TY - RPRT A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Characterising Phase Transformations of Different LTT Alloys and their Effect on Residual Stresses and Cold Cracking N2 - Novel martensitic filler materials with specially adjusted martensite start temperatures (Ms) can counteract the cooling specific shrinkage due to expansion effects of the weld metal associated with phase transformations. That can be exploited to create compressive residual stresses in the weld and adjacent areas, i.e. beneficial for increasing fatigue strength. The Ms temperature is shifted via the chemical composition, mainly by the alloying elements nickel and chromium, resulting as well in different retained austenite contents. Investigations were made using different Low Transformation Temperature (LTT) alloys with varying nickel content. The resulting phase transformation temperatures were - for the first time - detected using high energy synchrotron diffraction and Single Sensor Differential Thermal Analysis (SS-DTA). Compared to angle dispersive diffraction, energy dispersive diffraction offers the possibility to measure residual stresses of the martensite and austenite phase parallel fast in one experiment up to depths of 100 µm. The residual stresses show significant distributions dependent on Ms temperature. The effect on the cold cracking behaviour of these alloys was investigated using the Tekken test. Results show that cold cracking can be avoided when appropriate contents of retained austenite are existent. PY - 2009 IS - IX-2311-09 SP - 1 EP - 9 PB - International Institute of Welding CY - Paris AN - OPUS4-19749 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Stress build up in low transformation temperature filler material under defined restraint conditions T2 - JOM-15 Fifteenth International Conference on the Joining of Materials CY - Helsingor, Denmark DA - 2009-05-04 PY - 2009 AN - OPUS4-19388 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - In-Situ of the Residual Stress Stability of Low Transformation Temperature (LTT)-Filler Materials T2 - 1st International Workshop "In-Situ with Photons, Neutrons and Electrons Scattering" CY - Berlin, Germany DA - 2009-09-01 PY - 2009 AN - OPUS4-19845 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - In-Situ Observation of Phase Transformations during Welding of low Transformation Temperatur Filler Material T2 - THERMEC 2009 International Conference on Processing & Manufactoring of Advanced Materials Processing, Fabrication, Properties, Applications CY - Berlin, Germany DA - 2009-08-25 PY - 2009 AN - OPUS4-19869 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - In-Situ Studies of Phase Transformation an Residual Stresses in LTT Alloys During Welding Using Synchrotron Radiation T2 - 1st Inernational Workshop "In-Situ Studies with Photons, Neutrons an Electrons Scattering", BAM CY - Berlin, Germany DA - 2009-09-01 PY - 2009 AN - OPUS4-19868 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Gibmeier, J. T1 - In-situ observation of phase transformations during welding of low transformation temperature filler material KW - LTT filler material KW - In-situ observation KW - Energy dispersive diffraction KW - Transformation temperature KW - Residual stress PY - 2010 DO - https://doi.org/10.4028/www.scientific.net/MSF.638-642.3769 SN - 0255-5476 VL - 638-642 SP - 3769 EP - 3774 PB - Trans Tech Publications CY - Aedermannsdorf, Switzerland AN - OPUS4-20725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne A1 - Altenkirch, J. T1 - In-situ Synchrotron-Beugungsuntersuchungen zur Umwandlungskinetik und zur Dehnungsentwicklung beim Lichtbogenschweißen T2 - Arbeitsgemeinschaft Wärmebehandlung und Werkstofftechnik e.V., AWT Fachausschuss 13 Eigenspannungen CY - Stuttgart, Germany DA - 2009-11-04 PY - 2009 AN - OPUS4-20968 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Anwendung des neuen Controlled Tensile Weldability (CTW) Tests zur Untersuchung der Heißrissneigung T2 - Tagung Werkstoffprüfung CY - Bad Neuenahr, Germany DA - 2009-12-07 PY - 2009 AN - OPUS4-20658 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Brauser, Stephan A1 - Kromm, Arne T1 - Synchrotron diffraction for in-situ characterizations of materials behaviour T2 - 3rd Inter-university research seminar (IURS 2010) - Advances in welding and joining CY - Pusan, Korea DA - 2010-05-13 KW - In-situ diffraction KW - Phase transformation KW - High strength steel KW - Residual stress PY - 2010 SP - 127 EP - 131 CY - Pusan, Korea AN - OPUS4-21352 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - In situ phase characterization of low transformation temperature (LTT) alloy by means of synchrotron diffraction N2 - Cold cracking resistance is a relevant evaluation criterion for welded joints and affected by residual stresses which result from the welding procedure. Compressive residual stresses can thereby have a positive influence on preventing cracking. A unique possibility of generating compressive residual stresses already during the welding procedure is offered by the socalled Low Transformation Temperature (LTT) filler wires. Compared to conventional wires, these materials show decreased phase transformation temperatures which can work against the cooling-specific contraction. In consequence, distinct compressive residual stresses can be observed within the weld and adjacent areas. The strength of these fillers makes them potentially applicable to high-strength steel welding. Investigations were carried out to determine the phase transformation behaviour of different LTT-filler materials. Transformation temperatures were identified using Single Sensor Differential Thermal Analysis (SS-DTA). Additionally Synchrotron radiation was used to measure the transformation kinetics of all involved crystalline phases during heating and cooling of a simulated weld thermal cycle. KW - In-situ phase analysis KW - Energy dispersive diffraction KW - Phase transformation PY - 2010 SN - 1684-579X VL - 5 IS - 158 SP - 17 EP - 23 PB - Izdat. Masinostroenie CY - Moskva, Russia AN - OPUS4-21829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Lausch, Thomas A1 - Kromm, Arne T1 - Effects of heat control on the stress build up during high strength steel welding under defined restraint conditions T2 - International Conference on high strength steels for hydropower plants CY - Takasaki, Japan DA - 2009-07-20 KW - Welding KW - Heat control KW - Stress build up KW - High-strength steel KW - Restraint intensity PY - 2009 UR - http://www-it.jwes.or.jp/proceedings/en/3-10.pdf SP - 10-1 - 10-8 AN - OPUS4-22317 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - In-situ studiesof phase transformation and residual stress build up in martensitic materials using synchrotron radiation T2 - 2nd IURS - Inter-university research symposium CY - Canmore, Alberta, Canada DA - 2009-05-20 KW - In-situ diffraction KW - Phase transformation KW - LTT alloy KW - Residual stress PY - 2009 IS - Paper 12 SP - 1 EP - 5 AN - OPUS4-22499 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Lausch, Thomas A1 - Kromm, Arne T1 - Effects of heat control on the stress build up during high-strength steel welding under defined restraint conditions T2 - 62nd IIW Annual assembly and conference CY - Singapore DA - 2010-07-12 KW - Welding KW - Heat control KW - Stress build up KW - High-strength steel KW - Restraint intensity PY - 2009 IS - IIW Doc IX-2316-09 (IX-L-1055-09) SP - 1 EP - 8 AN - OPUS4-22316 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Brauser, Stephan T1 - Synchrotron diffraction for visualization of solid state phase transformations T2 - VISUAL-JW 2010 - The international symposium on visualization in joining & welding science through advanced measurements and simulation CY - Osaka, Japan DA - 2010-11-11 KW - Synchrotron KW - EDXRD KW - Martensite KW - Residual stress KW - TRIP steel KW - Phase transformation PY - 2010 IS - MTJW-1 SP - 123 EP - 124 AN - OPUS4-22653 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - In-Situ EDXRD zur Eigenspannungsentwicklung beim Lichtborgenschweißen T2 - AWT Fachausschuss 13 Eigenspannungen, Arbeitsgemeinschaft Wärmebehandlung und Werksofftechnik e. V. CY - Karlsruhe, Germany DA - 2011-04-12 PY - 2011 AN - OPUS4-23564 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kromm, Arne A1 - Kannengießer, Thomas ED - Borsutzki, M. T1 - Anwendung des neuen Controlled Tensile Weldability (CTW) Tests zur Untersuchung der Heißrissneigung T2 - Tagung Werkstoffprüfung 2006 CY - Bad Neuenahr, Deutschland DA - 2006-12-07 KW - Heißrisstest KW - 1.4565 KW - Heißrissneigung KW - Dehnung KW - Dehngeschwindigkeit KW - Heißriss KW - Erstarrungsriss KW - Konstruktiver Einfluss PY - 2006 SN - 3-514-00734-9 SP - 451 EP - 456 PB - Stahleisen CY - Düsseldorf AN - OPUS4-14362 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - CT-02 In-situ-phase analysis using synchrotron radiation of low transformation temperature (LTT) welding material T2 - IIW International Congress, 2nd Latin American Welding Congress, XXXIV Consolda - National Welding Congress CY - Sao Paulo, Brazil DA - 2008-05-18 PY - 2008 SN - 85-8718210-2 SP - 1 EP - 12 AN - OPUS4-18591 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - CT-01 Formation of welding residual stresses in low transformation temperature (LTT) materials T2 - IIW International Congress, 2nd Latin American Welding Congress, XXXIV Consolda - National Welding Congress CY - Sao Paulo, Brazil DA - 2008-05-18 PY - 2008 SN - 85-8718210-2 SP - 1 EP - 12 AN - OPUS4-18590 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - In-situ-phase analysis using synchroton radiation of low transformation temperature (LTT) welding material T2 - IIW International Congress, 2nd Latin American Welding Congress, XXXIV CONSOLDA-National Welding Congress CY - São Paulo, Brazil DA - 2008-05-18 PY - 2008 AN - OPUS4-17812 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Characterizing phase transformations of different LTT alloys and their effect on residual stresses and cold cracking N2 - Novel martensitic filler materials with specially adjusted martensite start temperatures (Ms) can counteract the cooling specific shrinkage due to expansion effects of the weld metal associated with phase transformations. That can be exploited to create compressive residual stresses in the weld and adjacent areas, i.e. beneficial for increasing fatigue strength. The Ms-temperature is shifted via the chemical composition, mainly by the alloying elements nickel and chromium, resulting as well in different retained austenite contents. Investigations were made using different Low Transformation Temperature (LTT) alloys with varying nickel content. The resulting phase transformation temperatures were — for the first time — detected using high energy synchrotron diffraction and Single Sensor Differential Thermal Analysis (SS-DTA). Compared to angle dispersive diffraction, energy dispersive diffraction offers the possibility to measure residual stresses of the martensite and austenite phase parallel fast in one experiment up to depths of 100 μm. The residual stresses show significant distributions dependent on the Ms-temperature. The effect on the cold cracking behaviour of these alloys was investigated using the Tekken test. Results show that cold cracking can be avoided when appropriate contents of retained austenite are existent. KW - Austenite KW - Cold cracking KW - Martensite KW - Low KW - Temperature KW - Transformation PY - 2011 SN - 0043-2288 SN - 1878-6669 VL - 55 IS - 03/04 SP - 48 EP - 56 PB - Springer CY - Oxford AN - OPUS4-23402 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kannengießer, Thomas A1 - Lausch, Thomas A1 - Kromm, Arne T1 - Effects of heat control on the stress build-up during high-strength steel welding under defined restraint conditions N2 - Realization and safe operation of modern welded structures are progressively requiring for base and filler materials to cope with continually increasing loads, Analyses with a view to crack prevention therefore need to accommodate particularly the structural design (restraint intensity) and the thermomechanical effects in terms of stresses introduced during welding, Against this background, multi-run welding experiments were carried out in an IRC - (Instrumented Restraint Cracking) Test under defined restraint intensity in order to examine the influence of heat control (preheating and interpass temperatures) on the weldinq-specific forces and stresses, The experiments revealed significant rises in the reaction force and stress after welding with increasing preheating and interpass temperature, Furthermore, various concepts for calculating the preheating temperature are discussed, It is demonstrated that the hitherto existing concepts for high-strength finegrained structural steels can lead to divergent results. KW - Cracking KW - Heat KW - High strength steels KW - Restraint KW - Stress KW - Testing PY - 2011 SN - 0043-2288 SN - 1878-6669 VL - 55 IS - 07/08 SP - 58 EP - 65 PB - Springer CY - Oxford AN - OPUS4-24294 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Altenkirch, J. A1 - Gibmeier, J. A1 - Kostov, V. A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Doyle, S. A1 - Wanner, A. T1 - Time- and temperature-resolved synchrotron X-ray diffraction: observation of phase transformation and strain evolution in novel low temperature transformation weld filler materials N2 - Solid-state phase transformations and the evolution of thermal and elastic strains in novel low temperature transformation (LTT) weld filler materials in the near surface region are monitored in real time by means of an innovative experimental set-up at the PDIFF (powder diffraction) beamline at the synchrotron light source ANKA (Angströmquelle Karlsruhe) at the KIT (Karlsruhe Institute for Technology). The key components of the diffraction set-up are two fast microstrip line detectors, which enables the strain evolution to be followed as a function of time and temperature for a 0.5?s counting time. During controlled heating and cooling cycles, as well as during near welding cycles, the martensite–austenite–martensite phase transitions are analysed. The transformation kinetics are monitored during resistance heating of small chips of the pure LTT alloys and during gas tungsten arc welding of simplified LTT welds using a specially designed welding rig for in-situ studies on the diffraction instruments. Under the mechanically unconstrained condition allowing free thermal expansion and shrinkage, the LTT alloys are found to exhibit decreasing transformation temperatures Ac and MS and increasing phase fraction of retained austenite for increasing Ni content. The strain evolution during welding reveals increased compressive stresses upon welding, which is attributed to the martensite formation upon cooling, which counteracts the thermal contraction strains. Comparison of the transformation temperatures reveals higher values than in the pure LTT alloys, but no variation between the different alloys. On the one hand, this is attributed to preferred grain orientation affecting the diffraction measurements and the determination of the transformation temperatures. On the other hand, it is possible that with the different chemical compositions of the LTT alloys and the mechanical constraints during welding, the evolution of the residual strain and stress may vary and result in counteracting affects with respect to lowered martensite start temperatures. KW - In-situ synchrotron X-ray diffraction KW - Low temperature transformation KW - Welding PY - 2011 DO - https://doi.org/10.1177/0309324711413190 SN - 0309-3247 SN - 2041-3130 VL - 46 IS - 7 SP - 563 EP - 579 PB - Sage CY - London AN - OPUS4-24683 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Influence of Heat Control on Welding Residual Stresses in Multi-layer Component Joints T2 - IIW Intermediate Meeting 2012 CY - Cambridge, England DA - 2012-02-20 PY - 2012 AN - OPUS4-25539 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Kurzvorstellung des Projektes H2SuD / Wasserstoff und Schweißen Einfluss des Schweißens auf die Wasserstoffaufnahme und Degradation im Betrieb befindlicher H2 Gasleitungen N2 - Die Wasserstoffinfrastruktur ist eine zentraler Bestandteil der erfolgreichen Umsetzung der wasserstoffbasierten Energiewende. Dabei bilden Ferngasleitungen quasi das "Rückgrat" der Transportinfrastruktur großer Gasmengen. Dabei müssen unter Umständen Reparaturen an den Pipelines durchgeführt werden. Dabei ist in der Erdgasinfrastruktur das Schweißen an in Betrieb befindlichen (d.h. von Gas durchflossenen) Pipelines Stand der Technik. Es ist jedoch vollkommen offen, inwieweit diese Technik auf die reine Wasserstoffpipelines übertragbar sind. Hierzu leistet das Projekt H2SuD wichtige Beiträge zur Aufklärung des Einfluss eines Reparaturschweißprozesses auf die Wasserstoffaufnahme und Degradation im Betrieb befindlicher H2 Gasleitungen. T2 - Sitzung des DIN-Gemeinschaftsarbeitsausschusses NA 092 00 05 GA, NAS/NMP: Zerstörende Prüfung von Schweißverbindungen CY - Berlin, Germany DA - 15.03.2023 KW - Wasserstoff KW - Pipeline KW - Reparatur KW - Schweißen PY - 2023 AN - OPUS4-57169 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liepold, Philipp A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Einfluss des Einspanngrades auf die Bildung von Erstarrungsrissen in Überlappverbindungen hochfester Stähle N2 - Im Beitrag werden Ergebnisse aus Versuchen mit dem Controlled Thermal Severity (CTS)-Test vorgestellt, der für sehr stark eingespannte Kehlnähte bekannt ist. Niedriglegierte Schweißungen an hochfesten Stählen sind nicht anfällig für Erstarrungsrissbildung. Unter dem besonderen Einfluss eines hohen Einspanngrades wurde die Erstarrungsrissneigung durch Abmessen der Rissflächen als Funktion der Schweißparameter und des Einspanngrades für vier hochfeste Schweißzusätze im MAG-Schweißen untersucht. Die Tests zeigen, dass sowohl eine Erhöhung des Einspanngrades als auch eine Änderung der Schweißparameter (hinsichtlich Streckenenergie und Geschwindigkeit) zu mehr Erstarrungsrissfläche führen. Besonders die Kombination aus sehr hohem Einspanngrad und hoher Streckenenergie plus hoher Schweißgeschwindigkeit sollte im Sinne der Erstarrungsrissminimierung vermieden werden. T2 - DVS-Congress CY - Erfurt, Germany DA - 16.09.2024 KW - CTS KW - Erstarrungsrisse KW - Kehlnähte PY - 2024 VL - 2024 SP - 193 EP - 200 AN - OPUS4-61069 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wandtke, Karsten A1 - Engelking, Lorenz A1 - Schröpfer, Dirk A1 - Scharf-Wildenhain, Ronny A1 - Hälsig, Andre A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Fertigungsbedingte Beanspruchungen und Kaltrisssicherheit in generativ gefertigten Bauteilen aus hochfesten Feinkornbaustählen N2 - Additive Fertigungsverfahren wie das Direct Energy Deposition-Arc (DED-Arc) oder Wire Arc Additive Manufacturing (WAAM) ermöglichen die effiziente Herstellung gewichtsoptimierter, endkonturnaher Bauteile im modernen Stahlbau. Steigerungen der Effizienz können durch den Einsatz hochfester Stähle erreicht werden, insbesondere durch Verringerung von Wandstärken und Bauteilgewicht sowie signifikante Einsparung von Kosten, Zeit und Ressourcen. DED-Arc Schweißzusatzwerkstoffe sind bereits auf dem Markt verfügbar, allerdings fehlen Richtlinien und quantitative Kenntnisse über die schweißbedingte Beanspruchung während der Fertigung und im Betrieb, welche den industriellen Einsatz stark limitieren. In einem gemeinsamen Projekt der BAM und der Technischen Universität Chemnitz wurden die wesentlichen Einflüsse und komplexen Wechselwirkungen von Werkstoff, Fertigungsverfahren, Konstruktion und Bearbeitungsschritten auf die Eigenspannungen untersucht. Ziel war es, den stahlverarbeitenden Anwendern, insbesondere KMU, eine risssichere und beanspruchungsgerechte Herstellung und Modifizierung von Bauteilen und Halbzeugen aus hochfesten Feinkornbaustahl unter Verwendung MSG-basierter generativer Verfahren zu ermöglichen. T2 - DVS Innovationstage 2024 CY - Düsseldorf, Germany DA - 10.04.2024 KW - Wire Arc Additive Manufacturing (WAAM) KW - Feinkornbaustähle KW - Additive Fertigung KW - Kaltrisssicherheit KW - Direct Energy Deposition-Arc (DED-Arc) PY - 2024 SP - 96 EP - 104 AN - OPUS4-61932 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wandtke, Karsten A1 - Schröpfer, Dirk A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - WAAM process influences on local microstructure and residual stresses in high-strength steels N2 - High-strength fine-grain structural steels have great potential for weight optimization of many modern engineering structures. Efficient manufacturing can be achieved here above all by Wire Arc Additive Manufacturing (WAAM). First commercial high-strength welding consumables for WAAM are already available. Due to a lack of knowledge and guidelines for the industry regarding welding residual stresses and component safety in manufacturing and operation, their application is still severely limited. Residual stresses play a crucial role here, as the special microstructure of high-strength steels is sensitive to cold cracking. For this reason, process- and material-related influences, as well as the design effects on residual stress formation, are being investigated in a project funded by the AiF (FOSTA P1380/IGF 21162 BG). This study focuses on determining the interactions between heat control during WAAM process, resulting hardness, microstructure, and residual stresses, analyzed by X-ray diffraction. Welding experiments using geometrically similar AM specimens show that, with regard to the heat input, the energy per unit length in particular leads to significantly affected cooling times and microstructures and causes pronounced localized effects in terms of residual stresses in the upper weld beads. T2 - 46th MPA-Seminar CY - Stuttgart, Germany DA - 12.10.2021 KW - Wire Arc Additive Manufacturing KW - High-strength structural steels KW - Vickers hardness KW - Residual stresses PY - 2021 VL - 46 SP - 296 EP - 306 PB - MPA-Stuttgart AN - OPUS4-53571 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Wandtke, Karsten A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Einfluss der Wärmeführung auf die Eigenschaften und fertigungsbedingten Beanspruchungen additiv geschweißter hochfester Feinkornbaustähle N2 - Hochfeste Feinkornbaustähle verfügen über ein großes Potenzial für gewichtsoptimierte, effiziente Strukturen in vielen modernen Stahlkonstruktion. Weitere Effizienzsteigerungen können durch additives Fertigen sowie bionische Bauweisen erreicht werden. Kommerzielle hochfeste Zusatzwerkstoffe für additives MSG-Schweißen (engl.: Wire Arc Additive Manufacturing, WAAM) sind bereits von den Schweißzusatzherstellern lieferbar. Derzeit ist jedoch eine breite industrielle Anwendung insbesondere für KMU aufgrund fehlender quantitativer Erkenntnisse und Richtlinien bezüglich schweißbedingter Beanspruchungen und Bauteilsicherheit während der Herstellung und des Betriebs stark limitiert. In einem gemeinsamen Forschungsprojekt (FOSTA-P1380/IGF21162BG) der BAM und der TU Chemnitz werden die mit Eigenspannungsausbildung und der Gefahr einer Kaltrissbildung verbundenen prozess- und werkstoffbedingten sowie konstruktiven Einflüsse untersucht. Im Fokus dieser Analysen steht die Bestimmung der Wechselwirkungen zwischen WAAM-Prozessparametern bzw. der Wärmeführung auf das Gefüge und die Eigenspannungen. Hierfür werden Referenzproben als offene Hohlquader mit definierten Abmessungen vollautomatisiert mit einem speziellen, hochfesten WAAM-Massivdraht (Streckgrenze >790 MPa) geschweißt. Die gezielte Einstellung der geometrischen Eigenschaften erfolgt durch Schweißparameter und Nahtaufbau bei ca. 4 kg/h mittlerer Abschmelzleistung. Die Wärmeführung wird innerhalb eines statistischen Versuchsplanes mittels Streckenenergie (200 kJ/m bis 650 kJ/m) und Zwischenlagentemperatur (100 °C bis 300 °C) so variiert, dass die t8/5-Abkühlzeiten dem empfohlenen Verarbeitungsbereich entsprechen (ca. 5 s bis 20 s). Ziel ist es bei konstanten geometrisch-konstruktiven Randbedingungen, den Einfluss der Wärmeführung auf Gefüge und resultierende Eigenspannungen zu analysieren. Für die Streckenenergie können neben den Gefügeeinflüssen aufgrund der resultierenden Abkühlzeit deutliche Effekte insbesondere auf die lokalen Eigenspannungen im Bauteil belegt werden. Das Schweißen mit zu hoher Wärmeeinbringung bzw. Abschmelzleistung kann zu ungünstigen Gefüge- und Bauteileigenschaften führen, gleichzeitig jedoch niedrigere Zugeigenspannungsniveaus bewirken. Solche komplexen Wechselwirkungen gilt es letztlich mit diesen Untersuchungen zu klären, um leicht anwendbare Verarbeitungsempfehlungen und Normvorgaben für ein wirtschaftliches, anforderungsgerechtes und risssicheres WAAM von hochfesten Stählen den Anwendern zur Verfügung zu stellen. T2 - DVS Congress 2021 CY - Online meeting DA - 14.09.2021 KW - MAG-Schweißen KW - Hochfester Stahl KW - Eigenspannungen KW - Additive Fertigung KW - Kaltrisssicherheit PY - 2021 SN - 978-3-96144-146-4 VL - 371 SP - 16 EP - 22 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-56669 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Härtel, S. A1 - Wandtke, Karsten A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Einfluss der Wärmeführung auf die Eigenschaften und fertigungsbedingten Beanspruchungen additiv geschweißter hochfester Feinkornbaustähle N2 - Hochfeste Feinkornbaustähle verfügen über ein großes Potenzial für gewichtsoptimierte, effiziente Strukturen in vielen modernen Stahlkonstruktion. Weitere Effizienzsteigerungen können durch additives Fertigen sowie bionische Bauweisen erreicht werden. Kommerzielle hochfeste Zusatzwerkstoffe für additives MSG-Schweißen (engl.: Wire Arc Additive Manufacturing, WAAM) sind bereits von den Schweißzusatzherstellern lieferbar. Derzeit ist jedoch eine breite industrielle Anwendung insbesondere für KMU aufgrund fehlender quantitativer Erkenntnisse und Richtlinien bezüglich schweißbedingter Beanspruchungen und Bauteilsicherheit während der Herstellung und des Betriebs stark limitiert. In einem gemeinsamen Forschungsprojekt (FOSTA-P1380/IGF21162BG) der BAM und der TU Chemnitz werden die mit Eigenspannungsausbildung und der Gefahr einer Kaltrissbildung verbundenen prozess- und werkstoffbedingten sowie konstruktiven Einflüsse untersucht. Im Fokus dieser Analysen steht die Bestimmung der Wechselwirkungen zwischen WAAM-Prozessparametern bzw. der Wärmeführung auf das Gefüge und die Eigenspannungen. Hierfür werden Referenzproben als offene Hohlquader mit definierten Abmessungen vollautomatisiert mit einem speziellen, hochfesten WAAM-Massivdraht (Streckgrenze >790 MPa) geschweißt. Die gezielte Einstellung der geometrischen Eigenschaften erfolgt durch Schweißparameter und Nahtaufbau bei ca. 4 kg/h mittlerer Abschmelzleistung. Die Wärmeführung wird innerhalb eines statistischen Versuchsplanes mittels Streckenenergie (200 kJ/m bis 650 kJ/m) und Zwischenlagentemperatur (100 °C bis 300 °C) so variiert, dass die t8/5-Abkühlzeiten dem empfohlenen Verarbeitungsbereich entsprechen (ca. 5 s bis 20 s). Ziel ist es bei konstanten geometrisch-konstruktiven Randbedingungen, den Einfluss der Wärmeführung auf Gefüge und resultierende Eigenspannungen zu analysieren. Darüber hinaus erfolgt die Bestimmung des Einflusses der t8/5-Abkühlzeit auf die mechanisch-technologischen Eigenschaften des speziellen, hochfesten WAAM-Massivdrahts mithilfe von Dilatometeranalysen. Für die Streckenenergie können neben den Gefügeeinflüssen aufgrund der resultierenden Abkühlzeit deutliche Effekte insbesondere auf die lokalen Eigenspannungen im Bauteil belegt werden. Das Schweißen mit zu hoher Wärmeeinbringung bzw. Abschmelzleistung kann zu ungünstigen Gefüge- und Bauteileigenschaften führen, gleichzeitig jedoch niedrigere Zugeigenspannungsniveaus bewirken. Die Dilatometeranalysen zeigen für den untersuchten WAAM-Schweißzusatzwerkstoff eine großes t8/5-Zeitfenster mit einer vergleichsweise geringen Abnahme der Zugfestigkeit mit zunehmender t8/5-Abkühlzeit. Solche komplexen Wechselwirkungen gilt es letztlich mit diesen Untersuchungen zu klären, um leicht anwendbare Verarbeitungsempfehlungen und Normvorgaben für ein wirtschaftliches, anforderungsgerechtes und risssicheres WAAM von hochfesten Stählen den Anwendern zur Verfügung zu stellen. T2 - 42. Assistentenseminar Fügetechnik CY - Brunswick, Germany DA - 06.10.2021 KW - MAG-Schweißen KW - Hochfester Stahl KW - Eigenspannungen KW - Additive Fertigung KW - Kaltrisssicherheit PY - 2022 SN - 978-3-96144-210-2 VL - 385 IS - 42 SP - 94 EP - 101 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-56642 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -