TY - JOUR A1 - Fahmy, A. A1 - Saeed, A. A1 - Dawood, U. A1 - Abdelbary, H. A1 - Altmann, Korinna A1 - Schönhals, Andreas T1 - Nano-MnO2/xanthan gum composite films for NO2 gas sensing N2 - Nowadays, sensors based on polymers/nanostructured metal oxide composites have been investigated exten-sively because of their sensitivity to NO2 gas at ambient temperature. In this work, nanocomposite membranes of xanthan gum (XG) with different contents of MnO2 nanoparticles were prepared as a potential NO2 gas sensor operating at room temperature by a simple one-step oxidation-reduction reaction. The structural, morphological, thermal, and electrical properties of the composite membrane were investigated. The FT-IR results confirm the successful preparation of MnO2 through the oxidation of XG by KMnO4 and reveal further the structural changes of the XG/MnO2 nanocomposite upon its exposure to NO2 gas. The capping of the synthesized MnO2 nano-particles by XG, the surface composition of the XG/MnO2 nanocomposite membranes, and the effect of NO2 gas on the surface composition was investigated using the XPS technique. The DC conductivity and dielectric loss of nanocomposites were higher than for neat XG. The conductivities of the nanocomposites XG/MO-4, XG/MO-4/ low NO2, and XG/MO-4/high NO2 composites are half, one, and three orders of magnitude higher than that for pure XG revealing a transition from insulating to conductive properties. The results demonstrated that XG/MnO2 nanocomposite membranes are promising for potential applications in NO2 gas sensing. KW - Gas sensors KW - Membranes KW - Metal oxides KW - Nanocomposites KW - Semiconductors PY - 2022 DO - https://doi.org/10.1016/j.matchemphys.2022.127277 SN - 0254-0584 VL - 296 SP - 1 EP - 14 PB - Elsevier B.V. AN - OPUS4-56769 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Saeed, A. M. A1 - Saied, M. A. A1 - Szymoniak, Paulina A1 - Altmann, Korinna A1 - Schönhals, Andreas A1 - Fahmy, Alaa T1 - High performance novel polyelectrolyte membrane consisting of polyvinyl alcohol-phenylsilanol-polypyrrole N2 - The synthesis of composite membranes based on PVA, PPy, and sulfonated–hydrolyzed TMPS was investigated for application in proton–exchange membrane fuel cells. FT–IR confirmed the hydrolysis of TMPS through the appearance of Si–OH vibrations, disappearance of Si–O–CH3 bands, reduced CH3 stretching intensity (2840 cm− 1), and successful sulfonation of the phenyl ring (1030 cm− 1). XPS verified the introduction of sulfonic acid groups by identifying S2p peaks between 166–170 eV. Scanning electron microscopy (SEM) showed an incorporation of PPy and that the membrane morphology altered by silanol leading to an increased surface roughness and inducing phase separation in comparison to pure PVA. The PVA–PPy–Si membrane which did not undergo phase separation demonstrated improved mechanical stability (maximum stress 5.91 MPa), reduced methanol uptake (22%, lower than Nafion’s 30%), and enhanced thermal resistance compared to PVA–PPy and PVA–Si. It also exhibited a high ion–exchange capacity (1.5mmol g− 1, exceeding Nafion® at 0.9mmol g− 1 ) and a proton conductivity of 0.036 S/cm, twice that of Nafion 117. These combined properties identify the PVA–PPy–Si composite as a promising high–performance polyelectrolyte membrane for fuel cell applications. KW - Polyelectrolyte membrane PY - 2026 DO - https://doi.org/10.1016/j.apsusc.2026.166495 SN - 1873-5584 VL - 731 SP - 1 EP - 11 PB - Elsevier B.V. AN - OPUS4-65627 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -