TY - JOUR A1 - Adamczyk, Burkart A1 - Neuhold, S. A1 - Drissen, P. A1 - Algermissen, D. A1 - Presoly, P. A1 - Sedlazeck, K. P. A1 - Schenk, J. A1 - Raith, J. G. A1 - Pomberger, R. A1 - Vollprecht, D. T1 - Tailoring the FeO/SiO2 ratio in electric arc furnace slags to minimize the leaching of Vanadium and Chromium N2 - Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior. KW - Electric arc furnace slags KW - FactSage calculations KW - EAF slags KW - Leaching control mechanisms KW - Melting experiments PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-507748 DO - https://doi.org/10.3390/app10072549 VL - 10 IS - 7 SP - 2549 EP - 2565 AN - OPUS4-50774 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Neuhold, S. A1 - Algermissen, D. A1 - Drissen, P. A1 - Adamczyk, Burkart A1 - Presoly, P. A1 - Sedlazeck, K. P. A1 - Schenk, J. A1 - Raith, J. G. A1 - Pomberger, R. A1 - Vollprecht, D. T1 - Tailoring the FeO/SiO2 Ratio in Electric Arc Furnace Slags to Minimize the Leaching of Vanadium and Chromium N2 - Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior. KW - Electric arc furnace (EAF) slags KW - FactSageTM calculations KW - Leaching control mechanisms KW - Melting experiments PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-571517 DO - https://doi.org/10.3390/app10072549 VL - 10 IS - 7 SP - 1 EP - 18 PB - MDPI AN - OPUS4-57151 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wulfert, H. A1 - Keyßner, M. A1 - Ludwig, H.M. A1 - Adamczyk, Burkart A1 - Schiffers, A. T1 - Hochreaktive Zementkomponenten aus Stahlwerksschlacken verbessern Ökologie und Ökonomie N2 - Stahlwerksschlacken besitzen keine ausgeprägte Hydraulizität. Deshalb haben sie bislang als Kompositmaterial im Zement noch keine Verbreitung gefunden. Stattdessen werden LD-Konverter- und Elektroofen-Schlacken insbesondere im Straßenbau in ungebundenen Tragschichten, aber auch in bituminös gebundenen Trag- und Deckschichten eingesetzt. Das Ziel einer zentralen Forschungsaufgabe bei der Loesche GmbH war und ist die Modifizierung dieser Schlacken, um daraus Produkte mit hohen Gebrauchswerteigenschaften zu generieren. Durch die Modifikationen soll hydraulisch hochreaktives Material bei gleichzeitiger Rückgewinnung des Metallinhaltes erzeugt werden. KW - Stahlwerkschlacke KW - LD-Schlacke KW - Zement KW - Lichtbogenofen KW - Alit KW - Hydraulizität PY - 2014 SN - 0340-4803 SN - 0340-479x VL - 133 IS - 12 SP - 45 EP - 50 PB - Verl. Stahleisen CY - Düsseldorf AN - OPUS4-30479 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Simon, Franz-Georg A1 - Adamczyk, Burkart A1 - Kley, Gerd T1 - Refractory materials from waste N2 - The recycling of refractory materials in the chemical, metallurgical and glass industry has only had minor relevance until now because of the high performance required from these materials (stability against corrosion, inert when coming into contact with the glass melt, etc.). Refractory lifetimes are limited because of corrosion at higher temperatures. The best furnace lifetimes has been achieved with chromium oxide and chromium oxide corund refractories. Waste from the production and use of refractory material is generated in three main forms: as residues from cutting and grinding, as refractories which have limited or no contact with glass melts, and as refractories with infiltration of sublimation residues or condensates. The waste material is classified as hazardous waste due to its chromium content. In this study, arc furnace technology was used for thermal treatment of the waste materials to enable recycling of refractory materials. (author abst.) KW - Refractories KW - Thermochemical treatment KW - Chromium oxide KW - Eco-material PY - 2003 UR - https://www.jim.or.jp/journal/e/pdf3/44/07/1251.pdf SN - 1345-9678 SN - 1347-5320 VL - 44 IS - 7 SP - 1251 EP - 1254 PB - Japan Institute of Metals CY - Sendai AN - OPUS4-2832 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kley, Gerd A1 - Brenneis, Rudolf A1 - Adamczyk, Burkart A1 - Simon, Franz-Georg T1 - Thermochemical treatment - Technologies for recovery and utilisation of materials KW - Thermochemical treatment KW - Materials separation KW - Refractories KW - Stainless steel PY - 2006 SN - 1009-606X VL - 6 IS - 2 SP - 231 EP - 236 CY - Beijing AN - OPUS4-12346 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Peplinski, Burkhard A1 - Adamczyk, Burkart A1 - Kley, Gerd A1 - Adam, Karin A1 - Emmerling, Franziska A1 - Simon, Franz-Georg T1 - New horizons of the structural characterization of stainless steel slags by X-ray powder diffraction KW - AOD slag KW - Metal recovery KW - Metallurgy KW - Rietveld method KW - Slags KW - Stainless steel slags KW - Quantitative phase analysis (QPA) PY - 2007 SN - 0930-486X VL - 26 SP - 61 EP - 66 PB - Oldenbourg CY - München AN - OPUS4-16666 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wulfert, H. A1 - Ludwig, H.M. A1 - Adamczyk, Burkart T1 - The 'Klinkerweg': new process technology by Loesche PY - 2013 SN - 0263-6050 SN - 0308-8855 IS - September SP - 5 EP - 6 PB - Swan CY - Leatherhead AN - OPUS4-29089 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wulfert, H. A1 - Keyssner, M. A1 - Ludwig, H.M. A1 - Adamczyk, Burkart T1 - Metal recovery and conversion of steel slag into highly reactive cement components / Metallgewinnung und Umwandlung von LD-Schlacke in hochreaktive Zementkomponenten KW - Alite KW - Hydraulically active material KW - Arc furnace KW - Steel slag KW - LD-slag PY - 2013 SN - 0949-0205 N1 - Sprachen: Deutsch/Englisch - Languages: German/English VL - 9 SP - 34 EP - 40 PB - Bauverl. BV CY - Gütersloh AN - OPUS4-29090 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Adamczyk, Burkart A1 - Kühn, M. A1 - Mudersbach, D. T1 - Reduktion von Schlacken aus der Herstellung von Edelstählen PY - 2007 SN - 0948-4795 VL - 14 IS - 2 SP - 10 EP - 11 PB - FEhs CY - Duisburg AN - OPUS4-27374 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kemnitz, E. A1 - Zhu, Y. A1 - Adamczyk, Burkart T1 - Enhanced Lewis acidity by aliovalent cation doping in metal fluorides N2 - A model regarding the generation of acidity in binary metal fluorides has been proposed and its validity has been examined for several binary fluoride systems with the general compositions MF3/M'F3 and MF2/M'F3. In accordance with this hypothesis, the binary systems (CrF3/AlF3, CrF3/FeF3 and AlF3/VF3) do not show acidities larger than the sum of the acidities of the component fluorides. The hypothesis predicts the generation of Lewis acidity when MF2 is the major component (host) and generation of Brønsted acidity when MF3 acts as the host for the MF2/M'F3. The experimental results (surface acidity and catalytic activity) confirmed the predictions made from this hypothesis for binary combinations MgF2/ M'F3 (M'=Cr, Al, Fe, V). The application of this model is discussed in terms of other parameters: ionic radii and the fluoride affinity of the metal fluorides involved. PY - 2002 DO - https://doi.org/10.1016/S0022-1139(02)00022-2 SN - 0022-1139 SN - 1873-3328 VL - 114 SP - 163 EP - 170 PB - Elsevier CY - Amsterdam AN - OPUS4-1661 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -