, D. A1 - Hodoroaba, Vasile-Dan A1 - Rades, Steffi A1 - Unger, Wolfgang T1 - Lateral resolution of nanoscaled images delivered by surface-analytical instruments: application of the BAM-L200 certified reference material and related ISO standards N2 - The certified reference material BAM-L200, a nanoscale stripe pattern for length calibration and specification of lateral resolution, is described. BAM-L200 is prepared from a cross-sectioned epitaxially grown layer stack of AlxGa1–xAs and InxGa1–xAs on a GaAs substrate. The surface of BAM-L200 provides a flat pattern with stripe widths ranging down to 1 nm. Calibration distances, grating periods and stripe widths have been certified by TEM with traceability to the length unit. The combination of gratings, isolated narrow stripes and sharp edges of wide stripes offers plenty of options for the determination of lateral resolution, sharpness and calibration of length scale at selected settings of imaging surface-analytical instruments. The feasibility of the reference material for an analysis of the lateral resolution is demonstrated in detail by evaluation of ToF-SIMS, AES and EDX images. Other applications developed in the community are summarized, too. BAM-L200 fully supports the implementation of the revised International Standard ISO 18516 (in preparation) which is based on knowledge outlined in the Technical Report ISO/TR 19319:2013. KW - AES KW - BAM-L200 KW - CRM KW - EDX KW - Imaging KW - Lateral resolution KW - Sharpness KW - Standardisation KW - STXM KW - ToF-SIMS KW - XPEEM KW - XPS KW - Certified reference material KW - Imaging surface analysis PY - 2015 DO - https://doi.org/10.1007/s00216-014-8135-7 SN - 1618-2642 SN - 1618-2650 VL - 407 IS - 11 SP - 3211 EP - 3217 PB - Springer CY - Berlin AN - OPUS4-33033 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tötzke, C. A1 - Gaiselmann, G. A1 - Osenberg, M. A1 - Bohner, J. A1 - Arlt, Tobias A1 - Markötter, Henning A1 - Hilger, A. A1 - Wieder, F. A1 - Kupsch, Andreas A1 - Müller, Bernd R. A1 - Hentschel, Manfred P. A1 - Banhart, J. A1 - Schmidt, V. A1 - Lehnert, W. A1 - Manke, I. T1 - Three-dimensional study of compressed gas diffusion layers using synchrotron X-ray imaging N2 - We present a synchrotron X-ray tomographic study on the morphology of carbon fiber-based gas diffusion layer (GDL) material under compression. A dedicated compression device is used to provide well-defined compression conditions. A flat compression punch is employed to study the fiber geometry at different degrees of compression. Transport relevant geometrical parameters such as porosity, pore size and tortuosity distributions are calculated. The geometric properties notably change upon compression which has direct impact on transport conditions for gas and fluid flow. The availability of broad 3D paths, which are most important for the transport of liquid water from the catalyst layer through the GDL, is markedly reduced after compression. In a second experiment, we study the influence of the channel-land-pattern of the flow-field on shape and microstructure of the GDL. A flow-field compression punch is employed to reproduce the inhomogeneous compression conditions found during fuel cell assembly. While homogenously compressed underneath the land the GDL is much less and inhomogeneously compressed under the channel. The GDL material extends far into the channel volume where it can considerably influence gas and fluid flow. Loose fiber endings penetrate deeply into the channel and form obstacles for the discharge of liquid water droplets. KW - Synchrotron X-ray tomography KW - Gas diffusion layer (GDL) KW - Microstructure KW - Water transport path KW - Pore size analysis KW - Geometrical tortuosity PY - 2014 DO - https://doi.org/10.1016/j.jpowsour.2013.12.062 SN - 0378-7753 VL - 253 SP - 123 EP - 131 PB - Elsevier CY - Amsterdam [u.a.] AN - OPUS4-29979 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Henning, L. M. A1 - Müller, J. T. A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard A1 - Schmidt, J. A1 - Bekheet, M. F. A1 - Gurlo, A. A1 - Simon, U. T1 - Hierarchically porous and mechanically stable monoliths from ordered mesoporous silica and their water filtration potential N2 - Mechanically stable structures with interconnected hierarchical porosity combine the benefits of both small and large pores, such as high surface area, pore volume, and good mass transport capabilities. Hence, lightweight micro-/meso-/macroporous monoliths are prepared from ordered mesoporous silica COK-12 by means of spark plasma sintering (SPS, S-sintering) and compared to conventionally (C-) sintered monoliths. A multi-scale model is developed to fit the small angle X-ray scattering data and obtain information on the hexagonal lattice parameters, pore sizes from the macro to the micro range, as well as the dimensions of the silica population. For both sintering techniques, the overall mesoporosity, hexagonal pore ordering, and amorphous character are preserved. The monoliths' porosity (77–49%), mesopore size (6.2–5.2 nm), pore volume (0.50–0.22 g cm-3 ), and specific surface area (451–180 m2 g-1) decrease with increasing processing temperature and pressure. While the difference in porosity is enhanced, the structural parameters between the C-and S-sintered monoliths are largely converging at 900 C, except for the mesopore size and lattice parameter, whose dimensions are more extensively preserved in the S-sintered monoliths, however, coming along with larger deviations from the theoretical lattice. Their higher mechanical properties (biaxial strength up to 49 MPa, 724 MPa HV 9.807 N) at comparable porosities and ability to withstand ultrasonic treatment and dead-end filtration up to 7 bar allow S-sintered monoliths to reach a high permeance (2634 L m-2 h-1 bar-1), permeability (1.25 x 10^-14 m2), and ability to reduce the chemical oxygen demand by 90% during filtration of a surfactant-stabilized oil in water emulsion, while indicating reasonable resistance towards fouling. KW - SAXS KW - Hierarchically porous KW - Silica KW - Water filtration PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-555928 DO - https://doi.org/10.1039/D2NA00368F SN - 2516-0230 SP - 1 EP - 17 PB - Royal Society of Chemistry CY - Cambridge AN - OPUS4-55592 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wiedensohler, A. A1 - Wiesner, A. A1 - Weinhold, K. A1 - Birmili, W. A1 - Herrmann, M. A1 - Merkel, M. A1 - Müller, T. A1 - Pfeifer, S. A1 - Schmidt, A. A1 - Tuch, T. A1 - Velarde, F. A1 - Quincey, P. A1 - Seeger, Stefan A1 - Nowak, A. T1 - Mobility particle size spectrometers: Calibration procedures and measurement uncertainties N2 - Mobility particle size spectrometers (MPSS) belong to the essential instruments in aerosol science that determine the particle number size distribution (PNSD)in the submicrometer size range. Following calibration procedures and target uncertainties against standards and reference instruments are suggested for a complete MPSS quality assurance program: a) calibration of the CPC counting efficiency curve (within 5% for the plateau counting efficiency; within 1 nm for the 50% detection efficiency diameter), b) sizing calibration of the MPSS, using a certified polystyrene latex (PSL) particle size standard at 203 nm (within 3%), c) intercomparison of the PNSD of the MPSS (within 10% and 20% of the dN/dlogDP concentration for the particle size range 20 – 200 nm and 200 to 800 nm, respectively), and d) intercomparison of the integral PNC of the MPSS (within 10%). Furthermore, following measurement uncertainties have been investigated: a) PSL particle size standards in the range from 100-500nm match within 1% after sizing calibration at 203 nm. b) Bipolar diffusion chargers based on the radioactive nuclides Kr85, Am241 and Ni63 and a new ionizer based on corona discharge follow the recommended bipolar charge distribution, while soft X-ray-based charges may alter faster than expected. c) The use of a positive high voltage supply show a 10% better performance than a negative one. d) The intercomparison of the integral PNC of an MPSS against the total number concentration is still within the target uncertainty at an ambient pressure of approximately 500 hPa. KW - Measurement uncertainties KW - Mobility particle size spectrometer (MPPS) KW - Condensation particle counter (CPC) KW - Calibration PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-425060 DO - https://doi.org/10.1080/02786826.2017.1387229 SN - 1521-7388 VL - 52 IS - 2 SP - 146 EP - 164 PB - Tailor & Francis CY - USA AN - OPUS4-42506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Chowdhary, S. A1 - Schmidt, R. F. A1 - Sahoo, A. K. A1 - tom Dieck, T. A1 - Hohmann, T. A1 - Schade, B. A1 - Brademann-Jock, Kerstin A1 - Thünemann, Andreas A1 - Netz, R. R. A1 - Gradzielski, M. A1 - Koksch, B. T1 - Rational design of amphiphilic fluorinated peptides: Evaluation of self-assembly properties and hydrogel formation N2 - Advanced peptide-based nanomaterials composed of self-assembling peptides (SAPs) are of emerging interest in pharmaceutical and biomedical applications. The introduction of fluorine into peptides, in fact, offers unique opportunities to tune their biophysical properties and intermolecular interactions. In particular, the degree of fluorination plays a crucial role in peptide engineering as it can be used to control the characteristics of fluorine-specific interactions and, thus, peptide conformation and self-assembly. Here, we designed and explored a series of amphipathic peptides by incorporating the fluorinated amino acids (2S)-4-monofluoroethylglycine (MfeGly), (2S)-4,4-difluoroethylglycine (DfeGly) and (2S)-4,4,4-trifluoroethylglycine (TfeGly) as hydrophobic components. This approach enabled studying the impact of fluorination on secondary structure formation and peptide self-assembly on a systematic basis. We show that the interplay between polarity and hydrophobicity, both induced differentially by varying degrees of side chain fluorination, does affect peptide folding significantly. A greater degree of fluorination promotes peptide fibrillation and subsequent formation of physical hydrogels in physiological conditions. Molecular simulations revealed the key role played by electrostatically driven intra-chain and inter-chain contact pairs that are modulated by side chain fluorination and give insights into the different self-organization behaviour of selected peptides. Our study provides a systematic report about the distinct features of fluorinated oligomeric peptides with potential applications as peptide-based biomaterials. KW - Small-angle X-ray scattering KW - SAXS KW - Amyloid PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-553504 DO - https://doi.org/10.1039/D2NR01648F SN - 2040-3364 VL - 14 IS - 28 SP - 10176 EP - 10189 PB - Royal Society of Chemistry AN - OPUS4-55350 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -