TY - CONF A1 - Agea Blanco, Boris A1 - Blaess, C. A1 - Reinsch, Stefan A1 - Brauer, D. A1 - Müller, Ralf T1 - Sintering and foaming of barium and calcium silicate glass powders N2 - Sintering and foaming of barium and calcium silicate glass powder compacts have been studied for different powder milling. Sintering was measured by means of heating microscopy backed up by XRD, DTA, Vacuum Hot Extraction (VHE) and electron microscopy. Foaming intensity strongly increased with decreasing glass partiefe size. Although powder compacts were uniaxially pressed and sintered in ambient air, foaming was affected by the milling atmosphere and most intensive for milfing in C02. Conformingly, VHE studies revealed that foaming of fully sintered samples was mainly driven by C02, even for powders milled in technical air, Ar and N2. Prolonged storage of air milled barium silicate glass powders in ambient air before pressing and sintering caused further increase of foaming intensity. These findings indicate that carbonaceous species are preferentially trapped to or close beneath the powder surface during milling and later storage. The temperature range of C02 degassing from fully sintered barium and calcium silicate g/ass powder compacts fits the temperature ranges of decomposition of BaC03 and CaC03 mix-milled with the respective barium and calcium silicate glass powders. T2 - IMAPS/ACerS 11th International CICMT conference and exhibition CY - Dresden, Germany DA - 20.04.2015 KW - Sintering KW - Foaming KW - Silicate glass powders KW - Barium and calcium silicate plass powders KW - Degassing PY - 2015 SN - 978-1510804562 SP - 31 EP - 37 AN - OPUS4-35250 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -