TY - JOUR A1 - Schönherr, J. A. A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Geilen, M. B. A1 - Klein, M. A1 - Oechsner, M. T1 - Robust determination of fatigue crack propagation thresholds from crack growth data N2 - The robust determination of the threshold against fatigue crack propagation DKth is of paramount importance in fracture mechanics based fatigue assessment procedures. The standards ASTM E647 and ISO 12108 introduce operational definitions of DKth based on the crack propagation rate da/dN and suggest linear fits of logarithmic DK– da/dN test data to calculate DKth. Since these fits typically suffer from a poor representation of the actual curvature of the crack propagation curve, a method for evaluating DKth using a nonlinear function is proposed. It is shown that the proposed method reduces the artificial conservativeness induced by the evaluation method as well as the susceptibility to scatter in test data and the influence of test data density. KW - Fatigue crack propagation threshold KW - ISO 12108 KW - ASTM E647 KW - Data evaluation methods KW - Experimental determination PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-552153 DO - https://doi.org/10.3390/ma15144737 SN - 1996-1944 VL - 15 IS - 14 SP - 1 EP - 21 PB - MDPI CY - Basel AN - OPUS4-55215 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - The effect of the environmental conditions on the threshold against fatigue crack propagation N2 - The threshold against fatigue crack propagation (ΔKth) is a crucial parameter for the damage tolerance assessment of engineering components subjected to cyclic loading and it is composed by two distinct components, one intrinsic, dependent on the elastic material properties and the lattice type, and one extrinsic, related to the occurrence of crack closure effects. An important issue is that several factors can influence ΔKth and, in general, the fatigue crack propagation behavior. In this work, the influence of the experimental procedure, air humidity, stress ratio and test frequency on da/dN-ΔK data has been investigated. Results are discussed with their potential causes and consequences on the calculations of the residual lifetime. KW - Fatigue crack propagation threshold KW - Crack closure effect KW - Experimental procedure KW - Environmental conditions PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-544905 DO - https://doi.org/10.1016/j.prostr.2022.03.030 VL - 38 SP - 292 EP - 299 PB - Elsevier B.V. AN - OPUS4-54490 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Vergleichende Untersuchungen zum intrinsischen Schwellenwert der da/dN-ΔK-Kurve N2 - Für die Bestimmung der Restlebensdauer zyklisch beanspruchter Bauteile kommt dem Schwellenwert für Ermüdungsrissausbreitung, Δ𝐾𝑡ℎ, und dem sich anschließenden Schwellenwertbereich der 𝑑𝑎𝑑𝑁⁄−Δ𝐾-Kurve große Bedeutung zu. Dem stehen Unsicherheiten bei der Bestimmung und Analyse gegenüber. Der Aufsatz befasst sich mit der Ermittlung des sogenannten intrinsischen Schwellenwerts, der als robuster Eingangsparameter für eine „rissschließfreie“ Analyse der Restlebensdauer von entscheidender Bedeutung ist. T2 - 53. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Online meeting DA - 18.02.2021 KW - Schadenstolerante Bauteilauslegung, Restlebensdauer, intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung PY - 2021 SN - 2366-4797 SP - 211 EP - 220 PB - Deutscher Verband für Materialforschung und -prüfung e.V. (DVM) CY - Berlin AN - OPUS4-52704 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Der Schwellenwert der da/dN-∆K-Kurve als Auslegungskriterium für die Bauteilbewertung N2 - Für die Bestimmung der Restlebensdauer zyklisch beanspruchter Bauteile kommt dem Schwellenwert für Ermüdungsrissausbreitung ∆Kth und dem sich anschließenden Schwellenwertbereich der da/dN-∆K-Kurve große Bedeutung zu. Dem stehen Unsicherheiten bei der Bestimmung und Analyse gegenüber. Der Aufsatz befasst sich mit der Ermittlung des sogenannten intrinsischen Schwellenwerts, der als robuster Eingangsparameter für eine „rissschließfreie“ Analyse der Restlebensdauer von entscheidender Bedeutung ist. T2 - Tagung Werkstoffprüfung 2020 CY - Online meeting DA - 03.12.2020 KW - Schadenstolerante Bauteilauslegung, KW - Intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung KW - Restlebensdauer PY - 2020 DO - https://doi.org/10.48447/WP-2020-025 SP - 1 EP - 8 AN - OPUS4-52788 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - The use of effective fatigue crack propagation data obtained at closure-free conditions for component assessment N2 - The knowledge of fatigue crack propagation data in terms of their effective values is important for a conservative and safe life assessment of components subjected to cyclic loading. To overcome issues related to the precise consideration of the crack-closure effects on experimental data obtained at small R ratios, closure-free data have been obtained at R ≈ 0.8 by different experimental procedures. The statistical analysis of the intrinsic fatigue crack propagation threshold obtained experimentally has shown a small data scatter and good agreement between procedures. When compared with effective values obtained from analytical corrections of closure-affected data, the data obtained at R ≈ 0.8 should lead to a conservative life estimation. T2 - 43rd International Conference on Materials Mechanics CY - Sani, Greece DA - 05.06.2022 KW - Component assessment KW - Effective crack propagation data KW - Experimental procedure KW - Crack-closure PY - 2022 SP - 104 EP - 108 AN - OPUS4-56851 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Schönherr, J. A. A1 - Geilen, M. B. A1 - Klein, M. A1 - Oechsner, M. T1 - Recent developments in the determination of fatigue crack propagation thresholds N2 - The impact of crack closure and environmental effects on the experimental determination of the fatigue crack propagation threshold is a major problem for the assessment of cyclically loaded components, especially at low stress ratios 𝑅. In this work, the influence of the experimental procedure and air humidity on d𝑎∕d𝑁 − 𝛥𝐾 data at different 𝑅 is discussed. Unlike the results at 𝑅 = −1, the threshold values obtained at 𝑅 ≈ 0.8, i.e. under negligible crack closure levels, show a very small scatter band regardless of the variation of the test parameters and environmental conditions. KW - Fatigue crack propagation threshold KW - Component assessment KW - Crack closure KW - Environmental effects KW - Testing parameters PY - 2022 DO - https://doi.org/10.1016/j.ijfatigue.2022.107131 SN - 0142-1123 VL - 164 SP - 1 EP - 15 PB - Elsevier Ltd. AN - OPUS4-55403 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Schönherr, J. A. T1 - Ermittlung des intrinsischen Schwellenwerts und dessen Validierung als Werkstoffparameter N2 - Die Anwendung bruchmechanischer Methoden zur schadenstoleranten Bauteilauslegung ist für zyklische Lasten im Bereich der Paris-Geraden Stand der Technik. Technisch relevant sind jedoch häufig geringere Lasten im Schwellenwertbereich der d𝑎/d𝑁-Δ𝐾-Kurve. Aufgrund des großen Einflusses von Rissschließeffekten ist dessen Bestimmung jedoch nicht nur aufwändig, sondern auch potenziell fehlerbehaftet. Die Bauteilauslegung erfolgt zweckmäßigerweise auf der Basis effektiver, d. h. rissschließkorrigierter Rissfortschrittsdaten. Von großer Bedeutung ist auch der intrinsische Schwellenwert, unterhalb dessen keine Risserweiterung mehr eintritt. In diesem Forschungsprojekt erfolgte eine Untersuchung des Einflusses verschiedener Prüfverfahren und Umgebungsbedingungen auf die Ermittlung des Schwellenwerts gegen Ermüdungsrissausbreitung Δ𝐾th. Es wurden statistisch abgesicherte Empfehlungen zur experimentellen Ermittlung des intrinsischen Schwellenwerts Δ𝐾th,eff abgeleitet. Dieser dient auch als Eingangsparameter einer weiterentwickelten Prozedur zur Bauteilauslegung auf der Basis bei einem Lastverhältnis von 𝑅 ≈ 0,8 ermittelter, effektiver, Rissfortschrittsdaten. Es zeigte sich, dass die bei einem Lastverhältnis von 𝑅 ≈ 0,8 in Laborluft bei höherer Prüffrequenzen (≥90 Hz) ermittelten Schwellenwerte eine konservative Abschätzung des intrinsischen Schwellenwerts erlaubten. Bei Lastverhältnissen 𝑅 ≪ 0,8 wurde ein teilweise stark ausgeprägter Einfluss extrinsischer Effekte auf das Rissfortschrittsverhalten festgestellt. Eine Untersuchung der Bruchflächen ergab Oxidschichtdicken in der Größenordnung mehrerer hundert Nanometer. Bei Reduktion der Prüffrequenz auf ≈55 Hz und Prüfung in feuchter Luft (60 % r.F. und 80 % r.F.) konnte auch bei 𝑅 = 0,8 Rissschließen beobachtet werden. Die weiterentwickelte Prozedur zur Bauteilauslegung auf Basis effektiver Rissfortschrittsdaten lieferte aber stets konservative Ergebnisse in einem tolerierbaren Fehlerbereich und ist deshalb zur Anwendung geeignet. Die im Projekt gewonnenen Erkenntnisse tragen zu einer robusten Bauteilauslegung auf bruchmechanischer Basis bei. Der stark reduzierte Versuchsumfang bei Nutzung effektiver Rissfortschrittsdaten gegenüber der Ermittlung von spannungsverhältnisabhängigen Rissfortschrittskurven beschleunigt und vereinfacht die Bauteilauslegung auf Basis bruchmechanischer Methoden. KW - Schwellenwert gegen Ermüdungsrissausbreitung KW - Einflussfaktoren auf Rissfortschrittsdaten KW - Bauteilauslegung KW - Rissschließeffekte PY - 2023 SN - 978-3-96780-151-4 SP - 1 EP - 190 PB - Forschungsvereinigung Stahlanwendung e. V. CY - Düsseldorf AN - OPUS4-58459 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Vojtek, T. A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Pokorný, P. A1 - Jambor, M. A1 - Hutař, P. T1 - Determination of fatigue crack propagation thresholds for steel in presence of environmental effects N2 - The experimental determination of the resistance to fatigue crack propagation in steel, particularly in the socalled near-threshold regime, is a crucial issue for safety-relevant components which are designed to operate for a large number of loading cycles before undergoing periodic inspections. This work summarizes the most relevant results of extensive experimental campaigns conducted at BAM and IPM over the last years, which have been devoted to the determination of fatigue crack propagation characteristics on medium and high strength steels. The influence of environment, oxide-induced crack closure and test methodologies in the near-threshold regime are discussed. KW - Steel KW - Fatigue crack propagation threshold KW - Oxide-induced crack closure KW - Environmental effect PY - 2021 DO - https://doi.org/10.1016/j.ijfatigue.2021.106449 SN - 0142-1123 VL - 153 SP - 1 PB - Elsevier Ltd. AN - OPUS4-53525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -