TY - GEN A1 - Coniglio, Nicolas A1 - Cross, Carl Edward ED - Jürgen Hirsch, ED - Skrotzki, Birgit ED - Günter Gottstein, T1 - Effect of Cooling Rate and Silicon Content on Solidification Path and Phase Constituents in 6060 Aluminium Castings and Weld Metal T2 - 11th International Conference on Aluminium Alloys (ICAA 11) CY - Aachen, Germany DA - 2008-09-22 KW - Weld Metal Microstructure KW - Cast Microstructure KW - Al-Mg-Si Alloy System KW - 6060 Aluminium Alloy KW - 4043 Filler Alloy KW - Silicon Content KW - Cooling Rate KW - Phase Constituents KW - Solidification Path PY - 2008 SN - 978-3-527-32367-8 VL - 2 SP - 1889 EP - 1893 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-18309 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Coniglio, Nicolas A1 - Cross, Carl Edward A1 - Michael, Thomas A1 - Lammers, Marco T1 - Defining a critical weld dilution to avoid solidification cracking in aluminum N2 - Al-Mg-Si alloys are known to be highly susceptible to solidification cracking except when using an appropriate filler metal (e.g., 4343 or 5356), although the amount of dilution required to avoid cracking has never been a well-defined quantity. The aim of the present study is to determine a relationship between filler metal dilution, local strain rate conditions, and cracking susceptibility. Making use of the controlled tensile weldability (CTW) test and local strain extensometer measurements, a boundary has been established between crack and non-crack conditions for different local strain rates and dilution amounts, holding all other welding parameters constant. This boundary, presented in the form of critical strain rate-dilution map, defines the critical amount of 4043 filler metal required to avoid solidification cracking when arc welding 6060 aluminium, depending upon local strain rate. T2 - Light Alloy Seminar CY - Clausthal, Germany DA - 2006-11-20 KW - Dilution KW - Solidification Cracking KW - Al-Mg-Si Alloys KW - 6060 Aluminium KW - Arc Welding KW - Strain Rate KW - 4043 Filler Dilution PY - 2008 SN - 0043-2296 SN - 0096-7629 VL - 87 IS - 8 SP - 237 EP - 247 PB - American Welding Society CY - New York, NY AN - OPUS4-18311 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Coniglio, Nicolas A1 - Cross, Carl Edward ED - Carl E. Cross, ED - John C. Lippold, ED - Böllinghaus, T. ED - Herold, H. T1 - Weld parameter and minor element effects on solidification crack initiation in Aluminium N2 - Earlier work has established that a critical amount of 4043 filler is required to avoid solidification cracking when arc-welding 6060 aluminium, depending upon local strain conditions. For example, when the mushy zone behind the weld pool experiences a tensile strain from combined thermal and shrinkage stresses, the possibility exists for crack initiation. For a greater rate of strain, it has been determined that a greater 4043 dilution (i.e. higher weld metal silicon content) is required to avoid crack initiation. Making use of the Controlled Tensile Weldability (CTW) test and local strain extensometer measurements, a boundary has been established between crack and no-crack conditions for different local strain rates and filler dilutions, holding all other welding parameters constant. Using this established boundary as a line of reference, additional parameters have now been examined and their influence on cracking has been characterized. These parameter influences have included studies of weld travel speed, weld pool contaminants (Fe, O, and H), and grain refiner additions (TiAl3 + Boron). Each parameter has been independently varied and its effect on cracking susceptibility quantified in terms of a critical strain rate required to initiate cracking for a given 4043 filler dilution. T2 - Hot cracking phenomena in welds II CY - Berlin, Germany DA - 2006-03-05 KW - Aluminium Alloys KW - Solidification Cracking KW - Weld Defect KW - Hot Cracking KW - Crack Initiation KW - Critical Strain Rate KW - Parameter Effects KW - Minor Elements PY - 2008 SN - 978-3-540-78627-6 SP - 277 EP - 310 PB - Springer CY - Berlin AN - OPUS4-18323 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Cross, Carl Edward A1 - Coniglio, Nicolas ED - Carl E. Cross, ED - John C. Lippold, ED - Böllinghaus, T. ED - Herold, H. T1 - Weld solidification cracking: critical conditions for crack initiation and growth N2 - A perspective will be given that outlines important considerations in evaluating and predicting weldability. An examination will be made of the local conditions necessary for solidifications crack initiation and growth in a weld. This will be done in light of two prominent thermo-mechanical approaches involving critical strain and critical strain rate. Critical conditions will be identified based upon values available in the literature. Methods used to measure strain and strain rate will be compared. The interpretation of crack lenght measurements commonly used to quantify weldability will be questioned, based upon our current understanding of the problem. Complications and problem areas needing better definition will be identified and discussed, including strain distribution in the mushy zone, segregation at grain boundaries, effect of impurities, and effect of cooling rate on solidification path. Finally, a suggestion will be made for a new approach to weld development using in-situ strain rate measurements and new composition-strain rate maps that define the boundary between crack an no-crack conditions. T2 - Hot cracking phenomena in welds II CY - Berlin, Germany DA - 2007-03-05 KW - Solidification Cracking KW - Hot Cracking KW - Crack Initiation KW - Crack Growth KW - Critical Strain KW - Critical Strain Rate KW - Weldability Testing KW - Crack Prediction PY - 2008 SN - 978-3-540-78627-6 SP - 39 EP - 58 PB - Springer CY - Berlin AN - OPUS4-18319 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Coniglio, Nicolas A1 - Cross, Carl Edward T1 - Characterization of solidification path for Aluminium 6060 weld metal with variable 4043 filler dilution N2 - Aluminium alloy 6060 is typical of a family of Al-Mg-Si extrusion alloys, which are considered weldable only when using an appropriate filler alloy such as 4043 (Al-5Si) or 5356 (Al-5Mg). This study concerns the thermal analysis and solidification path determination of aluminium alloy 6060 diluted with variable amounts of 4043. Casting of controlled mixtures of alloys 6060 and 4043 was used to simulate different weld dilutions in order to facilitate thermal analysis. Thermal analysis and metallography were applied in order to reveal solidification reactions and phases, and allow calculation of solid fraction versus temperature curves. Although the liquidus temperature was little affected, different phases formed with increased 4043 dilution, with a trend toward lower temperature reactions and a larger fraction interdendritic constituent. KW - Aluminium alloys KW - Light metals KW - Solidification cracking KW - Cracking KW - Defects KW - Hot cracking KW - Analysis techniques KW - Cooling KW - Cooling rate KW - Temperature KW - Practical investigations KW - Microstructure KW - Dilution KW - Reference lists PY - 2006 UR - http://www.iiw-iis.org/ SN - 0043-2288 SN - 1878-6669 VL - 50 IS - 11/12 SP - 14 EP - 23 PB - Springer CY - Oxford AN - OPUS4-14219 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Cross, Carl Edward A1 - Coniglio, Nicolas A1 - Schempp, Philipp A1 - Mousavi, M.G. ED - Lippold, J. ED - Böllinghaus, T. ED - Cross, C.E. ED - et al., T1 - Critical conditions for weld solidification crack growth N2 - The occurrence of solidification cracking during welding remains a little understood phenomenon, in spite of extensive studies and tests performed to evaluate and compare the relative weldability of many different alloys. From an approach often adopted in the welding community attributed to Prokhorov, solidification cracks are believed to form when a critical tensile strain is exceeded, specific to the alloy, assuming that the mushy-zone has limited ductility. Tensile stresses and strains normally form behind a moving weld pool as a result of solidification shrinkage and thermal contraction, as influenced by welding parameters and the degree of restraint. KW - Solidification cracking KW - Aluminium alloy KW - Crack growth KW - Strain rate model PY - 2011 SN - 978-3-642-16863-5 U6 - https://doi.org/10.1007/978-3-642-16864-2_2 IS - Part 2 SP - 25 EP - 41 PB - Springer CY - Berlin, Heidelberg AN - OPUS4-23846 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -