TY - CONF A1 - Bruno, Giovanni A1 - Serrano Munoz, Itziar A1 - Kupsch, Andreas A1 - Müller, Bernd R. T1 - X-Ray-Refraction-Imaging-Techniques high-resolution microstructural characterization N2 - X-ray refraction is analogous to visible light deflection by matter; it occurs at boundaries between different media. The main difference between visible light and X-rays is that in the latter case deflection angles are very small, from a few seconds to a few minutes of arc (i.e., the refraction index n is near to 1). Trivially but importantly, deflection of X-rays is also sensitive to the orientation of the object boundaries. These features make X-ray refraction techniques extremely suitable to a) detect defects such as pores and microcracks and quantify their densities in bulk (not too heavy) materials, and b) evaluate porosity and particle properties such as orientation, size, and spatial distribution (by mapping). While X-ray refraction techniques cannot in general image single defects, their detectability is simply limited by the wavelength of the radiation. We thereby show the application of X-ray refraction 2D mapping (topography) and tomography to different sorts of problems in materials science and technology: 1) Sintering of SiC green bodies; 2) Porosity analysis in additively manufactured alloys; 3) Fiber de-bonding in metal and polymer matrix composites. Such techniques, especially at the Synchrotron BESSY II, Berlin, Germany, can be used in-situ, i.e. when the specimen is subjected to temperatures or external loads. Applications of in-situ X-ray refraction radiography on aluminum alloys and composites are also shown. The use of X-ray refraction analysis yields quantitative information, which can be directly input in kinetics, mechanical and damage models. T2 - ICT 2023 CY - Fürth, Germany DA - 27.02.2023 KW - X-ray refraction KW - Composites KW - In-situ KW - Additive Manufacturing KW - Sintering KW - Ceramics PY - 2023 AN - OPUS4-57200 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Erdmann, Maren A1 - Kupsch, Andreas A1 - Müller, Bernd R. A1 - Hentschel, Manfred P. A1 - Niebergall, Ute A1 - Böhning, Martin A1 - Bruno, Giovanni ED - Erdmann, Maren T1 - Diesel-induced transparency of plastically deformed high-density polyethylene JF - Journal of Materials Science N2 - High-density polyethylene becomes optically transparent during tensile drawing when previously saturated with diesel fuel. This unusual phenomenon is investigated as it might allow conclusions with respect to the material behavior. Microscopy, differential scanning calorimetry, density measurements are applied together with two scanning X-ray scattering techniques: wide angle X-ray scattering (WAXS) and X-ray refraction, able to extract the spatially resolved crystal orientation and internal surface, respectively. The sorbed diesel softens the material and significantly alters the yielding characteristics. Although the crystallinity among stretched regions is similar, a virgin reference sample exhibits strain whitening during stretching, while the diesel-saturated sample becomes transparent. The WAXS results reveal a pronounced fiber texture in the tensile direction in the stretched region and an isotropic orientation in the unstretched region. This texture implies the formation of fibrils in the stretched region, while spherulites remain intact in the unstretched parts of the specimens. X-ray refraction reveals a preferred orientation of internal surfaces along the tensile direction in the stretched region of virgin samples, while the sample stretched in the diesel-saturated state shows no internal surfaces at all. Besides from stretching saturated samples, optical transparency is also obtained from sorbing samples in diesel after stretching. KW - PE-HD Sorption KW - Cavitation KW - Diesel Fuel KW - X-ray refraction KW - WAXS KW - Internal Surfaces KW - Crystal Texture PY - 2019 DO - https://doi.org/10.1007/s10853-019-03700-8 SN - 1573-4803 SN - 0022-2461 VL - 54 IS - 17 SP - 11739 EP - 11755 PB - Springer US CY - US AN - OPUS4-48226 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Evsevleev, Sergei A1 - Müller, Bernd R. A1 - Lange, Axel A1 - Kupsch, Andreas T1 - Refraction driven X-ray caustics at curved interfaces JF - Nuclear Instruments and Methods in Physics Research Section A: Accelerators, Spectrometers, Detectors and Associated Equipment N2 - X-ray refraction related interaction has received rising interest since about two decades in the field of imaging, beam shaping and analysis although being discovered a century ago. Due to refraction at interfaces in inhomogeneous media X-rays undergo natural focusing (or defocusing) of waves, revealing caustics. Such Kind of intensity patterns are well-known for visible light, but have been sparsely discussed for X-rays. The Variation of irradiation density may be predicted in case of known shapes. Analogously to light optics, the intensity distributions cover several orders of magnitude including complete extinction. The partly convergent (and divergent) caustic stripes originate from narrow zones of typical size of some 10−6 of the boundary curvature radius. For the deflection of plane wave synchrotron radiation (energy in the range of some keV to some ten keV) at rods and tubes of several μm diameter, we find good Agreement between experiments and modeling by ray tracing according to Snell’s law without additional diffraction contributions. Apart from Basic Research implications, caustics may influence the performance of irradiation technologies such as sterilization or molecular cross-linking. KW - X-ray caustics KW - X-ray refraction KW - Irradiation KW - Radiation shielding KW - Synchrotron Radiation PY - 2019 UR - http://www.sciencedirect.com/science/article/pii/S0168900218314591 DO - https://doi.org/10.1016/j.nima.2018.10.152 SN - 0168-9002 SN - 1872-9576 VL - 916 SP - 275 EP - 282 PB - Elsevier AN - OPUS4-46924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kupsch, Andreas A1 - Trappe, Volker A1 - Müller, Bernd R. A1 - Bruno, Giovanni T1 - Evolution of CFRP stress cracks observed by in situ X-ray refractive imaging N2 - Modern air-liners and rotor blades of wind turbines are basically made of fiber reinforced plastics (FRP). Their failure heavily impairs the serviceability and the operational safety. Consequently, knowledge of the failure behavior under static and cyclic loads is of great interest to estimate the operational strength and to compare the performance of different materials. Ideally, the damage evolution under operational load is determined with in-situ non-destructive testing techniques. Here, we report on in-situ synchrotron X-ray imaging of tensile stress induced cracks in carbon fiber reinforced plastics (CFRP) due to inter fiber failure. An in-house designed compact-tensile testing machine with a load range up to 15 kN was integrated into the beam path. Since conventional radiographs do not reveal sufficient contrast to distinct cracks due to inter fiber failure and micro cracking from fiber bundles, the Diffraction Enhanced Imaging technique (DEI) is applied in order to separate primary and scattered (refracted) radiation by means of an analyzer crystal. In the laboratory, scanning X-ray refraction topography of CFRP has been applied long before but it comes along with several disadvantages: the long total measuring time hampers real time (in-situ) measurements and the required small beam size hinders end-to-end imaging. The introduced technique overcomes both drawbacks. Imaging and tensile test rig are run unsynchronized at the greatest possible frame rate (0.7 s-1 at 28.8 µm pixel size) and smallest possible strain rate (5.5∙10-4 s-1). For 0°/90° non-crimped fabrics (ncf) the first inter fiber cracks occurred at 380 MPa (strain 0.7 %). Prior to failure at about 760 MPa (strain 2.0 %) we observe the evolution of a nearly equidistant 1 mm grid of cracks running across the entire sample in the fully damaged state before total failure. T2 - 41st Risø International Symposium on Materials Science - Materials and Design for Next Generation Wind Turbine Blades CY - Online meeting DA - 07.09.2020 KW - X-ray refraction KW - Diffraction Enhanced Imaging KW - Carbon Fiber Reinforced Plastics KW - In situ tensile test KW - Crack evolution PY - 2020 AN - OPUS4-51223 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kupsch, Andreas A1 - Trappe, Volker A1 - Müller, Bernd R. A1 - Bruno, Giovanni T1 - Evolution of CFRP stress cracks observed by in situ X-ray refractive imaging N2 - Modern air-liners and wind turbine rotor blades are made up primarily of fiber reinforced plastics. Failure of these materials heavily impairs the serviceability and the operational safety. Consequently, knowledge of the failure behavior under static and cyclic loads is of great interest to estimate the operational strength and to compare the performance of different materials. Ideally, the damage evolution under operational load is determined with in-situ non-destructive testing techniques. Here, we report in-situ synchrotron X-ray imaging of tensile stress induced cracks in carbon fiber reinforced plastics due to inter-fiber failure. An inhouse designed compact tensile testing machine with a load range up to 15 kN was integrated into the beamline. Since conventional radiographs do not reveal sufficient contrast to distinguish cracks due to inter-fiber failure and micro cracking from fiber bundles, the Diffraction Enhanced Imaging (DEI) technique is applied in order to separate primary and scattered (refracted) radiation by means of an analyzer crystal. This technique allows fast measurements over large fields-of-view and is ideal for in-situ investigations. T2 - 12th BESSY@HZB User Meeting 2020 CY - Online meeting DA - 10.12.2020 KW - Carbon Fiber Reinforced Plastics KW - Crack evolution KW - Diffraction Enhanced Imaging KW - In situ tensile test KW - X-ray refraction PY - 2020 AN - OPUS4-51802 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kupsch, Andreas A1 - Hentschel, Manfred P. A1 - Lange, Axel A1 - Bruno, Giovanni A1 - Müller, Bernd R. T1 - Direct X-ray refraction of micro structures T2 - ECNDT 2014 - 11th European conference on non-destructive testing (Proceedings) N2 - For the first time we present direct 2D imaging of refracted X-rays without any discrimination of the Primary radiation. X-refraction works in analogy to visible light optics: X-rays are entirely deflected at interfaces where discontinuities of (electron) density occur. This is demonstrated at the example of inner and outer surfaces of model samples of well-defined geometry (fibres, capillaries, and monodisperse micro particles). The samples are scanned through a 50 μm monochromatic (20 keV) pencil beam. In order to warrant a sufficient angular resolution a 2D detector (pixel size 7 μm) is placed 3 m downstream of the sample. Scanning the sample in micron steps allows for detecting local changes of interface / surface orientation directly in two dimensions. At the actual angular resolution of about 3 seconds of arc (scattering vector increments Δk = 10-3 nm-1) and 50 μm spatial resolution (scanning) the material’s inner surfaces (with nanometer separation) can be characterized even at sampling rates below 1 second per frame. Moreover, our technique is suited to directly determine particle diameters of up to 250 nm by means of diffraction fringes. Some potential applications to technical submicron structures are discussed. T2 - ECNDT 2014 - 11th European conference on non-destructive testing CY - Prague, Czech Republic DA - 06.10.2014 KW - X-ray refraction KW - Phase contrast KW - Edge artefact KW - Soft matter radiography KW - Wavelet transformation KW - Huygens elementary waves PY - 2014 SN - 978-80-214-5018-9 SP - 1 EP - 9 AN - OPUS4-31970 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kupsch, Andreas A1 - Hentschel, Manfred P. A1 - Lange, Axel A1 - Müller, Bernd R. T1 - X-ray dark field imaging T2 - ECNDT 2014 - 11th European conference on non-destructive testing (Proceedings) N2 - A new kind of enhanced contrast X-ray imaging of weakly absorbing materials in dark field mode is presented. Samples such as plastics and biological tissue are a perpetual challenge for radiographic imaging. Recent innovative approaches such as Diffraction Enhanced Imaging (DEI), “phase contrast”, grating interferometry (Talbot-Lau), or Refraction Enhanced Imaging (REI) have in common that they yield enhanced contrast based on deflected X-rays. Here, we introduce a REI modification, which works with a slightly bent single crystal reflecting in Bragg geometry. The samples are placed upstream of the thin crystal within a parallel synchrotron beam. The crystal’s curvature creates a dark-field stripe in the transmission image, similar to the inverse of a Darwin-Prins rocking curve of plane crystals. The reflection condition is met better or worse as a steady function of incidence position. Refracted beam portions of sample interfaces appear bright on black stripes. The entire image is finally synthesized by multiple dark-field stripes. The technique is an alternative to the mentioned techniques. We demonstrate the technique’s advantage by examples of biological and technical microstructures. T2 - ECNDT 2014 - 11th European conference on non-destructive testing CY - Prague, Czech Republic DA - 06.10.2014 KW - X-ray refraction KW - Refraction enhanced imaging (REI) KW - Phase contrast KW - Radiology KW - Soft matter radiography PY - 2014 SN - 978-80-214-5018-9 SP - 1 EP - 7 AN - OPUS4-31971 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Hentschel, Manfred P. A1 - Bruno, Giovanni A1 - Onel, Yener A1 - Wolk, Thomas A1 - Staude, Andreas A1 - Ehrig, Karsten A1 - Müller, Bernd R. T1 - Evaluating porosity in cordierite diesel particulate filter materials: advanced X-ray techniques and new statistical analysis methods T2 - ECNDT 2014 - 11th European conference on non-destructive testing (Proceedings) T2 - ECNDT 2014 - 11th European conference on non-destructive testing CY - Prague, Czech Republic DA - 2014-10-06 KW - Porous ceramics KW - Diesel particulate filters KW - Pore orientation KW - X-ray computed tomography KW - X-ray refraction KW - DIVA algorithm KW - Phase contrast KW - Edge artefact KW - Soft matter radiography KW - Wavelet transform KW - Huygens elementary waves PY - 2014 SN - 978-80-214-5018-9 SP - 1 EP - 8(?) AN - OPUS4-31973 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Hentschel, Manfred P. A1 - Onel, Yener A1 - Wolk, Thomas A1 - Staude, Andreas A1 - Ehrig, Karsten A1 - Müller, Bernd R. A1 - Bruno, Giovanni T1 - Evaluating porosity in cordierite diesel particulate filter materials, part 1 X-ray refraction JF - Journal of ceramic science and technology N2 - Bi-continuous porous ceramics for filtration applications possess a particularly complicated microstructure, with porosity and solid matter being intermingled. Mechanical, thermal, and filtration properties can only be precisely estimated if the morphology of both solid matter and porosity can be quantitatively determined. Using x-ray absorption and refraction, we quantitatively evaluate porosity and pore orientation in cordierite diesel particulate filter ceramics. Porosity values turn out to agree with mercury intrusion measurements, while pore orientation factors agree with published crystallographic texture data. KW - Porous ceramics KW - Pore orientation KW - X-ray refraction KW - Synchrotron KW - Interface PY - 2013 DO - https://doi.org/10.4416/JCST2013-00021 SN - 2190-9385 VL - 4 IS - 4 SP - 169 EP - 176 PB - Göller CY - Baden-Baden AN - OPUS4-29939 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kupsch, Andreas A1 - Müller, Bernd R. A1 - Lange, Axel A1 - Bruno, Giovanni T1 - Microstructure Characterization of Ceramics via 2D and 3D X-Ray Refraction Techniques JF - Journal of the European Ceramic Society N2 - 3D imaging techniques are very fashionable nowadays, and allow enormous progress in understanding ceramic microstructure, its evolution, and its link to mechanical, thermal, and transport properties. In this feature article, we report the use of a powerful, yet not so wide-spread, set of X-ray techniques based on refraction effects. X-ray refraction allows determining internal specific surface (surface per unit volume) in a non-destructive fashion, position and orientation sensitive, and with a nanometric detectability. While the techniques are limited by the X-ray absorption of the material under investigation, we demonstrate showcases of ceramics and composite materials, where understanding of process parameter influence or simply of microstructural parameters could be achieved in a way unrivalled even by high-resolution techniques such as electron microscopy or computed tomography. KW - X-ray refraction KW - Porosity KW - Specific surface KW - Crack detection KW - Composites PY - 2017 DO - https://doi.org/10.1016/j.jeurceramsoc.2016.12.031 SN - 0955-2219 SN - 1873-619X VL - 37 IS - 5 SP - 1879 EP - 1889 PB - Elsevier CY - Amsterdam AN - OPUS4-39094 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kupsch, Andreas A1 - Trappe, Volker A1 - Müller, Bernd R. A1 - Bruno, Giovanni T1 - Evolution of CFRP stress cracks observed by in situ X-ray refractive imaging JF - IOP conference series: Materials science and engineering N2 - Modern air-liners and wind turbine rotor blades are made up primarily of fiber reinforced plastics. Failure of these materials heavily impairs the serviceability and the operational safety. Consequently, knowledge of the failure behavior under static and cyclic loads is of great interest to estimate the operational strength and to compare the performance of different materials. Ideally, the damage evolution under operational load is determined with in situ non-destructive testing techniques. Here, we report in-situ synchrotron X-ray imaging of tensile stress induced cracks in carbon fiber reinforced plastics due to inter-fiber failure. An inhouse designed compact tensile testing machine with a load range up to 15 kN was integrated into the beamline. Since conventional radiographs do not reveal sufficient contrast to distinguish cracks due to inter-fiber failure and micro cracking from fiber bundles, the Diffraction Enhanced Imaging (DEI) technique is applied in order to separate primary and scattered (refracted) radiation by means of an analyzer crystal. This technique allows fast measurements over large fields-of-view and is ideal for in-situ investigations. Imaging and the tensile test are run at the highest possible frame rate (0.7 s-1 ) and the lowest possible strain rate (5.5∙10-4 s -1 ). For 0°/90° non-crimp fabrics, the first inter-fiber cracks occur at 380 MPa (strain 0.8 %). Prior to failure at about 760 MPa (strain 2.0 %), we observe the evolution of nearly equidistant (1 mm distance) cracks running across the entire sample in the fully damaged state. KW - X-ray refraction KW - Diffraction Enhanced Imaging KW - Carbon Fiber Reinforced Plastics KW - In situ tensile test KW - Crack evolution PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-515060 DO - https://doi.org/10.1088/1757-899X/942/1/012035 SN - 1757-8981 SN - 1757-899X VL - 942 SP - 012035-1 EP - 012035-9 PB - IOP publishing CY - Bristol, UK AN - OPUS4-51506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lange, Axel A1 - Kupsch, Andreas A1 - Müller, Bernd R. A1 - Hentschel, Manfred P. T1 - Edge artefacts of radiographic images by X-ray refraction T2 - 18th WCNDT - World conference on nondestructive testing (Proceedings) N2 - The relevance of nano sized structures and interfaces in upcoming technologies requires new non-destructive Xray techniques exploiting attenuation as well as scattering. In the course of driving the resolution and the contrast of modern radiography into micro and nano metre dimension the inevitable scattering effects require increased attention. Several radiologists interpret the observed edge artefacts simply by 'phase contrast' due to different X-ray path lengths within the sample and others refer to Fresnel scattering. The ultra small angle scattering is of high intensity and may reach the level of the primary beam. We present monochromatic synchrotron measurements on rather simply shaped objects (such as plates and cylinders) which prove clearly the dominance of refraction intensity over total reflection and coherent small angle scattering. The refraction conditions hold for angles of incidence of several degrees to the surface, but typical deflection angles range from several seconds to minutes of arc. Additionally to the concept of 'phase contrast' of the primary beam its deflection becomes the essential issue. The appropriate removal of the attenuation contribution enables the imaging of inner surfaces and interfaces by refraction scanning topography. The presented measurements of reference particles demonstrate the reliability of laboratory refraction scanners applying X-ray tubes. T2 - 18th WCNDT - World conference on nondestructive testing CY - Durban, South Africa DA - 2012-04-16 KW - X-ray refraction KW - Small angle scattering KW - Phase contrast radiography KW - Refraction topography KW - Nanostructures KW - Nanocracks PY - 2012 UR - http://www.ndt.net/article/wcndt2012/papers/274_wcndtfinal00274.pdf SN - 978-0-620-52872-6 SP - 1 EP - 11(?) AN - OPUS4-25836 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Laquai, René A1 - Müller, Bernd R. A1 - Kupsch, Andreas A1 - Nellesen, J. A1 - Tillmann, W. T1 - Characterizing damage evolution in metal matrix composites with X-ray refraction topography and in situ tensile loading N2 - In this study a metal-matrix-composite with aluminum matrix and Al2O3 particles was investigated with x-ray refraction topography and in-situ tensile loading. It could be observed that after reaching a certain load the specific surface increased steadily. However, the classical radiographs taken for comparison show no damage in the sample. T2 - 8th Joint BER II and BESSY II User Meeting CY - Berlin, Germany DA - 07.12.2016 KW - X-ray refraction KW - Metal matrix composites KW - In-situ loading KW - Synchrotron PY - 2016 AN - OPUS4-39113 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Laquai, René A1 - Schaupp, Thomas A1 - Griesche, Axel A1 - Müller, Bernd R. A1 - Kupsch, Andreas A1 - Hannemann, Andreas A1 - Kannengießer, Thomas A1 - Bruno, Giovanni T1 - Quantitative analysis of hydrogen-assisted microcracking in duplex stainless steel through X-ray refraction 3D imaging JF - Advanced engineering materials N2 - While the problem of the identification of mechanisms of hydrogen assisted damage has and is being thoroughly studied, the quantitative analysis of such damage still lacks suitable tools. In fact, while, for instance, electron microscopy yields excellent characterization, the quantitative analysis of damage requires at the same time large field-of-views and high spatial resolution. Synchrotron X-ray refraction techniques do possess both features. In this work, we show how synchrotron X-ray refraction computed tomography (SXRCT) can quantify damage induced by hydrogen embrittlement in a lean duplex steel, yielding results that overperform even those achievable by synchrotron X-ray absorption computed tomography. As already reported in literature, but this time using a non-destructive technique, we show that the hydrogen charge does not penetrate to the center of tensile specimens. By the comparison between virgin and hydrogen-charged specimens, we deduce that cracks in the specimen bulk are due to the rolling process rather than hydrogen-assisted. We show that (micro)cracks propagate from the surface of tensile specimens to the interior with increasing applied strain, and we deduce that a significant crack propagation can only be observed short before rupture. KW - 2101 duplex stainless steel KW - Hydrogen embrittlement KW - Synchrotron radiation KW - X-ray refraction KW - Computed tomography KW - Microcracking PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-542811 DO - https://doi.org/10.1002/adem.202101287 SN - 1438-1656 SP - 1 EP - 10 PB - Wiley-VCH CY - Weinheim AN - OPUS4-54281 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Laquai, René A1 - Schaupp, Thomas A1 - Müller, Bernd R. A1 - Griesche, Axel A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Kannengießer, Thomas A1 - Bruno, Giovanni T1 - 3D Crack analysis in hydrogen charged lean duplex stainless steel with synchrotron refraction CT T2 - Proceeedings of the 19th World Conference on Non-Destructive Testing 2016 N2 - Hydrogen in metals can cause a degradation of the mechanical properties, the so-called hydrogen embrittlement. In combination with internal stresses, hydrogen assisted cracking (HAC) can occur. This phenomenon is not completely understood yet. To better characterise the cracking behaviour, it is important to gain information about the evolution of the 3D crack network. For this purpose samples of lean duplex stainless steel were loaded with hydrogen by means of electrochemical charging and investigated by means of synchrotron refraction CT and SEM fractography after uniaxial tensile loading. Synchrotron refraction CT is an analyser-based imaging (ABI) technique. It uses a Si (111) single crystal as analyser, which is placed into the beam path between sample and detector. According to Bragg’s law only incident x-rays within a narrow range around the Bragg-angle are diffracted from the analyser into the detector. Hence, the analyser acts as an angular filter for the transmitted beam. This filtering allows to turn the refraction and scattering of x-rays into image contrast. Refraction occurs at all interfaces, where the density of the material changes and is more sensitive to density changes than the attenuation. Therefore, it is possible to detect smaller cracks than with classical x-ray imaging techniques, like CT, with comparable spacial resolution. It also visualises the 3D structure of the cracks and gains quantitative information about their morphology and distribution. Since cracks introduced by HAC are usually very small and have a small opening displacement, synchrotron refraction CT is expected to be well suited for imaging this cracking mechanism and can be a valuable tool to characterise the formation and the evolution of a 3D crack network. T2 - WCNDT 2016 CY - München, Germany DA - 13.06.2016 KW - X-ray refraction KW - Computed tomography KW - Hydrogen assisted cracking KW - Duplex stainless steel PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-366481 SN - 978-3-940283-78-8 VL - BB 158 SP - Tu.4.B.3, 1 EP - 9 AN - OPUS4-36648 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mani, Deepak A1 - Kupsch, Andreas A1 - Müller, Bernd R. A1 - Bruno, Giovanni T1 - Diffraction Enhanced Imaging Analysis with Pseudo-Voigt Fit Function JF - Journal of Imaging N2 - Diffraction enhanced imaging (DEI) is an advanced digital radiographic imaging technique employing the refraction of X-rays to contrast internal interfaces. This study aims at qualitatively and quantitatively evaluating images acquired using this technique and to assess how different fitting functions to the typical rocking curves (RCs) influence the quality of images. RCs are obtained for every image pixel. This allows the separate determination of the absorption and the refraction properties of the material in a position-sensitive manner. Comparison of various types of fitting functions reveals that the Pseudo-Voigt (PsdV) function is best suited to fit typical RCs. A robust algorithm was developed in the Python programming language, which reliably extracts the physically meaningful information from each pixel of the image. We demonstrate the potential of the algorithm with two specimens: a silicone gel specimen that has well-defined interfaces, and an additively manufactured polycarbonate specimen. KW - Diffraction Enhanced Imaging KW - Analyzer-Based Imaging KW - X-ray refraction KW - Non-Destructive Evaluation KW - Pseudo-Voigt fit function KW - Python PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-553791 DO - https://doi.org/10.3390/jimaging8080206 SN - 2313-433X VL - 8 IS - 8 SP - 1 EP - 13 PB - MDPI CY - Basel, Switzerland AN - OPUS4-55379 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mouiya, M. A1 - Martynyuk, M. A1 - Kupsch, Andreas A1 - Laquai, R. A1 - Müller, Bernd R. A1 - Doyen, N.T. A1 - Tamraoui, Y. A1 - Serrano Munoz, Itziar A1 - Huger, M. A1 - Kachanov, M. A1 - Bruno, Giovanni T1 - The stress–strain behavior of refractory microcracked aluminum titanate: The effect of zigzag microcracks and its modeling JF - Journal of the American Ceramic Society N2 - The stress–strain behavior of ceramics, such as aluminum titanate, has certain features that are unusual for brittle materials—in particular, a substantial nonlinearity under uniaxial tension, and load–unload hysteresis caused by the sharp increase of the incremental stiffness at the beginning of unloading. These features are observed experimentally and are attributed to microcracking. Here we compare different degrees of stress–strain nonlinearity of aluminum titanate materials and quantitatively model them. We use advanced mechanical testing to observe the mechanical response at room and high temperature; electron microscopy, and X-ray refraction radiography to observe the microstructural changes. Experiments show that two types of microcracks can be distinguished: (i) microcracks induced by cooling from the sintering temperature (due to heterogeneity and anisotropy of thermal expansion), with typical sizes of the order of grain size, and (ii) much larger microcracks generated by the mechanical loading. The two microcrack types produce different effects on the stress–strain curves. Such microcracks and the features of the stress–strain behavior depend on the density of the cooling-induced microcracks and on the distribution of grain sizes. They are modeled analytically and numerically. KW - Hystersis KW - Nonlinear stress-strain curve KW - Refractory KW - Stiffness KW - X-ray refraction PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-580517 DO - https://doi.org/10.1111/jace.19325 SN - 1551-2916 VL - 106 SP - 6995 EP - 7008 PB - Wiley-Blackwell CY - Oxford [u.a.] AN - OPUS4-58051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Bernd R. A1 - Cooper, R.C. A1 - Lange, Axel A1 - Kupsch, Andreas A1 - Wheeler, M. A1 - Hentschel, Manfred P. A1 - Staude, Andreas A1 - Pandey, A. A1 - Shyam, A. A1 - Bruno, Giovanni T1 - Stress-induced microcrack density evolution in β-eucryptite ceramics: Experimental observations and possible route to strain hardening JF - Acta Materialia N2 - In order to investigate their microcracking behaviour, the microstructures of several β-eucryptite ceramics, obtained from glass precursor and cerammed to yield different grain sizes and microcrack densities, were characterized by laboratory and synchrotron x-ray refraction and tomography. Results were compared with those obtained from scanning electron microscopy (SEM). In SEM images, the characterized materials appeared fully dense but computed tomography showed the presence of pore clusters. Uniaxial tensile testing was performed on specimens while strain maps were recorded and analyzed by Digital Image Correlation (DIC). X-ray refraction techniques were applied on specimens before and after tensile testing to measure the amount of the internal specific surface (i.e., area per unit volume). X-ray refraction revealed that (a) the small grain size (SGS) material contained a large specific surface, originating from the grain boundaries and the interfaces of TiO2 precipitates; (b) the medium (MGS) and large grain size (LGS) materials possessed higher amounts of specific surface compared to SGS material due to microcracks, which decreased after tensile loading; (c) the precursor glass had negligible internal surface. The unexpected decrease in the internal surface of MGS and LGS after tensile testing is explained by the presence of compressive regions in the DIC strain maps and further by theoretical arguments. It is suggested that while some microcracks merge via propagation, more close mechanically, thereby explaining the observed X-ray refraction results. The mechanisms proposed would allow the development of a strain hardening route in ceramics. KW - Beta-eucryptite KW - Microcracked ceramics KW - X-ray refraction KW - Tensile load KW - Strain hardening KW - Synchrotron KW - BAMline KW - Computed Tomography KW - CT PY - 2018 UR - http://www.sciencedirect.com/science/article/pii/S1359645417308881 DO - https://doi.org/10.1016/j.actamat.2017.10.030 SN - 1359-6454 SN - 1873-2453 VL - 144 IS - Supplement C SP - 627 EP - 641 PB - Elsevier B.V. AN - OPUS4-43024 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schob, D. A1 - Roszak, R. A1 - Sagradov, I. A1 - Sparr, H. A1 - Ziegenhorn, M. A1 - Kupsch, Andreas A1 - Léonard, Fabien A1 - Müller, Bernd R. A1 - Bruno, Giovanni T1 - Experimental determination and numerical simulation of material and damage behaviour of 3D printed polyamide 12 under quasi-static loading JF - Archives of Mechanics N2 - In order to characterise the material and damage behaviour of additively manufactured polyamide 12 (PA12) under quasi-static load and to implement it in a numerical model, experiments under quasi-static load as well as microstructural investigations were carried out. Selective laser sintering (SLS) was used as the manufacturing process. For the classification of the material behaviour, quasi-static cyclic tests with holding times as well as tensile tests were performed. X-ray refraction and computed tomography (CT) were used to investigate the damage behaviour. The Chaboche model, which has already been applied for metallic materials under thermomechanical loading, served as the basis for the selection of the numerical material model. The same procedure was used for the selection of the damage model, where the Gurson–Tvergaard–Needleman (GTN) model was chosen, which was already used for porous metallic materials. The Chaboche model shows very good agreement with experimental results. Furthermore, the coupling with the GTN model allows a very good modelling of the damage behaviour. Finally, it could be shown that the selected models are suitable to simulate the material and damage behaviour of 3D printed PA12. KW - Polyamide 12 KW - 3D printing KW - Viscoplastic KW - Chaboche model KW - Damage KW - GTN model KW - X-ray refraction KW - Computed tomography PY - 2019 DO - https://doi.org/10.24423/aom.3162 SN - 0373-2029 VL - 71 IS - 4-5 SP - 507 EP - 526 PB - IPPT PAN - Polish Academy of Sciences, Institute of Fundamental Technological Research CY - Warsaw AN - OPUS4-49409 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schob, D. A1 - Sagradov, I. A1 - Roszak, R. A1 - Sparr, H. A1 - Franke, R. A1 - Ziegenhorn, M. A1 - Kupsch, Andreas A1 - Léonard, Fabien A1 - Müller, Bernd R. A1 - Bruno, Giovanni T1 - Experimental determination and numerical simulation of material and damage behaviour of 3D printed polyamide 12 under cyclic loading JF - Enginnering Fracture Mechanics N2 - The material and damage behaviour of additively manufactured polyamide 12 under cyclic loading was characterized by cyclic tests and microstructure analysis by using microscopy, X-ray refraction, and computed tomography. The results were used to determine parameters for the viscoplastic material model by Chaboche and a damage model by Gurson-Tvergaard-Needleman. The temperature was monitored during the experiments and the self-heating effect was observed. By including this effect, a higher accuracy could be achieved with the results of mechanical experiments. KW - 3D printing Polyamide 12 KW - Chaboche model KW - GTN model KW - Material and damage behaviour KW - X-ray refraction KW - Computed tomography PY - 2020 DO - https://doi.org/10.1016/j.engfracmech.2019.106841 SN - 0013-7944 VL - 229 SP - 106841-1 EP - 106841-13 PB - Elsevier Ltd. CY - Amsterdam AN - OPUS4-50557 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -