TY - CHAP A1 - Leinitz, Sarah A1 - Lu, Z. A1 - Becker, S. A1 - Stephan, D. A1 - von Klitzing, R. A1 - Schmidt, Wolfram ED - Mechtcherine, V. ED - Khayat, K. ED - Secrieru, E. T1 - Influence of different accelerators on the rheology and early hydration of cement paste N2 - Special applications like pumping, spraying or printing of concrete require the precise adjustment of very specific rheological properties at different time steps during the casting process. Superplasticizers such as polycarboxylate ethers (PCE) can be used to obtain the required flowability, which, possibly in combination with additional rheology modifying admixtures, generate the required specified consistency. However, after the application, the concrete should change the rheological properties immediately in order to avoid deformations at rest. Therefore, the use of accelerators can be effective. Accelerators influence the hydration of cementitious materials, and thus the rheological properties over the course of time and the setting. In this paper, the influence of different accelerators on the rheology and early hydration of cement paste as well as the interaction of accelerator and PCE are presented. Methods like rheometry, needle penetration tests and practical Tests like spread flow were applied. The used accelerators showed accelerating behavior on the cement pastes without and in the presence of PCE. At the same time an influence on the rheology could be observed. This effect was less in the mixes with PCE, especially at the highest water/cement ratio (w/c). KW - Rheology KW - Cement paste KW - Accelerator KW - Superplasticizer KW - Setting PY - 2019 SN - 978-3-030-22565-0 U6 - https://doi.org/10.1007/978-3-030-22566-7 SN - 2211-0844 VL - 23 SP - 106 EP - 115 PB - Springer ET - 1 AN - OPUS4-49139 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ji, Y. A1 - Becker, S. A1 - Lu, Z. A1 - Mezhov, Alexander A1 - von Klitzing, R. A1 - Schmidt, Wolfram A1 - Stephan, D. T1 - Effect of resting time on rheological properties of glass bead suspensions: Depletion and bridging force among particles N2 - The effect of resting time on the rheological properties of cement suspensions is generally explained by early formed structure and overconsumption of polycarboxylate superplasticizers (PCEs). In this paper, we propose that the influence of resting time on the rheological properties is closely related to size variation of non-absorbed PCE. To identify this, glass bead suspensions were prepared with various amounts of PCE and ionic solution, and their rheological properties were evaluated at various times. We found that the yield stress increases with time at higher PCE concentrations and higher ionic strength solutions. Adsorbed PCE during resting tends to bridge the particles rather than disperse them. In addition, it was found that hydrodynamic radius of PCE increased with resting time, and depletion forces resulting from non-absorbed PCE size changes correlate well with the increased yield stress. KW - Depletion force KW - Ionic stregth KW - PCE KW - Rheology KW - Resting time PY - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-587193 SN - 0002-7820 SP - 1 EP - 16 PB - Wiley online library CY - Weinheim AN - OPUS4-58719 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Haist, M. A1 - Link, J. A1 - Nicia, D. A1 - Leinitz, Sarah A1 - Baumert, C. A1 - von Bronk, T. A1 - Cotardo, D. A1 - Eslami Pirharati, M. A1 - Fataei, S. A1 - Garrecht, H. A1 - Gehlen, C. A1 - Hauschildt, I. A1 - Ivanova, I. A1 - Jesinghausen, S. A1 - Klein, C. A1 - Krauss, H.-W. A1 - Lohaus, L. A1 - Lowke, D. A1 - Mazanec, O. A1 - Pawelczyk, S. A1 - Pott, U. A1 - Radebe, N. W. A1 - Riedmiller, J. J. A1 - Schmid, H.-J. A1 - Schmidt, Wolfram A1 - Secrieru, E. A1 - Stephan, D. A1 - Thiedeitz, M. A1 - Wilhelm, M. A1 - Mechtcherine, V. T1 - Interlaboratory study on rheological properties of cement pastes and reference substances: comparability of measurements performed with different rheometers and measurement geometries N2 - This paper presents the results of an interlaboratory study of the rheological properties of cement paste and ultrasound gel as reference substance. The goal was to quantify the comparability and reproducibility of measurements of the Bingham parameters yield stress and plastic viscosity when measured on one specific paste composition and one particular ultrasound gel in different laboratories using different rheometers and measurement geometries. The procedures for both in preparing the cement paste and carrying out the rheological measurements on cement paste and ultrasound gel were carefully defined for all of the study’s participants. Different conversion schemes for comparing the results obtained with the different measurement setups are presented here and critically discussed. The procedure proposed in this paper ensured a reasonable comparability of the results with a coefficient of variation for the yield stress of 27% and for the plastic viscosity of 24%, despite the individual measurement series’ having been performed in different labs with different rheometers and measurement geometries. KW - Rheometry KW - Rheology KW - Interlaboratory test KW - Test setup KW - Testing procedure KW - Cement paste KW - Ultrasound gel PY - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-511220 SN - 1871-6873 VL - 53 IS - 4 SP - 92 PB - Rilem AN - OPUS4-51122 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -