TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Baumann, O. A1 - Modersohn, W. A1 - Halle, T. T1 - Influence of the post-weld surface treatment on the corrosion resistance of the duplex stainless steel 1.4062 T2 - Tagungsband zum 19. Werkstofftechnischen Kolloquium N2 - The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polished or blasting depending on the application and the requested corrosion resistance. Blasted surfaces are often used in industrial practice due to the easier and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the different performed corrosion tests (potential measurement, KorroPad-test and pitting potential) on welding seams with different surface treatments. T2 - 19. Werkstofftechnisches Kolloquium Chemnitz CY - Chemnitz, Germany DA - 16.03.2017 KW - Corrosion resistance KW - Duplex stainless steel KW - Influence PY - 2017 SN - 978-3-00-055705-7 SN - 1439-1597 VL - 61 SP - 172 EP - 180 PB - Schriftreihe Werkstoffe und werkstofftechnische Anwendungen CY - Chemnitz AN - OPUS4-40168 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rosemann, Paul A1 - Müller, C. A1 - Baumann, O. A1 - Modersohn, W. A1 - Halle, T. T1 - Influence of the post-weld surface treatment on the corrosion resistance of the duplex stainless steel 1.4062 JF - IOP Conf. Series: Materials Science and Engineering N2 - The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polished or blasting depending on the application and the requested corrosion resistance. Blasted surfaces are often used in industrial practice due to the easier and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the different performed corrosion tests (potential measurement, KorroPad-test and pitting potential) on welding seams with different surface treatments. T2 - 19th Chemnitz Seminar on Materials Engineering – 19. Werkstofftechnisches Kolloquium CY - Chemnitz, Germany DA - 16.03.2017 KW - Corrosion resistance KW - Welding KW - Duplex stainless steels KW - Pitting corrosion KW - Surface treatment PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-395374 DO - https://doi.org/10.1088/1757-899X/181/1/012019 SN - 1757-899X SN - 1757-8981 VL - 181 IS - Conference 1 SP - Article UNSP 012019, 1 EP - 9 PB - IOP Publishing CY - Bristol, UK AN - OPUS4-39537 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Baumann, O. A1 - Müller, C. T1 - Influence of the post-weld surface treatment on the corrosion resistance of the duplex stainless steel 1.4062 N2 - The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polishing or blasting depending on the requested corrosion resistance. Blasted surfaces are often used in the industrial practice due to the faster and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the results of different corrosion tests (KorroPad-testing and pitting potentials). T2 - Materials Science and Engineering 2018 (MSE) CY - Darmstadt, Germany DA - 26.09.2018 KW - Duplexstahl KW - Korrosion KW - Nichtrostender Stahl KW - Schweißen KW - Oberflächenbearbeitung KW - Strahlen KW - KorroPad PY - 2018 AN - OPUS4-46090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Guljamow, A. A1 - Delißen, Friedmar A1 - Baumann, O. A1 - Thünemann, Andreas A1 - Dittmann, E. T1 - Unique properties of eukaryote-type actin and profilin horizontally transferred to cyanobacteria JF - PLoS one N2 - A eukaryote-type actin and its binding protein profilin encoded on a genomic island in the cyanobacterium Microcystis aeruginosa PCC 7806 co-localize to form a hollow, spherical enclosure occupying a considerable intracellular space as shown by in vivo fluorescence microscopy. Biochemical and biophysical characterization reveals key differences between these proteins and their eukaryotic homologs. Small-angle X-ray scattering shows that the actin assembles into elongated, filamentous polymers which can be visualized microscopically with fluorescent phalloidin. Whereas rabbit actin forms thin cylindrical filaments about 100 µm in length, cyanobacterial actin polymers resemble a ribbon, arrest polymerization at 5-10 µm and tend to form irregular multi-strand assemblies. While eukaryotic profilin is a specific actin monomer binding protein, cyanobacterial profilin shows the unprecedented property of decorating actin filaments. Electron micrographs show that cyanobacterial profilin stimulates actin filament bundling and stabilizes their lateral alignment into heteropolymeric sheets from which the observed hollow enclosure may be formed. We hypothesize that adaptation to the confined space of a bacterial cell devoid of binding proteins usually regulating actin polymerization in eukaryotes has driven the co-evolution of cyanobacterial actin and profilin, giving rise to an intracellular entity. PY - 2012 DO - https://doi.org/10.1371/journal.pone.0029926 SN - 1932-6203 VL - 7 IS - 1 SP - e29926-1 - e29926-11 PB - PubMed Central AN - OPUS4-25403 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -