TY - GEN A1 - Müller, R. A1 - Brechbühl, Y. A1 - Lutzenberger, S. A1 - Said, Samir A1 - Auersch, Lutz A1 - Guigou-Carter, C. A1 - Villot, M. A1 - Müller, R. ED - Degrande, G. ED - al., et T1 - Vibration Excitation at Turnouts, Mechanism, Measurements and Mitigation Measures N2 - There is a strong need for cost-effective mitigation measures for turnouts. SBB has initiated a series of examinations using different methodologies to gain a deeper understanding of the excitation mechanisms at low frequencies, in addition to that obtained in the RIVAS project. To date it is not yet clear what constitutes a complete measurement data set that would enable understanding most of the vibration excitation mechanisms in turnouts. Increasing vibration at turnouts in comparison to normal track is observed for all measured frequencies. The different methodologies are presented in the paper. Under-sleeper pads (USP) are a cost-effective method to reduce vibration at frequencies above 63 Hz (1/3 octave), but there is probably no improvement for frequencies below 63 Hz. A first test of new frog geometry did not show relevant improvements in Vibration emission in comparison to a reference frog geometry. Axle box acceleration measurements are an interesting method to identify defects in a turnout. A specialized measurement system of rail roughness could identify certain geometry Problem areas for some frogs. Noise increases also are observed at turnouts for frequencies ranging between 80 to 1000 Hz. The use of railway source models to calculate contact forces for ballasted track and turnouts seems promising, in particular for understanding the influence of ground. KW - Turnout KW - Switch KW - Vibration excitation KW - Vibration measurements PY - 2021 SN - 978-3-030-70288-5 DO - https://doi.org/10.1007/978-3-030-70289-2_42 SN - 1612-2909 VL - 150 SP - 403 EP - 410 PB - Springer Nature Switzerland AG CY - Cham AN - OPUS4-52612 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Abou-Ras, D. A1 - Caballero, R. A1 - Fischer, C.-H. A1 - Kaufmann, C.A. A1 - Lauermann, I. A1 - Mainz, R. A1 - Mönig, H. A1 - Schöpke, A. A1 - Stephan, C. A1 - Streeck, C. A1 - Schorr, S. A1 - Eicke, A. A1 - Döbeli, M. A1 - Gade, B. A1 - Hinrichs, J. A1 - Nunney, T. A1 - Dijkstra, H. A1 - Hoffmann, V. A1 - Klemm, D. A1 - Efimova, V. A1 - Bergmaier, A. A1 - Dollinger, G. A1 - Wirth, Thomas A1 - Unger, Wolfgang A1 - Rockett, A.A. A1 - Perez-Rodriguez, A. A1 - Alvarez-Garcia, J. A1 - Izquierdo-Roca, V. A1 - Schmid, T. A1 - Choi, P.-P. A1 - Müller, M. A1 - Bertram, F. A1 - Christen, J. A1 - Khatri, H. A1 - Collins, R.W. A1 - Marsillac, S. A1 - Kötschau, I. T1 - Comprehensive comparison of various techniques for the analysis of elemental distributions in thin films N2 - The present work shows results on elemental distribution analyses in Cu(In,Ga)Se2 thin films for solar cells performed by use of wavelength-dispersive and energy-dispersive X-ray spectrometry (EDX) in a scanning electron microscope, EDX in a transmission electron microscope, X-ray photoelectron, angle-dependent soft X-ray emission, secondary ion-mass (SIMS), time-of-flight SIMS, sputtered neutral mass, glow-discharge optical emission and glow-discharge mass, Auger electron, and Rutherford backscattering spectrometry, by use of scanning Auger electron microscopy, Raman depth profiling, and Raman mapping, as well as by use of elastic recoil detection analysis, grazing-incidence X-ray and electron backscatter diffraction, and grazing-incidence X-ray fluorescence analysis. The Cu(In,Ga)Se2 thin films used for the present comparison were produced during the same identical deposition run and exhibit thicknesses of about 2 µm. The analysis techniques were compared with respect to their spatial and depth resolutions, measuring speeds, availabilities, and detection limits. KW - Elemental distributions KW - Comparison KW - Depth profiling KW - Chemical mapping KW - Thin films KW - Solar cells KW - Chalcopyrite-type KW - Cu(In,Ga)Se2 PY - 2011 DO - https://doi.org/10.1017/S1431927611000523 SN - 1431-9276 SN - 1435-8115 VL - 17 IS - 5 SP - 728 EP - 751 PB - Cambridge University Press CY - New York, NY AN - OPUS4-24506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller-Mai, C.M. A1 - Berger, Georg A1 - Stiller, M. A1 - Gildenhaar, Renate A1 - Jörn, Daniela A1 - Ploska, Ute A1 - Houshmand, A. A1 - Bednarek, A. A1 - Koch, C. A1 - Knabe, C. T1 - Evaluation of degradable bone cements for percutaneous augmentation of bone defects KW - Bone defect KW - Bioactive bone cement KW - Calcium alkali orthophosphates KW - Histology KW - Histomorphometry KW - Knochendefekt KW - Bioaktiver Knochenzement KW - Calciumalkaliorthophosphat KW - Histologie KW - Histomorphometrie PY - 2010 DO - https://doi.org/10.1002/mawe.201000706 SN - 0933-5137 SN - 1521-4052 VL - 41 IS - 12 SP - 1040 EP - 1047 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-22891 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Masendorf, R. A1 - Müller, C. A1 - Henkel, C. A1 - Klingelhöffer, Hellmuth A1 - Klubberg, F. A1 - Scholz, A. A1 - Wagener, R. ED - Borsutzki, M. ED - Moninger, G. T1 - DIN 50100 Schwingfestigkeitsversuch - Aktueller Stand der Überarbeitung N2 - DIN 50100 definiert die Bedingungen für den Schwingfestigkeitsversuch, der zur Ermittlung von Kennwerten dient, die das Verhalten metallischer Werkstoffe und Bauteile bei zyklischer Beanspruchung mit einer konstanten Lastamplitude beschreiben (Wöhlerversuch). Die Norm umfasst die Versuchsdurchführung, die Versuchsauswertung sowie die Dokumentation von lastgeregelten Wöhlerversuchen im Zeit- und Langzeitfestigkeitsbereich. Mit DIN 50100 soll erreicht werden, dass die Wöhlerlinien verschiedener Prüfstellen miteinander vergleichbar und die wesentlichen Randbedingungen der Versuchsdurchführung dokumentiert werden. Da die Ergebnisse von Schwingfestigkeitsversuchen streuen, ist die Treffsicherheit für die Schätzung der Kennwerte von der Anzahl der Versuche einer Versuchsreihe abhängig. In Abhängigkeit von einer geforderten Treffsicherheit wird durch die DIN 50100 der erforderliche Stichprobenumfang vorgegeben. T2 - Tagung Werkstoffprüfung 2014 - Fortschritte in der Werkstoffprüfung für Forschung und Praxis CY - Bad Neuenahr, Germany DA - 03.12.2015 PY - 2015 SN - 978-3-514-00816-8 SP - 175 EP - 180 PB - Verlag Stahleisen CY - Düsseldorf AN - OPUS4-35176 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kunz, C. A1 - Büttner, T.N. A1 - Naumann, B. A1 - Boehm, A.V. A1 - Gnecco, E. A1 - Bonse, Jörn A1 - Neumann, C. A1 - Turchanin, A. A1 - Müller, F.A. A1 - Gräf, S. T1 - Large-area fabrication of low- and high-spatial-frequency laser-induced periodic surface structures on carbon fibers N2 - The formation and properties of laser-induced periodic surface structures (LIPSS) were investigated on carbon fibers under irradiation of fs-laser pulses characterized by a pulse duration τ = 300 fs and a laser wavelength λ = 1025 nm. The LIPSS were fabricated in an air environment at normal incidence with different values of the laser peak fluence and number of pulses per spot. The morphology of the generated structures was characterized by using scanning electron microscopy, atomic force microscopy and Fast-Fourier transform analyses. Moreover, the material structure and the surface chemistry of the carbon fibers before and after laser irradiation was analyzed by micro Raman spectroscopy and X-ray photoelectron spectroscopy. Large areas in the cm2 range of carbon fiber arrangements were successfully processed with homogenously distributed high- and low-spatial frequency LIPSS. Beyond those distinct nanostructures, hybrid structures were realized for the very first time by a superposition of both types of LIPSS in a two-step process. The findings facilitate the fabrication of tailored LIPSS-based surface structures on carbon fibers that could be of particular interest for e.g. fiber reinforced polymers and concretes. KW - Fs-Laser KW - Laser-induced periodic surface structures (LIPSS) KW - Carbon fibers KW - Large area structuring PY - 2018 UR - https://www.sciencedirect.com/science/article/pii/S0008622318302781 DO - https://doi.org/10.1016/j.carbon.2018.03.035 SN - 0008-6223 SN - 1873-3891 VL - 133 SP - 176 EP - 185 PB - Elsevier Ltd. AN - OPUS4-44625 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Strangfeld, Christoph A1 - Müller-Vahl, H. F. A1 - Nayeri, C. N. A1 - Paschereit, C. O. A1 - Greenblatt, D. T1 - Airfoil synchronous surging and pitching N2 - Combined surging and pitching of an airfoil at the identical frequency (i.e. synchronously), at four different phase differences, was investigated theoretically and experimentally. The most general unsteady theoretical formulation was adopted to calculate the lift coefficient, and then extended to explicitly compute the unsteady bound vortex sheet. This was used for comparison with experiments and facilitated the computation of both Joukowsky and impulsive-pressure lift contributions. Experiments were performed using a symmetric 18 % thick airfoil in an unsteady wind tunnel at an average Reynolds number of 3.0*10^5 , with a free-stream oscillation amplitude of 51 %, an angle-of-attack range of 2° +- 2° and a reduced frequency of 0.097. In general, excellent correspondence was observed between theory and experiment, representing the first direct experimental validation of the general theory. It was shown, both theoretically and experimentally, that the lift coefficient was not accurately represented by independent superposition of surging and pitching effects, due to variations in the instantaneous effective reduced frequency not accounted for during pure pitching. Deviations from theory, observed at angle-of-attack phase leads of 90° and 180°, were attributed to bursting of separation bubbles during the early stages of the acceleration phase. The largest deviations occurred when the impulsive-pressure lift contribution was small relative to the Joukowsky contribution, because the latter was most affected by bubble bursting. Bubble bursting resulted in large form-drag oscillations that occurred at identical phase angles within the oscillation cycle, irrespective of the phase difference between surging and pitching, as well as in the absence of pitching. KW - Unsteady aerodynamics KW - Dynamic stall KW - Separation bubble KW - Bubble bursting PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630068 DO - https://doi.org/10.1017/jfm.2025.220 SN - 1469-7645 VL - 1009 SP - 1 EP - 33 PB - Cambridge University Press (CUP) AN - OPUS4-63006 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seah, M.P. A1 - Spencer, S.J. A1 - Bensebaa, F. A1 - Vickridge, I. A1 - Danzebrink, H. A1 - Krumrey, M. A1 - Gross, Thomas A1 - Österle, Werner A1 - Wendler, E. A1 - Rheinländer, B. A1 - Azuma, Y. A1 - Kojima, I. A1 - Suzuki, N. A1 - Suzuki, M. A1 - Tanuma, S. A1 - Moon, D.W. A1 - Lee, H.J. A1 - Cho, H.M. A1 - Chen, H.Y. A1 - Wee, A. T. S. A1 - Osipowicz, T. A1 - Pan, J.S. A1 - Jordaan, W.A. A1 - Hauert, R. A1 - Klotz, U. A1 - van der Marel, C. A1 - Verheijen, M. A1 - Tamminga, Y. A1 - Jeynes, C. A1 - Bailey, P. A1 - Biswas, S. A1 - Falke, U. A1 - Nguyen, N.V. A1 - Chandler-Horowitz, D. A1 - Ehrstein, J.R. A1 - Muller, D. A1 - Dura, J.A. T1 - Critical review of the current status of thickness measurements for ultrathin SiO2 on Si - Part V: Results of a CCQM pilot study N2 - Results are reported from a pilot study under the Consultative Committee for Amount of Substance (CCQM) to compare measurements of and resolve any relevant measurement issues in, the amount of thermal SiO2 oxide on (100) and (111) orientation Si wafer substrates in the thickness range 1.5 - 8 nm. As a result of the invitation to participate in this activity, 45 sets of measurements have been made in different laboratories using 10 analytical methods: medium-energy ion scattering spectrometry (MEIS), nuclear reaction analysis (NRA), RBS, elastic backscattering spectrometry (EBS), XPS, SIMS, ellipsometry, grazing-incidence x-ray reflectrometry (GIXRR), neutron reflectometry and transmission electron microscopy (TEM). The measurements are made on separate sets of 10 carefully prepared samples, all of which have been characterised by a combination of ellipsometry and XPS using carefully established reference conditions and reference parameters. The results have been assessed against the National Physical Laboratory (NPL) data and all show excellent linearity. The remaining data sets correlate with the NPL data with average root-mean-square scatters of 0.15 nm, half being better than 0.1 nm and a few at or better than 0.05 nm. Each set of data allows a relative scaling constant and a zero thickness offset to be determined. Each method has an inherent zero thickness offset between 0 nm and 1 nm and it is these offsets, measured here for the first time, that have caused many problems in the past. There are three basic classes of offset: water and carbonadeous contamination equivalent to ~1 nm as seen by ellipsometry; adsorbed oxygen mainly from water at an equivalent thickness of 0.5 nm as seen by MEIS, NRA, RBS and possibly GIXRR; and no offset as seen by XPS using the Si 2p peaks. Each technique has a different uncertainty for the scaling constant and consistent results have been achieved. X-Ray photoelectron spectroscopy has large uncertainties for the scaling constant but a high precision and, critically, if used correctly, has zero offset. Thus, a combination of XPS and the other methods allows the XPS scaling constant to be determined with low uncertainty, traceable via the other methods. XPS laboratories returning results early were invited to test a new reference procedure. All showed very significant improvements. The reference attenuation lengths thus need scaling by 0.986 ± 0.009 (at an expansion factor of 2) deduced from the data for the other methods. Several other methods have small offsets and, to the extent that these can be shown to be constant or measurable, then these methods will also show low uncertainty. Recommendations are provided for parameters for XPS, MEIS, RBS and NRA to improve their accuracy. KW - Calibration KW - Ellipsometry KW - GIXRR KW - Interlaboratory study KW - MEIS KW - Neutron reflectometry KW - NRA KW - RBS KW - Silicon dioxide KW - SIMS KW - XPS PY - 2004 DO - https://doi.org/10.1002/sia.1909 SN - 0142-2421 SN - 1096-9918 VL - 36 IS - 9 SP - 1269 EP - 1303 PB - Wiley CY - Chichester AN - OPUS4-5549 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gross, U. A1 - Müller-Mai, C. A1 - Knabe, C. A1 - Berger, Georg A1 - Ploska, Ute A1 - Gildenhaar, Renate ED - Vincenzini, P. T1 - Animal experiments with biomaterials for direct bone contact displaying higher or lower solubility in comparison to TCP and HA products T2 - 10th International Ceramics Congress ; 3rd Forum on New Materials ; 10th CIMTEC 2002 CY - Florence, Italy DA - 2002-07-14 PY - 2004 SP - 369 EP - 376 PB - Techna CY - Faenza AN - OPUS4-3500 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Seah, M.P. A1 - Spencer, S.J. A1 - Bensebaa, F. A1 - Vickridge, I. A1 - Danzebrink, H. A1 - Krumrey, M. A1 - Gross, Thomas A1 - Österle, Werner A1 - Wendler, E. A1 - Rheinländer, B. A1 - Azuma, Y. A1 - Kojima, I. A1 - Suzuki, N. A1 - Suzuki, M. A1 - Tanuma, S. A1 - Moon, D.W. A1 - Lee, H.J. A1 - Cho, H.M. A1 - Chen, H.Y. A1 - Wee, A. T. S. A1 - Osipowicz, T. A1 - Pan, J.S. A1 - Jordaan, W.A. A1 - Hauert, R. A1 - Klotz, U. A1 - van der Marel, C. A1 - Verheijen, M. A1 - Tamminga, Y. A1 - Jeynes, C. A1 - Bailey, P. A1 - Biswas, S. A1 - Falke, U. A1 - Nguyen, N.V. A1 - Chandler-Horowitz, D. A1 - Ehrstein, J.R. A1 - Muller, D. A1 - Dura, J.A. T1 - Ultra-thin SiO2 on Si, Part V: Results of a CCQM Pilot Study of Thickness Measurements KW - SiO2 KW - Thin films KW - Thickness KW - XPS KW - Ellipsometry KW - TEM PY - 2003 SN - 1473-2734 SP - 57 pages AN - OPUS4-4118 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Miccoli, Lorenzo A1 - Perrone, C. A1 - Müller, Urs A1 - Gardei, André A1 - Ziegert, C. T1 - Comparison of mechanical behavior of different earth masonry typologies in cultural heritage N2 - The paper has been developed in the framework of a larger EC‐research program called NIKER, in which BAM and other seventeen research partners from the Mediterrean area are jointly involved. It aims to develop and validate innovative materials and technologies for the systemic improvement of the seismic behavior of Cultural Heritage assets. The death tolls brought about by recent catastrophes in developing countries where many inhabitants lived in earthen dwellings (Gujarat, India 2001, Bam, Iran 2003 and Concepción, Chile 2010 Earthquakes, Tamil Nadu 2004 Tsunami) have brought about research studies aimed at improving earth construction in terms of strength, seismic resistance and speed of construction. In comparison to the recent advances in research on stone and brick masonry, knowledge on the material properties and failure mechanisms of earthen Building construction is limited and scattered. The research presented here by aims making a comparison of mechanical behaviour between different earth masonry material typologies, consisting of earth block masonry, rammed earth and cob. T2 - WCCE-ECCE-TCCE Joint conference 2 - Seismic protection of cultural heritage CY - Antalya, Turkey DA - 31.10.2011 KW - Earth masonry KW - Material test KW - Cultural heritage KW - Seismic resistance PY - 2011 SN - 978-605-01-0188-1 SP - 25 EP - 36 AN - OPUS4-24836 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Miccoli, Lorenzo A1 - Perrone, C. A1 - Müller, Urs A1 - Gardei, André A1 - Ziegert, C. ED - Drochytka, R. ED - Bohus, S. T1 - Structural performances of earthen building materials. A comparison between different typologies N2 - Traditional construction techniques utilizing earthen materials are often seen as inferior compared to modern ways of building. Structural earthen elements are perceived as vulnerable towards environmental influences (moisture, frost) and in particular towards the load scenarios during earthquakes. In comparison to the recent advances in research on stone and brick masonry, knowledge on the structural performance of earthen building construction is limited and scattered. Consequently the confidence in the performance of these earthen buildings constructed in the traditional techniques during earthquakes is fairly low. The research presented here aims to make a comparison of mechanical behavior between different earth masonry material typologies, consisting of earth block masonry, rammed earth and cob. The paper has been developed in the framework of a larger research program called NIKER. BAM and other seventeen research partners from the Mediterrean area are jointly involved to develop and validate innovative materials and technologies for the systemic improvement of the seismic behavior of Cultural Heritage assets T2 - 2nd WTA - Internaitonal PhD Symposium - Building materials and buidling technology to preserve the built heritage CY - Brno, Czech Republic DA - 06.10.2011 KW - Earth masonry KW - Material test KW - Mechanical behavior KW - Cultural heritage PY - 2011 SN - 978-3-937066-21-9 SN - 0947-6830 N1 - Serientitel: WTA-Schriftenreihe – Series title: WTA-Schriftenreihe VL - 2 / Part 2 IS - 36 SP - 86 EP - 94 PB - WTA Publications AN - OPUS4-24928 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gross, U. A1 - Müller-Mai, C. A1 - Voigt, C. A1 - Berger, Georg A1 - Spitzer, Andrea T1 - In Vivo Tests of a Highly Porous Rapidly Resorbable Dicalcium Potassium Sodium Phosphate Glass-Ceramics N2 - Glass-ceramics containing Ca2KNa(PO4)2 as the main crystalline phase have a solubility which is 8 times higher than that of alpha-tricalcium phosphate ceramics. When using these compositions in drug delivery systems, especially in bone, it is necessary to create a material with a high open porosity. A Ca2KNa(PO4)2-based glass-ceramic was prepared from a borosilicate glass melt. The processed material includes minor amounts of boron which are low enough for medical application. Tissue response was studied using an animal model. Particles were implanted in rabbit femurs. Bone and soft tissue development occurred at the particle interfaces. In general, most particles were enclosed in the network of trabecular bone. The advantages of using a biomaterial with high porosity (pore size of 1-3 micron), together with rapid biodegradation, bioactivity and biocompatibility, despite traces of boron, were shown. 4 refs. T2 - 14th International Symposium on Ceramics in Medicine CY - Palm Springs, CA, USA DA - 2001-11-14 PY - 2002 DO - https://doi.org/10.4028/www.scientific.net/KEM.218-220.307 SN - 1013-9826 VL - 218-220 SP - 307 EP - 310 PB - Trans Tech Publ. CY - Aedermannsdorf AN - OPUS4-1935 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gross, U. A1 - Müller-Mai, C. A1 - Voigt, C. A1 - Berger, Georg A1 - Spitzer, Andrea T1 - In vivo test of a high porous rapidly resorbable dicalcium potassium sodium phosphate glass-ceramics T2 - 14th International Symposium on Ceramics in Medicine ; Annual meeting of the International Society for Ceramics in Medicine 2001 CY - Palm Springs, CA, USA DA - 2001-11-14 PY - 2002 SN - 1013-9826 VL - 218-220 SP - 307 EP - 310 PB - Trans Tech Publ. CY - Aedermannsdorf AN - OPUS4-1893 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gross, U. A1 - Müller-Mai, C. A1 - Knabe, C. A1 - Berger, Georg A1 - Ploska, Ute A1 - Gildenhaar, Renate ED - Vincenzini, P. T1 - Animal experiments with biomaterials for direct bone contact which possess in comparison to TCP and HA products higher or lower solubility T2 - 10th International Ceramics Congress ; 3rd Forum on New Materials ; 10th CIMTEC 2002 CY - Florence, Italy DA - 2002-07-14 PY - 2003 PB - Techna CY - Faenza AN - OPUS4-1894 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kunz, C. A1 - Bonse, Jörn A1 - Spaltmann, Dirk A1 - Neumann, C. A1 - Turchanin, A. A1 - Bartolomé, J. F. A1 - Müller, F. A. A1 - Gräf, S. T1 - Tribological performance of metal-reinforced ceramic composites selectively structured with femtosecond laser-induced periodic surface structures N2 - The impact of femtosecond (fs) laser-induced periodic surface structures (LIPSS) on tribological properties was investigated for metal-reinforced ceramic composites (Al2O3-ZrO2-Nb). For this purpose, the metallic niobium (Nb) phase was selectively structured with LIPSS in an air environment with different values of the fs-laser peak fluence by near-infrared fs-laser radiation (λ = 1025 nm, τ = 300 fs, frep = 1 kHz), taking advantage of the different light absorption behavior of ceramic and metal. The tribological performance was evaluated by reciprocating sliding tests in a ball-on-disc configuration using Ringer's solution as lubricant. The surfaces were characterized before and after laser irradiation by optical microscopy, scanning electron microscopy, atomic force microscopy, X-ray photoelectron spectroscopy, energy dispersive X-ray spectroscopy and by measuring the contact angle with Ringer's solution. The LIPSS formation resulted in an increased wetting of the surface with the lubricant. Moreover, the selectively structured composite surfaces revealed a coefficient of friction significantly reduced by a factor of ~3 when compared to the non-irradiated surface. Furthermore, the formation of a laser-induced oxidation layer was detected with NbO as the most prominent oxidation state. Selectively structured composites with outstanding mechanical properties and enhanced tribological performance are of particular interest for biomedical applications. KW - Laser-induced periodic surface structures (LIPSS) KW - Femtosecond laser ablation KW - Ceramic matrix composites KW - Tribology PY - 2020 DO - https://doi.org/10.1016/j.apsusc.2019.143917 SN - 0169-4332 SN - 1873-5584 VL - 499 IS - 1 SP - 143917 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-49255 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller-Vahl, H. F. A1 - Strangfeld, Christoph A1 - Nayeri, C. N. A1 - Paschereit, C. O. A1 - Greenblatt, D. T1 - Dynamic Stall Under Combined Pitching and Surging N2 - Dynamic stall often occurs under conditions of simultaneous unsteady pitching and surging (e.g., rotorcraft and wind turbines), butmanymodels employ a dimensionless time base that implicitly assumes that surging is superimposed, in a quasi-steady manner, on dynamic pitching. An unsteady wind tunnel was used to examine this assumption, where a technique was developed to quantify the unsteady effects of surging on a pitching NACA 0018 airfoil. The technique involved performing multiple harmonic pitching experiments under nominally steady freestream conditions that bracketed a corresponding 50% surging amplitude (1.25 ⋅ 105 ≤ Re ≤ 3.75 ⋅ 105). By interpolating these data, unsteady-pitching/quasi-steady-surging data sets were constructed and compared with de facto synchronous pitch and surging experiments, thereby isolating the unsteady effects of surging on a pitching airfoil. Both large and small poststall maximum angles of attack (αs + 5° and αs + 15°) were considered at multiple pitch-surge phase differences. During deep dynamic stall (αs � 15°), with large-scale separation, surging was seen to have a secondary effect on the unsteady aerodynamics. However, at small poststall maximum angles of attack (αs + 5°), either light or deep dynamic stall behavior was observed depending upon the pitch-surge phase difference. This was attributed to Reynolds number history effects, exemplified by boundary-layer transition, and thus it can be referred to as “transitional” dynamic stall. KW - Dynamic stall KW - Angle of attack oscillations KW - Free stream velocity osciallations PY - 2020 DO - https://doi.org/10.2514/1.J059153 VL - 58 IS - 12 SP - 5134 EP - 5145 PB - American Institute of Aeronautics and Astronautics AN - OPUS4-51037 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Thieme-Hack, M. A1 - Berghaus, U. A1 - Brümmer, F. A1 - Elsner, U. A1 - Färber, C. A1 - Frank, D. A1 - Illgas, M. A1 - Kalbe, Ute A1 - Kathage, J. A1 - Leers, A. A1 - Müller, B. A1 - Röger-Göpfert, C. A1 - Russland, H.-J. A1 - Schnabel, B. A1 - Schneider, O. A1 - Schockmann, D. A1 - Schomakers, H. A1 - Schwalbe, D. A1 - Stegemann, D. A1 - van den Berg, T. A1 - Kramps, S. T1 - Fachbericht Kunststoffsportböden - Nachhaltige Kunststoffbelagsauswahl für Sportfreianlagen N2 - Kunststoff- und Kunststoffrasenflächen kommt bei intensiv genutzten Flächen als Allwetterbeläge eine große Bedeutung zu. Sie leisten einen wichtigen Beitrag zur Absicherung eines ganzjähriger Sportangebote. Gerade Kunststoffrasen ist aber in den letzten Jahren häufig in die Kritik geraten, insbesondere durch gefährliche Inhaltsstoffe und andere negative Einflüsse auf die Umwelt. Dies hat bei Bauherren zu einer Verunsicherung geführt und Fragen aufgeworfen, die erst teilweise beantwortet sind. Die Diskussionen rund um diesen Allwetterbelag haben bereits dazu geführt, dass von Seiten der Industrie viel verändert wurde und neue innovative Lösungen gefunden werden. Der Fachbericht stellt eine Handreichung für Fachleute und interessierte Laien dar, um mehr Klarheit besonders hinsichtlich der Umweltanforderungen zu erzielen. KW - Kunststoffsportbeläge KW - Kunstrasen KW - Umweltverträglichkeit KW - Schadstofftransfer KW - Mikroplastik PY - 2022 UR - https://shop.fll.de/de/fachbericht-kunststoffsportboeden-broschuere.html SP - 1 EP - 70 PB - Forschungsgesellschaft Landschaftsentwicklung Landschaftsbau (FLL) CY - Bonn AN - OPUS4-54390 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wisniewski, W. A1 - Thieme, C. A1 - Müller, Ralf A1 - Reinsch, Stefan A1 - Groß-Barsnick, S.-M. A1 - Rüssel, C. T1 - Oriented surface nucleation and crystal growth in a 18BaO·22CaO·60SiO2 mol% glass used for SOFC seals N2 - A glass of the composition 37BaO·16CaO·47SiO2 wt% produced on an industrial scale is crystallized at 970 °C for times ranging from 15 min to 2 h. The crystallization at the immediate surface as well as the crystal growth into the bulk are analyzed using scanning electron microscopy (SEM) including energy dispersive X-ray spectroscopy (EDXS) and electron backscatter diffraction (EBSD) as well as X-ray diffraction in the Θ–2Θ setup (XRD). The immediate surface shows the oriented nucleation of walstromite as well as the formation of wollastonite and an unknown phase of the composition BaCaSi3O8. All three phases also grow into the bulk where walstromite ultimately dominates the kinetic selection and grows throughout the bulk due to a lack of bulk nucleation. Walstromite shows systematic orientation changes as well as twinning during growth. A critical analysis of the XRD-patterns acquired from various crystallized samples indicates that their evaluation is problematic and that phases detected by XRD in this system should be verified by another method such as EDXS. KW - Glass KW - Surface nucleation KW - Orientation KW - EBSD PY - 2018 DO - https://doi.org/10.1039/c7ce02008b VL - 20 IS - 6 SP - 787 EP - 795 PB - Royal Society of Chemistry AN - OPUS4-44405 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Berger, Georg A1 - Müller-Mai, C. A1 - Voigt, C. A1 - Gross, U. ED - Wise, D. L. T1 - Bone development and bone structure depend on surface roughness and structure of metalic implants KW - Bone Development KW - Surface Structure PY - 2000 SN - 0-8247-0318-9 SP - 457 EP - 481 PB - Dekker CY - New York AN - OPUS4-878 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Strangfeld, Christoph A1 - Müller-Vahl, H. A1 - Nayeri, C. N. A1 - Paschereit, C. O. A1 - Greenblatt, D. T1 - Airfoil in a high amplitude oscillating stream N2 - A combined theoretical and experimental investigation was carried out with the objective of evaluating theoretical predictions relating to a two-dimensional airfoil subjected to high amplitude harmonic oscillation of the free stream at constant angle of attack. Current theoretical approaches were reviewed and extended for the purposes of quantifying the bound, unsteady vortex sheet strength along the airfoil chord. This resulted in a closed form solution that is valid for arbitrary reduced frequencies and amplitudes. In the experiments, the bound, unsteady vortex strength of a symmetric 18 % thick airfoil at low angles of attack was measured in a dedicated unsteady wind tunnel at maximum reduced frequencies of 0.1 and at velocity oscillations less than or equal to 50 %. With the boundary layer tripped near the leading edge and mid-chord, the phase and amplitude variations of the lift coefficient corresponded reasonably well with the theory. Near the maximum lift coefficient overshoot, the data exhibited an additional high-frequency oscillation. Comparisons of the measured and predicted vortex sheet indicated the existence of a recirculation bubble upstream of the trailing edge which sheds into the wake and modifies the Kutta condition. Without boundary layer tripping, a mid-chord bubble is present that strengthens during flow deceleration and its shedding produces a dramatically different effect. Instead of a lift coefficient overshoot, as per the theory, the data exhibit a significant undershoot. This undershoot is also accompanied by high-frequency oscillations that are characterized by the bubble shedding. In summary, the location of bubble and ist subsequent shedding play decisive roles in the resulting temporal aerodynamic loads. KW - vortex shedding KW - aerodynamics KW - general fluid mechanics PY - 2016 DO - https://doi.org/10.1017/jfm.2016.126 SN - 0022-1120 VL - 2016 IS - 793 SP - 79 EP - 108 AN - OPUS4-35594 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Urs A1 - Ziegert, C. A1 - Kaiser, C. A1 - Röhlen, U. T1 - Eigenschaften industrieller Lehmbauprodukte für den Mauerwerksbau und Verhalten von Lehmsteinmauerwerk N2 - Der Beitrag gibt einen Überblick über die Eigenschaften industriell hergestellter Bauprodukte aus Lehm für den Mauerwerksbau. Die Qualität der industriellen Fertigung dieser Produktgruppe hat inzwischen einen Stand erreicht, der vergleichbar mit dem anderer Bauprodukte ist. Lehm-Putzmörtel gibt es als Universalputze für ein- oder mehrlagige Anwendung oder in Form von Unter-, Ober- oder Feinputzen. Lehmsteine werden in verschiedenen Größen und mit Lochung angeboten. Die mechanischen Eigenschaften verschiedener Lehmsteinsorten sind geprägt durch Druckfestigkeiten bis 11 N/mm2, mit üblichen Werten bei 2 bis 5 N/mm2. Ein kritischer Punkt ist die Abhängigkeit der Festigkeitseigenschaften der Lehmsteine von der Materialfeuchte. Die vorliegenden Untersuchungen haben jedoch gezeigt, dass in einem Luftfeuchtebereich von 40 bis 70 % RLF die Druckfestigkeit von Lehmsteinen verhältnismäßig konstant ist. Mauerwerk, errichtet mit Lehmsteinen und Lehm-Mauermörtel, zeigt ähnliche Druckfestigkeiten und E-Module wie Mauerwerk, das mit Porenbetonsteinen errichtet wurde. Infolge einer geringeren Haftscherfestigkeit zwischen Lehmmörtel und Lehmstein ist die Schubfestigkeit von Lehmsteinmauerwerk vergleichsweise niedrig.------------------------------------------------------------------------------------------------------------------------------------- Properties of industrially produced earthen building products for masonry and behaviour of earth block masonry. The contribution gives an overview of the properties of industrially produced earthen building products for masonry. In the meantime the quality of the industrial production of this group of building materials reached a level similar to that of other products for construction. Earth plasters exist as plasters for universal, one or multi layer applications or as lower, upper or finish plasters. Earth blocks are provided in different sizes and with different perforations. The mechanical properties of different earth block types are signified by compressive strength of up to 11 N/mm2 but are typically in a range between 2 and 5 N/mm2. A critical point is the correlation of the strength of earthen materials with their moisture content. Results from earth blocks showed that in a relative humidity window between 40 and 70 % rh the compressive strength of earth blocks is fairly constant. Masonry made from earth block and earth mortar exhibited compressive strength and elastic modules similar to masonry made with aerated autoclaved concrete blocks. The shear strength of earth block masonry, however, is fairly low, due to the weak bond between earth block and earth mortar. PY - 2012 DO - https://doi.org/10.1002/dama.201200527 SN - 1432-3427 SN - 1437-1022 VL - 16 IS - 1 SP - 17 EP - 28 PB - Ernst CY - Berlin AN - OPUS4-27744 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Miccoli, Lorenzo A1 - Perrone, C. A1 - Fontana, Patrick A1 - Müller, Urs A1 - Ziegert, C. T1 - Charakterisierung und Modellierung der mechanischen Eigenschaften von Lehmsteinmauerwerk / Mechanical characterization and modelling of earth block masonry N2 - Das Wissen über die Materialeigenschaften und die Versagensmechanismen bei Lehmbaustoffen ist begrenzt und lückenhaft. Im Rahmen des EU-Projekts NIKER (www.niker.eu) wurden deshalb die mechanischen Eigenschaften von Bauteilen aus Lehm unter statischer Druck- und Schubbeanspruchung bestimmt. Ziel der Untersuchungen war es, grundlegende Daten zum Verformungs- und Versagensverhalten von Lehmbauteilen zu erhalten und dieses mit einem numerischen Modell zu beschreiben. Die Versuchsergebnisse belegten das spröde Verhalten von Lehmsteinmauerwerk bei uniaxialer Druckbelastung und zeigten, dass das Versagen von Lehmsteinmauerwerk infolge Schubbelastung nach Erstrissbildung in Mörtelfugen und Lehmsteinen durch Gleiten der Lehmsteine entlang der Mörtelfugen erfolgt. Die numerische Makromodellierung erbrachte zwar befriedigende Resultate hinsichtlich des Spannungs-Dehnungs-Verhaltens, jedoch konnte bei der simulierten Rissbildung keine Übereinstimmung mit den in den Versuchen beobachteten Rissbildern erzielt werden. Bei Lehmsteinmauerwerk ist also eine wesentlich aufwendigere Mikromodellierung notwendig, um das Versagensverhalten korrekt beschreiben zu können.-------------------------------------------------------------------------------------------------------------- Knowledge of the material properties and failure mechanisms of earthen materials is limited and scattered. Within the framework of the NIKER project (www.niker.eu) funded by EC, the mechanical properties of earthen material elements were therefore determined under static compression and shear loads. The aim was to obtain fundamental data on deformation behaviour and failure mechanisms of earthen material structural elements and to describe them by means of a numerical model. The test results confirmed the brittle behaviour of earth block masonry under monoaxial compressive load and showed that the failure of earth block masonry under shear load occurs by sliding of the earth blocks along the mortar joints after initial cracking in mortar joints and earth block. Numerical macro modelling showed satisfying results with regard to stress-strain behaviour, but the simulated crack pattern was not consistent with experimental observations. In the case of earth block masonry, it is thus necessary to use micro modelling approaches in order to correctly predict the failure process at local level. KW - Lehmstein Mauerwerk KW - Druckversuche KW - Schubversuche KW - F.E.M. Modellierung PY - 2012 DO - https://doi.org/10.1002/dama.201200555 SN - 1432-3427 SN - 1437-1022 N1 - Sprachen: Deutsch/Englisch - Languages: German/English VL - 16 IS - 6 SP - 279 EP - 292 PB - Ernst CY - Berlin AN - OPUS4-27589 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, U. A1 - Miccoli, Lorenzo A1 - Perrone, C. A1 - Ziegert, C. T1 - Vergleich und Modellierung der mechanischen Eigenschaften von Bauteilen aus Lehmsteinmauerwerk, Wellerlehm und Stampflehm N2 - Im Rahmen des EU-Projekts NIKER (www.niker.eu) wurden die mechanischen Eigenschaften von Bauteilen aus Lehmsteinmauerwerk, Wellerlehm und Stampflehm bestimmt. Ziel war es grundlegende Daten zum Festigkeits- und Verformungsverhalten von Lehmbauteilen zu erhalten. Die Daten wurden als Eingangsgrößen zur Modellierung des Bauteilverhaltens verwendet. Die Ergebnisse zeigten, dass unter Druckbeanspruchung Lehmsteinmauerwerk und Stampflehm ein ähnliches Verformungsverhalten aufweisen. Dagegen zeigte Wellerlehm zwar deutlich niedrigere Druckfestigkeiten aber das Nachbruchverhalten war im Vergleich zu den beiden anderen Bauweisen wesentlich deutlicher ausgeprägt. Erste Ergebnisse zur Makromodellierung des Festigkeits- und Verformungsverhaltens sowohl im elastischen als auch plastischen Bereich zeigen eine gute Übereinstimmung mit den experimentell ermittelten Daten. Die Modellierung auch von komplizierteren Lehmbauteilformen unter statischer Last scheint somit in absehbarer Zeit möglich. T2 - Lehm 2012 - 6. Internationale Fachtagung für Lehmbau CY - Weimar, Germany DA - 05.10.2012 KW - Stampflehm KW - Lehmstein KW - Mauerwerk KW - Wellerlehm KW - Mechanische Eigenschaften PY - 2012 SN - 978-3-00-039649-6 IS - Session C SP - 320 EP - 331 AN - OPUS4-26936 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Miccoli, Lorenzo A1 - Müller, Urs A1 - Perrone, C. A1 - Ziegert, C. T1 - Earth block masonry, rammed earth and cob: earthen components from different construction techniques and their structural performance N2 - Both in developed and developing countries, modern building materials tend to be preferred to traditional earthen construction. Reasons include low durability, inadequate performance under seismic loading and, in developing countries, a wish to replace what is perceived as 'poor' with what is perceived as 'rich'. In an age when building permissions and construction standards are a must, particularly in seismic areas, even when an owner is willing to build in earth, construction approval needs to be granted: we rely on values and standards to build, but the necessary data on material properties and structural performance of earthen building techniques is scarce if compared to the abundance of data for other materials (clay brick masonry, concrete, steel) available to the engineer. At the same time, traditional builders' skills, knowledge and confidence in earthen building techniques are decreasing if not disappearing. A wallette testing campaign was thus carried out with the aim of filling this knowledge gap. Prior to the wallette campaign, material properties, including composition and physical-mechanical parameters, were determined. Compression and diagonal compression (shear) tests were then performed, and a basic analysis of the mechanical behaviour of structural elements built in cob is provided in relation to earth block (adobe) masonry and rammed earth elements. Cob, shown to have low compressive resistance, has a relatively ductile post-peak behaviour if compared to earth block masonry specimens which, as expected, show a marked brittle behaviour. In terms of shear strength, cob performs relatively well in view of its low compressive strength. The study is part of our work within the framework of the ongoing project NIKER funded by the European Commission dealing with improving the structural performance of Cultural Heritage assets in order to limit earthquake hazards. T2 - Terra 2012 - 11th International conference on the study and conservation of earthen architecture heritage CY - Lima, Peru DA - 22.04.2012 KW - Earth block KW - Rammed earth KW - Cob KW - Mechanical properties KW - Earthen architecture KW - Earth block masonry PY - 2012 SN - 978-9972-2885-5-5 IS - Theme 6 - t6_066 SP - 1 EP - 10 AN - OPUS4-30380 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kennedy, D.C. A1 - Orts-Gil, G. A1 - Lai, C.-H. A1 - Müller, Larissa A1 - Haase, A. A1 - Luch, A. A1 - Seeberger, P. H. T1 - Carbohydrate functionalization of silver nanoparticles modulates cytotoxicity and cellular uptake N2 - Background Increasing use of silver nanoparticles (Ag-NPs) in various products is resulting in a greater likelihood of human exposure to these materials. Nevertheless, little is still known about the influence of carbohydrates on the toxicity and cellular uptake of nanoparticles. Methods Ag-NPs functionalized with three different monosaccharides and ethylene glycol were synthesized and characterised. Oxidative stress and toxicity was evaluated by protein carbonylation and MTT assay, respectively. Cellular uptake was evaluated by confocal microscopy and ICP-MS. Results Ag-NPs coated with galactose and mannose were considerably less toxic to neuronal-like cells and hepatocytes compared to particles functionalized by glucose, ethylene glycol or citrate. Toxicity correlated to oxidative stress but not to cellular uptake. Conclusions Carbohydrate coating on silver nanoparticles modulates both oxidative stress and cellular uptake, but mainly the first has an impact on toxicity. These findings provide new perspectives on modulating the bioactivity of Ag-NPs by using carbohydrates. KW - Silver KW - Nanoparticles KW - Carbohydrates KW - Nanotoxicology KW - Bio-Interfaces PY - 2014 UR - http://www.jnanobiotechnology.com/content/12/1/59 DO - https://doi.org/10.1186/s12951-014-0059-z SN - 1477-3155 VL - 12 IS - 59 SP - 1 EP - 8 PB - BioMed Central CY - London AN - OPUS4-34345 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Scharlach, C. A1 - Müller, Larissa A1 - Wagner, S. A1 - Kobayashi, Y. A1 - Kratz, H. A1 - Ebert, M. A1 - Jakubowski, Norbert A1 - Schellenberger, E. T1 - LA-ICP-MS allows quantitative microscopy of europium-doped iron oxide nanoparticles and is a possible alternative to ambiguous Prussian blue iron staining N2 - The development of iron oxide nanoparticles for biomedical applications requires accurate histological evaluation. Prussian blue iron staining is widely used but may be unspecific when tissues contain substantial endogenous iron. Here we tested whether microscopy by laser ablation coupled to inductively coupled plasma mass spectrometry (LA-ICP-MS) is sensitive enough to analyze accumulation of very small iron oxide particles (VSOP) doped with europium in tissue sections. KW - Atherosclerotic plaques KW - LA-ICP-MS microscopy KW - Quantification KW - Element microscopy KW - Histology PY - 2016 DO - https://doi.org/10.1166/jbn.2016.2230 SN - 1550-7033 SN - 1550-7041 VL - 12 IS - 5 SP - 1001 EP - 1010 AN - OPUS4-36189 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Kauss, N. A1 - Halle, T. T1 - Einfluss der Wärmebehandlung auf Mikrostruktur und Korrosionsverhalten kohlenstoffhaltiger nichtrostender Stähle N2 - Das Korrosionsverhalten von kohlenstoffhaltigen martensitischen nichtrostenden Stählen variiert in Abhängigkeit der Wärmebehandlung (WB) und der damit eingestellten Mikrostruktur deutlich stärker als bei kohlenstoffarmen ferritischen und austenitischen nichtrostenden Stählen. Bei erhöhtem Kohlenstoffgehalt bestimmt die diffusionsgesteuerte Bildung und Auflösung von Chromkarbiden die Verteilung von Chrom und Kohlenstoff im Gefüge. Bisher lag der Fokus von Forschungsarbeiten zum Einfluss der WB auf dem Anlassen im allgemein bekannten Sensibilisierungsbereich dieser Werkstoffgruppe zwischen 200 °C und 700 °C und der dort auftretenden Chromverarmung. Mit der gezielten WB des X46Cr13 (1.4034) wird gezeigt, dass Temperatur und Dauer beim Austenitisieren sowie die anschließende Abkühlung beim Härten das Korrosionsverhalten schon vor dem Anlassen signifikant beeinflussen. Auf der Basis von thermodynamischen Berechnungen wurden definierte WB ausgewählt, um gezielt unterschiedliche Volumengehalte von Chromkarbiden im Gefüge und somit auch unterschiedliche Chrom bzw. Kohlenstoffgehalte im Mischkristall zu erzeugen. Anschließend wurden die resultierenden Gefügezustände hinsichtlich Chromkarbidanteil und Härte verglichen und das Korrosionsverhalten mit der elektrochemisch potentiodynamischen Reaktivierung (EPR) sowie durch einen Schnelltest mit der KorroPad-Prüfung untersucht. Dabei konnte ein direkter Zusammenhang zwischen WB, Mikrostrukturänderungen und Korrosionsverhalten festgestellt werden. Mit steigender Austenitisierungstemperatur wird der Anteil an Chromkarbiden reduziert und der Kohlenstoff- und Chromgehalt der Matrix erhöht, bis eine vollständige Auflösung der Chromkarbide gegeben und die chemische Nennzusammensetzung der Legierung im Mischkristall erreicht ist. In der direkten Folge wird die Ausbildung der für nichtrostende Stähle charakteristischen Passivschicht erleichtert und das Lochkorrosionsverhalten verbessert. Die Abkühlrate hat neben den Austenitisierungsparametern ebenfalls einen großen Einfluss auf das Korrosionsverhalten. So führt eine langsame Abkühlung an Luft zu einer Chromverarmung im Gefüge, die eine deutlich erhöhte Lochkorrosionsanfälligkeit zur Folge hat. In Abhängigkeit der WB von kohlenstoffhaltigen nichtrostenden Stählen können Mikrostruktur, Härte und Korrosionsbeständigkeit in einem weiten Bereich variieren. T2 - 20. Werkstofftechnisches Kolloquium CY - Chemnitz, Germany DA - 14.03.2018 KW - Nichtrostender Stahl KW - Wärmebehandlung KW - EPR KW - KorroPad KW - Korrosionsbeständigkeit KW - ThermoCalc KW - Sensibilisierung KW - Martensitischer nichtrostender Stahl KW - Passivschicht PY - 2018 SN - 978-3-00-058901-0 SN - 1439-1597 VL - 72 SP - 711 EP - 720 PB - Eigenverlag CY - Chemnitz AN - OPUS4-44559 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, C. T1 - Wärmebehandlung und Korrosionsbeständigkeit druckaufgestickter nichtrostender Stähle N2 - Gefüge und Eigenschaften nichtrostender Stählen werden maßgeblich von ihrer chemischen Zusammensetzung und der Wärmebehandlung bestimmt. Eine spezielle Werkstoffgruppe der austenitischen nichtrostenden Stähle enthält ca. 19 Gew.-% Mangan und 0,8 Gew.-% Stickstoff, um das austenitische Gefüge ohne das Legieren mit Nickel sicherzustellen. Die herausragenden mechanischen Eigenschaften dieser Werkstoffe (Rm von 900 2.000 MPa, A5 > 50 %, Av > 350 J) werden nach der Wärmebehandlung (Lösungsglühen und Abschrecken) durch gezielte Kaltverfestigung eingestellt. Das Lösungsglühen beseitigt vorhandene Kaltverfestigung und unerwünschte Ausscheidungsphasen (Cr2N, M23C6 und Sigma-Phase) und bewirkt die homogene Verteilung der Legierungselemente (insbesondere Stickstoff) im Austenit. Dies ist zur Erzielung der Korrosionsbeständigkeit von entscheidender Bedeutung. Im Poster werden systematische Untersuchungen zur Korrosionsbeständigkeit dieser vielversprechenden Werkstoffklasse vorgestellt und die Interaktion zwischen Legierungszusammensetzung, Wärmebehandlung, Gefüge und Korrosionsbeständigkeit dargestellt. Die vom Gefüge bedingten Veränderungen der Korrosionsbeständigkeit werden durch verschiedene Methoden ermittelt und interpretiert. T2 - GfKORR-Jahrestagung 2017 CY - Frankfurt a. M., Germany DA - 07.11.2017 KW - Wärmebehandlung KW - Korrosion KW - Nichtrostender Stahl KW - EPR KW - KorroPad KW - Sensibilisierung KW - Stickstoff KW - ThermoCalc PY - 2017 AN - OPUS4-42833 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Kauss, N. A1 - Müller, C. A1 - Halle, T. T1 - Heat treatment and corrosion resistance of cutlery N2 - Hardness and pitting corrosion resistance are the major quality criteria of cutlery. Both are achieved by the heat treatment (austenitization, quenching and tempering) of the normally used martensitic stainless steels. The established quality control method regarding the pitting corrosion resistance is an alternating immersion test in 1 % NaCl solution at 60 °C according to DIN EN ISO 8442. This standard test shows a high deviation, which limits any optimization of the heat treatment process. New approaches for corrosion testing of martensitic stainless-steels were developed and used in the last years to connect the weak pitting corrosion resistance of martensitic stainless-steels with the phenomenon of chromium depletion. The tempering temperatures used in the industrial heat treatment of cutlery are too low to explain the appearance of chromium depletion. For this reason, a systematic investigation of three heat treatment parameters (austenitization time, cooling speed and tempering temperature) were performed on the martensitic stainless-steels X50CrMoV15 (1.4116) to detect their contribution to chromium depletion. The electrochemical potentiodynamic reactivation (EPR), which is very sensitive to any change of the microstructure, was used to quantify the degree of chromium depletion. The KorroPad indicator-test was applied to correlate low pitting corrosion resistance to the presence of chromium depletion. The results of all investigations allow conclusions about the very small process window, which is necessary to achieve cutlery with high pitting corrosion resistance. T2 - EUROCORR 2018 CY - Krakow, Poland DA - 09.09.2018 KW - Corrosion KW - KorroPad KW - Stainless steel KW - Corrosion resistance KW - Heat treatment KW - EPR KW - Pitting corrosion KW - Martensitic stainless steels KW - REM PY - 2018 AN - OPUS4-45952 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Roßberg, S. A1 - Pensel, P. A1 - Halle, T. A1 - Burkert, A. T1 - Precipitation behavior and corrosion resistance of nickel-free, high-nitrogen austenitic stainless steels N2 - Nickel-free, nitrogen alloyed austenitic stainless-steels, with about 19 wt.-% Mn and 0,8 wt. % N, are an interesting alternative to classic CrNi austenitic stainless steels due to their superior mechanical properties (Rm > 900 MPa, A5 > 50 %, Av > 350 J) in the solution annealed condition. The formation of chromium-rich nitrides during suboptimal heat treatment, processing or application leads to an inhomogeneous distribution of alloying elements in the microstructure, which reduces the corrosion resistance. Consequently, an accurate knowledge of the sensitization behavior is indispensable for the use of nickel-free, high-nitrogen austenitic stainless steels. The relationship between artificial aging, phase formation and corrosion resistance was investigated on the alloys X8CrMnN18-19 (1.3815) and X8CrMnMoN18-19-2 (1.4456), both alloyed with 0,8 wt.-% Nitrogen, in the present work. The microstructural evolution was studied by LM and SEM while the corrosion resistance was characterized with the electrochemical potentiodynamic reactivation (EPR) and the KorroPad indicator-test. Both alloys showed increased corrosion susceptibility within critical aging parameters. Finally, a sensitization diagram was described successfully for both alloys showing the positive effect of molybdenum. T2 - EUROCORR 2018 CY - Krakow, Poland DA - 09.09.2018 KW - Corrosion KW - KorroPad KW - Stainless steel KW - Corrosion resistance KW - Heat treatment KW - ThermoCalc KW - Pitting corrosion KW - Nitrogen PY - 2018 AN - OPUS4-45954 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Baumann, O. A1 - Müller, C. T1 - Influence of the post-weld surface treatment on the corrosion resistance of the duplex stainless steel 1.4062 N2 - The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polishing or blasting depending on the requested corrosion resistance. Blasted surfaces are often used in the industrial practice due to the faster and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the results of different corrosion tests (KorroPad-testing and pitting potentials). T2 - Materials Science and Engineering 2018 (MSE) CY - Darmstadt, Germany DA - 26.09.2018 KW - Duplexstahl KW - Korrosion KW - Nichtrostender Stahl KW - Schweißen KW - Oberflächenbearbeitung KW - Strahlen KW - KorroPad PY - 2018 AN - OPUS4-46090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wolff, M. A1 - Wonneberger, R. A1 - Freiberg, K.E. A1 - Hertwig, Andreas A1 - Bonse, Jörn A1 - Giebeler, L. A1 - Koitzsch, A. A1 - Kunz, C. A1 - Weber, H. A1 - Hufenbach, J.K. A1 - Müller, F.A. A1 - Gräf, S. T1 - Formation of laser-induced periodic surface structures on Zr-based bulk metallic glasses with different chemical composition N2 - Bulk metallic glasses (BMG) are amorphous metal alloys known for their unique physical and mechanical properties. In the present study, the formation of femtosecond (fs) laser-induced periodic surface structures (LIPSS) on the Zr-based BMGs Zr46Cu46Al8, Zr61Cu25Al12Ti2, Zr52.5Cu17.9Al10Ni14.6Ti5 (Vit105) and Zr57Cu15.4Al10Ni12.6Nb5 (Vit106) was investigated as a function of their different chemical composition. For this purpose, LIPSS were generated on the sample surfaces in an air environment by fs-laser irradiation (λ = 1025 nm, τ = 300 fs, frep = 100 kHz). The surface topography was characterized by scanning electron microscopy and atomic force microscopy. Moreover, the impact of LIPSS formation on the structure and chemical surface composition was analyzed before and after fs-laser irradiation by X-ray diffraction and X-ray photoelectron spectroscopy as well as by transmission electron microscopy in combination with energy dispersive X-ray spectroscopy. Despite the different chemical composition of the investigated BMGs, the fs-laser irradiation resulted in almost similar properties of the generated LIPSS patterns. In the case of Zr61Cu25Al12Ti2, Vit105 and Vit106, the surface analysis revealed the preservation of the amorphous state of the materials during fs-laser irradiation. The study demonstrated the presence of a native oxide layer on all pristine BMGs. In addition, fs-laser irradiation results in the formation of laser-induced oxide layers of larger thickness consisting of an amorphous ZrAlCu-oxide. The precise laser-structuring of BMG surfaces on the nanoscale provides a versatile alternative to thermoplastic forming of BMG surfaces and is of particular interest for the engineering of functional material surfaces. KW - Bulk metallic glasses KW - Femtosecond laser KW - Laser-induced periodic surface structures (LIPSS) KW - Chemical analysis KW - Oxidation PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-581799 DO - https://doi.org/10.1016/j.surfin.2023.103305 SN - 2468-0230 VL - 42 SP - 1 EP - 11 PB - Elsevier B.V. AN - OPUS4-58179 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hösl, Simone A1 - Neumann, B. A1 - Techritz, Sandra A1 - Linscheid, M. A1 - Theuring, F. A1 - Scheler, C. A1 - Jakubowski, Norbert A1 - Müller, Larissa T1 - Development of a calibration and standardization procedure for LA-ICP-MS using a conventional ink-jet printer for quantification of proteins in electro- and western-blot assays N2 - We developed new procedures for internal standardization and calibration to be used for laser ablation inductively coupled plasma mass spectrometry (LA-ICP-MS) for elemental micro mapping imaging of biological samples like Western blot membranes and tissue sections. These procedures are based on printing of metal spiked inks onto the top of thin layer samples for simultaneous internal standardization and calibration of LA-ICP-MS. In the case of internal standardization the ink is spiked with indium as an internal standard and homogenously printed over the entire membrane (size 56 cm2) prior to LA-ICP-MS detection, a standard deviation (RSD) value of 2% was achieved. In the second approach the metal content of lanthanide tagged proteins and antibodies after biological work flows was quantified by LA-ICP-MS on nitro-cellulose membranes. In this case the inks spiked with varying metals were printed with different densities on the same nitrocellulose membranes in well-defined squares to produce matrix-matched calibration standards. For validation and calibration the ink squares were excised and the specific metal content was measured by liquid ICP-MS after solubilization of the membrane slice. For the printed calibration standard limits of detection (LOD) of <4 fmol for different metals and relative process standard deviations of 1–2% only were determined via LA-ICP-MS. PY - 2014 DO - https://doi.org/10.1039/c4ja00060a SN - 0267-9477 SN - 1364-5544 VL - 29 IS - 7 SP - 1282 EP - 1291 PB - Royal Society of Chemistry CY - London AN - OPUS4-31171 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Philipp A1 - Miccoli, Lorenzo A1 - Fontana, Patrick A1 - Ziegert, C. T1 - Development of partial safety factors for earth block masonry N2 - The main aim of the research was the development of a first valid database for material parameters of earth block masonry (EBM) with particular regard to statistical characteristics. A solid database is needed for the determination of the materials partial safety factor. Therefore, compressive strength tests were carried out with two types of earth blocks and two types of prefabricated earth mortar. The evaluation has shown that the mean variation of the compressive strength was remarkably less than expected, which indicates high quality standards of the components earth block and mortar with regard to industrial production. Using the reliability method, a partial safety factor for EBM subjected to compression was determined on the basis of these test results. The findings have shown that a common calculation method for EBM based on partial safety factors following the valid masonry construction standard is feasible. KW - Partial safety factor KW - Earth block masonry (EBM) KW - Reliability KW - Compressive strength PY - 2017 DO - https://doi.org/10.1617/s11527-016-0902-9 SN - 1871-6873 SN - 1359-5997 VL - 50 IS - 1 SP - 1 EP - 14 PB - Springer AN - OPUS4-38937 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Baumann, O. A1 - Modersohn, W. A1 - Halle, T. T1 - Influence of the post-weld surface treatment on the corrosion resistance of the duplex stainless steel 1.4062 N2 - The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polished or blasting depending on the application and the requested corrosion resistance. Blasted surfaces are often used in industrial practice due to the easier and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the different performed corrosion tests (potential measurement, KorroPad-test and pitting potential) on welding seams with different surface treatments. T2 - 19. Werkstofftechnisches Kolloquium Chemnitz CY - Chemnitz, Germany DA - 16.03.2017 KW - Corrosion resistance KW - Duplex stainless steel KW - Influence PY - 2017 SN - 978-3-00-055705-7 SN - 1439-1597 VL - 61 SP - 172 EP - 180 PB - Schriftreihe Werkstoffe und werkstofftechnische Anwendungen CY - Chemnitz AN - OPUS4-40168 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, C. T1 - Einfluss der Abkühlgeschwindigkeit auf die Korrosionsbeständigkeit martensitischer nichtrostender Stähle N2 - Martensitische nichtrostende Stähle werden in verschiedenen technischen Bereichen eingesetzt, bei denen eine optimale Kombination aus hoher mechanischer Festigkeit und guter korrosiver Beständigkeit gefordert wird. Beide Eigenschaften werden in der Industrie primär durch die Wärmebehandlung gesteuert. Die Korrosionseigenschaften sind dabei stark von der diffusionsbedingten Bildung und Auflösung von Chromkarbiden abhängig. In vergangenen wissenschaftlichen Arbeiten konnte nachgewiesen werden, dass die Abkühlgeschwindigkeit nach dem Austenitisieren einen großen Einfluss auf die Bildung solcher Karbide hat. Der Einfluss der Abkühlgeschwindigkeit auf die Lochkorrosionsbeständigkeit wurde an den Stählen 1.4108 und 1.4116 systematisch untersucht. Mit Hilfe des Stirnabschreckversuches wurde dabei die Abkühlgeschwindigkeiten variiert und anschließend die Veränderung von Gefüge, Lochkorrosionsbeständigkeit und Härte untersucht. Als Ergebnis konnten kritische Abkühlgeschwindigkeiten ermittelt werden, bei denen eine kritische Verringerung der Korrosionsbeständigkeit einsetzt. T2 - GfKORR-Jahrestagung 'Duplex-Stähle – Nische oder Zukunft ?' CY - Frankfurt/M., Germany DA - 15.11.2016 KW - Korrosionsbeständigkeit KW - Martensitische nichtrostende Stähle KW - Abkühlgeschwindigkeit PY - 2016 AN - OPUS4-39473 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Müller, P. A1 - Fontana, Patrick A1 - Miccoli, Lorenzo A1 - Ziegert, C. ED - Jäger, W. T1 - Versuchsgestützte Kalibrierung von Teilsicherheitsbeiwerten im Lehmmauerwerksbau - Empfehlungen für die Erarbeitung eines Bemessungskonzepts N2 - Ziel der vorliegenden Untersuchung war es zu überprüfen, inwiefern eine Bemessungsvorschrift auf Basis von Teilsicherheitsbeiwerten im Lehmmauerwerksbau möglich ist. Bemessungsvorschriften im konventionellen Mauerwerksbau und im Lehmmauerwerksbau waren aufgrund des prinzipiell gleichen Tragverhaltens stets eng miteinander verknüpft. Die im Rahmen dieser Arbeit durchgeführten Druckversuche an Lehmmauermörtel, Lehmsteinen und Lehmmauerwerk konnten zeigen, dass die Streuungen der Festigkeiten von Lehmbaustoffen aufgrund der industriellen Herstellung sehr gering sind. Es konnte festgestellt werden, dass eine Bemessung auf Grundlage des semiprobabilistischen Bemessungskonzeptes in Anlehnung an den konventionellen Mauerwerksbau möglich ist. Neben einem ersten Vorschlag des Teilsicherheitsbeiwertes für den Lastzustand Druck werden Vorschläge für Prüfvorschriften im Lehmbau beziehungsweise deren Modifikation unterbreitet und künftige Forschungsschwerpunkte herausgearbeitet. KW - Baustoffe KW - Lehmmauerwerk KW - Lehmbau KW - Teilsicherheitsbeiwert KW - Zuverlässigkeit KW - Druckfestigkeit KW - Prüfverfahren KW - Bemessung KW - Normung KW - Feuchteabhängige Festigkeit PY - 2017 SN - 978-3-433-03161-2 SP - 181 EP - 194 PB - Ernst & Sohn CY - Berlin AN - OPUS4-39628 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Miccoli, Lorenzo A1 - Fontana, Patrick A1 - Ziegert, C. A1 - Müller, P. ED - Modena, C. ED - da Porto, F. ED - Valluzzi, M. R. T1 - Calibration of partial safety factors for earth block masonry under compression loading N2 - The goal of the present study is to assess the feasibility to develop a first reliable database of materials parameters for Earth Block Masonry (EBM). The database is crucial when defining the materials safety factors. In the first part an experimental campaign of compressive tests were carried out on two types of earth block and two types of earth mortar. The results showed that the mean variation of the compressive strength was remarkably less than expected. This low variation is related to a production with high quality standards of the materials employed. In the second part a partial safety factor for EBM under uniaxial compression was determined through the reliability method. The results proved the reliability of a common calculation method for EBM based on partial safety factors following the current standards. T2 - IB2MAC 2016 - 16th International Brick and Block Masonry Conference CY - Padua, Italy DA - 26.06.2016 KW - earth block masonry KW - partial safety factors KW - uniaxial compression test PY - 2016 SN - 978-1-138-02999-6 SP - 857 EP - 864 PB - CRC Press Taylor & Francis Group CY - London, UK AN - OPUS4-37145 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Meyer, A. A1 - Halle, T. ED - Lampke, T. ED - Wagner, G. ED - Wagner, M. F.-X. T1 - Einfluss von Stickstoff auf Mikrostruktur und Korrosionsverhalten martensitischer nichtrostender Stähle N2 - Die Korrosionsbeständigkeit martensitischer nichtrostender Stähle (MNS) wird wesentlich von der chemischen Zusammensetzung und dem Wärmebehandlungszustand beeinflusst. Beides bestimmt die Verteilung der Legierungselemente im Gefüge und die daraus resultierenden Werkstoffeigenschaften. Das Legieren mit Stickstoff bewirkt im Allgemeinen eine Verbesserung der Lochkorrosionsbeständigkeit von nichtrostenden Stählen. Bei martensitischen nichtrostenden Stählen ist dieser Effekt nicht nur auf den Stickstoffgehalt selbst zurückzuführen, sondern auch auf den gleichzeitig verringerten Kohlenstoffgehalt, der ebenfalls das Ergebnis der Wärmebehandlung beeinflusst. In dieser Arbeit wird der Einfluss von Stickstoff auf die Korrosionsbeständigkeit in Bezug zum Härtungsprozess von MNS dargestellt. Dazu wird vergleichend der Effekt von Austenitisierungsdauer, -temperatur und Abkühlgeschwindigkeit auf Gefüge, Härte und Korrosionsbeständigkeit der MNS X50CrMoV15 und X30CrMoN15 1 untersucht. Die Abkühlgeschwindigkeit wurde mit dem Stirnabschreckversuch gezielt variiert, um den Einfluss von Abkühlgeschwindigkeiten von > 100 K/s bis 1 K/s zu charakterisieren. Die Veränderungen der Korrosionsbeständigkeit werden durch die elektrochemisch potentiodynamische Reaktivierung (EPR) und durch die Bestimmung kritischer Lochkorrosionspotentiale dokumentiert. Neben diesem experimentellen Ansatz werden auch die Ergebnisse von thermodynamischen Berechnungen mit der Software Thermocalc vorgestellt und abschließend auch zur Interpretation des Einflusses von Stickstoff auf die Korrosionsbeständigkeit martensitischer nichtrostender Stähle genutzt. T2 - 18. Werkstofftechnisches Kolloquium der TU Chemnitz CY - Chemnitz, Germany DA - 10.03.2016 KW - Korrosionsbeständigkeit KW - Corrosion resistance KW - Wärmebehandlung KW - Heat treatment KW - Nichtrostende Stähle KW - Stainless steels KW - Thermocalc KW - Thermocalc PY - 2016 SN - 978-3-00-052212-3 SN - 1439-1597 VL - 59 SP - 325 EP - 336 PB - TU Chemnitz, Fakultät für Maschinenbau, Institut für Werkstoffwissenschaft und Werkstofftechnik CY - Chemnitz AN - OPUS4-37263 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Halle, T. T1 - Einfluss der Schweißnaht-Nachbehandlung auf die Korrosionsbeständigkeit vom Duplexstahl 1.4062 N2 - Der Duplexstahl 1.4062 (X2CrNi22-2) hat sich im Bauwesen als Werkstoffalternative zu den nichtrostenden Austeniten etabliert. Die Korrosionsbeständigkeit von Schweißverbindungen wird, neben dem Grundwerkstoff, dem Schweißzusatzwerkstoff und dem Schweißverfahren, auch sehr stark von der Schweißnaht-Nachbehandlung beeinflusst. Je nach zukünftigem Anwendungsbereich, geforderter Optik und Korrosionsbeständigkeit wird die Schweißnaht geschliffen, gebeizt, elektropoliert oder gestrahlt, um die beim Schweißen entstehenden An-lauffarben zu entfernen. Gestrahlte Oberflächen sind in der industriellen Praxis häufig anzutreffen, da sie deutlich schneller und kostengünstiger herzustellen sind als geschliffene, gebeizte oder polierte Oberflächen. Das Strahlen mit Korund ist außerdem effektiver als das Strahlen mit Glasperlen. In den letzten Jahren wurden korrosionsanfällige Oberflächen bei nichtrostenden Stählen beobachtet, wenn diese mit Korund geschliffen wurden. Daher wird nun auch beim Strahlen kritisch hinterfragt, ob die eingesetzten Strahlmittel die Korrosionsbeständigkeit beeinflussen. Diese Fragestellung wird beantwortet, indem geschliffene, gebeizte, polierte und mit verschiedenen Strahlmitteln gestrahlte Schweißverbindungen vom Duplexstahl 1.4062 im Vergleich zu gleichartig behandeltem Walzmaterial untersucht werden. Die Ergebnisse der Korrosionsuntersuchungen werden vorgestellt und mit den rasterelektronenmikroskopischen Untersuchungen der gestrahlten Oberflächen korreliert. T2 - 16. Sommerkurs Werkstoffe und Fügen CY - Magdeburg, Germany DA - 08.09.2017 KW - Duplexstahl KW - Nichtrostender Stahl KW - Schweißen KW - Oberflächenbearbeitung KW - Strahlen KW - Korrosion PY - 2017 SN - 978-3-944722-58-0 DO - https://doi.org/10.24352/UB.OVGU-2017-75 SP - 63 EP - 70 AN - OPUS4-41888 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Kauss, N. A1 - Müller, C. A1 - Halle, T. T1 - Einfluss der Abkühlgeschwindigkeit auf die Neigung zur Chromverarmung martensitischer nichtrostender Stähle N2 - Die Legierungselemente (Chrom und Kohlenstoff) und die Wärmebehandlung bestimmen Korrosionsbeständigkeit und Härte martensitischer nichtrostender Stähle. Verschiedene wissenschaftliche Arbeiten haben bereits gezeigt, dass die Korrosionsbeständigkeit sehr stark vom Anteil an Chromkarbiden im Gefüge bestimmt wird. Der kombinierte Einfluss von Kohlenstoffgehalt und der Abkühlgeschwindigkeit beim Härten wurde mit Fokus auf die Korrosionsbeständigkeit bisher nur unzureichend untersucht. Die Literatur liefert außerdem gegensätzliche Aussagen über den Einfluss der Abkühlgeschwindigkeit, was möglicherweise auf unterschiedliche Kohlenstoffgehalte zurückgeführt werden kann. In dieser Arbeit wird daher systematisch untersucht, ab welcher Abkühlgeschwindigkeit es bei den Werkstoffen X20Cr13 und X46Cr13 zu Karbidbildung und Chromverarmung kommt. Die Variation der Abkühlgeschwindigkeit erfolgte für die industriell relevante Härtetemperatur von 1050 °C mit dem Stirnabschreckversuch. In Abhängigkeit von der Abkühlgeschwindigkeit wurden an den Stirnabschreckproben Gefüge, Härte und Korrosionsbeständigkeit (EPR, kritische Lochkorrosionspotentiale) untersucht und die Ergebnisse mit thermodynamischen Berechnungen (ThermoCalc) korreliert. Aus den Ergebnissen wird abgeleitet, unter welchen Bedingungen die Abkühlgeschwindigkeit die Korrosionsbeständigkeit beeinflusst. T2 - 16. Sommerkurs Werkstoffe und Fügen CY - Magdeburg, Germany DA - 08.09.2017 KW - Wärmebehandlung KW - Korrosion KW - Chromverarmung KW - EPR KW - Martensitischer nichtrostender Stahl KW - ThermoCalc KW - Lochkorrosion PY - 2017 SN - 978-3-944722-58-0 DO - https://doi.org/10.24352/UB.OVGU-2017-75 SP - 71 EP - 78 AN - OPUS4-41889 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Halle, T. T1 - Sensibilisierungsverhalten vom stickstofflegierten, austenitischen, nichtrostenden Stahl 1.4456 N2 - Austenitische nichtrostende Stähle kommen seit vielen Jahren in den verschiedensten industriellen Zweigen zum Einsatz (Pharma-, Medizin- und Lebensmittelindustrie, Bauwesen, Energie- und Antriebstechnik). Druckaufgestickte nichtrostende Austenite mit ca. 19 Gew.-% Mangan und 0,8 Gew.-% Stickstoff, sind als nickelfreie Variante seit einigen Jahren großtechnisch auf dem Markt verfügbar. In diesen Stählen wird die austenitische Matrix ohne die Legierungszugabe von Nickel sichergestellt, während gleichzeitig die korrosive Beständigkeit und die mechanischen Eigenschaften verbessert werden. Wie bei allen nichtrostenden Stählen beeinflussen die chemische Zusammensetzung und die Wärmebehandlung entscheidend das Gefüge und die Eigenschaften. Durch Lösungsglühen, Abschrecken und gezieltes Kaltverfestigen können bei diesen Stählen hervorragende mechanische Kennwerte erreicht werden (Rm von 900 MPa bis 2.000 MPa, A5 > 50 %, Av > 350 J). In der Regel dient das Lösungsglühen der Beseitigung unerwünschter Ausscheidungsphasen (Cr2N, M23C6 und Sigma-Phase) und der homogenen Verteilung der Legierungselemente im Austenit, was auch die Voraussetzung für eine hohe Korrosionsbeständigkeit darstellt. Wird die homogene Verteilung der Legierungselemente (Cr, Mo und N) durch suboptimale Wärmebehandlungs-, Verarbeitungs- oder Einsatzbedingungen beeinträchtigt, kann die korrosive Beständigkeit nicht auf Dauer gewährleistet werden. Daher ist die genaue Kenntnis vom Sensibilisierungsverhalten dieser hochstickstofflegierten Stähle unerlässlich. Am stickstofflegierten Werkstoff 1.4456 (X8CrMnMoN18-18-2) wird das Sensibilisierungsverhalten am lösungsgeglühten Zustand durch die gezielte Variation der Warmauslagerungsparameter untersucht. Dabei wird im Temperaturbereich von 500 °C bis 900 °C die Glühdauer systematisch variiert, um zu ermitteln, wann Ausscheidungen im Gefüge auftreten und ob diese die Korrosionsbeständigkeit beeinträchtigen. Die verschiedenen Sensibilisierungszustände werden mit dem EPR Verfahren, der KorroPad-Prüfung und dem REM vergleichend untersucht. Zur besseren Interpretation der experimentellen Ergebnisse werden auch thermodynamische Berechnungen genutzt, welche die Existenzbereiche der verschiedenen Ausscheidungsphasen vorhersagen. Damit kann die Veränderung der Korrosionsbeständigkeit mit dem Auftreten der verschiedenen Phasen korreliert und die Anwendbarkeit der experimentellen Methoden für stickstofflegierte Stähle nachgewiesen werden. T2 - 16. Sommerkurs Werkstoffe und Fügen CY - Magdeburg, Germany DA - 08.09.2017 KW - Nichtrostender Stahl KW - Wärmebehandlung KW - Korrosion KW - Stickstoff KW - EPR KW - KorroPad KW - ThermoCalc PY - 2017 SN - 978-3-944722-58-0 DO - https://doi.org/10.24352/UB.OVGU-2017-75 SP - 79 EP - 86 AN - OPUS4-41890 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rosemann, Paul A1 - Müller, C. A1 - Kauss, N. A1 - Halle, T. T1 - Einfluss der Wärmebehandlung auf die Korrosionsbeständigkeit von Schneidwaren N2 - Härte und Korrosionsbeständigkeit sind die wichtigsten Qualitätsmerkmale von Schneidwaren. Diese werden nur durch eine optimal durchgeführte Wärmebehandlung des martensitischen nichtrostenden Stahls 1.4116 (X50CrMoV15) erreicht. In der industriellen Fertigung wird die Korrosionsbeständigkeit von Schneidwaren durch Wechseltauchversuche überprüft, die herstellerübergreifend eine große Schwankung der Korrosionsbeständigkeit belegen. In den letzten Jahren wurden neue elektrochemische Untersuchungsmethoden für die Werkstoffgruppe der martensitischen nichtrostenden Stähle entwickelt, welche die geringe Lochkorrosionsbeständigkeit von Schneidwaren auf das Phänomen der Chromverarmung zurückzuführen. Derzeit wird in der wissenschaftlichen und in der industriellen Gemeinschaft der Schritt des Anlassens als Hauptursache der Chromverarmung angesehen. Bei Schneidwaren sind die Anlasstemperaturen aber zu gering, um die auftretende Chromverarmung zu erklären. Aus diesem Grund wurden drei verschiedene Wärmebehandlungsparameter (Austenitisierungsdauer, Abkühlgeschwindigkeit und Anlasstemperatur) systematische untersucht, um deren Beitrag zur Chromverarmung darzustellen. Dazu wird die Untersuchungsmethode der elektrochemisch potentiodynamischen Reaktivierung (EPR) eingesetzt, die sehr sensibel auf Veränderungen im Gefüge reagiert und den Grad an Chromverarmung ermittelt. Außerdem wurde die KorroPad-Prüfung durchgeführt und kritische Lochkorrosionspotentiale ermittelt, um den Zusammenhang zwischen Chromverarmung und Lochkorrosionsbeständigkeit herzustellen. Die Ergebnisse aller Untersuchungen verdeutlichen wie eng das Prozessfenster ist, in dem Schneidwaren mit hoher Korrosionsbeständigkeit hergestellt werden können. T2 - 72. HärtereiKongress CY - Cologne, Germany DA - 26.10.2016 KW - Schneidwaren KW - Wärmebehandlung KW - nichtrostender Stahl KW - martensitisch KW - Lochkorrosion KW - EPR KW - KorroPad PY - 2017 DO - https://doi.org/10.3139/105.110317 SN - 1867-2493 VL - 72 IS - 2 SP - 87 EP - 98 PB - Carl Hanser CY - München AN - OPUS4-41241 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller-Mai, C. T1 - Degradable bone cements for percutaneous augmentation of bone defects T2 - 12th Intern. and Interdisciplinary Symp. Biomaterials and Biomechanics: Fundamentals and Clinical Applications 2010, Univ. Duisburg-Essen CY - Duisburg-Essen, Germany DA - 2010-03-17 PY - 2010 AN - OPUS4-21140 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ziegert, C. A1 - Müller, Urs A1 - Röhlen, U. T1 - Standardization of earth blocks in Germany T2 - 8th International masonry conference 2010 CY - Dresden, Germany DA - 2010-07-04 KW - Standardization KW - Earth blocks KW - Testing procedures PY - 2010 SP - 981 EP - 988 AN - OPUS4-22306 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Ziegert, C. A1 - Dierks, K. A1 - Müller, Urs ED - Jäger, W. T1 - Lehmsteine und Lehmmörtel - Nachhaltige Bauprodukte auf dem Weg zur Stoffnorm N2 - Lehm ist ein seit Jahrtausenden bewährter, weit verbreiteter und heute ein moderner Baustoff. Für vordringliche Bauaufgaben in der Altbausanierung, dem energieeffizienten Neubau sowie dem Bauen in Entwicklungs- und Schwellenländern ist Lehm hervorragend geeignet. Der Baustoff Lehm ist zu einem Material für anspruchsvolle Bauvorhaben geworden. Seine Ästhetik und Ausstrahlung, seine Wirkung für Raumklima und Wohlbefinden werden von vielen Menschen geschätzt. Besonders zukunftsrelevant sind die umweltspezifischen Eigenschaften des Materials, z.B. die unerreichbar günstige Energiebilanz vieler Lehmbaustoffe. Lehmsteine werden im Neubau überwiegend für die Ausmauerung von Holzständerkonstruktionen verwendet (Bild 1). Die Anwendung für tragende Wände ist derzeit noch untergeordnet, gewinnt aber an Bedeutung. In der Altbausanierung und Denkmalpflege wird Lehm als historisch authentischer Baustoff und aufgrund seiner bauphysikalischen Qualitäten vielfältig eingesetzt. KW - Lehm KW - Normung KW - Prüfmethode PY - 2011 SN - 978-3-433-02956-5 DO - https://doi.org/10.1002/9783433600801.ch3 SN - 0170-4958 VL - 36 IS - Kap. III SP - 57 EP - 70 PB - Ernst & Sohn CY - Berlin AN - OPUS4-23328 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Winkler, Helmut A1 - Kessler-Kramer, C. A1 - Müller, Harald S. T1 - Biegezugprüfung mit zyklischer Belastung N2 - Zur genaueren Kenntnis des Einflusses der Ermüdungsbelastung auf das Versagen von Beton wurde das Ermüdungsverhalten von gekerbten Betonbalken in kraft- und verformungsgeregelten Dreipunktbiegezugversuchen untersucht. Für die verformungsgeregelten Versuche wurde eine neuentwickelte Versuchstechnik angewendet, mit der auch unter hochzyklischer Beanspruchung mit Lastspielzahlen von bis zu einer Million Zyklen sowohl der ansteigende als auch der abfallende Ast in einem Kraft-Verformungsdiagramm aufgezeichnet werden kann. KW - Beton KW - Bruchmechanik KW - Ermüdung KW - Schwingung PY - 2001 SN - 0025-5300 VL - 43 IS - 3 SP - 72 EP - 77 PB - Carl Hanser Verlag CY - München AN - OPUS4-12397 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Spange, St. A1 - Müller, H. A1 - Jäger, Christian A1 - Bellmann, C. T1 - Fabrication of carbon/silica hybrid materials using cationic polymerization and the sol-gel process PY - 2002 SN - 1022-1360 SN - 0258-0322 SN - 1521-3900 VL - 177 IS - 1 SP - 111 EP - 124 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-11017 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bahlmann, Stefanie A1 - Rübner, Katrin A1 - Meng, Birgit A1 - Hauer, B. A1 - Klein, H. A1 - Müller, C. A1 - Ruppert, J. A1 - Schäfer, S. A1 - Spanka, G. A1 - Wassing, W. A1 - Zunzer, U. T1 - Potenziale des Sekundärstoffeinsatzes im Betonbau - Teilprojekt B1 KW - Nachhaltigkeit KW - Sekundäre Gesteinskörnung KW - Rezyklierte Gesteinskörnung KW - Betonbrechsand KW - Müllverbrennungsasche PY - 2007 SN - 978-3-410-65772-9 SN - 0171-7197 N1 - Geburtsname von Bahlmann, Stefanie: Ramolla, S. - Birth name of Bahlmann, Stefanie: Ramolla, S. IS - 572 SP - 131 EP - 222 PB - Beuth AN - OPUS4-16361 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schroeder, H. A1 - Müller, Urs A1 - Ziegert, C. T1 - Buildingcodes and standards in earth building - current situation in Germany T2 - Earth USA 2011 - 6th International earthbuidling conference CY - Albuquerque, NM, USA DA - 2011-09-30 KW - Lehmbau KW - Normen KW - Bauprodukte PY - 2011 SN - 978-0-9824660-2-5 SP - 140 EP - 148 AN - OPUS4-25646 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vercoutère, C. A1 - Müller, K. A1 - Chiotti, L. A1 - Nespoulet, R. A1 - Staude, Andreas A1 - Riesemeier, Heinrich A1 - Reiche, I. T1 - Rectangular beads from the final gravettian level of the Abri Pataud: raw material identification and its archaeological implications N2 - The Final Gravettian level (level 2) of the abri Pataud (Dordogne, France) yielded a large assemblage of body ornaments that consists essentially of 85 quite standardized rectangular beads. Some uncertainty remained about the raw material in which these small beads were made: mammoth ivory, reindeer antler or bone? Non-invasive methods were employed in order to determine the raw material. First chemical analyses using microbeam Proton Induced X-ray Emission analysis (microPIXE) did not enable us to conclude definitively. Therefore, synchrotron and laboratory X-ray microtomography (microCT) were applied on eight beads and allowed us to identify ivory for all of them except for one, which shows slightly different morphological features. KW - Abri Pataud KW - Gravettien final KW - Ivoire de mammouth KW - MicroPIXE KW - MicroCT KW - Perles rectangulaires KW - Final Gravettian KW - Mammoth ivory KW - Rectangular beads PY - 2011 SN - 1960-1360 VL - 35 SP - 259 EP - 271 PB - Presses Univ. de Rennes CY - Rennes AN - OPUS4-26250 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -