TY - CONF A1 - Artinov, Antoni T1 - On the search for the origin of the bulge effect in high power laser beam welding N2 - The shape of the weld pool in laser beam welding plays a major role to understand the dynamics of the melt and its solidification behavior. The aim of the present work was its experimental and numerical investigation. To visualize the geometry of the melt pool in the longitudinal section a butt joint configuration of 15 mm thick structural steel and transparent quartz glass was used. The weld pool shape was recorded by means of a high-speed video camera and two thermal imaging MWIR and VIS cameras. The observations show that the dimensions of the weld pool vary depending on the depth. The regions close to the surface form a teardrop shaped weld pool. A bulge-region and its temporal evolution were observed approximately in the middle of the depth of the weld pool. Additionally, a transient numerical simulation was performed until reaching a steady state to obtain the weld pool shape and to understand the formation mechanism of the observed bulging phenomena. A fixed keyhole with an experimentally obtained shape was used to represent the full-penetration laser beam welding process. The model considers the local temperature field, the effects of phase transition, thermo-capillary convection, natural convection and temperature-dependent material properties up to evaporation temperature. It was found that the Marangoni convection and the movement of the laser heat source are the dominant factors for the formation of the bulging-region. Good correlation between the numerically calculated and the experimentally observed weld bead shapes and the time-temperature curves on the upper and bottom surface were found. T2 - International Congress on Applications of Lasers & Electro-Optics (ICALEO®) CY - Orlando, FL, USA DA - 14.10.2018 KW - High power laser beam welding KW - Solidification cracking KW - Bulging effect KW - Numerical modelling PY - 2018 AN - OPUS4-46339 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Artinov, Antoni T1 - A simplified model for numerical simulation of laser metal deposition process with beam oscillation N2 - A simplified model for the numerical simulation of the laser metal deposition process with beam oscillation is proposed. The model studies circular and lateral oscillations in order to reduce the porosity of the deposited part, to increase the process efficiency and the gap bridging ability as well. The deposition rate is increased by modifying the shape and the width of the molten pool through an optimized laser beam power distribution and oscillation amplitude. The relationship between the process conditions and the shape of the fabricated part are determined. It is found that an increase of the amplitude by a lateral oscillation of the beam reduces the heat flux and hence the shape of the deposited wall. A good correlation between the numerically calculated results and the experimental measurements is obtained. T2 - 9th International Conference on Beam Technologies and Laser Applications CY - St. Petersburg, Russia DA - 17.09.2018 KW - Numerical modelling KW - Laser metal deposition KW - Beam oscillations PY - 2018 AN - OPUS4-46017 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ivanov, Sergei A1 - Artinov, Antoni A1 - Valdaytseva, Ekaterina A1 - Stankevich, Stanislav A1 - Andreevich, Gleb T1 - A simplified model for numerical simulation of laser metal deposition process with beam oscillation N2 - A model of laser metal deposition with beam oscillation has been developed. The proposed model consists of two coupled sub-models calculating the heat transfer in the deposited part and the free surface of the molten pool, respectively. The heat transfer simulation of the deposited part solves a three-dimensional quasi-stationary heat conduction problem. The free surface of the molten pool are determined by solving the Laplace-Young equation. The developed model enables the layer-by-layer prediction of the shape of the deposited part and the resulting temperature field. It is shown that for an oscillation amplitude equal to the beam radius the peak value of the heat flux decreases by about 53% and 73% in the case of lateral oscillation and circular oscillation, respectively. Lateral oscillating laser beam results in a higher penetration depth due to the higher thermal efficiency. The amplitude of the laser beam oscillation effects the shape of the deposited wall and the deposition rate. A good correlation between the numerically calculated and experimentally observed results is obtained. KW - Laser metal deposition KW - Beam oscillation KW - Numerical modelling PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-467081 DO - https://doi.org/10.1088/1742-6596/1109/1/012006 SN - 1742-6588 SN - 1742-6596 VL - 1109 SP - 012006, 1 EP - 8 PB - IOP Publ. CY - Bristol AN - OPUS4-46708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meng, Xiangmeng A1 - Artinov, Antoni A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Numerical study of additional element transport in wire feed laser beam welding N2 - The transport phenomena in the wire feed laser beam welding are investigated numerically. A three-dimensional transient heat transfer and fluid flow model coupled with free surface tracing and element transport is developed. A ray-tracing method with local grid refinement algorithm is used to calculate the multiple reflections and Fresnel absorption on the keyhole wall. The filler material flows backward along the lateral side of the weld pool, and subsequently flows forward along the longitudinal plane. The occurrence of the bulging phenomenon may further prevent the downward transfer of the additional elements to the root of the weld pool. KW - Laser beam welding KW - Element transport KW - Filler wire KW - Numerical modelling PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-513271 DO - https://doi.org/10.1016/j.procir.2020.09.129 VL - 94 SP - 722 EP - 725 PB - Elsevier B.V. AN - OPUS4-51327 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Artinov, Antoni A1 - Bachmann, Marcel A1 - Meng, Xiangmeng A1 - Karkhin, V. A1 - Rethmeier, Michael T1 - On the relationship between the bulge effect and the hot cracking formation during deep penetration laser beam welding N2 - Recent studies have confirmed the widening of the weld pool interface, known as a bulge effect, during deep penetration high power laser beam welding. The link between such geometric particularities of the weld pool shape and the hot cracking phenomena is significant. The present work seeks to extend the level of understanding by investigating their relationship. A coupled multiphysics, multiscale numerical framework is developed, comprising a series of subsequent analyses. The study examines the influences of the bulge on the three most dominant effects causing hot cracking, namely the thermal cycles, the mechanical loading, and the local microstructure. The bulge in the weld pool shape forms approximately in the middle of the plate, thus correlating with the location of hot cracking. It increases the hot cracking susceptibility by enhancing the three dominant effects. The numerical results are backed up by experimental data. T2 - 11th CIRP Conference on Photonic Technologies [LANE 2020] KW - Hot cracking KW - Bulge effect KW - Numerical modelling KW - Laser beam welding KW - Deep penetration PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-512783 DO - https://doi.org/10.1016/j.procir.2020.09.002 SN - 2212-8271 VL - 94 SP - 5 EP - 10 PB - Elsevier B.V. CY - Amsterdam [u.a.] AN - OPUS4-51278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Artinov, Antoni T1 - On the relationship between the bulge effect and the hot cracking formation during deep penetration laser beam welding N2 - Recent studies have confirmed the widening of the weld pool interface, known as a bulge effect, during deep penetration high power laser beam welding. The link between such geometric particularities of the weld pool shape and the hot cracking phenomena is significant. The present work seeks to extend the level of understanding by investigating their relationship. A coupled multiphysics, multiscale numerical framework is developed, comprising a series of subsequent analyses. The study examines the influences of the bulge on the three most dominant effects causing hot cracking, namely the thermal cycles, the mechanical loading, and the local microstructure. The bulge in the weld pool shape forms approximately in the middle of the plate, thus correlating with the location of hot cracking. It increases the hot cracking susceptibility by enhancing the three dominant effects. The numerical results are backed up by experimental data. T2 - 11th CIRP Conference on Photonic Technologies [LANE 2020] CY - Online meeting DA - 07.09.2020 KW - Hot cracking KW - Bulge effect KW - Numerical modelling KW - Laser beam welding KW - Deep penetration PY - 2020 AN - OPUS4-51277 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Artinov, Antoni T1 - Mathematical analysis of the bulging effect in high power laser beam welding of thick steel sheets N2 - The present work is devoted to the mathematical analysis of the bulging effect in high-power laser beam welding of thick steel sheets. The numerical results are based upon experimental results from previous studies, revealing the relationships between the bulging effect, the hot cracking formation, and the distribution of alloying elements in the weld pool. The widening of the molten pool in its middle area is observed for both complete and partial penetration welding of 8 mm - 15 mm thick structural steel sheets. The weld pool shape is extracted from the simulations to evaluate the extent of the necking and bulging of the solidification isotherm and their influence on the hot cracking formation and the mixing behavior of the weld pool. Relying on an earlier numerical study utilizing a fixed keyhole, simulation models considering a dynamic keyhole are developed thereto. The link between the bulge and the studied phenomena is found to be significant. T2 - Beam Technologies & Laser Applications CY - Saint Petersburg, Russia DA - 20.09.2021 KW - Deep penetration laser beam welding KW - Bulge effect KW - Numerical modelling KW - Hot cracking KW - Necking KW - Mixing behavior PY - 2021 AN - OPUS4-53375 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Artinov, Antoni A1 - Bakir, Nasim A1 - Bachmann, Marcel A1 - Gumenyuk, Andrey A1 - Na, S.-J. A1 - Rethmeier, Michael T1 - On the search for the origin of the bulge effect in high power laser beam welding N2 - The shape of the weld pool in laser beam welding plays a major role to understand the dynamics of the melt and its solidification behavior. The aim of the present work was its experimental and numerical investigation. To visualize the geometry of the melt pool in the longitudinal section a butt joint configuration of 15 mm thick structural steel and transparent quartz glass was used. The weld pool shape was recorded by means of a high-speed video camera and two thermal imaging MWIR and VIS cameras. The observations show that the dimensions of the weld pool vary depending on the depth. The regions close to the surface form a teardrop shaped weld pool. A bulge-region and its temporal evolution were observed approximately in the middle of the depth of the weld pool. Additionally, a transient numerical simulation was performed until reaching a steady state to obtain the weld pool shape and to understand the formation mechanism of the observed bulging phenomena. A fixed keyhole with an experimentally obtained shape was used to represent the full-penetration laser beam welding process. The model considers the local temperature field, the effects of phase transition, thermo-capillary convection, natural convection and temperature-dependent material properties up to evaporation temperature. It was found that the Marangoni convection and the movement of the laser heat source are the dominant factors for the formation of the bulging-region. Good correlation between the numerically calculated and the experimentally observed weld bead shapes and the time-temperature curves on the upper and bottom surface were found. T2 - International Congress on Applications of Lasers & Electro-Optics (ICALEO®) CY - Orlando, USA DA - 14.10.2018 KW - Bulging effect KW - High power laser beam welding KW - Numerical modelling KW - Solidification cracking PY - 2019 SP - 1 EP - 8 AN - OPUS4-47139 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -