TY - JOUR A1 - Adamczyk, Burkart A1 - Brenneis, Rudolf A1 - Adam, Christian A1 - Mudersbach, D. T1 - Recovery of chromium from AOD-converter slags N2 - Slags from the production of high-alloyed steel contain both chemically bound chromium (mainly as Cr2O3) in the mineral fraction and elemental chromium in the metallic remainders. Thermochemical post treatment of the slag in an electric arc furnace under reducing conditions enables the nearly complete recovery of the total amount of chromium in form of a metallic alloy. The best results were achieved by resistance melting (submerged electrodes) with addition of a reducing agent into the melt. The efficiencies of the reducing agents carbon, aluminium, silicon (as ferrosilicon) and silicon carbide were investigated and compared. As aluminium is the strongest reducing agent, it is less selective and reduces much more SiO2 than Cr2O3. While SiC shows only low reactivity because of its high thermal resistance, carbon and silicon had the highest reducing potentials: More than 97% of the chemically bound chromium can be recovered by application of these reducing agents. Due to the high temperature required for the reduction of the chromium compounds, the reduction of SiO2 as an undesired side reaction cannot be avoided. However, compared with mechanical procedures that are limited to the recovery of the metallic remainders, the total chromium recovery can be significantly increased by the described reductive melting procedure. KW - Arc furnace KW - By-product KW - Chromium recovery KW - High-alloyed steel KW - Reductive melting KW - Slag treatment KW - Slag KW - Thermochemical treatment PY - 2010 DO - https://doi.org/10.1002/srin.201000193 SN - 1611-3683 SN - 0177-4832 VL - 81 IS - 12 SP - 1078 EP - 1083 PB - Verl. Stahleisen CY - Düsseldorf AN - OPUS4-22898 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Peplinski, Burkhard A1 - Adam, Christian A1 - Adamczyk, Burkart A1 - Müller, Ralf A1 - Michaelis, Matthias A1 - Krahl, T. A1 - Emmerling, Franziska T1 - Nanocrystalline and stacking-disordered beta-cristobalite AlPO4: the now deciphered main constituent of a municipal sewage sludge ash from a full-scale incineration facility N2 - For the first time evidence is provided that a nanocrystalline and stacking-disordered, chemically stabilized β-cristobalite form of AlPO4 occurs in a sewage sludge ash (SSA). This proof is based on a combined X-ray powder diffraction and X-ray fluorescence investigation of an SSA produced at a large-scale fluidized bed incineration facility serving a catching area with a population of 2 million. The structural and chemical characterization was carried out on 'as received' SSA samples as well as on solid residues remaining after leaching this SSA in sodium hydroxide solution. Thus, it was ascertained that the observed nanocrystalline and stacking-disordered cristobalite-like component belongs to the aluminum phosphate component of this SSA, rather than to its silicon dioxide component. In addition, a direct proof is presented that the chemically stabilized β-cristobalite form of AlPO4 does crystallize from X-ray amorphous precursors under conditions that mimic the huge heating rate and short retention time (just seconds at T ≈ 850°C), typical for fluidized bed incinerators. KW - Aluminum phosphate KW - Chemical stabilization of high-temperature forms KW - Cristobalite form KW - Stacking disorder KW - Incinerator ash KW - Sewage sludge ash PY - 2015 DO - https://doi.org/10.1017/S0885715614001213 SN - 0885-7156 VL - 30 IS - Supplement S 1 SP - S31 EP - S35 PB - JCPDS CY - Swarthmore, Pa. AN - OPUS4-33435 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Taube, Mareike Carolin A1 - Adamczyk, Burkart A1 - Adam, Christian A1 - Feldmann, Ines A1 - Ostermann, Markus A1 - Reuter, M. A1 - Stelter, M. T1 - Tantalrecycling aus pyrometallurgischen Rückständen N2 - Gegenstand dieser Arbeit ist die Untersuchung eines bestehenden pyrometallurgischen Prozesses zur Rückgewinnung von Tantal und Niob aus metallurgischen Reststoffen mit vorwiegend niedriger Wertstoffkonzentration. Zur näheren Erforschung der im vorliegenden Stoffsystem ablaufenden Reduktionsprozesse wurden in einem Elektrolichtbogenofen Schmelzversuche im Pilotmaßstab durchgeführt. Als Reduktionsmittel diente Koks, welcher mithilfe einer Argon-gespülten Eisenlanze in die flüssige mineralische Schmelze eingebracht wurde. Während der Reduktionsbehandlung werden Refraktärmetalle wie Tantal und Niob in ihre Carbide überführt und anschließend in der erschmolzenen eisenbasierten Metallphase am Boden des Reaktors angereichert. Neben Tantal und Niob gelangt auch ein Teil des im Einsatzmaterial enthaltenen Titans als unerwünschtes Begleitelement in die Metallphase. Sein Großteil verbleibt jedoch als Oxid in der Schlacke und wird dort hauptsächlich im Mineral Perowskit (CaTiO3) gebunden. Die erstarrten Schlackeproben wurden mit verschiedenen Methoden wie Röntgenfluoreszensanalyse, Röntgenbeugung und Rasterelektronenmikroskopie mit gekoppelter energiedispersiver Röntgenanalyse untersucht, um die Bildung tantalhaltiger Mineralphasen zu verschiedenen Stadien des Reduktionsprozesses zu verfolgen. Die hier gewonnenen Erkenntnisse zeigen, dass weniger die durch das Einblasen von Koks verursachte Reduktionsreaktion, sondern das Absinken der tantalreichen Eisentröpfchen in der flüssigen mineralischen Schmelze, gefolgt von ihrer Anreicherung in die Metallphase, für die Kinetik ausschlaggebend ist. N2 - An existing pyrometallurgical process for tantalum and niobium recovery, mainly from low grade pyrometallurgical residues, was investigated. Melting experiments were carried out in a pilot-scale electric arc furnace to study the material system during the reduction process caused by blowing coke into the liquid mineral melt. During the pyrometallurgical treatment refractory metals such as tantalum and niobium are converted into their carbides and enriched in the molten iron-based metal phase. Titanium is also enriched in the metal phase as an unwanted accompanying element, but most of it remains in oxidic form in the slag and is mainly bound in the mineral perovskite. Cooled down slag samples were analysed using XRF, XRD, SEM and EDX to investigate the formation of mineral phases rich in tantalum during various stages of the reduction process. The results show that the settling of the tantalum-rich iron droplets in the molten slag into the metal phase May play a greater role for the kinetics than the actual reduction reaction caused by blowing in coke. KW - Tantal KW - Recycling KW - Reduktionsprozess KW - Perowskit KW - Elektrolichtbogenofen PY - 2020 SN - 1613-2394 VL - 73 IS - 4 SP - 196 EP - 205 PB - GDMB Verlag GmbH CY - Clausthal-Zellerfeld AN - OPUS4-51064 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Taube, Mareike Carolin A1 - Adam, Christian A1 - Adamczyk, Burkart A1 - Beckmann, T. A1 - Reuter, M. A1 - Stelter, M. ED - Reiser, B. T1 - Recycling von metallurgischen Rückständen - Schmelzversuche zeigen, wie die Tantalrückgewinnung aus Zinnschlacken und weiteren Reststoffen optimiert werden kann N2 - Since the recycling of tantalum bearing post-consumer waste is practically not existent, metallurgical residues are the most important feed for the tantalum recycling. Most tin ores naturally contain significant quantities of refractory metals. During the smelting process in primary tin production these elements are enriched in the slag phase. This slag is a highly valuable raw material for tantalum production due to its considerable concentration of tantalum and its functioning as an additional slag former in further pyrometallurgical treatment. In this paper the first process stage of an existing pyrometallurgical process for tantalum recovery, mainly from low grade pyrometallurgical residues, is discussed. Smelting trials were carried out in a pilot-scale electric arc furnace to analyse the effect of feeding on the activity of carbon as a reducing agent. Therefore, blowing petroleum coke through an iron lance and the manual adding of coke into the melting bath were tested. During the pyrometallurgical treatment elements with a high affinity to carbon were reduced to their carbide form and enriched in the molten iron-based metal phase. The objective of the process was to reduce the oxidic tantalum completely and to enrich it into the metal phase. Furthermore, the transfer of unwanted elements such as titanium into the metal phase was aimed to be avoided. Spoon test specimens were taken from the liquid mineral melt to follow the evolution of the reduction process. The cooled down solidified melting bath was investigated by using the XRD and EDX method to characterise the slag system and to identify relevant mineral phases. N2 - Da das Recycling von tantalhaltigen Post-Consumer-Abfällen praktisch nicht existiert, stellen metallurgische Reststoffe eine äußerst wichtige Rohstoffquelle für das Tantalrecycling dar. Die meisten Zinnerze enthalten von Natur aus erhebliche Mengen an Refraktärmetallen. Diese Elemente werden in den Schlacken der pyrometallurgischen Primärzinngewinnung angereichert. Aufgrund ihrer vergleichsweise hohen Wertstoffkonzentration und ihrer Funktion als zusätzlicher Schlackenbildner stellen diese Schlacken einen wertvollen Rohstoff für die Verhüttung tantalhaltiger Reststoffe dar. In der vorliegenden Arbeit wird ein existierendes Verfahren zur Tantalrückgewinnung diskutiert, dem hauptsächlich pyrometallurgische Rückstände geringer Wertstoffkonzentration als Einsatzstoff dienen. Mit Hilfe des Verfahrens sollte dasoxidisch vorliegende Tantal vollständig reduziert und in der Metallphase angereichert werden. Weiterhin sollte vermieden werden, dass unerwünschte Elemente wie Titan in die Metallphase überführt werden. Ziel der Untersuchung war es, die ablaufenden Reduktionsprozesse besser zu verstehen, um so Ansätze für die Prozessoptimierung identifizieren zu können. KW - Lichtbogenofen KW - Pyrometallurgie KW - Recycling KW - Tantal KW - Zinnschlacke PY - 2020 SN - 0934-3482 VL - 33 SP - 10 EP - 17 PB - Rhombos-Verlag CY - Berlin AN - OPUS4-50656 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Adamczyk, Burkart A1 - Neuhold, S. A1 - Drissen, P. A1 - Algermissen, D. A1 - Presoly, P. A1 - Sedlazeck, K. P. A1 - Schenk, J. A1 - Raith, J. G. A1 - Pomberger, R. A1 - Vollprecht, D. T1 - Tailoring the FeO/SiO2 ratio in electric arc furnace slags to minimize the leaching of Vanadium and Chromium N2 - Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior. KW - Electric arc furnace slags KW - FactSage calculations KW - EAF slags KW - Leaching control mechanisms KW - Melting experiments PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-507748 DO - https://doi.org/10.3390/app10072549 VL - 10 IS - 7 SP - 2549 EP - 2565 AN - OPUS4-50774 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vogel, Christian A1 - Hermann, P. A1 - Kästner, B. A1 - Adamczyk, Burkart A1 - Hoehl, A. A1 - Ulm, G. A1 - Adam, Christian T1 - Air and chlorine gas corrosion of different silicon carbides analyzed by nano-Fourier-transform infrared (nano-FTIR) spectroscopy N2 - The present study shows the potential of high-resolution imaging and nano-Fourier-transform infrared (nano-FTIR) spectroscopy for corrosion science. The protective oxidation layers of different chlorine-gas treated silicon carbides (SiCs) were characterized with these techniques. A nitrified SiC showed the highest resistant strength against chlorine corrosion at 1000 °C compared to the other SiCs. Nano-FTIR spectroscopy with a lateral resolution below 40 nm detected differences in the crystallinity of the bulk-SiC and in the transitional region to the protective layer. Furthermore, high-resolution imaging provides deep insight in the interfacial layer between bulk-SiC and the protective oxidation layer on sub-micrometer scale. KW - Nano-Fourier-transform infrared spectroscopy KW - Scattering-type scanning near-field optical microscopy (s-SNOM) KW - Synchrotron radiation KW - Corrosion KW - Silicon carbide KW - Chlorine PY - 2018 DO - https://doi.org/10.1016/j.corsci.2017.12.002 SN - 0010-938X VL - 131 SP - 324 EP - 329 PB - Elsevier AN - OPUS4-43648 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Peplinski, Burkhard A1 - Adamczyk, Burkart A1 - Formanek, P. A1 - Meyer, Christian A1 - Krüger, O. A1 - Scharf, Holger A1 - Reinsch, Stefan A1 - Ostermann, Markus A1 - Nofz, Marianne A1 - Jäger, Christian A1 - Adam, Christian A1 - Emmerling, Franziska T1 - Nanocrystalline and stacking-disordered beta-cristobalite AlPO4 chemically stabilized at room temperature: synthesis, physical characterization, and X-ray powder diffraction data N2 - This paper reports the first successful synthesis and the structural characterization of nanocrystalline and stacking-disordered β-cristobalite AlPO4 that is chemically stabilized down to room temperature and free of crystalline impurity phases. Several batches of the title compound were synthesized and thoroughly characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy, selected area electron diffraction, energy dispersive X-ray spectroscopy mapping in SEM, solid-state 31P nuclear magnetic resonance (31P-NMR) spectroscopy including the TRAPDOR method, differential thermal analysis (DTA), gas-sorption methods, optical Emission spectroscopy, X-ray fluorescence spectroscopy, and ion chromatography. Parameters that are critical for the synthesis were identified and optimized. The synthesis procedure yields reproducible results and is well documented. A high-quality XRD pattern of the title compound is presented, which was collected with monochromatic copper radiation at room temperature in a wide 2θ range of 5°–100°. KW - Stabilization of high-temperature phase at RT KW - Nanochrystalline AlPO4 KW - Beta-christobalite structure type KW - High-cristobalite form KW - Aluminium phosphate PY - 2017 DO - https://doi.org/10.1017/S0885715617000537 SN - 1945-7413 SN - 0885-7156 VL - 32 IS - S1 SP - S193 EP - S200 PB - JCPDS-ICDD CY - Cambridge AN - OPUS4-42235 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Adam, Christian A1 - Stephan, Dietmar A1 - Meng, Birgit A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Hirsch, Tamino A1 - Manninger, Tanja T1 - Effect of gypsum on the hydration of fused cement clinker from basic oxygen furnace slag N2 - Fused cement clinker can be produced from molten basic oxygen furnace slag (BOFS) by way of a reductive thermochemical treatment. During the thermochemical treatment, oxidic iron is reduced to metallic iron and separated. The resulting low-iron slag has a chemical and mineralogical composition similar to ordinary Portland cement (OPC) clinker. In this study, the hydraulic reactivity of the fused clinker from BOFS with and without gypsum was investigated using isothermal calorimetry, differential scanning calorimetry, in situ X-ray diffraction and powder X-ray diffraction. Furthermore, a synthetic fused clinker without foreign ions and fused clinker produced by a mixture of both materials was studied. The hydraulic reaction of the fused clinker from BOFS was considerably slower than that of OPC. However, the reaction can be accelerated by adding gypsum as a sulfate carrier. Furthermore, the results showed an increased reaction rate with decreasing content of foreign ions such as Fe, P or Mn. KW - General Materials Science KW - Building and Construction PY - 2024 DO - https://doi.org/10.1680/jadcr.23.00070 SN - 0951-7197 SP - 1 EP - 19 PB - Telford AN - OPUS4-59391 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kley, Gerd A1 - Brenneis, Rudolf A1 - Adamczyk, Burkart A1 - Simon, Franz-Georg T1 - Thermochemical treatment - Technologies for recovery and utilisation of materials KW - Thermochemical treatment KW - Materials separation KW - Refractories KW - Stainless steel PY - 2006 SN - 1009-606X VL - 6 IS - 2 SP - 231 EP - 236 CY - Beijing AN - OPUS4-12346 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Simon, Franz-Georg A1 - Adamczyk, Burkart A1 - Kley, Gerd T1 - Refractory materials from waste N2 - The recycling of refractory materials in the chemical, metallurgical and glass industry has only had minor relevance until now because of the high performance required from these materials (stability against corrosion, inert when coming into contact with the glass melt, etc.). Refractory lifetimes are limited because of corrosion at higher temperatures. The best furnace lifetimes has been achieved with chromium oxide and chromium oxide corund refractories. Waste from the production and use of refractory material is generated in three main forms: as residues from cutting and grinding, as refractories which have limited or no contact with glass melts, and as refractories with infiltration of sublimation residues or condensates. The waste material is classified as hazardous waste due to its chromium content. In this study, arc furnace technology was used for thermal treatment of the waste materials to enable recycling of refractory materials. (author abst.) KW - Refractories KW - Thermochemical treatment KW - Chromium oxide KW - Eco-material PY - 2003 UR - https://www.jim.or.jp/journal/e/pdf3/44/07/1251.pdf SN - 1345-9678 SN - 1347-5320 VL - 44 IS - 7 SP - 1251 EP - 1254 PB - Japan Institute of Metals CY - Sendai AN - OPUS4-2832 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Peplinski, Burkhard A1 - Adam, Christian A1 - Reuther, H. A1 - Vogel, Christian A1 - Adamczyk, Burkart A1 - Menzel, Michael A1 - Emmerling, Franziska A1 - Simon, Franz-Georg T1 - First identification of the tridymite form of AlPO4 in municipal sewage sludge ash N2 - Sewage sludge and sewage sludge ashes (SSA) are produced in huge amounts at municipal waste water treatment plants (WWTP) all around the world and have become an issue for many urbanized areas. To deal with this unceasing mass flow in an ecologically and economically responsible way a comprehensive chemical and structural characterization of all types of SSA is needed. X-ray powder diffraction (XRD) is one of the most promising analytical methods for this task. Although, there has been ample chemical evidence showing that many SSA contain aluminium phosphate as a major component up to now no aluminium phosphate or aluminium-rich mixed phosphate phase has been reported to be identified by XRD in a SSA produced at a mono-incineration facility. The outcome of the present com-bined XRD and Mossbauer spectroscopy investigation provides comprehensive evidence closing this gap for the first time. KW - Aluminium phosphate KW - AlPO4 KW - Tridymite KW - Sewage sludge ash KW - Incinerator KW - Ash PY - 2011 DO - https://doi.org/10.1524/zkpr.2011.0067 SN - 0044-2968 VL - 1 SP - 443 EP - 448 PB - Oldenbourg CY - München AN - OPUS4-24297 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Peplinski, Burkhard A1 - Adamczyk, Burkart A1 - Kley, Gerd A1 - Adam, Karin A1 - Emmerling, Franziska A1 - Simon, Franz-Georg T1 - New horizons of the structural characterization of stainless steel slags by X-ray powder diffraction KW - AOD slag KW - Metal recovery KW - Metallurgy KW - Rietveld method KW - Slags KW - Stainless steel slags KW - Quantitative phase analysis (QPA) PY - 2007 SN - 0930-486X VL - 26 SP - 61 EP - 66 PB - Oldenbourg CY - München AN - OPUS4-16666 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -