TY - CONF A1 - von der Ehe, Kerstin A1 - Kömmling, Anja A1 - Wolff, Dietmar T1 - Neutron radiation shielding material polyethylene: consequences of gamma irradiation N2 - High and ultra-high molecular weight polyethylenes are high performance materials, which are predestined for a wide range of applications due to characteristics like high density, low weight, good dimensional stability, high chemical resistance, and high hydrogen content. These polymers are used in two demanding areas: as implant material in medical technology (only ultra-high molecular weight polyethylenes) and as a component for neutron shielding purposes in casks for storage and transport of radioactive waste. In the medical field (joint replacements) as well as during neutron radiation shielding application, high and ultra-high molecular weight polyethylenes are exposed to gamma irradiation: in the first case requested as sterilization process and for surface-crosslinking and in the second case existing as a side effect of inserting the radioactive material in the cask. Given that polyethylene as shielding material has to withstand any type of degradation affecting safety relevant aspects to be applicable for long-term radiation shielding purposes for instance over a period of 40 years, the durability of the material is of special interest. High molecular weight polyethylene (HMW-PE; LUPOLEN 5261Z; Lyondell Basell) and ultra-high molecular weight polyethylene (UHMW-PE; GUR 4120; Ticona) were subjected to gamma radiation and afterwards thermally treated. The gamma doses used are in the range of 50 to 600 kGy and irradiation takes place at RT using a Co-60 source. The planned thermal treatment will take place at a temperature of 125 °C for periods of minimum 30 days and maximum of five years. With the applied conventional analytical techniques it is possible to detect structural changes of both types of polyethylene induced by gamma irradiation and certainly of thermal treatment. Through gamma irradiation melting temperature, crystallinity, and density, respectively increased. Furthermore both polyethylenes get oxidized and cross-linked. With regard to the special application as neutron radiation shielding material in casks for storage and transport of radioactive materials, the impact of irradiation lead to changes of material properties. A consolidated view indicates that the detected changes of the irradiated (U)HMW-PE are not safety relevant for long-term neutron radiation shielding purposes over a period of 40 years in Germany. T2 - WM2015 Conference CY - Phoenix, Arizona, USA DA - 15.03.2015 KW - Gamma radiation KW - Polyehtylene KW - HMW KW - DSC KW - IR KW - Crosslinking PY - 2015 SN - 978-0-9828171-4-8 SP - 15062, 1 EP - 10 AN - OPUS4-33254 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kömmling, Anja A1 - von der Ehe, Kerstin A1 - Wolff, Dietmar A1 - Jaunich, Matthias T1 - Effect of high-dose gamma irradiation on (U)HMWPE neutron shielding materials N2 - High and ultra-high molecular weight polyethylenes were gamma-irradiated with doses up to 600 kGy. The changes in the material properties were analysed using DSC, DMA, IR spectroscopy, as well as measurements of density and insoluble content. The irradiation led to an increase of the degree of crystallinity because of chain scissions during irradiation, leading to shorter and thus more mobile chains. Both the plateau value of the shear modulus G′ and the insoluble content increased with Irradiation dose, indicating the formation of additional crosslinks. Furthermore, IR spectroscopy revealed irradiation induced oxidation and the formation of double bonds, indicating that some of the hydrogen atoms responsible for the neutron shielding capability have been released. KW - Ultra high molecular weight KW - Polyethylene KW - Gamma irradiation KW - Crosslinking KW - Oxidation PY - 2018 U6 - https://doi.org/10.1016/j.radphyschem.2017.02.014 SN - 0969-806X VL - 142 SP - 29 EP - 33 PB - Elsevier AN - OPUS4-42941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kömmling, Anja A1 - Chatzigiannakis, E. A1 - Beckmann, Jörg A1 - Wachtendorf, Volker A1 - von der Ehe, Kerstin A1 - Braun, Ulrike A1 - Jaunich, Matthias A1 - Schade, U. A1 - Wolff, Dietmar T1 - Discoloration Effects of High-Dose gamma-Irradiation and Long-Term Thermal Aging of (U) HMW-PE N2 - Two polyethylene types with ultra-high (UHMWPE) and high molecular weight (HMW-PE) used as neutron radiation shielding materials in casks for radioactive waste were irradiated with doses up to 600 kGy using a 60Co gammasource. Subsequently, thermal aging at 125∘C was applied for up to one year. Degradation effects in the materials were characterized using colorimetry, UV-Visspectroscopy, IR spectroscopy, and DSC. Both materials exhibited a yellowing upon irradiation.The discoloration of UHMW-PE disappeared again after thermal aging.Therefore, the yellowing is assumed to originate fromannealable color centers in the formof free radicals that are trapped in the crystalline regions of the polymer and recombine at elevated temperatures. For the antioxidantcontaining HMWPE, yellowing was observed after both irradiation and thermal aging. The color change was correlated mainly to decomposition products of the antioxidant in addition to trapped radicals as in UHMW-PE. Additionally, black spots appeared after thermal aging of HMW-PE. KW - Irradiation KW - UHMWPE KW - Colour center KW - Yellowness index PY - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-423992 SN - 1687-9422 VL - 2017 IS - Article ID 1362491 SP - 1 EP - 10 PB - Hindawi AN - OPUS4-42399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -