TY - CONF A1 - Simbruner, Kai A1 - Billone, M. C. A1 - Zencker, Uwe A1 - Liu, Y. Y. A1 - Völzke, Holger T1 - Brittle Failure Analysis of High-Burnup PWR Fuel Cladding Alloys N2 - The general aim of this research is the development of methods for predicting mechanical behavior and identification of limiting conditions to prevent brittle failure of high-burnup (HBU) pressure water reactor (PWR) fuel cladding alloys. A finite element (FE) model of the ring compression test (RCT) was created to analyze the failure behavior of zirconium-based alloys with radial hydrides during the RCT. An elastic-plastic material model describes the zirconium alloy. The stress-strain curve needed for the elastic-plastic material model was derived by inverse finite element analyses. Cohesive zone modeling is used to reproduce sudden load drops during RCT loading. Based on the failure mechanism in non-irradiated ZIRLO® claddings, a micro-mechanical model was developed that distinguishes between brittle failure along hydrides and ductile failure of the zirconium matrix. Two different cohesive laws representing these types of failure are present in the same cohesive interface. The key differences between these constitutive laws are the cohesive strength, the stress at which damage initiates, and the cohesive energy, which is the damage energy dissipated by the cohesive zone. Statistically generated matrix-hydride distributions were mapped onto the cohesive elements and simulations with focus on the first load drop were performed. Computational results are in good agreement with the RCT results conducted on high-burnup M5® samples. It could be shown that crack initiation and propagation strongly depend on the specific configuration of hydrides and matrix material in the fracture area. T2 - 26th International Conference on Structural Mechanics in Reactor Technology - SMiRT 26 CY - Potsdam, Germany DA - 10.07.2022 KW - Cladding Embrittlement KW - Cohesive Zone Modelling KW - Spent Nuclear Fuel KW - Ring Compression Test PY - 2022 SP - 1 EP - 10 AN - OPUS4-55434 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Zencker, Uwe A1 - Aguado, Carlos A1 - Arkoma, Asko A1 - Bertsch, Johannes A1 - Cristóbal Beneyto, Miguel A1 - Feria Marquez, Francisco A1 - Herranz, Luis Enrique A1 - Ivanov, Ivan A1 - Király, Márton A1 - Nasyrow, Ramil A1 - Papaioannou, Dimitrios A1 - Ruiz-Hervias, Jesus A1 - Vlassopoulos, Efstathios T1 - Thermo-mechanical-chemical properties of unirradiated and irradiated samples of spent nuclear fuel rod segments and cladding N2 - The report addresses the experimental characterisation, thermo-mechanical modelling and performance of unirradiated and irradiated samples of spent nuclear fuel rod segments and cladding. Hydrogen is relocated in nuclear fuel claddings by diffusion along temperature, stress, and concentration gradients, and towards a liner if existent. The precipitation of hydrides during cool-down at the beginning of the storage is influenced by mechanical stress. A strong accumulation of hydrides and a disadvantageous hydride alignment in relation to the stress state can affect the mechanical properties and compromise the fuel cladding integrity. Neutron radiography is used to determine spatially resolved hydrogen and hydride distributions in claddings. A liner in duplex claddings attracts hydrogen, which will then no longer be available to form detrimental hydrides in the bulk part of the cladding. Individual three-point bending and gravitational impact tests on filled pressurised spent nuclear fuel rod segments were conducted in hot-cell facilities. The material behaviour under three-point bending in the presence of hydrides and at different temperatures was systematically investigated in quasi-static laboratory tests on unirradiated rod segments with and without surrogate pellets until rupture. Ring compression tests were carried out on irradiated and unirradiated samples at different temperatures and both with and without radial hydrides. With radial hydrides, brittle failure is possible even at low deformation and simultaneously low temperature. Crack initiation will occur on the radial hydride with the highest fracture mechanics load, which depends on the hydride size in the regions with the highest hoop stresses. Due to the high hydrogen content used in creep tests conducted, precipitation hardening of the hydrides in the zirconium alloy significantly reduces the creep rate, as it strengthens the material and inhibits the dislocation sliding. The use of finite element analyses on mechanical tests to determine the cladding properties using a numerical optimisation method based on a large number of automatically generated sensitivity calculations is demonstrated. The brittle fracture of cladding samples with radial hydrides in the ring compression test can be described with a cohesive zone model if the cohesive parameters are selected appropriately and the hydride morphology is specified. Progress was made in the verification, validation and enhancement of spent fuel performance codes by the compilation of a representative validation database (related to rod internal pressure, fission gas release, rod void volume, and in-clad hydrogen distribution), the enhancement of CIEMAT’s FRAPCON-xt code for rod internal pressure prediction at high burnup, the enhancement of CIEMAT’s in-clad hydrogen performance subroutine HYDCLAD with more phenomenological modelling, the extension of INL’s BISON code with a cladding creep law for dry storage, and a benchmark with FRAPCON-xt and BISON simulating in-reactor and dry storage scenarios. KW - Spent Nuclear Fuel KW - Cladding KW - Experimental Characterisation KW - Modelling KW - Fuel Performance Code PY - 2024 SP - 1 EP - 102 PB - European Joint Programme EURAD AN - OPUS4-61008 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Völzke, Holger T1 - Brittle Failure Limits of Spent Fuel Claddings Subjected to Long-Term Dry Interim Storage Conditions N2 - The mechanical properties of spent fuel claddings can be adversely affected under the conditions of long-term dry interim storage, so that the failure limits may be reached in case of mechanical loads during handling or transport after storage. Pre-storage drying and the early stage of interim storage can expose the cladding to higher temperatures and higher tensile hoop stresses than those associated with in-reactor operation and pool storage. During slow cooling of a cladding tube under internal pressure, radial hydrides may precipitate in zirconium-based cladding alloys. This can lead to embrittlement of the material and sudden failure of the cladding integrity under mechanical stress. In order to prevent brittle failure, numerical methods are being developed to predict the mechanical behaviour and identify limiting conditions. Experimental investigations, numerical analyses and evaluation methods are discussed. An established experimental method for characterising cladding materials is the Ring Compression Test (RCT). Some test results on irradiated cladding tubes after operation in pressure water reactors are publicly available. However, it is helpful to carry out studies on unirradiated surrogate claddings with similar material properties to reduce the effort associated with irradiated samples in hot cells and to perform material tests with a wider range of parameters. On the basis of such experimental data, load-displacement curves have been numerically analysed for a selection of cladding materials. Radial hydrides can cause a sample to break suddenly due to fracture even at low deformation. Noticeable load drops in the RCT are caused by unstable crack propagation through the radial hydride network. The failure mechanism is quasi-cleavage in the hydrides and micro-void nucleation, growth, and coalescence in the zirconium matrix, with ductile tearing patches connecting adjacent hydrides. The cohesive zone approach was used to simulate the failure process taking into account the radial hydride morphology. The developed method can adequately describe both the deformation and failure behaviour of irradiated as well as unirradiated claddings of zirconium-based alloys with radial hydrides under RCT conditions. Limiting conditions can be expressed in terms of fracture energy and cohesive strength. T2 - IAEA International Conference on the Management of Spent Fuel from Nuclear Power Plants - Meeting the Moment CY - Vienna, Austria DA - 10.06.2024 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2024 SP - 1 EP - 10 AN - OPUS4-60323 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe T1 - Brittle Failure Limits of Spent Fuel Claddings Subjected to Long-Term Dry Interim Storage Conditions N2 - The mechanical properties of spent fuel claddings can be adversely affected under the conditions of long-term dry interim storage, so that the failure limits may be reached in case of mechanical loads during handling or transport after storage. Pre-storage drying and the early stage of interim storage can expose the cladding to higher temperatures and higher tensile hoop stresses than those associated with in-reactor operation and pool storage. During slow cooling of a cladding tube under internal pressure, radial hydrides may precipitate in zirconium-based cladding alloys. This can lead to embrittlement of the material and sudden failure of the cladding integrity under mechanical stress. In order to prevent brittle failure, numerical methods are being developed to predict the mechanical behaviour and identify limiting conditions. Experimental investigations, numerical analyses and evaluation methods are discussed. An established experimental method for characterising cladding materials is the Ring Compression Test (RCT). Some test results on irradiated cladding tubes after operation in pressure water reactors are publicly available. However, it is helpful to carry out studies on unirradiated surrogate claddings with similar material properties to reduce the effort associated with irradiated samples in hot cells and to perform material tests with a wider range of parameters. On the basis of such experimental data, load-displacement curves have been numerically analysed for a selection of cladding materials. Radial hydrides can cause a sample to break suddenly due to fracture even at low deformation. Noticeable load drops in the RCT are caused by unstable crack propagation through the radial hydride network. The failure mechanism is quasi-cleavage in the hydrides and micro-void nucleation, growth, and coalescence in the zirconium matrix, with ductile tearing patches connecting adjacent hydrides. The cohesive zone approach was used to simulate the failure process taking into account the radial hydride morphology. The developed method can adequately describe both the deformation and failure behaviour of irradiated as well as unirradiated claddings of zirconium-based alloys with radial hydrides under RCT conditions. Limiting conditions can be expressed in terms of fracture energy and cohesive strength. T2 - IAEA International Conference on the Management of Spent Fuel from Nuclear Power Plants - Meeting the Moment CY - Vienna, Austria DA - 10.06.2024 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2024 AN - OPUS4-60324 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Gaddampally, Mohan Reddy A1 - Völzke, Holger T1 - Failure Analysis on Irradiated Claddings Subjected to Long-Term Dry Interim Storage N2 - Long-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. The cladding is the first barrier for the spent fuel pellets. An established method for characterising the cladding material is the ring compression test (RCT), in which a small, cylindrical sample of the cladding tube is subjected to a compressive load. Radial hydrides may precipitate in zirconium-based alloys (Zircaloy) under pre-storage drying and during slow cooling, which result in embrittlement of the cladding material and eventually a possible sudden failure of cladding integrity under additional mechanical loads. The focus of the presented research is on the development of appropriate nu-merical methods for predicting the mechanical behaviour and identification of limiting conditions to prevent brittle fracture of Zircaloy claddings. A modelling approach based on cohesive zones is ex-plained which is able to reproduce the propagation of cracks initiated at radial hydrides in the zir-conium matrix. The developed methods are applied to defueled samples of cladding alloy ZIRLO®, which were subjected to a thermo-mechanical treatment to reorient existing circumferential hy-drides to radial hydrides. A selected sample showing sudden load drops during a quasi-static ring compression test is analysed by means of fracture mechanics for illustrative purposes. Based on the developed fracture mechanics approach, not only the deformation behaviour but also the fail-ure behaviour of irradiated as well as unirradiated Zircaloy claddings with radial hydrides under RCT loading conditions can be adequately described. T2 - 27th International Conference on Structural Mechanics in Reactor Technology - SMiRT 27 CY - Yokohama, Japan DA - 03.03.2024 KW - Cladding Embrittlement KW - Cohesive Zone Modelling KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2024 SP - 1 EP - 8 AN - OPUS4-60671 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe T1 - Failure Analysis on Irradiated Claddings Subjected to Long-Term Dry Interim Storage N2 - Long-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. The cladding is the first barrier for the spent fuel pellets. An established method for characterising the cladding material is the ring compression test (RCT), in which a small, cylindrical sample of the cladding tube is subjected to a compressive load. Radial hydrides may precipitate in zirconium-based alloys (Zircaloy) under pre-storage drying and during slow cooling, which result in embrittlement of the cladding material and eventually a possible sudden failure of cladding integrity under additional mechanical loads. The focus of the presented research is on the development of appropriate nu-merical methods for predicting the mechanical behaviour and identification of limiting conditions to prevent brittle fracture of Zircaloy claddings. A modelling approach based on cohesive zones is ex-plained which is able to reproduce the propagation of cracks initiated at radial hydrides in the zir-conium matrix. The developed methods are applied to defueled samples of cladding alloy ZIRLO®, which were subjected to a thermo-mechanical treatment to reorient existing circumferential hy-drides to radial hydrides. A selected sample showing sudden load drops during a quasi-static ring compression test is analysed by means of fracture mechanics for illustrative purposes. Based on the developed fracture mechanics approach, not only the deformation behaviour but also the fail-ure behaviour of irradiated as well as unirradiated Zircaloy claddings with radial hydrides under RCT loading conditions can be adequately described. T2 - 27th International Conference on Structural Mechanics in Reactor Technology - SMiRT 27 CY - Yokohama, Japan DA - 03.03.2024 KW - Cladding Embrittlement KW - Cohesive Zone Modelling KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2024 AN - OPUS4-60672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe T1 - Embrittlement of spent fuel claddings during long-term dry interim storage - Current approach at BAM N2 - In this presentation, the actual situation of long-term dry interim storage of spent nuclear fuel in Germany is reported. An extension of the interim storage period between 40 and 100 years for at least a relevant number of casks is foreseeable. To demonstrate the integrity of fuel rods and cladding tubes throughout the extended dry interim storage, a potential cladding embrittlement should be investigated. The current approach at BAM is a research project on experimental and numerical investigations of sudden failure of unirradiated pre-hydrided cladding tubes after hydride reorientation at small deformation under Ring Compression Test conditions. A fracture mechanics based failure analysis and suggested failure criteria for a potential brittle failure of spent fuel claddings after long-term dry interim storage under mechanical loads are discussed. T2 - IAEA - Second Coordinate Research Meeting and Consultancy Meeting on Ageing Management Programmes for Spent Fuel Dry Storage Systems CY - Lemont, IL, USA DA - 29.04.2019 KW - Ageing Management KW - Extended Storage KW - Spent Nuclear Fuel KW - Cladding Embrittlement KW - Ring Compression Test PY - 2019 AN - OPUS4-48745 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe T1 - Brittle failure of spent fuel claddings during long-term dry interim storage N2 - The current research project BRUZL (Fracture mechanical analysis of spent fuel claddings during long-term dry interim storage) is presented. General aim of the project is the development of methods for risk assessment and identification of boundary conditions to prevent potential sudden brittle failure of spent fuel claddings at small deformation during long-term dry interim storage and subsequent transportation. The project is funded by the Federal Ministry for Economic Affairs and Energy (BMWi) under contract no. 1501561. T2 - 3rd GRS Workshop on Safety of Extended Dry Storage of Spent Nuclear Fuel CY - Garching, Germany DA - 05.06.2019 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2019 AN - OPUS4-48867 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe T1 - Brittle failure of spent fuel claddings under long-term dry interim storage conditions – Preliminary analysis N2 - The evaluation of cladding integrity is a major issue to be demonstrated in Germany for extended interim storage periods up to 100 years and subsequent transportation considering operational and accidental conditions with respect to reactor operation, cask drying and dry interim storage. The chemical reaction between the zirconium fuel cladding and the cooling water in water-cooled reactors produces hydrogen and zirconium oxide. Hydrogen diffuses into the cladding and precipitates as zirconium hydrides when the solubility limit is reached, preferably oriented in hoop direction. At high temperatures during vacuum drying procedures, the hydrides can dissolve. Over a succeeding period of slow cooling with existing hoop stress the hydrides precipitate again, but partly reoriented along the radial direction of the cladding. This change of microstructure in combination with a decreasing temperature (0.5...2 K/year) during (extended) interim storage and additional mechanical load by handling procedures or under accident conditions could lead to a potential cladding embrittlement and consequently increased failure probability. The current research project BRUZL (Fracture mechanical analysis of spent fuel claddings under long-term dry interim storage conditions) has been launched by BAM to investigate potential sudden brittle failure of spent fuel claddings at small deformation under long-term dry interim storage conditions and is presented. T2 - IAEA International Conference on the Management of Spent Fuel from Nuclear Power Reactors CY - Vienna, Austria DA - 24.06.2019 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2019 AN - OPUS4-48868 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Simbruner, Kai A1 - Völzke, Holger T1 - Brittle failure of spent fuel claddings under long-term dry interim storage conditions – Preliminary analysis N2 - The evaluation of cladding integrity is a major issue to be demonstrated in Germany for extended interim storage periods up to 100 years and subsequent transportation considering operational and accidental conditions with respect to reactor operation, cask drying and dry interim storage. The chemical reaction between the zirconium fuel cladding and the cooling water in water-cooled reactors produces hydrogen and zirconium oxide. Hydrogen diffuses into the cladding and precipitates as zirconium hydrides when the solubility limit is reached, preferably oriented in hoop direction. At high temperatures during vacuum drying procedures, the hydrides can dissolve. Over a succeeding period of slow cooling with existing hoop stress the hydrides precipitate again, but partly reoriented along the radial direction of the cladding. This change of microstructure in combination with a decreasing temperature (0.5...2 K/year) during (extended) interim storage and additional mechanical load by handling procedures or under accident conditions could lead to a potential cladding embrittlement and consequently increased failure probability. The current research project BRUZL (Fracture mechanical analysis of spent fuel claddings under long-term dry interim storage conditions) has been launched by BAM to investigate potential sudden brittle failure of spent fuel claddings at small deformation under long-term dry interim storage conditions and is presented. T2 - IAEA International Conference on the Management of Spent Fuel from Nuclear Power Reactors CY - Vienna, Austria DA - 24.06.2019 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2019 SP - Paper IAEA-CN-272/49, 1 EP - 8 AN - OPUS4-48869 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -