TY - JOUR A1 - Strommer, Bettina A1 - Schulze, Dietmar A1 - Schartel, Bernhard A1 - Böhning, Martin T1 - Networking Skills: The Effect of Graphene on the Crosslinking of Natural Rubber Nanocomposites with Sulfur and Peroxide Systems N2 - Tailored crosslinking in elastomers is crucial for their technical applications. The incorporation of nanoparticles with high surface-to-volume ratios not only leads to the formation of physical networks and influences the ultimate performance of nanocomposites, but it also affects the chemical crosslinking reactions. The influence of few-layer graphene (FLG) on the crosslinking behavior of natural rubber is investigated. Four different curing systems, two sulfur-based with different accelerator-to-sulfur ratios, and two peroxide-based with different peroxide concentrations, are combined with different FLG contents. Using differential scanning calorimetry (DSC), vulcametry (MDR) and swelling measurements, the results show an accelerating effect of FLG on the kinetics of the sulfur-based curing systems, with an exothermic reaction peak in DSC shifted to lower temperatures and lower scorch and curing times in the MDR. While a higher accelerator-to-sulfur ratio in combination with FLG leads to reduced crosslinking densities, the peroxide crosslinkers are hardly affected by the presence of FLG. The good agreement of crosslink densities obtained from the swelling behavior confirms the suitability of vulcameter measurements for monitoring the complex vulcanization process of such nanocomposite systems in a simple and efficient way. The reinforcing effect of FLG shows the highest relative improvements in weakly crosslinked nanocomposites. KW - Nanocomposite KW - Elastomers KW - Graphene KW - Crosslinking KW - Network KW - Rubber KW - Vulcanization PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-560409 DO - https://doi.org/10.3390/polym14204363 VL - 14 IS - 20 PB - MDPI AN - OPUS4-56040 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Strommer, Bettina A1 - Schulze, Dietmar A1 - Schartel, Bernhard A1 - Böhning, Martin T1 - The quantification of anisotropy in graphene/natural rubber nanocomposites: Evaluation of the aspect ratio, concentration, and crosslinking N2 - In the processing of nanocomposites, high shear stresses at elevated tempera-tures orient two-dimensional nanoparticles like graphene. This orientationleads to anisotropic mechanical, thermal or barrier properties of the nanocom-posite. This anisotropy is addressed in this study by comparing graphene (few-layer graphene, FLG) with a nanoscaled carbon black (nCB) at a filler contentof 3 phr, by varying the vulcanization, and by comparing different FLG con-tents. Transmission electron microscopy gives insight into the qualitative ori-entation in the nanocomposite with FLG or nCB. The storage moduli paralleland normal to the orientation reveal the direction dependency of reinforce-ment through dynamic mechanical analysis (DMA). Dimensional swellingmeasurements show a restriction of the expansion parallel to the FLG orienta-tion, and an increased expansion normal to the orientation. The vulcanizationsystem and crosslinking determine the respective level of property values, andhigher crosslinking densities increase the anisotropy in DMA resulting invalues of up to 2.9 for the quantified anisotropy factor. With increasing FLGcontent, the anisotropy increases. A comparison of the results reveals swellingmeasurements as the most suitable method for the determination of anisot-ropy. Compared to recent literature, the presented processing induces higheranisotropy, leading to higher reinforcing effects in the direction of orientation KW - Natural rubber KW - Graphene KW - Nanocomposite KW - Mechanical properties KW - Swelling PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-571522 DO - https://doi.org/10.1002/app.53753 SN - 1097-4628 VL - 140 IS - 16 SP - 1 EP - 15 PB - Wiley online library CY - Hoboken, New Jersey (USA) AN - OPUS4-57152 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Emamverdi, Farnaz A1 - Huang, J. A1 - Szymoniak, Paulina A1 - Bojdys, M. J. A1 - Böhning, Martin A1 - Schönhals, Andreas T1 - Structure and molecular mobility of phosphinine-based covalent organic frameworks – glass transition of amorphous COFs N2 - Two-dimensional covalent organic frameworks (COFs) based on phosphinine and thiophene building blocks have been synthesized with two different side groups. The materials are denoted as CPSF-MeO and CPSF-EtO where CxxF correspond to the covalent framework, whereas P and S are related to heteroatoms phosphorous and sulfur. MeO and EtO indicate the substituents, i.e. methoxy and ethoxy. Their morphologies were studied by scanning electron microcopy and X-ray scattering. The absence of crystalline reflexes in the X-ray pattern reveal that both materials are amorphous and can be considered as glasses. Furthermore, N2 adsorption measurements indicate substantial Brunauer–Emmett–Teller (BET) surface area values pointing to the formation of three-dimensional pores by stacking of the aromatic 2D layer. An analysis of the porosity of both COFs showed a mean radius of the pores to be of ca. 4 nm, consistent with their chemical structure. The COFs form nanoparticles with a radius of around 100 nm. The thermal behavior of the COFs was further investigated by fast scanning calorimetry. These investigations showed that both COFs undergo a glass transition. The glass transition temperature of CPSF-EtO is found to be ca. 100 K higher than that for CPSF-MeO. This large difference in the glass transition is discussed to be due to a change in the interaction of the COF sheets induced by the longer ethoxy group. It might be assumed that for CPSF-EtO more individual COF sheets assemble to larger stacks than for CPSF-MeO. This agrees with the much larger surface area value found for CPSF-EtO compared to CPSF-MeO. To corroborate the results obtained be fast scanning calorimetry dielectric measurements were conducted which confirm the occurrence of a dynamic glass transition. The estimated temperature dependence of the relaxation rates of the dielectric relaxation and their absolute values agrees well with the data obtained by fast scanning calorimetry. Considering the fragility approach to the glass transition, it was further found that CPSF-MeO is a fragile glass former whereas CPSF-EtO behaves as a strong glass forming material. This difference in the fragility points also to distinct differences in the interaction between the 2D COF molecules in both materials. KW - Covalent Organic frameworks PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-596770 DO - https://doi.org/10.1039/d3ma01123b SP - 1 EP - 10 PB - Royal Society of Chemistry (RSC) AN - OPUS4-59677 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zorn, R. A1 - Lohstroh, W. A1 - Zamponi, M. A1 - Harrison, W. A1 - Budd, P. A1 - Böhning, Martin A1 - Schönhals, Andreas T1 - Molecular mobility of a polymer of intrinsic microporosity revealed by quasielastic neutron scattering N2 - Quasielastic neutron scattering by employing a combination of time-of-flight and backscattering techniques is carried out to explore the molecular mobility of a polymer of intrinsic microporosity (PIM-1) at microscopic time scales in comparison with a high-performance polyimide. Molecular fluctuations can change the structure of the temporary network of micropores and open or close pathways for gas molecules. Therefore, the investigation might help to understand the selectivity of PIMs in gas separation processes. The performed neutron scattering experiments provide evidence for a low-temperature relaxation process, which was assigned to methyl group rotation. This methyl group rotation was analyzed in terms of jump diffusion in a three-fold potential. The analysis results in a fraction of methyl groups which are immobilized. For PIM-1 it was found that the fraction of immobilized methyl groups decreases with increasing temperature up to 350 K. At higher temperatures the number of immobilized methyl group increases gain due to an underlying relaxation process. This motional process on a somewhat larger length scale might lead to a reversible structural rearrangement which partially hinders the strongly localized methyl group rotation. In addition, it was found that the activation energy for the methyl group rotation for PIM-1 and the polyimide is significantly higher than for conventional polymers. KW - Polymer of intrinsic microporosity KW - Quasielastic neutron scattering PY - 2020 DO - https://doi.org/10.1021/acs.macromol.0c00963 SN - 0024-9297 SN - 1520-5835 VL - 53 IS - 15 SP - 6731 EP - 6739 PB - American Chemical Society CY - Washington, DC AN - OPUS4-51147 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kolmangadi, Mohamed Aejaz A1 - Szymoniak, Paulina A1 - Smales, Glen Jacob A1 - Alentiev, D. A1 - Bermeshev, M. A1 - Böhning, Martin A1 - Schönhals, Andreas T1 - Molecular Dynamics of Janus Polynorbornenes: Glass Transitions and Nanophase Separation N2 - For the first time, dielectric and calorimetric investigations of an homologous series of Janus polynorbornenes with rigid main backbones and flexible -Si(OR)3 side groups, of differing length alkyl chains (R = Propyl, Butyl, Hexyl, Octyl, Decyl) is reported. Generally, this class of polymers has some potential for applications in the field of gas separation membranes. Two dielectrically active processes are observed at low temperatures, denoted as β- and α- relaxation. The former can be assigned to localized fluctuations, whilst the latter is related to the glassy dynamics of the flexible -Si(OR)3 side groups, creating a nanophase separation in both the alkyl chain rich and backbone rich domains. This is confirmed through temperature modulated DSC measurements and X-ray scattering experiments. The glass transition temperatures of the backbone rich domains, which are beyond or near to their degradation temperatures in terms of conventional DSC, are determined for the first time using Fast Scanning Calorimetry employing both fast heating and cooling rates. This is complimented with scattering experiments that show how the size of the alkyl chain rich domains increases with chain length. Alongside these results, a significant conductivity contribution was observed for all poly(tricyclononenes) with -Si(OR)3 side groups, which is interpreted in terms of a percolation model. KW - Polynorbornenes KW - Broadband Dielectric Spectrscopy KW - Advanced calorimetry PY - 2020 DO - https://doi.org/10.1021/acs.macromol.0c01450 VL - 53 IS - 17 SP - 7410 EP - 7419 PB - ACS AN - OPUS4-51196 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schönhals, Andreas A1 - Szymoniak, Paulina A1 - Kolmangadi, Mohamed Aejaz A1 - Böhning, Martin A1 - Zamponi, M. A1 - Frick, B. A1 - Appel, M. A1 - Günther, G. A1 - Russina, M. A1 - Alentiev, D. A1 - Bermeshev, M. A1 - Zorn, R. T1 - Microscopic dynamics of highly permeable super glassy polynorbornenes revealed by quasielastic neutron scattering N2 - The molecular dynamics of addition-type poly(tricyclononenes) with Si-substituted bulky side groups has been investigated by a combination of neutron time-of-flight and neutron backscattering spectroscopy methods on a time scale from 0.1 ps to ca. 3 ns. The investigated poly(tricyclononenes) PTCNSi1 and PTCNSi2g both bear a high microporosity which makes them promising candidates for active separation layers for gas separation membranes. At least for larger gas molecules it is assumed that the pathways for diffusion require an enlargement of pre-existing micropores in terms of an activated zone. A low temperature relaxation process was found for both polymers by the performed neutron scattering experiments. This process was assigned to the methyl group rotation. It was analysed in terms of a jump diffusion in a three-fold potential. The analysis of the dependence of the elastic incoherent structure factor on the scattering vector yields the number of methyl groups which might be immobilized. For PTCNSi1 (3 methyl groups in the monomeric unit) it was found that all methyl groups take part in the methyl group rotation whereas for PTCNSi2g (6 methyl groups in monomeric unit) a considerable number of methyl groups are blocked in their rotation. This immobilization of methyl groups is due to the sterically demanding arrangement of the methyl groups in PTCNSi2g. This conclusion is further supported by the result that the activation energy for the methyl group rotation is three times higher for PTCNSi2g than that of PTCNSi1. KW - Highly permeably polynorbornenes KW - Polymers of intrinsic microporosity KW - Gas separation membranes KW - Quasielastic neutron scattering PY - 2021 DO - https://doi.org/10.1016/j.memsci.2021.119972 SN - 0376-7388 VL - 642 PB - Elesevier B.V. AN - OPUS4-53508 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kolmangadi, Mohamed Aejaz A1 - Szymoniak, Paulina A1 - Smales, Glen Jacob A1 - Bermeshev, M. A1 - Schönhals, Andreas A1 - Böhning, Martin T1 - Molecular mobility of polynorbornenes with trimethylsiloxysilyl side groups: Influence of the polymerization mechanism N2 - We report dielectric and calorimetric studies on metathesis and addition-type polytricyclononenes, both based on the same monomer bearing three pendant OSiMe3 groups. For the addition-type polymer, dielectric spectroscopy reveals a β*-process related to the microporosity, whereas for its metathesis counterpart, the segmental dynamics manifests as an α-process related to a glass transition. Besides active dielectric processes, a significant conductivity contribution is detected for both samples which for the microporous additiontype polymer is three orders of magnitude greater than for the metathesis polymer. The broadband dielectric spectroscopy is complemented by detailed calorimetric investigations, comprising DSC, FSC, and TMDSC. The calorimetric methods detected the glass transition for the metathesis polymer in agreement with the observed dielectric α-process. Furthermore, the already reported gas transport properties for both polymers are compared, setting them in correlation with the observed molecular mobility and conductivity behavior. The discussed results reflect significant differences in molecular mobility of the two polymers affecting the appearance of microporosity which strongly determines the gas transport properties. KW - Microporous polymers KW - Molecular mobility KW - Electrical conductivity KW - Membrane polymers KW - Gas separation PY - 2022 DO - https://doi.org/10.22079/JMSR.2021.538060.1495 SN - 2476-5406 VL - 8 IS - 3 SP - 1 EP - 9 PB - Membrane Processes Research Laboratory (MPRL) CY - Tehran AN - OPUS4-54303 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zorn, R. A1 - Szymoniak, Paulina A1 - Kolmangadi, Mohamed Aejaz A1 - Wolf, M. A1 - Alentiev, D. A1 - Bermeshev, M. A1 - Böhning, Martin A1 - Schönhals, Andreas T1 - Low frequency vibrational density of state of highly permeable super glassy polynorbornenes – The Boson peak N2 - Inelastic incoherent neutron time-of flight scattering was employed to measure the low frequency density of states for a series of addition polynorbornenes with bulky side groups. The rigid main chain in combination with the bulky side groups give rise to a microporosity of these polymers in the solid state. The microporosity characterized by the BET surfaces area varies systematically in the considered series. Such materials have some possible application as active separation layer in gas separation membranes. All investigated materials show excess contributions to the Debye type density of states characteristic for glasses known as Boson peak. The maximum position of the Boson peak shifts to lower frequency values with increasing microporosity. Data for PIM-1 and Matrimid included for comparison are in good agreement to this dependency. This result supports the sound wave interpretation of the Boson peak. KW - Polynorbornes KW - Neutron Scattering PY - 2020 DO - https://doi.org/10.1039/d0cp03360j SN - 1463-9076 VL - 22 IS - 33 SP - 18381 EP - 18387 PB - Royal Chemical Society AN - OPUS4-51165 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Böhning, Martin A1 - Goering, Harald A1 - Hao, Ning A1 - Schönhals, Andreas T1 - Polymer-based Nanocomposites - Particle Dispersion and Physical Properties T2 - Nanofair 2005 CY - Dresden, Germany DA - 2005-11-29 KW - Polymerbasierte Nanokomposite PY - 2005 SN - 3-18-091920-5 N1 - Serientitel: VDI-Berichte – Series title: VDI-Berichte IS - 1920 SP - 263 EP - 267 PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-11589 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Becker, D. A1 - Konnertz, Nora A1 - Böhning, Martin A1 - Schmidt, J. A1 - Thomas, A. T1 - Light-switchable polymers of intrinsic microporosity N2 - The interest in (micro)porous systems is greater than ever before with microporous polymers finding application in areas such as gas storage/separation and catalysis. In contrast to the vast majority of publications on microporous polymers seeking ever higher values for surface area or uptake capacity for a particular gas, this work presents a means to render a microporous system responsive to electromagnetic stimuli. The incorporation of a diarylethene (DAE) derivative in the backbone of a polymer of intrinsic microporosity (PIM) produces a microporous system that exhibits photochromism as proven by UV–vis absorption and NMR studies. In the resulting DAE-PIM, surface area is not a fixed unalterable property but can be influenced by the external and nondestructive stimulus light in a reversible manner. Furthermore, in combination with Matrimid, free-standing membranes can be produced that display light-switchable diffusivity and permeability for carbon dioxide and oxygen. In this way, material scientists are offered the potential to employ only one system that can assume several states with different properties for each. KW - Gaspermeation KW - Diffusion KW - Polymer intrinsischer Mikroporosität KW - UV-VIS PY - 2016 DO - https://doi.org/10.1021/acs.chemmater.6b02619 SN - 0897-4756 VL - 28 IS - 23 SP - 8523 EP - 8529 PB - ACS CY - Whashington,DC AN - OPUS4-38735 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Robertson, Daniela A1 - Böhning, Martin A1 - Schröder, Hartmut A1 - Brummermann, K. A1 - Kaudinya, I. A1 - Saathoff, F. T1 - Möglichkeiten der Abschätzung der Langzeitbeständigkeit von Kunststoffdichtungsbahnen (KDB) auf Polyolefinbasis für den Tunnelbau N2 - Im Rahmen eines von der Bundesanstalt für Straßenwesen (BASt) initiierten Forschungsvorhabens (15.449/2007/ERB: „Prüfverfahren zur Beurteilung der Lebensdauer von Kunststoffdichtungsbahnen für Straßentunnel“) wurden anhand von Untersuchungen an Kunststoffdichtungsbahnen (KDB) auf Basis von Polyolefinwerkstoffen die Möglichkeiten der Beurteilung der oxidativen Langzeitbeständigkeit sondiert. Im Mittelpunkt stand die Erprobung des Autoklaventests in Anlehnung an DIN EN ISO 13438 (Methode C1/C2) an ausgewählten, für den Tunnelbau repräsentativen marktüblichen KDB-Produkten. Die Untersuchungen im Autoklaven bei erhöhten Temperaturen (60 °C, 70 °C und 80 °C) und Sauerstoffdrücken (11, 21 und 51 bar) wurden durch vergleichende Versuche im Wärmeschrank (Ofen) bei erhöhter Temperatur (85 °C) in Anlehnung an DIN EN 14575 ergänzt. Die KDBProdukte wurden außerdem einer eingehenden Materialcharakterisierung (Zugprüfung, DMA, DSC) unterzogen. Weiterhin wurden Bauwerksdaten recherchiert und auf ihre Nutzbarkeit zur Bewertung und Prüfbarkeit der Langzeitbeständigkeit von KDB in Tunneln betrachtet. Ziel war auch, die Anwendbarkeit des bisher vorgeschlagenen Extrapolationsmodells zur Auswertung der Ergebnisse von Autoklaventests an im Tunnelbau marktüblichen Produkten für Nutzungsdauern über 25 Jahre zu überprüfen und zur Entwicklung eines geeigneten Prüfverfahrens beizutragen. Der Beitrag geht auf Ergebnisse des Vorhabens ein und zeigt erste Schlussfolgerungen und weiteren Untersuchungsbedarf auf. Die Ergebnisse werden in den „Empfehlungen zu Dichtungssystemen im Tunnelbau EAG-EDT“ des Arbeitskreises 5.1 „Kunststoffe in der Geotechnik und im Wasserbau“ berücksichtigt, deren 2. Auflage in Vorbereitung ist. Aspekte des thermischen Verhaltens der eingesetzten Werkstoffe sowie mögliche Anpassungen der Prüfrandbedingungen für die Autoklaventests werden ergänzt und Hinweise zur Interpretation von Prüfergebnissen gegeben. Außerdem wurden inzwischen ausgehend von den Ergebnissen des Forschungsvorhabens erste Autoklaven-Ringversuche in drei Prüfinstitutionen initiiert. T2 - 12. Informations- und Vortragstagung über "Kunststoffe in der Geotechnik" CY - Munich, Germany DA - 03.03.2011 KW - Kunststoffdichtungsbahnen auf Polyolefinbasis KW - Oxidative Langzeitbeständigkeit KW - Autoklaventest - beschleunigte Alterung KW - DSC KW - DMA PY - 2011 SN - 978-3-940476-26-5 IS - Geotechnik Sonderheft 2011 SP - 35 EP - 42 AN - OPUS4-24399 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Böhning, Martin A1 - Goering, Harald A1 - Fritz, Andreas A1 - Brzezinka, Klaus-Werner A1 - Turky, Gamal A1 - Schönhals, Andreas A1 - Schartel, Bernhard T1 - Dielectric Study of Molecular Mobility in Poly(propylene-graft-maleic anhydride)/Clay Nanocomposites N2 - Polymer/clay nanocomposite materials based on poly(propylene-graft-maleic anhydride) (PPgMAH) and two different organophilic modified clays were investigated by dielectric relaxation spectroscopy (DRS). In contrast to ungrafted polypropylene (PP), PPgMAH shows a dielectrically active relaxation process which can be assigned to localized fluctuations of the polar maleic anhydride groups. Its relaxation rate exhibits an unusual temperature dependence, which could be attributed to a redistribution of water molecules in the polymeric matrix. This is confirmed by a combination of Raman spectroscopy and thermogravimetric experiments (TGA) with real-time dielectric measurements under controlled atmospheres. In the nanocomposites this relaxation process is shifted to higher frequencies up to 3 orders of magnitude compared to the unfilled polymer. This indicates a significantly enhanced molecular mobility in the interfacial regions. In the nanocomposite materials a separate high-temperature process due to Maxwell-Wagner-Sillars (MWS) polarization was observed. The time constant of this MWS process can be correlated with characteristic length scales in nanocomposites and therefore provides additional information on dispersion and delamination/exfoliation of clay platelets in these materials. These properties also influence the diffusivity of the water molecules as revealed by real-time dielectric investigations. KW - Polymer clay nanocomposites KW - Molecular mobility KW - Dielectric relaxation spectroscopy PY - 2005 DO - https://doi.org/10.1021/ma048315c SN - 0024-9297 SN - 1520-5835 VL - 38 IS - 7 SP - 2764 EP - 2774 PB - American Chemical Society CY - Washington, DC AN - OPUS4-7281 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Böhning, Martin A1 - Tidjani, Adams A1 - Wald, Oliver A1 - Brzezinka, Klaus-Werner A1 - Turky, Gamal A1 - Goering, Harald A1 - Schartel, Bernhard A1 - Schönhals, Andreas T1 - Dielectric and gas transport properties of polypropylene-clay nanocomposites T2 - Frühjahrstagung des Arbeitskreises Festkörperphysik bei der DPG CY - Regensburg, Germany DA - 2002-03-11 PY - 2002 SN - 0420-0195 SN - 0372-5448 SN - 0343-9216 IS - CPP 5.4 SP - 425 CY - Bad Honnef AN - OPUS4-2036 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin T1 - Gas transport and molecular mobility in polymer/POSS nanocomposites T2 - Euromembrane 2006 CY - Taormina, Italy DA - 2006-09-24 PY - 2006 AN - OPUS4-11214 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin T1 - Investigation of swollen polymer/gas-systems: atomistic packing models based on experimental properties T2 - Frühjahrstagung der Deutschen Physikalischen Ges. / AKF Condensed Matter CY - Dresden, Germany DA - 2006-03-26 PY - 2006 AN - OPUS4-11316 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin T1 - Gas Transport and Molecular Mobility in Polymer Based Nanocomposite Systems T2 - 1st International Conference on Advanced Materials and their application, National Research Centre, Physics Division CY - Cairo, Egypt DA - 2005-12-12 PY - 2005 AN - OPUS4-10976 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin T1 - Small Molecules in Polymers and Polymer based Nanocomposites - Molecular Probes for Material Characterization and Design T2 - Polydays 2004 (Berliner Polymerentage); Universität Potsdam, Campus "Am Neuen Palais" CY - Potsdam, Germany DA - 2004-10-04 PY - 2004 AN - OPUS4-7297 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin A1 - Goering, Harald T1 - Preparation and Characterisation of Nanoscaled Nanostructured Materials T2 - Nanofair 2004 CY - Karlsruhe, Germany DA - 2004-11-22 PY - 2004 AN - OPUS4-7296 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin A1 - Robertson, Daniela A1 - Schröder, Hartmut T1 - Autoclave testing: a new approach for the evaluation of oxidative long-term resistance of geosynthetics N2 - Oxidative long time resistance is essential for many polyolefin based products, especially if repair or exchange is not possible as encountered in many building and geotechnical applications. Current regulations and recommendations for geosynthetics cover mainly the needs of a maximum lifetime of 25 years, though many applications require longer lifetimes up to 100 years and more. Reliable testing of the long time oxidation resistance is complicated by the complex interplay of physicochemical processes and reactions in combination with the need of relatively short testing durations, usually not exceeding 12 months. Thus for conventional atmospheric oven testing, the use of temperatures higher than 100 °C is inevitable, making conclusive Arrhenius extrapolations often questionable. Practical assessments of oxidative durability consist of exposures under accelerated ageing conditions with subsequent characterization of exposed material samples with respect to their residual stabilization and/or their mechanical properties. The autoclave test combines exposures at elevated temperatures with higher oxygen pressures and is performed with material samples immersed in a well defined aqueous medium representing critical environments in geosynthetic applications and including extraction of additives. Under these conditions meaningful results can be obtained within reasonable testing durations at only moderately elevated temperatures up to 80 °C. Application of different physicochemical methods, such as tensile testing, OIT /HP-OIT and analysis of residual antioxidant content (ICOT), in order to determine the time dependent degradation behaviour, reveal valuable information about mechanisms and effectiveness of the used antioxidants. Corresponding results for exposures at different temperatures and oxygen pressures are the basis for a 3D-extrapolation in order to estimate the expected service life. Different empirical models are presented and discussed with respect to their practical impact. T2 - EuroGeo4, 4th European Geosynthetics Conference CY - Edinburgh, UK DA - 2008-09-07 KW - Ageing KW - Degradation KW - Geotextiles KW - Polyolefin KW - Polypropylene KW - Oxidative resistance KW - Lifetime prediction PY - 2008 IS - Paper 143 SP - 1 EP - 8 AN - OPUS4-18424 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heuchel, M. A1 - Hölck, Ole A1 - Böhning, Martin A1 - Siegert, R. A1 - Hofmann, D. ED - Qi, Y. ED - H.E. Fang, ED - N. Reynolds, ED - Liu, Z.-K. T1 - Knowledge-based approach to gas sorption in glassy polymers by combining experimental and molecular simulation techniques N2 - We present a method which allows to calculate gas sorption in complex polymers where, as slow processes, gas induced plasticization and volume dilation are important factors. Since the relaxational swelling of the polymer matrix that is observed at elevated gas concentrations takes hours or days, the swelling process is orders of magnitudes too slow to simulate the respective molecular dynamics in reasonable time and effort. To address this apparent incompatibility of experiment and simulation, we use single representative reference states from experiment and construct atomistic packing models according to these specifications. Gas sorption of CO2 and CH4 was successfully calculated on polysulfone, a 6FDA-polyimide, and a polymer of intrinsic microporosity, PIM-1, at 308 K and pressures up to 50 bar. T2 - MRS Fall Meeting 2008 - Symposium W - Computational Materials Design via Multiscale Modeling CY - Boston, MA, USA DA - 2008-12-01 KW - Gas sorption KW - Molecular modelling KW - Simulation KW - Glassy polymers PY - 2009 DO - https://doi.org/10.1557/PROC-1130-W06-10 VL - 1130 SP - W06 EP - W10 AN - OPUS4-19106 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin T1 - Gas sorption in glassy polymers - Comparative characterization using experimental and molecular modeling techniques T2 - EUROMEMBRANE 2009 Conference CY - Montpellier, France DA - 2009-09-06 PY - 2009 AN - OPUS4-20018 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Böhning, Martin A1 - Hölck, Ole A1 - Heuchel, M. A1 - Hofmann, D. T1 - Characterization of gas sorption in glassy polymers combining experimental and molecular modeling techniques KW - Glassy Polymers KW - Gas Sorption KW - Molecular Modelling KW - Diffusion PY - 2008 SN - 0743-0515 VL - 98 SP - 875 EP - 876 PB - Division of Polymeric Materials Science and Engineering, American Chemical Society CY - Washington, DC AN - OPUS4-17485 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin T1 - Autoclave testing - a new approach for the evaluation of oxidative long-term resistance of geosynthetics T2 - 4th European Geosynthetics Conference CY - Edinburgh, Scotland DA - 2008-09-07 PY - 2008 AN - OPUS4-18295 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin T1 - Gas transport in glassy polymers and PNCs - experiment, analysis, modeling of diffusion, sorption and dilation T2 - Workshop: Polymers, University of Zagreb, Faculty of Mechanical Engineering and Naval Architecture, Laboratory for Non-Metals CY - Zagreb, Croatia DA - 2012-05-23 PY - 2012 AN - OPUS4-25969 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin T1 - Gas transport in glassy polymers and PNCs - experiment, analysis, modeling of diffusion, sorption and dilation T2 - Workshop: Nanostructured and Nanocomposite Membranes for Gas und Vapour Separation CY - Cetraro, Italy DA - 2012-05-15 PY - 2012 AN - OPUS4-26631 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin T1 - Correlation of gas diffusivity and local chain mobility in polycarbonate/POSS nanocomposites as determined by broadband dielectric relaxation spectroscopy T2 - Euromembrane 2012 CY - London, England DA - 2012-09-23 PY - 2012 AN - OPUS4-26629 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin T1 - Kinetic analysis of gas sorption and gas induced dilation and relaxation behaviour of PIM-1 compared to other glassy polymers T2 - Euromembrane 2012 CY - London, England DA - 2012-09-23 PY - 2012 AN - OPUS4-26630 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schartel, Bernhard A1 - Frasca, Daniele A1 - Schulze, Dietmar A1 - Wachtendorf, Volker A1 - Krafft, Bernd A1 - Morys, Michael A1 - Böhning, Martin A1 - Rybak, Thomas T1 - Multilayer graphene rubber nanocomposites N2 - Multilayer Graphene (MLG), a nanoparticle with a specific surface of BET = 250 m²/g and thus made of only approximately 10 graphene sheets, is proposed as a nanofiller for rubbers. When homogenously dispersed, it works at low loadings enabling the replacement of carbon black (CB), increase in efficiency, or reduction in filler concentration. Actually the appropriate preparation yielded nanocomposites in which just 3 phr are sufficient to significantly improve the rheological, curing and mechanical properties of different rubbers, as shown for Chlorine-Isobutylene-Isoprene Rubber (CIIR), Nitrile-Butadiene Rubber (NBR), Natural Rubber (NR), and Styrene-Butadiene Rubber (SBR). A mere 3 phr of MLG tripled the Young’s modulus of CIIR, an effect equivalent to 20 phr of carbon black. Similar equivalents are observed for MLG/CB mixtures. MLG reduces gas permeability, increases thermal and electrical conductivities, and retards fire behavior. The later shown by the reduction in heat release rate in the cone calorimeter. The higher the nanofiller concentration is (3 phr, 5 phr, and 10 phr was investigated), the greater the improvement in the properties of the nanocomposites. Moreover, the MLG nanocomposites improve stability of mechanical properties against weathering. An increase in UV-absorption as well as a pronounced radical scavenging are proposed and were proved experimentally. To sum up, MLG is interesting as a multifunctional nanofiller and seems to be quite ready for rubber development. T2 - TOP 2016, VIII International Conference on “Times of Polymers and Composites” CY - Naples, Italy DA - 19.06.2016 KW - Graphene KW - Nanocomposite KW - Rubber PY - 2016 SN - 978-0-7354-1390-0 DO - https://doi.org/10.1063/1.4949621 SN - 0094-243X SN - 1551-7616 VL - 1736 SP - 020046, 1 EP - 4 PB - AIP AN - OPUS4-36864 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -