TY - JOUR A1 - Adamczyk, Burkart A1 - Brenneis, Rudolf A1 - Adam, Christian A1 - Mudersbach, D. T1 - Recovery of chromium from AOD-converter slags N2 - Slags from the production of high-alloyed steel contain both chemically bound chromium (mainly as Cr2O3) in the mineral fraction and elemental chromium in the metallic remainders. Thermochemical post treatment of the slag in an electric arc furnace under reducing conditions enables the nearly complete recovery of the total amount of chromium in form of a metallic alloy. The best results were achieved by resistance melting (submerged electrodes) with addition of a reducing agent into the melt. The efficiencies of the reducing agents carbon, aluminium, silicon (as ferrosilicon) and silicon carbide were investigated and compared. As aluminium is the strongest reducing agent, it is less selective and reduces much more SiO2 than Cr2O3. While SiC shows only low reactivity because of its high thermal resistance, carbon and silicon had the highest reducing potentials: More than 97% of the chemically bound chromium can be recovered by application of these reducing agents. Due to the high temperature required for the reduction of the chromium compounds, the reduction of SiO2 as an undesired side reaction cannot be avoided. However, compared with mechanical procedures that are limited to the recovery of the metallic remainders, the total chromium recovery can be significantly increased by the described reductive melting procedure. KW - Arc furnace KW - By-product KW - Chromium recovery KW - High-alloyed steel KW - Reductive melting KW - Slag treatment KW - Slag KW - Thermochemical treatment PY - 2010 U6 - https://doi.org/10.1002/srin.201000193 SN - 1611-3683 SN - 0177-4832 VL - 81 IS - 12 SP - 1078 EP - 1083 PB - Verl. Stahleisen CY - Düsseldorf AN - OPUS4-22898 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -