TY - JOUR A1 - de Carvello, J. M. F. A1 - Carvalho Fontes, W. A1 - de Azevedo, C. F. A1 - Brigolini, G. J. A1 - Schmidt, Wolfram A1 - Fiorotti Peixoto, R. A. T1 - Enhancing the eco-efficiency of concrete using engineered recycled mineral admixtures and recycled aggregates N2 - Non-conventional densely packed concrete mixtures are proposed and evaluated in this paper using engineered recycled mineral admixtures and recycled aggregates obtained from steel slag, quartz mining tailings, and quartzite mining tailings. High fines content sand-concretes containing coarser- and finer-than-cement recycled powders were designed to obtain blends with broader particle-size ranges and improved packing density. As a result, compressive strength up to 99 MPa, cement intensity up to 2.33 kg/m³/MPa, and consumption of recycled material up to 95 vol% were obtained. Compressive strengths up to 66 MPa and cement intensity up to 2.34 kg/m³/MPa were also obtained with the addition of coarse aggregates to such sand-concrete mixtures, with consumption of recycled material up to 96.5%. The results launch new insights on the role of recycled admixtures and aggregates on the mixture design of cement-based composites regarding efficiency improvement and technological performance. KW - Low-cement concrete KW - Recycled mineral admixture KW - Basic oxygen furnace slag KW - Quartzite mining tailing KW - Packing density PY - 2020 DO - https://doi.org/10.1016/j.jclepro.2020.120530 VL - 257 SP - 1 EP - 12 PB - Elsevier AN - OPUS4-58401 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rodrigues, A. C. P. A1 - Feller, A. A1 - Agudo Jácome, Leonardo A1 - Azevedo, C. R. F. T1 - Use of synthetic Fe3O4-rich tribofilms to investigate the effect of microconstituents, temperature and atmosphere on the friction coefficient during pin-on-disc tribotest N2 - This work investigates the effect of the tribotesting parameters (temperature, atmosphere, and third body chemical composition) on the coefficient of friction (CoF) during pin-on-disc dry (PoD) sliding tribotests using artificial third bodies. The third body comprised nanometric Fe3O4-based binary to quaternary chemical compositions containing copper, graphite, and zirconia. These mixtures were manually or ball-milled prepared, and pin-on-disc tribotests were conducted at 23 °C and 400 °C under air or nitrogen atmospheres. Combining PoD and artificial third body to create synthetic tribofilms might be useful for testing new formulations of Cu-free friction materials. Microstructural characterisation of the tribofilms was used to study the stability of the Fe3O4, copper, and graphite nanoparticles under different testing conditions to understand their effects on the CoF. For the Fe3O4-C-ZrO2-X systems, the ball milling mixing promoted the formation of turbostratic graphite in the tribofilm, impairing the lubricating effect of the graphite under air atmosphere at 23 °C. The formation of monoclinic CuO in the tribofilms during tribotests at 400 °C under air and N2 atmospheres promoted a lubricating effect. KW - Tribology KW - Microstructure KW - Oxide KW - Transmission electron microscopy PY - 2022 DO - https://doi.org/10.1088/2051-672X/ac9d51 SN - 2051-672X VL - 10 IS - 4 SP - 044009-1 EP - 044009-18 PB - IOP Pobilishing AN - OPUS4-56467 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -