TY - JOUR A1 - Vöse, Markus A1 - Fedelich, Bernard A1 - Owen, J. T1 - A simplified model for creep induced grain boundary cavitation validated by multiple cavity growth simulations JF - Computational materials science N2 - Simulations of cavitation processes on a grain boundary under creep conditions have been carried out, taking into account nucleation, growth, coalescence and sintering of multiple cavities. Cavity growth rates have been calculated through a resolution procedure based on the use of holomorphic complex functions. Three dimensionless parameters have been identified that are responsible for the cavitation development. Parameter studies have been carried out in order to characterise the mechanisms that are responsible for the cavitation development. These studies have been used to develop a physically motivated, simplified model in order to describe the cavitation development of the simulations in terms of global state variables. The simplified model is able to reproduce the cavitation development for all considered combinations of the dimensionless parameters and allows the description of the thickening behaviour of a cavitating grain boundary. KW - Creep damage KW - Grain boundary diffusion KW - Cavitation KW - Simulation PY - 2012 DO - https://doi.org/10.1016/j.commatsci.2012.01.033 SN - 0927-0256 VL - 58 SP - 201 EP - 213 PB - Elsevier CY - Amsterdam AN - OPUS4-25630 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vöse, Markus A1 - Fedelich, Bernard ED - Maruyama, K. ED - Abe, F. ED - Igarashi, M. ED - Kishida, K. ED - Suzuki, M. ED - Yoshimi, K. T1 - Grain boundary cavitation under time-varying normal stresses T2 - 12th International conference on creep and fracture of engineering materials and structures (Proceedings) T2 - 12th International conference on creep and fracture of engineering materials and structures CY - Kyoto, Japan DA - 2012-05-27 KW - Creep damage KW - Grain boundary diffusion KW - Cavitation KW - Simulation KW - Evolution equations PY - 2012 SP - 1 EP - 4(?) AN - OPUS4-27544 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vöse, Markus A1 - Fedelich, Bernard A1 - Otto, F. A1 - Eggeler, G. T1 - Micromechanical modeling of creep damage in a copper-antimony alloy JF - Procedia materials science N2 - A micromechanical model of creep induced grain boundary damage is proposed, which allows for the simulation of creep damage in a polycrystal with the finite element method. Grain boundary cavitation and sliding are considered via a micromechanically motivated cohesive zone model, while the grains creep following the slip system theory. The model has been calibrated with creep test data from pure Cu single crystals and a coarse-grained polycrystalline Cu-Sb alloy. The test data includes porosity measurements and estimates of grain boundary sliding. Finally, the model has been applied to Voronoi models of polycrystalline structures. In particular the influence of grain boundary sliding on the overall creep rate is demonstrated. T2 - ECF20 - 20th European conference on fracture CY - Trondheim, Norway DA - 28.06.2014 KW - Creep damage KW - Grain boundary sliding KW - Cohesive zone KW - Micromechanical model KW - Polycrystal PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-309914 DO - https://doi.org/10.1016/j.mspro.2014.06.006 SN - 2211-8128 VL - 3 SP - 21 EP - 26 PB - Curran CY - Red Hook, NY, USA AN - OPUS4-30991 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Epishin, Alexander A1 - Link, T. A1 - Klingelhöffer, Hellmuth A1 - Fedelich, Bernard A1 - Portella, Pedro Dolabella T1 - Creep damage of single-crystal nickel base superalloys: mechanisms and effect on low cycle fatigue JF - Materials at high temperatures N2 - The main mechanisms of creep damage of single-crystal nickel-base superalloys are the loss of the interface coherency, coarsening of the γ / γ'-microstructure, precipitation of topologically closed packed phases and growth of porosity. This degradation deteriorates the mechanical properties such as yield stress, creep lifetime and especially low-cycle fatigue life, which can be reduced nearly by a factor of 10. The degradation kinetics during creep was characterised quantitatively on the superalloy CMSX-4. A new non-destructive testing technique was applied to cover a wide test parameter range with few specimens in a relatively short time: repeated load annealing of wedge shaped specimens. KW - Creep damage KW - Nickel-base superalloys KW - Low-cycle fatigue KW - Rafting KW - Porosity KW - Prior exposure PY - 2010 DO - https://doi.org/10.3184/096034009X12603595726283 SN - 0960-3409 VL - 27 IS - 1 SP - 53 EP - 59 PB - Science Reviews CY - St. Albans, Herts. [u.a.] AN - OPUS4-23912 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Epishin, Alexander A1 - Link, T. A1 - Klingelhöffer, Hellmuth A1 - Fedelich, Bernard A1 - Portella, Pedro Dolabella ED - S.R. Holdsworth, ED - I.A. Shibli, T1 - Creep damage mechanisms of single-crystal Nickel base superalloys T2 - Creep and fracture in high temperature components (Proceedings) T2 - 2nd ECCC Creep Conference CY - Zurich, Switzerland DA - 2009-04-21 KW - Creep damage KW - Nickel-base superalloys PY - 2009 SN - 978-1-60595-005-1 SP - 692 EP - 701 PB - DEStech Publications, Inc. AN - OPUS4-19448 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -