TY - CONF A1 - Kromm, Arne T1 - Residual stress reduction using LTT welding consumables with focus on the weld geometry N2 - This article focuses on the selective placement of additional LTT layers to generate compressive residual stresses in fatigue-critical areas of conventional weld joints. This enables an economical solution without effecting the integrity of welded joints. For this, longitudinal stiffeners made of high-strength steel were gas metal arc welded using conventional welding consumable in the first layer. Afterwards, a chromium-nickel alloyed LTT welding consumable was deposit on front sides of the stiffeners. By varying the welding parameters, different weld geometries of the LTT filler metal could be analyzed. The effects of additional LTT layers were investigated with regards to residual stresses, microstructure and strength. X-ray residual stresses measurements show that the residual stresses at the failure critical weld toe are significantly reduced by using additional LTT layers. While the conventional weld is characterized by tensile residual stresses, compressive residual stresses can be detected at the LTT weld. The level of residual stresses is influenced by the geometry of the LTT layer. Additional LTT layers with a high offset to the conventional weld generate more compressive residual stress in the HAZ than with a low offset. Therefore, the weld geometry has a considerable impact on the residual stress profile. T2 - IIW Intermediate Meeting Comission II-A CY - Incheon, Republic of Korea DA - 12.03.2024 KW - LTT KW - Residual stress KW - High strength steel PY - 2024 AN - OPUS4-59747 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Hensel, J. A1 - Wandtke, Karsten A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Einfluss von Wärmeführung und Bauteildesign auf die Eigenschaften und fertigungsbedingten Beanspruchungen additiv geschweißter hochfester Feinkornbaustähle N2 - Hochfeste Feinkornbaustähle verfügen über großes Potenzial für gewichtsoptimierte, effiziente Strukturen in vielen modernen Stahlkonstruktion. Weitere Effizienzsteigerungen können durch additives Fertigen sowie bionische Bauweisen erreicht werden. Hochfeste Zusatzwerkstoffe für additives MSG-Schweißen (engl.: Wire Arc Additive Manufacturing, WAAM) sind bereits von den Schweißzusatzherstellern lieferbar. Eine breite industrielle Anwendung insbesondere für KMU ist aufgrund fehlender quantitativer Erkenntnisse und Richtlinien bezüglich schweißbedingter Beanspruchungen und Bauteilsicherheit während der Herstellung und des Betriebs derzeit stark limitiert. In einem gemeinsamen Forschungsprojekt (FOSTA-P1380/IGF21162BG) der BAM und der TU Chemnitz werden daher die mit Eigenspannungsausbildung und der Gefahr einer Kaltrissbildung verbundenen prozess- und werkstoffbedingten sowie konstruktiven Einflüsse beim WAAM hochfester Stähle untersucht. Der vorliegende Beitrag fokussiert die Analyse der Auswirkungen von Schweißwärmeführung und Design der WAAM-Bauteile auf die Abkühlbedingungen, Gefüge, mechanisch-technologischen Eigenschaften und Eigenspannungen. Hierfür werden geometrisch definierte Probenkörper (Hohlquader) vollautomatisiert mit einem speziellen, hochfesten WAAM-Massivdraht (Streckgrenze >790 MPa) geschweißt. Die Wärmeführung und Probenabmessungen werden innerhalb eines statistischen Versuchsplans variiert. Die Schweißwärmeführung wird dabei so eingestellt, dass die t8/5-Abkühlzeiten im empfohlenen Verarbeitungsbereich (ca. 5 s bis 20 s) sichergestellt sind. Hierzu ließen sich über zusätzliche thermo-physikalische Umformsimulationen mittels Dilatometer die komplexen Wärmezyklen abbilden und die resultierende Zugfestigkeit des Schweißgutes bestimmen. Das WAAM-Schweißen komplexer Geometrien mit variierenden Schweißwärmeführungen und geometrischen Verhältnissen bzw. Wanddicken bedingt neben den Auswirkungen auf die Abkühlbedingungen, Abkühlzeiten und Gefüge deutliche Einflüsse auf die konstruktiven Steifigkeitsverhältnisse beim Schweißen. Es zeigen sich anhand der Schweißexperimente signifikante Auswirkungen durch Probenskalierung und Wärmeeinbringung auf die resultierenden lokalen Eigenspannungen. Die Folge können ungünstige Bauteileigenschaften und risskritische Zugeigenspannungen sein. T2 - DVS Congress 2022 CY - Koblenz, Germany DA - 19.09.2022 KW - MAG-Schweißen KW - Additive Fertigung KW - Eigenspannungen KW - Hochfester Stahl KW - Kaltrisssicherheit KW - Wärmeführung KW - Windenergie PY - 2022 SN - 978-3-96144-189-1 VL - 382 SP - 737 EP - 745 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-56719 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Load analyses of welded high-strength steel structures using image correlation and diffraction techniques N2 - In an increasing number of modern steel applications, high-strength structural steel grades are demanded to meet specifications regarding a high load-bearing capacity and a low operating weight. Lightweight design rules enhance the safety requirements, especially for welded joints. Besides a higher cracking risk for high-strength steel welds, the formation of tensile residual stresses might lead to fracture due to overloading or premature failure if not adequately considered. In this study, a stress-strain analysis was conducted at component-related structures from S960QL using digital image correlation while preheating, welding and cooling adjacent to the weld seam. X-ray diffraction analysis of the local residual stresses in the weld seam showed a good comparability with global analyses using either a DIC system or a special testing facility, which allowed in situ measurements of welding loads. By analysing two different seam geometries, it could be shown that lower multi-axial stresses arise if a narrower weld groove is used. Comparative analyses revealed a direct correlation of the local residual stresses in the weld with transverse shrinkage restraint, whereas the residual stress level in the HAZ is significantly affected by the bending restraint of the weld construction and the occurring bending stresses, respectively. KW - Process parameters KW - Residual stresses KW - Restraint KW - GMAwelding KW - High-strength steels PY - 2018 DO - https://doi.org/10.1007/s40194-018-0566-x SN - 0043-2288 SN - 1878-6669 VL - 62 IS - 3 SP - 459 EP - 469 PB - Springer CY - Berlin, Heidelberg AN - OPUS4-44270 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Projektkurzvorstellung: Bewertung konstruktiv bedingter Erstarrungsrisse beim Schweißen hochfester Feinkornbaustähle N2 - Die Integrität von Leichtbaustrukturen aus hochfesten Stählen ist zunehmend durch die Bildung von Heißrissen gefährdet. Aktuell treten Erstarrungsrisse an Konstruktionsmerkmalen auf, obwohl heißrisssichere niedriglegierte Grund- und Zusatzwerkstoffe als auch Schweißprozessbedingungen eingesetzt wurden. Werkstoff- und prozessseitig wurden diese Rissursachen bereits eingehend erforscht. Untersuchungen zum Aspekt der konstruktiv bedingten Heißrissvermeidung, aus denen sich Empfehlungen für ein beanspruchungsgerechtes Gestalten für KMU ableiten lassen, liegen bislang lückenhaft vor bzw. sind veraltet und für hochfeste Leichtbauten kaum zielführend. Konstruktive Gegenmaßnahmen zur Vermeidung von Erstarrungsrissen liegen oft nicht vor. Das Design und die konstruktiven Randbedingungen beeinflussen die Erstarrungsrisse entscheidend. Um eine schnelle Umsetzbarkeit der Resultate für KMU zu ermöglichen, soll eine einfache und kostengünstige Methodik zur Heißrissbewertung entwickelt werden. Gerade KMU haben einen hohen Nachholbedarf an heißrisssicheren und wirtschaftlichen Leichtbaulösungen. Konstrukteure und Anwender aus KMU würden durch fundierte Kenntnisse über mögliche erstarrungsrisskritische Beanspruchungszustände kostenintensive Qualitätsmängel vermeiden. Das Ziel ist es, Kenngrößen zu identifizieren, die während des Schweißens unter realitätsnahen Bedingungen erfasst werden können. Diese Parameter werden als Transfergrößen genutzt, um eine Heißrissbewertung eines geschweißten Bauteils zu ermöglichen. Anliegen des Vorhabens wird die Prüfung und Bewertung von typischen Beanspruchungszuständen beim Schweißen von Leichtbaustrukturen hinsichtlich ihrer Erstarrungsrissneigung sein. Durch Ableitung klassifizierter Gestaltungshinweise wird ein signifikanter Beitrag zur Steigerung der Wettbewerbsfähigkeit insbesondere für KMU geliefert. Die Ergebnisse werden in Normen zur sicheren schweißtechnischen Fertigung von Leichtbaustrukturen aus hochfesten Stählen direkt einfließen. T2 - Sitzung des NA 092-00-05 GA "Gemeinschaftsarbeitsausschuss NAS/NMP: Zerstörende Prüfung von Schweißverbindungen (DVS AG Q 4/Q 4.1)" CY - Online meeting DA - 10.03.2022 KW - Schweißen KW - Erstarrungsrisse KW - hochfester Stahl PY - 2022 AN - OPUS4-54579 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Einfluss spanender Bearbeitungsschritte auf die Eigenspannungen additiv gefertigter Komponenten aus hochfestem Stahl N2 - Diese Studie konzentriert sich auf den Einfluss der Bearbeitung auf die Eigenspannungen und den Verzug von WAAM-Proben. Definierte Proben wurden vollautomatisch mit einem speziellen WAAM-Massivdraht (Streckgrenze >820 MPa) mit unterschiedlichen geometrischen Designs geschweißt. Der Eigenspannungszustand vor und nach dem Abtrennen der AM-Struktur von der Substratplatte wurde mittels Röntgenbeugung an der Probenoberfläche analysiert und durch 3D-Verformungsanalysen mittels Photogrammetrie ergänzt. Die Ergebnisse zeigen einen signifikanten Einfluss der Geometrie auf die Relaxation und Umverteilung der Eigenspannungen. T2 - NA 092-00-05 GA "Gemeinschaftsarbeitsausschuss NAS/NMP: Zerstörende Prüfung von Schweißverbindungen (DVS AG Q 4/Q 4.1) CY - Berlin, Germany DA - 20.03.2024 KW - DED-arc KW - Eigenspannungen KW - Hochfester Stahl PY - 2024 AN - OPUS4-59753 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Increasing the Significance of Varestraint Tests through Improved Crack Evaluation N2 - It was found that there is a systematic dependence of the crack growth on the welding parameters as well as on the load. Decreasing welding speeds with simultaneously higher heat input promote crack formation with increasing strain rate. Based on the results, a new crack criterion was finally selected which allows an extended assessment of the material behavior during the MVT-test. The threshold introduced can quantify the dependencies of the crack formation on the welding and testing parameters, which could not be comprehensively described with the conventional evaluation. In principle, the evaluation routine can also be transferred to other Varestraint or externally loaded hot cracking tests. T2 - IIW Intermediate Meeting Comission II-c CY - Garching, Germany DA - 06.03.2023 KW - Solidification cracking KW - Varestraint-Test PY - 2023 AN - OPUS4-57131 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Kromm, Arne A1 - Mente, Tobias A1 - Brackrock, Daniel A1 - Czeskleba, Denis A1 - Kannengießer, Thomas T1 - Component test for the assessment of delayed hydrogen-assisted cracking in thick-walled SAW joints for offshore applications N2 - Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods, or jackets. These components are typically constructed using submerged arc welding (SAW) with high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen-assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicates the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam/layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled with over 20 passes and a seam length of 1000 mm. Additional welded stiffeners simulated the effect of a high restraint, to achieve critical HAC conditions. The necessity of a minimum waiting time (MWT) before the NDT can be conducted (to exclude HAC) was critically verified by the application of ultrasonic testing of the welded joint at different time-steps of the NDT of up to 48 h after the completion welding. The residual stresses were determined by a robot XRD goniometer. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modeling allowed the qualitative estimation of the hydrogen diffusion in the weld. No noticeable HAC occurrence was identified and confirms the high cracking resistance of the investigated material. Finally, the applicability of the MWT concept should be critically discussed. KW - Hydrogen KW - Cold cracking KW - Minimum Waiting Time KW - Offshore steel grade KW - Component test PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-591981 DO - https://doi.org/10.1007/s40194-023-01658-5 SP - 1 EP - 15 PB - Springer Science and Business Media LLC AN - OPUS4-59198 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Thomas, Maximilian A1 - Kannengießer, Thomas A1 - Gibmeier, Jens T1 - On the interpretation of Varestraint and Transvarestraint hot cracking test results N2 - The Varestraint test and its variant Transvarestraint are one of the most widely used techniques for evaluating a material solidification cracking sensitivity during welding. The result of such tests is a crack length which is proportional to the material’s cracking susceptibility. Nevertheless, the welding and load parameters can unintentionally influence the crack length, which in some cases can distort the material evaluation. An approach is described as to how these effects can be assessed with the aid of a digital crack analysis. The crack lengths are compared position-dependently with their possible propagation due to the weld pool movement during continuous loading. The index derived from this can be used by the operator to evaluate his test parameters. In addition, a comparison of the results of different Varestraint setups is made possible. Alongside experimental results, a numerical sensitivity analysis is presented on how individual welding and loading parameters can affect the crack lengths. KW - Varestraint test KW - Solidification cracking KW - Weldability PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-595089 DO - https://doi.org/10.1007/s40194-024-01706-8 SN - 0043-2288 SP - 1 EP - 13 PB - Springer Science and Business Media LLC AN - OPUS4-59508 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wandtke, Karsten A1 - Schröpfer, Dirk A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Hensel, J. T1 - Fertigungsbedingte Beanspruchungen und Kaltrisssicherheit in generativ gefertigten Bauteilen aus hochfesten Feinkornbaustählen - Kurzdarstellung der Projektergebnisse, FOSTA P1380 N2 - Die Verwendung hochfester Feinkornbaustähle hat für viele Anwendungen des Stahlbaus ein großes Potenzial für gewichtsoptimierte, effiziente Strukturen mit ho-her mechanischer Beanspruchbarkeit. Weitere Zugewinne an Effizienz sind durch generative Fertigungsschritte sowie bionische Bauweisen erzielbar. Hierzu stehen bereits kommerzielle hochfeste drahtförmige Zusatzwerkstoffe für formgebendes MSG-Schweißen zur Verfügung. Dem Einsatz stehen noch fehlende quantitative Aussagen zu den fertigungsbedingten Beanspruchungen und der Bauteilsicherheit während Herstellung und Betrieb im Wege. Dies betrifft insbesondere prozess- sowie materialbedingte Einflüsse und die konstruktive Schrumpfbehinderung verbunden mit der Ausbildung hoher Zugeigenspannungen und damit zusammenhängenden Kaltrissbildung. Hierfür wurden im Projekt detaillierte und anwenderbezogene Kenntnisse zu den komplexen Wechselwirkungen zwischen Schweißprozess und Wärmeführung während der Fertigung, der metallurgischen Vorgänge und insbesondere der vorliegenden konstruktiven Einflüsse auf die entstehenden Eigenspannungen erarbeitet, um ein frühzeitiges Bauteilversagen aufgrund eines hohen fertigungsbedingten Beanspruchungsniveaus bis hin zu einer Rissbildung während der Fertigung sicher zu vermeiden. Gleichzeitig wurden die Einflüsse auf die mechanisch-technologischen Gütewerte systematisch analysiert. Zudem wurden die Auswirkungen trennender Verfahren durch Entfernen der Substratplatte sowie durch die spanende Bearbeitung der Vorformlinge zu Endbauteilgeometrien geklärt, da diese unmittelbar den Eigenspannungszustand beeinflussen und deutlichen Verzug der Bauteile auslösen. Für das generative Schweißen konnten Verarbeitungsempfehlungen sowie Normenvorgaben erarbeitet werden. Dies hilft insbesondere KMU eine wirtschaftliche, beanspruchungsgerechte und risssichere generative Fertigung von Bauteilen aus hochfesten Feinkornbaustählen zu ermöglichen. KW - MAG-Schweißen KW - Additive Fertigung KW - Eigenspannungen KW - Kaltrisssicherheit KW - Hochfester Stahl PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-582198 N1 - Das IGF-Vorhaben IGF-Nr. 21162 BG (P 1380) "Fertigungsbedingte Beanspruchungen und Kaltrisssicherheit in generativ gefertigten Bauteilen aus hochfesten Feinkornbaustählen" der Forschungsvereinigung Stahlanwendung e. V. wurde über die AiF im Rahmen des Programms zur Förderung der Industriellen Gemeinschaftsforschung (IGF) vom Bundesministerium für Wirtschaft und Klimaschutz aufgrund eines Beschlusses des Deutschen Bundestages gefördert. SP - 1 EP - 2 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-58219 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Witte, Julien A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Stresses in repair welding of high-strength steels—part 1: restraint and cold cracking risk N2 - AbstractThe sustainable and resource-efficient production of wind energy plants requires the use of modern high-strength fine-grain structural steels. This applies to both foundation and erection structures, like mobile or ship cranes. During the assembly of steel structures, unacceptable defects can occasionally be found in the weld area. In most cases, the economical solution would be local thermal gouging of the affected areas and re-welding. Due to the high shrinkage restraint of the joint groove in the overall structure, the superposition of global and local welding-induced stresses may lead to crack formation and component failure, particularly in interaction with the degradation of the microstructure and mechanical properties of high-strength steels during the repair process. However, manufacturers hardly have any information about these issues and there is a lack of recommendations and guidelines to take these safety-relevant aspects into account in adequate repair concepts. The aim of this research is to derive recommendations for repair concepts appropriate to the stresses and materials involved providing a basis for standards and guidelines to avoid cold cracking, damage and expensive reworking especially for high-strength steels. Part 1 of this study involves systematic investigations of influences of shrinkage restraint during repair welding of two high-strength steels S500MLO for offshore application and S960QL for mobile crane structures. The quantification of the shrinkage restraint of repair weld joints was achieved by means of experimental and numerical restraint intensity analysis. In welding experiments with self-restrained slot specimens, restraint intensity and introduction of hydrogen via the welding arc using anti spatter spray were varied systematically to analyse the effect on welding result, residual stresses and cold cracking. It could be shown that increasing restraint intensities result in significantly higher transverse residual stress levels. In the case of hydrogen introduction S500MLO showed no cold cracking independent of the restraint conditions. However, S960QL was found to be considerably cold cracking sensitive if hydrogen is introduced. With increasing restraint intensity length and number of cold cracks increases significantly. Part 2 [1] of this study is focussed on microstructure and residual stresses due to gouging and stress optimization via adequate heat control parameters in repair welding. KW - Metals and Alloys KW - Mechanical Engineering KW - Mechanics of Materials PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-595212 DO - https://doi.org/10.1007/s40194-024-01691-y SN - 0043-2288 SP - 1 EP - 13 PB - Springer Science and Business Media LLC AN - OPUS4-59521 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Witte, Julien A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Stresses in repair welding of high-strength steels—part 2: heat control and stress optimization N2 - In welding of high-strength steels, e.g. for foundations and erection structures of wind energy plants, unacceptable defects can occasionally be found in the weld area, which should be removed by thermal gouging and subsequent re-welding. High shrinkage restraint of repair welds may lead to crack formation and component failure, predominantly in interaction with degraded microstructures and mechanical properties due to repair cycles. This study aims for elaboration of recommendations for repair concepts appropriate to the stresses and materials involved to avoid cold cracking, damage and expensive reworking. In part 1 [1] of this study, systematic investigations of influences of shrinkage restraint on residual stresses and cold cracking risk during repair welding of two high-strength steels S500MLO for offshore application and S960QL for mobile crane structures were focussed. In this part 2, the microstructure, particularly hardness, and residual stresses due to gouging and influences of heat control parameters in repair welding are analysed. A clear reduction in residual stress after gouging can be observed, especially for the specimens with restrained transverse shrinkage. Gouging to a depth of approx. 2/3 of the seam height does not lead to a complete relaxation of the observed reaction forces. Particularly for the higher strength steel S960QL, there are pronounced areas influenced by the gouging process in which a degradation of the microstructure and properties should be assumed. Overall, the repair welds show a significant increase in the width of the weld and HAZ compared to the original weld, especially in the case of S960QL/G89. The repair welds show higher welding-induced stresses than the original welds, especially in the areas of the HAZ and the base metal close to the weld seam. This behaviour can be attributed overall to increased restraint conditions due to the remaining root weld or shorter gouge grooves. In good agreement with earlier investigations, the residual stresses transverse to the weld can be significantly reduced by upwardly limited working or interpass temperatures, and the reaction stresses resulting from high restraint conditions can be effectively counteracted. The influence of the heat input on the stress formation is low compared to the interpass temperature for both test materials. KW - Repair-welding KW - Wind Energy KW - High-strength steels KW - Cold cracking KW - Residual stresses KW - Offshore steels PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600259 DO - https://doi.org/10.1007/s40194-024-01731-7 SN - 0043-2288 SP - 1 EP - 15 PB - Springer Nature AN - OPUS4-60025 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Quackatz, Lukas A1 - Westin, Elin Marianne A1 - Griesche, Axel A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Treutler, Kai A1 - Wesling, Volker A1 - Wessman, Sten T1 - Assessing ferrite content in duplex stainless weld metal: WRC ‘92 predictions vs. practical measurements N2 - AbstractThe weldability of stainless steels is largely controlled by the chemical composition, and alloys with ferritic or ferritic-austenitic solidification show the highest resistance to hot cracking. As the resulting phase balance also affects the final properties, it may be beneficial to both foresee and measure the weld metal ferrite content. The WRC ‘92 constitution diagram is currently the most accurate prediction tool available, but it does not take the cooling rate into consideration and the precision may be less accurate for stainless steels with high ferrite numbers (FNs). This study aims to assess the reliability of the WRC ‘92 diagram for weld metals with FN  50. The chemical composition was altered through gas tungsten arc welding (GTAW) of UNS S32205 with ER347 filler wire that had been coated using physical vapor deposition (PVD) with either niobium (Nb), copper (Cu), nickel (Ni), manganese (Mn), carbon (C), or silicon (Si). The actual ferrite content was evaluated using image analysis, FeriteScope and X-ray diffraction (XRD). While predictions from the WRC ‘92 diagram were deemed acceptable for Ni, Si, and Mn, notable deviations were observed for Nb, Cu, and C. The FeriteScope exhibited a consistent trend with image analysis, albeit with slightly higher FN values, wider scatter, and the conversion factor from FN to vol% is open for discussion. The lowest accuracy and largest spread were obtained using non-contact XRD, rendering it unsuitable for ferrite measurements of welds. These findings underscore the need for improved prediction tools and appropriate measurement methods for assessing ferrite content in duplex weld metals. KW - Duplex stainless steel KW - Welding KW - Phase balance KW - Microscopy KW - Microstructure PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-618777 DO - https://doi.org/10.1007/s40194-024-01878-3 SN - 1878-6669 VL - 69 IS - 1 SP - 31 EP - 45 PB - Springer CY - Berlin AN - OPUS4-61877 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Quackatz, Lukas A1 - Westin, Elin Marianne A1 - Griesche, Axel A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Treutler, Kai A1 - Wesling, Volker A1 - Wessman, Sten T1 - Assessing ferrite content in duplex stainless weld metal: WRC ‘92 predictions vs. practical measurements N2 - AbstractThe weldability of stainless steels is largely controlled by the chemical composition, and alloys with ferritic or ferritic-austenitic solidification show the highest resistance to hot cracking. As the resulting phase balance also affects the final properties, it may be beneficial to both foresee and measure the weld metal ferrite content. The WRC ‘92 constitution diagram is currently the most accurate prediction tool available, but it does not take the cooling rate into consideration and the precision may be less accurate for stainless steels with high ferrite numbers (FNs). This study aims to assess the reliability of the WRC ‘92 diagram for weld metals with FN  50. The chemical composition was altered through gas tungsten arc welding (GTAW) of UNS S32205 with ER347 filler wire that had been coated using physical vapor deposition (PVD) with either niobium (Nb), copper (Cu), nickel (Ni), manganese (Mn), carbon (C), or silicon (Si). The actual ferrite content was evaluated using image analysis, FeriteScope and X-ray diffraction (XRD). While predictions from the WRC ‘92 diagram were deemed acceptable for Ni, Si, and Mn, notable deviations were observed for Nb, Cu, and C. The FeriteScope exhibited a consistent trend with image analysis, albeit with slightly higher FN values, wider scatter, and the conversion factor from FN to vol% is open for discussion. The lowest accuracy and largest spread were obtained using non-contact XRD, rendering it unsuitable for ferrite measurements of welds. These findings underscore the need for improved prediction tools and appropriate measurement methods for assessing ferrite content in duplex weld metals. KW - Duplex stainless steel KW - Phase fraction prediction KW - WRC diagram PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-623682 DO - https://doi.org/10.1007/s40194-024-01878-3 VL - 69 SP - 31 EP - 45 PB - Springer Science and Business Media LLC AN - OPUS4-62368 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Liepold, Philipp A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Transvarestraint testing of high-strength steel filler metal N2 - High-strength steel welds are typically not known to be susceptible to Solidification Cracking (SC). However, modern light-weight constructions may force welding in highly restrained conditions, which are known to increase the probability of Solidification Crack (SC) emergence. In this article, the Modified Varestraint-Transvarestraint (MVT) test was used to evaluate the hot cracking susceptibility of welds made from high-strength, low-alloyed filler material. The materials tested include solid wires and a metal-cored wire. All wires are typically used in the Gas Metal Arc Welding (GMAW) process. Susceptibility to SC was measured over a wide range of welding parameters and bending speeds. Results show little affinity of the tested materials to SC. However, crack length increases in most cases with arc energy ( U ∙ I∕welding speed ) and welding speed. The length of the longest crack in one test specimen follows a similar trend until high welding speeds, where stagnation of crack length with changing arc energy was observed. KW - MVT KW - Varestraint KW - Transvarestraint KW - Solidification cracking KW - High-strength steel PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630084 DO - https://doi.org/10.1007/s40194-025-02042-1 SN - 1878-6669 VL - 2025 SP - 1 EP - 12 PB - Springer CY - Berlin ; Heidelberg AN - OPUS4-63008 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Influence of residual stresses and heat control on stress relief cracking in a CrMoV steel mockup N2 - Preventing failures in the manufacture or operation of petrochemical reactors made from creep-resistant, low-alloy steels such as 13CrMoV9-10 still requires research, despite over 60 years of investigation into the field of stress relief cracking. Welding this steel grade requires care. This is due to its low toughness and high strength in the welded condition if not heat treated after welding, combined with an increased susceptibility to cracking during stress relaxation. Previous research on cracking in creep resistant steels has focused on thermal and metallurgical factors; however, little knowledge has been gained on cracking under real-life restraint conditions. In this work, the influence of welding heat control on cracking was investigated by simulating the manufacturing conditions prevailing in the construction of petrochemical reactors using a special weld mockup. The application of acoustic emission analysis showed that cracks formed during post-weld heat treatment in a temperature range between 300 °C and 500 °C. Compared to small scale samples, the toughness of the restrained welds was significantly lower. SEM and TEM analyses of all samples revealed early ageing due to early precipitation of special carbides during post-weld heat treatment under restraint. Neutron diffraction experiments showed that the residual stresses in the weld seam reach the yield point of the material. The presentation provides an overview of how a comprehensive assessment of the integrity of submerged arc welded CrMoV steels can be achieved in the laboratory. T2 - Cracking Phenomena in Welding and Additive Manufacturing 2025 CY - Trollhättan, Sweden DA - 12.03.2025 KW - CrMoV KW - Stress Relief Cracking KW - Sub-merged arc welding PY - 2025 AN - OPUS4-62783 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Optimization of welding loads with narrow groove and application of modified spray arc process N2 - Current efforts for lightweight design result in a growing application of high-strength fine-grained structural steel in modern constructions, e.g. mobile cranes, with yield strength from 960 MPa. The design of welded structures and welding processes becomes more challenging with increasing material strength and elastic ratios. High residual stresses are able to diminish lifetime, load capacity and component safety and should be avoided. Recent analyses have shown strong influences of heat control and restraint of the weld due to arising reaction stresses, superimposing with local residual welding stresses. Modern inverter technologies allowed the development of numerous modified spray arc processes driven by power source manufacturers, which provide virtually similar features and several benefits, enabling welding of narrower seams with reduced weld volumes and total heat inputs. This research focuses on welding loads due to modified weld seams. The global reaction forces and moments and their superposition with local residual stresses in welded components due to external shrinkage restraints were investigated using a special testing facility and XRD. The restraint intensity, weld seam geometry and welding process were varied for statistical evaluations of resulting welding loads. When welding under restraint, a reduction of the weld seam volume causes significantly lower reaction stress levels. KW - Residual stresses KW - MAG welding KW - Restraint KW - High-strength steels KW - Process parameters PY - 2017 DO - https://doi.org/10.1007/s40194-017-0484-3 SN - 1878-6669 SN - 0043-2288 VL - 61 IS - 6 SP - 1077 EP - 1087 PB - Springer CY - Berlin Heidelberg AN - OPUS4-41071 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Investigation of restraint intensity influence on solidification cracking of high-strength filler materials in fillet welds via CTS testing N2 - Next to chemical composition, metallurgy and welding parameters, the intensity of restraint is one of the variables influencing solidification cracking. Tests like the Houldcroft Test, rate the hot cracking susceptibility indirectly on the amount of restraint the welding can endure without cracking. Modern lightweight steel construction welds can be subject to a larger amount of restraint due to their high-strength nature compared to classical use cases. By varying the plate thickness of Controlled Thermal Severity (CTS) tests produced out of S1100 QL, it was possible to vary the intensity of restraint on fillet welds at a high level. Testing was conducted with four different filler wires for Metal Active Gas (MAG) welding, including three solid and one metal-cored wire. In addition, two sets of welding parameters were tested. The first set with high heat input and high welding speed was shown to be more prone to solidification cracking compared to the second set with lower heat input and welding speed. The results show an increase in solidification cracking with increasing restraint severity. T2 - IIW Intermediate Meeting Comission II-A CY - Incheon, Republic of Korea DA - 12.03.2024 KW - Solidification cracking KW - High strength steel KW - Weldability PY - 2024 AN - OPUS4-59748 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reichel, Levin A1 - Kromm, Arne A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Moderne Schweißverfahren zur Optimierung von Reparaturschweißungen an hochfesten Offshore-Stählen N2 - The successful energy transition in Germany will require offshore wind turbines with outputs >10 MW in the future, for which high-strength steels with a yield strength of up to 500 MPa and wall thicknesses up to 150 mm are increasingly being used. The repair of weld seams when detecting defects during NDT requires local-ized gouging and rewelding. This involves high demands on welding manufacturing, especially for high-strength steels. Due to a lack of investigations, there are no re-pair concepts and information in standards and guidelines, particularly for high-strength thick plate joints made of high-strength offshore steels. However, these are urgently needed to enable processors, especially SMEs, to carry out safe and eco-nomical repairs. Therefore, BAM started the FOSTA project P1629 (IGF 01IF22746N) to investigate the stress-optimized repair (local gouging and welding) of high-strength thick plate joints made of offshore grades in the yield strength range off 355 to 460 MPa and similar weld metal with controlled high-performance GMAW processes and optimized narrower gouging grooves. The experimental analyses consider the complex interaction of material, process, and design-related influences on the formation of weld-related stresses and the special microstructure of high-strength fine-grain structural steels. Welding-related material degradation and crack-critical residual tensile stresses need to be avoided to ensure high component safety and performance. With component-related welding experiments on special testing equipment, adapted process and heat control concepts along with variable groove configurations will be developed and recommendations for guidelines elabo-rated. This is the prerequisite for fully utilizing the strength potential of high-strength steels and making a valuable contribution to the energy transition in Germany, espe-cially for steel-processing SMEs. T2 - Symposium Materialtechnik TU Clausthal CY - Clausthal-Zellerfeld, Germany DA - 19.02.2025 KW - Reparaturschweißen KW - Thermisches Ausfugen KW - Offshore KW - Sprühlichtbogen KW - Eigenspannungen PY - 2025 AN - OPUS4-62630 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Influence of Residual Stresses on Stress Relief Cracking of Thick Walled Creep Resistant Steel Welds N2 - Controlling the residual stress level during welding of creep-resistant Cr-Mo-V steels is crucial to avoid so called stress relief cracking (SRC) during post weld heat treatment (PWHT) of large-scale components. In the present study, a laboratory scale test specimen (400 mm x 400 mm x 25 mm) was used to simulate thick-walled component welds made of 13CrMoV9-10. The aim was to identify the level and distribution of residual stresses to evaluate the suitability of the specimen for laboratory based SRC testing. High restraint was ensured by the specimen geometry with a narrow welding gap in the center. This gap was filled by submerged arc welding in a multi-layer technique. Two specimens were welded with identical parameters and compared in the as-welded state and after PWHT (705 °C for 10 h). Neutron diffraction was used to determine the residual stresses in the weld metal, the heat-affected zone (HAZ) and the base material at different depths longitudinal, transverse, and normal to the welding direction. The experiments were performed on the instrument E3 of the research reactor BERII of HZB Berlin, Germany. Complementarily, laboratory X-ray diffraction was applied to characterize the surface residual stresses. In the welded state, especially in the weld metal and the adjacent HAZ, the residual stress can reach the yield strength of the untreated material. The highest levels occur in the longitudinal direction. The transverse and normal directions are characterized by residual stress of lower magnitude. As expected, the residual stress is almost completely relieved after PWHT. T2 - International Conference on Residual Stresses ICRS-11 CY - Nancy, France DA - 27.03.2022 KW - Welding KW - Creep-resistant steel KW - Stress relief cracking KW - Residual stress KW - Post weld heat treatment PY - 2022 AN - OPUS4-54577 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Assessing ferrite content in duplex stainless steel weld metals: WRC '92 predictions vs. practical measurements N2 - The weldability of stainless steels is largely controlled by the chemical composition, and alloys with ferritic or ferritic-austenitic solidification show the highest resistance to hot cracking. As the resulting phase balance also affects the final properties, it may be beneficial to both foresee and measure the weld metal ferrite content. The WRC ’92 constitution diagram is currently the most accurate prediction tool available, but it does not take the cooling rate into consideration and the precision may be less accurate for stainless steels with high ferrite numbers (FN). This study aims to validate the reliability of the WRC ’92 diagram for weld metals with FN > 50. The chemical composition was altered through gas tungsten arc welding (GTAW) of UNS S32205 with ER347 filler wire that had been PVD-coated with either niobium (Nb), copper (Cu), nickel (Ni), manganese (Mn), carbon (C), or silicon (Si). The actual ferrite content was assessed using image analysis, FERITSCOPE® and X-ray diffraction (XRD). While the WRC ’92 diagram predictions were deemed accurate to acceptable for Ni, Si, and Mn, notable deviations were observed for Nb, Cu, and C. The FeriteScope exhibited a consistent trend with image analysis, though the values were higher, and scatter was wider, and the conversion factor is open for discussion. The lowest accuracy and largest spread were obtained using non-contact XRD, rendering it unsuitable for ferrite measurements of welds. T2 - IIW Intermediate Meeting Comission IX-H CY - Incheon, Republic of Korea DA - 12.03.2024 KW - Duplex Stainless Steel KW - Ferrite KW - WRC 92 PY - 2024 AN - OPUS4-59750 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Dixneit, Jonny A1 - Dilger, K. A1 - Nitschke-Pagel, T. A1 - Hensel, J. A1 - Eslami, H. T1 - Schwingfestigkeitsverbesserung hochfester Schweißverbindungen mit Hilfe neuartiger LTT-Zusatzwerkstoffe N2 - Die Verwendung von LTT-Zusatzwerkstoffen stellt einen alternativen Ansatz zu den sonst üblichen Verfahren der Schweißnahtnachbehandlung zur Schwingfestigkeitserhöhung geschweißter Stahlkonstruktionen dar. Der wesentliche Wirkmechanismus beruht auf der Beeinflussung des Eigenspannungszustands durch die niedrige Martensitstarttemperatur bereits während des Schweißens. Dadurch werden die Druckeigenspannungen aus der behinderten Volumenausdehnung infolge Phasenumwandlung voll wirksam. Weiter weist die Schweißnaht eine hohe Härte auf, die die Schwingrissbildung verzögern kann, allerdings auch zu einer niedrigen Kerbschlagarbeit führt. Im vorliegenden Forschungsvorhaben wurden grundlegende Untersuchungen zur schweißtechnischen Verarbeitung eines LTT-Zusatzwerkstoffes durchgeführt. Dies beinhaltet die Sicherstellung der Schweißbarkeit sowie die Charakterisierung der Verbindungseigenschaften. Untersuchungen zur Schweißeignung machten deutlich, dass ein sicherer Einsatz in dem für hochfeste Stähle zur Verfügung stehenden Arbeitsfenster möglich ist. Der verwendete LTT-Zusatz auf Cr-Ni-Basis lässt sich mit hoher Nahtgüte fügen. Auch die mechanischen Eigenschaften erlauben den Einsatz im Bereich hochfester Stähle mit einer Streckgrenze von 960 MPa. Entwicklungspotential gibt es hinsichtlich der Zähigkeit. Die in dieser Arbeit erreichten Kerbschlagwerte liegen deutlich unter denen kommerziell verfügbarer konventioneller Schweißgüter. Die Untersuchungen belegen, dass der Effekt der martensitischen Phasenumwandlung im gesamten Schweißgut zum Tragen kommt. Die angestrebten hohen Druckeigenspannungen finden sich vornehmlich im Schweißgutinnern. Im weiteren Vorgehen wurden Schwingfestigkeitsuntersuchungen an den Stählen S355J2 und S960Q unter Verwendung konventioneller Zusatzwerkstoffe im Vergleich zum LTT-Zusatz durchgeführt. Die verwendeten Konstruktionsdetails sind ein Stumpfstoß unter Variation der Schweißnahtausführung (DY-Naht und V-Naht), ein Kreuzstoß mit HV-Naht sowie ein Überlappstoß mit einseitig und beidseitig geschweißter Kehlnaht. Weitergehend wurde eine bauteilähnliche Probe (die Längssteife) untersucht, bei der der LTT-Zusatzwerkstoff als zusätzliche Schweißlage aufgebracht wurde. Neben der Schwingfestigkeit wurden die Schweißnähte hinsichtlich der Eigenspannungen, der Eigenspannungsstabilität im Schwingversuch sowie metallografisch charakterisiert. Eine generell positive Wirkung des LTT-Zusatzwerkstoffes im Hinblick auf die Schwingfestigkeitssteigerung kann nicht bestätigt werden. Teilweise ist eine Steigerung der Schwingfestigkeit bei Substitution konventioneller Zusatzwerkstoffe zu beobachten, teilweise zeigt sich kein Effekt. Ursächlich hierfür ist die bei manchen Stoßformen mangelnde Steifigkeit quer zur Schweißnaht, die zur Ausbildung hoher Druckeigenspannungen infolge Phasenumwandlung notwendig wäre. Die bauteilähnliche Längssteife bestätigt allerdings das grundlegende Potential der LTT-Zusatzwerkstoffe bei Vorliegen hinreichender Steifigkeit. KW - Schweißen KW - Eigenspannungen KW - Schwingfestigkeit KW - Hochfester Stahl KW - LTT PY - 2020 UR - https://matplus.shop/produkt/p-1060-schwingfestigkeitsverbesserung-hochfester-schweissverbindungen-mit-hilfe-neuartiger-ltt-zusatzwerkstoffe SN - 978-3-946885-75-7 VL - P 1060 SP - 1 EP - 123 PB - Verlag und Vertriebsgesellschaft CY - Düsseldorf AN - OPUS4-51216 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Influence of Residual Stresses on Stress Relief Cracking of Thick-Walled Creep-Resistant Steel Welds N2 - Controlling the residual stress level during welding of creep-resistant Cr-Mo-V steels is crucial to avoid so called stress relief cracking (SRC) during post weld heat treatment (PWHT) of large-scale components. In the present study, a laboratory scale test specimen (400 mm x 400 mm x 25 mm) was used to simulate thick-walled component welds made of 13CrMoV9-10. The aim was to identify the level and distribution of residual stresses to evaluate the suitability of the specimen for laboratory based SRC testing. High restraint was ensured by the specimen geometry with a narrow welding gap in the center. This gap was filled by submerged arc welding in a multi-layer technique. Two specimens were welded with identical parameters and compared in the as-welded state and after PWHT (705 °C for 10 h). Neutron diffraction was used to determine the residual stresses in the weld metal, the heat-affected zone (HAZ) and the base material at different depths longitudinal, transverse, and normal to the welding direction. The experiments were performed on the instrument E3 of the research reactor BERII of HZB Berlin, Germany. Complementarily, laboratory X-ray diffraction was applied to characterize the surface residual stresses. In the welded state, especially in the weld metal and the adjacent HAZ, the residual stress can reach the yield strength of the untreated material. The highest levels occur in the longitudinal direction. The transverse and normal directions are characterized by residual stress of lower magnitude. As expected, the residual stress is almost completely relieved after PWHT. T2 - AJP 2023 3rd International Conference on Advanced Joining Processes CY - Braga, Portugal DA - 19.10.2023 KW - Residual stress KW - Creep-resistant steel KW - Stress relief cracking KW - Neutron diffraction PY - 2023 AN - OPUS4-58646 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dixneit, Jonny A1 - Kromm, Arne A1 - Hannemann, Andreas A1 - Friedersdorf, Peter A1 - Kannengießer, Thomas A1 - Gibmeier, J. T1 - In-situ load analysis in multi-run welding using LTT filler materials N2 - Modifying the level of mostly detrimental welding residual stresses already during the welding process would be highly attractive as time- and cost-consuming post processing may be prevented. The nature of stress buildup during welding-associated cooling is highly affected by phase transformations. Up to now, it is not clear in which way this is applicable to real component welding exhibiting high shrinkage restraint and complex heat input. In this study, two different low transformation temperature (LTT) alloys have been investigated concerning the stress development in restrained multi-run butt welding in order to evaluate the potential of stress reduction. Pulsed gas metal arc welding (P-GMAW) welding was executed on a testing facility designed to simulate real lifelike restraint conditions of component weldments. The effect of reducedMS-temperatures and the heat control on the globally acting stresses was monitored by in-situ measurement of the reaction forces during welding fabrication. Additional local residual stress measurements allowed analyzing global as well as local loading of the welded construction. Although phase transformation has a significant influence on unloading the joint during each weld pass, the reaction stress upon cooling to room temperature seems to be determined mainly by the heat input. On the surface, low longitudinal residual stresses were observed in case of LTT whereas transverse residual stresses are less affected. T2 - 69th IIW Annual Assembly and International Conference CY - Melbourne, Australia DA - 10.07.2016 KW - Phase transformation temperature KW - Residual stress KW - Welding KW - Dilution KW - Restraint PY - 2016 DO - https://doi.org/10.1007/s40194-016-0373-1 SN - 0043-2288 VL - 60 IS - 6 SP - 1159 EP - 1168 PB - Springer CY - Heidelberg AN - OPUS4-37892 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Observation of martensite formation by combined use of synchrotron diffraction and dilatometry N2 - Welding residual stress engineering by means of an adjusted martensite phase transformation would be highly attractive as detrimental tensile residual stresses may be prevented already during welding without time and cost intensive post processing. The present study shows a synchrotron diffraction analysis of a martensitic steel subjected to thermo-mechanical load cycles. Experiments were conducted regarding the microstructural strain response during the austenite to martensite transformation. The strains are a function of the temperature and the specific loads applied during cooling. The relation between the transformation plasticity of the material, the amount of martensite formed and the arising strains can thus be assessed. The lattice plane specific strains were compared to experimental findings from (macro) dilatation tests. It is shown that the microscopic material behavior differs remarkably from the one observed on the macroscopic scale, what leads to characteristic residual stresses in the material. T2 - Material Science & Technology (MS&T16) 3rd International Workshop of In-situ Studies with Photons, Neutrons and Electrons Scattering CY - Salt Lake City, UT, USA DA - 23.10.2016 KW - Residual stress KW - Martensite KW - Dilatometry KW - Synchrotron diffraction KW - Neutron diffraction PY - 2016 AN - OPUS4-37999 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Optimierung schweißbedingter Beanspruchungen an Bauteilen aus hochfesten feinkornbaustählen beim Einsatz modifizierter Sprühlichtbogenprozesse N2 - Im Forschungsprojekt wurden unter gezielter definierter Schrumpfbehinderung Schweißexperimente an hochfesten Feinkornbaustählen durchgeführt, um den Einfluss der Wärmeführung sowie den Einsatz modifizierter Sprühlichtbogenprozesse verbunden mit schmaleren Nahtfugen auf die lokalen Eigenspannungen und die Gesamteigenbeanspruchungen an geschweißten Bauteilen zu analysieren. In dem Vortrag wurden für das IGF-Vorhaben 17978 N "Bauteilbeanspruchung modifizierter Sprühlichtbögen" die wesentlichen Zusammenhänge zu schweißbedingten Beanspruchungen an hochfesten Schweißverbindungen sowie einige der erarbeiteten Erkenntnisse und erreichten Ziele des Forschungsprojektes in Bezug auf die wasserstoffunterstützte Kaltrissbildung vorgestellt. T2 - Sitzung AG Q4.1 Wasserstoffunterstützte Rissbildung CY - Duisburg, Germany DA - 15.03.2016 KW - Modifizierter Sprühlichtbogen KW - Eigenspannungen KW - MAG-Schweißen KW - Hochfeste Feinkornbaustähle KW - Einspannung KW - Röntgendiffraktometrie KW - Schweißprozessparameter PY - 2016 AN - OPUS4-38791 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - Characterising phase transformations of different LTT alloys and their effect on residual stresses and cold cracking N2 - Novel martensitic filler materials with specially adjusted martensite start temperatures (Ms) can counteract the cooling specific shrinkage due to expansion effects of the weld metal associated with phase transformations. That can be exploited to create compressive residual stresses in the weld and adjacent areas, i.e. beneficial for increasing fatigue strength. The Ms temperature is shifted via the chemical composition, mainly by the alloying elements nickel and chromium, resulting as well in different retained austenite contents. Investigations were made using different Low Transformation Temperature (LTT) alloys with varying nickel content. The resulting phase transformation temperatures were – for the first time – detected using high energy synchrotron diffraction and Single Sensor Differential Thermal Analysis (SS-DTA). Compared to angle dispersive diffraction, energy dispersive diffraction offers the possibility to measure residual stresses of the martensite and austenite phase parallel fast in one experiment up to depths of 100 µm. The residual stresses show significant distributions dependent on Ms temperature. The effect on the cold cracking behaviour of these alloys was investigated using the Tekken test. Results show that cold cracking can be avoided when appropriate contents of retained austenite are existent. KW - Austenite KW - Cold cracking KW - Martensite KW - Low themperature KW - Transformation PY - 2011 DO - https://doi.org/10.1007/BF03321286 SN - 0043-2288 VL - 55 IS - 3 SP - 48 EP - 56 PB - International Institute of Welding CY - France AN - OPUS4-38978 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Engineering approach to assess residual stresses in welded components N2 - Present trends to lightweight design lead to an expanding relevance of high-strength fine-grained structural steels especially in mobile crane constructions. With growing material strength, the challenge for welding fabrication increases, since high loading capacities and safety requirements have to be accomplished. The utilisation of the high strength potential often requires complex constructions associated with high restraint conditions while welding. Increased residual stresses may occur due to superimposing reaction and restraint stresses, which have to be quantified and evaluated to ensure the safety and integrity of high-strength steel constructions. Particularly, the scope of residual stresses has to be taken into account for different effects in the HAZ, notches, weld and base metal. Commonly, conservative assumptions of residual stresses lead to distinct underestimations of the load bearing capacity particularly for welded high-strength steel constructions. This study concludes results of recent works of the researchers regarding the complex interaction among heat control, material and restraint intensity on the residual stress state in welded components. These analyses are extended by further experiments. Based on the obtained major effects, an approach for a welding residual stress assessment regarding component design according to prevailing standards for crane construction, an important application for high-strength steels, is presented. KW - Process parameters KW - Residual stresses KW - MAG welding KW - Restraint KW - High-strength steels PY - 2017 DO - https://doi.org/10.1007/s40194-016-0394-9 SN - 0043-2288 SN - 1878-6669 VL - 91 IS - 1 SP - 91 EP - 106 PB - Springer CY - Berlin, Heidelberg AN - OPUS4-39044 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Influence of machining on residual stresses in additive manufactured high-strength steel components N2 - This study focuses on the effect of machining on the residual stresses and distortion of WAAM specimens. Defined specimens were welded fully automatically with a special WAAM solid wire (yield strength >820 MPa) with different geometric designs. The residual stresses state before and after cutting of the AM structure from the substrate plate were analyzed by means of X-ray diffraction on the specimen surface and complementary by 3d deformation analyses using photogrammetry. The results reveal significant influences of the geometry on the relaxation and redistribution of residual stresses. T2 - IIW Intermediate Meeting Comission IX-AM CY - Incheon, South Korea DA - 12.03.2024 KW - Residual stress KW - DED-arc KW - High strength steel PY - 2024 AN - OPUS4-59751 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Einfluss der Schweiß- und Prüfparameter bei der Heißrissbewertung hochfester Schweißzusatzwerkstoffe N2 - Die Heißrissneigung beim Schweißen kann mittels einer ganzen Reihe von Prüfverfahren ermittelt werden. Eine etablierte Methode ist die sogenannte Varestraint-Prüfung, welche auch an der Bundesanstalt für Materialforschung und -prüfung (BAM) als modifizierter Varestraint/Transvarestraint-Test (MVT) zum Einsatz kommt. Die Ergebnisse von Varestraint-Prüfungen hängen jedoch stets in unterschiedlichem Maße von der individuellen Prüfmaschinenauslegung und den verwendeten Prüfparametern ab. Dies kann zu einer uneinheitlichen Bewertung des Rissverhaltens führen, wenn die Risslänge konventionell als Kriterium für die Rissneigung herangezogen wird. Scheinbare Abhängigkeiten von Prozessparametern erschweren dann die Interpretation der Ergebnisse. Eine neuartige Bewertungsmethodik entkoppelt den Maschineneinfluss vom Materialverhalten und verwendet die Dehnrate als Risskriterium in Analogie zu Prokhorovs Heißrissmodell. Die neue Auswertung wird anhand einer Studie hochfester Schweißzusatzwerkstoffe vorgestellt, deren Rissverhalten in Abhängigkeit der chemischen Zusammensetzung und der Schweißparameter bewertet wird. T2 - 5. Symposium Materialtechnik CY - Clausthal-Zellerfeld, Germany DA - 23.02.2023 KW - Heißrisse KW - Varestraint-Test KW - Materialprüfung PY - 2023 AN - OPUS4-57070 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wandtke, Karsten A1 - Schröpfer, Dirk A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Hensel, J. T1 - Influence of the WAAM process and design aspects on residual stresses in high-strength structural steels N2 - Wire arc additive manufacturing (WAAM) enables the efficient production of weight-optimized modern engineering structures. Further increases in efficiency can be achieved by using high-strength structural steels. Commercial welding consumables for WAAM are already available on the market. Lack of knowledge and guidelines regarding welding residual stress and component safety during production and operation leads to severely limited use for industry applications. The sensitive microstructure of high-strength steels carries a high risk of cold cracking; therefore, residual stresses play a crucial role. For this reason, the influences of the material, the WAAM process, and the design on the formation of residual stresses and the risk of cold cracking are being investigated. The material used has a yield strength of over 800 MPa. This strength is adjusted via solid solution strengthening and a martensitic phase transformation. The volume expansion associated with martensite formation has a significant influence on the residual stresses. The focus of the present investigation is on the additive welding parameters and component design on their influence on hardness and residual stresses, which are analyzed by means of X-ray diffraction (XRD). Reference specimens (hollow cuboids) are welded fully automated with a systematic variation of heat control and design. Welding parameters and AM geometry are correlated with the resulting microstructure, hardness, and residual stress state. Increased heat input leads to lower tensile residual stresses which causes unfavorable microstructure and mechanical properties. The component design affects heat dissipation conditions and the intensity of restraint during welding and has a significant influence on the residual stress. KW - DED-arc KW - Additive manufacturing KW - High-strength steel filler metal KW - Residual stress PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-572698 DO - https://doi.org/10.1007/s40194-023-01503-9 SN - 1878-6669 VL - 67 IS - 4 SP - 987 EP - 996 PB - Springer CY - Berlin AN - OPUS4-57269 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Optimierung schweißbedingter Beanspruchungen an Bauteilen aus hochfesten Feinkornbaustählen durch Wärmeführung N2 - Höherfeste Feinkornbaustähle werden zunehmend in modernen Schweißkonstruktionen bspw. dem Mobilkranbau eingesetzt. Während der schweißtechnischen Verarbeitung sind für diese Stahlgüten aufgrund ihres speziellen Gefüges und relativ hohen Streckgrenzenverhältnisses engere Verfahrensgrenzen einzuhalten als bei Stählen mit niedrigerer Festigkeit. Zudem erfordert die Sicherheit höherfester Schweißverbindungen präzise Kenntnisse über die Höhe und Verteilung schweißbedingter Beanspruchungen, da diese die erreichbare Tragfähigkeit und Bauteilperformance sowie den wirtschaftlichen Einsatz beeinflussen. Geltende Fertigungsrichtlinien für Schweißkonstruktionen wurden vorrangig für niedrigfeste Güten erarbeitet und vernachlässigen reale Steifigkeits- und Wärmeableitungsbedingungen. In dieser Arbeit wird deshalb der Einfluss der Wärmeführung auf die Eigenspannungsausbildung und Gesamtbeanspruchung in Schweißverbindungen typischer Vertreter höherfester Feinkornbaustähle (z.B. S960QL) systematisch untersucht. Zur Berücksichtigung äußerer Bauteilsteifigkeiten wurden die Proben in Nahtquerrichtung unter definierten realitätsnahen Einspanngraden in speziellen dreidimensional wirkenden Prüfanlagen mehrlagig geschweißt. Dabei ließen sich die resultierenden Kräfte und Spannungen multiaxial in-situ analysieren und ein deutlicher Einfluss der Wärmeführung auf den Kräfte- und Momentenhaushalt aufzeigen. Mittels statistischer Auswertung wurden wesentliche Aussagen für adaptierte Wärmeführungs- und Schweißparameter zur Beanspruchungsoptimierung entwickelt. Die Bewertung der Effekte und Interaktionen der Einflussfaktoren nach Wirkungsart und -ort gestattete zudem, Ansätze zur Berücksichtigung schweißbedingter Beanspruchungen bei der Auslegung höherfester Schweißkonstruktionen zu erarbeiten. T2 - AG Q4.1 Wasserstoffunterstützte Rissbildung CY - Berlin, Germany DA - 07.03.2017 KW - Höherfester Feinkornbaustahl KW - MAG-Schweißen KW - Wärmeführung KW - Schweißprozessparameter KW - Eigenspannungen KW - Bauteilversuch KW - Einspanngrad KW - Beanspruchungen PY - 2017 AN - OPUS4-41067 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Influence of the weld geometry on the residual stress reduction using low transformation temperature welding consumables N2 - Low transformation temperature (LTT) welding consumables offer an innovative approach to increase the fatigue strength of welded high-strength steel structures. LTT welding consumables are characterized by a martensitic phase transformation near ambient temperature, which generates compressive residual stresses in the weld and heat affected zone (HAZ). The aim is to achieve a weld geometry, which generate high compressive residual stresses at the fatigue crack critical weld toe. Longitudinal stiffeners were gas metal arc welded using a conventional welding consumable; the base material was a high strength steel S700M. A chromium-nickel alloyed LTT consumable was deposit subsequently just on front sides of the stiffeners. Different welding parameters led to varying cross sections of the weld. The residual stresses were determined using X-ray diffraction (XRD) in the crack critical HAZ. When using only the conventional, the HAZ is characterized by high tensile residual stresses. The additional application of the LTT alloy leads to a significant reduction of the tensile residual stresses. Depending on the weld geometry, even compressive residual stresses can be observed at the weld toe T2 - ECRS 2024 CY - Prague, Czech Republic DA - 03.06.2024 KW - LTT (Low Transformation Temperature) KW - Residual stress reduction KW - Fatigue PY - 2024 AN - OPUS4-60305 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Mehraxiale schweißbedingte Beanspruchungen und Werkstoffverhalten bei der Bauteilmontage höherfester Feinkornbaustähle N2 - Der zunehmende Bedarf an hochfesten Feinkornbaustählen in modernen Schweißkonstruktionen, in einer deutlich wachsenden Anzahl von Branchen wie dem Hoch-, Anlagen- und Kranbau, führte in den letzten Jahren zur Entwicklung zahlreicher Grund- und Zusatzwerkstoffe. Neben der Erreichung anforderungsgerechter mechanischer Eigenschaften wird die wirtschaftliche Verarbeitung dieser Güten durch hohe Sicherheitsanforderungen an die Schweißnaht bestimmt. Hohe Zugeigenspannungen in der Schweißverbindung können die Beanspruchbarkeit und Sicherheit eines geschweißten Bauteils wesentlich reduzieren. Insbesondere bei einer hohen konstruktiven Schrumpfbehinderung können die Beanspruchungen auch schon während der Fertigung ein risskritisches Niveau erreichen. Mittels geeigneten Wärmeführungen beim Schweißen und der adäquaten Auswahl von Schweißprozess und Zusatzwerkstoffen ist sowohl eine Minimierung der sich lokal in der Naht bildenden Zugeigenspannungen als auch der globalen infolge von Abstützeffekten auftretenden Reaktionsspannungen und -momente erzielbar. Im Rahmen zweier AiF-Forschungsvorhaben IGF.-Nr. 17267 N und 17978 N wurden verschiedene experimentelle Beanspruchungsanalysen durchgeführt, um den Schweißprozess hinsichtlich der resultierenden schweißbedingten Beanspruchungen zu untersuchen. Hierfür war es erforderlich, die Steifigkeitsverhältnisse so wie sie beim Schweißen realer Bauteilstrukturen auftreten, auf Schweißexperimente im Labor zu übertragen. Dazu wurde bspw. eine an der BAM eigens entwickelte Prüfanlage eingesetzt, mit der die mehraxialen Belastungen analysiert wurden, die mit bis zu 2 MN beim Vorwärmen, Schweißen und Abkühlen auftreten. Die Schweißeigenspannungen wurden mittels Röntgendiffraktometrie bestimmt. Zwar zeigten sich für niedrige Arbeitstemperaturen beim Schweißen ein signifikant reduziertes Gesamtbeanspruchungsniveau nach der Abkühlung der gesamten Schweißnaht. Die langen Abkühlphasen während der mehrlagigen schweißtechnischen Fertigung führen jedoch speziell bei den ersten Schweißraupen zu sehr hohen Reaktionsspannungen. Dabei erwiesen sich schmalere Nahtfugen verbunden mit dem Einsatz modifizierter Schweißprozesse und der Einsatz dehnfähiger Schweißzusätze für das Wurzelschweißen als geeignete Mittel, um eine deutliche Absenkung des Beanspruchungsniveaus beim Schweißen unter Schrumpfbehinderung zu erreichen. Ferner ist damit eine weitere wesentliche Reduzierung der Gesamtbeanspruchung und insbesondere der Zugeigenspannungen in der WEZ möglich. Mithilfe dieser Erkenntnisse ist die Optimierung der schweißbedingten Beanspruchungen unter Nutzung einer adaptierten Wärmeführung zur verbesserten Ausnutzung des Festigkeitspotentials höherfester Feinkornbaustähle erreichbar. T2 - Sitzung AG Q4.1 Wasserstoffunterstützte Rissbildung CY - Halle, Germany DA - 14.03.2018 KW - Bauteilprüfung KW - Eigenspannungen KW - MAG-Schweißen KW - Hochfeste Feinkornbaustähle PY - 2018 AN - OPUS4-45501 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Dittmann, Florian A1 - Varfolomeev, Igor T1 - Effect of weld design on fatigue strength of welded components using LTT filler materials N2 - Low transformation temperature (LTT) filler metals are an innovative approach to reduce tensile residual stress in weld seams and the surrounding heat affected zone (HAZ). The reduced tensile stress leads to an improvement in the fatigue strength of welded components. LTT filler metals are characterized by a reduced martensite start temperature (Ms), which is close to room temperature because of their chemical composition. This paper focuses on the hybrid use of LTT filler metals, where the LTT filler is applied as an additional layer to conventional welds on fatigue-critical spots. Conventional gas metal arc welded longitudinal stiffeners are used as specimens and at the face ends of the stiffeners, a second LTT layer was added with various weld modifications. These modifications were achieved by changing the welding parameters such as welding speed and offset to the first layer. These samples were used to analyze shape, dilution and resulting Ms, residual stress and fatigue strength. The dilution and dilatometer verified Ms did not change significant, although the surface of the 2nd LTT weld seam was varying clear with each modification. However, the weld modification had a significant effect on the residual stress state and the fatigue strength. The X-ray determined residual stress in the HAZ became lower when the weld toe of the LTT layer was further away from the stiffener. The Fatigue strength is clearly dependent on the residual stress state. The lower the residual stress at weld toe, the higher the fatigue strength. All samples with LTT weld exhibit significantly higher fatigue strength values than conventionally single and double-layer welded samples. The results show that on the one hand LTT filler metals increase the fatigue strength, and on the other hand the impact of LTT fillers materials is not restricted to the dilution and Ms, the shape of the weld seam must also be considered. T2 - IIW Intermediate Meeting CII CY - Trollhättan, Sweden DA - 10.03.2025 KW - LTT (Low Transformation Temperature) KW - Residual stress reduction KW - Fatigue strength KW - High-strength steels KW - Welding PY - 2025 AN - OPUS4-62708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gibmeier, J. A1 - Weidemann, Jens A1 - Dixneit, Jonny A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - Influence of structural stiffness on the residual stresses during welding of low transformation temperature alloys N2 - Low Transformation Temperature (LTT) alloys are high alloyed filler materials, which exhibit a martensitic phase transformation at comparatively low temperatures in order to prevent high tensile residual stresses. A number of publications have already shown that even compressive residual stresses can be observed when using LTT filler materials. Up to know it is not clear in which way this it applicable to multi-run welding exhibiting high shrinkage restraint and complex heat input. In this study the potential for stress reduction during welding of LTT alloys was studied by numerical simulation. This allows for evaluation of the stress development in every single weid run. Additionally, the impact of the structural stiffness was incorporated by modelling a special sample geometry exhibiting a high intensity of restraint. The results show that the stress formation in weid longitudinal direction is determined by the phase transformation as high compressive residual stresses were found here independent from the weid run. On the other hand the transformation induced stresses in weid transverse direction are superimposed by tensile stresses originated from shrinkage restraint. With increasing number of runs the tensile residual stress level is raised. The results were confirmed by residual stress measurements using diffraction methods. T2 - 11th International Seminar - Numerical Analysis of Weldability CY - Graz, Austria DA - 27.09.2015 KW - Influence KW - Structural stiffness KW - Residual stresses KW - Low transformation KW - Temperature alloys KW - Welding PY - 2016 SN - 978-3-85125-490-7 SN - 2410-0544 SP - 259 EP - 276 PB - Verlag der Technischen Universität Graz CY - Graz AN - OPUS4-38998 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schaupp, Thomas A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Welding residual stresses in 960 MPa grade QT and TMCP high-strength steels N2 - High-strength steels with yield strengths ≥ 690 MPa are becoming increasingly significant for modern steel constructions. Both quenched and tempered (QT) high-strength steels and steels produced by the thermo-mechanically controlled process (TMCP) are currently available. TMCP-steels are usually provided with a typical mill scale. Apart from the manufacturing process these steels differ also in their chemical composition. The influence of these differences are investigated here with focus on the residual stresses formed during TIG welding. Bead on plate welds have shown characteristic residual stress distributions depending on the type of steel as well as on the heat input and preheat temperature. The following work demonstrates that the fluid flow, induced by the elements present in the mill scale, leads to a deeper penetration of the material. This can also lead to increased residual stresses in the surface of the weld and the HAZ. Furthermore, higher heat input and preheat temperature can induce higher tensile residual stresses − which are evident in the present study. KW - Residual stresses KW - High-strength steel KW - Welding KW - Mill scale KW - Phase transformation PY - 2017 DO - https://doi.org/10.1016/j.jmapro.2017.05.006 SN - 1526-6125 VL - 27 SP - 226 EP - 232 PB - ELSEVIER AN - OPUS4-40312 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Untersuchungen zur Kaltrissvermeidung in geschweißten Bauteilen aus hochfestem Stahl T2 - 39. VDI-Jahrestagung Schadensanalyse - Wasserstoff in metallischen Bauteilen CY - Würzburg, Germany DA - 2013-10-08 PY - 2013 AN - OPUS4-29215 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Residual Stress Engineering by Low Transformation Temperature Alloys - State of the Art and Recent Developments T2 - 66th IIW Annual Assembly 2013 CY - Essen, Germany DA - 2013-09-11 PY - 2013 AN - OPUS4-29109 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gibmeier, J. A1 - Obelode, E. A1 - Altenkirch, J. A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Residual stress in steel fusion welds joined using low transformation temperature (LTT) filler material N2 - Welding residual stress is of major concern for structural integrity assessment in industrial components. Shear and volume strains resulting from the austenite-martensite-transformation affect the development of residual stress during welding. Controlling the phase transformation allows adjustment of the welding residual stress. Low transformation temperature (LTT) weld filler materials exhibiting reduced MS-temperatures allow postponing the phase transformation. The associated strain arising from the delayed transformation compensates for the thermal contraction strains and as such may reduce tensile or even introduce compressive residual stress. In this article we discuss the tri-axial residual stress distribution in 15 mm S690Q steel plates joined with LTT filler materials with 10 wt% Cr and a Ni-content that varies from 8 to 12 wt%. Using complementary synchrotron X-ray and neutron diffraction stress analysis the macroscopic residual stress was derived from the phase specific lattice strain and phase fraction of martensite and retained austenite, respectively. The local phase specific unstrained lattice parameters were determined using stress relieved combs. The investigation revealed increasing phase fraction of retained austenite with increasing Ni-content. Further, independent of the Ni-content in each weld in the fusion zone, significant compressive residual stresses were found in the longitudinal direction, which are balanced by tensile residual stresses in the heat affected zone (HAZ). In the weld transverse and normal direction the stress distribution is qualitatively similar but less in magnitude. The increased amount of retained austenite reduces the compressive stress arising from shear and volume strains during the delayed phase transformation and therefore no significant increase in compression was observed for decreasing MS-temperatures. KW - Welding residual stresses KW - Neutron diffraction KW - LTT filler materials PY - 2014 DO - https://doi.org/10.4028/www.scientific.net/MSF.768-769.620 SN - 0255-5476 VL - 768-769 SP - 620 EP - 627 PB - Trans Tech Publications CY - Aedermannsdorf, Switzerland AN - OPUS4-29706 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Effect of martensitic phase transformation on stress build-up during multilayer welding N2 - Innovative low transformation temperature (LTT) welding filler materials are featuring a characteristic chemical composition which favors the formation of martensite at comparatively low temperatures. This permits deliberate adjustment of welding residual stresses. Even though numerous investigations can be found in the literature on this issue, they provide only little insight into the interaction between phase transformation and resulting welding residual stresses. For this purpose, a component weld test was performed in a special large-scale testing facility. The results illustrate that the desired residual stress control by using LTT alloys is actually feasible. With increasing shrinkage restraint, however, higher tensile residual stresses are formed in transverse direction of the weld. By contrast, the residual stress level in longitudinal weld direction is nearly independent of the restraint conditions. On-line stress analysis revealed that the amount of stress reduction during cooling of the individual weld runs is dependent on the weld volume undergoing phase transformation. Overall, evidence was furnished that the approach of residual stress engineering by LTT alloys is suitable even in the case of large-scale multilayer welding. KW - LTT KW - Martensite KW - Multilayer Welding KW - Phase Transformation KW - Residual Stress PY - 2014 DO - https://doi.org/10.4028/www.scientific.net/MSF.768-769.660 SN - 0255-5476 VL - 768-769 SP - 660 EP - 667 PB - Trans Tech Publications CY - Aedermannsdorf, Switzerland AN - OPUS4-29708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Held, E. A1 - Ohl, H. A1 - Gibmeier, J. A1 - Dixneit, Jonny A1 - Kromm, Arne A1 - Kannengießer, Thomas ED - Petzow, G. T1 - Mikrostruktur- und Härteentwicklung in Schweißnähten mit neuartigen LTT-Schweißzusatzwerkstoffen N2 - Das Schweißen von hochfesten Stahlstrukturen ist Gegenstand aktueller Forschungsbestrebungen wobei unter anderem der Eigenspannungsausbildung eine entscheidende Rolle zugeordnet wird. Neuartige LTT (Low Transformation Temperature) Schweißzusatzwerkstoffe mit deutlich abgesenkten Martensitstarttemperaturen wurden entwickelt, um die Eigenspannungsentwicklung in der Schweißnaht durch die späte Martensitumformung während des Abkühlens des Schweißguts kontrollieren zu können. Auf diese Weise können in den Schweißnähten nicht nur Zugeigenspannungen reduziert sondern sogar gezielt Druckeigenspannungen eingebracht werden. Dies konnte bereits in verschiedenen Arbeiten zu diesem Themenkomplex gezeigt werden. Durch das gezielte Einbringen von Druckeigenspannungen in die Schweißnaht kann die Lebensdauer und die mechanische Integrität von hochfesten Schweißverbindungen ohne aufwändige mechanische oder thermische Nachbehandlungsverfahren deutlich erhöht w erden. Einen großen Einfluss auf die Eigenspannungsausbildung in Schweißnähten haben die Umwandlungstemperatur und die Schrumpfungsbehinderung bei der Abkühlung. In der vorliegenden Arbeit wird nun untersucht, wie der Grad der Einspannung sich auf die Mikrostruktur- und Härteentwicklung in Schweißnähten mit LTT -Zusatzwerkstoffen auswirkt. Der in dieser Arbeit untersuchte neuartige LTT-Schweißzusatzstoff wurde nach dem 10%Ni - 10%Cr-Konzept nach 111 ausgewählt. Die Schweißeignung des untersuchten Werkstoffes sowie die Beeinflussung der Mikrostrukturausbildung durch eine Variation des Nickelgehalt wurden bereits in vorangehenden Arbeiten eingehend untersucht. Hierbei zeigte sich, dass der Nickelgehalt einen signifikanten Einfluss auf die Martensitstarttemperatur und damit auf die lokale Mikrostrukturausbildung hat. Eine Erhöhung des Nickelgehaltes von S auf 12 Ma-% führt zu einer Verminderung der Martensitstarttemperatur von 16()°C auf etwa 60°C (bestimmt mittels in-situ Röntgenbeugungsanalysen im reinen Schweißgut). T2 - 47. Metallographie-Tagung CY - Friedrichshafen, Germany DA - 18.09.2013 PY - 2013 SN - 978-3-88355-398-6 VL - 45 SP - 297 EP - 302 AN - OPUS4-29710 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Capabilities of Diffraction Techniques in Welding Research T2 - International Workshop on Industrial Research using Synchrotron and Neutron Methods CY - Berlin, Germany DA - 2013-12-03 PY - 2013 AN - OPUS4-29705 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Properties and Weldability of Modified Low Transformation Temperature (LTT) Filler Wires T2 - IIW Intermediate Meeting - SC II-A CY - Berlin, Germany DA - 2014-04-01 PY - 2014 AN - OPUS4-30537 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gibmeier, J. A1 - Held, A. A1 - Altenkirch, J. A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Buslaps, T. T1 - Real time monitoring of phase transformation and strain evolution in LTT weld filler material using EDXRD N2 - For a newly developed 10% Cr and 10% Ni low transformation temperature (LTT) weld filler material, the local phase transformation kinetics and the strain evolution during gas tungsten arc welding (GTAW) under real welding conditions was studied. An experimental set-up and a measuring and evaluation strategy are presented to gain a real time insight into the welding process. The experiments were carried out at the beam line ID15@ESRF using a two detector EDXRD (energy dispersive X-ray diffraction) set-up and high energy synchrotron X-rays. The time-resolved diffraction analysis during welding was carried out locally throughout the weld in longitudinal as well as in transverse direction to the weld line to examine the interdependence of the strain state and the transformation kinetics. This comprehension is crucial for the optimization of the weld process, and thus for the tailoring of the resulting residual stress states, which is one of the main issues for the application of LTT alloys. Using the herein proposed approach EDXRD diffraction pattern can be monitored during real welding with a counting rate of 5 Hz. By means of the time resolved diffraction data the local transformation temperatures and times were determined and the local phasespecific strain evolutions are discussed with respect to the transformation rates and the time-delayed phase transformations. KW - In situ synchrotron X-ray diffraction KW - Low transformation temperature KW - Welding PY - 2014 DO - https://doi.org/10.1016/j.jmatprotec.2014.06.008 SN - 0924-0136 SN - 1873-4774 VL - 214 IS - 11 SP - 2739 EP - 2747 PB - Elsevier CY - Amsterdam AN - OPUS4-30955 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kromm, Arne A1 - Steppan, Enrico A1 - Kannengießer, Thomas ED - Kannengießer, Thomas ED - Babu, S. S. ED - Komizo, Y. ED - Ramirez, A.J. T1 - High-energy synchrotron study of the stress-strain behavior of hydrogen-charged high strength structural steel N2 - High strength structural steels are susceptible to hydrogen embrittlement. A critical combination of stress, amount of diffusible hydrogen and microstructure is believed to cause cold cracking. Especially during welding of high strength structural steels high tensile residual stresses may develop. Therefore, a feasibility study was conducted using synchrotron X-ray diffraction in order to analyze the stress–strain behavior during tensile loading. For that purpose two types of steel showing different hardening mechanisms were used. On the one hand a thermo-mechanically treated S1100MC and on the other hand a quenched and tempered S1300Q were chosen. The samples were electrochemically charged with hydrogen and subsequently stored in liquid nitrogen to prevent effusion. Tensile tests of the samples were conducted in a special load frame allowing for tilting the samples while applying constant loads. High energy synchrotron radiation was used for energy dispersive X-ray diffraction (EDXRD) analysis in transmission geometry. This method offers the possibility for measuring several diffraction lines of all contributing crystalline phases of the material. Strains as well as stresses applying the sin²ψ-method were determined for varying load situations. This feasibility study shows how the interaction of hydrogen and the stress/strain response may be assessed by diffraction methods. Examples are presented showing that hydrogen alters the load distribution as well as the strain behavior between different lattice planes in high strength steels. KW - High energy synchrotron radiation KW - Energy dispersive X-ray diffraction (EDXRD) KW - High strength structural steels KW - Tensile tests KW - Hydrogen embrittlement PY - 2014 SN - 978-3-319-06144-3 SN - 978-3-319-06145-0 DO - https://doi.org/10.1007/978-3-319-06145-0_10 SP - 165 EP - 176 PB - Springer AN - OPUS4-31356 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Properties and Weldability of Modified Low Transformation Temperature (LTT) Filler Wires T2 - IIW Annual Assembly - SC II-A CY - Seoul, South Korea DA - 2014-07-14 PY - 2014 AN - OPUS4-31093 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - In-situ observation of stress accumulation during sub-merged arc welding T2 - European Conference on Residual Stresses ECRS 9 CY - Troyes, France DA - 2014-07-07 PY - 2014 AN - OPUS4-31096 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Dixneit, Jonny A1 - Kannengießer, Thomas T1 - Residual stress engineering by low transformation temperature alloys - state of the art and recent developments N2 - Residual stress engineering in welding becomes more and more prominent as the use of tailored materials, e.g., high-strength steels, calls for maximum utilization of the material properties. As a consequence, residual stresses have to be considered as design criterion. Moreover, it may be utilized to improve the material's performance. Low transformation temperature alloys are a smart approach to control the residual stresses already during the welding process avoiding time-consuming postweld treatments. This paper gives an overview about the progress made in research in this topic with special focus on residual stresses. Basics as well as important developments will be addressed. KW - Residual stresses KW - Martensite KW - Low temperature KW - Transformation PY - 2014 DO - https://doi.org/10.1007/s40194-014-0155-6 SN - 0043-2288 SN - 1878-6669 VL - 58 IS - 5 SP - 729 EP - 741 PB - Springer CY - Oxford AN - OPUS4-31446 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schaupp, Thomas A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Welding residual stress distribution of quenched and tempered and thermo-mechanically hot rolled high strength steels N2 - Beside quenched and tempered (QT) high strength steels advanced technologies in steel manufacturing provide steels produced by the thermo-mechanical controlled process (TMCP) with yield strength of 960 MPa. These steels differ in the carbon and micro-alloying element content. With variation of heat control TIG-welded dummy seams on both steel types were performed. Analyses concerning microstructure and residual stress evolution due to welding showed typical stress distributions according to common concepts. Yet, the TMCP-steel shows higher residual stresses than the QT-steel. KW - Mill Scale KW - Quenched KW - Residual Stress KW - Tempered High Strength Steel KW - Thermo-Mechanical Controlled Process KW - Welding PY - 2014 DO - https://doi.org/10.4028/www.scientific.net/AMR.996.457 SN - 1022-6680 SN - 1662-8985 VL - 996 SP - 457 EP - 462 PB - Trans Tech Publ. CY - Zurich AN - OPUS4-31443 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Stress Build-Up during Mulitlayer Welding with Novel Martensitic Filler Materials N2 - Neuartige sogenannte Low-Transformation-Temperature (LTT)- Schweißzusätze weisen eine chemische Zusammensetzung auf, welche die Martensitbildung zu vergleichsweise niedrigen Temperaturen verschiebt. Dies wirkt sich maßgeblich auf die nach dem Schweißen vorliegenden Eigenspannungen aus. Obwohl dazu zahlreiche Veröffentlichungen vorliegen, blieben die Wirkzusammenhänge zwischen Umwandlungstemperatur und Schweißeigenspannungen bislang ungeklärt. Aus diesem Grund wurde in der vorliegenden Arbeit ein Versuch in einer Großprüfanlage durchgeführt, um den Einfluss der Martensitumwandlung während des Mehrlagenschweißens zu analysieren. Die In-Prozess-Beobachtung der auftretenden Kräfte und Momente offenbarte, dass die Eigenspannungsreduktion vom jeweils umwandelnden Volumen abhängt. Die Analyse der Schweißeigenspannungen verdeutlichte, dass die angestrebte Eigenspannungsbeeinflussung durch den Zusatzwerkstoff stark von den Randbedingungen (d. h. Nahtaufbau, Blechdicke) abhängt und einer Bewertung im jeweiligen Anwendungsfall bedarf. N2 - Controlling the level of mostly detrimental residual stresses already during the welding process would be highly attractive as time and cost consuming post processing may be prevented. Innovative Low Transformation Temperature (LTT-) filler materials are specially designed for Controlling weld residual stresses by means of adjusted martensite formation already during welding. Numerous publications can be found on this issue, but they provide only little insight into the interaction between martensite formation and resulting welding residual stresses. Within this study a component weld test was performed in a special large-scale testing facility. In-situ load analysis revealed that the amount of stress reduction during deposition of the individual weld runs is dependent on the weld volume undergoing phase transformation related to the shrinking volume. The residual stresses found alter welding show that the desired residual stress control by using LTT alloys is sensitive to welding boundary conditions (i. e. weld geometry, plate thickness) and to be evaluated separately for varying weld scenarios. T2 - Spannungsentstehung während des Mehrlagenschweißens mit einem neuartigen martensitischen Schweißzusatz KW - Residual stresses KW - LTT filler material KW - Martensite KW - Phase transformation KW - Welding KW - Eigenspannungen KW - LTT-Zusatzwerkstoff KW - Martensit KW - Phasenumwandlung KW - Schweißen PY - 2014 DO - https://doi.org/10.3139/105.110210 SN - 2194-1831 SN - 1867-2493 VL - 69 IS - 2 SP - 80 EP - 88 PB - Hanser CY - München AN - OPUS4-30719 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bhatti, A.A. A1 - Barsoum, Z. A1 - Van der Mee, V. A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Fatigue strength improvement of welded structures using new low transformation temperature filler materials N2 - The results reported in this research study are part of a larger EU RFCS (Research Fund for Coal and Steel) project where the aim is to study the fatigue behavior of improved welds in high strength steels by utilizing different improvement techniques. In this particular study LTT (Low Transformation Temperature) weld filler material have been investigated and their possibility to improve the fatigue strength. The characteristic of these filler material is that they undergo phase transformation at temperature close to room temperature which will reduce the tensile residual stress in the weld and in some cases result in compressive residual stresses. Two different LTT alloy compositions have been developed, with different Ms (Martensite Start) temperatures in order to study the amount of tensile/compressive residual stresses produced by these wires. Welding residual stress measurements were carried out by X-ray diffraction technique. Plates with welded longitudinal attachments were fabricated in 700 MPa and 960 MPa steel grades using different LTT filler materials. These specimens were fatigue tested in constant and variable amplitude loading and the fatigue test results were compared with results from specimen welded with conventional weld filler material. KW - Residual stresses KW - LTT KW - Welded joints KW - Fatigue testing PY - 2013 DO - https://doi.org/10.1016/j.proeng.2013.12.074 SN - 1877-7058 VL - 66 SP - 192 EP - 201 PB - Elsevier Ltd. CY - Amsterdam [u.a.] AN - OPUS4-30609 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Capabilities of Diffraction Techniques in Welding Research T2 - ESS Science Symposium - Future Engineering Diffraction Research in Materials Processing and Testing CY - Prague, Czech Republic DA - 2014-11-17 PY - 2014 AN - OPUS4-32042 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Transformation Plasticity during Martensite Formation analyzed by Synchrotron Diffraction T2 - MSE 2014: Materials Science and Engineering CY - Darmstadt, Germany DA - 2014-09-23 PY - 2014 AN - OPUS4-32017 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -