TY - JOUR A1 - Heyn, A. A1 - Kotula, Stefan A1 - Ebell, Gino A1 - Babutzka, M. T1 - Results of a Round Robin Test for the Determination of Polarization Resistances on Differently Weathered Zinc Samples Using Gel Electrolytes N2 - This article presents the results of a round robin test throughout Germany with 19 participating institutions. Corrosion productlayer resistances (RL ) were determined on two differently weathered pure zinc samples and a sample activated with NaOH bymeans of electrochemical measurement of the linear polarization resistance (LPR) using agar‐based gel electrolytes. The roundrobin test was organized by the Bundesanstalt für Materialforschung und ‐prüfung (BAM) in Berlin. The measurements werecarried out by the participants in the period from May to July 2021. The results are summarized in this article comprising anassessment of the reproducibility and repeatability of the measurements. The methodology is suitable for distinguishing zincsurfaces after exposure to different atmospheres based on the corrosion product layer resistances (RL). In addition, possibleproblems in the application of the method were identified, and solutions for improving reproducibility and repeatability arediscussed. The results and knowledge from the round robin test are incorporated into a new test standard (DIN 50023:2024‐07)for this measurement method KW - Corrosion PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630546 DO - https://doi.org/10.1002/maco.202414696 SN - 1521-4176 SP - 1 EP - 12 PB - Wiley AN - OPUS4-63054 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heyn, A. A1 - Meist, M. A1 - Michael, O. A1 - Babutzka, M. A1 - Valet, Svenja A1 - Ebell, Gino T1 - Electrochemical characterization of surfaces of galvanized steels under different exposure conditions using gel electrolytes N2 - The corrosion behavior of galvanized steels and zinc components under atmospheric exposure depends mostly on the corrosion product‐based cover layer formation under the prevailing conditions. The use of agar‐based gel electrolytes makes it possible to use electrochemical methods to obtain a characteristic value from these cover layers that describe their current and future protective capacity. It is shown here that different states of galvanized steel can be distinguished very well under laboratory conditions and that this method is also suitable for use under practical conditions. Based on the characteristic values and assuming future time of wetness, it is very easy to draw up a forecast for the future corrosion rate, which provides plausible values. KW - Materials Chemistry KW - Metals and Alloys KW - Surfaces, Coatings and Films KW - Mechanical Engineering KW - Mechanics of Materials KW - Environmental Chemistry KW - Corrosion KW - Znc PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599234 DO - https://doi.org/10.1002/maco.202414389 SP - 1 EP - 16 PB - Wiley VHC-Verlag AN - OPUS4-59923 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kauss, Norman A1 - Heyn, A. A1 - Michael, O. A1 - Schymura, M. A1 - Rosemann, P. T1 - Application limits and sensitisation behaviour of the manganese- and nitrogen-alloyed austenitic stainless steel P2000 (X13CrMnMoN18-14-3) N2 - Nickel‐free high‐nitrogen‐alloyed stainless steels like the P2000 (X13CrMnMoN18‐14‐3) were developed to enhance the strength and corrosion resistance of austenitic stainless steels like 304 and 316 while keeping the typical high ductility. The mechanical and corrosive properties of P2000 were investigated and compared with 304 and 316 to highlight the application opportunities of this new alloy. The microstructure of the solution‐annealed condition was characterised by electron backscatter diffraction and the mechanical properties were studied by uniaxial tensile tests, Charpy impact tests and hardness measurements. The passivation behaviour was analysed using the electrochemical potentiodynamic reactivation, whereas the pitting corrosion resistance was compared by pitting potentials and pitting temperatures. However, secondary thermal influences or suboptimal heat treatment can impair the corrosion resistance due to the precipitation of secondary phases and the resulting sensitisation. Thermodynamic calculations and artificial ageing treatment in the range of 500–900°C for up to 100 h were used to determine critical time–temperature parameters for sensitisation. The microstructure of the various aged states was evaluated by scanning electron microscopy and compared with the degrading corrosion resistance characterised by the KorroPad method. KW - Austenitic stainless steel KW - Electrochemical methods KW - High‐nitrogen steel KW - Mechanical properties KW - Corrosion resistance PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-527925 DO - https://doi.org/10.1002/maco.202112450 VL - 71 IS - 10 SP - 1656 EP - 1667 PB - Wiley-VCH GmbH AN - OPUS4-52792 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kauss, Norman A1 - Heyn, A. A1 - Halle, T. A1 - Rosemann, Paul T1 - Detection of sensitisation on aged lean duplex stainless steel with different electrochemical methods N2 - Ageing at 600 °C (from 0.1 h up to 20 h) leads to the formation of precipitations at the ferrite-ferrite (α/α) and ferrite-austenite (α/γ) grain boundaries of the lean duplex stainless steel (LDSS) X2CrNiN22-2. This leads to sensitisation due to chromium depletion and decreased pitting corrosion resistance proven by the results of various electrochemical methods (DL-EPR and determination of CPT, Epit). These results were compared with the KorroPad method, which uses an agar-based gel-electrolyte for the detection of stainless steel surfaces prone to pitting corrosion. However, the standard configuration of the KorroPad showed no differentiation for the various ageing conditions. Therefore, modified versions of the KorroPad with two, five and ten times higher NaCl and potassium ferrocyanide III (K3[Fe(CN)6]) concentrations were successfully used to visualise the behaviour detected by DL-EPR, Epit and CPT. Therefore, the KorroPad method can also detect a microstructure related reduction of pitting corrosion resistance, which can drastically reduce the experimental effort to generate sensitisation diagrams for stainless steels. KW - Lean duplex KW - Stainless steel KW - Sensitisation KW - Polarisation KW - Critical pitting temperature KW - Pitting corrosion KW - KorroPad KW - Ageing treatment PY - 2019 DO - https://doi.org/10.1016/j.electacta.2019.05.081 SN - 0013-4686 SN - 1873-3859 VL - 317 SP - 17 EP - 24 PB - Elsevier AN - OPUS4-48374 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin A1 - Burkert, Andreas A1 - Heise, Svenja A1 - Heyn, A. T1 - Korrosionsuntersuchungen mit gelartigen Elektrolyten an Zink - Eine innovative Prüfmethodik N2 - Ein neuer Ansatz bei elektrochemischen Korrosionsuntersuchungen kann durch den Einsatz von gelartigen Elektrolyten als Alternative zu wässrigen Prüfelektrolyten beschritten werden. Gelartige Elektrolyte ermöglichen minimalinvasive Untersuchungen an natürlich gebildeten Zinkdeckschichten. Dadurch können korrosionsrelevante Kennwerte ermittelt werden, die Aussagen zur Deckschichtbildung und zur Stabilität von atmosphärisch gebildeten Deckschichten erlauben. In diesem Beitrag wird anhand verschiedener Untersuchungen an Reinzink der Mehrwert von gelartigen Elektrolyten für die Korrosionsforschung und -prüfung verdeutlicht. Darüber hinaus werden neue Erkenntnisse zur Deckschichtbildung von Zink unter atmosphärischen Bedingungen vorgestellt. T2 - GfKORR-Jahrestagung 2019 CY - Frankfurt a. M. DA - 12.11.2019 KW - Zink KW - Gelartige Elektrolyte KW - Korrosionsuntersuchungen KW - Deckschichtbildung PY - 2019 SN - 978-3-935406-71-0 SP - 53 EP - 64 AN - OPUS4-49642 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Balzer, M. A1 - Fenker, M. A1 - Kappl, H. A1 - Müller, Thoralf A1 - Heyn, A. A1 - Heiss, A. A1 - Richter, A. T1 - Corrosion protection of steel substrates by magnetron sputtered TiMgN hard coatings: Structure, mechanical properties and growth defect related salt spray test results N2 - Hard and wear resistant coatings deposited by PVD techniques have been characterized for decades for their capabilities to protect steel substrates from corrosion. In the present work the effect of Mg incorporated into TiN coatings is described in terms of the corrosion behavior as well as the mechanical and structural properties. TiN and TiMgN films with Mg contents between 10 and 35 at.% were deposited onto mirror polished 100Cr6 (1.3505) steel samples with 2.5 and 5 μm thickness by using DC magnetron sputtering. The corrosion protection capabilities of the coatings were characterized by neutral salt spray (NSS) test, considering the amounts and sizes of growth defects inherent in each coated sample as determined by a recently developed optical scan method (Large Area High Resolution mapping). The defect data were statistically analyzed for improved interpretation of NSS test results. Chosen growth defects were additionally analyzed by focused ion beam technique. Furthermore the coating composition and morphology, the hardness and the tribological behavior were characterized. Polished steel samples coated with 2.5 μm TiMgN containing about 35 at.% Mg were in the plane free of corrosion after 24 h in a NSS test. TiMgN with 10 or 20 at.% Mg only provided a slightly improved corrosion protection in relation to pure TiN coatings, which was limited to certain types of growth defects. The highest Mg containing coatings exhibited a decreased hardness down to 1200 or 1800 HV depending on type of deposition (HV 1200: Ti- and Mg-target with rotating substrate holder, 1800: Mg-plugged Ti-target with static substrate holder), but also showed a strongly improved wear resistance against Al2O3 related to pure TiN. By analyzing the NSS test results it was found that the corrosion behavior of the coated samples did not only depend strongly on the Mg content, but also on the sample individual defect concentrations. Therefore this subject is extensively discussed. KW - Physical vapour deposition (PVD) KW - Corrosion KW - Growth defects KW - Pinholes KW - Magnesium KW - TiMgN PY - 2018 DO - https://doi.org/10.1016/j.surfcoat.2018.05.037 SN - 0257-8972 VL - 349 IS - 9 SP - 82 EP - 92 PB - Elsevier B.V. AN - OPUS4-45712 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kauss, N. A1 - Heyn, A. A1 - Rosemann, Paul T1 - How to Detect Sensitivity on Aged Lean-Duplex Stainless Steel With Electrochemical Methods N2 - The influence of isothermal ageing on microstructure, sensitisation and pitting corrosion resistance of the lean duplex stainless steel (LDSS) X2CrNiN23-4 was investigated with various electrochemical methods. The aging at 600 °C (from 0.1 h up to 20 h) lead to the formation of precipitations at the ferrite-ferrite (α/α) and ferrite-austenite (α/γ) grain boundaries, inducing sensitisation due to chromium depletion. The degree of sensitisation was evaluated with the double loop electrochemical potentiokinetic reactivation method (DL-EPR) according to ASTM G108 and correlated with critical pitting potentials (Epit) as well as critical pitting temperature (CPT) measured in an electrolyte according to ASTM G48 using electrochemical noise. Up to an ageing time of 1 h, the sensitisation did rise significantly, stabilising at a nearly constant level with a slight drop at 20 h. This behaviour correlated perfectly with the potentiodynamically determined pitting potentials Epit and sensitisation. The CPT showed a higher sensitivity at short ageing times compared to the DL-EPR and Epit. Finally, the KorroPad method was applied to visualise the sensitisation induced reduction of pitting corrosion resistance. The “KorroPad” is an agar-based gel-electrolyte containing 0.1 mol/l sodium chloride (NaCl) and 0.1 mol/l potassium ferricyanide III (K3[Fe(CN)6]), invented at the Federal Institute of Materials Research and Testing in Berlin (Germany) to detect surfaces of stainless steel prone to pitting corrosion. The standard configuration of the KorroPad showed no differentiation for the various aging conditions. Increasing the concentration of both NaCl and potassium ferrocyanide III to 0.5 M shifts the detection limit of the KorroPad method to stainless steels with higher corrosion resistance, producing the same trends detected by standard electrochemical pitting corrosion values (Epit, CPT) and sensitisation (DL-EPR). By that, the KorroPad method was successfully adjusted to the lean-duplex stainless steel X2CrNiN23-4, enabling short-time testing to detect sensitization. T2 - Electrochemical Methods in Corrosion Research 2018 CY - Cambridge, UK DA - 22.07.2018 KW - Corrosion testing KW - Duplex stainless steels KW - Corrosion KW - KorroPad KW - Pitting corrosion KW - EPR KW - Electrochemical noise KW - Stainless steel PY - 2018 AN - OPUS4-45615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin A1 - Burkert, Andreas A1 - Heyn, A. T1 - Corrosion investigations on zinc coatings by using gel-type electrolytes N2 - A new approach to the assessment of the corrosion behaviour of zinc coatings under atmospheric conditions can be achieved using gel-type electrolytes as an alternative to standard aqueous test electrolytes. Gel-type electrolytes allow minimally invasive corrosion investigations on zinc coatings. They also provide the possibility to carry out corrosion investigations onsite. By using gel-type electrolytes corrosion-relevant characteristic values such as corrosion currents and polarization resistances can be determined. These allow to describe the formation and the stability of the formed corrosion product layers under various climatic conditions. With this knowledge, a prediction of the zinc coating life cycle is possible. In this contribution, the value of gel-type electrolytes for corrosion research on zinc coatings is presented. T2 - Intergalva 2018 CY - Berlin, Germany DA - 17.06.2018 KW - Deckschichtbildung KW - Layer formation KW - Gelartige Elektrolyte KW - Gel-type electrolytes KW - Korrosionsprüfung KW - Corrosion testing KW - Zinkdeckschichten KW - Zinc coatings PY - 2018 SP - 385 EP - 392 AN - OPUS4-45245 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Babutzka, Martin A1 - Heyn, A. A1 - Rosemann, Paul T1 - Influence of austenitizing and tempering on the corrosion behavior and sensitization of martensitic stainless steel X50CrMoV15 N2 - Electrochemical tests, hardness measurements, and microstructure analysis are performed to study the influence of austenitizing, quenching, and tempering parameters on the corrosion resistance of the martensitic stainless steel grade X50CrMoV15 (1.4116). Different heat treatment states were studied using an adapted EPR-Test to evaluate the chromium distribution and depletion caused by the formation and dissolution of chromium rich carbides. The EPR results were correlated with pitting corrosion behavior, demonstrating the strong effect of heat treatment parameters on the susceptibility of martensitic stainless steels to corrosion phenomena. KW - Martensitic stainless steel KW - Electrochemical potentiokinetic reactivation KW - Heat treatment KW - Pitting corrosion PY - 2018 DO - https://doi.org/10.1002/maco.201810170 SN - 0947-5117 SN - 1521-4176 VL - 69 IS - 10 SP - 1338 EP - 1349 PB - Wiley-VCH Verlag CY - Weinheim AN - OPUS4-46138 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heyn, A. T1 - Korrosionsschutzmechanismen bei TiMgN-Hartstoffschichten auf Stahl N2 - Die Präsentation behandelt ein abgeschlossenes DFG Projekt welches die Fragestellung um das Korrosionsverhalten von TiMgN-Hartstoffschichten beleuchtet. Am Beginn des Vorhabens und in dessen weiterem Verlauf standen zahlreiche Ergebnisse die belegen, dass durch den Einbau von Mg in TiN-Hartstoffschichten das Korrosionsverhalten der beschichteten Stahlproben verbessert wird. Es gilt vorab festzuhalten, dass durch die TiMgN-Schicht eine großflächige Abschirmung des Stahls vor dem umgebenden Medium gegeben ist. Jedoch liegt bei nicht auszuschließenden Defekten bis zum Stahl, bedingt durch die Herstellung und/oder dem späteren Gebrauch, eine Gefährdung durch lokale Korrosion vor. Bei Kontakt mit wässriger, chloridhaltiger Lösung benetzt die Oberfläche und verbindet die TiMgN-Schicht über die Defekte mit dem dort freiliegenden Stahlsubstrat über den Elektrolyten. Zur Wirkungsweise des Korrosionsschutzes durch Mg in TiMgN konnten zum Ende des Vorhabens drei grundsätzliche Mechanismen identifiziert werden. T2 - 20. Werkstofftechnisches Kolloquium CY - Chemnitz, Germany DA - 14.03.2018 KW - Korrosion KW - Hartstoffschichten KW - PVD KW - Magnesium KW - TiN PY - 2018 AN - OPUS4-44538 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -