TY - JOUR A1 - El-Batahgy, A. A1 - Saiyah, A. A1 - Khafagi, S. A1 - Gumenyuk, Andrey A1 - Gook, S. A1 - Rethmeier, Michael T1 - Shielded metal arc welding of 9%Ni steel using matching ferritic filler metal N2 - Motivated by the tensile strength loss of 9%Ni steel arc welded joints made using Ni-based austenitic filler metals, the feasibility of maintaining the tensile strength using matching ferritic filler metal has been demonstrated. In comparison with shielded metal arc welded joint made using Ni-based austenitic electrode ENiCrMo-6, higher tensile strength comparable to that of the base metal was obtained using matching ferritic electrode. Besides, sufficient impact toughness energies with much lower mismatch were obtained for weld metal and heat-affected zone. Welded joint with a lower mechanical mismatching is of considerable importance for achieving acceptable combination of tensile strength and impact toughness.Abetter combination of These mechanical properties is ensured by applying a post weld heat treatment. KW - Mechanical mismatching KW - Mechanical properties KW - Microstructure KW - Austenitic welding electrode KW - Matching ferritic welding electrode PY - 2020 DO - https://doi.org/10.1080/13621718.2020.1846936 SN - 1362-1718 SP - 1 EP - 7 PB - Taylor & Francis AN - OPUS4-51835 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - El-Batahgy, A. A1 - Elkousy, M. A1 - Al-Rahman, A. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Gook, S. T1 - Retaining Mechanical Properties of GMA-Welded Joints of 9%Ni Steel Using Experimentally Produced Matching Ferritic Filler Metal N2 - Motivated by the loss of tensile strength in 9%Ni steel arc-welded joints performed using commercially available Ni-based austenitic filler metals, the viability of retaining tensile strength using an experimentally produced matching ferritic filler metal was confirmed. Compared to the austenitic Ni-based filler metal (685 MPa), higher tensile strength in gas metal arc (GMA) welded joints was achieved using a ferritic filler metal (749 MPa) due to its microstructure being similar to the base metal (645 MPa). The microstructure of hard martensite resulted in an impact energy of 71 J (-196 °C), which was two times higher than the specified minimum value of _>34 J. The tensile and impact strength of the welded joint is affected not only by its microstructure, but also by the degree of its mechanical mismatch depending on the type of filler metal. Welds with a harder microstructure and less mechanical mismatch are important for achieving an adequate combination of tensile strength and notched impact strength. This is achievable with the cost-effective ferritic filler metal. A more desirable combination of mechanical properties is guaranteed by applying low preheating temperature (200 °C), which is a more practicable and economical solution compared to the high post-weld heat treatment (PWHT) temperature (580 °C) suggested by other research. KW - 9%Ni steel KW - Ni-based austenitic filler metal KW - Mechanical mismatching KW - Microstructure KW - Post-weld heat treatment KW - Preheating KW - Matching ferritic filler metal PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-564610 DO - https://doi.org/10.3390/ma15238538 SN - 1996-1944 VL - 15 IS - 23 SP - 1 EP - 14 PB - MDPI AN - OPUS4-56461 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Siayah, A. A1 - El-Batahgy, A. A1 - Khafagi, S. A1 - Gumenyuk, Andrey A1 - Gook, S. A1 - Rethmeier, Michael T1 - A study on shielded metal arc welding of 9%Ni steel using non-conventional ferritic welding electrode for LNG facilities N2 - The present research work aims at clarification of the effect of the welding electrode type on the mechanical properties of SMA welded joints of 9%Ni steel plates. Properties of produced SMA welded joints were evaluated using different non-destructive and destructive investigation methods. In comparison with the conventionally used Ni-based welding electrode ENiCrMo-3 (AWS A5.11), an experimentally produced non-conventional ferritic welding electrode with 11%Ni (ENi11-Company specification) has resulted in a better combination of the mechanical properties of SMA welded joints of this steel type for critical cryogenic applications. Besides, a positive economic impact for the experimentally produced non-conventional ferritic welding electrode, due to its lower cost, could be another attractive aspect. T2 - 4th International Conference on Welding and Failure Analysis of Engineering Materials CY - Aswan, Egypt DA - 19.11.2018 KW - 9%Ni steel, KW - SMAW KW - Conventional Ni-based austenitic welding electrode KW - Mechanical properties KW - Ferritic welding electrode PY - 2018 SP - W-21, 1 EP - 3 AN - OPUS4-46736 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - El-Batahgy, A. A1 - Saiyah, A. A1 - Khafagi, S. A1 - Gumenyuk, Andrey A1 - Gook, Sergej A1 - Rethmeier, Michael T1 - Shielded metal arc welding of 9%Ni steel using matching ferritic filler metal N2 - Motivated by the tensile strength loss of 9%Ni steel arc welded joints made using Ni-based austenitic filler metals, the feasibility of maintaining the tensile strength using matching ferritic filler metal has been demonstrated. In comparison with shielded metal arc welded joint made using Ni-based austenitic electrode ENiCrMo-6, higher tensile strength comparable to that of the base metal was obtained using matching ferritic electrode. Besides, sufficient impact toughness energies with much lower mismatch were obtained for weld metal and heat-affected zone. Welded joint with a lower mechanical mismatching is of considerable importance for achieving acceptable combination of tensile strength and impact toughness. A better combination of These mechanical properties is ensured by applying a post weld heat treatment. KW - 9%Ni steel KW - Ni-based austenitic welding electrode KW - Matching ferritic welding electrode KW - Mechanical properties KW - Mechanical mismatching KW - Microstructure KW - SMAW PY - 2020 DO - https://doi.org/10.1080/13621718.2020.1846936 VL - 26 IS - 2 SP - 116 EP - 122 PB - Taylor & Francis AN - OPUS4-52025 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jokisch, T. A1 - Gook, S. A1 - Marko, A. A1 - Üstündag, Ömer A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser beam welding of additive manufactured components: Applicability of existing valuation regulations N2 - With additive manufacturing in the powder bed, the component size is limited by the installation space. Joint welding of additively manufactured parts offers a possibility to remove this size limitation. However, due to the specific stress and microstructure state in the additively built material, it is unclear to what extent existing evaluation rules of joint welding are also suitable for welds on additive components. This is investigated using laser beam welding of additively manufactured pipe joints. The welds are evaluated by means of visual inspection, metallographic examinations as well as computed tomography. The types of defects found are comparable to conventional components. This is an indicator that existing evaluation regulations also map the possible defects occurring for weld seams on additive components. KW - Weld imperfections KW - Additive manufacturing KW - Weldability KW - Laser welding PY - 2022 VL - 2 SP - 109 EP - 113 PB - DVS Media GmbH AN - OPUS4-56374 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrat, T. A1 - Marko, A. A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael ED - Mayr, P. ED - Berger, M. T1 - Baustrategien zur Beeinflussung von Materialauftrag und Temperaturentwicklung bei der additiven Fertigung mittels Laser-Pulver-Auftragschweißen N2 - Die Weiterentwicklung des Laser-Pulver-Auftragschweißens im Bereich der additiven Fertigung stellt dieses Verfahren vor neue Herausforderungen. Bauteile können schnell und endformnah hergestellt werden, was diese Technik für den Prototypenbau sowie Kleinserienfertigung interessant macht. Die Vielzahl an Varianten, um ein Volumen aus einzelnen Schichten aufzubauen, erhöhen die Möglichkeiten die Eigenschaften des entstehenden Bauteils zu beeinflussen. Hierfür müssen Strategien entwickelt werden, welche einen gleiclunäßigen Materialauftrag bei gleichzeitig optimalen Materialeigenschaften gewährleisten. Die durchgeführten Untersuchungen behandeln den Einfluss von Pendelstrategien sowie Spiralstrategien auf die Temperaturentwicklung und stellen diese vergleichend gegenüber. Um den unterschiedlichen Bedingungen bei der Bauteilfertigung Rechnung zu tragen, wurden Versuche in Randbereichen sowie im zentralen Bereich des Testobjekts untersucht. Die Ergebnisse verdeutlichen die Notwendigkeit angepasste Baustrategien zu entwickeln, um durch einen stabilen Fertigungsprozess Qualität und Eigenschaften eines Bauteils gewährleisten zu können. T2 - FüMoTec 2017 CY - Chemnitz, Germany DA - 14.11.2017 KW - Laser-Pulver-Auftragschweißen KW - Additiv KW - Pendelstrategie KW - Spiralstrategie KW - Temperaturentwicklung PY - 2017 SN - 978-3-96100-034-0 SN - 2365-8096 SN - 2365-810X VL - 2017/2 SP - 27 EP - 36 PB - readbox unipress CY - Münster AN - OPUS4-43104 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - El-Batahgy, A. A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Effect of laser-beam and hybrid-laser-arc welding parameters and filler metal on microstructure and mechanical properties of thick heat-treated steel X8ni9+Qt640 for cryogenic service N2 - The present research work encloses results of experimental investigations of the interaction between welding process parameters for laser-beam and hybrid-laser-arc as well as type of the filler metal and the achievable mechanical properties of the weld joints on steel grade X8Ni9+QT640 for cryogenic service containing 9% nickel. The results obtained contribute to the development and conversion in the industrial practice a new laser beam-based welding technology for the automated manufacturing of facilities for the liquefaction, storage and the transport of natural gases (LNG facilities). The results show, that the martensitic microstructure of the laser weld metal including low amount of retained austenite not exceeding 3.5% leads to the relatively low V-notch impact energy. The remarkable heterogeneity in the chemical composition of the weld metal through the weld thickness could be recognized in the case of hybrid-laser-arc welding with ERNiCrMo-3 austenitic filler metal, what also led to insufficient impact toughness of the weld metall. The most promising results could be achieved by using 11%Ni filler wire, which is similar to the base metal and provides a homogeneous microstructure with uniform distribution of Ni through the weld seam. It is remarkable, that a correlation between Charpy impact toughness and wire feeding speed and respectively process heat input exists. The highest toughness values were 134±58 J at -196C. The both laser as well as laser-hybrid welds passed the tensile test. The failure stress of 720±3 MPa with a fracture location in the base material was achieved for all samples tested. T2 - 4th International Conference on Welding and Failure Analysis of Engineering Materials CY - Aswan, Egypt DA - 19.11.2018 KW - Hybrid-laser-arc welding KW - Laser-beam welding, KW - Cryogenic steel KW - Microstructure KW - Tensile strength PY - 2018 SP - W-29, 1 EP - 10 AN - OPUS4-46738 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Graf, B. A1 - Marko, A. A1 - Petrat, T. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - 3D laser metal deposition: process steps for additive manufacturing N2 - Laser metal deposition (LMD) is an established technology for two-dimensional surface coatings. It offers high deposition rates, high material flexibility, and the possibility to deposit material on existing components. Due to these features, LMD has been increasingly applied for additive manufacturing of 3D structures in recent years. Compared to previous coating applications, additive manufacturing of 3D structures leads to new challenges regarding LMD process knowledge. In this paper, the process steps for LMD as additive manufacturing technology are described. The experiments are conducted using titanium alloy Ti-6Al-4Vand Inconel 718. Only the LMD nozzle is used to create a shielding gas atmosphere. This ensures the high geometric flexibility needed for additive manufacturing, although issues with the restricted size and quality of the shielding gas atmosphere arise. In the first step, the influence of process parameters on the geometric dimensions of single weld beads is analyzed based on design of experiments. In the second step, a 3D build-up strategy for cylindrical specimen with high dimensional accuracy is described. Process parameters, travel paths, and cooling periods between layers are adjusted. Tensile tests show that mechanical properties in the as-deposited condition are close to wrought material. As practical example, the fir-tree root profile of a turbine blade is manufactured. The feasibility of LMD as additive technology is evaluated based on this component. KW - Laser metal deposition KW - Build-up strategy KW - Deposition rate KW - Additive manufacturing PY - 2018 DO - https://doi.org/10.1007/s40194-018-0590-x SN - 0043-2288 SN - 1878-6669 VL - 62 IS - 4 SP - 877 EP - 883 PB - Springer Berlin Heidelberg CY - Heidelberg AN - OPUS4-44868 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gook, S. A1 - Midik, A. A1 - Biegler, M. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Joining 30 mm Thick Shipbuilding Steel Plates EH36 Using a Process Combination of Hybrid Laser Arc Welding and Submerged Arc Welding N2 - This article presents a cost-effective and reliable method for welding 30 mm thick sheets of shipbuilding steel EH36. The method proposes to perform butt welding in a two-run technique using hybrid laser arc welding (HLAW) and submerged arc welding (SAW). The HLAW is performed as a partial penetration weld with a penetration depth of approximately 25 mm. The SAWis carried out as a second run on the opposite side. With a SAWpenetration depth of 8 mm, the weld cross-section is closed with the reliable intersection of both passes. The advantages of the proposed welding method are: no need for forming of the HLAW root; the SAW pass can effectively eliminate pores in the HLAWroot; the high stability of the welding process regarding the preparation quality of the weld edges. Plasma cut edges can be welded without lack of fusion defects. The weld quality achieved is confirmed by destructive tests. KW - Shipbuilding steel KW - Hybrid laser arc welding KW - Submerged arc welding KW - Hardness KW - Bending test KW - Two-run welding technique KW - Microstructure PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-556090 DO - https://doi.org/10.3390/jmmp6040084 SN - 2504-4494 VL - 6 IS - 4 SP - 1 EP - 11 PB - MDPI CY - Basel AN - OPUS4-55609 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gook, S. A1 - Krieger, S. A1 - Gumenyuk, Andrey A1 - El-Batahgy, A. M. A1 - Rethmeier, Michael T1 - Notch impact toughness of laser beam welded thick sheets of cryogenic nickel alloyed steel X8Ni9 N2 - The paper deals with the investigations of the impact toughness of laser beam welded 14.5 mm thick sheets made of cryogenic steel X8Ni9 as a function of preheating. This 9% nickel alloyed steel is widely used in the liquefied natural gas (LNG) industry. An application of highly efficient welding processes such as high-power laser beam welding (LBW) in LNG sector requires an understanding of the interactions between the LBW process parameters and weld properties, in particular the impact toughness. The results show that the original fine-grained martensitic microstructure of the base metal (BM) is significantly changed by melting and crystallization during the LBW, what can lead to a decrease in the impact toughness of the weld metal (WM) below the required level. An optimal preheating temperature range leads to the favorable thermal welding cycle and is of remarkable importance for maintaining the notch impact toughness of laser beam welded joints of these thick steel sheets. A parameter window was identified in which V-notch impact toughness comparable to that of the BM at -196 °C was achieved. KW - Cryogenic steel KW - Laser beam welding KW - Preheating KW - Welding thermal cycle KW - Microstructure KW - Hardness KW - V-notch impact toughness PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-513250 DO - https://doi.org/10.1016/j.procir.2020.09.095 VL - 94 SP - 627 EP - 631 PB - Elsevier B.V. AN - OPUS4-51325 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tölle, Florian A1 - Gumenyuk, Andrey A1 - Backhaus, A. A1 - Olschok, S. A1 - Rethmeier, Michael A1 - Reisgen, U. T1 - Welding residual stress reduction by scanning of a defocused beam N2 - The residual stresses in narrow electron or laser beam welds with high stress gradients are decreased without any contact surfaces or additional equipment by applying the welding beam after welding in a defocused mode for heating the material regions in a certain distance from the weld on both sides. In case of electron beam application, the beam is positioned and focused by the electromagnetic coil with high frequency. In case of laser beam application a laser scanner optics enables fast positioning by an optomechanic beam deflection, while defocusing of the laser beam is obtained by increasing the distance between scanner optics and workpiece. Dependent on the component geometry and on the beam power different process parameters are used. The adjustable process parameters are the radius and the power of the defocused beam and the transversal and longitudinal distances between the welding and the defocused beam. The mechanism and the influence of the process parameters are investigated by FEM-simulation and a number of experiments on a ferritic steel S355J2+N with 5 mm thickness. FEM-simulation is used to reduce the matrix of process parameters for the experiments. The best experimental result shows a stress reduction of about 70%. KW - Residual stresses KW - Stress reduction KW - High energy beam welding KW - Post-weld heat treatment KW - Laser scanner optics PY - 2012 DO - https://doi.org/10.1016/j.jmatprotec.2011.07.019 SN - 0924-0136 SN - 1873-4774 VL - 212 IS - 1 SP - 19 EP - 26 PB - Elsevier CY - Amsterdam AN - OPUS4-24787 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Tölle, Florian A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Backhaus, A. A1 - Olschok, S. A1 - Reisgen, U. T1 - Eigenspannungsreduzierung in Elektronen- und Laserstrahlschweißnähten mittels nachlaufender Wärmefelder durch schnelle Strahldefokussierung und -ablenkung N2 - Schweißeigenspannungen - im Besonderen infolge von Strahlschweißprozessen - annähernd der werkstoffspezifischen Streckgrenze können durch eine mögliche Spannungsrelaxation oder verstärkte Spannungsrisskorrosion lebensdauerreduzierende Konsequenzen mit sich ziehen. Aus diesem Grund wurden viele Verfahren entwickelt, welche diese Eigenspannungen reduzieren können. Jedoch sind diese Verfahren kostenintensiv oder nur für breite Schweißnähte und einfache Bauteilgeometrien anwendbar. Die in dieser Arbeit dargestellte Methode nutzt den Schweißstrahl für den Schweißprozess sowie in defokussierter Form für eine thermische Nachbehandlung des Bauteils. Hierfür läuft der defokussierte Strahl durch hochfrequente Strahlablenkung beidseitig der Schweißnaht mit einer bestimmten zeitlichen Distanz dem Schmelzbad nach und wird zum Aufheizen dieser Materialbereiche genutzt. Mit dieser Prozedur ist es möglich die Spannungen in schmalen Schweißnähten mit großen Spannungsgradienten im Vergleich zu anderen spannungsreduzierenden Verfahren ohne Kontaktflächen oder zusätzlichem Equipment effizient zu reduzieren. Abhängig von der Bauteilgeometrie und der Strahlleistung können unterschiedliche Prozessparameter für dieses Verfahren angewandt werden. Es werden die Mechanismen der Eigenspannungsreduzierung in diesem Prozess und deren Abhängigkeit von den Prozessparametern anhand von Ergebnissen aus FEM-Simulationen diskutiert. Zudem wird in einer Reihe von experimentellen Ergebnissen die Anwendbarkeit von bereits für lineare Schweißnähte ermittelte Verfahrensparameter auf axiale und radiale Rundnähte nachgewiesen. Hierbei zeigen die besten experimentellen Ergebnisse für Elektronenstrahl- sowie für Laserstrahlschweißnähte Spannungsreduktionen größer als 90 %. T2 - DVS Congress 2011 - Große Schweißtechnische Tagung CY - Hamburg, Deutschland DA - 27.09.2011 PY - 2011 SN - 978-3-87155-267-0 VL - 275 SP - 465 EP - 471 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-24545 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tölle, Florian A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Backhaus, A. A1 - Olschok, S. A1 - Reisgen, U. T1 - Mechanische Entlastung zur Eigenspannungsreduzierung in Strahlschweißnähten durch Anwendung eines defokussierten Strahls - Teil 2: Qualifizierung für komplexe Nahtgeometrien N2 - Schweißzugeigenspannungen in Strahlschweißnähten auf Höhe der lokalen Werkstoffstreckgrenze können die Bauteileigenschaften sowie deren Lebensdauer negativ beeinflussen. Die Nutzung der Schweißquelle für eine nachträgliche Behandlung der geschweißten Bauteile bietet eine kostengünstige und flexible Methode zur Reduzierung dieser Spannungen. Dabei wird durch einen oszillierenden defokussierten Elektronen- bzw. Laserstrahl, der Werkstoff beidseitig der Schweißnaht auf mehrere hundert Grad Celsius erwärmt, um dort zusätzliche Zugspannungsbereiche hervorzurufen. Die so erzeugten Längszugspannungszonen führen zu einer mechanischen Entlastung der Schweißnaht. Experimentelle Messungen der Längseigenspannungen an linearen Elektronen- und Laserstrahlschweißnähten im ersten Teil des Beitrags zeigten, dass die Spannungen mit diesem Verfahren um bis zu 70% reduziert werden können. In weiteren experimentellen Untersuchungen wird dieses Verfahren für kompliziertere Schweißnahtgeometrien getestet. An axialen sowie radialen Rundnähten an ferritischen Werkstoffen konnten ebenfalls hohe Spannungsreduktionen von über 50% erzielt werden. Zudem wurde dieses Verfahren mit einer für das Schweißen üblichen Laserstrahlschweißoptik ohne Scan-Funktion geprüft. Hierbei zeigte das Wärmebehandeln in zwei Arbeitsschritten noch größere Spannungsreduktionen im Vergleich zur Anwendung einer Laserstrahlscanneroptik zur quasisimultanen Wärmebehandlung auf beiden Seiten der Schweißnaht. ------------------------------------------------------------------------------------------------------------------------------------------- Residual tensile welding stresses in beam welds at the level of the local yield strength of the material may influence the properties of components as well as their service lives. The utilisation of the welding source for the subsequent treatment of the welded components offers a cost-favourable and flexible method of reducing these stresses. In this respect, an oscillating defocused electron or laser beam serves to heat the material on both sides of the weld up to several hundred degrees Celsius in order to induce additional tensile stress regions there. The longitudinal tensile stress zones produced in this way lead to the mechanical relief of the weld. Experimental measurements of the longitudinal residual stresses on linear electron and laser beam welds in the first part of the article showed that the stresses can be reduced by up to 70% with this process. In further experimental investigations, this process is tested for more complicated weld geometries. It was also possible to achieve great reductions in the stresses (over 50%) on both axial and radial circular welds on ferritic materials. Moreover, this process was tested with laser beam welding optics which are customary for welding and do not perform a scanning function. In this respect, the heat treatment in two work steps showed even greater reductions in the stresses in comparison with the application of laser beam scanner optics for quasi-simultaneous heat treatment on both sides of the weld. KW - Elektronenstrahlschweißen KW - Laserstrahlschweißen KW - Simulation und Berechnung KW - Spannungen KW - Wärmebehandlung KW - Electron beam welding KW - Laser welding KW - Simulation and calculation KW - Stresses KW - Heat treatment PY - 2012 SN - 0036-7184 VL - 64 IS - 7 SP - 406 EP - 411 PB - Verl. für Schweißen u. Verwandte Verfahren, DVS-Verl. CY - Düsseldorf AN - OPUS4-26339 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schneider, André A1 - Gumenyuk, Andrey A1 - Lammers, Marco A1 - Malletschek, A. A1 - Rethmeier, Michael T1 - Laser beam welding of thick titanium sheets in the field of marine technology N2 - The ever larger requirements of the material selection in the range of maritime industry necessitate the application of high-tech materials. Titanium because of its excellent mechanical properties at low weight is an attractive alternative for the construction of ships. The goal of this investigation was to design a welding method for joining samples of 16 mm thick Ti3Al2.5 V. The welding experiments with a 20 kW Yb-fiber laser source and varying combinations of parameters were intended to qualify the laser beam welding process. The welding results were analyzed by non-destructive and destructive testing. In addition, the welding tests were recorded with two high-speed cameras to observe the weld pool and the vapor plume. The evaluation of the high-speed images in correlation with the results of non-destructive testing shows, that a significant improvement of process stability and weld quality can be achieved by the suppression of the vapor plume. KW - Titanium alloy KW - Maritime industry KW - Vapor plume KW - Laser beam welding KW - Ti3Al2.5V PY - 2014 DO - https://doi.org/10.1016/j.phpro.2014.08.046 SN - 1875-3892 VL - 56 SP - 582 EP - 590 PB - Elsevier CY - Amsterdam [u.a.] AN - OPUS4-31439 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Uhlmann, E. A1 - Stark, R. A1 - Rethmeier, Michael A1 - Baumgarten, J. A1 - Bilz, M. A1 - Geisert, C. A1 - Graf, B. A1 - Grosser, H. A1 - Heitmüller, F. A1 - Manthei, M. A1 - Reinkober, S. A1 - Gumenyuk, A. ED - Redding, L. ED - Roy, R. T1 - Maintenance, repair and overhaul in through-life engineering services N2 - Maintenance, Repair and Overhaul (MRO) is acquiring increasing commercial and socio-economic significance. For products and goods with high investment costs and a long lifespan, especially in the sectors of energy and transportation, a considerable portion of commercial profits are generated by after-sales services. In the field of research and development, not enough attention has been paid so far to tasks and approaches involving MRO. The field thus has a limited scientific background, despite a high potential in the business sector for technological and scientific optimization. The challenges and chances of MRO for sustainable enterprises will be explained with reference to the Fraunhofer Innovation Cluster Maintenance, Repair and Overhaul in Energy and Transport. The developments and project results of the four fields of innovation »Cleaning«, »Repair and Overhaul«, »Condition Monitoring and Diagnosis«, as well as »MRO Planning and Digital Assistance« will be explained. PY - 2015 SN - 978-3-319-12111-6 DO - https://doi.org/10.1007/978-3-319-12111-6_9 N1 - Serientitel: Decision Engineering – Series title: Decision Engineering SP - Part III, Chapter 9, 129 EP - 156 PB - Springer AN - OPUS4-32553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tölle, Florian A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Backhaus, A. A1 - Olschok, S. A1 - Reisgen, U. T1 - Mechanische Entlastung zur Eigenspannungsreduzierung in Strahlschweißnähten durch Anwendung eines defokussierten Strahls - Teil 1: Spannungsabbaumechanismus an linearen Strahlschweißnähten N2 - Schweißzugeigenspannungen in Strahlschweißnähten auf Höhe der lokalen Werkstoffstreckgrenze können die Bauteileigenschaften sowie deren Lebensdauer beeinflussen. Die Nutzung der Schweißquelle für eine nachträgliche Behandlung der geschweißten Bauteile bietet eine kostengünstige und flexible Methode zur Reduzierung dieser Spannungen. Dabei wird durch einen oszillierenden defokussierten Elektronen- bzw. Laserstrahl der Werkstoff beidseitig der Schweißnaht auf mehrere hundert Grad Celsius erwärmt, um dort zusätzliche Zugspannungsbereiche hervorzurufen. Die so erzeugten Längszugspannungszonen führen zu einer mechanischen Entlastung der Schweißnaht. Experimentelle Messungen zeigen, dass die Längseigenspannungen in der Schweißnaht mit diesem Verfahren um bis zu 70% reduziert werden können. Hierbei wurde neben der experimentellen Untersuchung dieses Verfahrens an Linearnähten an 5 mm dicken Blechen des Werkstoffs S355J2+N auch eine umfassende Analyse der Einflüsse der Verfahrensparameter auf die Spannungsreduktion mittels FEMSimulation durchgeführt. Anhand der Ergebnisse wird der Entlastungsmechanismus diskutiert. ------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------ Residual tensile welding stresses in beam welds at the level of the local yield strength of the material may influence the properties of components as well as their service lives. The utilisation of the welding source for the subsequent treatment of the welded components offers a cost-favourable and flexible method of reducing these stresses. In this respect, an oscillating defocused electron or laser beam serves to heat the material on both sides of the weld up to several hundred degrees Celsius in order to induce additional tensile stress regions there. The longitudinal tensile stress zones produced in this way lead to the mechanical relief of the weld. Experimental measurements show that the longitudinal residual stresses in the weld can be reduced by up to 70% with this process. In this case, not only was the experimental investigation into this process conducted on linear welds on 5 mm thick sheets made of the S355J2+N material but a comprehensive analysis of the influences of the process parameters on the stress reduction was also made by means of FEM simulation. The relief mechanism is discussed on the basis of the results. KW - Elektronenstrahlschweißen KW - Laserstrahlschweißen KW - Simulation und Berechnung KW - Spannungen KW - Wärmebehandlung KW - Electron beam welding KW - Laser welding KW - Simulation and calculation KW - Stresses KW - Heat treatment PY - 2012 SN - 0036-7184 VL - 64 IS - 6 SP - 332 EP - 340 PB - Verl. für Schweißen u. Verwandte Verfahren, DVS-Verl. CY - Düsseldorf AN - OPUS4-26340 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jokisch, T. A1 - Gook, S. A1 - Marko, A. A1 - Üstündag, Ömer A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laserstrahlschweißen additiv gefertigter Bauteile: Einsetzbarkeit bestehender Bewertungsvorschriften N2 - Bei der additiven Fertigung im Pulverbett ist die Bauteilgröße durch den Bauraum begrenzt. Das Verbindungsschweißen additiv gefertigter Teile bietet eine Möglichkeit diese Größenbegrenzung aufzuheben. Aufgrund des spezifischen Spannungs- und Gefügezustands im additiv aufgebauten Teil ist jedoch unklar, inwiefern bestehende Bewertungsvorschriften des Verbindungsschweißens auch für Schweißnähte an additiv gefertigten Bauteilen geeignet sind. Dies wird anhand des Laserstrahlschweißens additiv gefertigter Rohrverbindungen untersucht. Die Schweißnähte werden mittels visueller Prüfung, metallografischer Untersuchungen sowie Computertomografie ausgewertet. Die festgestellten Fehlerarten sind vergleichbar zu konventionellen Bauteilen. Dies ist ein Indikator dafür, dass bestehende Bewertungsvorschriften die möglichen auftretenden Defekte auch für Schweißnähte an additiven Bauteilen abbilden. KW - Schweißunregelmäßigkeiten KW - Additive Fertigung KW - Laserstrahlschweißen KW - Schweißeignung PY - 2021 VL - 73 IS - 3 SP - 132 EP - 137 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-53575 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reisgen, U. A1 - Olschok, S. A1 - Backhaus, A. A1 - Rethmeier, Michael A1 - Gumenyuk, Andrey A1 - Tölle, Florian T1 - Reduction of weld residual stresses with the electron beam N2 - High weiding residual stresses can cause Service life reducing consequences. Even though many processes have been developed to reduce these stresses, they are only applicable for wider welds and simple component geometries or are cost-intensive, respectively. This work introduces a possibility to reduce the weid residual stresses by means of the electron beam. The same tool is used for the production of the welded seam and the weid residual stresses are reduced touchless, in a multiple-process technique or in a second working step. Other process steps, spanning orshifting of the component or even additional machines are no longer required when this rnethod is used. Via beam oscillation and multiple-process technique, the defocused electron beam produces thermal fields in transversal and lateral distance to the welded seam which impose compressive stress on the ambient material. With the help of adjusted heating fields in defined distance from the weid seam, the residual stresses in the weld seam are, e.g. in the case of ferritic Steel, reduced by up to 73%. In this work, the basic mechanism for stress relief is introduced and also the influence of different process Parameters, e.g. beam power, deflection parameters, diameter of the defocused electron beam and work distances between thermal fields and welded seams exert on the reduction of residual stresses. Moreover, different results made with ferritic and austenitic Steel are presented in the form of linear and circumferential welds. T2 - 2nd International electron beam welding conference (IEBW) CY - Aachen, Germany DA - 26.03.2012 PY - 2012 SN - 978-3-87155-299-1 N1 - Serientitel: DVS-Berichte – Series title: DVS-Berichte VL - 285 SP - 128 EP - 132 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-26110 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jokisch, T. A1 - Marko, A. A1 - Gook, S. A1 - Üstündag, Ö. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser Welding of SLM-Manufactured Tubes Made of IN625 and IN718 N2 - The advantage of selective laser melting (SLM) is its high accuracy and geometrical flexibility. Because the maximum size of the components is limited by the process chamber, possibilities must be found to combine several parts manufactured by SLM. An application where this is necessary, is, for example, the components of gas turbines, such as burners or oil return pipes, and inserts, which can be joined by circumferential welds. However, only a few investigations to date have been carried out for the welding of components produced by SLM. The object of this paper is, therefore, to investigate the feasibility of laser beam welding for joining SLM tube connections made of nickel-based alloys. For this purpose, SLM-manufactured Inconel 625 and Inconel 718 tubes were welded with a Yb:YAG disk laser and subsequently examined for residual stresses and defects. The results showed that the welds had no significant influence on the residual stresses. A good weld quality could be achieved in the seam circumference. However, pores and pore nests were found in the final overlap area, which meant that no continuous good welding quality could be accomplished. Pore formation was presumably caused by capillary instabilities when the laser power was ramped out. KW - Inconel 718 KW - Laser welding KW - Selective Laser Melting KW - Laser Powder Bed Fusion PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-489679 DO - https://doi.org/10.3390/ma12182967 SN - 1996-1944 VL - 12 IS - 18 SP - 2967, 1 EP - 15 PB - Multidisciplinary Digital Publishing Institute CY - Basel AN - OPUS4-48967 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gook, S. A1 - El-Batahgy, A. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Hybrid laser arc welding of thick plates X8Ni9 for LNG tank construction N2 - Results of experimental investigations of the relationship between laser-hybrid welding process parameters, type of the filler metal and the mechanical properties of the welds made from 9% nickel cryogenic steel X8Ni9 are discussed. The results contribute to the development and conversion in the industrial practice a new laser beam-based welding technology for the automated manufacturing of LNG tanks. The remarkable heterogeneity in the chemical composition of the weld metal as well as an insufficient impact toughness could be indicated by using austenitic filler wire. The most promising results were achieved by applying 11%Ni filler wire, which is similar to the base material. A correlation between impact toughness and wire feeding speed could be shown. The highest impact toughness was 134 J at -196°C. The laser-hybrid welds passed the tensile test. The failure stress of 720 MPa with a fracture location in the base metal was achieved for all samples tested. T2 - Lasers in Manufacturing Conference 2019 CY - Munich, Germany DA - 24.06.2019 KW - X8Ni9 KW - Hybrid Laser Arc Welding KW - Cryogenic Steel KW - Low Temperature Toughness PY - 2019 SP - 1 EP - 11 PB - WLT Wissenschaftliche Gesellschaft Lasertechnik e.V. AN - OPUS4-48972 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Reisgen, U. A1 - Schleser, M. A1 - Abdurakhmanov, A. A1 - Gumenyuk, Andrey T1 - Measuring of plasma properties induced by non-vacuum electron beam welding N2 - Electron beam plasma measurement was realised by means of DIABEAM system invented by ISF RWTH Aachen. The Langmuir probe method is used for measurement. The relative simplicity of the method and the possibility of dispersion of high power on the probe allow its application for the investigation of high-power electron beams. The key element of the method is a rotating thin tungsten wire, which intersects the beam transversely on its axis and collects part of the current by itself. The signals, which are registered in the DIABEAM as a voltage, were taken in the form of amplitude. The conversion of the probe current into the distribution along the beam radius was realised using the Abel's method. A voltage-current characteristic was built for the beam current. The local electron density as well as the electron temperature, the floating potential and the plasma potential were measured and calculated by means of this characteristic. KW - Plasma KW - Diagnostic KW - Welding PY - 2012 DO - https://doi.org/10.1063/1.3675874 SN - 1070-664X VL - 19 SP - 0131006-1 EP - 0131006-7 PB - American Institute of Physics CY - Melville, NY, USA AN - OPUS4-25474 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Petrovskii, V.N. A1 - Uspenskii, S.A. A1 - Shcheglov, Pavel A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigation of a vapor-plasma welding torch induced by a high-power ytterbium fiber laser KW - Laser welding KW - Condensation KW - Diagnostic of the torch PY - 2011 SN - 2079-5629 VL - 2 IS - 2 SP - 159 EP - 165 PB - MAIK Nauka AN - OPUS4-24811 LA - rus AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Shcheglov, Pavel A1 - Uspenskii, S.A. A1 - Gumenyuk, Andrey A1 - Petrovskii, V.N. A1 - Rethmeier, Michael A1 - Yermachenko, V. M. T1 - Plume attenuation of laser radiation during high power fiber laser welding N2 - The results of an in-situ plume-laser interaction measurement during welding of mild steel with a 5 kW ytterbium fiber laser are reported. A measurement of the attenuation of probe laser beam passing through the plume has allowed to estimate the plume characteristics like the size of the extinction area and the spatial distribution of the extinction coefficient. The power loss of the fiber laser radiation propagating through the whole plume length was calculated. Together with a measured temporal characteristics of extinction the result indicates a significant decreasing of the laser radiation stability, which can lead to the formation of the macroscopic welding defects. KW - Laser welding KW - Plume KW - Beam attenuation KW - Particles PY - 2011 DO - https://doi.org/10.1002/lapl.201110010 SN - 1612-2011 VL - 8 IS - 6 SP - 475 EP - 480 PB - Wiley-VCH CY - Berlin AN - OPUS4-24812 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shcheglov, Pavel A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Uspensky, S.A. A1 - Petrovsky, V.N. T1 - Study of welding plume in high-power fiber laser welding T2 - LTWMP '11 - 5th International conference "Laser technologies in welding and materials processing" CY - Crimea, Ukraine DA - 2011-05-24 PY - 2011 SP - 142 EP - 147 AN - OPUS4-25473 LA - rus AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Shcheglov, Pavel A1 - Uspenskiy, S.A. T1 - SPEKTRAL'NAYa DIAGNOSTIKA PARO-PLAZMENNOGO FAKELA PRI SVARKE MOShchNYM ITTERBIEVYM VOLOKONNYM LAZEROM PY - 2013 DO - https://doi.org/10.7868/S0030403413070209 SN - 0030-4034 VL - 115 IS - 1 SP - 160 EP - 167 PB - Akad. Verl. CY - Moskva [u.a.] AN - OPUS4-29262 LA - rus AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gumenyuk, Andrey A1 - Petrovskiy, V.N. A1 - Rethmeier, Michael A1 - Shcheglov, Pavel A1 - Uspenskiy, S.A. T1 - Condensed metal particles influence during the high power fiber laser welding N2 - Different types of lasers are used nowadays for a number of technological Solutions, Modem high power solid-state lasers with high brightness of Radiation like Fiber or disc lasers find ever more applications in welding technology. Apart from the replacement of the CC>2-iasers traditionaHy used fcr these purposes, they provide new technological possibilities of metal treatment, such as using industrial robots and remote welding with high power laser radiation. The possibility of flexible optical fiber delivery of the radiation to any point gives a great technological advantage and permits welding processes to be realized with complicated weld seam geomelries and different positions using a minimum of additional fixtures. The short wavelength of the high power solid state lasers (1.07 ’m) causes another advantage. The coefflcient of inverse 170 Bremsstrahlung absorption from free electrons in plasma for such radiation is about 100 times lower than for the COi-iaser radiation. Owing to this fact, using the solid state lasers allows it to avoid a negative influence of the welding plume. However, a short wavelength can lead to another kind of laser Radiation attenuation, which is connected with the formation of a cloud consisting of small metal particles that absorb and scatter laser radiation. This cloud arises due to the condensation of hot metal vapor by flying out from the deep Penetration channel and broadening in relatively cold atmosphere over the metal Surface. Some theoretical and experimental approaches were made in advance in Order to estimate the influence of the Condensed particles on laser radiation and welding quality. In this paper a systematic study including the determination of the Cloud size and its dynamical characteristics is presented. The results were obtained within the scope of the first stage of the metal vapor condensation process Investigation during welding with high power fiber lasers. T2 - International Conference 'Lasers in Science, Technology, Medicine' CY - Moscow, Russia DA - 19.09.2011 PY - 2011 VL - 22 SP - 170 EP - 177 AN - OPUS4-29166 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Uspenskiy, S.A. A1 - Shcheglov, Pavel A1 - Petrovskiy, V.N. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Spectral diagnostics of a vapor-plasma plume produced during welding with a high-power ytterbium fiber laser N2 - We have conducted spectroscopic studies of the welding plasma formed in the process of welding with an ytterbium fiber laser delivering output power of up to 20 kW. The influence of shielding gases (Ar, He) on different parts of the welding plume is investigated. The absorption coefficient of the laser radiation by the welding-plume plasma is estimated. Scattering of 532-nm probe radiation from particles of the condensed metal vapor within the caustic of a high-power fiber laser beam is measured. Based on the obtained results, conclusions are made on the influence of the plasma formation and metal vapor condensation on the radiation of the high-power fiber laser and the stability of the welding process. PY - 2013 DO - https://doi.org/10.1134/S0030400X13070205 SN - 0030-400X SN - 1562-6911 VL - 115 IS - 1 SP - 140 EP - 146 PB - MAIK Nauka/Interperiodica Publ. / Pleiades Publishing, Ltd. CY - Moscow AN - OPUS4-28983 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - El-Batahgy, A.M. T1 - Laser and hybrid laser-arc welding of cryogenic 9 % NI Steel N2 - Heat treated 9%Ni steel is considered the most suitable and economic material for construction of large-size liquefied natural gas (LNG) storage tanks which operate at cryogenic temperatures (-196°C). Strength above 700 MPa as well as a minimum impact value of 60 J are required to ensure reliable operation of the LNG tanks at operating temperature. Conventional arc welding processes, including shielded metal arc welding, gas metal arc welding, gas tungsten arc welding and submerged arc welding, are currently used in construction of LNG tanks. Ni based filler wire is the preferred filler metal of choice in LNG tank construction. The main problem with this choice is the lower mechanical properties, particularly tensile strength of the weld metal. To compensate, the wall thickness needs to be excessively thick to ensure the strength of the welded structures. Ni based filler material is expensive and a large quantity is needed to fill the multi-pass weld grooves. These factors significantly add to the cost in the fabrication of LNG storage tanks. For these reasons, exploration of new welding technologies is a priority. A big potential can be seen in laser based welding techniques. Laser beam welding results in much smaller fusion zone with chemical composition and mechanical properties similar to that of the base material. Laser welding is a much faster process and allows for a joint geometry which requires less filler material and fewer welding passes. The advantages of laser welding can help to overcome the problems pointed out above. Trials of autogenous laser welding, laser cold-wire welding and hybrid laser-arc welding conducted on the 9%Ni steel are presented in this paper. Chemical composition of the weld metal as well as effects of welding parameters on the weld formation, microstructure and tensile strength is discussed. Filler wire penetration depth as well as character of its distribution in the narrow laser welds was examined using EPMA - electron probe microanalysis. KW - hardness KW - cryogenic steel KW - laser welding KW - microstructure KW - tensile strength PY - 2016 UR - http://gns.mephi.ru/sites/default/files/journal/file/en.2016.1-4.pdf SN - 2499-9733 VL - 1 IS - 18 SP - 34 EP - 45 PB - Research Nuclear University MEPHl CY - Moskau, Russia AN - OPUS4-36553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pavlov, V.A. A1 - Zavialov, S.V. A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Development of a measuring technology of strain field in welds N2 - In the article considered the problem of hot cracks occurrence during laser welding process. The main reason of their appearance is strain. The optical method for measuring full field strain locally near the solidification front during laser welding process is proposed. The proposed method of optical measurement allows to determine the real values of the critical strain for various materials characterizing the occurrence of hot cracks in laser welding process. T2 - 20th international conference "Digital signal processing and applications DSPA-2018" CY - Moskau, Russia DA - 28.03.2018 KW - Solidification cracking KW - Critical strain KW - Strain rate KW - Optical measurement KW - Laser welding KW - In situ strain PY - 2018 SN - 978-5-905278-33-4 SP - 749 EP - 754 AN - OPUS4-44910 LA - rus AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - El-Batahgy, A.M. A1 - Gumenyuk, Andrey A1 - Gook, S. A1 - Rethmeier, Michael T1 - Comparison between GTA and laser beam welding of 9%Ni steel for critical cryogenic applications N2 - IncomparisonwithGTAweldedjoints,highertensilestrengthcomparabletothatofthebasemetalwasobtained for laser beam welded joints due to fine martensitic microstructure. Impact fracture toughness values with much lower mismatching were obtained for laser beam welded joints due to similarity in the microstructures of its weld metal and HAZ. In this case, the lower impact fracture toughness obtained (1.37J/mm2) was much higher than that of the GTA welded joints (0.78J/mm2), which was very close to the specified minimum value (≥0.75J/mm2). In contrast to other research works, the overall tensile and impact properties are influenced not only by the fusion zone microstructure but also by the size of its hardened area as well as the degree of its mechanical mismatching, as a function of the welding process. A better combination of tensile strength and impact toughness of the concerned steel welded joints is assured by autogenous laser beam welding process. KW - Impact absorbed energy KW - 9%Ni steel KW - GTAW KW - Laser beam welding KW - Fusion zone size KW - Microstructure Tensile strength PY - 2018 DO - https://doi.org/10.1016/j.jmatprotec.2018.05.023 SN - 0924-0136 IS - 261 SP - 193 EP - 201 PB - Elsevier AN - OPUS4-45776 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -