TY - JOUR A1 - Mack, D. E. A1 - Laquai, René A1 - Müller, Bernd R. A1 - Helle, O. A1 - Sebold, D. A1 - Vaßen, R. A1 - Bruno, Giovanni T1 - Evolution of porosity, crack density, and CMAS penetration in thermal barrier coatings subjected to burner rig testing N2 - Degradation of thermal barrier coatings (TBCs) in gas‐turbine engines due to calcium–magnesium–aluminosilicate (CMAS) glassy deposits from various sources has been a persistent issue since many years. In this study, state of the art electron microscopy was correlated with X‐ray refraction techniques to elucidate the intrusion of CMAS into the porous structure of atmospheric plasma sprayed (APS) TBCs and the formation and growth of cracks under thermal cycling in a burner rig. Results indicate that the sparse nature of the infiltration as well as kinetics in the burner rig are majorly influenced by the wetting behavior of the CMAS. Despite the obvious attack of CMAS on grain boundaries, the interaction of yttria‐stabilized zirconia (YSZ) with intruded CMAS has no immediate impact on structure and density of internal surfaces. At a later stage the formation of horizontal cracks is observed in a wider zone of the TBC layer. KW - Characterization KW - CMAS KW - Synchrotron X‐ray refraction radiography KW - Thermal barrier coatings PY - 2019 DO - https://doi.org/10.1111/jace.16465 SN - 0002-7820 SN - 1551-2916 VL - 102 IS - 10 SP - 6163 EP - 6175 PB - Wiley CY - Oxford AN - OPUS4-47804 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Miccoli, Lorenzo A1 - Silva, R. A. A1 - Oliveira, D. V. A1 - Müller, U. T1 - Static behavior of cob: Experimental testing and finite-element modeling N2 - The aim of this paper is to implement a numerical model to reproduce the nonlinear behavior of cob walls under shear loading. Axial compression, pull-off, and diagonal compression tests were carried out to derive the mechanical parameters. In addition, the stressstrain relationships, the nonlinear behavior, and the failure modes were defined. The experimental results were then used to calibrate a finiteelement model. The material behavior was simulated through a macromodeling approach adopting the total strain rotating crack model. A sensitivity analysis was conducted to assess the effects of varying the parameters with higher uncertainty on the structural behavior. The numerical model achieved good correspondence with the experimental results in terms of simulation of the shear stress–shear strain relationship and of damage pattern. KW - Cob KW - Compression behavior KW - Shear behavior KW - Digital image correlation KW - Finite-element method PY - 2019 DO - https://doi.org/10.1061/(ASCE)MT.1943-5533.0002638 SN - 0899-1561 SN - 1943-5533 VL - 31 IS - 4 SP - 04019021-1 EP - 04019021-13 PB - ASCE American Society of Civil Engineers AN - OPUS4-47316 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Blaeß, Carsten A1 - Müller, Ralf A1 - Poologasundarampilai, G. A1 - Brauer, D. S. T1 - Sintering and concomitant crystallization of bioactive glasses N2 - The sintering of bioactive glasses allows for the preparation of complex structures, such as three‐dimensional porous scaffolds. Such 3D constructs are particularly interesting for clinical applications of bioactive glasses in bone regeneration, as the scaffolds can act as a guide for in‐growing bone cells, allowing for good Integration with existing and newly formed tissue while the scaffold slowly degrades. Owing to the pronounced tendency of many bioactive glasses to crystallize upon heat treatment, 3D scaffolds have not been much exploited commercially. Here, we investigate the influence of crystallization on the sintering behavior of several bioactive glasses. In a series of mixed‐alkali glasses an increased CaO/alkali metal oxide Ratio improved sintering compared to Bioglass 45S5, where dense sintering was inhibited. Addition of small amounts of calcium fluoride helped to keep melting and sintering temperatures low. Unlike glass 13‐93, these new glasses crystallized during sintering but this did not prevent densification. Variation in bioactive glass particle size allowed for fine‐tuning the microporosity resulting from the sintering process. KW - Bioactive glass KW - Crystallization KW - Scaffolds KW - Sintering PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-485458 DO - https://doi.org/10.1111/ijag.13477 SN - 2041-1286 VL - 10 IS - 4 SP - 449 EP - 462 PB - Wiley AN - OPUS4-48545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schob, D. A1 - Roszak, R. A1 - Sagradov, I. A1 - Sparr, H. A1 - Ziegenhorn, M. A1 - Kupsch, Andreas A1 - Léonard, Fabien A1 - Müller, Bernd R. A1 - Bruno, Giovanni T1 - Experimental determination and numerical simulation of material and damage behaviour of 3D printed polyamide 12 under quasi-static loading N2 - In order to characterise the material and damage behaviour of additively manufactured polyamide 12 (PA12) under quasi-static load and to implement it in a numerical model, experiments under quasi-static load as well as microstructural investigations were carried out. Selective laser sintering (SLS) was used as the manufacturing process. For the classification of the material behaviour, quasi-static cyclic tests with holding times as well as tensile tests were performed. X-ray refraction and computed tomography (CT) were used to investigate the damage behaviour. The Chaboche model, which has already been applied for metallic materials under thermomechanical loading, served as the basis for the selection of the numerical material model. The same procedure was used for the selection of the damage model, where the Gurson–Tvergaard–Needleman (GTN) model was chosen, which was already used for porous metallic materials. The Chaboche model shows very good agreement with experimental results. Furthermore, the coupling with the GTN model allows a very good modelling of the damage behaviour. Finally, it could be shown that the selected models are suitable to simulate the material and damage behaviour of 3D printed PA12. KW - Polyamide 12 KW - 3D printing KW - Viscoplastic KW - Chaboche model KW - Damage KW - GTN model KW - X-ray refraction KW - Computed tomography PY - 2019 DO - https://doi.org/10.24423/aom.3162 SN - 0373-2029 VL - 71 IS - 4-5 SP - 507 EP - 526 PB - IPPT PAN - Polish Academy of Sciences, Institute of Fundamental Technological Research CY - Warsaw AN - OPUS4-49409 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -