TY - CONF A1 - Meinel, Dietmar A1 - Ehrig, Karsten A1 - L'Hostis, V. A1 - Muzeau, B. A1 - Paetsch, O. T1 - Examination of damage processes in concrete with CT N2 - In order to extend the lifetime of buildings and constructions at the macro scale it is necessary to understand the damage processes of building materials at the micro scale. In particular, durability of reinforced concrete structures is one of the most important equirements for construction planning and restoration of buildings. Therefore degradation mechanisms were reproduced on laboratory specimens. CT (Computed Tomography) is commonly used for non-destructive microstructural defect analysis for recurring tests on concrete specimens. In this work a few examples of CT applications on cementitious materials (including cement paste, mortar and concrete specimens) will be presented. Firstly, in order to quantify the degradation processes, specimens analysed were damaged by corrosion due to carbonation and due to chloride ingress. Particular focus has been set to the analysis of cracks. An automated crack detection tool, developed by Zuse Institut Berlin (ZIB) and BAM in ZIBAmira, has been applied for quantitative analysis of crack parameters and 3D visualization of cracks. Furthermore the distribution of corrosion products has been evaluated inside the cement matrix and visualized in 3D data sets. Another important factor for the ageing stability of concrete is the interfacial transition zone (ITZ). The ITZ consists of a layer of cement paste (20 to 40 μm) over every aggregate where porosity is generally increased in comparison with the bulk. This zone could be a preferential zone for transfer of aggressive species. To visualize the ITZ, a small sample of mortar with a diameter of 10mm has been prepared and scanned using the industrial μCT setup at BAM with a spatial resolution of 5μm voxel size. In addition the extracted surface of aggregates could be used for load simulations. We finally show how CT examination of drilled samples taken from building materials in conjunction with laboratory experiments is helpful for further evaluations of damage processes in concrete. T2 - Conference on industrial computed tomography (ICT) 2014 CY - Wels, Austria DA - 25.02.2014 KW - X-ray computed tomography KW - Concrete KW - Corrosion KW - Crack detection KW - 3D visualization PY - 2014 SN - 978-3-8440-2557-6 SN - 1610-4773 SP - 111 EP - 122 PB - Shaker Verlag GmbH AN - OPUS4-30332 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meinel, Dietmar T1 - Computertomographie T2 - Arbeitskolloquium zum Projekt Römische Großbronzen am UNESCO Welterbe Limes CY - Bonn, Germany DA - 2014-04-11 PY - 2014 AN - OPUS4-30335 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meinel, Dietmar T1 - Examination of Damage Processes in Concrete with CT T2 - Conference on Industrial Computed Tomography (ICT) CY - Wels, Austria DA - 2014-02-25 PY - 2014 AN - OPUS4-30310 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meinel, Dietmar A1 - Staude, Andreas A1 - Ehrig, Karsten ED - Bernard, D. ED - Buffière, J.-Y. ED - Pollock, T. ED - Poulsen, H.F. ED - Rollett, A. ED - Uchic, M. T1 - Analyzing microstructure and damage in construction materials with 3D micro CT N2 - This poster presentation gives an overview of the great potential of X-ray micro computed tomography (CT) to cast light on the evolution of the microstructure in construction materials. Prevention of damage is of major economic and social importance in the development of suitable construction materials such as concrete and asphalt. Therefore a non-destructive testing method such as CT is an appropriate tool for visualization of the inner structure. Its combination with other test methods allows understanding the damage processes such as crack propagation or corrosion. We show examples of internal structure analyses on a wide range of materials: Automatic 3D crack detection and the visualization of corrosion products inside of steel reinforced concrete, pore and shape analysis of lightweight aggregates and the visualization of deformation of high-pressure loaded aerated concrete specimens, distribution of aggregates inside concrete, and determination of the surface of porous asphalt core samples. Segmented structures serve, e.g., as input data for simulation of transport phenomena or virtual load tests. T2 - 2nd International congress on 3D materials science 2014 CY - Annecy, France DA - 29.06.2014 KW - X-ray computed tomography KW - Concrete KW - Asphalt KW - Corrosion KW - Crack detection KW - 3D visualization PY - 2014 SP - 23 EP - 28 PB - Wiley AN - OPUS4-31069 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meinel, Dietmar T1 - Analyse von Schädigungsprozessen in Beton - Was leistet die CT? Teil 2: Analyse der CT-Daten N2 - Der rekonstruierte CT-Datensatz liefert Informationen über die Dichteverteilung im Untersuchungsobjekt in Form einer Grauwertedarstellung. Zur quantitativen Bestimmung der anhand der Grauwertunterschiede separierbaren Strukturen bedarf es einer genauen Determinierung der diese Strukturen abgrenzenden Übergänge. Am Beispiel der Oberflächenbestimmung an einer Stahlbetonprobe wird der Unterschied zwischen globalem und lokalem Schwellwert gezeigt. Die so erzeugten Oberflächen dienen dem dimensionellen Messen innerhalb des CT-Datensatzes, dem Fitten von Regelgeometrien oder der Durchführung automatischer Analysen (Poren, Wandstäken, Faserorientierung). Zur Reduzierung der Datenmenge und zur Verwendung in Simulationsprogrammen können die gefundenen Oberflächen auch in ein Netzmodell überführt werden. Gezeigt wird der Einsatz dieser Techniken an Untersuchungen von Betonproben in der BAM. T2 - Summer School im Rahmen des DFG Schwerpunktprogramms 2020 "Zyklische Schädigungsprozesse in Hochleistungsbetonen im Experimental-Virtual-Lab" CY - Hotel Park Soltau, 29614 Soltau, Germany DA - 25.06.2018 KW - Computertomographie KW - In-situ CT KW - Bildverarbeitung KW - Beton KW - Korrosion PY - 2018 AN - OPUS4-45431 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Brinker, U. A1 - Meinel, Dietmar A1 - Teßmann, B. A1 - Lübke, H. ED - Lewerentz, Annette T1 - Die menschlichen Skelettreste der zur anthropologischen Rudolf-Virchow-Sammlung gehörenden Kollektion des Fundplatzes Rinnukalnsim Norden Lettlands – Resultat eines Forschungsstreites des 19. Jahrhunderts im damaligen Livland N2 - In der anthropologischen Rudolf-Virchow-Sammlung der Berliner Gesellschaft für Anthropologie, Ethnologie und Urgeschichte (BGAEU) befindet sich eine größere Anzahl menschlicher Schädel aus dem Gebiet des heutigen Lettlands, die Mehrzahl dabei von der im Norden Lettlands am Burtnieksee gelegenen Fundstelle Riņņukalns. Der nachfolgende Aufsatz beschreibt die Gründe, warum diese Stücke in den 1870er Jahren in die Sammlung gelangt sind, und präsentiert eine anthropologische Dokumentation und Analyse der Schädelfunde vom Riņņukalns aus der Sammlung. KW - Mikro-CT KW - Anthropologie KW - Schädelfunde PY - 2018 SN - 978-3-86757-994-0 SN - 0178-7896 VL - 39 SP - 35 EP - 54 PB - Berliner Gesellschaft für Anthropologie, Ethnologie und Urgeschichte CY - Berlin AN - OPUS4-48071 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meinel, Dietmar T1 - Die Computertomographien an den Funden der Qubbet el-Hawa T2 - Das Wachsausschmelzverfahren als Kulturtechnik im Alten Ägypten CY - Rheinische Friedrich-Wilhelms-Universität, Bonn DA - 2015-03-06 PY - 2015 AN - OPUS4-32824 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meinel, Dietmar T1 - Analyzing Microstructure and Damage in Construction materials with 3D Micro CT T2 - International Congress on 3D Materials Science CY - Annecy, France DA - 2014-06-29 PY - 2014 AN - OPUS4-31004 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Meinel, Dietmar A1 - Willer, F. ED - Fitzenreiter, M. ED - Willer, F. ED - Auenmüller, J. T1 - Röntgen-Mikro-Computertomographie (µCT) - Virtuelle Freilegung innenliegender Strukturen N2 - Im Frühjahr 1969 wurde bei Ausgrabungen der Universität Bonn unter Leitung von Elmar Edel auf der Qubbet el-Hawa ein außergewöhnliches Depot mit Materialien einer antiken Gusswerkstatt gefunden. Im Zuge der Fundteilung gelangten die meisten Stücke des Konvolutes in das Ägyptische Museum der Universität Bonn und werden dort aufbewahrt. Die Deponierung des für die Forschung zur antiken Metallurgie bisher einzigartigen Konvoluts geschah im Zuge der Nachnutzung von Grabanlagen aus dem Alten Reich (um 2100 v. u. Z.) in der ägyptischen Spätzeit (um 550 – 400 v. u. Z.). Das Depot enthält Objekte, die alle Fertigungsstufen von Metallgegenständen im Wachsausschmelzverfahren dokumentieren. Es wurden Stücke von Rohwachs sowie Wachsmodelle und die zu deren Herstellung genutzten Negativformen gefunden. Weiterhin enthielt es vollständige Gussformen, die in einem aufwendigen Mehrschalenverfahren hergestellt wurden und teilweise bereits für den Guss ausgebrannt worden sind. Schließlich zählen einige Metallfiguren sowie weitere figürliche Objekte zum Konvolut, die alle in den Bereich einer kunsthandwerklichen Werkstatt deuten. Eine Besonderheit stellen zudem Gussformen dar, in denen Fragmente von Metallfiguren zur Reparatur im Überfangguss vorbereitet waren. Das Depot wurde in der Gesamtpublikation der Bonner Grabungen bisher nur summarisch vorgestellt. 2014/15 initiierten die Abteilung Ägyptologie der Universität Bonn und das LVR-LandesMuseum Bonn unter Ludwig D. Morenz und Michael Schmauder ein gemeinsames und von der Fritz-Thyssen-Stiftung gefördertes Forschungsprojekt, das von Martin Fitzenreiter, Johannes Auenmüller und Frank Willer geleitet wurde. In Kooperation mit Dietmar Meinel (Bundesanstalt für Materialforschung und -prüfung Berlin / BAM, Fachbereich 8.5 Mikro-ZfP), Roland Schwab (Curt-Engelhorn-Zentrum Archäometrie gGmbH, Mannheim), Gerwulf Schneider (FU Berlin, Exzellenzcluster TOPOI), Ursula Baumer und Patrick Dietemann (beide Doerner-Institut / München), Thorsten Geisler-Wierwille (Steinmann Institut für Geologie, Mineralogie und Paläontologie der Universität Bonn) sowie Ursula Tegtmeier (Labor für Archäobotanik der Universität Köln) wurden die Objekte des Konvolutes eingehend und mit zeitgemäßen Verfahren untersucht. Die Ergebnisse dieses Forschungsprojekts werden in dieser Publikation vorgelegt. KW - Mikro-CT KW - Bronzeguss KW - Digitale Bildverarbeitung PY - 2016 SN - 978-3-86893-225-6 SP - 82 EP - 117 PB - EB-Verlag CY - Berlin AN - OPUS4-39208 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meinel, Dietmar T1 - Computertomographie in der BAM N2 - Überblicksvortrag über die Aktivitäten des FB 8.5 im Bereich der industriellen Computertomographie T2 - 6. Geo-CT / Imaging Workshop CY - Institut für Geowissenschaften, Jena, Germany DA - 10.11.2016 KW - Mikro-CT KW - Synchrotron CT KW - In-situ 3D-CT PY - 2016 AN - OPUS4-39209 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -