TY - CONF A1 - Fritzsche, André A1 - Avilov, Vjaceslav A1 - Gumenyuk, Andrey A1 - Hilgenberg, Kai A1 - Rethmeier, Michael T1 - High power laser beam welding of thick-walled ferromagnetic steels with electromagnetic weld pool support N2 - The paper describes an experimental investigation of high power laser beam welding with an electromagnetic weld pool support for up to 20 mm thick plates made of duplex steel (AISI 2205) and mild steel (S235JR). The results of the welding tests show a successful application of this technology at ferromagnetic metals. Irregular sagging was suppressed successfully. An ac-power of less than 2 kW at oscillation frequencies between 800 Hz and 1.7 kHz is necessary for a full compasation of the hydrostatic pressure. Thus, it was demonstrated that the electromagnetic weld pool support is not only limited to non-ferromagnetic metals like austenitic steels. For future studies with duplex steel, the use of filler material has to take into account with regard to the balance of the mixed austenitic and ferritic phases. T2 - LANE - 9 International Conference on Photonic Technologies CY - Fürth, Germany DA - 19.09.2016 KW - Laser beam welding KW - Thick-walled steel KW - Ferromagnetic steel KW - Weld pool support PY - 2016 AN - OPUS4-37772 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fritzsche, André A1 - Hilgenberg, Kai A1 - Teichmann, F. A1 - Pries, H. A1 - Rethmeier, Michael T1 - Electromagnetic Porosity Reduction in Laser Beam Welding of Die-Cast Aluminum Alloy N2 - The present paper investigates the electromagnetic porosity reduction in partial penetration laser beam welding of 6 mm aluminum die casting AlSi9MnMg. Applying an electromagnetic field, a significant reduction of the porosity as well as smoothing of the surface of aluminum die casting can be observed. Starting from the reference case without an electromagnetic support, the porosity was reduced by 76 %. Especially big pores can be removed from the weld pool effectively due to their beneficial volume-to-area ratio whereas very small metallurgical pores tend to remain within the weld pool even when higher magnetic flux densities are applied. T2 - Lasers in Manufacturing Conference 2017 CY - Munich, Germany DA - 26.06.2017 KW - Laser beam welding KW - Die-cast aluminum KW - Porosity reduction KW - Electromagnetic influence PY - 2017 AN - OPUS4-41245 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -