TY - JOUR A1 - Harder, Ulrike A1 - Geißler, Heinz A1 - Gaber, Martin A1 - Hähnert, Manfred A1 - Dersch, O. A1 - Rauch, F. T1 - Determination of the water content of alkali lime silica glasses by IR spectroscopy using nuclear reaction analysis for calibration PY - 1998 SN - 0927-4472 VL - 71 IS - 1 SP - 12 EP - 18 PB - Elsevier CY - Amsterdam AN - OPUS4-2309 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kautek, Wolfgang A1 - Hertwig, Andreas A1 - Martin, Sven A1 - Krüger, Jörg A1 - Lenzner, Matthias A1 - Spielmann, C. A1 - Lenner, M. A1 - Bunte, J. A1 - Puester, T. A1 - Burmester, T. A1 - Fiedler, A. A1 - Heberer, E. A1 - Brose, M. A1 - Stingl, A. A1 - Kiehl, P. A1 - Hönigsmann, H. A1 - Trautinger, F. A1 - Grabner, G. T1 - Safety in Femtosecond Laser Technology - Recent Results of a European Research Project (406) T2 - International Laser Safety Conference 2003 ; ILSC 2003 CY - Jacksonville, FL, USA DA - 2003-03-10 PY - 2003 SN - 0-912035-38-2 SP - 1(?) EP - 10(?) PB - Laser Institute of America CY - Orlando, Fla. AN - OPUS4-2259 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Martin A1 - Malow, Marcus A1 - Krause, Ulrich A1 - Neumann, F. T1 - Untersuchung des Verhaltens von Steinkohlen unter dem Gesichtspunkt des Ex-Schutzes N2 - Die Kenntnis des Brenn- und Explosionsverhaltens von Stäuben ermöglicht die Festlegung geeig-neter Explosionsschutzmaßnahmen. Am Beispiel von Steinkohle- Mahlanlagen werden Untersu-chungen zur Bestimmung sicherheitstechnischer Kenngrößen (STK) von Stäuben vorgestellt. Hier-bei erfolgt zunächst die auf den Anwendungsfall abgestimmte Auswahl geeigneter Untersuchungs-verfahren und deren Anpassung an vorliegende Randbedingungen. Aufbauend auf die gewonnenen Erkenntnisse werden Schlussfolgerungen für den sicheren Betrieb von Steinkohle- Mahlanlagen getroffen. T2 - VGB-Konferenz "Kraftwerke im Wettbewerb 2007, Neue Kraftwerke - mit Erfahrung und Innovation die Zukunft gestalten" CY - Hamburg, Deutschland DA - 2007-04-25 KW - Explosionsschutz KW - Steinkohle KW - Mahlanlagen KW - Selbstentzündung PY - 2007 IS - CD-ROM SP - 15 Seiten PB - VGB PowerTech e.V. CY - Hamburg AN - OPUS4-14785 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmidt, Martin A1 - Malow, Marcus A1 - Krause, Ulrich A1 - Neumann, F. T1 - Untersuchung des Entzündungs- und Brandverhaltens von Steinkohlen unter dem Gesichtspunkt des Ex-Schutzes KW - Explosionsschutz KW - Steinkohle KW - Mahlanlagen KW - Selbstentzündung PY - 2007 SN - 1435-3199 VL - 87 IS - 7 SP - 67 EP - 72 PB - VGB PowerTech e.V. CY - Essen AN - OPUS4-15711 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Szymoniak, Paulina A1 - Kolmangadi, Mohamed A. A1 - Böhning, Martin A1 - De Souza, N. R. A1 - Juranyi, F. A1 - Zorn, R. A1 - Schönhals, Andreas T1 - Inelastic and Quasielastic Neutron Scattering on Polynorbornenes with Bulky Carbocyclic Side groups N2 - This study investigates the molecular mobility and vibrational properties of polynorbornenes with bulky carbocyclic side groups using inelastic and quasielastic neutron scattering techniques. The polymers, synthesized via metathesis and addition polymerization, exhibit varying degrees of microporosity, which ignificantly influences their gas separation performance. By inelastic neutron scattering experiments, it could be shown that all considered polymers have excess contributions to the low frequency vibrational density of states known as the Boson peak. The maximum frequency of the Boson peak correlates to the microporosity of the polymers. This correlation supports the sound wave interpretation of the Boson peak, suggesting that the microporous structure enhances the compressibility of the material at a microscopic length scale. The molecular mobility, particularly the methyl group rotation, was characterized using elastic scans and quasielastic neutron scattering. The study revealed a temperature dependent relaxation process, with the onset of molecular fluctuations observed around 200 K for the polymer containing methyl groups. For the polymer having no methyl groups only elastic scattering is observed. The methyl group rotation was analyzed in terms of a jump diffusion in a threefold potential with three equivalent energy minima. This leads to an almost correct description of the q dependence of the elastic incoherent scattering function when the number of hydrogen nuclei undergoing the methyl group rotation is considered. It was further evidenced that the fraction of methyl undergoing the methyl group rotation increases with increasing temperature. KW - Polymers of Intrinsic Microporosity KW - Neutron scattering PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630297 DO - https://doi.org/10.1016/j.polymer.2025.128358 SN - 1873-2291 VL - 328 SP - 241 PB - Elsevier Ltd. AN - OPUS4-63029 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mensinger, M. A1 - Fischer, O. A1 - Oberhaidinger, F. A1 - Stimmelmayer, L. A1 - Ebell, Gino A1 - Babutzka, Martin T1 - Grouted joint for integral composite frame bridges suitable for hot dip galvanizing N2 - Due to the corrosion resistance of carbon steel, bridge constructions are currently protected against corrosion by applied coating systems. These coating systems need to be renewed after approximately 25 50 years. Galvanized constructions without any welding areas at the construction site could be prepared as grouted joints and can be used without any renewing for about 100 years. T2 - Intergalva 2022 CY - Rome, Italy DA - 20.06.2022 KW - Corrosion KW - Galvanized steel KW - Bridge PY - 2022 AN - OPUS4-55096 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Krause, Martin A1 - Borchardt, Kerstin A1 - Lange, Marco A1 - Behrens, Matthias A1 - Maack, Stefan A1 - Mielentz, Frank A1 - Milmann, Boris A1 - Schaurich, Dieter A1 - Wöstmann, Jens A1 - Hintzpeter, F. A1 - Sodeikat, C. T1 - Kosteneinsparung durch Anwendung zerstörungsfreier Prüfverfahren für Betonbauteile beim Bauen im Bestand N2 - In Zeiten knapper Kassen wird überall nach Wegen gesucht Kosten einzusparen. Im Bauwesen geht es dabei um Kosteneinsparungen ohne Reduktion der Sicherheit und Dauerhaftigkeit des Bauwerks. Beim Bauen im Bestand können mit einer zerstörungsfreien Prüfung von Bauwerken die Weiternutzung oder die erforderlichen Umbauten optimiert werden und so Kosten eingespart werden. KW - Zerstörungsfreie Prüfung KW - Bauen im Bestand KW - Radar KW - Ultraschallecho KW - Kosteneinsparung PY - 2011 SN - 978-3-8167-8611-5 VL - 101 SP - 1 EP - 95 PB - Fraunhofer IRB Verl. CY - Stuttgart ET - Abschlussbericht AN - OPUS4-26649 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - van Wingerden, K. A1 - Kluge, Martin A1 - Habib, Abdel Karim A1 - Skarsvag, H. L. A1 - Ustolin, F. A1 - Paltrinieri, N. A1 - Odsaeter, L. H. ED - Pierucci, S. ED - Klemes, J. J. T1 - Experimental Investigation into the Consequences of Release of Liquified Hydrogen onto and under Water N2 - Large-scale experiments have been performed to investigate the possible consequences of realistic amounts of liquified hydrogen (LH2) encountering water. The experiments aimed at simulating an accidental release of LH2 onto water, for instance during the fuelling of a ship. For liquified natural gas (LNG), it has been demonstrated that physical explosions may occur when it is spilled onto water. These phenomena are referred as rapid phase transitions (RPTs). It cannot be excluded that RPTs are also possible in the case of LH2. The tests were performed at the Test Site Technical Safety of the Bundesanstalt für Materialforschung und –prüfung (BAM) in Horstwalde, Germany. The tests were performed in a 10 m x 10 x 1.5 m basin filled with water. LH2 releases of up to about 1 kg/s were established releasing directly from a trailer carrying LH2. The releases occurred from a height of 50 cm above the water surface pointing downwards, 30 cm under the water surface pointing downwards and 30 cm under the water surface pointed along the water surface. All release configurations resulted in a very chaotic LH2-water mixing zone, causing considerable evaporation and resulting in minor over pressures. No RPTs were observed. The main phenomenon to be observed is, however, an ignition of the released gas cloud resulting in significant blast wave overpressures and heat radiation to the surroundings. The ignition occurred in all under-water releases and in about 90 % of the releases above the water surface. T2 - 17th EFCE International Symposium on Loss Prevention and Safety Promotion in Process Industries CY - Prague, Czech Rebpublic DA - 05.06.2022 KW - Liquid Hydrogen KW - LH2 KW - Release KW - RPT KW - Rapid Phase Transition PY - 2022 DO - https://doi.org/10.3303/CET2290091 SN - 2283-9216 VL - 90 SP - 541 EP - 546 PB - AIDIC CY - Milano AN - OPUS4-55324 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - van Wingerden, K. A1 - Kluge, Martin A1 - Habib, Abdel Karim A1 - Ustolin, F. A1 - Paltrinieri, N. ED - Pierucci, S. ED - Klemes, J. J. T1 - Medium-scale tests to investigate the possibility and effects of BLEVEs of storage vessels containing liquified hydrogen N2 - Experiments have been performed to determine the consequences of a storage vessel containing liquified hydrogen (LH2) is engulfed by a fire. The tests were performed at the Test Site Technical Safety of the Bundesanstalt für Materialforschung und –prüfung (BAM) in Germany within a research cooperation between BAM and Gexcon as part of the SH2IFT program. Three tests were performed using double-walled vacuum insulated vessels of 1 m3 volume varying the orientation of the vessel and the effect of the insulation material used (perlite or multi-layer insulation (MLI)). The degree of filling of the vessel was approximately 35 % in each of the tests performed. The fire load was provided by a propane fed burner positioned under the storage vessel and designed to give a homogeneous fire load. In one of the tests a rupture of the storage vessel occurred causing a blast, a fireball and fragments. Apart from measuring these consequences, the conditions in the vessel (e.g. temperatures and pressure) during the heating process were monitored in all three tests. The work described was undertaken as part of the project Safe Hydrogen fuel handling and Use for Efficient Implementation (SH2IFT). T2 - 17th EFCE International Symposium on Loss Prevention and Safety Promotion in Process Industries CY - Prague, Czech Republic DA - 05.06.2022 KW - Liquid hydrogen KW - LH2 KW - BLEVE KW - Cryogenic tank PY - 2022 DO - https://doi.org/10.3303/CET2290092 SN - 2283-9216 VL - 90 SP - 547 EP - 552 PB - AIDIC CY - Milano AN - OPUS4-55323 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lozano-Martín, D. A1 - Pazoki, F. A1 - Kipphardt, Heinrich A1 - Khanipour, P. A1 - Tuma, Dirk A1 - Horillo, A. A1 - Chamorro, C. R. T1 - Thermodynamic (p, ρ, T) characterization of a reference high-calorific natural gas mixture when hydrogen is added up to 20 % (mol/mol) N2 - The injection of hydrogen into the natural-gas grid is an alternative during the process of a gradual decarbonization of the heat and power supply. When dealing with hydrogen-enriched natural gas mixtures, the performance of the reference equations of state habitually used for natural gas should be validated by using high-precision experimental thermophysical data from multicomponent reference mixtures prepared with the lowest possible uncertainty in composition. In this work, we present experimental density data for an 11-compound high-calorific (hydrogen-free) natural gas mixture and for two derived hydrogen-enriched natural gas mixtures prepared by adding (10 and 20) mol-% of hydrogen to the original standard natural gas mixture. The three mixtures were prepared gravimetrically according to ISO 6142–1 for maximum precision in their composition and thus qualify for reference materials. A single-sinker densimeter was used to determine the density of the mixtures from (250–350) K and up to 20 MPa. The experimental density results of this work have been compared to the densities calculated by three different reference equations of state for natural gas related mixtures: the AGA8-DC92 EoS, the GERG-2008 EoS, and an improved version of the GERG-2008 EoS. While relative deviations of the experimental density data for the hydrogen-free natural gas mixture are always within the claimed uncertainty of the three considered equations of state, larger deviations can be observed for the hydrogen-enriched natural gas mixtures from any of the three equations of state, especially for the lowest temperature and the highest pressures. KW - Hydrogen-enriched natural gas KW - Single-sinker densimeter KW - High-pressure density KW - Equations of state PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-604742 DO - https://doi.org/10.1016/j.ijhydene.2024.05.028 SN - 0360-3199 VL - 70 SP - 118 EP - 135 PB - Elsevier BV CY - Amsterdam AN - OPUS4-60474 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Köhler, B. A1 - Schubert, F. A1 - Algernon, Daniel A1 - Gardei, André A1 - Mielentz, Frank A1 - Krause, Martin ED - Thompson, D. O. T1 - Experimental study of elastic waves in concrete for NDE in civil engineering N2 - Laser vibrometric contactless sound field measurements at a concrete test block are presented. Both excitation by an ultrasonic probe and by an impactor were used. The wave modes can be identified by their geometric wave forms and propagation velocities. Additionally, numerical simulation of the experimental situation is used to support this interpretation. Possible applications of the presented technique are discussed. ©2005 American Institute of Physics T2 - 31th Annual Review of Progress in Quantitative Nondestructive Evaluation CY - Golden, CO, USA DA - 2004-07-25 KW - Ultraschall KW - Impact-Echo KW - Wellenausbreitung KW - Visualisierung KW - Modellierung PY - 2005 SN - 0-7354-0245-0 DO - https://doi.org/10.1063/1.1916840 SN - 0743-0760 SN - 0094-243X N1 - Serientitel: AIP conference proceedings – Series title: AIP conference proceedings IS - 760 SP - 1439 EP - 1445 PB - American Institute of Physics CY - Melville, NY AN - OPUS4-5480 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -