TY - CONF A1 - Rosemann, Paul A1 - Kauss, N. A1 - Müller, C. A1 - Halle, T. T1 - Heat treatment and corrosion resistance of cutlery N2 - Hardness and pitting corrosion resistance are the major quality criteria of cutlery. Both are achieved by the heat treatment (austenitization, quenching and tempering) of the normally used martensitic stainless steels. The established quality control method regarding the pitting corrosion resistance is an alternating immersion test in 1 % NaCl solution at 60 °C according to DIN EN ISO 8442. This standard test shows a high deviation, which limits any optimization of the heat treatment process. New approaches for corrosion testing of martensitic stainless-steels were developed and used in the last years to connect the weak pitting corrosion resistance of martensitic stainless-steels with the phenomenon of chromium depletion. The tempering temperatures used in the industrial heat treatment of cutlery are too low to explain the appearance of chromium depletion. For this reason, a systematic investigation of three heat treatment parameters (austenitization time, cooling speed and tempering temperature) were performed on the martensitic stainless-steels X50CrMoV15 (1.4116) to detect their contribution to chromium depletion. The electrochemical potentiodynamic reactivation (EPR), which is very sensitive to any change of the microstructure, was used to quantify the degree of chromium depletion. The KorroPad indicator-test was applied to correlate low pitting corrosion resistance to the presence of chromium depletion. The results of all investigations allow conclusions about the very small process window, which is necessary to achieve cutlery with high pitting corrosion resistance. T2 - EUROCORR 2018 CY - Krakow, Poland DA - 09.09.2018 KW - Corrosion KW - KorroPad KW - Stainless steel KW - Corrosion resistance KW - Heat treatment KW - EPR KW - Pitting corrosion KW - Martensitic stainless steels KW - REM PY - 2018 AN - OPUS4-45952 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Roßberg, S. A1 - Pensel, P. A1 - Halle, T. A1 - Burkert, A. T1 - Precipitation behavior and corrosion resistance of nickel-free, high-nitrogen austenitic stainless steels N2 - Nickel-free, nitrogen alloyed austenitic stainless-steels, with about 19 wt.-% Mn and 0,8 wt. % N, are an interesting alternative to classic CrNi austenitic stainless steels due to their superior mechanical properties (Rm > 900 MPa, A5 > 50 %, Av > 350 J) in the solution annealed condition. The formation of chromium-rich nitrides during suboptimal heat treatment, processing or application leads to an inhomogeneous distribution of alloying elements in the microstructure, which reduces the corrosion resistance. Consequently, an accurate knowledge of the sensitization behavior is indispensable for the use of nickel-free, high-nitrogen austenitic stainless steels. The relationship between artificial aging, phase formation and corrosion resistance was investigated on the alloys X8CrMnN18-19 (1.3815) and X8CrMnMoN18-19-2 (1.4456), both alloyed with 0,8 wt.-% Nitrogen, in the present work. The microstructural evolution was studied by LM and SEM while the corrosion resistance was characterized with the electrochemical potentiodynamic reactivation (EPR) and the KorroPad indicator-test. Both alloys showed increased corrosion susceptibility within critical aging parameters. Finally, a sensitization diagram was described successfully for both alloys showing the positive effect of molybdenum. T2 - EUROCORR 2018 CY - Krakow, Poland DA - 09.09.2018 KW - Corrosion KW - KorroPad KW - Stainless steel KW - Corrosion resistance KW - Heat treatment KW - ThermoCalc KW - Pitting corrosion KW - Nitrogen PY - 2018 AN - OPUS4-45954 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Baumann, O. A1 - Müller, C. T1 - Influence of the post-weld surface treatment on the corrosion resistance of the duplex stainless steel 1.4062 N2 - The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polishing or blasting depending on the requested corrosion resistance. Blasted surfaces are often used in the industrial practice due to the faster and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the results of different corrosion tests (KorroPad-testing and pitting potentials). T2 - Materials Science and Engineering 2018 (MSE) CY - Darmstadt, Germany DA - 26.09.2018 KW - Duplexstahl KW - Korrosion KW - Nichtrostender Stahl KW - Schweißen KW - Oberflächenbearbeitung KW - Strahlen KW - KorroPad PY - 2018 AN - OPUS4-46090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grötzsch, D. A1 - Streeck, C. A1 - Nietzold, Carolin A1 - Malzer, W. A1 - Mantouvalou, I. A1 - Nutsch, A. A1 - Dietrich, Paul A1 - Unger, Wolfgang A1 - Beckhoff, B. A1 - Kanngießer, B. T1 - A sealable ultrathin window sample cell for the study of liquids by means of soft X-ray spectroscopy N2 - A new sample cell concept for the analysis of liquids or solid-liquid interfaces using soft X-ray spectroscopy is presented, which enables the complete sealing of the cell as well as the Transport into vacuum via, for example, a load-lock system. The cell uses pressure monitoring and active as well as passive pressure regulation systems, thereby facilitating the full control over the pressure during filling, sealing, evacuation, and measurement. The cell design and sample preparation as well as the crucial sealing procedure are explained in detail. As a first proof-of-principle experiment, successful nitrogen K-edge fluorescence yield near-edge X-ray absorption fine structure experiments of a biomolecular solution are presented. For this purpose, it is shown that the careful evaluation of all involved parameters, such as window type or photon flux, is desirable for optimizing the experimental result. KW - X-ray spectroscopy KW - Analysis of liquids KW - Wet cell KW - Concanavalin A KW - NEXAFS PY - 2017 DO - https://doi.org/10.1063/1.5006122 SN - 0034-6748 SN - 1089-7623 VL - 88 IS - 12 SP - 123112-1 EP - 123112-7 PB - American Institute of Physics AN - OPUS4-43611 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kern, Simon A1 - Wander, Lukas A1 - Meyer, Klas A1 - Guhl, Svetlana A1 - Gottu Mukkula, A. R. A1 - Holtkamp, M. A1 - Salge, M. A1 - Fleischer, C. A1 - Weber, N. A1 - Engell, S. A1 - Paul, Andrea A1 - King, R. A1 - Maiwald, Michael T1 - Raw data of pilot plant runs for CONSENS project (Case study 1) N2 - In case study one of the CONSENS project, two aromatic substances were coupled by a lithiation reaction, which is a prominent example in pharmaceutical industry. The two aromatic reactants (Aniline and o-FNB) were mixed with Lithium-base (LiHMDS) in a continuous modular plant to produce the desired product (Li-NDPA) and a salt (LiF). The salt precipitates which leads to the formation of particles. The feed streams were subject to variation to drive the plant to its optimum. The uploaded data comprises the results from four days during continuous plant operation time. Each day is denoted from day 1-4 and represents the dates 2017-09-26, 2017-09-28, 2017-10-10, 2017-10-17. In the following the contents of the files are explained. KW - Process Analytical Technology KW - Multivariate Data Analysis KW - Nuclear Magnetic Resonance KW - Near Infrared Spectroscopy KW - Continuous Manufacturing KW - CONSENS PY - 2018 DO - https://doi.org/10.5281/zenodo.1438233 PB - Zenodo CY - Geneva AN - OPUS4-48063 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Baumann, O. A1 - Modersohn, W. A1 - Halle, T. T1 - Influence of the post-weld surface treatment on the corrosion resistance of the duplex stainless steel 1.4062 N2 - The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polished or blasting depending on the application and the requested corrosion resistance. Blasted surfaces are often used in industrial practice due to the easier and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the different performed corrosion tests (potential measurement, KorroPad-test and pitting potential) on welding seams with different surface treatments. T2 - 19. Werkstofftechnisches Kolloquium Chemnitz CY - Chemnitz, Germany DA - 16.03.2017 KW - Corrosion resistance KW - Duplex stainless steel KW - Influence PY - 2017 SN - 978-3-00-055705-7 SN - 1439-1597 VL - 61 SP - 172 EP - 180 PB - Schriftreihe Werkstoffe und werkstofftechnische Anwendungen CY - Chemnitz AN - OPUS4-40168 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paul, Astrid A1 - Ziegert, C. A1 - Fontana, Patrick A1 - Meyer, J. T1 - StandardBoard - Produktnorm für Lehmplatten T1 - StandardBoard - A product standard for earthen panels N2 - Die Anwendung von modernen Lehmbaustoffen hat in den letzten Jahren überdurchschnittliche Wachstumsraten erreicht. Für Bauherren und Planer ausschlaggebend ist häufig ihr extrem niedriger CO2-Äquivalentkennwert. Entsprechend wurden Lehmplatten in einem Projekt mit Pilotcharakter für den Umbau des alten Abgeordnetenhauses in Bonn zum Gebäude des Klimareferats der Vereinten Nationen verwendet. Bei der Entscheidung für die Bauweise mit Lehmplatten standen vor allem raumklimatische und schallschutztechnische, das heißt gesundheitliche Aspekte, aber auch der Wunsch nach erhöhter Nachhaltigkeit im Vordergrund. Durch das Fehlen einer Norm entstehen im Vergleich zu geregelten Bauprodukten jedoch noch deutliche Wettbewerbsnachteile für Produzenten von Lehmplatten. Planer und Anwender sehen aufgrund fehlender Prüfzertifikate nicht selten von der Anwendung dieser Lehmbaustoffe ab. Wie schon für Lehmsteine und Lehmmörtel sollen deshalb jetzt auch für Lehmplatten an der Bundesanstalt für Materialforschung und -prüfung (BAM) in dem Projekt StandardBoard Grundlagen für eine Produktnorm geschaffen werden. Darin ist als Projektpartner der Hersteller Conluto beteiligt. Zweck des in Erarbeitung befindlichen Regelwerks ist es, über die Festlegung von Qualitätsanforderungen und Prüfvorschriften die Gebrauchstauglichkeit von Lehmplatten sicherzustellen und somit einerseits Sicherheit für Planer und Anwender und andererseits Vergleichbarkeit und damit Konkurrenzfähigkeit zu konventionellen Plattenprodukten für gleiche Einbaubereiche zu erreichen. Darüber hinaus stellt sie ein Instrument dar, um die besonderen ökologischen und bauphysikalischen Eigenschaften der Lehmbaustoffe hervorzuheben. Die Erarbeitung des Regelwerks erfolgt in enger Abstimmung mit dem Dachverband Lehm e. V. (DVL). N2 - In recent years. the utilization of modern building materials made from soil has extended considerably. For building principals and designers. this decision is often determined by their extremely low carbon dioxide equivalent. A paradigm is the application of earth panels in the conversion of the former House of Representatives in Bonn to the secretariat of the United Nations Framework Convention on Climate Change. The choice of earth panels was determined not only by considerations of indoor climate and acoustic insulation issues. but particularly by an endeavour to attain a high level of sustainability. The lack of a standard causes producers of earth panels to experience considerable competitive disadvantages. With the absence of test certificates. designers as well as implementers refrain from using earth materials. The project StandardBoard has been initiated with the purpose of developing the basis for a product standard for earth panels. being realized at the BAM. where also standards for earth blocks and earth mortars have been developed. The BAM is cooperating with the project partner Conluto. a manufacturer of earth panels. The object of the standard being in development is to guarantee the usability of earth panels by stating quality requirements and testing procedures and thereby to achieve safety for designers and users as well as competitiveness with established panels. Furthermore. a standard allows to emphasize the special ecological and climatic features of earth materials. The drafting of the standard is coordinated in close relation to the German Association for Earth Construction (DVL). T2 - Lehm 2016 - 7. Internationale Fachtagung für Lehmbau - 7th International Conference on Building with Earth CY - Weimar, Germany DA - 12.11.2016 KW - Baustoffe KW - Moderne Lehmbaustoffe KW - Lehmplatte KW - Normung KW - Prüfung KW - Produktqualität KW - Building materials KW - Modern earthen building materials KW - Earth panel KW - Standardisation KW - Testing KW - Product quality PY - 2016 SP - 1 EP - 12 PB - Eigenverlag Dachverband Lehm e. V. CY - Weimar AN - OPUS4-38996 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Meyer, A. A1 - Halle, T. ED - Lampke, T. ED - Wagner, G. ED - Wagner, M. F.-X. T1 - Einfluss von Stickstoff auf Mikrostruktur und Korrosionsverhalten martensitischer nichtrostender Stähle N2 - Die Korrosionsbeständigkeit martensitischer nichtrostender Stähle (MNS) wird wesentlich von der chemischen Zusammensetzung und dem Wärmebehandlungszustand beeinflusst. Beides bestimmt die Verteilung der Legierungselemente im Gefüge und die daraus resultierenden Werkstoffeigenschaften. Das Legieren mit Stickstoff bewirkt im Allgemeinen eine Verbesserung der Lochkorrosionsbeständigkeit von nichtrostenden Stählen. Bei martensitischen nichtrostenden Stählen ist dieser Effekt nicht nur auf den Stickstoffgehalt selbst zurückzuführen, sondern auch auf den gleichzeitig verringerten Kohlenstoffgehalt, der ebenfalls das Ergebnis der Wärmebehandlung beeinflusst. In dieser Arbeit wird der Einfluss von Stickstoff auf die Korrosionsbeständigkeit in Bezug zum Härtungsprozess von MNS dargestellt. Dazu wird vergleichend der Effekt von Austenitisierungsdauer, -temperatur und Abkühlgeschwindigkeit auf Gefüge, Härte und Korrosionsbeständigkeit der MNS X50CrMoV15 und X30CrMoN15 1 untersucht. Die Abkühlgeschwindigkeit wurde mit dem Stirnabschreckversuch gezielt variiert, um den Einfluss von Abkühlgeschwindigkeiten von > 100 K/s bis 1 K/s zu charakterisieren. Die Veränderungen der Korrosionsbeständigkeit werden durch die elektrochemisch potentiodynamische Reaktivierung (EPR) und durch die Bestimmung kritischer Lochkorrosionspotentiale dokumentiert. Neben diesem experimentellen Ansatz werden auch die Ergebnisse von thermodynamischen Berechnungen mit der Software Thermocalc vorgestellt und abschließend auch zur Interpretation des Einflusses von Stickstoff auf die Korrosionsbeständigkeit martensitischer nichtrostender Stähle genutzt. T2 - 18. Werkstofftechnisches Kolloquium der TU Chemnitz CY - Chemnitz, Germany DA - 10.03.2016 KW - Korrosionsbeständigkeit KW - Corrosion resistance KW - Wärmebehandlung KW - Heat treatment KW - Nichtrostende Stähle KW - Stainless steels KW - Thermocalc KW - Thermocalc PY - 2016 SN - 978-3-00-052212-3 SN - 1439-1597 VL - 59 SP - 325 EP - 336 PB - TU Chemnitz, Fakultät für Maschinenbau, Institut für Werkstoffwissenschaft und Werkstofftechnik CY - Chemnitz AN - OPUS4-37263 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Halle, T. T1 - Einfluss der Schweißnaht-Nachbehandlung auf die Korrosionsbeständigkeit vom Duplexstahl 1.4062 N2 - Der Duplexstahl 1.4062 (X2CrNi22-2) hat sich im Bauwesen als Werkstoffalternative zu den nichtrostenden Austeniten etabliert. Die Korrosionsbeständigkeit von Schweißverbindungen wird, neben dem Grundwerkstoff, dem Schweißzusatzwerkstoff und dem Schweißverfahren, auch sehr stark von der Schweißnaht-Nachbehandlung beeinflusst. Je nach zukünftigem Anwendungsbereich, geforderter Optik und Korrosionsbeständigkeit wird die Schweißnaht geschliffen, gebeizt, elektropoliert oder gestrahlt, um die beim Schweißen entstehenden An-lauffarben zu entfernen. Gestrahlte Oberflächen sind in der industriellen Praxis häufig anzutreffen, da sie deutlich schneller und kostengünstiger herzustellen sind als geschliffene, gebeizte oder polierte Oberflächen. Das Strahlen mit Korund ist außerdem effektiver als das Strahlen mit Glasperlen. In den letzten Jahren wurden korrosionsanfällige Oberflächen bei nichtrostenden Stählen beobachtet, wenn diese mit Korund geschliffen wurden. Daher wird nun auch beim Strahlen kritisch hinterfragt, ob die eingesetzten Strahlmittel die Korrosionsbeständigkeit beeinflussen. Diese Fragestellung wird beantwortet, indem geschliffene, gebeizte, polierte und mit verschiedenen Strahlmitteln gestrahlte Schweißverbindungen vom Duplexstahl 1.4062 im Vergleich zu gleichartig behandeltem Walzmaterial untersucht werden. Die Ergebnisse der Korrosionsuntersuchungen werden vorgestellt und mit den rasterelektronenmikroskopischen Untersuchungen der gestrahlten Oberflächen korreliert. T2 - 16. Sommerkurs Werkstoffe und Fügen CY - Magdeburg, Germany DA - 08.09.2017 KW - Duplexstahl KW - Nichtrostender Stahl KW - Schweißen KW - Oberflächenbearbeitung KW - Strahlen KW - Korrosion PY - 2017 SN - 978-3-944722-58-0 DO - https://doi.org/10.24352/UB.OVGU-2017-75 SP - 63 EP - 70 AN - OPUS4-41888 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Kauss, N. A1 - Müller, C. A1 - Halle, T. T1 - Einfluss der Abkühlgeschwindigkeit auf die Neigung zur Chromverarmung martensitischer nichtrostender Stähle N2 - Die Legierungselemente (Chrom und Kohlenstoff) und die Wärmebehandlung bestimmen Korrosionsbeständigkeit und Härte martensitischer nichtrostender Stähle. Verschiedene wissenschaftliche Arbeiten haben bereits gezeigt, dass die Korrosionsbeständigkeit sehr stark vom Anteil an Chromkarbiden im Gefüge bestimmt wird. Der kombinierte Einfluss von Kohlenstoffgehalt und der Abkühlgeschwindigkeit beim Härten wurde mit Fokus auf die Korrosionsbeständigkeit bisher nur unzureichend untersucht. Die Literatur liefert außerdem gegensätzliche Aussagen über den Einfluss der Abkühlgeschwindigkeit, was möglicherweise auf unterschiedliche Kohlenstoffgehalte zurückgeführt werden kann. In dieser Arbeit wird daher systematisch untersucht, ab welcher Abkühlgeschwindigkeit es bei den Werkstoffen X20Cr13 und X46Cr13 zu Karbidbildung und Chromverarmung kommt. Die Variation der Abkühlgeschwindigkeit erfolgte für die industriell relevante Härtetemperatur von 1050 °C mit dem Stirnabschreckversuch. In Abhängigkeit von der Abkühlgeschwindigkeit wurden an den Stirnabschreckproben Gefüge, Härte und Korrosionsbeständigkeit (EPR, kritische Lochkorrosionspotentiale) untersucht und die Ergebnisse mit thermodynamischen Berechnungen (ThermoCalc) korreliert. Aus den Ergebnissen wird abgeleitet, unter welchen Bedingungen die Abkühlgeschwindigkeit die Korrosionsbeständigkeit beeinflusst. T2 - 16. Sommerkurs Werkstoffe und Fügen CY - Magdeburg, Germany DA - 08.09.2017 KW - Wärmebehandlung KW - Korrosion KW - Chromverarmung KW - EPR KW - Martensitischer nichtrostender Stahl KW - ThermoCalc KW - Lochkorrosion PY - 2017 SN - 978-3-944722-58-0 DO - https://doi.org/10.24352/UB.OVGU-2017-75 SP - 71 EP - 78 AN - OPUS4-41889 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Halle, T. T1 - Sensibilisierungsverhalten vom stickstofflegierten, austenitischen, nichtrostenden Stahl 1.4456 N2 - Austenitische nichtrostende Stähle kommen seit vielen Jahren in den verschiedensten industriellen Zweigen zum Einsatz (Pharma-, Medizin- und Lebensmittelindustrie, Bauwesen, Energie- und Antriebstechnik). Druckaufgestickte nichtrostende Austenite mit ca. 19 Gew.-% Mangan und 0,8 Gew.-% Stickstoff, sind als nickelfreie Variante seit einigen Jahren großtechnisch auf dem Markt verfügbar. In diesen Stählen wird die austenitische Matrix ohne die Legierungszugabe von Nickel sichergestellt, während gleichzeitig die korrosive Beständigkeit und die mechanischen Eigenschaften verbessert werden. Wie bei allen nichtrostenden Stählen beeinflussen die chemische Zusammensetzung und die Wärmebehandlung entscheidend das Gefüge und die Eigenschaften. Durch Lösungsglühen, Abschrecken und gezieltes Kaltverfestigen können bei diesen Stählen hervorragende mechanische Kennwerte erreicht werden (Rm von 900 MPa bis 2.000 MPa, A5 > 50 %, Av > 350 J). In der Regel dient das Lösungsglühen der Beseitigung unerwünschter Ausscheidungsphasen (Cr2N, M23C6 und Sigma-Phase) und der homogenen Verteilung der Legierungselemente im Austenit, was auch die Voraussetzung für eine hohe Korrosionsbeständigkeit darstellt. Wird die homogene Verteilung der Legierungselemente (Cr, Mo und N) durch suboptimale Wärmebehandlungs-, Verarbeitungs- oder Einsatzbedingungen beeinträchtigt, kann die korrosive Beständigkeit nicht auf Dauer gewährleistet werden. Daher ist die genaue Kenntnis vom Sensibilisierungsverhalten dieser hochstickstofflegierten Stähle unerlässlich. Am stickstofflegierten Werkstoff 1.4456 (X8CrMnMoN18-18-2) wird das Sensibilisierungsverhalten am lösungsgeglühten Zustand durch die gezielte Variation der Warmauslagerungsparameter untersucht. Dabei wird im Temperaturbereich von 500 °C bis 900 °C die Glühdauer systematisch variiert, um zu ermitteln, wann Ausscheidungen im Gefüge auftreten und ob diese die Korrosionsbeständigkeit beeinträchtigen. Die verschiedenen Sensibilisierungszustände werden mit dem EPR Verfahren, der KorroPad-Prüfung und dem REM vergleichend untersucht. Zur besseren Interpretation der experimentellen Ergebnisse werden auch thermodynamische Berechnungen genutzt, welche die Existenzbereiche der verschiedenen Ausscheidungsphasen vorhersagen. Damit kann die Veränderung der Korrosionsbeständigkeit mit dem Auftreten der verschiedenen Phasen korreliert und die Anwendbarkeit der experimentellen Methoden für stickstofflegierte Stähle nachgewiesen werden. T2 - 16. Sommerkurs Werkstoffe und Fügen CY - Magdeburg, Germany DA - 08.09.2017 KW - Nichtrostender Stahl KW - Wärmebehandlung KW - Korrosion KW - Stickstoff KW - EPR KW - KorroPad KW - ThermoCalc PY - 2017 SN - 978-3-944722-58-0 DO - https://doi.org/10.24352/UB.OVGU-2017-75 SP - 79 EP - 86 AN - OPUS4-41890 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -