TY - JOUR A1 - Agea Blanco, Boris A1 - Reinsch, Stefan A1 - Müller, Ralf T1 - Sintering and foaming of barium silicate glass powder compacts JF - Frontiers in Materials Glass Science N2 - The manufacture of sintered glasses and glass-ceramics, glass matrix composites, and glass-bounded ceramics or pastes is often affected by gas bubble formation. Against this background, we studied sintering and foaming of barium silicate glass powders used as SOFC sealants using different powder milling procedures. Sintering was measured by means of heating microscopy backed up by XPD, differential thermal analysis, vacuum hot extraction (VHE), and optical and electron microscopy. Foaming increased significantly as milling progressed. For moderately milled glass powders, subsequent storage in air could also promote foaming. Although the powder compacts were uniaxially pressed and sintered in air, the milling atmosphere significantly affected foaming. The strength of this effect increased in the order Ar ≈ N2 < air < CO2. Conformingly, VHE studies revealed that the pores of foamed samples predominantly encapsulated CO2, even for powders milled in Ar and N2. Results of this study thus indicate that foaming is caused by carbonaceous species trapped on the glass powder surface. Foaming could be substantially reduced by milling in water and 10 wt% HCl. KW - Glass powder KW - Sintering KW - Foaming KW - SOFC PY - 2016 UR - http://journal.frontiersin.org/article/10.3389/fmats.2016.00045/full?&utm_source=Email_to_authors_&utm_medium=Email&utm_content=T1_11.5e1_author&utm_campaign=Email_publication&field=&journalName=Frontiers_in_Materials&id=214488 DO - https://doi.org/10.3389/fmats.2016.00045 SN - 2296-8016 VL - 3 SP - Article 45, 1 EP - 10 AN - OPUS4-38303 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agea Blanco, Boris A1 - Blaeß, Carsten A1 - Reinsch, Stefan A1 - Sojref, Regine A1 - Brauer, D. S. A1 - Müller, Ralf T1 - Sintering and foaming of barium and calcium silicate glass powders N2 - Unexpected bubble bursting (foaming) is a huge problem in the fabrication of sintered glasses, sintered glass-ceramics and glass matrix composites. In this presentation the main aspects of foaming are shown for two completely different glass powders: 1) used as a SOFC sealand 2) bioactive glass T2 - Glashüttentag 2016 CY - Berlin, Germany DA - 29.09.16 KW - Bubble KW - Foaming KW - Glass powders PY - 2016 AN - OPUS4-38319 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agea Blanco, Boris A1 - Blaess, C. A1 - Reinsch, Stefan A1 - Brauer, D. A1 - Müller, Ralf T1 - Sintering and foaming of barium and calcium silicate glass powders T2 - IMAPS/ACerS 11th International CICMT conference and exhibition (Proceedings) N2 - Sintering and foaming of barium and calcium silicate glass powder compacts have been studied for different powder milling. Sintering was measured by means of heating microscopy backed up by XRD, DTA, Vacuum Hot Extraction (VHE) and electron microscopy. Foaming intensity strongly increased with decreasing glass partiefe size. Although powder compacts were uniaxially pressed and sintered in ambient air, foaming was affected by the milling atmosphere and most intensive for milfing in C02. Conformingly, VHE studies revealed that foaming of fully sintered samples was mainly driven by C02, even for powders milled in technical air, Ar and N2. Prolonged storage of air milled barium silicate glass powders in ambient air before pressing and sintering caused further increase of foaming intensity. These findings indicate that carbonaceous species are preferentially trapped to or close beneath the powder surface during milling and later storage. The temperature range of C02 degassing from fully sintered barium and calcium silicate g/ass powder compacts fits the temperature ranges of decomposition of BaC03 and CaC03 mix-milled with the respective barium and calcium silicate glass powders. T2 - IMAPS/ACerS 11th International CICMT conference and exhibition CY - Dresden, Germany DA - 20.04.2015 KW - Sintering KW - Foaming KW - Silicate glass powders KW - Barium and calcium silicate plass powders KW - Degassing PY - 2015 SN - 978-1510804562 SP - 31 EP - 37 AN - OPUS4-35250 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agea Blanco, Boris A1 - Reinsch, Stefan A1 - Müller, Ralf T1 - Sintering and Foaming of Barium Silicate Glass Powders N2 - The manufacture of sintered glasses and glass-ceramics, glass matrix composites, and glass-bounded ceramics or pastes is often affected by gas bubble formation. Against this background, we studied sintering and foaming of barium silicate glass powders used as SOFC sealants using different powder milling procedures. Sintering was measured by means of heating microscopy backed up by XPD, differential thermal analysis, vacuum hot extraction (VHE), and optical and electron microscopy. Foaming increased significantly as milling progressed. For moderately milled glass powders, subsequent storage in air could also promote foaming. Although the powder compacts were uniaxially pressed and sintered in air, the milling atmosphere significantly affected foaming. The strength of this effect increased in the order Ar ≈ N2 < air < CO2. Conformingly, VHE studies revealed that the pores of foamed samples predominantly encapsulated CO2, even for powders milled in Ar and N2. Results of this study thus indicate that foaming is caused by carbonaceous species trapped on the glass powder surface. Foaming could be substantially reduced by milling in water and 10 wt% HCl. T2 - 91. Glastechnische Tagung CY - Weimar, Germany DA - 29.05.2017 KW - Glass powder sintering KW - Milling KW - Foaming KW - Degassing KW - SOFC PY - 2017 AN - OPUS4-42858 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -