TY - CONF A1 - Suárez Ocaño, Patricia A1 - Agudo Jácome, Leonardo T1 - Oxidation Behavior of the AlMo0.5NbTa0.5TiZr Chemically Complex Alloy N2 - The chemically complex alloys that contain mostly refractory elements (rCCAs), may be highly resistant to heat and load, which makes them attractive candidates for use at extremely high temperatures associated with technological applications such as aeroengine turbines. However, the oxidation behavior remains an emerging field within the CCA community. The fully heat treated AlMo0.5NbTa0.5TiZr rCCA contains a dual-phase microstructure that resembles the γ/ γ’ pattern of the well-known Ni-base superalloys, however with a continuous Al-Zr-Ti-rich B2 ordered matrix embedding Mo-Nb-Ta-rach bcc precipitates. The question thus arises what is the oxidation behavior of this rCCA alloy? In this study, this question is addressed via in situ and ex situ X-ray diffraction (XRD) in dry and humid air in the 800–1000 °C regime. Electron microscopic investigations complement the findings. In situ synchrotron experiments were carried out at the KMC2 beamline of the Helmholtz Zentrum Berlin (HZB), with a wavelength of 1.5418 Å at 800 and 950 °C under dry and humid (≈ 40% rH, laboratory air) air for 12 h. Scanning and transmission electron microscopy was performed before and after exposure to spatially resolve the scale development ex situ. In general, 12 h exposure led to an oxide scale which internal oxidation reaches several tens of microns, and which is dominated by Zr-, Ti- and Mo-containing oxides although aluminum oxide was also always present. Main differences are observed between temperatures, while the humidity played a lesser role. T2 - International Conference on High Entropy Materials (ICHEM) 2023 CY - Knoxville, TN, USA DA - 18.06.2023 KW - High entropy superalloy KW - High temperature oxidation KW - In situ synchrotron diffraction KW - Electron microscopy PY - 2023 AN - OPUS4-63857 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wehmann, N. A1 - Lenting, C. A1 - Stawski, T. M. A1 - Agudo Jácome, Leonardo T1 - Anhydrite formation in planetary surface environments - The case of the Atacama Desert N2 - Gypsum (CaSO4∙2H2O), bassanite (CaSO4∙0.5H2O), and anhydrite (CaSO4) are essential evaporite minerals for the evolution of hyper-arid surface environments on Earth and Mars (Voigt et al. 2019; Vaniman et al. 2018). The formation mechanism of especially anhydrite has been a matter of scientific debate for more than a century (van’t Hoff et al. 1903). To date, there exists no model that can reliably predict anhydrite formation at earth’s surface conditions. While thermodynamics favor its formation, it is hardly achieved on laboratory time scales at conditions fitting either the Atacama Desert on Earth, or the surface of Mars (Wehmann et al. 2023). In light of most recent developments (e.g. Stawski et al. 2016), that advocate for a complex, non-classical nucleation mechanism for all calcium sulphates, we present an analysis of natural samples from the Atacama Desert to identify key features that promote the nucleation and growth of anhydrite under planetary surface conditions. Our analyses reveal at least three distinct anhydrite facies, with differing mineralogy and micro- to nano-structures. The facies are (1) aeolian deposits with sub-μm grain sizes, (2) (sub-)surface nodules that formed from aeolian deposits and (3) selenites with secondary anhydrite rims. Possible mechanisms of their formation will be discussed. T2 - 10th Granada-Münster Discussion Meeting CY - Münster, Germany DA - 29.11.2023 KW - Calcium sulfates KW - Nucleation KW - Planetary surface KW - Hyper-arid PY - 2023 AN - OPUS4-59111 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Suárez Ocaño, Patricia A1 - Agudo Jácome, Leonardo T1 - Creep degradation of the high entropy superalloy AlMo0.5NbTa0.5TiZr N2 - The refractory high entropy superalloy (RSA) AlMo0.5NbTa0.5TiZr was the first of a class, with a dual-phase microstructure that resembles that of γ/γ’ in Ni-base superalloys), and the open question whether it performs better as structural alloy under high temperature (HT) applications. Here, we address the HT creep behavior and its associated microstructural degradation of this RSA. The material was produced by arc-melting, heat treatment in argon (24 h @ 1400 °C + 4 h hot isostatic pressure @ 1370 °C & 170 MPa). Interrupted vacuum creep tests were performed at 900-1100 °C and 30-120 MPa. Scanning (S) and transmission (T) electron microscopy (EM) were used to reveal degradation mechanisms. At 1100 °C (Fig.1, middle), the dual A2/B2 microstructure coarsens and partially transforms into a Zr-Al-rich phase (red arrow). An additional external load pronounces directional coarsening. Results are further discussed on the base dislocation and additional damage mechanisms. T2 - International Conferende on Strength of Materials (ICSMA) 2022 CY - Metz, France DA - 26.06.2022 KW - High entropy superalloy KW - Rrafting KW - Dislocation creep KW - Phase transformation PY - 2022 AN - OPUS4-63856 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - Effect of a circular notch on [001] tensile creep behavior of the Ni-base superalloy single crystal LEK 94 at 1020 °C N2 - Ni-base superalloy single crystals have been used in turbine blades for hot sections of gas turbines for over four decades. In order to increase the efficiency of the turbines, a continuous increase in the inlet temperature of combustion gases into the turbine has driven the design of turbine blades to complicated shapes and the presence of a complex pattern of cooling channels. These three-dimensional shapes, together with the inhomogeneous distribution of stresses along the blade, induce an also complicated triaxial stress state, which does not compare to uniaxial tests that are performed to characterize high temperature properties such as creep. A round notch on a test piece represents a simple configuration that generates a quasi-isostatic stress state across the notch. In the present contribution, the effect of a sharp round notch on the microstructural micromechanisms within the notched region cylindrical bars, loaded along [001] at 1020 °C and 160 MPa net stress, is studied. To this end, a series of interrupted creep tests is conducted on plain and notched bars and the microstructure is compared. Results are discussed in terms of degree microstructural coarsening, and dislocation activity. The effect of notch generation via grinding is also discussed in these terms. The presence of carbides evolving in from residual carbon is also shown and discussed. .Funding by the German Research Association (DFG) [grant number AG 191/1] is acknowledge T2 - DGM-Arbeitskreis mechanisches Werkstoffverhalten bei hoher Temperatur CY - Hochschule Augsburg, Germany DA - 20.09.2018 KW - Superalloy single crystals KW - Microstructure KW - Electron microscopy KW - Creep KW - Multiaxial stress state PY - 2018 AN - OPUS4-46050 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - Characterization of dislocation networks N2 - The presentation shows how the three-dimensional quantification of dislocations and their characteristic features, e.g. Burgers vector, line direction, dislocation density, is carried out at the transmission electron microscope in scanning mode (STEM) at Division 5.1 at BAM. Exemplarily, the methods are shown for Ni-base superalloy single crystals, for which a short introduction is given using further TEM techniques. Additional examples on low angle grain boundaries, nucleation of oxides at dislocations and interaction of dislocations and carbides are shown. The content of the presentation was addapted, aiming at scientists who work within the DFG Priority Programme 1713 "Strong coupling of thermo-chemical and thermo-mechanical states in applied materials". T2 - SPP 1713: Focus Group Meeting Experiments CY - Berlin, Germany DA - 27.06.2016 KW - Dislocation KW - Transmission electron microscopy KW - Three-dimensional (3D) characterization KW - Ni-base superalloy KW - Creep PY - 2016 AN - OPUS4-40278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - Three-Dimensional Characterization of Superdislocation Interactions in the High Temperture and Low Stress Creep Regime of Ni-Base Superalloy Single Crystals T2 - 13th International Conference on Creep and Fracture of Engineering Materials and Structures (CREEP 2015) CY - Toulouse, France DA - 2015-05-31 PY - 2015 AN - OPUS4-34517 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - High Temperature and Low Stress (011)<01-1> Shear Creep Deformation of the Single Crystal Ni-Based Superalloy LEK 94 - elementary softening and deformation processes T2 - 17th International Conference on the Strength of Materials (ICSMA17) CY - Brno, Czech Republic DA - 2015-10-01 PY - 2015 AN - OPUS4-34516 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - Diffraction Contrast in Scanning Transmission Electron Microscopy (STEM) as a Powerful Tool for Quantitative Dislocation Analysis T2 - Symposium "Recent prograss in transmission electron microscopy and atom probe analysis of advanced high temperatur materials" vom SFB/TR 103 CY - Bochum, Germany DA - 2014-03-06 PY - 2014 AN - OPUS4-32950 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - Diffraction Contrast in Scanning Transmission Electron Microscopy (STEM) as a Powerful Tool for Quantitative Dislocation Analysis T2 - Institutskolloquium, Institut für Materialphysik der westfälischen Wilhelms-Universität Münster CY - Münster, Germany DA - 2014-06-24 PY - 2014 AN - OPUS4-32949 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - Structural Defects in Advanced Alloys and Intermetallics T2 - DGM-Arbeitskreis (AK) Mechanisches Werkstoffverhalten bei hoher Temperatur CY - Mülheim an der Ruhr, Germany DA - 2013-10-09 PY - 2013 AN - OPUS4-32952 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - Structural Defects in Advanced Alloys and Intermetallics T2 - Microscopy Conference (MC) 2013 CY - Regensburg, Germany DA - 2013-08-25 PY - 2013 AN - OPUS4-32951 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - Revealing the Nature of Melt Pool Boundaries in Additively Manufactured Stainless Steel by Nano-sized Modulation N2 - Additive manufacturing (AM) of metallic alloys has gained momentum in the past decade for industrial applications. The microstructures of AM metallic alloys are complex and hierarchical from the macroscopic to the nanometer scale. When using laser-based powder bed fusion (L-PBF) process, two main microstructural features emerge at the nanoscale: the melt pool boundaries (MPB) and the solidification cellular substructure. Here, details of the MPB are revealed to clearly show the three-dimensional nature of MPBs with changes of cell growth of direction and their relation to their surrounding cellular substructure, as investigated by transmission electron microscopy (TEM) for L-PBF 316L austenitic stainless steel (cf. Figure 1). A hitherto unknown modulated substructure with a period of 21 nm is further discovered within cells as the result of a partial Ga+-focused ion beam-induced ferritic transformation of the austenite. Cell cores and cell boundaries differ notably regarding the modulated substructure. T2 - 3. Fachtagung Werkstoffe und Additive Fertigung 2022 CY - Dresden, Germany DA - 11.05.2022 KW - Additive manufacturing KW - Austenitic steel 316L KW - Melt pool boundary KW - Microstructural characterization KW - Transmission electron microscopy PY - 2022 AN - OPUS4-54836 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - 3D reconstruction and quantification of dislocation substructures from TEM stereo pairs N2 - Dislocations are the carriers of plastic deformation. As such, their characterization offers important information on the properties they affect. In this contribution, a new tool is presented, which is incorporated in Amira ZIB Edition and allows for three-dimensional (3D) imaging and quantification of dislocations substructures from thick regions an electron-transparent specimen. In the tool, the dislocation segments are traced on diffraction contrast images that are obtained in the transmission electron microscope (TEM). The uncertainties related to the experimental setup and to the proposed method are discussed on the base of a tilt series. T2 - AVIZO / AMIRA User Meeting CY - Berlin, Germany DA - 14.11.2018 KW - Dislocation KW - Diffraction contrast KW - Scanning transmission electron microscopy (STEM) PY - 2018 AN - OPUS4-47394 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - Dislocation analysis in Ni-base superalloy single crystals N2 - The LEK94 is a Ni-base superalloy single crystal (SX) of the second generation, a materials class which is important for its high temperature creep resistance (>1000°C) in first stage blades of low-to-medium pressure gas turbines. Monocrystalline Ni-base superalloy SXs have a two-phase microstructure consisting of small cubes (' phase with the ordered L12 crystal structure, cube edge length: 500 nm), separated by thin channels (γ phase with fcc solid solution structure, channel width: 20 nm). The microstructural evolution during high temperature and low stress tensile creep has been thoroughly investigated previously, mainly for [001] loading, both in terms of dislocation activity (filling of γ channels, formation of dislocation networks, cutting of the γ’ phase) as well as phase coarsening (rafting, topological inversion). Other loading geometries have received less attention. The present work studies high temperature and low stress creep deformation of the superalloy LEK 94 at temperatures around 1000°C, where rafting occurs. Differences between loading under different uniaxial, biaxial and triaxial stress states are discussed. Stereo-microscopy and g∙b analysis in the scanning transmission electron microscopy mode (STEM) are combined for microstructural analysis. The focus is set on the role of dislocation interactions with the aging microstructure. Both development in STEM characterization methods, as well as the roles of phase coarsening, γ channel filling, microstructural heterogeneity and γ’ phase cutting are discussed. T2 - Eingeladener Vortrag CY - US Air Force Research Laboratories, Dayton, OH, USA DA - 19.07.2016 KW - Doslocation KW - Superalloy KW - Microscopy KW - Creep PY - 2016 AN - OPUS4-41945 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - Quantitative 3D Stereo Microscopy in Diffraction Contrast (S)TEM N2 - The realistic description of plastic deformation caused by dislocations demands the representative measurement of their features, e.g., Burgers vector, slip plane, line direction and density. In the case of bulk deformation of technical alloys, reliable data must be ensured for large regions. Nonetheless, the (thin) filiform nature of dislocations and also the heterogeneity in some microstructures additionally require flexible analysis techniques that resolve the details of their interactions. Strong and clear channeling contrasts, faint extinction contours and the absence of chromatic aberration make scanning transmission electron microscopy (STEM) an ideal imaging mode in wide and thick regions of TEM foils, as opposed to conventional (C)TEM. It is the purpose of this contribution to show how STEM can be applied for quantitative measurement of dislocation features. Furthermore, a new tool will be presented, which enables the three-dimensional (3D) reconstruction, visualization and quantification of dislocation densities and directions from stereo-pairs. The application of these techniques will be shown on a monocrystalline Ni-base superalloy, an important class of structural materials that has been implemented in the first row blades of gas turbines. The examples are extracted from specimens subjected to creep deformation at high temperature and low stress under various macroscopic deformation geometries. The spacial and angular accuracy are discussed as well as possible sources of error. T2 - Symposium on Advanced Mechanical and Microstructural Characterization Methods for SX Ni- and Co-based Superalloys CY - Bochum, Germany DA - 13.09.2017 KW - Dislocation KW - Scanning Transmission Electron Microscopy KW - Microscopy KW - 3D reconstruction PY - 2017 AN - OPUS4-42175 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - Mechanisms of M23C6 Carbide Precipitation in Ni-Base Superalloy Single Crystals N2 - The demand for improved castability and low angle grain boundary (LAGB) resistance has led to the addition of low contents of e.g., B, Hf, Zr or C, into large industrial gas turbine components made of Ni-base superalloy single crystals (SXs). Due to the long-term application of Ni-base superalloy SX components in the temperature regime > 1000 °C, the formation of carbides is highly probable, which could jeopardize mechanical properties, such as high cycle fatigue. In the present contribution, the effect of internal and external stresses on the nucleation and growth characteristics of M23C6 carbides is investigated. Creep experiments are performed on the Ni-base superalloy SX LEK 94, which shows a low C concentration (= 0.1 at. %), at 1020 °C under parallel and circularly notched tensile specimens at a nominal stress of 160 MPa in the crystallographic direction [001]. The carbides are then characterized via scanning (S) and transmission (T) electron microscopy (EM). Nucleation is enhanced in the dendritic cores, often as coalesced colonies, extending over micrometers within M-rich (M: Cr, Re, W, Mo) γ channels. Lath shapes with facets on {100} (parallel to growth direction) and {111} are common. These facets exist since early stages (Fig.1a) and later develop misfit dislocations (Fig.1b), preserving the orientation relationship {100}γ || {100}M23C6. Fig. 1c shows a region from the creep gage, where carbides interact with superdislocations in the γ’ phase. Possible mechanisms are discussed. T2 - European Congress and Exhibition on Advanced Materials and Processes (EUROMAT) 2017 CY - Thessaloniki, Greece DA - 17.09.2017 KW - Superalloy KW - TEM KW - Carbide KW - Nucleation KW - Pore KW - Dislocation PY - 2017 AN - OPUS4-42176 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - Cyclic operation performance of 9 -12% cr ferritic martensitic steels part 1: cyclic mechanical behavior under fatigue and creep fatigue loading N2 - 9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in fossil fueled power plants due to their excellent creep and oxidation resistance, but changes in electricity markets during the last two decades have considerably changed the typical working conditions of these facilities. The growing share of renewable energy sources in power generation forces most of these plants into flexible operation with frequent load shifts or shutdowns. These cyclic operation profiles constitute a major lifetime issue, raising the question which fundamental processes govern the reaction of ferritic-martensitic steels to cyclic load and temperature variations. The present contribution reports on current findings obtained in a multidisciplinary project funded by German Ministry of Education and Research (BMBF) which combines cyclic mechanical and cyclic oxidation testing of different 9-12% Cr grades with detailed microstructural analyses and related micromechanical modeling. In the present first part of our contribution, an overview will be given on the results obtained in the mechanical testing programme of the project. Mechanical analyses were carried out on P91 and (mainly) P92 steel grades, particularly looking at softening phenomena and lifetimes obtained in isothermal cyclic loading (low cycle fatigue, LCF), non-isothermal cyclic loading (thermo-mechanical fatigue, TMF), and service-like combinations of creep and fatigue periods. For this purpose, cylindrical specimens were extracted from thick-walled steam pipes, orthogonal to the pipe axis, and subjected to strain controlled cyclic loading (± 0.2 to ±0.5 % mechanical strain) to different degrees of softening at temperatures up to 620 °C. The test results will be presented and discussed with a focus on the impact of hold periods (i.e. combined creep-fatigue conditions) on mechanical softening, lifetime and crack formation. Details on the microstructural evolution and their representation in a micromechanical model will be given in a second, complementary contribution to this conference. T2 - 45. MPA-Seminar CY - Stuttgart, Germany DA - 01.10.2019 KW - Tempered Martensite Ferritic Steels KW - Low Cycle Fatigue KW - Creep-Fatigue KW - Thermo-Mechanical Fatigue KW - P92 PY - 2019 AN - OPUS4-50050 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo A1 - Roohbakhshan, Farshad T1 - Cyclic Operation Performance of 9-12% Cr Ferritic-Martensitic Steels. Part 2: Microstructural Evolution during Cyclic Loading and its Representation in a Physically-based Micromechanical Model N2 - The current trend towards cyclic, “flexible” operation of fossil-fueled power plants constitutes a major issue regarding lifetime and operational safety of the respective installations and their components, as was outlined in our complementary contribution (Part 1). The present contribution reports on the investigation of the microstructure evolution in cyclically loaded ferritic-martensitic steels and its representation in a physically-based micromechanical model. For this purpose, specimens of P92 steel grade from the mechanical test programme outlined in our companion contribution (Part 1) were analyzed by scanning electron microscopy (SEM), including backscattered diffraction (EBSD) mapping, and transmission electron microscopy (TEM). A novel method was implemented to improve angular resolution of EBSD scans. Additionally, a correlative microscopy approach was developed and used to correlate EBSD and TEM measurements on the same locations of thick regions of electron transparent specimens. By applying these techniques, a detailed quantitative microstructure description of the as-received material condition, namely in terms of subgrain morphology and dislocation density/distributions, was established. Comparisons of as-received and cyclically loaded conditions from tests interrupted at different stages of lifetime indicate a rapid redistribution of in-grain dislocations with a strong interaction between mobile dislocations and low angle grain boundaries (LABs). The proposed micromechanical model is formulated in a viscoplastic self-consistent (VPSC) scheme, which is a mean-field approach that allows us to include the crystal details at the level of slip systems while avoiding the considerable computational costs of full-field approaches (such as the classical crystal plasticity finite element analysis). Being physically-based, the model uses dislocation densities and includes the interaction between dislocations, e.g. annihilation of mobile dislocations, and evolution of microstructure, e.g. the grain coarsening. Particularly, the constitutive laws for dislocation evolution and interaction between dislocations and low angle boundaries are calibrated based on two-dimensional discrete dislocation dynamic (2D DDD) simulations, which are performed at a micro-/meso-scale. The results of the beforementioned EBSD experiments are considered as a direct input, involving e.g. the amount of geometrically necessary dislocations, average misorientations and grain characteristics. T2 - 45th MPA-Seminar 2019 CY - Leinfelden-Echterdingen, Germany DA - 01.10.2019 KW - Tempered martensite ferritic steel KW - Dislocation KW - Electron backscattered diffraction (EBSD) KW - Transmission electron microscopy (TEM) KW - Microstructure KW - Physically based material model PY - 2019 AN - OPUS4-49346 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kianinejad, Kaveh A1 - Fedelich, Bernard A1 - Darvishi Kamachali, Reza A1 - Schriever, Sina A1 - Manzoni, Anna Maria A1 - Agudo Jácome, Leonardo A1 - Megahed, Sandra A1 - Kamrani, Sepideh A1 - Saliwan Neumann, Romeo T1 - Experimentally informed multiscale creep modelling of additive manufactured Ni-based superalloys N2 - Excellent creep resistance at elevated temperatures, i.e. T / T_m> 0.5, due to γ-γ’ microstructure is one of the main properties of nickel-based superalloys. Due to its great importance for industrial applications, a remarkable amount of research has been devoted to understanding the underlying deformation mechanism in a wide spectrum of temperature and loading conditions. Additive manufactured (AM) nickel-based superalloys while being governed by similar γ-γ’ microstructure, exhibit AM-process specific microstructural characteristics, such as columnar grains, strong crystallographic texture (typically <001> fiber texture parallel to build direction) and compositional inhomogeneity, which in turn leads to anisotropic creep response in both stationary and tertiary phases. Despite the deep insights achieved recently on the correlation between process parameters and the resulting microstructure, the anisotropic creep behavior and corresponding deformation mechanism of these materials are insufficiently understood so far. One reason for this is the lack of capable material models that can link the microstructure to the mechanical behavior. To overcome this challenge, a multiscale microstructure-based approach has been applied by coupling crystal plasticity (CP) and polycrystal model which enables the inclusion of different deformation mechanisms and microstructural characteristics such as crystallographic texture and grain morphology. The method has been applied to experimental data for AM-manufactured INCONEL-738LC (IN738). The effect of different slip systems, texture, and morphology on creep anisotropy at 850°C has been investigated. Results suggest a strong correlation between superlattice extrinsic stacking fault (SESF) and microtwinning and observed creep anisotropy. T2 - EUROMAT 23 CY - Frankfurt a. M., Germany DA - 04.09.2023 KW - IN738LC KW - Creep anisotropy KW - Crystal plasticity PY - 2023 AN - OPUS4-58263 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - Low-Cycle Fatigue Behavior of Laser Powder Bed Fused Inconel 718 at Room and High Temperature N2 - The nickel-base superalloy Inconel 718 (IN718) is one of the most commonly used Ni-based superalloys for high temperature structural applications for its remarkable strength, as well as creep, fatigue, and corrosion resistance up to 650 °C. While IN718 has traditionally been employed as cast or wrought material, it is difficult to machine because of its high strength and toughness. The additive manufacturing of IN718 components made by metal AM has thus gained extensive attention to produce expensive near-net shaped components of high-temperature alloys such as IN718, for it saves material and costs in processing and machining steps. Among all metal additive manufacturing (AM) technologies, laser powder bed fusion (PBF-LB/M) is the most widespread, IN718 being one of the most common alloys produced with it. However, high cooling rates associated to the PBF-LB/M process, hinders the primary strengthening phases γ’’ and γ’ to form, as these cooling rates induce a dislocation cellular substructure, at which walls primary Laves phases bind segregating Nb, Ti and Mo. Many of the therefore needed heat-treatment strategies can then promote Laves-phase transformation into the stable δ phase along the cell and grain boundaries. Laves and δ phases, as well as grain-boundary primary carbides may have adverse effects on mechanical properties. The mostly needle-shaped δ phase was namely found to have a detrimental effect on creep rupture life while no direct effect on LCF fatigue life was evident. In this work room- and high-temperature (650 °C) low-cycle fatigue behavior of PBF-LB/M IN718 is investigated in the four-step heat-treated state and compared to wrought IN718. The microstructure of both materials is characterized across length scales via microscopy methods. The fatigue life at room temperature of the PBF-LB/M IN718 material is slightly lower than that for the wrought material, which is reversed at 650 °C. The cyclic stress response for both materials is marked by cyclic softening that is more pronounced at higher test temperatures. Multiple secondary cracks form at high strain amplitudes, at both room and high temperatures. High testing temperatures enhance specially crack formation at the transitions of regions between elongated grains and columns of stacked grains with ripple patterns in the PBF-LB/M material. Additional to this behavior, pronounced crack branching and deflection indicate that the cracks are controlled by sharp micromechanical gradients. T2 - EUROMAT 2025 CY - Granada, Spain DA - 14.09.2025 KW - Additive manufacturing KW - Low-cycle fatigue KW - Microstructural characterization KW - Ni-base superalloy PY - 2025 AN - OPUS4-64354 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -