TY - CONF A1 - Charmi, Amir A1 - Heimann, Jan A1 - Duffner, Eric A1 - Hashemi, Seyedreza A1 - Prager, Jens T1 - Application of deep learning for structural health monitoring of a composite overwrapped pressure vessel undergoing cyclic loading N2 - Structural health monitoring (SHM) using ultrasonic-guided waves (UGWs) enables continuous monitoring of components with complex geometries and provides extensive information about their structural integrity and their overall condition. Composite overwrapped pressure vessels (COPVs) used for storing hydrogen gases at very high pressures are an example of a critical infrastructure that could benefit significantly from SHM. This can be used to increase the periodic inspection intervals, ensure safe operating conditions by early detection of anomalies, and ultimately estimate the remaining lifetime of COPVs. Therefore, in the digital quality infrastructure initiative (QI-Digital) in Germany, an SHM system is being developed for COPVs used in a hydrogen refueling station. In this study, the results of a lifetime fatigue test on a Type IV COPV subjected to many thousands of load cycles under different temperatures and pressures are presented to demonstrate the strengths and challenges associated with such an SHM system. During the cyclic testing up to the final material failure of the COPV, a sensor network of fifteen surface-mounted piezoelectric (PZT) wafers was used to collect the UGW data. However, the pressure variations, the aging process of the COPV, the environmental parameters, and possible damages simultaneously have an impact on the recorded signals. This issue and the lack of labeled data make signal processing and analysis even more demanding. Thus, in this study, semi-supervised, and unsupervised deep learning approaches are utilized to separate the influence of different variables on the UGW data with the final aim of detecting and localizing the damage before critical failure. T2 - 11th European Workshop on Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Structural health monitoring KW - Deep learning KW - Ultrasonic-guided waves KW - Anomaly detection KW - Damage localization PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-607396 DO - https://doi.org/10.58286/29751 SP - 1 EP - 8 AN - OPUS4-60739 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenberg, Rainer A1 - Charmi, Amir T1 - Virtual-lab-based determination of a macroscopic yield function for additively manufactured parts N2 - This work presents a method for the yield function determination of additively manufactured parts of S316L steel. A crystal plasticity model is calibrated with test results and used afterwards to perform so-called virtual experiments, that account for the specific process-related microstructure including crystallographic and morphological textures. These simulations are undertaken on a representative volume element (RVE), that is generated from EBSD/CT-Scans on in-house additively manufactured specimen, considering grain structure and crystal orientations. The results of the virtual experiments are used to determine an anisotropic Barlat yield function, that can be used in a macroscopical continuum-sense afterwards. This scale-bridging approach enables the calculation of large-scale parts, that would be numerically too expensive to be simulated by a crystal plasticity model. T2 - 3. Tagung des DVM-Arbeitskreises Additiv gefertigte Bauteile und Strukturen CY - Berlin, Germany DA - 07.11.2018 KW - Virtual experiments KW - Additive manufacturing KW - Anisotropy KW - Crystal plasticity KW - Scale-bridging PY - 2018 AN - OPUS4-46895 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenberg, Rainer A1 - Charmi, Amir T1 - Virtual-lab-based determination of a macroscopic yield function for additively manufactured parts N2 - Diese Arbeit beschreibt eine Methode für die Ermittlung einer Fließfunktion für additiv gefertigte Bauteile des Werkstoffs S316L. Ein Kristallplastizitätsmodell wird zunächst mit experimentellen Daten kalibriert. Anschließend werden mit diesem Modell sogenannte virtuelle Experimente durchgeführt, die die prozeßspezifische Mikrostruktur in Form von kristallographischen und morphologischen Texturen miteinbeziehen. Diese Simulationen werden mit einem representativen Volumenelement (RVE) durchgeführt, das aus EBSD/CT-Scans an additiv gefertigten Proben generiert wurde und daher die Kornstruktur und Kristallorientierungen enthält. Die virtuellen Experimente werden durchgeführt, um anhand der damit erhaltenen Fließpunkte eine anisotrope Barlat-Fließfunktion zu bestimmen. Dieser skalenübergreifende Ansatz ermöglicht die Simulation großer Strukturen, für die die Anwendung eines Kristallplastizitätsmodells numerisch zu teuer wäre. N2 - This work presents a method for the yield function determination of additively manufactured parts of S316L steel. A crystal plasticity model is calibrated with test results and used afterwards to perform so-called virtual experiments, that account for the specific process-related microstructure including crystallographic and morphological textures. These simulations are undertaken on a representative volume element (RVE), that is generated from EBSD/CT-Scans on in-house additively manufactured specimen, considering grain structure and crystal orientations. The results of the virtual experiments are used to determine an anisotropic Barlat yield function, that can be used in a macroscopical continuum-sense afterwards. This scale-bridging approach enables the calculation of large-scale parts, that would be numerically too expensive to be simulated by a crystal plasticity model. T2 - 3. Tagung des DVM-Arbeitskreises Additiv gefertigte Bauteile und Strukturen CY - Berlin, Germany DA - 07.11.2018 KW - Additive manufacturing KW - Scale-bridging KW - Crystal plasticity KW - Virtual experiments KW - Anisotropy PY - 2018 SN - 2509-8772 SP - 153 EP - 158 PB - DVM CY - Berlin AN - OPUS4-46570 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heimann, Jan A1 - Charmi, Amir A1 - Karapanagiotis, Christos A1 - Hashemi, Seyedreza A1 - Prager, Jens T1 - How structural health monitoring can be embedded in a digital quality infrastructure: an example. N2 - The digital Quality Infrastructure (QI) initiative “QI-Digital” in Germany is focusing on implementing new technologies and approaches to ensure that the task of quality assurance is more efficient and ready for the digital and green transformation of the economy. The implementation of quality control key elements, such as Smart Standards, Digital Certificates and QI-cloud solutions shall contribute to solving the socio-economic, ecological, and technological challenges of our time. Hydrogen is a key energy carrier and has the potential to play a significant role in the energy transition, especially in mobility. An essential factor for the broad acceptance of hydrogen-based mobility is the availability of refueling stations that operate reliably and safely. Using the example of a Hydrogen Refueling Station (HRS) built within the QI-Digital initiative, the Federal Institute for Material Research and Testing (BAM) aims to establish a real laboratory where modern measurement techniques and new digital methods are implemented to enhance operational safety, availability, and economic efficiency and render the technology more attractive for the industry. In this work, we present an approach to establish a Structural Health Monitoring (SHM) system on a high-pressure buffer inside HRS and show how it could be embedded into a digital QI. The high-pressure buffers are essential components of the plant which are currently inspected periodically without regard to their operating history. Focusing on the transition to a continuous and digitally supported monitoring of the component’s integrity during operation the novel inspection scheme will be linked to a completely digitalized component-related documentation and tested using digital certificates. This allows the operational safety and, if necessary, the remaining useful lifetime to be assessed on an ongoing basis and to be a valuable contribution to increasing sustainability. T2 - 11th European Workshop on Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Structural health monitoring KW - Quality infrastructure KW - Digital transformation KW - Reliability KW - Quality control KW - Industry 4.0 PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-607109 DO - https://doi.org/10.58286/29769 SN - 1435-4934 SP - 1 EP - 7 PB - NDT.net AN - OPUS4-60710 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heimann, Jan A1 - Yilmaz, Bengisu A1 - Charmi, Amir A1 - Duffner, Eric A1 - Schukar, Marcus A1 - Prager, Jens T1 - Structural Health Monitoring (SHM) for continuous monitoring of hydrogen pressure vessels N2 - While hydrogen is one of the most promising energy carriers, the safety of hydrogen storage technology remains one of the most important factors for technological and societal approval. While the engineering safety factors of the pressure vessels are kept high, the periodic inspection and the limited lifetime are making the application very costly considering manpower, time, money, and material waste. The development of an integrated structural health monitoring system can allow an easy transition from the current situation to cost-effective predictive maintenance. Hence, we propose to integrate three different SHM systems into hydrogen pressure vessels, namely guided wave ultrasonics, acoustic emission, and fibre optic sensing, to continuously monitor the condition and integrity. In this work, we evaluated the condition of a Type IV composite overwrapped pressure vessel using ultrasonic guided wave propagation. We mounted fifteen piezo-electric wafers on the composite cylinder by shaping three rings containing five sensors each. We acquired data from the sensor network following different boundary conditions with artificial damages on the selected locations. The data were evaluated with guided wave tomography techniques using ultrasonic features (amplitude, frequency, etc.) as well as artificial intelligence (AI). The results suggest that both traditional guided wave fusion techniques and AI-based characterization methods can detect artificial damages. In future work, it is planned to integrate acoustic emission and fibre optic sensing. Moreover, the measurement and the test results will be implemented into a digital twin to derive trends and make predictions on the damage propagation as well as the remaining useful lifetime. This work has received funding from German Ministry of Economic Affairs and Climate Actions within the QI-Digital initiative (www.qi-digital.de). T2 - SCHALL 23 CY - Wetzlar, Germany DA - 21.03.2023 KW - Structural Health Monitoring KW - Ultrasonic Guided Waves KW - Composite Overwrapped Pressure Vessel KW - Hydrogen PY - 2023 AN - OPUS4-58026 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Karapanagiotis, Christos A1 - Heimann, Jan A1 - Duffner, Eric A1 - Charmi, Amir A1 - Schukar, Marcus A1 - Hashemi, Seyedreza A1 - Prager, Jens T1 - Towards predictive maintenance of hydrogen pressure vessels based on multi-sensor data N2 - In this paper, we report on a sensor network for structural health monitoring (SHM) of Type IV composite overwrapped pressure vessels (COPVs) designed for hydrogen storage. The sensor network consists of three different SHM sensing technologies: ultrasonic guided waves (GW), acoustic emission (AE) testing, and distributed fiber optic sensors (DFOS). We present an experimental setup for a lifetime test, where a COPV is subjected to cyclic loading. Data from all sensors are collected and centrally evaluated. The COPV failed after approximately 60,000 load cycles, and the sensor network proved capable of detecting and localizing the damage even before the failure of the COPV. This multi-sensor approach offers significantly more channels of information and could therefore enable a transition from costly and time-consuming periodic inspections to more efficient and modern predictive maintenance strategies, including artificial intelligence (AI)-based evaluation. This not only has a positive effect on operational c KW - Ffiber optic sensors KW - Acoustic emission KW - Guided waves KW - Hydrogen KW - Digital twin KW - Structural health monitoring PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-618948 DO - https://doi.org/10.58286/30513 SP - 1 EP - 8 PB - NDT.net AN - OPUS4-61894 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Karapanagiotis, Christos A1 - Heimann, Jan A1 - Duffner, Eric A1 - Charmi, Amir A1 - Schukar, Marcus A1 - Hashemi, Seyedreza A1 - Prager, Jens T1 - Towards predictive maintenance of hydrogen pressure vessels based on multi-sensor data fusion and digital twin modeling N2 - Hydrogen pressure vessels are among the most essential components for reliable hydrogen technology. Under current regulations, a mostly conservative strategy is employed, restricting the usage time of hydrogen pressure vessels without providing information on the real remaining lifetime. During the service life, pressure vessels are inspected periodically. However, no established method that can provide continuous monitoring or information on the remaining safe service life of the vessel. In this paper, we propose a sensor network for Structural Health Monitoring (SHM) of hydrogen pressure vessels where data from all sensors are collected and centrally evaluated. Specifically, we integrate three different SHM sensing technologies namely Guided Wave ultrasonics (GW), Acoustic Emission testing (AT), and distributed Fiber Optic Sensing (FOS). This integrated approach offers significantly more information and could therefore enable a transition from costly and time-consuming periodic inspections to more efficient and modern predictive maintenance strategies, including Artificial Intelligence (AI)-based evaluation. This does not only have a positive effect on the operational costs but enhances safety through early identification of critical conditions in the overall system in real-time. We demonstrate an experimental set-up of a lifetime test where a Type IV Composite Overwrapped Pressure Vessel (COPV) is investigated under cyclic loading instrumented with AT, FOS, and GW methods. We acquired data from the sensor network until the pressure vessel failed due to material degradation. The data collected using the three different SHM sensor technologies is planned to be evaluated individually, using data fusion, and AI. In the future, we aim to integrate the measurement setup into a hydrogen refueling station with the data stream implemented into a digital signal processing chain and a digital twin. T2 - 11th European Workshop on Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Acoustic emission KW - Ultrasonic guided waves KW - Fiber optic sensors KW - Hydrogen KW - Pressure vessels KW - Structural health monitoring KW - Machine learning PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-602764 UR - https://www.ndt.net/search/docs.php3?id=29702 SP - 1 EP - 8 PB - NDT.net AN - OPUS4-60276 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Charmi, Amir A1 - Falkenberg, Rainer A1 - Ávila Calderón, Luis A1 - Mohr, Gunther A1 - Sommer, Konstantin A1 - Ulbricht, Alexander A1 - Sprengel, Maximilian A1 - Saliwan Neumann, Romeo A1 - Evans, Alexander A1 - Skrotzki, Birgit T1 - Mechanical anisotropy of additively manufactured stainless steel 316L: An experimental and numerical study N2 - The underlying cause of mechanical anisotropy in additively manufactured (AM) parts is not yet fully understood and has been attributed to several different factors like microstructural defects, residual stresses, melt pool boundaries, crystallographic and morphological textures. To better understand the main contributing factor to the mechanical anisotropy of AM stainless steel 316L, bulk specimens were fabricated via laser powder bed fusion (LPBF). Tensile specimens were machined from these AM bulk materials for three different inclinations: 0◦, 45◦, and 90◦ relative to the build plate. Dynamic Young’s modulus measurements and tensile tests were used to determine the mechanical anisotropy. Some tensile specimens were also subjected to residual stress measurement via neutron diffraction, porosity determination with X-ray micro-computed tomography (μCT), and texture analysis with electron backscatter diffraction (EBSD). These investigations revealed that the specimens exhibited near full density and the detected defects were spherical. Furthermore, the residual stresses in the loading direction were between −74 ± 24 MPa and 137 ± 20 MPa, and the EBSD measurements showed a preferential ⟨110⟩ orientation parallel to the build direction. A crystal plasticity model was used to analyze the elastic anisotropy and the anisotropic yield behavior of the AM specimens, and it was able to capture and predict the experimental behavior accurately. Overall, it was shown that the mechanical anisotropy of the tested specimens was mainly influenced by the crystallographic texture. KW - Mechanical anisotropy KW - Residual stress KW - Crystal plasticity KW - Selective laser melting (SLM) KW - Laser beam melting (LBM) PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-511719 DO - https://doi.org/10.1016/j.msea.2020.140154 SN - 0921-5093 VL - 799 SP - 140154 PB - Elsevier B.V. AN - OPUS4-51171 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Charmi, Amir T1 - Virtual-lab-based determination of a macroscopic yield function for additively manufactured parts N2 - This work aims for a yield function description of additively manufactured parts of S316L steel at the continuum-mechanical macro-scale by means of so-called virtual experiments using a crystal plasticity (CP) model at meso-scale. Additively manufactured parts require the consideration of the specific process-related microstructure, which prevents this material to be macroscopically treated as isotropic, because of crystallographic as well as topological textures. From virtual experiments, yield loci under various loading conditions are simulated. The scale bridging from meso- to macro-scale is realised by the identification of the simulated yield loci as a modified anisotropic Barlat-type yield model representation. T2 - Workshop on Additive Manufacturing, BAM CY - Berlin, Germany DA - 13.05.2019 KW - Virtual experiments KW - Additive manufacturing KW - Anisotropy KW - Crystal plasticity KW - Scale-bridging PY - 2019 AN - OPUS4-48064 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Charmi, Amir T1 - A multiscale numerical framework for the simulation of anistropic material response of additively manufactured stainless steel 316L undergoing large plastic deformation N2 - Additive manufacturing (AM) offers significantly greater freedom of design compared to conventional manufacturing processes since the final parts are built layer by layer. This enables metal AM, also known as metal 3D printing, to be utilized for improving efficiency and functionality, for the production of parts with very complex geometries, and rapid prototyping. However, despite many technological advancements made in recent years, several challenges hinder the mass adoption of metal AM. One of these challenges is mechanical anisotropy which describes the dependency of material properties on the material orientation. Therefore, in this work, stainless steel 316L parts produced by laser-based powder bed fusion are used to isolate and understand the root cause of anisotropy in AM parts. Furthermore, an efficient and accurate multiscale numerical framework is presented for predicting the deformation behavior of actual AM parts on the macroscale undergoing large plastic deformations. Finally, a novel constitutive model for the plastic spin is formulated to capture the influence of the microstructure evolution on the material behavior on the macroscale. KW - Additive Fertigung KW - Austenitischer Stahl KW - Finite-Elemente-Methode KW - Mehrskalenmodell KW - Simulation PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:gbv:wim2-20240207-173356-002 DO - https://doi.org/10.25643/dbt.59550 SP - 1 EP - 163 PB - Bauhaus-Universität Weimar CY - Weimar AN - OPUS4-59511 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Charmi, Amir T1 - Virtual-lab-based determination of a macroscopic yield function for additively manufactured parts N2 - This work aims for an yield function description of additively manufactured (AM) parts of S316L steel at the continuum-mechanical macro-scale by means of so-called virtual experiments using a crystal plasticity (CP) model at meso-scale. Additively manufactured parts require the consideration of the specific process-related microstructure, which prevents this material to be macroscopically treated as isotropic, because of crystallographic as well as topological textures. EBSD/CT-Scans from in-house additively manufactured specimen extract the unique microstructural topology which is converted to a representative volume element (RVE) with grain structure and crystal orientations. Crystal plasticity model parameters on this RVE are calibrated and validated by means of mechanical testing under different texture angles. From virtual experiments on this RVE, yield loci under various loading conditions are simulated. The scale bridging from meso- to macro-scale is realised by the identification of the simulated yield loci as a modified anisotropic Barlat-type yield model representation. T2 - The First European Conference on Structural Integrity of Additively Manufactured Materials (ESIAM19) CY - Trondheim, Norway DA - 09.09.2019 KW - Virtual experiments KW - Additive manufacturing KW - Anisotropy KW - Crystal plasticity KW - Scale-bridging PY - 2019 AN - OPUS4-49376 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -