TY - JOUR A1 - Abou-Ras, D. A1 - Caballero, R. A1 - Fischer, C.-H. A1 - Kaufmann, C.A. A1 - Lauermann, I. A1 - Mainz, R. A1 - Mönig, H. A1 - Schöpke, A. A1 - Stephan, C. A1 - Streeck, C. A1 - Schorr, S. A1 - Eicke, A. A1 - Döbeli, M. A1 - Gade, B. A1 - Hinrichs, J. A1 - Nunney, T. A1 - Dijkstra, H. A1 - Hoffmann, V. A1 - Klemm, D. A1 - Efimova, V. A1 - Bergmaier, A. A1 - Dollinger, G. A1 - Wirth, Thomas A1 - Unger, Wolfgang A1 - Rockett, A.A. A1 - Perez-Rodriguez, A. A1 - Alvarez-Garcia, J. A1 - Izquierdo-Roca, V. A1 - Schmid, T. A1 - Choi, P.-P. A1 - Müller, M. A1 - Bertram, F. A1 - Christen, J. A1 - Khatri, H. A1 - Collins, R.W. A1 - Marsillac, S. A1 - Kötschau, I. T1 - Comprehensive comparison of various techniques for the analysis of elemental distributions in thin films JF - Microscopy and Microanalysis N2 - The present work shows results on elemental distribution analyses in Cu(In,Ga)Se2 thin films for solar cells performed by use of wavelength-dispersive and energy-dispersive X-ray spectrometry (EDX) in a scanning electron microscope, EDX in a transmission electron microscope, X-ray photoelectron, angle-dependent soft X-ray emission, secondary ion-mass (SIMS), time-of-flight SIMS, sputtered neutral mass, glow-discharge optical emission and glow-discharge mass, Auger electron, and Rutherford backscattering spectrometry, by use of scanning Auger electron microscopy, Raman depth profiling, and Raman mapping, as well as by use of elastic recoil detection analysis, grazing-incidence X-ray and electron backscatter diffraction, and grazing-incidence X-ray fluorescence analysis. The Cu(In,Ga)Se2 thin films used for the present comparison were produced during the same identical deposition run and exhibit thicknesses of about 2 µm. The analysis techniques were compared with respect to their spatial and depth resolutions, measuring speeds, availabilities, and detection limits. KW - Elemental distributions KW - Comparison KW - Depth profiling KW - Chemical mapping KW - Thin films KW - Solar cells KW - Chalcopyrite-type KW - Cu(In,Ga)Se2 PY - 2011 DO - https://doi.org/10.1017/S1431927611000523 SN - 1431-9276 SN - 1435-8115 VL - 17 IS - 5 SP - 728 EP - 751 PB - Cambridge University Press CY - New York, NY AN - OPUS4-24506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kim, K. J. A1 - Kim, A. S. A1 - Jang, J. S. A1 - Suh, J. K. A1 - Wirth, Thomas A1 - Hodoroaba, Vasile-Dan A1 - Unger, Wolfgang A1 - Araujo, J. R. A1 - Archanjo, B. S. A1 - Galhardo, C. E. A1 - Damasceno, J. A1 - Achete, C. A. A1 - Wang, H. A1 - Wang, M. A1 - Bennett, J. A1 - Simons, D. A1 - Kurokawa, A. A1 - Terauchi, S. A1 - Fujimoto, T. A1 - Streeck, C. A1 - Beckhoff, B. A1 - Spencer, S. A1 - Shard, A. T1 - Measurement of mole fractions of Cu, In, Ga and Se in Cu(In,Ga)Se2 films JF - Metrologia N2 - CCQM key comparison K-129 for the quantitative analysis of Cu(In,Ga)Se2 (CIGS) films has been performed by the Surface Analysis Working Group (SAWG) of the Consultative Committee for Amount of Substance (CCQM). The objective of this key comparison is to compare the equivalency of the National Metrology Institutes (NMIs) and Designated Institutes (DIs) for the measurement of mole fractions of Cu, In, Ga and Se in a thin CIGS film. The measurand of this key comparison is the average mole fractions of Cu, In, Ga and Se of a test CIGS alloy film in the unit of mole fraction (mol/mol). Mole fraction with the metrological unit of mol/mol can be practically converted to atomic fraction with the unit of at%. In this key comparison, a CIGS film with certified mole fractions was supplied as a reference specimen to determine the relative sensitivity factors (RSFs) of Cu, In, Ga and Se. The mole fractions of the reference specimen were certified by isotope dilution - inductively coupled plasma/mass spectrometry (ID-ICP/MS) and are traceable to the SI. A total number counting (TNC) method was recommended as a method to determine the signal intensities of the constituent elements acquired in the depth profiles by Secondary Ion Mass Spectrometry (SIMS), X-ray Photoelectron Spectroscopy (XPS) and Auger Electron Spectroscopy (AES). Seven NMIs and one DI participated in this key comparison. The mole fractions of the CIGS films were measured by depth profiling based-SIMS, AES and XPS. The mole fractions were also measured by non-destructive X-Ray Fluorescence (XRF) Analysis and Electron Probe Micro Analysis (EPMA) with Energy Dispersive X-ray Spectrometry (EDX). In this key comparison, the average degrees of equivalence uncertainties for Cu, In, Ga and Se are 0.0093 mol/mol, 0.0123 mol/mol, 0.0047 mol/mol and 0.0228 mol/mol, respectively. These values are much smaller than that of Fe in a Fe-Ni alloy film in CCQM K-67 (0.0330 mol/mol). This means that the quantification of multi-element alloy films is possible by depth profiling analysis using the TNC method. KW - CIGS KW - Key comparison KW - CCQM KW - SIMS KW - XPS KW - AES KW - XRF KW - EPMA PY - 2016 UR - http://iopscience.iop.org/article/10.1088/0026-1394/53/1A/08011 DO - https://doi.org/10.1088/0026-1394/53/1A/08011 SN - 0026-1394 SN - 1681-7575 VL - 53, Technical Supplement SP - Article 08011, 1 EP - 19 PB - IOP Publishing AN - OPUS4-38110 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kim, K.J. A1 - Jang, J. S. A1 - Kim, A. S. A1 - Suh, J.K. A1 - Chung, Y.-D. A1 - Hodoroaba, Vasile-Dan A1 - Wirth, Thomas A1 - Unger, Wolfgang A1 - Kang, H. J. A1 - Popov, O. A1 - Popov, I. A1 - Kuselman, I. A1 - Lee, Y. H. A1 - Sykes, D. E. A1 - Wang, M. A1 - Wang, H. A1 - Ogiwara, T. A1 - Nishio, M. A1 - Tanuma, S. A1 - Simons, D. A1 - Szakal, C. A1 - Osborn, W. A1 - Terauchi, S. A1 - Ito, M. A1 - Kurokawa, A. A1 - Fujiimoto, T. A1 - Jordaan, W. A1 - Jeong, C. S. A1 - Havelund, R. A1 - Spencer, S. A1 - Shard, A. A1 - Streeck, C. A1 - Beckhoff, B. A1 - Eicke, A. A1 - Terborg, R. T1 - CCQM pilot study P-140: Quantitative surface analysis of multi-element alloy films JF - Metrologia N2 - A pilot study for the quantitative surface analysis of multi-element alloy films has been performed by the Surface Analysis Working Group (SAWG) of the Consultative Committee for Amount of Substance (CCQM). The aim of this pilot study is to ensure the equivalency in the measurement capability of national metrology institutes for the quantification of multi-element alloy films. A Cu(In,Ga)Se2 (CIGS) film with non-uniform depth distribution was chosen as a representative multi-element alloy film. The atomic fractions of the reference and the test CIGS films were certified by isotope dilution - inductively coupled plasma/mass spectrometry. A total number counting (TNC) method was used as a method to determine the signal intensities of the constituent elements, which are compared with their certified atomic fractions. The atomic fractions of the CIGS films were measured by various methods, such as Secondary Ion Mass Spectrometry (SIMS), Auger Electron Spectroscopy (AES), X-ray Photoelectron Spectroscopy (XPS), X-Ray Fluorescence (XRF) analysis and Electron Probe Micro Analysis (EPMA) with Energy Dispersive X-ray Spectrometry (EDX). Fifteen laboratories from eight National Metrology Institutes (NMIs), one Designated Institute (DI) and six non-NMIs participated in this pilot study. Although the average atomic fractions of 18 data sets showed rather poor relative standard deviations of about 5.5 % to 6.8 %, they were greatly improved to about 1.5 % to 2.2 % by excluding 5 strongly deviating data sets from the average atomic fractions. In this pilot study, the average expanded uncertainties of SIMS, XPS, AES, XRF and EPMA were 3.84%, 3.68%, 3.81%, 2.88% and 2.90%, respectively. These values are much better than those in the key comparison K-67 for composition of a Fe-Ni alloy film. As a result, the quantification of CIGS films using the TNC method was found to be a good candidate as a subject for a CCQM key comparison. KW - CCQM KW - Pilot study KW - Surface analysis KW - Alloy films KW - CIGS PY - 2015 DO - https://doi.org/10.1088/0026-1394/52/1A/08017 SN - 0026-1394 SN - 1681-7575 VL - 52 IS - Technical Supplement SP - Article 08017 PB - Inst. of Physics Publ. CY - Bristol AN - OPUS4-35306 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gildenhaar, Renate A1 - Knabe, C. A1 - Wirth, Cynthia A1 - Linow, Ulf A1 - Houshmand, A. A1 - Berger, Georg T1 - Calcium alkaline phosphate scaffolds for bone regeneration 3D-fabricated by additive manufacturing JF - Key engineering materials N2 - Calcium alkaline phosphate granulates can be used for substitution of several bone defects but for the reconstruction of large skeletal parts in the maxillofacial and orthopaedic fields fitted scaffolds are preferable. Within the additive manufacturing methods, the 3D printing process offers exciting opportunities to generate defined porous scaffolds. We used a R1 printer from ProMetal Company, USA, for producing scaffolds directly from a ceramic powder. For this direct free form fabrication technology the powder has to possess a lot of specific properties both for the generation of a stable green body and also for the subsequent sintering preparation. For this printing process we prepared different granules in a fluidized bed process containing Ca2KNa(PO4)2 as main crystalline phase. Granules were characterized by different methods and several sieve fractions were used for preparing disc like and cylindrical parts. The suitability of granules for this printing process was determined by porosity and strength of produced bodies. Next to granules' performance both of these properties can be directly influenced by 3D printing process parameters. With knowledge of suitable process parameters scaffolds with different porosity in a respective desired design can be created. In this study, cylindrical scaffolds with graded porosity were produced for bone regeneration of segmental defects in maxillofacial surgery and dental implantology by tissue engineering. KW - 3D printing KW - Calcium alkaline phosphates KW - Ceramic scaffolds KW - Oral surgery PY - 2012 DO - https://doi.org/10.4028/www.scientific.net/KEM.493-494.849 SN - 1013-9826 N1 - Geburtsname von Wirth, Cynthia: Gomes, C. M. - Birth name of Wirth, Cynthia: Gomes, C. M. VL - 493-494 SP - 849 EP - 854 PB - Trans Tech Publ. CY - Aedermannsdorf AN - OPUS4-24989 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lopez-Heredia, M.A. A1 - Gildenhaar, Renate A1 - Berger, Georg A1 - Linow, Ulf A1 - Wirth, Cynthia A1 - Günster, Jens A1 - Houshmand, A. A1 - Stiller, M. A1 - Knabe-Ducheyne, C. T1 - Effect of stressed and unstressed cell culture environments on the viability of MC3T3 cells with calcium phosphates JF - Bioceramics development and applications T2 - ISACB-6 - International symposium on apatite and correlative biomaterials CY - Nantes, France DA - 2013-06-05 KW - Cell culture media KW - Fetal bovine serum KW - Stressed KW - Unstressed KW - Calcium alkaline orthophosphates PY - 2013 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-299387 DO - https://doi.org/10.4172/2090-5025.S1-002 SN - 2090-5017 SN - 2090-5025 N1 - Geburtsname von Wirth, Cynthia: Gomes, C. M. - Birth name of Wirth, Cynthia: Gomes, C. M. SP - 1 EP - 3(?) PB - Ashdin AN - OPUS4-29938 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Streeck, C. A1 - Wirth, Thomas A1 - Unger, Wolfgang A1 - Beckhoff, B. T1 - Qualifying calibration samples for advanced thin film materials characterisation JF - SPECTROSCOPY EUROPE N2 - In this article the question of the certification of calibration samples for the characterisation of advanced thin film materials is addressed within the framework of reliable process control or quality management purposes. Reference measurement techniques can be used in order to address the gap in appropriate certified reference materials (CRMs) for thin film analyses. They allow for qualifying out-of-production samples originating from an operating production line as calibration samples. As a template for this procedure, CIGS [Cu(In,Ga)Se2] layers, that are absorber layers for high efficiency thin-film solar cells, have been used for establishing and validating reference-free X-ray fluorescence (XRF) analysis and Auger-electron spectroscopy (AES) as reference measurement techniques. The focus was on determining the average mole fractions in the CIGS layers obtaining results traceable to the SI unit system. Reference-free XRF is physically traceable and is based upon radiometrically calibrated instrumentation and knowledge of atomic fundamental data. Sputter-assisted AES can be established as a chemically traceable method after careful calibration using a certified reference material (CRM) based on a total number counting method. KW - CIGS KW - X-ray fluorescence (XRF) KW - Auger-electron spectroscopy (AES) PY - 2018 UR - https://www.spectroscopyeurope.com/article/qualifying-calibration-samples-advanced-thin-film-materials-characterisation VL - 30 IS - 1 SP - 11 EP - 14 PB - John Wiley & Sons Ltd CY - Chichester, West Sussex PO19 8SQ, UK AN - OPUS4-44260 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bernardino, R. A1 - Wirth, C. A1 - Stares, S.L. A1 - Salmoria, G.V. A1 - Hotza, D. A1 - Günster, Jens T1 - Manufacturing of SiO2-Coated b-TCP Structures by 3D Printing using a Preceramic Polymer as Printing Binder and Silica Source JF - Journal Ceramic Science Technology N2 - Tricalcium phosphate (b-TCP) can be used as bone graft, exhibiting suitable bioabsorption and osteoconduction properties. The presence of silica may induce the formation of a hydroxyapatite layer, enhancing the integration between implant and bone tissue. Preceramic polymers present silicon in their composition, being a source of SiO2 after thermal treatment. Using the versatility of 3D printing, b-TCP and a polysiloxane were combined to manufacture a bulkb-TCP with a silica coating. For the additive manufacturing process, PMMA powder was used as passive binder for the b-TCP particles, and polymethylsilsesquioxane (MK), dissolved in an organic solvent, was used both as a printing binder (ink) and as the source of SiO2 for the coating. Five distinct coating compositions were printed with increasing amounts of MK. The structures were then submitted to heat treatment at 1180 °C for 4 h. XRD and FTIR showed no chemical reaction between the calcium phosphate and silica. SEM allowed observation of a silicon-based ating on the structure surface. Mechanical strength of the sintered porous structures was within the range of that of trabecular bones. KW - Tricalcium Phosphate KW - 3D-Printing KW - Preceramic polymer KW - Bone regeneration PY - 2018 DO - https://doi.org/10.4416/JCST2017-00056 VL - 9 IS - 1 SP - 37 EP - 41 PB - Göller Verlag CY - 76532 Baden-Baden AN - OPUS4-45715 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zocca, Andrea A1 - Elsayed, H. A1 - Bernardo, E. A1 - Wirth, Cynthia A1 - Lopez-Heredia, M.A. A1 - Knabe, C. A1 - Colombo, P. A1 - Günster, Jens T1 - 3D-printed silicate porous bioceramics using a non-sacrificial preceramic polymer binder JF - Biofabrication N2 - Silicate bioceramics possess an excellent bioactivity; however, shaping them into complex geometries is still challenging. Therefore, this paper aims to present a new strategy for the shaping of a bioglass-ceramic with controlled geometry and properties starting from a glass powder combined with a preceramic polymer, i.e. a silicon resin, and reactive fillers. The powder-based three-dimensional (3D)-printing of wollastonite (CaSiO3)-based silicate bioceramic parts was demonstrated in this work. The resin plays a dual role, as it not only acts as a non-sacrificial binder for the filler powders in the printing process but it also reacts with the fillers to generate the desired bioceramic phases. The mechanical and physical properties, i.e. ball-on-three-balls test, density, porosity and morphology, were evaluated in 3D-printed discs. These samples possessed a total porosity around 64 vol% and a biaxial flexural strength around 6 MPa. The raw materials used in this work also enabled the 3D-printing of scaffolds possessing a designed multi-scale porosity, suitable bioceramic phase assemblage and a compressive strength of 1 MPa (for cylindrical scaffolds with total porosity ~80 vol%). Solubility in TRIS/HCl and in vitro assays, i.e. viability, cytotoxicity and apoptosis assays, were also performed. In vitro tests indicated good cell viability and no cytotoxicity effect on the cells. KW - KNN KW - Glass microspheres PY - 2015 DO - https://doi.org/10.1088/1758-5090/7/2/025008 SN - 1758-5082 VL - 7 IS - 2 SP - 025008 PB - IOP Publ. CY - Philadelphia AN - OPUS4-34957 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sun, C. A1 - Tian, X. A1 - Wang, L. A1 - Liu, Y. A1 - Wirth, Cynthia A1 - Günster, Jens A1 - Li, D. A1 - Jin, Z. T1 - Effect of particle size gradation on the performance of glass-ceramic 3D printing process JF - Ceramics International N2 - Particle size gradation is regarded as an effective method for overcoming the contradicting requirements in three-dimensional printing (3DP). In present work, particle size gradation was optimized to obtain both acceptable flowability of the powder material and high-strength 3D-printed glass-ceramic products. The effect of gradation on the printing process, sintering process and performance of the 3D-printed glass-ceramic products was investigated comprehensively. The glass-ceramic powders with three size ranges were mixed in certain proportions and applied to print parts. The result showed parts printed with powder mixed by 60 wt% 45–100 µm and 40 wt% 0–25 µm particles had satisfactory density of 1.60 g/cm³ and bending strength of 13.8 MPa. The flowability decreased with an increasing proportion of fine particles. Part density was determined by the powder bulk density in the powder bed as well as the shrinkage during sintering while strength of part was found to be dependent on the sintering degree. KW - Flowability KW - Glass-ceramic KW - Particle size gradation KW - Three-dimensional printing KW - Mechanical properties PY - 2017 DO - https://doi.org/10.1016/j.ceramint.2016.09.197 SN - 0272-8842 VL - 43 IS - 1 SP - 578 EP - 584 PB - Elsevier AN - OPUS4-39783 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kraffert, K. A1 - Karg, M. A1 - Schmack, R. A1 - Clavel, G. A1 - Boissiere, C. A1 - Wirth,, Thomas A1 - Pinna, N. A1 - Kraehnert, R. T1 - Stabilization of Mesoporous Iron Oxide Films against Sintering and Phase Transformations via Atomic Layer Deposition of Alumina and Silica JF - Advanced materials interfaces N2 - The stabilization of crystal phases and nanostructured morphologies is an essential topic in application-driven design of mesoporous materials. Many applications, e.g. catalysis, require high temperature and humidity. Typical metal oxides transform under such conditions from a metastable, low crystal-line material into a thermodynamically more favorable form, i.e. from ferrihy-drite into hematite in the case of iron oxide. The harsh conditions induce also a growth of the crystallites constituting pore walls, which results in sintering and finally collapse of the porous network. Herein, a new method to stabi-lize mesoporous templated metal oxides against sintering and pore collapse is reported. The method employs atomic layer deposition (ALD) to coat the internal mesopore surface with thin layers of either alumina or silica. The authors demonstrate that silica exerts a very strong influence: It shifts hematite formation from 400 to 600 °C and sintering of hematite from 600 to 900 °C. Differences between the stabilization via alumina and silica are rationalized by a different interaction strength between the ALD material and the ferrihydrite film. The presented approach allows to stabilize mesoporous thin films that require a high crystallization temperature, with submonolayer quantity of an ALD material, and to apply mesoporous materials for high temperature applications. KW - Mesoporous oxides KW - Atomic layer deposition KW - Stabilization PY - 2018 DO - https://doi.org/10.1002/admi.201800360 VL - 5 IS - 14 SP - 1800360-1 EP - 1800360-9 PB - Wiley-VCH AN - OPUS4-47869 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hinze, A. A1 - Klages, C.-P. A1 - Zänker, A. A1 - Thomas, M. A1 - Wirth, Thomas A1 - Unger, Wolfgang T1 - ToF-SIMS imaging of DBD-plasma-printed microspots on BOPP substrates JF - Plasma processes and polymers N2 - Imaging ToF-SIMS has been applied to characterize the surface chemistry variations across small areas produced by a DBD-type plasma printing technique on a BOPP substrate using pure nitrogen and a nitrogen-hydrogen gas mixture. CH4N+ and CNO- secondary ions are detected with high yields remote from the discharge region. They are discussed to be due to surface modifications of the substrate by metastable gas-phase species. On the other hand, surface species exist that are preferentially formed by reactions of the substrate with short-lived species which are only present close to the plasma discharge region. A C3H8O+ secondary fragment ion is assumed to be a key fragment of such a surface species. KW - ToF-SIMS KW - Plasma KW - Polymer KW - Dielectric barrier discharges (DBD) KW - Plasma printing KW - Polymer modification KW - Surface modification KW - Time-of-flight secondary-ion mass spectroscopy (ToF-SIMS) imaging PY - 2008 DO - https://doi.org/10.1002/ppap.200700138 SN - 1612-8850 SN - 1612-8869 VL - 5 IS - 5 SP - 460 EP - 470 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-19342 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -